HYALURONATE FIBER AND MANUFACTURING METHOD THEREOF

Abstract

A high-strength hyaluronate fiber, suitable for use in a surgical suture, a lifting thread, a tissue-engineering scaffold, etc., and a manufacturing method thereof are proposed. The method includes (a) controlling a water content of a hyaluronate having a weight average molecular weight of 100-3,000 kDa to 50-95 wt % to prepare a hyaluronate paste, (b) melting the hyaluronate paste having a controlled water content at a temperature ranging from room temperature to 100° C., and then extruding the hyaluronate paste through a nozzle, and (c) drying the extruded spinning fluid to form a fiber. The hyaluronate fiber has the water content of 5-25 wt %, the tensile strength of 3 to 15 kg/mm.sup.2, and a smooth surface with small cracks, so that the hyaluronate fiber can be used for a surgical suture, a lifting thread, a filler for cosmetic surgery, a tissue-engineering scaffold, etc.

Claims

1. A hyaluronate fiber having a bending angle of 2 to 10° when measured by a following method of measuring the bending angle, a water content of 5 to 25 wt %, and a hyaluronate content of 90 wt % or more, based on a total fiber weight excluding water: <Method of measuring the bending angle> (a) preparing HA fiber having a length of 20 cm and a diameter of 1 mm, (b) fixing 3 cm of a first end of the HA fiber to an upper surface of a flat plate, and (c) measuring an angle (0) between an upper-surface extension line (B) of the flat plate and an extension line (T) of a second end of the HA fiber.

2. The hyaluronate fiber of claim 1, wherein the hyaluronate fiber has a tensile strength of 3 to 15 kg/mm.sup.2.

3. The hyaluronate fiber of claim 1, wherein a crack amount of the hyaluronate fiber is 15% or less of a surface area of the fiber.

4. A method of manufacturing a hyaluronate fiber, comprising: (a) controlling a water content of a hyaluronate having a weight average molecular weight of 100-3,000 kDa to 50-95 wt % to prepare a hyaluronate paste; (b) melting the hyaluronate paste having a controlled water content at a temperature ranging from room temperature to 100° C., and then extruding the hyaluronate paste through a nozzle; and (c) drying the extruded spinning fluid to form a fiber.

5. The method of claim 4, wherein the drying is performed at a temperature ranging from room temperature to 100° C.

6. The method of claim 4, wherein the manufactured hyaluronate fiber has a tensile strength of 3 to 15 kg/mm.sup.2.

7. A surgical suture, comprising the hyaluronate fiber of claim 1.

8. A filler for cosmetic surgery, comprising the hyaluronate fiber of claim 1.

9. A lifting thread, comprising the hyaluronate fiber of claim 1.

10. A tissue-engineering scaffold, comprising the hyaluronate fiber of claim 1.

Description

DESCRIPTION OF DRAWINGS

[0026] FIG. 1 illustrates a process of measuring a bending angle of a hyaluronate fiber in accordance with an embodiment of the present disclosure.

[0027] FIGS. 2 to 4 are micrographs of the surface of the hyaluronate fiber manufactured by the present disclosure.

BEST MODE

[0028] According to the present disclosure, when a hyaluronate paste having a water content that is controlled to be in a predetermined range is melted, extruded through a nozzle, and then dried, it is possible to manufacture a hyaluronate fiber having a high strength and a smooth surface without cracks.

[0029] In the present disclosure, the hyaluronate fiber is manufactured through the following method. First, the hyaluronate paste is prepared by controlling the percentage of water content of a hyaluronate to 50-95 wt %. The hyaluronate paste is melted at a temperature ranging from room temperature to 100° C., and then is extruded through the nozzle. Subsequently, this is dried at a temperature ranging from room temperature to 100° C., thus manufacturing the hyaluronate fiber.

[0030] As a result, it is possible to mass produce a hyaluronate fiber in which a water content thereof ranges from 5 to 25 wt %, a tensile strength thereof ranges from 3 to 15 kg/md, and a surface thereof is smooth without cracks.

[0031] Therefore, the present disclosure is directed to a hyaluronate fiber having a bending angle of 2 to 10° when measured by the following measuring method, a water content of 5 to 25 wt %, and a hyaluronate content of 90 wt % or more, based on a total fiber weight excluding water.

[0032] As shown in FIG. 1, the method of measuring the bending angle of the hyaluronate fiber is as follows:

[0033] (a) preparing HA fiber having a length of 20 cm and a diameter of 1 mm,

[0034] (b) fixing 3 cm of one end of the HA fiber to an upper surface of a flat plate, and

[0035] (c) measuring an angle θ between an upper-surface extension line B of the flat plate and an extension line (T) of the other end of the HA fiber.

[0036] In the present disclosure, the bending angle of the hyaluronate fiber relates to the convenient use of the hyaluronate fiber during a surgical procedure, and preferably ranges from 2 to 10°. When the bending angle is less than 2° and more than 10°, the convenience of using the fiber is reduced.

[0037] In the present disclosure, the water content of the hyaluronate fiber affects the bending angle, microbial contamination, and physical properties, and preferably ranges from 5 to 25 wt %, more preferably 5 to 15 wt %. When the water content is less than 5 wt %, the fiber maintains its shape but is hardened and inflexible, so that the fiber is easily broken. On the other hand, when the water content is more than 25 wt %, the fiber does not maintain its shape or does not properly perform its function.

[0038] Since the hyaluronate fiber of the present disclosure may be made exclusively of hyaluronate, the fiber has the hyaluronate content of 90-100 wt %, based on a total fiber weight excluding water. Depending on an application field, carriers or excipients which are commonly used in the art may be additionally included, but their types and content ranges are not particularly limited.

[0039] The hyaluronate fiber of the present disclosure has the tensile strength of 3 to 15 kg/md, and the crack amount of the fiber is 15% or less of the surface area of the fiber. In the present disclosure, the crack amount indicates the smoothness of the surface of the hyaluronate fiber. The crack amount may be measured by capturing the image of the surface of the hyaluronate fiber with a microscope and then calculating a ratio of cracks, such as pores (grooves) or linear gaps, present in a total hyaluronic-fiber image capturing area. The crack amount is preferably 15% or less. Meanwhile, when the crack amount exceeds 15%, this is not preferable because there is a risk of causing damage to the skin during the procedure.

[0040] Further, the present disclosure is directed to a method of manufacturing a hyaluronate fiber, including the steps of: (a) controlling a water content of a hyaluronate having a weight average molecular weight of 100-3,000 kDa to 50-95 wt % to prepare a hyaluronate paste; (b) melting the hyaluronate paste having a controlled water content at a temperature ranging from room temperature to 100° C., and then extruding the hyaluronate paste through a nozzle; and (c) drying the extruded spinning fluid to form a fiber.

[0041] In the present disclosure, the hyaluronate is produced by linking salt to hyaluronic acid. Examples of the hyaluronate may include sodium hyaluronate, calcium hyaluronate, and potassium hyaluronate, but the present disclosure is not limited thereto.

[0042] In the present disclosure, the hyaluronate preferably has the molecular weight of 100 to 3,000 kDa. Further, the water content in the hyaluronate of the hyaluronate paste ranges from 50 to 95 wt %.

[0043] The hyaluronate paste may be prepared by adding solvent to the hyaluronate. The solvent may use water or ethanol aqueous solution. It is preferable to perform a mixing operation until the solvent is uniformly mixed.

[0044] In order to smoothly perform the mass spinning process, the water content of the hyaluronate paste may range from 50 to 95 wt %, and preferably 88 to 92 wt %. When the water content is less than 50 wt %, high pressure is required during the spinning operation, and a large amount of cracks may be present in the manufactured fiber. On the other hand, when the water content is more than 95 wt %, the hyaluronate paste is in the form of liquid rather than paste, so that the fiber may be undesirably broken during the spinning operation.

[0045] In the present disclosure, after the hyaluronate paste is prepared, it is left at 0 to 100° C. for 6 to 12 hours to attain water equilibrium. When the temperature and the time are out of the above-described ranges, the water equilibrium is not properly achieved. The water equilibrium enables water molecules of the paste and the hyaluronic acid to be evenly mixed with each other. In the case of performing the spinning operation without the water equilibrium, the water molecules and the hyaluronic acid are not evenly mixed with each other, so that it is impossible to perform the spinning operation at a constant rate, or the crack amount in the manufactured fiber may be undesirably increased.

[0046] In the present disclosure, the hyaluronate paste having the water content controlled to 50-95 wt % is put into a spinning apparatus, is melted at a temperature ranging from room temperature to 100° C., and then is extruded through the nozzle, thus preparing spinning fluid. Here, when the temperature is less than about 15° C. that is room temperature, the hyaluronate paste is not melted and thereby is not extruded. On the other hand, when the temperature is more than 100° C., the paste may be undesirably boiled.

[0047] In the present disclosure, the extruded spinning fluid is dried, thus finally producing fiber. The drying operation is preferably performed at a temperature ranging from room temperature to 100° C. depending on the water content of the paste.

[0048] Since the hyaluronate fiber manufactured according to the present disclosure may have a hyaluronate content of 90 wt % or more, have a water content of 5 to 25 wt %, have a tensile strength of 3 to 15 kg/md, and have a smooth surface, there is no microbial contamination and it is easy to manage and use, so that the hyaluronate fiber of the present disclosure can be efficiently used in various types of tissue repair products, unlike an existing liquid hyaluronate tissue repair product.

[0049] Thus, the present disclosure addresses a surgical suture, a filler for cosmetic surgery, a lifting thread, and a tissue-engineering scaffold including the aforementioned hyaluronate fiber.

Mode for Invention

[0050] A better understanding of the present disclosure may be obtained through the following examples, which are set forth to illustrate, but are not to be construed as limiting the scope of the present disclosure, as will be apparent to those skilled in the art.

EXAMPLE 1

Preparation of Hyaluronate Paste

[0051] Water was applied to sodium hyaluronate (Hi-Aqua™, made by JinWOO Bio) having a molecular weight of 150 kDa, and then was mixed and kneaded to prepare a hyaluronate paste having a water content of 50-95 wt %.

[0052] The prepared hyaluronate paste was cold-stored at 4° C. for 12 hours to create water equilibrium.

EXAMPLE 2

Production of Hyaluronate Fiber by Spinning

[0053] The hyaluronate paste prepared in Example 1 was placed in a storage section of a spinning apparatus, melted at a temperature ranging from room temperature to 100° C., pressurized, and spun through a nozzle, followed by drying at 40° C., thus manufacturing a hyaluronate fiber having a water content of 0-95 wt %.

COMPARATIVE EXAMPLE 1

Preparation of Hyaluronate Paste

[0054] Water was applied to sodium hyaluronate (Hi-Aqua™, made by JinWOO Bio) having a molecular weight of 150 kDa, and then was mixed and kneaded to prepare a hyaluronate paste having a water content of 5-40 wt %. The prepared hyaluronate paste was cold-stored at 4° C. for 12 hours to create water equilibrium.

COMPARATIVE EXAMPLE 2

Preparation of Hyaluronate Paste

[0055] Water was applied to sodium hyaluronate (Hi-Aqua™, made by JinWOO Bio) having a molecular weight of 150 kDa, and then was mixed and kneaded to prepare a hyaluronate paste having a water content of 85 wt %. Water equilibrium was not created.

COMPARATIVE EXAMPLE 3

Production of Hyaluronate Fiber by Spinning

[0056] The hyaluronate paste prepared in Comparative Example 1 was placed in a storage section of a spinning apparatus, melted at a temperature ranging from room temperature to 100° C., pressurized, and spun through a nozzle, followed by drying at 40° C., thus manufacturing a hyaluronate fiber having a water content of 0-95 wt %.

COMPARATIVE EXAMPLE 4

Production of Hyaluronate Fiber by Spinning

[0057] The hyaluronate paste prepared in Comparative Example 2 was placed in a storage section of a spinning apparatus, melted at a temperature ranging from room temperature to 100° C., pressurized, and spun through a nozzle, followed by drying at 40° C., thus manufacturing a hyaluronate fiber having a water content of 0-95 wt %.

TEST EXAMPLE 1

Spinning-Process Evaluation Depending on Water Content of Hyaluronate Paste

[0058] The hyaluronate paste prepared in each of Example 1 and Comparative Example 1 was placed in a storage section of a spinning apparatus, melted at a temperature ranging from room temperature to 100° C., pressurized, and spun through a nozzle, followed by drying at 40° C., thus manufacturing a hyaluronate fiber having a water content of 0-95 wt %. A spinning speed was evaluated.

[0059] Consequently, Example 1 where the water content of the hyaluronate paste is 50-95 wt % showed a spinning speed of 0.05m/min, and Comparative Example 1 where the water content is 5-40 wt % showed a spinning speed of 0.4m/min.

TEST EXAMPLE 2

Bending-Angle Measurement of Hyaluronate Fiber

[0060] The bending angle of the hyaluronate fiber manufactured in Example 2 was measured by the following method, and the measured results are shown in Table 1.

[0061] (a) Preparing HA fiber having the length of 20 cm and the diameter of 1 mm.

[0062] (b) Fixing 3 cm of one end of the HA fiber to an upper surface of a flat plate.

[0063] (c) Measuring an angle 0 between an upper-surface extension line B of the flat plate and an extension line T of the other end of the HA fiber.

TABLE-US-00001 TABLE 1 Percentage of Water Content in Hyaluronate Fiber Bending Angle (wt %) (°) 95 90 50 80 25 10 20 8 10 3 5 2 0 0

[0064] From Table 1 above, when the water content in the hyaluronate fiber is 50 wt % or more, the bending angle was 80° or more. Thus, it is determined that this does not support cells and does not maintain its shape when injected into the human body, so that the fiber will not properly perform its function.

[0065] Furthermore, when the percentage of water content in the hyaluronate fiber is less than 5 wt %, it can be seen that the fiber maintains its shape but is hardened and inflexible, so that the fiber is easily broken.

[0066] In contrast, when the percentage of water content in the hyaluronate fiber ranges from 5 to 25 wt %, it can be seen that the bending angle is 2 to 10°, so that this is a suitable type of hyaluronate fiber during a procedure.

TEST EXAMPLE 3

Tensile-Strength Measurement of Hyaluronate Fiber

[0067] The tensile strength of the hyaluronate fiber manufactured in Example 2 was measured, and the measured results are shown in Table 2. The tensile strength was measured using a universal testing machine with a sample having the length of 5cm being mounted on a test jig and a crosshead speed being set to 2 mm/min.

TABLE-US-00002 TABLE 2 Percentage of Water Content In Hyaluronate Fiber Tensile Strength (wt %) (kg/mm.sup.2) 95 Not Measurable 50 0.27 30 2.83 25 3.24 20 5.29 10 10.53 5 13.38 0 Not Measurable

[0068] From Table 2 above, when the water content in the hyaluronate fiber is 50 wt % or more, it is determined that the tensile strength is rapidly reduced, is easily broken, and has no elasticity, so that the fiber cannot properly perform its function.

[0069] Furthermore, when the percentage of water content in the hyaluronate fiber is 5 wt % or less, the fiber maintains its shape but is hardened and easily broken, so that the tensile strength cannot be measured.

[0070] In contrast, when the percentage of water content in the hyaluronate fiber ranges from 5 to 25 wt %, it can be seen that the tensile strength ranges from 3.24 to 13.38 kg/mm.sup.2, and thereby this is the hyaluronate fiber that has the shape and function of a thread.

TEST EXAMPLE 4

Check of Crack Amount of Hyaluronate Fiber

[0071] An image of a surface of the hyaluronate fiber manufactured in each of Example 2 and Comparative Examples 3 and 4 was captured by a microscope (magnification: 200×). After the image of the surface of the hyaluronate fiber was captured through the microscope, an image was processed by the image processing software “Photoshop” (Adobe Systems Inc.), an image analysis software “Scion Image” (Scion Corporation) was used, and a crack amount was quantified. The results are shown in Table 3 and FIGS. 2 to 4.

TABLE-US-00003 TABLE 3 Crack Hyaluronate fiber Amount Note A Example 2: Water Content in  3-10% — Hyaluronate Fiber 10 wt % B Example 2: Water Content in  2-7% FIG. 2 Hyaluronate Fiber 20 wt % C Example 2: Water Content in  1-5% — Hyaluronate Fiber 50 wt % D Comparative Example 3: Water Content in 20-30% FIG. 3 Hyaluronate Fiber 10 wt % E Comparative Example 4: Water Content in 25-35% FIG. 4 Hyaluronate Fiber 10 wt %

[0072] From Table 3 above and FIGS. 2 to 4, in the case of A, B, and C in which the water content of the hyaluronate paste ranges from 50 to 95 wt % and which is manufactured through the water equilibrium, it can be seen that the crack amount is reduced in reverse proportion to the water content of the finished hyaluronate fiber.

[0073] In contrast, in the case of both D which is manufactured through the water equilibrium using the hyaluronate paste having the water content of 5 to 40 wt %, and E which is manufactured without the water equilibrium, it can be seen that the crack amount is increased.

[0074] For reference, in FIGS. 2 to 4, a total hyaluronic-fiber image capturing area was indicated by a blue line (rectangle), and cracks such as pores (grooves) or linear gaps were indicated by a red line (circle).

[0075] Although specific embodiments of the present disclosure have been disclosed in detail as described above, it is obvious to those skilled in the art that such description is merely of preferable exemplary embodiments and is not construed to limit the scope of the present disclosure. Therefore, the substantial scope of the present disclosure will be defined by the appended claims and equivalents thereof.

INDUSTRIAL APPLICABILITY

[0076] Since the hyaluronate fiber of the present disclosure has a smooth surface with a small crack, the hyaluronate fiber can be used for a surgical suture, a lifting thread, a filler for cosmetic surgery, a tissue-engineering scaffold, etc.