PROCESS FOR PREPARING POLYIMIDES

Abstract

The invention relates to a stoichiometric salt of a tetracarboxylic acid and a diamine of the following general formula (I),

##STR00001##

wherein R.sub.1 is selected from tetravalent residues of butane, cyclobutane, cyclopentane, cyclohexane, tetrahydrofurane and benzophenone and R.sub.2 is selected from divalent residues of unbranched, branched or cyclic aliphatic hydrocarbons with 3 to 15 carbon atoms, with the proviso that the salt of the formula (I) is water-soluble and is selected from compounds (1) to (28); and to the polyimides prepared from these salts by polycondensation.

Claims

1. A stoichiometric salt of a tetracarboxylic acid and a diamine of the following general formula (I): ##STR00012## wherein R.sub.1 is selected from tetravalent residues of butane, cyclobutane, cyclopentane, cyclohexane, tetrahydrofuran and benzophenone and R.sub.2 is selected from divalent residues of straight, branched or cyclic aliphatic hydrocarbons having from 3 to 15 carbon atoms, wherein i) the salt of formula (I) is water-soluble; and ii) it is selected from the following compounds: a) Salts of tetrahydrofuran-2,3,4,5-tetracarboxylic acid with aliphatic diamines Propane-1,3 -diammonium-dihydrogen-tetrahydrofuran-2,3,4,5 -tetracarboxylate (1), Butane-1,4-diammonium-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (2), Pentane-1,5-diammonium-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (3), 2,2-Dimethylpropane-1,3-diammonium-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (4), Hexane-1,6-diammonium-dihydrogen-tetrahydrofuran-2,3,4,5 -tetracarboxylate (5), 2-Methylpentane-1,5-diammonium-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (6), Heptane-1,7-diammonium-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (7), Octane-1,8-diammonium-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (8), Nonane-1,9-diammonium-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (9); b) Salts of tetrahydrofuran-2,3,4,5-tetracarboxylic acid with alicyclic diamines Cyclohexane-1,2-diammonium-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (10), Cyclohexane-1,3 -diammonium-dihydrogen-tetrahydrofuran-2,3,4,5 -tetracarboxylate (11), Cyclohexane-1,4-diammonium-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (12), Cyclohexane-1,3-bis(methanammonium)-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (13), Cyclohexane-1,4-bis(methanammonium)-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (14), Norbornane bis(methylammonium)-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (15), Isophorone diammonium-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (16), Tricyclo[5.2.1.0.sup.2,6]decane-3(4),8(9)-bis(methanammonium)-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (17), 4,4′-Methylene-bis(2-methylcyclohexylammonium)-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (18); c) Salts of 1,2,3,4-butanetetracarboxylic acid with alicyclic diamines Norbornane bis(methylammonium)-dihydrogen-1,2,3,4-butanetetracarboxylate (19), Tricyclo[5.2.1.0.sup.2,6]decane-3(4),8(9)-bis(methanammonium)-dihydrogen-1,2,3,4-butanetetracarboxylate (20); d) Salts of 1,2,3,4-cyclobutanetetracarboxylic acid with alicyclic diamines Norbornane bis(methylammonium)-dihydrogen-1,2,3,4-cyclobutanetetracarboxylate (21), Tricyclo[5.2.1.0.sup.2,6]decane-3(4),8(9)-bis(methanammonium)-dihydrogen-1,2,3,4-cyclobutanetetracarboxylate (22); e) Salts of 1,2,3,4-cyclopentanetetracarboxylic acid with alicyclic diamines Norbornane bis(methylammonium)-dihydrogen-1,2,3,4-cyclopentanetetracarboxylate (23), Tricyclo[5.2.1.0.sup.2,6]decane-3(4),8(9)-bis(methanammonium)-dihydrogen-1,2,3,4-cyclopentanetetracarboxylate (24); f) Salts of 1,2,4,5-cyclohexanetetracarboxylic acid with alicyclic diamines Norbornane bis(methylammonium)-dihydrogen-1,2,4,5-cyclohexanetetracarboxylate (25), Tricyclo[5.2.1.0.sup.2,6]decane-3(4),8(9)-bis(methanammonium)-dihydrogen-1,2,4,5-cyclohexane tetracarboxylate (26); and g) Salts of 3,3′,4,4′-benzophenonetetracarboxylic acid with alicyclic diamines Norbornane bis(methylammonium)-dihydrogen-3,3′,4,4′-benzophenone-tetracarboxylate (27), Tricyclo[5.2.1.0.sup.2,6]decane-3 (4), 8(9)-bis(methanammonium)-dihydrogen-3,3′,4,4′benzophenone tetracarboxylate (28).

2. The salt of formula (I) according to claim 1, wherein the salt is selected from compounds (2), (3) and (5) to (9) above; or the salt is selected from the above compounds (10) to (28), wherein the residue R.sub.2 of the alicyclic diammonium ion is a mixture of multiple isomers in each case.

3. A process for preparing the salt of formula (I) according to claim 1 by mixing the respective tetracarboxylic acid or dianhydride thereof with the respective diamine in a solvent and then isolating the stoichiometric salt thereby formed, wherein the tetracarboxylic acid or dianhydride thereof is dissolved, optionally under heating, in an organic solvent that is a solvent for both reactants but a non-solvent for the salt, followed by addition of the diamine and stirring of the reaction mixture to form the stoichiometric salt, which subsequently precipitates out of the solution and is isolated, wherein optionally an aliphatic diamine having a chain length of 4 to 9 carbon atoms is added; or an alicyclic diamine in the form of a mixture of multiple isomers is added.

4. The process according to claim 3, wherein a protic polar solvent, preferably isopropanol, is used.

5. A method of preparing polyimides comprising using the salt of formula (I) according to claim 1.

6. The method according to claim 5, wherein a polyimide is prepared by subjecting an aqueous solution of the salt of formula (I) to a processing step and subsequent heating in order to bring about polycondensation and simultaneously evaporate the water.

7. The method according to claim 6, wherein the aqueous solution of the salt is formed into a desired shape or applied to a surface in the processing step prior to heating.

8. The method according to claim 7, wherein the aqueous solution of the salt is formed into a desired shape by foaming, with a foaming agent and/or a foam stabilizer being optionally added to the aqueous solution of the salt prior to foaming.

9. The method according to claim 8, wherein at least one fatty acid dialkanolamide is added as a foam stabilizer.

10. A polyimide of general formula (II) prepared using a salt of formula (I): ##STR00013## wherein R.sub.1 and R.sub.2 are as previously defined and n is ≥2, wherein the polyimide is selected from the following: a) polyimides from tetrahydrofuran-2,3,4,5-tetracarboxylic acid and aliphatic diamines poly(N,N′-(1,3-propylene)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (101), poly(N,N′-(1,4-butylene)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (102), poly(N,N′-(1,5-pentylene)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (103), poly(N,N′-(2,2-dimethyl-1,3-propylene)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (104), poly(N,N′-(1,6-hexylene)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (105), poly(N,N′-(2-methyl-1,5-pentylene)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (106), poly(N,N′-(1,7-heptylene)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (107), poly(N,N′-(1,8-octylene)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (108), poly(N,N′-(1,9-nonylene)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (109); b) polyimides from tetrahydrofuran-2,3,4,5-tetracarboxylic acid and alicyclic diamines poly(N,N′-(1,2-cyclohexylene)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (110), poly(N,N′-(1,3-cyclohexylene)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (111), poly(N,N′-(1,4-cyclohexylene)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (112), poly(N,N′-(cyclohexane-1,3 -dimethylene)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (113), poly(N,N′-(cyclohexane-1,4-dimethylene)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (114), poly(N,N′-(norbornane dimethylene)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (115), poly(N,N′-(isophorylene)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (116), poly(N,N′-(tricyclo[5.2.1.0.sup.2,6]decane-3(4), 8(9)-dimethylene)tetrahydrofuran-2,3,4,5 -tetracarboxylic acid diimide) (117), poly(N,N′-(4,4′-methylene-bis(2-methylcyclohexyl)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (118); c) polyimides from 1,2,3,4-butanetetracarboxylic acid and alicyclic diamines poly(N,N′-(norbornane dimethylene)butane-1,2,3,4-tetracarboxylic acid diimide) (119), poly(N,N′-(tricyclo[5.2.1.0.sup.2,6]decane-3(4),8(9)-dimethylene)butane-1,2,3,4-tetracarboxylic acid diimide) (120); d) polyimides from 1,2,3,4-cyclobutanetetracarboxylic acid and alicyclic diamines poly(N,N′-(norbornane dimethylene)cyclobutane-1,2,3,4-tetracarboxylic acid diimide) (121), poly(N,N′-(tricyclo[5.2.1.0.sup.2,6]decane-3(4),8(9)-dimethylene)cyclobutane-1,2,3,4-tetracarboxylic acid diimide) (122); e) polyimides from 1,2,3,4-cyclopentanetetracarboxylic acid and alicyclic diamines poly(N,N′-(norbornane dimethylene)cyclopentane-1,2,3,4-tetracarboxylic acid diimide) (123), poly(N,N′-(tricyclo[5.2.1.0.sup.2,6]decane-3(4),8(9)-dimethylene)cyclopentane-1,2,3,4-tetracarboxylic acid diimide) (124); f) polyimides from 1,2,4,5-cyclohexanetetracarboxylic acid and alicyclic diamines poly(N,N′-(norbornane dimethylene)cyclohexane-1,2,4,5-tetracarboxylic acid diimide) (125), poly(N,N′-(tricyclo[5.2.1.0.sup.2,6]decane-3(4),8(9)-dimethylene)cyclohexane-1,2,4,5-tetracarboxylic acid diimide) (126); and g) polyimides from 3,3′,4,4′-benzophenonetetracarboxylic acid and alicyclic diamines poly(N,N′-(norbornane dimethylene)-3,3′,4,4′-benzophenone tetracarboxylic acid diimide) (127), poly(N,N′-(tricyclo[5.2.1.0.sup.2,6]decane-3(4),8(9)-dimethylene)-3,3′,4,4′-benzophenonetetracarboxylic acid diimide) (128).

Description

DISCLOSURE OF THE INVENTION

[0008] The present invention achieves this object in a first aspect by providing a stoichiometric salt of a tetracarboxylic acid and a diamine of the following general formula (I):

##STR00004##

wherein R.sub.1 is selected from tetravalent residues of butane, cyclobutane, cyclopentane, cyclohexane, tetrahydrofuran and benzophenone and R.sub.2 is selected from divalent residues of straight, branched or cyclic aliphatic hydrocarbons having from 3 to 15 carbon atoms, the stoichiometric salt of formula (I) being characterized in that
i) it is water-soluble; and
ii) it is selected from the following compounds:

a) Salts of tetrahydrofuran-2,3,4,5-tetracarboxylic acid with aliphatic diamines

[0009] Propane-1,3-diammonium-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (1), [0010] Butane-1,4-diammonium-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (2), [0011] Pentane-1,5-diammonium-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (3), [0012] 2,2-Dimethylpropane-1,3-diammonium-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (4), [0013] Hexane-1,6-diammonium-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (5), [0014] 2-Methylpentane-1,5-diammonium-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (6), [0015] Heptane-1,7-diammonium-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (7), [0016] Octane-1,8-diammonium-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (8), [0017] Nonane-1,9-diammonium-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (9);

b) Salts of tetrahydrofuran-2,3,4,5-tetracarboxylic acid with alicyclic diamines

[0018] Cyclohexane-1,2-diammonium-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (10), [0019] Cyclohexane-1,3-diammonium-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (11) [0020] Cyclohexane-1,4-diammonium-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (12), [0021] Cyclohexane-1,3-bis(methanammonium)-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (13), [0022] Cyclohexane-1,4-bis(methanammonium)-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (14), [0023] Norbornane bis(methylammonium)-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (15), [0024] Isophorone diammonium-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (16), [0025] Tricyclo[5.2.1.0.sup.2,6]decane-3(4),8(9)-bis(methanammonium)-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (17), [0026] 4,4′-Methylene-bis(2-methylcyclohexylammonium)-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (18);

c) Salts of 1,2,3,4-butanetetracarboxylic acid with alicyclic diamines

[0027] Norbornane bis(methylammonium)-dihydrogen-1,2,3,4-butanetetracarboxylate (19), [0028] Tricyclo[5.2.1.0.sup.2,6]decane-3(4),8(9)-bis(methanammonium)-dihydrogen-1,2,3,4-butanetetracarboxylate (20);

d) Salts of 1,2,3,4-cyclobutanetetracarboxylic acid with alicyclic diamines

[0029] Norbornane bis(methylammonium)-dihydrogen-1,2,3,4-cyclobutanetetracarboxylate (21), [0030] Tricyclo[5.2.1.0.sup.2,6]decane-3(4),8(9)-bis(methanammonium)-dihydrogen-1,2,3,4-cyclobutanetetracarboxylate (22);

e) Salts of 1,2,3,4-cyclopentanetetracarboxylic acid with alicyclic diamines

[0031] Norbornane bis(methylammonium)-dihydrogen-1,2,3,4-cyclopentanetetracarboxylate (23), [0032] Tricyclo[5.2.1.0.sup.2,6]decane-3(4),8(9)-bis(methanammonium)-dihydrogen-1,2,3,4-cyclopentanetetracarboxylate (24);

f) Salts of 1,2,4,5-cyclohexanetetracarboxylic acid with alicyclic diamines

[0033] Norbornane bis(methylammonium)-dihydrogen-1,2,4,5-cyclohexanetetracarboxylate (25), [0034] Tricyclo[5.2.1.0.sup.2,6]decane-3(4),8(9)-bis(methanammonium)-dihydrogen-1,2,4,5-cyclohexanetetracarboxylate (26); and

g) Salts of 3,3′,4,4′-benzophenonetetracarboxylic acid with alicyclic diamines

[0035] Norbornane bis(methylammonium)-dihydrogen-3,3′,4,4′-benzophenone-tetracarboxylate (27), [0036] Tricyclo[5.2.1.0.sup.2,6]decane-3(4),8(9)-bis(methanammonium)-dihydrogen-3,3′,4,4′-benzophenonetetracarboxylate (28).

[0037] All of these stoichiometric salts (1) to (28) of formula (I) have hitherto never been described in the literature and have not been suggested as possible combinations of a tetra-carboxylic acid and a diamine, and they are all readily soluble in water.

[0038] The average person skilled in the art may be of the opinion that, against the background of the prior art cited at the outset, in which numerous tetracarboxylic acid/diamine salt combinations are disclosed as water-soluble, it would have been obvious to prepare salts from other combinations and to examine them for their water solubility. In the course of their research, however, the inventors of the subject matter of the present application also prepared numerous combinations from among those disclosed as water-soluble in JP 2000/319389 A and found that the majority of the combinations of the diamines and tetracarboxylic acids listed there should not be water-soluble. More precisely, all of the salts that were tested using at least one aromatic reactant were not water-soluble—not even the salt from benzophenonetetracarboxylic acid and p-xylylenediamine, even though the one with m-xylylenediamine, which is the only one that is actually prepared and tested in JP 2000/319389 A, is indeed water-soluble and forms the basis for the Japanese patent applications cited above, which was extremely surprising. In addition, however, some salts of non-aromatic diamines or tetracarboxylic acids listed in JP 2000/319389 A were also insoluble in water, as is specifically demonstrated in the comparative examples that will follow. As a result, it can be assumed that, of the more than 700 possible combinations resulting from the acids and amines listed in JP 2000/319389 A, more than 600 are actually not water-soluble. The fact that the vast majority of these would turn out to be water-soluble when other combinations were investigated was therefore extremely surprising for the inventors of the subject matter of the present application and was in no way predictable.

[0039] In preferred embodiments of the invention, the salt of formula (I) is selected for the reasons set out below from either the above compounds (2), (3), and (5) to (9) or from the above compounds (10) to (28), in which the residue R.sub.2 of the alicyclic diammonium ion is present in each case as a mixture of multiple isomers.

[0040] These selections are based, on the one hand, on the surprising discovery that, among the salts from tetrahydrofuran-2,3,4,5-tetracarboxylic acid with aliphatic diamines, good film-forming properties were found in the preparation of surface coatings with an aqueous solution of the salts only starting from a diamine chain length of 4 carbon atoms—i.e., 1,4-diaminobutane in compound (2). In contrast, with aqueous solutions of the salt from tetrahydrofuran-2,3,4,5-tetracarboxylic acid with 1,3-diaminopropane, i.e., compound (1), and that with 2,2-dimethyl diaminopropane, i.e., compound (4), as well as the salt previously prepared by the inventors with ethylenediamine (see AT 519.038 A1), each exhibited strong foaming, which led to the formation of bubbles when they were used for surface coatings.

[0041] Furthermore, it was surprisingly found that, if the aliphatic diamine has a chain length of greater than 10 carbon atoms, it was no longer possible to obtain water-soluble salts—regardless of which tetracarboxylic acid was used.

[0042] And, on the other hand, of the compounds (10) to (28), all of which are salts of alicyclic diamines with various acids, including benzophenonetetracarboxylic acid, those salts in which the alicyclics exist as mixtures of multiple stereoisomers are preferable, as mentioned above. This is based on another surprising discovery by the inventors, namely that when isomer mixtures are present, the salts have better solubility than when using alicyclic diamines, of which only one stereoisomer exists. This was evident above all because, among the two diamines 4,4′-methylene-bis(cyclohexylamine) and the dimethyl derivative thereof, 4,4′-methylene-bis(2-methylcyclohexylamine), in combination with three different tetracarboxylic acids (aromatic, alicyclic, aliphatic), only the methylated derivative yielded a water-soluble salt, but not the unmethylated diamine, in all three cases. However, since this is diametrically opposed to the water solubility of the two diamines, the presence of stereoisomers apparently improves the water solubility of the stoichiometric salts.

[0043] All of this is explained and documented in more detail in the examples and comparative examples that will follow.

[0044] In a second aspect, the present invention also provides a process for preparing a salt of formula (I) according to the first aspect by mixing the respective tetracarboxylic acid or dianhydride thereof with the respective diamine in a solvent and then isolating the stoichiometric salt thereby formed , the process being characterized in that [0045] the tetracarboxylic acid or dianhydride thereof is dissolved, optionally under heating, in an organic solvent that is a solvent for both reactants but a non-solvent for the salt, followed by addition of the diamine and stirring of the reaction mixture to form the stoichiometric salt, which subsequently precipitates out of the solution and is isolated, wherein, optionally, namely in preferred embodiments, [0046] an aliphatic diamine having a chain length of 4 to 9 carbon atoms is added; or [0047] an alicyclic diamine in the form of a mixture of multiple isomers is added.

[0048] In contrast to the process disclosed in AT 519.038 A1, according to the present invention the tetracarboxylic acid and the diamine are not combined directly in water as a solvent for salt formation, but in an organic solvent that is capable of dissolving both reactants but not the salt thereof. This has the advantage that the salt formed in this manner precipitates out of the solution, while at least the majority of possible impurities remain in solution.

[0049] Polar solvents, especially protic polar solvents, are preferred as the solvent for this purpose, and isopropanol is particularly used since it is easy to evaporate from the precipitated salt.

[0050] In a third aspect, the present invention also provides the use of the salts of formula (I) according to the first aspect for the preparation of polyimides, for which purpose polyimides are prepared in preferred embodiments by subjecting an aqueous solution of the salt of formula (I) to a processing step and subsequent heating it in order to bring about polycondensation and simultaneously evaporate the water. This offers the advantage that no organic solvent escapes into the environment during processing and subsequent polycondensation.

[0051] In the processing step, the aqueous solution of the salt is preferably either formed into a desired shape or applied to a surface prior to heating. In preferred embodiments, the aqueous solution is formed into the desired shape by foaming, it being possible to add a foaming agent and/or a foam stabilizer prior to foaming as needed, for which purpose one or more fatty acid dialkanolamides can be added, for example.

[0052] And in a final aspect, the present invention also relates to polyimide of the general formula (II) that is prepared using a salt of formula (I):

##STR00005##

wherein R.sub.1 and R.sub.2 are as previously defined and n is ≥2, the resulting polyimide being characterized in that it is selected from the following:

a) polyimides from tetrahydrofuran-2,3,4,5-tetracarboxylic acid and aliphatic diamines

[0053] poly(N,N′-(1,3-propylene)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (101), [0054] poly(N,N′-(1,4-butylene)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (102), [0055] poly(N,N′-(1,5-pentylene)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (103), [0056] poly(N,N′-(2,2-dimethyl-1,3-propylene)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (104), [0057] poly(N,N′-(1,6-hexylene)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (105), [0058] poly(N,N′-(2-methyl-1,5-pentylene)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (106), [0059] poly(N,N′-(1,7-heptylene)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (107), [0060] poly(N,N′-(1,8-octylene)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (108), [0061] poly(N,N′-(1,9-nonylene)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (109);

b) polyimides from tetrahydrofuran-2,3,4,5-tetracarboxylic acid and alicyclic diamines

[0062] poly(N,N′-(1,2-cyclohexylene)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (110), [0063] poly(N,N′-(1,3-cyclohexylene)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (111), [0064] poly(N,N′-(1,4-cyclohexylene)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (112), [0065] poly(N,N′-(cyclohexane-1,3-dimethylene)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (113), [0066] poly(N,N′-(cyclohexane-1,4-dimethylene)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (114), [0067] poly(N,N′-(norbornane dimethylene)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (115), [0068] poly(N,N′-(isophorylene)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (116), [0069] poly(N,N′-(tricyclo[5.2.1.0.sup.2,6]decane-3(4),8(9)-dimethylene)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (117), [0070] poly(N,N′-(4,4′-methylene-bis(2-methylcyclohexyl)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (118);

c) polyimides from 1,2,3,4-butanetetracarboxylic acid and alicyclic diamines

[0071] poly(N,N′-(norbornane dimethylene)butane-1,2,3,4-tetracarboxylic acid diimide) (119), [0072] poly(N,N′-(tricyclo[5.2.1.0.sup.2,6]decane-3(4),8(9)-dimethylene)butane-1,2,3,4-tetracarboxylic acid diimide) (120);

d) polyimides from 1,2,3,4-cyclobutanetetracarboxylic acid and alicyclic diamines

[0073] poly(N,N′-(norbornane dimethylene)cyclobutane-1,2,3,4-tetracarboxylic acid diimide) (121), [0074] poly(N,N′-(tricyclo[5.2.1.0.sup.2,6]decane-3(4),8(9)-dimethylene)cyclobutane-1,2,3,4-tetracarboxylic acid diimide) (122);

e) polyimides from 1,2,3,4-cyclopentanetetracarboxylic acid and alicyclic diamines

[0075] poly(N,N′-(norbornane dimethylene)cyclopentane-1,2,3,4-tetracarboxylic acid diimide) (123), [0076] poly(N,N′-(tricyclo[5.2.1.0.sup.2,6]decane-3(4),8(9)-dimethylene)cyclopentane-1, 2,3,4-tetracarboxylic acid diimide) (124);

f) polyimides from 1,2,4,5-cyclohexanetetracarboxylic acid and alicyclic diamines

[0077] poly(N,N′-(norbornane dimethylene)cyclohexane-1,2,4,5-tetracarboxylic acid diimide) (125), [0078] poly(N,N′-(tricyclo[5.2.1.0.sup.2,6]decane-3(4),8(9)-dimethylene)cyclohexane-1,2,4,5-tetracarboxylic acid diimide) (126); and

g) polyimides from 3,3′,4,4′-benzophenonetetracarboxylic acid and alicyclic diamines

[0079] poly(N,N′-(norbornane dimethylene)-3,3′,4,4′-benzophenonetetracarboxylic acid diimide) (127), [0080] poly(N,N′-(tricyclo[5.2.1.0.sup.2,6]decane-3(4),8(9)-dimethylene)-3,3′,4,4′-benzophenone-tetracarboxylic acid diimide) (128).

[0081] Like the stoichiometric monomer salts of formula (I) used for their preparation, these polyimides are all novel, can be prepared from aqueous solutions of the salts in a simple, inexpensive, and environmentally friendly manner, and have advantageous properties, such as high flexibility on the part of coatings made of them.

EXAMPLES

[0082] The present invention will be described in greater detail below on the basis of concrete exemplary embodiments and comparative examples.

[0083] All reagents were purchased from commercial sources and used without further purification. IR spectra were obtained by means of FT-IR ATRR spectroscopy on a Tensor 27, and .sup.1H and .sup.13C-NMR spectra were recorded on an Avance 250 or DRX-400 FT spectrometer operating at 250 or 400 MHz, all from Bruker. TGA measurements were made using a Perkin Elmer TGA 8000 Thermogravimetric Analyzer, and a Hettich ROTANTA 460R centrifuge was used to centrifuge the monomer salt suspensions.

Synthesis 1

General Protocol for Preparing the Monomer Salts of Formula (I)

[0084] ##STR00006##

[0085] In a 50 ml round bottom flask fitted with a reflux condenser, around 0.7 mmol of the respective tetracarboxylic acid R.sub.1(COOH).sub.4 was mixed with 50 ml of isopropanol and stirred magnetically, optionally under heating to no more than 80° C., until a clear solution formed, which was allowed to cool. An equimolar amount of the respective diamine H.sub.2N—R.sub.2—NH.sub.2 was then added all at once at room temperature in solid form or, in the case of liquid diamines, using a micropipette, and the mixture was stirred under standard conditions for several hours. The resulting suspension of the precipitated stoichiometric salt was centrifuged for several minutes at 11,500 rpm, decanted, washed again with isopropanol, and again centrifuged at 11,500 rpm for several minutes, after which the liquid phase was decanted and the solid salt was dried under high vacuum to constant weight. The yields achieved were consistently quantitative.

Synthesis 2

[0086] General Protocol for Preparing the Polyimides of Formula (II)

##STR00007##

[0087] Consistently clear solutions of about 40% by weight were prepared of the respective monomer salt of formula (I) in 1 ml distilled water in a glass beaker. These solutions were applied using a Pasteur pipette to glass or aluminum surfaces, which were placed in a programmable oven at 50° C. and then subjected to a temperature program from 50° C. to 250° C. over 38-62 h in order to evaporate the water and to ensure complete polycondensation to the polyimide of formula (II). After the specimens had cooled, the resulting polyimide films were peeled off the surfaces and analyzed by FT-IRR-ATR and TGA.

Comparative Examples 1 to 107 and Examples 1 to 28

Preparation and Examination of Stoichiometric Salts of Formula (I)

[0088] Stoichiometric salts of formula (I) were prepared as described above under “Synthesis 1” and then tested for solubility by mixing 1 ml of distilled water with around 20 to 40% by weight of the respective salt and stirring for 15 minutes. Those salts with which no clear solution without appreciable amounts of precipitate as a sediment were obtained were referred to as being “insoluble in water.”

[0089] The following tetracarboxylic acids were used for this purpose:

##STR00008##

[0090] The diamines used were i) the following aliphatic diamines:

##STR00009##

as well as ii) the following alicyclic diamines:

##STR00010##

and iii) the following aromatic diamines:

##STR00011##

[0091] The results of the solubility tests obtained for the examples (B1 to B28) and comparative examples (C1 to C107) are summarized in the tables overleaf.

TABLE-US-00001 TABLE 1 Salts of tetrahydrofuran-2,3,4,5-tetracarboxylic acid Salt can be Compound Salt is water- derived from the Example Diamine no. soluble prior art Aliphatic diamines B1 Propane-1,3-diamine 1 yes no B2 Butane-1,4-diamine 2 yes no B3 Pentane-1,5-diamine 3 yes no B4 2,2-Dimethylpropane-1,3-diamine 4 yes no B5 Hexane-1,6-diamine 5 yes no B6 2-Methylpentane-1,5-diamine 6 yes no B7 Heptane-1,7-diamine 7 yes no B8 Octane-1,8-diamine 8 yes no B9 Nonane-1,9-diamine 9 yes no V1 Dodecane-1,12-diamine — no no Alicyclic diamines no B10 Cyclohexane-1,2-diamine 10 yes no B11 Cyclohexane-1,3-diamine 11 yes no B12 Cyclohexane-1,4-diamine 12 yes no B13 1,3-Cyclohexyl-bis(methylamine) 13 yes no B14 1,4-Cyclohexyl-bis(methylamine) 14 yes no B15 Norbornane bis(methylamine) 15 yes no B16 Isophorone diamine 16 yes no B17 Tricyclo[5.2.1.0.sup.2,6]decane-3(4),8(9)- 17 yes no bis(methylamine) V2 4,4′-Methylene-bis(cyclohexylamine) — no no B18 4,4′-Methylene-bis(2-methylcyclohexylamine) 18 yes no Aromatic diamines V3 m-Phenylenediamine — no no V4 p-Phenylenediamine — no no V5 m-Xylylenediamine — yes yes V6 p-Xylylenediamine — no no V7 2,4-Tolylenediamine — no no V8 2,6-Tolylenediamine — no no V9 Pyridine-2,6-diamine — no no V10 1,2,4-Triazole-3,5-diamine — no no V11 4,4′-Methylene-bis(phenylamine) — no no V12 3,3′-Dimethylbiphenyl-4,4′-diamine — no no

TABLE-US-00002 TABLE 2 Salts of 1,2,3,4-butanetetracarboxylic acid Salt can be Compound Salt is water- derived from the Example Diamine no. soluble prior art Aliphatic diamines V13 Propane-1,3-diamine — yes yes V14 Butane-1,4-diamine — yes yes V15 Pentane-1,5-diamine — yes yes V16 2,2-Dimethylpropane-1,3-diamine — yes yes V17 Hexane-1,6-diamine — yes yes V18 2-Methylpentane-1,5-diamine — yes yes V19 Heptane-1,7-diamine — yes yes V20 Octane-1,8-diamine — yes yes V21 Nonane-1,9-diamine — yes yes V22 Dodecane-1, 12-diamine no yes Alicyclic diamines yes V23 Cyclohexane-1,2-diamine — yes yes V24 Cyclohexane-1,3-diamine — yes yes V25 Cyclohexane-1,4-diamine — yes yes V26 1,3-Cyclohexyl-bis(methylamine) — yes yes V27 1,4-Cyclohexyl-bis(methylamine) — yes yes B19 Norbornane bis(methylamine) 15 yes no V28 Isophorone diamine 16 yes yes B20 Tricyclo[5.2.1.02.6]decane-3(4),8(9)- 17 yes no bis(methylamine) V29 4,4′-Methylene-bis(cyclohexylamine) — no yes V30 4,4′-Methylene-bis(2-methylcyclohexylamine) 18 yes yes Aromatic diamines V31 m-Phenylenediamine — no yes V32 p-Phenylenediamine — no yes V33 m-Xylylenediamine — yes yes V34 p-Xylylenediamine — no yes V35 2,4-Tolylenediamine — no yes V36 2,6-Tolylenediamine — no yes V37 Pyridine-2,6-diamine — no no V38 1,2,4-Triazole-3,5-diamine — no no V39 4,4′-Methylene-bis(phenylamine) — no yes V40 3,3′-Dimethylbiphenyl-4,4′-diamine — no yes

TABLE-US-00003 TABLE 3 Salts of 1,2,3,4-cyclobutanetetracarboxylic acid Salt can be Compound Salt is water- derived from the Example Diamine no. soluble prior art Aliphatic diamines V41 Propane-1,3-diamine — yes yes V42 Butane-1,4-diamine — yes yes V43 Pentane-1,5-diamine — yes yes V44 Hexane-1,6-diamine — yes yes V45 2-Methylpentane-1,5-diamine — yes yes V46 Heptane-1,7-diamine — yes yes V47 Octane-1,8-diamine — yes yes V48 Nonane-1,9-diamine — yes yes Alicyclic diamines — yes yes V49 Cyclohexane-1,2-diamine yes yes V50 Cyclohexane-1,3-diamine yes V51 Cyclohexane-1,4-diamine — yes yes V52 1,3-Cyclohexyl-bis(methylamine) — yes yes V53 1,4-Cyclohexyl-bis(methylamine) — yes yes B21 Norbornane bis(methylamine) 21 yes no V54 Isophorone diamine — yes yes B22 Tricyclo[5.2.1.0.sup.2.6]decane-3(4),8(9)- 22 yes no bis(methylamine) Aromatic diamines V55 m-Xylylenediamine — yes yes

TABLE-US-00004 TABLE 4 Salts of 1,2,3,4-cyclopentanetetracarboxylic acid Salt can be Compound Salt is water- derived from the Example Diamine no. soluble prior art Aliphatic diamines V56 Propane-1,3-diamine — yes yes V57 Butane-1,4-diamine — yes yes V58 Pentane-1,5-diamine — yes yes V59 Hexane-1,6-diamine — yes yes V60 2-Methylpentane-1,5-diamine — yes yes V61 Heptane-1,7-diamine — yes yes V62 Octane-1,8-diamine — yes yes V63 Nonane-1,9-diamine — yes yes Alicyclic diamines V64 Cyclohexane-1,2-diamine — yes yes V65 Cyclohexane-1,3-diamine — yes yes V66 Cyclohexane-1,4-diamine — yes yes V67 1,3-Cyclohexyl-bis(methylamine) — yes yes V58 1,4-Cyclohexyl-bis(methylamine) — yes yes B23 Norbornane bis(methylamine) 23 yes no V69 Isophorone diamine — yes yes B24 Tricyclo[5.2.1.0.sup.2,6]decane-3(4),8(9)- 24 yes no bis(methylamine) Aromatic diamines V70 m-Xylylenediamine — yes yes

TABLE-US-00005 TABLE 5 Salts of 1,2,4,5-cyclohexanetetracarboxylic acid Salt can be Compound Salt is water- derived from the Example Diamine no. soluble prior art Aliphatic diamines V71 Propane-1,3-diamine — yes yes V72 Butane-1,4-diamine — yes yes V73 Pentane-1,5-diamine — yes yes V74 Hexane-1,6-diamine — yes yes V75 2-Methylpentane-1,5-diamine — yes yes V76 Heptane-1,7-diamine — yes yes V77 Octane-1,8-diamine — yes yes V78 Nonane-1,9-diamine — yes yes Alicyclic diamines V79 Cyclohexane-1,2-diamine — yes yes V80 Cyclohexane-1,3-diamine — yes yes V81 Cyclohexane-1,4-diamine — yes yes V82 1,3-Cyclohexyl-bis(methylamine) — yes yes V83 1,4-Cyclohexyl-bis(methylamine) — yes yes B25 Norbornane bis(methylamine) 25 yes no V84 Isophorone diamine — yes yes B26 Tricyclo[5.2.1.0.sup.2.6]decane-3(4),8(9)- 26 yes no bis(methylamine) Aromatic diamines V85 m-Xylylenediamine — yes yes

TABLE-US-00006 TABLE 6 Salts of 3,3′,4,4′-benzophenonetetracarboxylic acid Salt can be Compound Salt is water- derived from the Example Diamine no. soluble prior art Aliphatic diamines V86 Butane-1,4-diamine — no yes V87 Pentane-1,5-diamine — no yes V88 2,2-Dimethylpropane-1,3-diamine — yes yes V8 Hexane-1,6-diamine — no yes V90 2-Methylpentane-1,5-diamine — no yes V91 Heptane-1,7-diamine — no yes V92 Octane-1,8-diamine — no yes V93 Nonane-1,9-diamine — no yes V94 Dodecane-1,12-diamine no yes Alicyclic diamines yes B27 Norbornane bis(methylamine) 27 yes no V95 Isophorone diamine — yes yes B28 Tricyclo[5.2.1.0.sup.2.6]decane-3(4),8(9)- 28 yes no bis(methylamine) V96 4,4′-Methylene-bis(cyclohexylamine) — no yes V97 4,4′-Methylene-bis(2-methylcyclohexylamine) — yes yes Aromatic diamines V98 m-Phenylenediamine — no yes V99 p-Phenylenediamine — no yes V100 m-Xylylenediamine — yes yes V101 p-Xylylenediamine — no yes V102 2,4-Tolylenediamine — no yes V103 2,6-Tolylenediamine — no yes V104 Pyridine-2,6-diamine — no no V105 1,2,4-Triazole-3,5-diamine — no no V106 4,4′-Methylene-bis(phenylamine) — no yes V107 3,3′-Dimethylbiphenyl-4,4′-diamine — no yes

[0092] A closer examination of the results in the above tables reveals that, of the 107 salts of the comparative examples, only 40 were not soluble in water, while 67 were, and that, of 107 salts, only 15 cannot be derived from the two lists disclosed in JP 2000/319389 A, while 91 can. It therefore seems, at first glance, that the majority of the salts that can be derived from the prior art—although by far not all—appear to be in fact soluble in water. However, this first impression is misleading for the following reasons.

[0093] After initially obtaining identical findings for the salts of tetrahydrofuran- and butanetetracarboxylic acid—namely that, of the aliphatic and alicyclic diamines used, only one was water-insoluble, particularly that with dodecane-1,12-diamine or 4,4′-methylene-bis(cyclohexylamine), and conversely, only the respective salt with the aromatic diamine m-xylylenediamine was water-soluble, while all of the others with aromatic diamines were not—it has been heretofore neglected to produce salts with other aromatic diamines for the three cycloaliphatic tetracarboxylic acids (of cyclobutane, -pentane and -hexane) in order to test their water solubility.

[0094] For these three acids, it was only confirmed that their salts with m-xylylenediamine also dissolve in water, as was already known from the prior art for the other three acids —including for the salt with benzophenonetetracarboxylic acid, which is the basis for the disclosures of the three Japanese patent applications cited above. On the other hand, a person skilled in the art can assume with some certainty that the three cycloaliphatic tetracarboxylic acids, in combination with the other aromatic diamines, also will not result in water-soluble salts, which is currently the subject of experiments being conducted by the inventors. This would result in another 27 salts that are not soluble in water but can be derived from JP 2000/319389 A, which would even out the above ratio between soluble and insoluble salts at 67:67.

[0095] What is more, JP 2000/319389 A lists a total of 61 aromatic and 26 non-aromatic diamines and 8 aromatic and 4 non-aromatic tetracarboxylic acids. Under the assumption based on the above results that the vast majority of the 628 derivable salts with at least one aromatic component are insoluble in water and the majority of the 104 derivable salts without an aromatic component are indeed water-soluble, all of the combinations that can be derived from JP 2000/319389 A end up with a ratio of soluble to insoluble salts of around 1:6.

[0096] This assumption is also supported by the fact that even the two aromatic diamines not disclosed in the prior art for the preparation of stoichiometric salts and used by the inventors for the first time for this purpose—i.e., diaminopyridine (pyridine-2,6-diamine) and diaminotriazole (1,2,4-triazole-3,5-diamine), which are relatively readily water-soluble diamines—did not produce a water-soluble salt with any of the three tetracarboxylic acids tested.

[0097] Even more surprising, however, was the behavior of some salts, which have opposite solubilities despite having strong structural similarities.

[0098] It is first and foremost a comparison between m-xylylenediamine and p-xylylenediamine that is striking, with the former consistently yielding water-soluble salts, whereas the latter did not form a water-soluble salt in any combination with tetracarboxylic acids—even though both diamines are liquids that are readily miscible with water. Judging from the above findings of the inventors, both they themselves in their earlier work and the inventors of the abovementioned Japanese applications happened to select an aromatic diamine—m-xylylenediamine—for their investigations that yields a water-soluble stoichiometric salt with various tetracarboxylic acids even though this was not the case for all of the other aromatic diamines that were tested.

[0099] Similarly surprising was the behavior of the salts prepared from the two diamines 4,4′-methylene-bis(cyclohexylamine) and the dimethyl derivative thereof, 4,4′-methylene-bis(2-methylcyclohexylamine), in combination with three different tetracarboxylic acids (aromatic, alicyclic, aliphatic). In all three cases, only the methylated derivative yielded a water-soluble salt, while the unmethylated diamine did not. This is of course in contrast to the water solubility of the diamines, for which about 4 g/l are cited in “Wikipedia” for 4,4′-methylene-bis(cyclohexylamine), while it is only around 88 mg/l for the dimethylated derivative 4,4′-methylene-bis(2-methylcyclohexylamine) (according to http://www.perflavory.com/docs/doc1195061.html), which is less by a factor of 45. Without wishing to be bound by any particular theory, the inventors conclude from this that the presence of stereoisomerism improves the water solubility of the stoichiometric salts, since it increases the likelihood of a molecule hydrating in an aqueous environment. In the case of the above dimethyl derivative, cis-trans isomers exist on both cyclohexyl rings, while the non-methylated diamine does not.

[0100] Consequently, in preparing water-soluble stoichiometric salts, it is preferable to select tetracarboxylic acids and/or diamines of which multiple stereoisomers exist and to use such mixtures of isomers rather than the pure isomers for salt formation, and more preferably both a mixture of isomers of the acid and one of the diamine. Of course, this applies not only, but above all, to alicyclic compounds.

[0101] For this reason, the inventors selected norbornane bis(methylamine) and tricyclo-[5.2.1.0.sup.2,6]decane-3(4),8(9)-bis(methylamine) as novel diamines that are not described in the literature for the preparation of such stoichiometric salts and of which multiple stereoisomers exist and which are also commercially available as isomer mixtures and do not have to be specially synthesized.

[0102] Consequently, of the compounds (10) to (28), i.e., the inventive salts of alicyclic diamines with various acids, including benzophenonetetracarboxylic acid, those salts in which the alicyclics are present as mixtures of multiple stereoisomers are preferred.

[0103] Under the circumstances described above, however, it is clear to those skilled in the art that, for any new combination of diamine and tetracarboxylic acid, it cannot be predicted whether the stoichiometric salt formed therefrom will be water-soluble or not, since the solubility obviously does not or does not only depend on whether or how well the acid and the amine are each soluble in water alone.

[0104] Moreover, in producing surface coatings using an aqueous solution of the stoichiometric monomer salts, better film-forming properties were observed when using the salts of tetrahydrofuran-2,3,4,5-tetracarboxylic acid with aliphatic diamines, i.e., compounds (1) to (9), starting at a diamine chain length of 4 carbon atoms, i.e., from 1,4-diaminobutane in compound (2). Pronounced foaming occurred with aqueous solutions of the salts of tetrahydrofuran-2,3,4,5-tetracarboxylic acid with 1,3-diaminopropane—i.e., compound (1)—and with 2,2-dimethyl diaminopropane—i.e., compound (4)—as well as with the salt that had already been prepared previously by the inventors (see AT 519.038 A1) with ethylenediamine, which led to the formation of bubbles when they were used for surface coating. It is for this reason that, as salts of formula (I) with aliphatic diamines, those with a linear chain length of the diamine residue R.sub.2 having at least 4 carbon atoms—i.e., compounds (2), (3), and (5) to (9)—are preferred according to the invention if they are to be used to produce polyimide films.

[0105] Even though, as will readily be understood, the use of the novel monomer salts of formula (I) according to the invention is not limited to the production of polyimide films, this still represents a preferred embodiment of their possible uses. As an alternative thereto, however, these can also be processed into polyimides in any other manner, for example by molding or foaming and subsequent heating in order to bring about polycondensation thereof. During foaming, foaming agents and/or foam stabilizers can be added as needed, for which purpose one or more fatty acid dialkanolamides can be used, for example. However, only polyimides that are formed by surface coating and subsequent heating will be described hereinafter.

[0106] The novel compounds (1) to (28) prepared according to “Synthesis 1” were characterized as previously described. The data are presented below, where “Tp” represents the polymerization temperature and “Td” represents the decomposition temperature of the monomer salts, each determined by means of TGA with a heating rate of 10 K/min.

Example 1

Propane-1,3-diammonium-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (1)

[0107] Tp.: 172° C.; Td.: -

[0108] IR (cm.sup.−1): 2969, 2826, 1721, 1561.

[0109] .sup.1H-NMR (250 MHz, D.sub.2O) δ: 4.82 (dd, J=3.8, 1.7 Hz, 2H), 3,47 (dd, J=3.8, 1.7 Hz, 2H), 3.10 (m, 4H), 2.07 (m, 2H).

[0110] .sup.13C-NMR (100 MHz, D.sub.2O) δ: 177.91, 175.76, 81.52, 52.28, 36.54, 24.79.

Example 2

Butane-1,4-diammonium-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (2)

[0111] Tp.: 149 C.; Td.: 394° C.

[0112] IR (cm.sup.−1): 2941, 2933, 1720, 1568.

[0113] .sup.1H-NMR (250 MHz, D.sub.2O) δ: 4,83 (dd, J=3,8, 1,6 Hz, 2H), 3,51 (dd, J=3,8, 1,6 Hz, 2H), 3,03 (t, J=7,3 Hz, 4H), 1.74 (t, J=7.3 Hz, 4H).

[0114] .sup.13C-NMR (100 MHz, D.sub.2O) δ: 178.11, 176.08, 81.63, 52.62, 38.79, 23.84.

Example 3

Pentane-1,5-diammonium-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (3)

[0115] Tp.: 149° C.; Td.: 396° C.

[0116] IR (cm.sup.−1): 2937, 2873, 1720, 1568.

[0117] .sup.1H-NMR (250 MHz, D.sub.2O) δ: 4.82 (dd, J=3.8, 1.5 Hz, 2H), 3.47 (dd, J=3.8, 1.5 Hz, 2H), 3.00 (m, 4H), 1.69 (m, 4H), 1.46 (m, 2H).

[0118] .sup.13C-NMR (100 MHz, D.sub.2O) δ: 177.92, 175.59, 81.56, 52.28, 39.12, 26.21, 22.63.

Example 4

2,2-Dimethylpropane-1,3-diammonium-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (4)

[0119] Tp.: 148° C.; Td.: -

[0120] IR (cm.sup.−1): 2969, 2899, 1719, 1571.

[0121] .sup.1H-NMR (250 MHz, D.sub.2O) δ: 4.81 (m, 2H), 3.45 (dd, J=4.0, 1.6 Hz, 2H), 3.01 (s, 4H), 1.14 (s, 6H).

[0122] .sup.13C-NMR (100 MHz, D.sub.2O) δ: 177.93, 175.81, 81.51, 52.33, 46.65, 32.31, 21.29.

Example 5

Hexane-1,6-diammonium-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (5)

[0123] Tp.: 156° C.; Td.: 444° C.

[0124] IR (cm.sup.−1): 2934, 2864, 1716, 1568.

[0125] .sup.1H-NMR (250 MHz, D.sub.2O) δ: 4.83 (m, 2H), 3.47 (dd, J=3.9, 1.5 Hz, 2H), 2.99 (m, 4H), 1.70 (m, 4H), 1.41 (m, 4H).

[0126] .sup.13C-NMR (100 MHz, D.sub.2O) δ: 177.77, 175.24, 81.49, 52.00, 39.31, 26.46, 25.07.

Example 6

2-Methylpentane-1,5-diammonium-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (6) Tp.: 142° C.; Td.: 441° C.

[0127] IR (cm.sup.−1): 2965, 2934, 1720, 1568.

[0128] .sup.1H-NMR (400 MHz, D.sub.2O) δ: 4.83 (dd, J=3.9, 1.5 Hz, 2H), 3.50 (dd, J=3.9, 1.5 Hz, 2H), 3.0 (m, 3H), 2.82 (m, 1H), 1.86 (m, 1H), 1.70 (m, 2H), 1.47 (m, 1H), 1.29 (m, 1 H), 1.00 (d, J=6.8 Hz, 3H).

[0129] .sup.13C-NMR (100 MHz, D.sub.2O) δ: 177.75, 175.24, 81.48, 51.99, 44.76, 39.37, 30.66, 29.92, 23.67, 15.79.

Example 7

Heptane-1,7-diammonium-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (7)

[0130] Tp.: 151° C.; Td.: 442° C.

[0131] IR (cm.sup.−1): 2932, 2861, 1722, 1572.

[0132] .sup.1H-NMR (250 MHz, D.sub.2O) δ: 4.84 (m, 2H), 3.50 (dd, J=3.9, 1.5 Hz, 2H), 2.98 (t, J=7.6 Hz, 4H), 1.65 (m, 4H), 1.37 (m, 6H).

[0133] .sup.13C-NMR (100 MHz, D.sub.2O) δ: 177.69, 175.13, 81.45, 51.92, 39.41, 27.63, 26.56, 25.32.

Example 8

Octane-1,8-diammonium-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (8)

[0134] Tp.: 145° C.; Td.: 444° C.

[0135] IR (cm.sup.−1): 2931, 2859, 1723, 1574.

[0136] .sup.1H-NMR (250 MHz, D.sub.2O) δ: 4.83 (m, 2H), 3.49 (dd, J=3.9, 1.5 Hz, 2H), 2.98 (t, J=7.5 Hz, 4H), 1.63 (m, 4H), 1.36 (m, 8H).

[0137] .sup.13C-NMR (100 MHz, D.sub.2O) δ: 177.80, 175.27, 81.51, 52.05, 39.46, 27.92, 26.64, 25.44.

Example 9

Nonane-1,9-diammonium-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (9)

[0138] Tp.: 147° C.; Td.: 444° C.

[0139] IR (cm.sup.−1): 2928, 2857, 1720, 1572.

[0140] .sup.1H-NMR (250 MHz, D.sub.2O) δ: 4.84 (dd, J=3.9, 1.5 Hz, 2H), 3.50 (dd, J=3.9, 1.5 Hz, 2H), 2.98 (t, J=7.5 Hz, 4H), 1.65 (m, 4H), 1.33 (m, 10H).

[0141] .sup.13C-NMR (100 MHz, D.sub.2O) δ: 177.77, 175.21, 81.50, 52.00, 39.48, 28.22, 28.05, 26.67, 25.50.

Example 10

Cyclohexane-1,2-diammonium-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (10)

[0142] Tp.: 172° C.; Td.: 378° C.

[0143] IR (cm.sup.−1): 2941, 2872, 1720, 1558.

[0144] C-NM (100 MHz, D.sub.2O) δ: 177.71, 175.60, 81.33, 52.07, 52.01, 49.77, 29.28, 25.69, 22.73, 20.15.

Beispiel 11

Cyclohexane-1,3-diammonium-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (11)

[0145] Tp.: 174° C.; Td.: 380° C.

[0146] IR (cm.sup.−1): 2969, 2876, 1721, 1573.

[0147] .sup.13C-NMR (100 MHz, D.sub.2O) δ: 177.74, 175.35, 81.45, 52.02, 48.09, 45.87, 33.92, 31.58, 28.65, 27.57, 23.68, 21.03, 17.56. [.sup.13C-NMR signals were determined by APT methods.]

Example 12

Cyclohexane-1,4-diammonium-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (12)

[0148] Tp.: 196° C.; Td.: 380° C.

[0149] IR (cm.sup.−1): 2938, 2874, 1717, 1566.

[0150] .sup.13C-NMR (100 MHz, D.sub.2O) δ: 178.34, 176.97, 81.80, 53.35, 48.42, 46.98, 27.98, 23.69.

Example 13

Cyclohexane-1,3-bis(methanammonium)-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (13)

[0151] Tp.: 152° C.; Td.: 451° C.

[0152] IR (cm.sup.−1): 2926, 2859, 1720, 1571.

[0153] .sup.13C-NMR (100 MHz, D.sub.2O) δ: 177.77, 175.31, 81.48, 52.06, 44.85, 42.81, 34.86, 32.96, 30.87, 30.45, 28.89, 27.62, 24.08, 19.20. [.sup.13C-NMR signals were determined by APT methods.]

Example 14

Cyclohexane-1,4-bis(methanammonium)-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (14)

[0154] Tp.: 153° C.; Td.: 454° C.

[0155] IR (cm.sup.−1): 2925, 2862, 1720, 1572.

[0156] .sup.13C-NMR (100 MHz, D.sub.2O) δ: 177.88, 175.48, 81.54, 52.21, 44.83, 42.56, 34.95, 32.89, 28.57, 23.67.

Example 15

Norbornane bis(methylammonium)-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (15)

[0157] Tp.: 160° C.; Td.: 426° C.

[0158] IR (cm.sup.−1): 2952, 2875, 1720, 1569.

Example 16

Isophorone diammonium-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (16)

[0159] Tp.: 163° C.; Td.: 389° C.

[0160] IR (cm.sup.−1): 2958, 2624, 1718, 1569.

[0161] .sup.13C-NMR (100 MHz, D.sub.2O) δ: 178.05, 175.94, 81.61, 52.74, 52.55, 45.19, 45.04, 42.32, 38.31, 33.78, 33.75, 30.83, 26.35, 21.59. [.sup.13C-NMR signals were determined by APT methods.]

Example 17

Tricyclo[5.2.1.0.SUP.2,6.]decane-3(4),8(9)-bis(methanammonium)-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (17)

[0162] Tp.: 151° C.; Td.: 433° C.

[0163] IR (cm.sup.−1): 2944, 2875, 1718, 1577.

Example 18

4,4′-Methylene-bis(2-methylcyclohexylammonium)-dihydrogen-tetrahydrofuran-2,3,4,5-tetracarboxylate (18)

[0164] Tp.: 170° C.; Td.: 409° C.

[0165] IR (cm.sup.−1): 2962, 2923, 1720, 1571.

Example 19

Norbornane bis(methylammonium)-dihydrogen-1,2,3,4-butanetetracarboxylate (19)

[0166] Tp.: 192° C.; Td.: 430° C.

[0167] IR (cm.sup.−1): 2949, 2871, 1621, 1548.

Example 20

Tricyclo[5.2.1.0.SUP.2,6.]decane-3(4),8(9)-bis(methanammonium)-dihydrogen-1,2,3,4-butane-tetracarboxylate (20)

[0168] Tp.: 163° C.; Td.: 369° C.

[0169] IR (cm.sup.−1): 2947, 2869, 1622, 1548.

[0170] .sup.13C-NMR (100 MHz, D.sub.2O) δ: 181.16, 180.09, 52.64, 47.81, 45.19, 45.01, 42.32, 38.70, 38.24, 33.75, 30.82, 27.51, 26.37, 25.96, 21.61. [.sup.13C-NMR signals were determined by APT methods.]

Example 21

Norbornane bis(methylammonium)-dihydrogen-1,2,3,4-cyclobutanetetracarboxylate (21)

[0171] IR (cm.sup.−1): 2947, 2869, 1718, 1548.

Example 22

Tricyclo[5.2.1.0.SUP.2,6.]decane-3(4),8(9)-bis(methanammonium)-dihydrogen-1,2,3,4-cyclobutanetetracarboxylate (22)

[0172] IR (cm.sup.−1): 2938, 2871, 1721, 1545.

Example 23

Norbornane bis(methylammonium)-dihydrogen-1,2,3,4-cyclopentanetetracarboxylate (23)

[0173] Tp.: 154° C.; Td.: 467° C.

[0174] IR (cm.sup.−1): 2948, 2871, 1687, 1560.

Example 24

Tricyclo[5.2.1.0.SUP.2,6.]decane-3(4),8(9)-bis(methanammonium)-dihydrogen-1,2,3,4-cyclopentanetetracarboxylate (24)

[0175] Tp.: 154° C.; Td.: 444° C. IR (cm.sup.−1): 2943, 2877, 1686, 1557.

Example 25

Norbornane bis(methylammonium)-dihydrogen-1,2,4,5-cyclohexanetetracarboxylate (25)

[0176] IR (cm.sup.−1): 2947, 2870, 1538.

Example 26

Tricyclo[5.2.1.0.SUP.2,6.]decane-3(4),8(9)-bis(methanammonium)-dihydrogen-1,2,4,5-cyclohexanetetracarboxylate (26)

[0177] Tp.: 168° C.; Td.: 458° C.

[0178] IR (cm.sup.−1): 2943, 2873, 1549.

Example 27

Norbornane bis(methylammonium)-dihydrogen-3,3′,4,4′-benzophenonetetracarboxylate (27)

[0179] IR (cm.sup.−1): 2947, 2871, 1720, 1556.

Example 28

Tricyclo[5.2.1.0.SUP.2,6.]decane-3(4),8(9)-bis(methanammonium)-dihydrogen-3,3′,4,4′-benzophenonetetracarboxylate (28)

[0180] Tp.: 183° C.; Td.: 455° C.

[0181] IR (cm.sup.−1): 2948, 2876, 1717, 1652, 1555.

Examples 29 to 56

Preparation of polyimides

[0182] As described in “Synthesis 2” above, films were prepared from the 28 novel stoichiometric salts of the present invention consisting of the following polyimides, which were characterized as previously described.

Example 29

Poly(N,N′-(1,3-propylene)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (101)

[0183] IR (cm.sup.−1): 2973, 2890, 1772, 1703, 1345.

Example 30

Poly(N,N′-(1,4-butylene)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (102)

[0184] Td.: 392° C.

[0185] IR (cm.sup.−1): 2941, 2871, 1770, 1690, 1353.

Example 31

Poly(N,N′-(1,5-pentylene)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (103)

[0186] Td.: 395° C.

[0187] IR (cm-1): 2940, 2864, 1780, 1748, 1686, 1336.

Example 32

Poly(N,N′-(2,2-dimethyl-1,3-propylene)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (104)

[0188] IR (cm.sup.−1): 2968, 2937, 1771, 1707, 1334.

Example 33

Poly(N,N′-(1,6-hexylene)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (105)

[0189] Td.: 419° C.

[0190] IR (cm.sup.−1): 2935, 2862, 1782, 1748, 1686, 1342.

Example 34

Poly(N,N′-(2-methyl-1,5-pentylene)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (106)

[0191] Td.: 405° C.

[0192] IR (cm.sup.−1): 2959, 2875, 1785, 1750, 1686, 1334.

Example 35

Poly(N,N′-(1,7-heptylene)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (107)

[0193] Td.: 410° C.

[0194] IR (cm.sup.−1): 2932, 2858, 1785, 1749, 1685, 1342.

Example 36

Poly(N,N′-(1,8-octylene)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (108)

[0195] Td.: 414° C.

[0196] IR (cm.sup.−1): 2929, 2855, 1781, 1746, 1685, 1344.

Example 37

Poly(N,N′-(1,9-nonylene)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (109)

[0197] Td.: 413° C.

[0198] IR (cm.sup.−1): 2929, 2857, 1782, 1749, 1686, 1340.

Example 38

Poly(N,N′-(1,2-cyclohexylene)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (110)

[0199] Td.: 378° C.

[0200] IR (cm.sup.−1): 2936, 2862, 1780, 1706, 1376.

Example 39

Poly(N,N′-(1,3-cyclohexylene)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (111)

[0201] Td.: 380° C.

[0202] IR (cm.sup.−1): 2938, 2865, 1778, 1701, 1365.

Example 40

Poly(N,N′-(1,4-cyclohexylene)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (112)

[0203] Td.: 380° C.

[0204] IR (cm.sup.−1): 2934, 2865, 1778, 1697, 1370.

Example 41

Poly(N,N′-(cyclohexane-1,3-dimethylene)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (113)

[0205] Td.: 438° C.

[0206] IR (cm.sup.−1): 2925, 2853, 1782, 1750, 1690, 1333.

Example 42

Poly(N,N′-(cyclohexane-1,4-dimethylene)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (114)

[0207] Td.: 415° C.

[0208] IR (cm.sup.−1): 2923, 2855, 1771, 1687, 1353.

Example 43

Poly(N,N′-(norbornane dimethylene)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (115)

[0209] Td.: 415° C.

[0210] IR (cm.sup.−1): 2948, 2872, 1781, 1747, 1691, 1334.

Example 44

Poly(N,N′-(isophorylene)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (116)

[0211] Td.: 388° C.

[0212] IR (cm.sup.−1): 2953, 2872, 1775, 1698, 1353.

Example 45

Poly(N,N′-(tricyclo[5.2.1.0.SUP.2,6.]decane-3(4),8(9)-dimethylene)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (117)

[0213] Td.: 437° C.

[0214] IR (cm.sup.−1): 2946, 2875, 1780, 1691, 1355.

Example 46

Poly(N,N′-(4,4′-methylene-bis(2-methylcyclohexyl)tetrahydrofuran-2,3,4,5-tetracarboxylic acid diimide) (118)

[0215] Td.: 380° C.

[0216] IR (cm.sup.−1): 2954, 2922, 1771, 1770, 1356.

Example 47

Poly(N,N′-(norbornane dimethylene)butane-1,2,3,4-tetracarboxylic acid diimide) (119)

[0217] Td.: 461° C.

[0218] IR (cm.sup.−1): 2941, 2866, 1773, 1692, 1340.

Example 48

Poly(N,N′-(tricyclo[5.2.1.0.SUP.2,6.]decane-3(4),8(9)-dimethylene)butane-1,2,3,4-tetracarboxylic acid diimide) (120)

[0219] Td.: 375° C.

[0220] IR (cm.sup.−1): 2952, 2874, 1776, 1695, 1365.

Example 49

Poly(N,N′-(norbornane dimethylene)cyclobutane-1,2,3,4-tetracarboxylic acid diimide) (121)

[0221] IR (cm.sup.−1): 2947, 2872, 1772, 1695, 1338.

Example 50

Poly(N,N′-(tricyclo[5.2.1.0.SUP.2,6.]decane-3(4),8(9)-dimethylene)cyclobutane-1,2,3,4-tetracarboxylic acid

[0222] diimide) (122)

[0223] IR (cm.sup.−1): 2942, 2874, 1771, 1697, 1338.

Example 51

Poly(N,N′-(norbornane dimethylene)cyclopentane-1,2,3,4-tetracarboxylic acid diimide) (123)

[0224] Td.: 444° C.

[0225] IR (cm.sup.−1): 2943, 2870, 1774, 1692, 1343.

Example 52

Poly(N,N′-(tricyclo[5.2.1.0.SUP.2,6.]decane-3(4),8(9)-dimethylene)cyclopentane-1,2,3,4-tetracarboxylic acid diimide) (124)

[0226] Td.: 444° C.

[0227] IR (cm.sup.−1): 2938, 2874, 1775, 1694, 1349.

Example 53

Poly(N,N′-(norbornane dimethylene)cyclohexane-1,2,4,5-tetracarboxylic acid diimide) (125)

[0228] IR (cm.sup.−1): 2945, 2871, 1771, 1694, 1340.

Example 54

Poly(N,N′-(tricyclo[5.2.1.0.SUP.2,6.]decane-3(4),8(9)-dimethylene)cyclohexane-1,2,4,5-tetracarboxylic acid diimide) (126)

[0229] Td.: 458° C.

[0230] IR (cm.sup.−1): 2936, 2871, 1771, 1693, 1342.

Example 55

Poly(N,N′-(norbornane dimethylene)-3,3′,4,4′-benzophenone tetracarboxylic acid diimide) (127)

[0231] IR (cm.sup.−1): 2946, 2871, 1772, 1702, 1341.

Example 56

Poly(N,N′-(tricyclo[5.2.1.0.SUP.2,6.]decane-3(4),8(9)-dimethylene)-3,3′,4,4′-benzophenone tetracarboxylic acid diimide) (128)

[0232] Td.: 455° C.

[0233] IR (cm.sup.−1): 2943, 2871, 1773, 1704, 1347.

[0234] The present invention thus provides a series of novel stoichiometric salts of a tetracarboxylic acid and a diamine which are all readily water-soluble and which are highly suitable for the preparation of polyimides, as is demonstrated by the provision of the corresponding polyimides.