PROCESS FOR PREPARING A POLYPROPYLENE COMPOSITION

Abstract

The invention relates to a process for producing a polypropylene composition by sequential polymerization the polypropylene composition having an improved balanced combination of high flowability, high stiffness and impact, and high level of optical properties.

Claims

1. A polypropylene composition obtainable by a sequential polymerization process comprising the steps: a) polymerizing in a first reactor monomers comprising propylene and optionally one or more comonomers selected from ethylene and C.sub.4-C.sub.10 alpha-olefins, to obtain a first propylene polymer fraction having a comonomer content in the range of 0.0 to 1.8 wt %, and a MFR.sub.2 in the range of from 15.0 to 40.0 g/10 min, as measured according to ISO 1133 at 230° C. under a load of 2.16 kg; b) polymerizing in a second reactor monomers comprising propylene and one or more comonomers selected from ethylene and C.sub.4-C.sub.10 alpha-olefins, in the presence of the first propylene polymer fraction, to obtain a second propylene polymer fraction having a comonomer content in the range of 2.0 to 12.0 wt %; c) extruding the second propylene polymer fraction in the presence of at least one alpha-nucleating agent; wherein the process is operated in the presence of a Ziegler-Natta catalyst with a transition metal of group 4 to 6 of the periodic table and the catalyst comprising an internal donor, wherein the internal donor is a non-phthalic internal donor; and wherein the non-phthalic internal donor is selected from (di)esters of non-phthalic carboxylic (di)acids wherein the (di)ester belongs to the group comprising malonates, maleates, citraconates, glutarates, cyclohexene-1,2-dicarboxylates, derivatives thereof, and mixtures thereof; wherein the polypropylene composition has: an MFR.sub.2 in the range of from 15.0 to 60.0 g/10 min, as measured according to ISO 1133 at 230° C. under a load of 2.16 kg, a comonomer content in the range of 2.0-12.0 wt %, a xylene soluble content (XCS) 5.6-15.0 wt %, as determined according to ISO 16152 at 25° C., and a haze value<17.0%, as measured according to ASTM D1003 on injection moulded plaques having 1 mm thickness produced as described in EN ISO 1873-2.

2. The polypropylene composition according to claim 1, wherein the polypropylene composition has an MFR.sub.2 in the range of from 15.0 to 40.0 g/10 min, as measured according to ISO 1133 at 230° C. under a load of 2.16 kg.

3. The polypropylene composition according to claim 1, wherein the polypropylene composition has a Comonomer ratio (CR) in the range of 5.0-50.0.

4. The polypropylene composition according to claim 1, wherein the polypropylene composition has a melting temperature T.sub.m>152° C.

5. The polypropylene composition according to claim 1, wherein the polypropylene composition has a melting temperature>152° C. and a crystallization temperature>120° C. as measured by DSC according to ISO 11357/3.

6. The polypropylene composition according to claim 1, wherein the polypropylene composition has a tensile modulus>750 MPa, as measured according to ISO 527-1:2012/ISO 527-2:2012 at 23° C. on injection moulded test specimens.

7. The polypropylene composition according to claim 1, wherein the polypropylene composition has a Charpy notched impact strength≥6.0 kJ/m.sup.2, as measured according to ISO 179/1eA at 23° C. on injection moulded test specimens.

8. The polypropylene composition according to claim 1, wherein the polypropylene composition has a xylene soluble fraction in the range of from 6.0 to 25.0 wt %, wherein said xylene soluble fraction has an ethylene content in the range of from 10.0 to 25.0 wt %, a crystalline fraction in the range of from 75.0 to 94.0 wt %, wherein said crystalline fraction has an ethylene content in the range of from 0.8 to 5.0 wt %, as determined according to CRYSTEX QC method, ISO 6427-B.

9. The polypropylene composition according to claim 1, wherein the catalyst further comprises a co-catalyst, an external donor, or a combination thereof.

10. An article comprising the polypropylene composition according to claim 1.

Description

BRIEF DESCRIPTION OF THE FIGURES

[0134] FIG. 1. Schematic diagram of the CRYSTEX QC instrument.

[0135] FIG. 2. Elution of the EP copolymer sample and obtained soluble and crystalline fractions in the TREF column (column filled with inert material e.g. glass beads) (see Del Hierro, P.; Ortin, A.; Monrabal, B.; ‘Soluble Fraction Analysis in polypropylene, The Column Advanstar Publications, February 2014. Pages 18-23)

EXAMPLES

I. Measuring Methods

[0136] a) Melt Flow Rate

[0137] The melt flow rate (MFR) is determined according to ISO 1133 and is indicated in g/10 min. The MFR is an indication of the flowability and hence the processability of the polymer. The higher the melt flow rate, the lower the viscosity of the polymer. The MFR.sub.2 of polypropylene is determined at a temperature of 230° C. and under a load of 2.16 kg.

[0138] b) DSC Analysis

[0139] The melting temperature and the crystallisation temperature are measured with a TA Instrument Q2000 differential scanning calorimetry device (DSC) according to ISO 11357/3 on 5 to 10 mg samples, under 50 mL/min of nitrogen atmosphere. Crystallisation and melting temperatures were obtained in a heat/cool/heat cycle with a scan rate of 10° C./min between 30° C. and 225° C. Crystallisation and melting temperatures were taken as the peaks of the endotherms and exotherms in the cooling step and the second heating step respectively.

[0140] c) Xylene Soluble Content (XCS, wt %)

[0141] The content of the polymer soluble in xylene is determined according to ISO 16152; 5.sup.th edition; 2005-07-01 at 25° C.

[0142] d) Tensile Modulus

[0143] Tensile Modulus is measured according to ISO 527-1:2012/ISO527-2:2012 at 23° C. and at a cross head speed=50 mm/min; using injection moulded test specimens as described in EN ISO 1873-2 (dog bone shape, 4 mm thickness).

[0144] e) Charpy Notched Impact

[0145] Charpy notched impact strength is determined according to ISO 179/1eA at 23° C. on injection moulded test specimens as described in EN ISO 1873-2 (80×10×4 mm).

[0146] f) Haze

[0147] Haze is determined according to ASTM D1003 on injection moulded plaques having 1 mm thickness and 60×60 mm.sup.2 area produced as described in EN ISO 1873-2.

[0148] g) Comonomer Content

Poly(propylene-co-ethylene)-ethylene Content by IR Spectroscopy

[0149] Quantitative infrared (IR) spectroscopy was used to quantify the ethylene content of the poly(ethylene-co-propene) copolymers through calibration to a primary method.

[0150] Calibration was facilitated through the use of a set of in-house non-commercial calibration standards of known ethylene contents determined by quantitative .sup.13C solution-state nuclear magnetic resonance (NMR) spectroscopy. The calibration procedure was undertaken in the conventional manner well documented in the literature. The calibration set consisted of 38 calibration standards with ethylene contents ranging 0.2-75.0 wt % produced at either pilot or full scale under a variety of conditions. The calibration set was selected to reflect the typical variety of copolymers encountered by the final quantitative IR spectroscopy method.

[0151] Quantitative IR spectra were recorded in the solid-state using a Bruker Vertex 70 FTIR spectrometer. Spectra were recorded on 25×25 mm square films of 300 um thickness prepared by compression moulding at 180-210° C. and 4-6 mPa. For samples with very high ethylene contents (>50 mol %) 100 um thick films were used. Standard transmission FTIR spectroscopy was employed using a spectral range of 5000-500 cm.sup.−1, an aperture of 6 mm, a spectral resolution of 2 cm.sup.−1, 16 background scans, 16 spectrum scans, an interferogram zero filling factor of 64 and Blackmann-Harris 3-term apodisation. Quantitative analysis was undertaken using the total area of the CH.sub.2 rocking deformations at 730 and 720 cm.sup.−1 (A.sub.Q) corresponding to (CH.sub.2).sub.>2 structural units (integration method G, limits 762 and 694 cm.sup.−1). The quantitative band was normalised to the area of the CH band at 4323 cm.sup.−1 (AR) corresponding to CH structural units (integration method G, limits 4650, 4007 cm.sup.−1). The ethylene content in units of weight percent was then predicted from the normalised absorption (A.sub.Q/A.sub.R) using a quadratic calibration curve. The calibration curve having previously been constructed by ordinary least squares (OLS) regression of the normalised absorptions and primary comonomer contents measured on the calibration set.

Poly(propylene-co-ethylene)-ethylene Content for Calibration Using .sup.13C NMR Spectroscopy

[0152] Quantitative .sup.13C{.sup.1H} NMR spectra were recorded in the solution-state using a Bruker Avance III 400 NMR spectrometer operating at 400.15 and 100.62 MHz for .sup.1H and .sup.13C respectively. All spectra were recorded using a .sup.13C optimised 10 mm extended temperature probehead at 125° C. using nitrogen gas for all pneumatics. Approximately 200 mg of material was dissolved in 3 ml of 1,2-tetrachloroethane-d.sub.2 (TCE-d.sub.2) along with chromium (III) acetylacetonate (Cr(acac).sub.3) resulting in a 65 mM solution of relaxation agent in solvent (Singh, G., Kothari, A., Gupta, V., Polymer Testing 28 5 (2009), 475). To ensure a homogenous solution, after initial sample preparation in a heat block, the NMR tube was further heated in a rotatory oven for at least 1 hour. Upon insertion into the magnet the tube was spun at 10 Hz. This setup was chosen primarily for the high resolution and quantitatively needed for accurate ethylene content quantification. Standard single-pulse excitation was employed without NOE, using an optimised tip angle, 1 s recycle delay and a bi-level WALTZ16 decoupling scheme (Zhou, Z., Kuemmerle, R., Qiu, X., Redwine, D., Cong, R., Taha, A., Baugh, D. Winniford, B., J. Mag. Reson. 187 (2007) 225, Busico, V., Carbonniere, P., Cipullo, R., Pellecchia, R., Severn, J., Talarico, G., Macromol. Rapid Commun. 2007, 28, 1128). A total of 6144 (6 k) transients were acquired per spectra. Quantitative .sup.13C{.sup.1H} NMR spectra were processed, integrated and relevant quantitative properties determined from the integrals. All chemical shifts were indirectly referenced to the central methylene group of the ethylene block (EEE) at 30.00 ppm using the chemical shift of the solvent. This approach allowed comparable referencing even when this structural unit was not present. Characteristic signals corresponding to the incorporation of ethylene were observed (Cheng, H. N., Macromolecules 17 (1984), 1950) and the comonomer fraction calculated as the fraction of ethylene in the polymer with respect to all monomer in the polymer: fE=(E/(P+E) The comonomer fraction was quantified using the method of Wang et. al. (Wang, W-J., Zhu, S., Macromolecules 33 (2000), 1157) through integration of multiple signals across the whole spectral region in the .sup.13C{.sup.1H} spectra. This method was chosen for its robust nature and ability to account for the presence of regio-defects when needed. Integral regions were slightly adjusted to increase applicability across the whole range of encountered comonomer contents. The mole percent comonomer incorporation was calculated from the mole fraction: E [mol %]=100*fE. The weight percent comonomer incorporation was calculated from the mole fraction:

E [wt %]=100*(fE*28.06)/((fE*28.06)+((1−fE)*42.08))

h) Crystex Analysis

Crystalline and Soluble Fractions Method

[0153] The crystalline (CF) and soluble fractions (SF) of the polypropylene (PP) compositions as well as the comonomer content and intrinsic viscosities of the respective fractions were analysed by the CRYSTEX QC, Polymer Char (Valencia, Spain).

[0154] A schematic representation of the CRYSTEX QC instrument is shown in FIG. 1. The crystalline and amorphous fractions are separated through temperature cycles of dissolution at 160° C., crystallization at 40° C. and re-dissolution in a1,2,4-trichlorobenzene (1,2,4-TCB) at 160° C. as shown in FIG. 2. Quantification of SF and CF and determination of ethylene content (C2) are achieved by means of an infrared detector (IR4) and an online 2-capillary viscometer which is used for the determination of the intrinsic viscosity (IV).

[0155] The IR4 detector is a multiple wavelength detector detecting IR absorbance at two different bands (CH3 and CH2) for the determination of the concentration and the Ethylene content in Ethylene-Propylene copolymers. IR4 detector is calibrated with series of 8 EP copolymers with known Ethylene content in the range of 2 wt.-% to 69 wt.-% (determined by 13C-NMR) and various concentration between 2 and 13 mg/ml for each used EP copolymer used for calibration.

[0156] The amount of Soluble fraction (SF) and Crystalline Fraction (CF) are correlated through the XS calibration to the “Xylene Cold Soluble” (XCS) quantity and respectively Xylene Cold Insoluble (XCI) fractions, determined according to standard gravimetric method as per ISO16152. XS calibration is achieved by testing various EP copolymers with XS content in the range 2-31 Wt %.

[0157] The intrinsic viscosity (IV) of the parent EP copolymer and its soluble and crystalline fractions are determined with a use of an online 2-capillary viscometer and are correlated to corresponding IV's determined by standard method in decalin according to ISO 1628. Calibration is achieved with various EP PP copolymers with IV=2-4 dL/g.

[0158] A sample of the PP composition to be analysed is weighed out in concentrations of 10 mg/ml to 20 mg/ml. After automated filling of the vial with 1,2,4-TCB containing 250 mg/l 2,6-tert-butyl-4-methylphenol (BHT) as antioxidant, the sample is dissolved at 160° C. until complete dissolution is achieved, usually for 60 min, with constant stirring of 800 rpm.

[0159] As shown in a FIG. 1 and FIG. 2, a defined volume of the sample solution is injected into the column filled with inert support where the crystallization of the sample and separation of the soluble fraction from the crystalline part is taking place. This process is repeated two times. During the first injection the whole sample is measured at high temperature, determining the IV[dl/g] and the C2[wt %] of the PP composition. During the second injection the soluble fraction (at low temperature) and the crystalline fraction (at high temperature) with the crystallization cycle are measured (Wt % SF, Wt % C2, IV). EP means ethylene propylene copolymer. PP means polypropylene.

II. Inventive and Comparative Examples

[0160] a) Catalyst Preparation

[0161] For the preparation of the catalyst 3.4 litre of 2-ethylhexanol and 810 ml of propylene glycol butyl monoether (in a molar ratio 4/1) were added to a 20.0 l reactor. Then 7.8 litre of a 20.0% solution in toluene of BEM (butyl ethyl magnesium) provided by Crompton GmbH, were slowly added to the well stirred alcohol mixture. During the addition, the temperature was kept at 10.0° C. After addition, the temperature of the reaction mixture was raised to 60.0° C. and mixing was continued at this temperature for 30 minutes. Finally after cooling to room temperature the obtained Mg-alkoxide was transferred to a storage vessel.

[0162] 21.2 g of Mg alkoxide prepared above was mixed with 4.0 ml bis(2-ethylhexyl) citraconate for 5 min After mixing the obtained Mg complex was used immediately in the preparation of the catalyst component.

[0163] 19.5 ml of titanium tetrachloride was placed in a 300 ml reactor equipped with a mechanical stirrer at 25.0° C. Mixing speed was adjusted to 170 rpm. 26.0 g of Mg-complex prepared above was added within 30 minutes keeping the temperature at 25.0° C. 3.0 ml of Viscoplex® 1-254 and 1.0 ml of a toluene solution with 2 mg Necadd 447™ was added. Then 24.0 ml of heptane was added to form an emulsion. Mixing was continued for 30 minutes at 25.0° C., after which the reactor temperature was raised to 90.0° C. within 30 minutes. The reaction mixture was stirred for a further 30 minutes at 90.0° C. Afterwards stirring was stopped and the reaction mixture was allowed to settle for 15 minutes at 90.0° C. The solid material was washed 5 times: washings were made at 80.0° C. under stirring for 30 min with 170 rpm. After stirring was stopped the reaction mixture was allowed to settle for 20-30 minutes and followed by siphoning.

[0164] Wash 1: washing was made with a mixture of 100 ml of toluene and 1 ml donor

[0165] Wash 2: washing was made with a mixture of 30 ml of TiCl4 and 1 ml of donor.

[0166] Wash 3: washing was made with 100 ml of toluene.

[0167] Wash 4: washing was made with 60 ml of heptane.

[0168] Wash 5: washing was made with 60 ml of heptane under 10 minutes stirring.

[0169] Afterwards stirring was stopped and the reaction mixture was allowed to settle for 10 minutes while decreasing the temperature to 70° C. with subsequent siphoning, followed by N.sub.2 sparging for 20 minutes to yield an air sensitive powder.

[0170] b) Inventive Examples (IE1, IE2, IE3, IE4 and IE5)

[0171] The second propylene polymer fractions related to the inventive examples (IE) were produced in a pilot plant with a prepolymerization reactor, one slurry loop reactor and one gas phase reactor. The solid catalyst component described above along with triethyl-aluminium (TEAL) as co-catalyst and dicyclo pentyl dimethoxy silane (D-donor) as external donor, were used in the inventive process.

[0172] The polymerization process conditions and properties of the propylene polymer fraction are described in Table 1.

[0173] The inventive polypropylene compositions were prepared by extruding the respective second propylene polymer fraction with a nucleating agent in a co-rotating twin screw extruder type Coperion ZSK 40 (screw diameter 40 mm, L/D ratio 38). The temperatures in the extruder were in the range of 190-230° C. In each of the inventive examples 0.05 wt % of Irganox 1010 (Pentaerythrityl-tetrakis(3-(3′,5′-di-tert. butyl-4-hydroxyphenyl)-propionate, CAS No. 6683-19-8, commercially available from BASF AG, Germany), 0.05 wt % of Irgafos 168 (Tris (2,4-di-t-butylphenyl) phosphite, CAS No. 31570-04-4, commercially available from BASF AG, Germany), 0.10 wt % of Calcium stearate (CAS. No. 1592-23-0, commercially available under the trade name Ceasit FI from Baerlocher GmbH, Germany) and 0.06 wt % of Glycerol monostearate (CAS No. 97593-29-8, commercially available with 90% purity under the trade name Grindsted PS 426 from Danisco A/S, Denmark) were added to the extruder as additives.

[0174] Following the extrusion step and after solidification of the strands in a water bath, the resulting polypropylene composition was pelletized in a strand pelletizer.

[0175] The polypropylene composition properties are described in Table 2.

[0176] c) Comparative Examples (CE1 and CE2)

[0177] CE1 is a C.sub.2 propylene random copolymer having an MFR.sub.2 of 13.0 g/10 min, produced in one reactor process and distributed by Borealis under the Trade name RE420MO.

[0178] CE2 is a C.sub.2 propylene random copolymer having an MFR.sub.2 of 20.0 g/10 min, produced in one reactor process and distributed by Borealis under the Trade name RF365MO.

TABLE-US-00001 TABLE 1 Polymerization process conditions and properties of the propylene polymer fractions IE1 IE2 IE3 IE4 IE5 Pre-polymerization reactor Temperature [° C.] 30 30 30 30 30 Catalyst feed [g/h] 4.4 5.9 2.9 2.8 1.7 D-Donor [g/t 41 41 40 41 40 propylene] TEAL/propylene [g/t 170 170 170 170 170 propylene] Al/D-Donor [Co/ED] [mol/mol] 8.3 8.3 8.4 8.3 8.5 Al/Ti [Co/TM] [mol/mol] 192 185 205 207 224 Residence Time [h] 0.3 0.3 0.3 0.3 0.3 Loop reactor (first propylene polymer fraction) Temperature [° C.] 70 70 70 70 70 Pressure [kPa] 5400 5400 5400 5400 5400 Residence time [h] 0.4 0.4 0.4 0.4 0.4 Split [%] 35 47 55 67 63 H.sub.2/C.sub.3 ratio [mol/kmol] 1.7 1.7 1.7 1.7 2.5 C.sub.2/C.sub.3 ratio [mol/kmol] 1.5 2.8 3.0 3.1 9.8 MFR.sub.2 [g/10 min] 22 19 19 19 19 C.sub.2 content of 1.sup.st [wt %] 0.5 0.6 0.5 0.5 1.5 propylene polymer fraction (Co F1) First gas-phase reactor (second propylene polymer fraction) Temperature [° C.] 80 80 80 80 80 Pressure [kPa] 2500 2500 2000 1900 1800 Residence time [h] 1.4 0.8 0.6 0.4 0.9 Split [%] 65 53 45 33 37 H.sub.2/C.sub.3 ratio [mol/kmol] 43.7 47.8 45.0 45.9 49.6 C.sub.2/C.sub.3 ratio [mol/kmol] 29.2 40.2 51.1 71.2 71.6 MFR.sub.2 [g/10 min] 24 18 20 20 16.8 C.sub.2 content of 2.sup.nd [wt %] 3.5 3.2 3.6 5.1 5.3 propylene polymer fraction (Co F2) C.sub.2 of 2.sup.nd propylene [wt %] 5.1 5.5 7.4 14.4 11.8 polymer (Como2) Comonomer ratio (CR)** 10.2 9.2 14.8 28.9 7.8 *Split relates to the amount of propylene polymer produced in each specific reactor. **Comonomer ratio defines the Comonomer of the second propylene polymer (Como2) divided by comonomer content of the first propylene polymer fraction (Co F1), e.g. for Ie1: 5.1/0.5

TABLE-US-00002 TABLE 2 Extrusion process conditions and polypropylene composition properties. IE1 IE2 IE3 IE4 IE5 CE1 CE2 Nucleating agent [wt %] 0.17 0.17 0.17 0.17 0.17 0.0 0.0 (Millad 3988 ®) Composition properties* MFR.sub.2 [g/10 27 22 24 23 18 13 20 min] C.sub.2 content (Co F2) [wt %] 3.5 3.2 3.6 5.1 5.3 3.4 3.4 XCS [wt %] 8.36 9.41 12.40 19.69 21.62 5.80 6.80 Tensile Modulus [MPa] 1157 1198 1084 888 803 921 1138 Charpy notched impact [kJ/m.sup.2] 6.20 6.48 6.84 10.21 9.64 5.3 4.5 strength Haze (1 mm) [%] 16.00 16.00 18.42 15.53 14.63 23 20 Tm [° C.] 158 159 160 160 156 150 151 Tc [° C.] 126 126 127 127 125 120 120 Crystex properties Soluble fraction [wt %] 8.4 9.0 11.0 16.3 17.7 Ethylene content in [wt %] 15.1 14.4 15.0 17.6 16.3 soluble fraction Crystalline fraction [wt %] 91.6 91.0 89.0 83.7 82.3 Ethylene content in [wt %] 2.3 1.8 2.4 2.8 3.4 crystalline fraction *measured on pellets obtained after the extrusion process.

[0179] From Table 2 it can be derived that the polypropylene compositions (inventive examples) show an improved balanced combination of high flowability, high stiffness and impact, and high level of optical properties (low haze value), compared to the comparative examples.