AIRBAG BASE FABRIC, AND METHOD FOR MANUFACTURING AIRBAG BASE FABRIC

Abstract

Object:

Conventional woven fabrics mounted on a loom have a fabric length difference between the center portion and the sides of the woven fabric, which increases the flaring rate. In the scouring shrinkage step, yarns shrink and the crimp ratio is changed, which further increases flaring.

Means for achieving object:

The use of a bar temple with a ring function in the weaving process reduces protrusions. Further, by setting the boiling-water shrinkage rate of incorporated additional yarn lower than that of base yarn, the shrinkage of the sides of the fabric can be efficiently suppressed.

Claims

1. A fabric for airbags comprising unremoved fringe selvages at the sides of the fabric, wherein the fabric has a flaring rate of 1.5% or less, and a slope of change in the flaring rate of 0.1 or less.

2. The fabric for air bags according to claim 1, wherein the fabric has a difference between warp and weft density of 1.5 yarns/2.54 cm or less.

3. The fabric for airbags according to claim 1, wherein the warp crimp ratio of the sides of the fabric is 80% or more relative to the warp crimp ratio of the center portion of the fabric.

4. A method for producing the fabric for airbags according to claim 1, comprising performing weaving by using a bar temple device with a ring function, the bar temple device comprising a ring-shaped weft gripper portion on each side of an inner bar of the bar temple.

5. A method for producing the fabric for airbags according to claim 1, comprising: performing weaving by incorporating, at each side of the fabric, at least two additional yarns in which the boiling-water shrinkage rate of a base yarn is larger than the boiling-water shrinkage rate of the additional yarn, and the difference in the boiling-water shrinkage rate between the base yarn and the additional yarn is 0.8% or more, using a bar temple device with a ring function, the bar temple device comprising a ring-shaped weft gripper portion on each side of an inner bar of the bar temple, and then performing scouring shrinkage.

Description

BRIEF DESCRIPTION OF DRAWINGS

[0021] FIG. 1 shows a bar temple with a ring function.

[0022] FIG. 2 shows a method for measuring the flaring rate.

DESCRIPTION OF EMBODIMENTS

[0023] The fabric for airbags according to the present invention is a woven fabric formed from a synthetic-fiber multifilament. The synthetic-fiber multifilament that constitutes the fabric for airbags has a total fineness of preferably 200 dtex or more and 600 dtex or less, and more preferably 300 dtex or more and 550 dtex or less. A total fineness of 200 dtex or more, due to the elimination of the need for overly increasing the weaving density, reduces an excessive increase in binding force of the warp and weft, thus making it easier for the packageability in an airbag module to fall within an appropriate range. A total fineness of 600 dtex or less makes it easier to reduce an excessive increase in rigidity of the yarns that constitute the woven fabric. A synthetic-fiber multifilament having a total fineness within the range of 200 dtex or more and 600 dtex or less is preferable because such a synthetic-fiber multifilament makes it easier to obtain a fabric for airbags that is moderately flexible and thus excellent in packageability in a module.

[0024] In the present invention, the total fineness of synthetic-fiber multifilament that constitutes the fabric for airbags is determined as follows. The warp yarns and weft yarns of a fabric obtained through a dry-finishing step are each removed from the fabric, and measurement is performed in accordance with JIS L 1013 (2010) 8.3.1. Specifically, a sample with a length of 90 cm is accurately taken with an initial tension applied. The absolute dry mass is measured, and the fineness based on corrected weight (dtex) is calculated using the following formula. The average of five measurements is determined to be the total fineness.

F0=10000×m/0.9×(100+R0)/100

F0: Fineness based on corrected weight (dtex)
m: Absolute dry mass of sample (g)
R0: Official moisture content (%)

[0025] The fabric for airbags of the present invention is woven with base yarn (warp and weft that compose the fabric for airbags) and woven by further incorporating additional yarn having specific physical properties.

[0026] In order to suppress flaring due to the shrinkage at the sides of the fabric during scouring shrinkage, as well as drying, the difference in the boiling-water shrinkage rate between the base yarn and the additional yarn is preferably 0.8 to 20%, more preferably 1.5 to 15%, and particularly preferably 4 to 12%. A difference in the boiling-water shrinkage rate between the base yarn and the additional yarn of below 0.8% reduces the effect of suppressing deformation due to shrinkage, whereas a difference in the boiling-water shrinkage rate between the base yarn and the additional yarn exceeding 20% adversely affects strength, air permeability, etc. since the base yarn shrinks too much, thereby damaging the weave structure.

[0027] The boiling-water shrinkage rate of the base yarn is preferably larger than the boiling-water shrinkage rate of the additional yarn.

[0028] The boiling-water shrinkage rate of the base yarn and the additional yarn used in the fabric for airbags in the present invention may be such that base yarn>additional yarn, and it is effective that the difference between them is 0.83 or more. The additional yarn may be multifilament yarn, monofilament yarn, or yarn subjected to crimping such as false twisting. The material used can be nylon 66 fiber, nylon 6 fiber, polyester fiber, etc. Typically, nylon 66 fiber is often used as the base yarn for the fabric for airbags. Since polyester fiber has a boiling-water shrinkage rate lower than that of nylon 66 fiber, it is preferable to use nylon 66 fiber as the base yarn and polyester fiber as the additional yarn.

[0029] In the present invention, the boiling-water shrinkage rate of the original yarn is measured in accordance with boiling-water shrinkage rate method B prescribed in JIS L 1013 (2010). Specifically, the boiling-water shrinkage rate is measured as follows. An initial tension is applied to a sample, and two points 500 mm apart are marked. The initial tension is then removed, and the sample is immersed in hot water at 100° C. for 30 minutes. The sample is then taken out, and water is gently wiped away with blotting paper or a cloth. The sample is air-dried, and then initial tension is applied again. The length between the two points is measured, and the dimensional change rate due to boiling water (%) is calculated using the following formula. The average of three measurements is determined to be the boiling-water shrinkage rate. When a sample shrinks as in the present invention, the dimensional change rate due to boiling water (%) is a negative value, and the absolute value (%) is defined as the boiling water shrinkage rate (%) of the present invention.

Boiling-water shrinkage rate (%)=(L−500)/500×100

L: length between two points (mm)

[0030] The material of the synthetic-fiber multifilament that constitutes the fabric for airbags according to the present invention is not particularly limited, and can be selected from a wide range of materials. To meet the characteristics described above, while taking economic efficiency into account, the material is preferably a multifilament composed of a polyamide based-resin such as nylon 6, nylon 66, and nylon 46, or a multifilament composed of a polyester-based resin that contains mainly polyethylene terephthalate.

[0031] The synthetic-fiber multifilament that constitutes the fabric for airbags according to the present invention may contain various additives that are typically used for improving the productivity or characteristics in the production process for the original yarn or in the production process for the fabric. The synthetic-fiber multifilament that constitutes the fabric for airbags according to the present invention, for example, may contain at least one member selected from the group consisting of heat stabilizers, antioxidants, light stabilizers, lubricants, antistatic agents, plasticizers, thickening agents, pigments, and flame retardants.

[0032] The fabric for airbags of the present invention is weaved by adjusting an appropriate tension and the number of weft yarns to be incorporated, while incorporating a bar temple with a ring function into a loom and considering the weaving properties. As shown in FIG. 1, the bar temple with a ring function has a structure in which a ring function c is provided at both sides of an inner bar b in a bar temple cover a. The surface of the inner bar b is plain or threaded, and the needles in the ring function c are arranged in one or more rows in the width direction. Furthermore, the inner bar b and the ring function c are detachable and are integrated during weaving. The additional yarn is incorporated using a separate winding device or is wound onto a loom beam beforehand for weaving.

[0033] The diameter of the inner bar b is preferably 5 mm to 50 mm, and the surface is preferably plain or threaded (screw with a minimum of one thread and a maximum of three). The material can be selected from POM (polyacetal), PET (polyethylene terephthalate), and metals having high corrosion and rust resistance (brass, aluminum, etc.). Furthermore, the bar temple can be plated to reduce damage to the original yarn (for anti-fluffing).

[0034] The number of additional yarns of the fabric for airbags according to the present invention is not particularly limited; however, as the number increases, the effect is likely to increase. Considering ease of operation or the like, the number of additional yarns is preferably 2 to 12. However, since the operation properties and quality differ depending of production facility, the number of additional yarns is not limited as long as the operation properties and quality are not impaired.

[0035] The width of the fabric for airbags according to the present invention is not particularly limited; however, the greater the width, the more likely that flaring will occur. Fabric for airbags with a width of 160 cm or more is effective, and a width of 180 cm or more is particularly effective.

[0036] The flaring reduction technique of the present invention particularly effectively works for a high-density fabric. The fabric for airbags according to the present invention preferably has a cover factor of 1800 to 2600, and particularly preferably 2000 to 2500.

[0037] The CF was measured using the following formula:

CF=(A×0.9).sup.1/2×(W1)+(B×0.9).sup.1/2×(W2)

wherein A and B indicate the thickness (dtex) of warp and weft, and W1 and W2 indicate a warp weaving density and a weft weaving density (yarns/2.54 cm).

[0038] The structure of the woven fabric of the fabric for airbags according to the present invention can be a plain weave, a twill weave, a sateen weave, or a variation of these weaving patterns; however, the structure is not particularly limited.

[0039] By incorporating additional yarn having a difference in the boiling-water shrinkage rate from that of base yarn of 3% or more (base yarn>additional yarn) into the selvages of the fabric for airbags according to the present invention, the flaring rate of the fabric for airbags is reduced to 1.5% or less, and the slope of the change in the flaring rate is reduced to 0.1 or less. Further, the difference in warp and weft density can be reduced to 1.5 yarns/2.54 cm or less.

[0040] Furthermore, the fabric for airbags according to the present invention can be further coated, as necessary, with silicone resin or the like, which can improve low air permeability. Such a fabric can be effectively used as a fabric for coated airbags.

EXAMPLES

[0041] The structure and effect of the present invention are explained in detail using Examples.

Measurement of Flaring Rate

[0042] The flaring rate indicates the rate of the length of the sides of the fabric relative to the length of the center portion of the fabric.

[0043] A full-width woven fabric having a length of the center portion of 100 cm is prepared, and the woven fabric is cut along with the weft yarn located at the front and rear sides of the center portion of the woven fabric (100-cm portion) until both sides. Further, as shown in FIG. 2, the following samples are cut from a side.

A1: A sample with a width of 1 cm cut from the position 1 cm from one side.
A2: A sample with a width of 2 cm from the position 2 cm from one side.
A3: A sample with a width of 2 cm from the position 4 cm from one side.
A4: A sample with a width of 6 cm from the position 6 cm from one side.
A5: A sample with a width of 10 am from the position 12 cm from one side.
B1: A sample with a width of 1 cm from the position 1 cm from the other side.
B2: A sample with a width of 2 cm from the position 2 cm from the other side.
B3: A sample with a width of 2 cm from the position 4 cm from the other side.
B4: A sample with a width of 6 cm from the position 6 cm from the other side.
B5: A sample with a width of 10 cm from the position 12 cm from the other side.

[0044] After cutting, the length of the center portion of each cut sample is measured, and measurement results are substituted into the following formula. Because flaring of the fabric is present at both sides, F1 or F2, whichever value is higher, is taken as the flaring rate of the fabric for airbags. Similarly, X1 or X2, whichever value is higher, is taken as the slope of the change in the flaring rate.

Flaring rate F1=(A1−100)/100*100

Flaring rate F2=(B1−100)/100*100

[0045] F1 or F2, whichever value is higher, is the flaring rate of the fabric for airbags.

Slope of the change in the flaring rate X1=(A1−A5)/15.5

Slope of the change in the flaring rate X2=(B1−B5)/15.5

[0046] The distance between measurement positions of A1 and A5 samples is 15.5 cm.

[0047] X1 or X2, whichever value is higher, is the slope of the change in the flaring rate of the fabric for airbags.

Weaving Density of Fabric

[0048] The measurement was performed in accordance with JIS L 1096 (2010) 8.6.1. More specifically, a sample was placed on a flat table, and unnatural crimping and tension were removed. The number of warp yarns and weft yarns in a 2.54-cm section was counted and determined to be the density. The number of measurements was at least n=35 at 5-cm intervals from the base of the selvage, and both warp (longitudinal) and weft (latitudinal) densities were measured, and the difference therebetween was calculated at each measurement point.

Measurement of Crimp Ratio

[0049] The crimp ratio was measured in accordance with the method described in JIS L1096 (1999) 8.7.2B.

[0050] As a sample, 10 warp yarns were extracted from the center of the fabric and 10 base yarns at the endmost in the warp direction excluding the additional yarn were extracted from each of the left and right sides of the fabric, and the average values for both the center and side of the fabric were determined.

[0051] Thereafter, by substituting the crimp ratio of the center of the fabric, and the crimp ratio of the sides having a larger difference from the center of the fabric, the difference in the warp crimp ratio between the center and the sides of the fabric can be confirmed.

Difference in the warp crimp ratio between the center and sides of the fabric=the warp crimp ratio of the sides of the fabric/the warp crimp ratio of the center of the fabric×100

Example 1

[0052] Using a nylon 66 filament original yarn having a fineness of 470 dtex/144 f and a boiling-water shrinkage rate of 5.5% (the monofilament cross-section was round) in the weft and warp direction of the base yarn, weaving was performed in a plain weave pattern so that the weft and warp both had a weaving density of 49.0 yarns/2.54 cm, by incorporating two additional yarns having a boiling-water shrinkage rate of −1.3% with a water-jet loom equipped with a bar temple with a ring function (15-mm diameter, inner bar surface plane). Thereafter, the fabric was passed through a hot-water shrinkage tank at 98° C. without drying and then continuously passed through a dry-finishing process using a two-step suction drum dryer in which the first step was adjusted to have a temperature T1 of 130° C., and the second step was adjusted to have a temperature T2 of 135° C.

Example 2

[0053] Using a nylon 66 filament original yarn having a fineness of 470 dtex/144 f and a boiling-water shrinkage rate of 5.5% (the monofilament cross-section was round) in the weft and warp direction of the base yarn, weaving was performed in a plain weave pattern so that the weft and warp both had a weaving density of 49.0 yarns/2.54 cm, by incorporating two additional yarns having a boiling-water shrinkage rate of 4.5% with a water-jet loom equipped with a bar temple with a ring function (15-mm diameter, inner bar surface plane). Thereafter, the fabric was passed through a hot-water shrinkage tank at 98° C. without drying and then continuously passed through a dry-finishing process using a two-step suction drum dryer in which the first step was adjusted to have a temperature T1 of 130° C., and the second step was adjusted to have a temperature T2 of 135° C.

Example 3

[0054] Using a nylon 66 filament original yarn having a fineness of 470 dtex/144 f and a boiling-water shrinkage rate of 5.5% (the monofilament cross-section was round) in the weft and warp direction of the base yarn, weaving was performed in a plain weave pattern so that the weft and warp both had a weaving density of 53.0 yarns/2.54 cm, by incorporating two additional yarns having a boiling-water shrinkage rate of −1.3% with a water-jet loom equipped with a bar temple with a ring function (15-mm diameter, inner bar surface plane). Thereafter, the fabric was passed through a hot-water shrinkage tank at 98° C. without drying and then continuously passed through a dry-finishing process using a two-step suction drum dryer in which the first step was adjusted to have a temperature T1 of 130° C., and the second step was adjusted to have a temperature T2 of 135° C.

Example 4

[0055] Using a nylon 66 filament original yarn having a fineness of 470 dtex/144 f and a boiling-water shrinkage rate of 5.5% (the monofilament cross-section was round) in the weft and warp direction of the base yarn, weaving was performed in a plain weave pattern so that the weft and warp both had a weaving density of 53.0 yarns/2.54 cm, by incorporating two additional yarns having a boiling-water shrinkage rate of 4.5% with a water-jet loom equipped with a bar temple with a ring function (15-mm diameter, inner bar surface plane). Thereafter, the fabric was passed through a hot-water shrinkage tank at 98° C. without drying and then continuously passed through a dry-finishing process using a two-step suction drum dryer in which the first step was adjusted to have a temperature T1 of 130° C., and the second step was adjusted to have a temperature T2 of 135° C.

Example 5

[0056] Using a nylon 66 filament original yarn having a fineness of 470 dtex/144 f and a boiling-water shrinkage rate of 7.0% (the monofilament cross-section was round) in the weft and warp direction of the base yarn, weaving was performed in a plain weave pattern so that the weft and warp both had a weaving density of 53.0 yarns/2.54 cm, by incorporating two additional yarns having a boiling-water shrinkage rate of 7.0% with a water-jet loom equipped with a bar temple with a ring function (15-mm diameter, inner bar surface plane). Thereafter, the fabric was passed through a hot-water shrinkage tank at 98° C. without drying and then continuously passed through a dry-finishing process using a two-step suction drum dryer in which the first step was adjusted to have a temperature T1 of 130° C., and the second step was adjusted to have a temperature T2 of 135° C.

Comparative Example 1

[0057] Using a nylon 66 filament original yarn having a fineness of 470 dtex/144 f and a boiling-water shrinkage rate of 5.53 (the monofilament cross-section was round) in the weft and warp direction of the base yarn, weaving was performed in a plain weave pattern so that the weft and warp both had a weaving density of 53.0 yarns/2.54 cm, by incorporating two additional yarns having a boiling-water shrinkage rate of 5.0% with a water-jet loom equipped with a bar temple. Thereafter, the fabric was passed through a hot-water shrinkage tank at 98° C. without drying and then continuously passed through a dry-finishing process using a two-step suction drum dryer in which the first step was adjusted to have a temperature T1 of 130° C., and the second step was adjusted to have a temperature T2 of 135° C.

Comparative Example 2

[0058] Using a nylon 66 filament original yarn having a fineness of 470 dtex/144 f and a boiling-water shrinkage rate of 7.0% (the monofilament cross-section was round) in the weft and warp direction of the base yarn, weaving was performed in a plain weave pattern so that the weft and warp both had a weaving density of 53.0 yarns/2.54 cm, by incorporating two additional yarns having a boiling-water shrinkage rate of 7.0% with a water-jet loom equipped with a bar temple. Thereafter, the fabric was passed through a hot-water shrinkage tank at 98° C. without drying and then continuously passed through a dry-finishing process using a two-step suction drum dryer in which the first step was adjusted to have a temperature T1 of 130° C., and the second step was adjusted to have a temperature T2 of 135° C.

TABLE-US-00001 TABLE 1 Comparative Comparative Item Unit Example 1 Example 2 Example 3 Example 4 Example 5 Example 1 Example 2 Total fitness of original dtex 470 470 470 470 470 470 470 yarn Number of original yarns yarns 144 144 144 144 144 144 144 Loom — WJL WJL WJL WJL WJL WJL WJL Holding device Bar temple Bar temple Bar temple Bar temple Bar temple Bar temple Bar temple with a ring with a ring with a ring with a ring with a ring function function function function function Ring needle Two rows Two rows Two rows Two rows Two rows — — Inner bar diameter 15-mm dia. 15-mm dia. 15-mm dia. 15-mm dia. 15-mm dia. 9-mm dia. 9-mm dia. Material POM POM POM POM POM POM POM Surface Plane Plane Plane Plane Plane Double- Double- thread thread screw screw Number of additional yarns Yarns 2 2 2 2 2 2 2 (each side) Shrinkage rate of base yarn % 5.5 5.5 5.5 5.5 7.0 5.5 7.0 Boiling-water shrinkage % −1.3 4.5 −1.3 4.5 7.0 5.0 7.0 rate of additional yarn Difference in boiling-water % 6.8 1.0 6.8 1.0 0.0 0.5 0.0 shrinkage rate Weave design density Yarns/ Warp 49.0 49.0 53.0 53.0 53.0 53.0 53.0 2.54 cm Weft 49.0 49.0 53.0 53.0 53.0 53.0 53.0 Actual density at the side Yarns/ Warp 50.1 50.3 54.1 54.2 54.4 54.9 54.7 2.54 cm Weft 49.2 49.1 53.4 53.1 53.2 53.2 53.1 Flaring rate % 0.80 0.98 0.97 1.01 1.15 1.70 1.72 Slope of change in flaring — 0.04 0.07 0.05 0.08 0.09 0.12 0.13 rate Difference in density Yarns/2.54 cm 0.9 1.2 0.7 1.1 1.2 1.7 1.6 between warp and weft Warp crimp ratio Center of fabric 9.9 9.7 13.4 11.8 11.4 11.0 11.1 Side of fabric 8.1 7.9 11.9 10.1 9.5 8.1 8.5 Warp crimp ratio of the % 81.8 81.4 88.3 85.6 83.3 73.6 76.6 sides of fabric/warp crimp ratio of the center of fabric × 100

INDUSTRIAL APPLICABLE

[0059] According to the present invention, specifying the flaring rate can improve the quality of the fabric for airbags and contribute to reduction in costs in the airbag manufacturing industry.