SYSTEMS, METHODS, AND MATERIALS FOR DETECTION AND REMOVAL OF HEAVY METALS FROM WATER

Abstract

Electrospun poly(acrylic) acid (PAA)/poly(vinyl) alcohol PVA nanofibers and integrated filtration membranes generated therefrom are disclosed herein. The membranes are suitable for use in selectively removing heavy metals such as lead and cadmium from water. The surface of the nanofibers is preferably functionalized with one or more chelating agents. The membranes have a high removal efficiency and adsorption capacity with well-distributed hid-density heavy metal adsorption sites with strong binding affinities for targeted heavy metals.

Claims

1. A membrane comprising nanofibers comprising: a. poly(acrylic) acid; and b. poly(vinyl) alcohol; wherein the membrane is generated by electrospinning of a polymer solution; wherein the membrane is functionalized with one or more chelating agents; and wherein the membrane is suitable for use in selectively removing heavy metals from water.

2. The membrane of claim 1, wherein the one or more cheating agents are selected from the group consisting of ethylenediamine and ethylenediaminetetraacetic acid.

3. The membrane of claim 2, wherein the one or more chelating agents include ethylenediamine.

4. The membrane of claim 2, wherein the one or more chelating agents include ethylenediaminetetraacetic acid.

5. The membrane of claim 1, wherein the poly(acrylic) acid and poly(vinyl) alcohol are crosslinked.

6. The membrane of claim 2, wherein the poly(acrylic) acid and poly(vinyl) alcohol are crosslinked.

7. The membrane of claim 1, wherein the one or more chelating agents are blended into the polymer solution during electrospinning.

8. The membrane of claim 2, wherein the one or more chelating agents are blended into the polymer solution during electrospinning.

9. The membrane of claim 1, wherein the one or more cheating agents are physically coated onto the surface of the nanofibers.

10. The membrane of claim 2, wherein the one or more chelating agents are physically coated onto the surface of the nanofibers.

11. The membrane of claim 1, wherein the membrane is capable of being regenerated after being used to remove heavy metals from water.

12. The membrane of claim 2, wherein the membrane is capable of being regenerated after being used to remove heavy metals from water.

13. A method of removing heavy moats from water comprising using the membrane of claim 1 to remove heavy metals from water.

Description

DETAILED DESCRIPTION

[0014] Electrospun poly(acrylic) acid (PAA)/poly(vinyl) alcohol PVA nanofibers and integrated filtration membranes generated therefrom are disclosed herein. The membranes are suitable for use in selectively removing heavy metals such as lead and cadmium from water. The membranes have a high removal efficiency and adsorption capacity with well-distributed high-density heavy metal adsorption sites with strong binding affinities for targeted heavy metals.

[0015] PAA is an effective material because it has abundant carboxyl groups, which provide a sufficient number of adsorption sites for heavy metals. The addition of PVA improves the water stability of the nanofibers, See Park, J.-C., el at. “Electrospun Poly(vinyl alcohol) Nanofibers: Effects of Degree of Hydrolysis and Enhanced Water Stability,” Polym, J. 2010, 42, 273-76. The PVA/PAA nanofibers have excellent water stability, mechanical properties, and water permeability.

[0016] In some embodiments, the water stability of the PVA/PAA nanofibers is achieved via crosslinking of PVA and PAA within the nanofibers.

[0017] The surface of the nanofibers may preferably be functionalized with one or more chelating agents. The chelating agent may be one or more chelating agents selected from the group consisting of ethylenediamine and ethylenediaminetetraacetic acid (EDTA).

[0018] The surface-functionalized nanofiber membranes preferably include a sufficient number of heavy metal bonding sites to rapidly remove heavy metals from water and reduce the concentration of targeted heavy metals in the treated water below designated limits. Membranes generated from the surface-functionalized nanofibers may preferably remove targeted heavy metals from 1-10 ppm in water to below limits prescribed by the U.S. Environmental Protection Agency (EPA) as of the filing date of the present application with an empty bed contact time (EBCT) of less than 5 minutes.

[0019] In some embodiments, the membrane may be regenerated after being used to remove heavy metals from water. Adsorbed heavy metals may be desorbed from the membrane using a suitable regeneration solution. The regeneration solution may include EDTA, as EDTA is known to be able to desorb heavy metals from chelation sites, See, e.g., Wang, Y. et al., supra; Peng, Y. et al. “A Versatile MOF-based Trap for Heavy Metal Ion Capture and Dispersion,” Nat. Commun. 2018, 9, 187. The regeneration solution may, for example, comprise aqueous EDTA and hydroxide. In some embodiments, the regeneration solution comprises 0.1 M EDTA-Na and 0.1 M NaOH.

[0020] Methods of using the disclosed membranes to remove heavy metals from water are also disclosed herein. The membranes may be used to remove lead, cadmium, or other heavy metals from water.

EXAMPLE

[0021] The following example is provided as a specific illustration. It should be understood, however, that the invention is not limited to the specific details set forth in the example. All parts and percentages in the example, as well as in the remainder of the disclosure, are by weight unless otherwise specified.

[0022] Further, any range of numbers recited above or in the paragraphs hereinafter describing or claiming various aspects of the invention, such as ranges that represent a particular set of properties, units of measure, conditions, physical states or percentages, is intended to literally incorporate expressly herein by reference or otherwise, any number falling within such range, including any subset of numbers or ranges subsumed within any range so recited. The term “about” when used as a modifier for or in conjunction with a variable, is intended to convey that the numbers and ranges disclosed herein may be flexible as understood by ordinarily skilled artisans and that practice of the disclosed invention by those skilled in the art using temperatures, concentrations, amounts, contents, carbon numbers, and properties that are outside of a literal range will achieve the desired result, namely, surface-functionalized PAA/PVA nanofiber materials and systems and methods for removal of heavy metals from water using integrated filtration membranes formed from said surface-functionalized PAA/PVA nanofiber materials.

Preparation of PAA/PVA Nanofibers

[0023] A PAA/PVA polymer solution is prepared by mixing three solutions (PAA: PVA: deionized water) to generate a mixed polymer solution of 10 wt % (5 wt % PAA, wt % PVA). The mixed polymer solution is stirred for 1 h to generate a homogeneous solution. Electrospun PAA/PVA nanofibers are then generated using an electrospinning apparatus. The applied voltage is 40 kV and the flow rate of the PAA/PVA solution is 22 mL/h. The nanofibrous membranes are deposited on a PET roll, which is rolling with a winding speed of 0.6 m/h. The electrospun nanofibrous membranes are then heat-treated at 145° C. for 30 min to impart water stability through crosslinking.

[0024] Chelating agents that enhance the affinity of heavy metals to the surface of the nanofibers are loaded during the electrospinning process by blending into the polymer solution or alternatively by physically coating the chelating agents on the surface of the nanofibers using vapor deposition such as chemical vapor deposition (CVD) or physical vapor deposition (PVD).

Analysis of Morphology, Water-Stability, Porosity and Water Permeability

[0025] The morphology of the surface and cross-section of nanofiber membranes is evaluated by scanning electron microscope (SEM). Specimens used for cross-sectional imaging are frozen and cracked in liquid nitrogen and then coated with gold. The fiber diameter is averaged by selecting 40 fibers in the SEM images. The variability in fiber diameter may be attributed to variability in the PAA content of the polymer solution. It is observed that increased PAA content results in increased average nanofiber diameter.

[0026] The porosity of crosslinked PVA/PAA nanofibers is calculated using Eq. 1:

[00001]$\begin{array}{cc}p=\left(1-\frac{\rho }{{\rho }_0}\right)\times 100& \left(1\right)\end{array}$

where ρ is the fiber density (mass/volume for regularly-shaped fiber membranes) and ρ.sub.a is the density of the PVA/PAA polymer mixture. ρ.sub.0 is calculated using Eq. 2.

[00002]$\begin{array}{cc}\frac{1}{{\rho }_0}=\frac{\mathrm{\omega 1}\%}{{\rho }_1}+\frac{\mathrm{\omega 2}\%}{{\rho }_2}& \left(2\right)\end{array}$

The thickness of all the nanofibers samples is approximately 30 μm. The densities of the pre-blended PVA and PAA polymers are calculated using a PVA polymer density of 1.25 g/m.sup.3 and a PAA polymer density of 1.44 g/m.sup.3, as provided in polymerdatabase.com. The porosity is found to decrease with increased fiber density. Water stability is evaluated by averaged swelling degree

[00003]$(S=\frac{W_s-W_d}{W_d},$

where W.sub.d and W.sub.s are the mass of fibers before and after immersing in deionized water for 48 h). The results obtained show a low averaged swelling degree, as compared to the averaged swelling degree of 9.69 for previously reported systems. See {circle around (C)}erná, M. et al., supra. The results show improved water stability after crosslinking for 2 h as compared to crosslinking for 0.5 h. In addition, the water flux does not change over 72 h continuous flow, which also demonstrates the stability of the membranes and their compatibility with water.

Evaluation of Heavy Metal Adsorption

[0027] Heavy metals removal efficiency is evaluated for surface-functionalized nanofibers by conducting batch adsorption studies. The concentration of the heavy metals is measured using inductively coupled plasma mass spectrometry (ICP-MS).

[0028] The previous description of the disclosed embodiments is provided to enable any person skilled in the art to make or use the invention disclosed herein. Although the various inventive aspects are disclosed in the context of one or more illustrated embodiments, implementations, and examples, it should be understood by those skilled in the art that the invention extends beyond the specifically disclosed embodiments to other alternative embodiments and or uses of the invention and obvious modifications and equivalents thereof. It should be also understood that the scope of this disclosure includes the various combinations or sub-combinations of the specific features and aspects of the embodiments disclosed herein, such that the various features, modes of implementation, and aspects of the disclosed subject matter may be combined with or substituted for one another. The generic principles defined herein may be applied to other embodiments without departing from the spirit or scope a the disclosure. Thus, the present disclosure is not intended to be limited to the embodiments shown herein but is to be accorded the widest scope consistent with the principles and novel features disclosed herein.

[0029] All references cited are hereby expressly incorporated herein by reference.