Method of light oil desulfurization in the presence of methane containing gas environment and catalyst structure

Abstract

Catalyst structures and corresponding methods are described for the desulfurization of sulfur-containing light oil or model compounds under a specified gas atmosphere. The sulfur-containing feedstock is effectively converted while producing valuable hydrocarbon products such as BTX and carbon disulfide, as well as utilizing methane or natural gas resources, providing an economical and environmental innovation in the petroleum industry.

Claims

1. A method for the desulfurization of a sulfur-containing hydrocarbon feedstock, the method comprising introducing the sulfur-containing feedstock within a reactor in the presence of a gas atmosphere and a catalyst structure, wherein the catalyst structure comprises a porous support structure that comprises an aluminosilicate material including at least the following metals located in the aluminosilicate material: silver and gallium, or gallium and cerium, or silver, gallium and cerium, or silver, gallium and molybdenum; wherein the gas atmosphere consists of pure gas or a mixture of gases selected from the group consisting of nitrogen, helium, methane, and natural gas.

2. The method of claim 1, wherein the sulfur-containing feedstock comprises light oils containing sulfur or compounds selected from the group consisting of thiophene, benzothiophene, dibenzothiophene and any combination and/or derivatives thereof.

3. The method of claim 1, wherein each metal loaded in the porous support structure is present in an amount from about 0.1 wt % to about 20 wt % based upon the total weight of the catalyst structure.

4. The method of claim 3 wherein the metals are loaded within the porous support structure in the form of one or more of the following salts: chlorides, nitrates, sulfates, sulfides and polythiometalates.

5. The method of claim 1, wherein the catalyst structure comprises the following metals loaded in the aluminosilicate material at the following weight percentages: 1 wt % silver, 1 wt % gallium, and 5 wt % cerium; or 1 wt % gallium and 5 wt % cerium; or 1 wt % silver and 1 wt % gallium.

6. The method of claim 1, wherein the catalyst structure further comprises a titanium oxide material including molybdenum and nickel loaded in the titanium oxide material.

7. The method of claim 1, wherein the catalyst structure further comprises a titanium oxide material having the following metals loaded in the titanium oxide material at the following weight percentages: 10 wt % molybdenum and 1.25 wt % nickel.

8. The method of claim 1, wherein the reactor comprises one or a combination of a batch reactor system, a continuous tubular reactor (CTR), and a semi-batch reactor.

9. The method of claim 1, wherein the following conditions are present in the reactor: a reaction temperature within the range of about 350° C. to about 450° C., and a pressure within the range of about 1 atm and about 50 atm.

10. The method of claim 1, wherein the reactor comprises a batch reactor, and a mass ratio of sulfur-containing feedstock to catalyst structure within the reactor is within the range of about 50:1 to about 1:10.

11. The method of claim 1, wherein the reactor comprises a continuous reactor, and a liquid hourly space velocity (LHSV) of the sulfur-containing feedstock is within the range of about 0.1 h.sup.−1 to about 10 h.sup.−1.

12. The method of claim 1, further comprising forming a plurality of products within the reactor, the plurality of products comprising carbon disulfide, benzene, toluene and xylenes.

13. A method for the desulfurization of a sulfur-containing hydrocarbon feedstock, the method comprising introducing the sulfur-containing feedstock within a reactor in the presence of a gas atmosphere and a catalyst structure, wherein the catalyst structure comprises an aluminosilicate material including silver, gallium and molybdenum loaded in the aluminosilicate material.

14. The method of claim 13, wherein the aluminosilicate material includes the following metals loaded in the porous support structure at the following weight percentages: 1 wt % silver, 1 wt % gallium, and 10 wt % molybdenum.

Description

DETAILED DESCRIPTION

(1) The present invention is directed toward the formulation of a heterogeneous catalyst and a process of utilizing the catalyst for light oil desulfurization under methane or natural gas environment for decreasing the sulfur content of such oil feedstock while also producing high value-added chemicals such as carbon disulfide, benzene, toluene and xylenes.

(2) In particular, described herein are methods of desulfurization of light oils or corresponding model compounds under a methane or natural gas environment. For example, light oils as described herein can be crude oils having an API gravity of 31.1° API or higher, and further having a dynamic viscosity of less than 2×10.sup.3 cP (mPa.Math.s). Some non-limiting examples of light oils that can be upgraded as described herein by desulfurization as well as producing desirable chemicals in the upgrading process include marine diesel oil, FCC diesel, renewable diesel, FCC gasoline and coker naphtha) and/or corresponding model compounds (such as thiophene, benzothiophene, dibenzothiophene, organic sulfide and their derivatives).

(3) It is observed that methane can be effectively activated, which facilitates the desulfurization process. In addition, other chemicals such as carbon disulfide (CS.sub.2) and BTX (benzene, toluene and xylenes) can be generated, which can be further utilized as solvents or intermediates in chemistry. This method provides a transformational way for oil desulfurization in the petroleum industry.

(4) In the following detailed description, while aspects of the disclosure are disclosed, alternate embodiments of the present disclosure and their equivalents may be devised without parting from the spirit or scope of the present disclosure. It should be noted that any discussion herein regarding “one embodiment”, “an embodiment”, “an exemplary embodiment”, and the like indicate that the embodiment described may include a particular feature, structure, or characteristic, and that such particular feature, structure, or characteristic may not necessarily be included in every embodiment. In addition, references to the foregoing do not necessarily comprise a reference to the same embodiment. Finally, irrespective of whether it is explicitly described, one of ordinary skill in the art would readily appreciate that each of the particular features, structures, or characteristics of the given embodiments may be utilized in connection or combination with those of any other embodiment discussed herein.

(5) Various operations may be described as multiple discrete actions or operations in turn, in a manner that is most helpful in understanding the claimed subject matter. However, the order of description should not be construed as to imply that these operations are necessarily order dependent. In particular, these operations may not be performed in the order of presentation. Operations described may be performed in a different order than the described embodiment. Various additional operations may be performed and/or described operations may be omitted in additional embodiments.

(6) For the purposes of the present disclosure, the phrase “A and/or B” means (A), (B), or (A and B). For the purposes of the present disclosure, the phrase “A, B, and/or C” means (A), (B), (C), (A and B), (A and C), (B and C), or (A, B and C).

(7) The terms “comprising,” “including,” “having,” and the like, as used with respect to embodiments of the present disclosure, are synonymous.

(8) In accordance with example embodiments, catalyst structures are described herein for use in the combination with processes for oil desulfurization utilizing methane or natural gas resources and one or more of such catalyst structures to achieve a product with lower sulfur content.

(9) The use of methane or natural gas, rather than hydrogen, in the oil desulfurization process obviates the need for an economically unfavorable hydrotreating step at high pressures and temperatures. The design of the catalyst so as to activate methane and sulfur-containing species and selectively form desired products is very important to the efficacy of the process. Particularly, the catalyst structures described herein facilitate the oil desulfurization process in the presence of methane or natural gas at low temperatures (e.g., in the range of 350-450° C., preferably at around 400° C.) and pressures (e.g., in the range of 1-50 atm, preferably at 30 atm) and in the presence of catalyst structures.

(10) Catalyst Structures

(11) In accordance with the present invention, a catalyst structure is provided that comprises one or a combination of mono or multi-metallic (e.g., bimetallic) active components loaded on highly porous supports for oil desulfurization in methane or natural gas environment. It is noted that the catalyst structures described herein can also be used for sulfur removal in other gas environments such as H.sub.2, He and N.sub.2 environments, although utilizing methane or natural gas environment is preferred.

(12) The catalyst structure can be synthesized by impregnating or doping a suitable support material with two or more metals. Suitably porous support material can be an aluminum oxide (i.e., Al.sub.2O.sub.3), an aluminosilicate (e.g. zeolite), a silicon oxide (i.e. SiO.sub.2), a titanium oxide (i.e. TiO.sub.2) or a silicon carbide (i.e. SiC). Some non-limiting examples of a suitable zeolite material as a support material for the catalyst structure include HZSM-5 type zeolite, L-type zeolite, HX type zeolite, HY type zeolite and a zeolite structure commercially available from Rive Technology (Monmouth Junction, N.J.). An ammonium type zeolite can also be utilized by conversion to a hydrogen type zeolite (e.g., by calcination in static air at a temperature of about 400-600° C. for a period of about 4-6 hours). When utilizing a zeolite material as the support material, a SiO.sub.2 to Al.sub.2O.sub.3 ratio of the zeolite support material can be in the range of 2.5-280 (i.e., a ratio of SiO.sub.2 to Al.sub.2O.sub.3 that is in the range of 2.5:1 to 280:1).

(13) Suitable metals that can be loaded on the porous support material by impregnation or doping include any one or more (e.g., any two or more) from the following group: molybdenum (Mo), nickel (Ni), cobalt (Co), silver (Ag), gallium (Ga), zinc (Zn), and cerium (Ce). Each metal dopant or the combination of metal dopants can be provided within the catalyst structure in an amount ranging from 0.1-20 wt % (i.e., based upon the total weight of the catalyst structure). Specific examples are provided herein of different metal loadings for catalyst structures.

(14) The porous support material can be doped with a suitable amount of one or more metals in the following manner. One or more metal salts can be dissolved in deionized water to form an aqueous solution at the suitable concentration(s) within the solution. Metal precursor salts that can be used to form the catalyst structure include, without limitation, chlorides, nitrates, sulfates, sulfides and polythiometalates. The one or more metal precursors in solution are then loaded into the porous support material to achieve a desired amount of metals within the catalyst structure (e.g., from 0.1-20 wt %). Any suitable loading process can be performed to load metals within the porous support material. Some non-limiting examples of metal loading processes include: IWI (incipient wetness impregnation, where an active metal precursor is first dissolved in an aqueous or organic solution, the metal-containing solution is then added to a catalyst support containing the same pore volume as the added solution volume, where capillary action draws the solution into the pores); WI (wet impregnation, where more liquid than the IWI volume is added to the support, and the solvent is then removed by evaporation); IE (ion-exchange, where metal cations are exchanged into the support from solution); and FI (framework incorporation, where metals are added to the support materials during the synthesis step of the support).

(15) Depending upon the particular loading process, the resultant metal-loaded catalyst structure can be dried at a temperature between about 80° C. to about 120° C. for a period of time between about 2 hours to about 24 hours. The dried catalyst structure can then be calcined under air, N.sub.2 or He gas at a temperature ranging from 300-700° C. and at a suitable ramped or stepwise increased heating rate (e.g., the heating rate at about 5-20° C./min), where such calcination temperatures, times and heating rates can be modified depending upon the type or types of metals doped into the catalyst structure as well as reaction conditions associated with the use of the catalyst structure.

(16) The resultant metal-doped catalyst structure is suitable for use in oil desulfurization under methane or natural gas environment in processes as described herein. The catalyst structure can be processed into a granular form with a granule size desired for a particular operation. The catalyst structure can also be formed into any other suitable configuration. For example, the catalyst structure in a powder form can be utilized in a batch reactor system, while the catalyst structure in a pelleted form can be utilized in a continuous flow reactor system.

(17) Systems and Methods for Oil Desulfurization Utilizing the Catalyst Structures

(18) The conversion of sulfur-containing species and selectivity towards valuable hydrocarbon products such as aromatics, especially benzene, toluene and xylenes can be fine-tuned using catalyst structures as described herein and under methane or natural gas environment. Different reactor systems and modified operating conditions (e.g., temperatures and pressures), as well as modifications of the catalyst structures within the reactor systems, can also be implemented to achieve varied product compositions. For example, when utilizing a batch reactor, a mass ratio of sulfur-containing feedstock to catalyst structure within the reactor can be within the range of about 50:1 to about 1:10. When utilizing a continuous reactor, a liquid hourly space velocity (LHSV) of the sulfur-containing feedstock can be within the range of about 0.1 h.sup.−1 to about 10 h.sup.−1. In addition, the reactor system can comprise one or a combination of a batch reactor system, a continuous tubular reactor (CTR), and a semi-batch reactor.

(19) Methane, as a main component in natural gas, is particularly useful for oil desulfurization in the presence of catalysts described herein. Methane is typically regarded as chemically inert due to its stable structure, and methane activation has been a challenge in natural gas utilization. However, it has been validated that methane utilization can be significantly enhanced with the assistance of the catalysts aforementioned.

(20) The desulfurization process as described herein further minimizes the generation of CO.sub.2. In particular, methane desulfurization utilizing the catalyst structures as described herein can result in the generation or production of CO.sub.2 that is less than 5% by weight of the oil product, in some scenarios less than 3% by weight, or even less than 1% by weight (e.g., substantially no CO.sub.2 is formed in the process).

(21) Some examples of desulfurizing sulfur-containing feedstocks using the aforementioned catalyst structure and process are now described.

Example 1

(22) 10 wt % Mo-1.25 wt % Ni—TiO.sub.2—S catalyst (MDS1) was prepared in the following manner. A TiO.sub.2 (P25, average particle size 21 nm) support structure in powder form obtained from Sigma-Aldrich was used without further treatment. The metal salts nickel nitrate (Ni(NO.sub.3).sub.2.6H.sub.2O) and ammonium tetrathiomolybdate ((NH.sub.4).sub.2MoS.sub.4) was dissolved in deionized water to form a precursor solution. The TiO.sub.2 support was impregnated with the metal precursor solution to achieve a suitable metal weight loading. The obtained wet powder was first dried in an oven at 100° C. overnight, followed by calcination at 350° C. in a nitrogen atmosphere for 2 hours with a nitrogen flow rate of 100 mL/min.

(23) 1 g dibenzothiophene (DBT), which is a model compound representing thiophenic sulfur species in diesel oil, was put in a 100 mL batch reactor. The catalyst was added and mechanical mixing was practiced. The reaction was carried out under 400° C. and a gas atmosphere of 32 atm CH.sub.4 and 3 atm N.sub.2. The weight ratio of DBT to catalyst was 5:1 and the reaction lasted 1 hour. The gas product was collected in air bags, and the soluble product was extracted by solvent 1,1,2,2-tetrachloroethane and separated from the solid product through filtration. DBT conversion, methane conversion, gas yield, soluble yield, coke yield and overall mass balance were measured and listed in Table 1. The composition of gas products is listed in Table 2. In addition, soluble products were also analyzed and the product distribution is listed in Table 3.

Example 2

(24) 1 wt % Ag-1 wt % Ga-5 wt % Ce/HZSM-5(23:1) catalyst (MAC1) was prepared in the following manner. An NH.sub.4-ZSM-5 (SiO.sub.2:Al.sub.2O.sub.3 molar ratio of 23:1) support structure in powder form obtained from Zeolyst USA was calcined in static air at 600° C. for 3 hours. The following metal salts were dissolved in deionized water to form a metal precursor solution: Ce(NO.sub.3).sub.3.6H.sub.2O, Ga(NO.sub.3).sub.3.9H.sub.2O and AgNO.sub.3. The HZSM-5 support was impregnated with the metal precursor solution to achieve a suitable metal weight loading. The obtained wet powder was first dried in an oven at 100° C. overnight, followed by calcination at 550° C. for 4 hours in static air.

(25) 1 g dibenzothiophene (DBT), which is a model compound representing thiophenic sulfur species in diesel oil, was put in a 100 mL batch reactor. The catalyst was added and mechanical mixing was practiced. The reaction was carried out under 400° C. and a gas atmosphere of 32 atm CH.sub.4 and 3 atm N.sub.2. The weight ratio of DBT to catalyst was 5:1 and the reaction lasted 1 hour. The gas product was collected in air bags, and the soluble product was extracted by solvent 1,1,2,2-tetrachloroethane and separated from the solid product through filtration. DBT conversion, methane conversion, gas yield, soluble yield, coke yield and overall mass balance were measured and listed in Table 1. Besides, the composition of gas products is listed in Table 2. Moreover, soluble products were also analyzed and the product distribution is listed in Table 3.

Example 3

(26) 10 wt % Mo-1.25 wt % Ni—TiO.sub.2—S catalyst (MDS1) was prepared in the following manner. A TiO.sub.2 (P25, average particle size 21 nm) support structure in powder form obtained from Sigma-Aldrich was used without further treatment. The metal salts nickel nitrate (Ni(NO.sub.3).sub.2.6H.sub.2O) and ammonium tetrathiomolybdate ((NH.sub.4).sub.2MoS.sub.4) was dissolved in deionized water to form a precursor solution. The TiO.sub.2 support was impregnated with the metal precursor solution to achieve a suitable metal weight loading. The obtained wet powder was first dried in an oven at 100° C. overnight, followed by calcination at 350° C. in a nitrogen atmosphere for 2 hours with a nitrogen flow rate of 100 mL/min.

(27) 1 wt % Ag-1 wt % Ga-5 wt % Ce/HZSM-5(23:1) (MAC1) catalyst was prepared in the following manner. An NH.sub.4-ZSM-5 (SiO.sub.2:Al.sub.2O.sub.3 molar ratio of 23:1) support structure in powder form obtained from Zeolyst USA was calcined in static air at 600° C. for 3 hours. The following metal salts were dissolved in deionized water to form a metal precursor solution: Ce(NO.sub.3).sub.3.6H.sub.2O, Ga(NO.sub.3).sub.3.9H.sub.2O and AgNO.sub.3. The HZSM-5 support was impregnated with the metal precursor solution to achieve a suitable metal weight loading. The obtained wet powder was first dried in an oven at 100° C. overnight, followed by calcination at 550° C. for 4 hours in static air.

(28) 1 g dibenzothiophene (DBT), which is a model compound representing thiophenic sulfur species in diesel oil, was put in a 100 mL batch reactor. The 10 wt % Mo-1.25 wt % Ni—TiO.sub.2—S catalyst and the 1 wt % Ag-1 wt % Ga-5 wt % Ce/HZSM-5(23:1) catalyst were added and mechanical mixing was practiced. The reaction was carried out under 400° C. and a gas atmosphere of 32 atm CH.sub.4 and 3 atm N.sub.2. The weight ratio of DBT to each catalyst was 5:1 and the reaction lasted 1 hour. The gas product was collected in air bags, and the soluble product was extracted by solvent 1,1,2,2-tetrachloroethane and separated from the solid product through filtration. DBT conversion, methane conversion, gas yield, soluble yield, coke yield and overall mass balance were measured and listed in Table 1. Besides, the composition of gas products is listed in Table 2. Moreover, soluble products were also analyzed and the product distribution is listed in Table 3.

Example 4

(29) 10 wt % Mo-1.25 wt % Ni—TiO.sub.2—S catalyst (MDS1) was prepared in the following manner. A TiO.sub.2 (P25, average particle size 21 nm) support structure in powder form obtained from Sigma-Aldrich was used without further treatment. The metal salts nickel nitrate (Ni(NO.sub.3).sub.2.6H.sub.2O) and ammonium tetrathiomolybdate ((NH.sub.4).sub.2MoS.sub.4) was dissolved in deionized water to form a precursor solution. The TiO.sub.2 support was impregnated with the metal precursor solution to achieve a suitable metal weight loading. The obtained wet powder was first dried in an oven at 100° C. overnight, followed by calcination at 350° C. in a nitrogen atmosphere for 2 hours with a nitrogen flow rate of 100 mL/min.

(30) 1 wt % Ag-1 wt % Ga-5 wt % Ce/HZSM-5(23:1) catalyst (MAC1) was prepared in the following manner. An NH.sub.4-ZSM-5 (SiO.sub.2:Al.sub.2O.sub.3 molar ratio of 23:1) support structure in powder form obtained from Zeolyst USA was calcined in static air at 600° C. for 3 hours. The following metal salts were dissolved in deionized water to form a metal precursor solution: Ce(NO.sub.3).sub.3.6H.sub.2O, Ga(NO.sub.3).sub.3.9H.sub.2O and AgNO.sub.3. The HZSM-5 support was impregnated with the metal precursor solution to achieve a suitable metal weight loading. The obtained wet powder was first dried in an oven at 100° C. overnight, followed by calcination at 550° C. for 4 hours in static air.

(31) 1 g dibenzothiophene (DBT), which is a model compound representing thiophenic sulfur species in diesel oil, was put in a 100 mL batch reactor. The 10 wt % Mo-1.25 wt % Ni—TiO.sub.2—S catalyst and the 1 wt % Ag-1 wt % Ga-5 wt % Ce/HZSM-5(23:1) catalyst were added and mechanical mixing was practiced. The reaction was carried out under 400° C. and a gas atmosphere of 35 atm N.sub.2. The weight ratio of DBT to each catalyst was 5:1 and the reaction lasted 1 hour. The gas product was collected in air bags, and the soluble product was extracted by solvent 1,1,2,2-tetrachloroethane and separated from the solid product through filtration. DBT conversion, methane conversion, gas yield, soluble yield, coke yield and overall mass balance were measured and listed in Table 1. Besides, the composition of gas products is listed in Table 2. Moreover, soluble products were also analyzed and the product distribution is listed in Table 3.

Example 5

(32) A commercial silicon carbide from Sigma-Aldrich with a specific surface area of 10 m.sup.2/g was used as the catalyst without further purification. 1 g dibenzothiophene (DBT), which is a model compound representing thiophenic sulfur species in diesel oil, was put in a 100 mL batch reactor. The reaction was carried out under 400° C. and a gas atmosphere of 32 atm CH.sub.4 and 3 atm N.sub.2. The weight ratio of DBT to catalyst was 5:1 and the reaction lasted 1 hour. The gas product was collected in air bags, and the soluble product was extracted by solvent 1,1,2,2-tetrachloroethane and separated from the solid product through filtration. DBT conversion, methane conversion, gas yield, soluble yield, coke yield and overall mass balance were measured and listed in Table 1. Besides, the composition of gas products is listed in Table 2. Moreover, soluble products were also analyzed and the product distribution is listed in Table 3.

Example 6

(33) 10 wt % Mo-1.25 wt % Ni—TiO.sub.2—O (MDS1-O) catalyst was prepared in the following manner. A TiO.sub.2 (P25, average particle size 21 nm) support structure in powder form obtained from Sigma-Aldrich was used without further treatment. The metal salts nickel nitrate (Ni(NO.sub.3).sub.2.6H.sub.2O) and ammonium heptamolybdate ((NH.sub.4).sub.6Mo.sub.7O.sub.24.4H.sub.2O) was dissolved in deionized water to form a precursor solution. The TiO.sub.2 support was impregnated with the metal precursor solution to achieve a suitable metal weight loading. The obtained wet powder was first dried in an oven at 100° C. overnight, followed by calcination at 550° C. for 4 hours in static air.

(34) 1 wt % Ag-1 wt % Ga-5 wt % Ce/HZSM-5(23:1) catalyst (MAC1) was prepared in the following manner. An NH.sub.4-ZSM-5 (SiO.sub.2:Al.sub.2O.sub.3 molar ratio of 23:1) support structure in powder form obtained from Zeolyst USA was calcined in static air at 600° C. for 3 hours. The following metal salts were dissolved in deionized water to form a metal precursor solution: Ce(NO.sub.3).sub.3.6H.sub.2O, Ga(NO.sub.3).sub.3.9H.sub.2O and AgNO.sub.3. The HZSM-5 support was impregnated with the metal precursor solution to achieve a suitable metal weight loading. The obtained wet powder was first dried in an oven at 100° C. overnight, followed by calcination at 550° C. for 4 hours in static air.

(35) 1 g dibenzothiophene (DBT), which is a model compound representing thiophenic sulfur species in diesel oil, was put in a 100 mL batch reactor. The 10 wt % Mo-1.25 wt % Ni—TiO.sub.2—O catalyst and the 1 wt % Ag-1 wt % Ga-5 wt % Ce/HZSM-5(23:1) catalyst were added and mechanical mixing was practiced. The reaction was carried out under 400° C. and a gas atmosphere of 32 atm CH.sub.4 and 3 atm N.sub.2. The weight ratio of DBT to each catalyst was 5:1 and the reaction lasted 1 hour. The gas product was collected in air bags, and the soluble product was extracted by solvent 1,1,2,2-tetrachloroethane and separated from the solid product through filtration. DBT conversion, methane conversion, gas yield, soluble yield, coke yield and overall mass balance were measured and listed in Table 1. Besides, the composition of gas products is listed in Table 2. Moreover, soluble products were also analyzed and the product distribution is listed in Table 3.

Example 7

(36) 10 wt % Mo-1.25 wt % Ni—TiO.sub.2—S-2 (MDS2) catalyst was prepared in the following manner. A TiO.sub.2 (P25, average particle size 21 nm) support structure in powder form obtained from Sigma-Aldrich was used without further treatment. The metal salts nickel nitrate (Ni(NO.sub.3).sub.2.6H.sub.2O) and ammonium heptamolybdate ((NH.sub.4).sub.6Mo.sub.7O.sub.24.4H.sub.2O) was dissolved in deionized water to form a precursor solution. The TiO.sub.2 support was impregnated with the metal precursor solution to achieve a suitable metal weight loading. The obtained wet powder was first dried in an oven at 100° C. overnight, followed by calcination at 550° C. for 4 hours in static air. The resultant catalyst was treated by 514 ppm ELS gas (N.sub.2 balance) in a tube furnace at 400° C. for 14 h.

(37) 1 wt % Ag-1 wt % Ga-5 wt % Ce/HZSM-5(23:1) catalyst (MAC1) was prepared in the following manner. An NH.sub.4-ZSM-5 (SiO.sub.2:Al.sub.2O.sub.3 molar ratio of 23:1) support structure in powder form obtained from Zeolyst USA was calcined in static air at 600° C. for 3 hours. The following metal salts were dissolved in deionized water to form a metal precursor solution: Ce(NO.sub.3).sub.3.6H.sub.2O, Ga(NO.sub.3).sub.3.9H.sub.2O and AgNO.sub.3. The HZSM-5 support was impregnated with the metal precursor solution to achieve a suitable metal weight loading. The obtained wet powder was first dried in an oven at 100° C. overnight, followed by calcination at 550° C. for 4 hours in static air.

(38) 1 g dibenzothiophene (DBT), which is a model compound representing thiophenic sulfur species in diesel oil, was put in a 100 mL batch reactor. The 10 wt % Mo-1.25 wt % Ni—TiO.sub.2—S-2 catalyst and the 1 wt % Ag-1 wt % Ga-5 wt % Ce/HZSM-5(23:1) catalyst were added and mechanical mixing was practiced. The reaction was carried out under 400° C. and a gas atmosphere of 32 atm CH.sub.4 and 3 atm N.sub.2. The weight ratio of DBT to each catalyst was 5:1 and the reaction lasted 1 hour. The gas product was collected in air bags, and the soluble product was extracted by solvent 1,1,2,2-tetrachloroethane and separated from the solid product through filtration. DBT conversion, methane conversion, gas yield, soluble yield, coke yield and overall mass balance were measured and listed in Table 1. Besides, the composition of gas products is listed in Table 2. Moreover, soluble products were also analyzed and the product distribution is listed in Table 3.

Example 8

(39) 10 wt % Mo-1.25 wt % Ni—TiO.sub.2—S-3 (MDS3) catalyst was prepared in the following manner. A TiO.sub.2 (P25, average particle size 21 nm) support structure in powder form obtained from Sigma-Aldrich was used without further treatment. The metal salts nickel nitrate (Ni(NO.sub.3).sub.2.6H.sub.2O) and ammonium heptamolybdate ((NH.sub.4).sub.6Mo.sub.7O.sub.24.4H.sub.2O) was dissolved in deionized water to form a precursor solution. The TiO.sub.2 support was impregnated with the metal precursor solution to achieve a suitable metal weight loading. The obtained wet powder was first dried in an oven at 100° C. overnight, followed by calcination at 550° C. for 4 hours in static air. The resultant catalyst was treated in a batch reaction together with carbon disulfide at 300° C. for 1 h, then put in a tube furnace and treated by 5 vol % H.sub.2 gas (Ar balance) at 400° C. for 2 h.

(40) 1 wt % Ag-1 wt % Ga-5 wt % Ce/HZSM-5(23:1) catalyst (MAC1) was prepared in the following manner. An NH.sub.4-ZSM-5 (SiO.sub.2:Al.sub.2O.sub.3 molar ratio of 23:1) support structure in powder form obtained from Zeolyst USA was calcined in static air at 600° C. for 3 hours. The following metal salts were dissolved in deionized water to form a metal precursor solution: Ce(NO.sub.3).sub.3.6H.sub.2O, Ga(NO.sub.3).sub.3.9H.sub.2O and AgNO.sub.3. The HZSM-5 support was impregnated with the metal precursor solution to achieve a suitable metal weight loading. The obtained wet powder was first dried in an oven at 100° C. overnight, followed by calcination at 550° C. for 4 hours in static air.

(41) 1 g dibenzothiophene (DBT), which is a model compound representing thiophenic sulfur species in diesel oil, was put in a 100 mL batch reactor. The 10 wt % Mo-1.25 wt % Ni—TiO.sub.2—S-3 catalyst and the 1 wt % Ag-1 wt % Ga-5 wt % Ce/HZSM-5(23:1) catalyst were added and mechanical mixing was practiced. The reaction was carried out under 400° C. and a gas atmosphere of 32 atm CH.sub.4 and 3 atm N.sub.2. The weight ratio of DBT to each catalyst was 5:1 and the reaction lasted 1 hour. The gas product was collected in air bags, and the soluble product was extracted by solvent 1,1,2,2-tetrachloroethane and separated from the solid product through filtration. DBT conversion, methane conversion, gas yield, soluble yield, coke yield and overall mass balance were measured and listed in Table 1. Besides, the composition of gas products is listed in Table 2. Moreover, soluble products were also analyzed and the product distribution is listed in Table 3.

Example 9

(42) 10 wt % Mo-1.25 wt % Ni—TiO.sub.2—S-4 (MDS4) catalyst was prepared in the following manner. A TiO.sub.2 (P25, average particle size 21 nm) support structure in powder form obtained from Sigma-Aldrich was used without further treatment. The metal salts nickel nitrate (Ni(NO.sub.3).sub.2.6H.sub.2O) and ammonium heptamolybdate ((NH.sub.4).sub.6Mo.sub.7O.sub.24.4H.sub.2O) was dissolved in deionized water to form a precursor solution. The TiO.sub.2 support was impregnated with the metal precursor solution to achieve a suitable metal weight loading. The obtained wet powder was first dried in an oven at 100° C. overnight, followed by calcination at 550° C. for 4 hours in static air. The resultant catalyst was treated by 1% ELS gas (N.sub.2 balance) in a tube furnace at 400° C. for 1 h.

(43) 1 wt % Ag-1 wt % Ga-5 wt % Ce/HZSM-5(23:1) catalyst (MAC1) was prepared in the following manner. An NH.sub.4-ZSM-5 (SiO.sub.2:Al.sub.2O.sub.3 molar ratio of 23:1) support structure in powder form obtained from Zeolyst USA was calcined in static air at 600° C. for 3 hours. The following metal salts were dissolved in deionized water to form a metal precursor solution: Ce(NO.sub.3).sub.3.6H.sub.2O, Ga(NO.sub.3).sub.3.9H.sub.2O and AgNO.sub.3. The HZSM-5 support was impregnated with the metal precursor solution to achieve a suitable metal weight loading. The obtained wet powder was first dried in an oven at 100° C. overnight, followed by calcination at 550° C. for 4 hours in static air.

(44) 1 g dibenzothiophene (DBT), which is a model compound representing thiophenic sulfur species in diesel oil, was put in a 100 mL batch reactor. The 10 wt % Mo-1.25 wt % Ni—TiO.sub.2—S-4 catalyst and the 1 wt % Ag-1 wt % Ga-5 wt % Ce/HZSM-5(23:1) catalyst were added and mechanical mixing was practiced. The reaction was carried out under 400° C. and a gas atmosphere of 32 atm CH.sub.4 and 3 atm N.sub.2. The weight ratio of DBT to each catalyst was 5:1 and the reaction lasted 1 hour. The gas product was collected in air bags, and the soluble product was extracted by solvent 1,1,2,2-tetrachloroethane and separated from the solid product through filtration. DBT conversion, methane conversion, gas yield, soluble yield, coke yield and overall mass balance were measured and listed in Table 1. Besides, the composition of gas products is listed in Table 2. Moreover, soluble products were also analyzed and the product distribution is listed in Table 3.

Example 10

(45) 10 wt % Mo-1.25 wt % Ni—TiO.sub.2—S catalyst (MDS1) was prepared in the following manner. A TiO.sub.2 (P25, average particle size 21 nm) support structure in powder form obtained from Sigma-Aldrich was used without further treatment. The metal salts nickel nitrate (Ni(NO.sub.3).sub.2.6H.sub.2O) and ammonium tetrathiomolybdate ((NH.sub.4).sub.2MoS.sub.4) was dissolved in deionized water to form a precursor solution. The TiO.sub.2 support was impregnated with the metal precursor solution to achieve a suitable metal weight loading. The obtained wet powder was first dried in an oven at 100° C. overnight, followed by calcination at 350° C. in a nitrogen atmosphere for 2 hours with a nitrogen flow rate of 100 mL/min.

(46) 1 wt % Ga-5 wt % Ce/HZSM-5(23:1) catalyst (MAC2) was prepared in the following manner. An NH.sub.4-ZSM-5 (SiO.sub.2:Al.sub.2O.sub.3 molar ratio of 23:1) support structure in powder form obtained from Zeolyst USA was calcined in static air at 600° C. for 3 hours. The following metal salts were dissolved in deionized water to form a metal precursor solution: Ce(NO.sub.3).sub.3.6H.sub.2O and Ga(NO.sub.3).sub.3.9H.sub.2O. The HZSM-5 support was impregnated with the metal precursor solution to achieve a suitable metal weight loading. The obtained wet powder was first dried in an oven at 100° C. overnight, followed by calcination at 550° C. for 4 hours in static air.

(47) 1 g dibenzothiophene (DBT), which is a model compound representing thiophenic sulfur species in diesel oil, was put in a 100 mL batch reactor. The 10 wt % Mo-1.25 wt % Ni—TiO.sub.2—S catalyst and the 1 wt % Ga-5 wt % Ce/HZSM-5(23:1) catalyst were added and mechanical mixing was practiced. The reaction was carried out under 400° C. and a gas atmosphere of 32 atm CH.sub.4 and 3 atm N.sub.2. The weight ratio of DBT to each catalyst was 5:1 and the reaction lasted 1 hour. The gas product was collected in air bags, and the soluble product was extracted by solvent 1,1,2,2-tetrachloroethane and separated from the solid product through filtration. DBT conversion, methane conversion, gas yield, soluble yield, coke yield and overall mass balance were measured and listed in Table 1. Besides, the composition of gas products is listed in Table 2. Moreover, soluble products were also analyzed and the product distribution is listed in Table 3.

Example 11

(48) 10 wt % Mo-1.25 wt % Ni—TiO.sub.2—S catalyst (MDS1) was prepared in the following manner. A TiO.sub.2 (P25, average particle size 21 nm) support structure in powder form obtained from Sigma-Aldrich was used without further treatment. The metal salts nickel nitrate (Ni(NO.sub.3).sub.2.6H.sub.2O) and ammonium tetrathiomolybdate ((NH.sub.4).sub.2MoS.sub.4) was dissolved in deionized water to form a precursor solution. The TiO.sub.2 support was impregnated with the metal precursor solution to achieve a suitable metal weight loading. The obtained wet powder was first dried in an oven at 100° C. overnight, followed by calcination at 350° C. in a nitrogen atmosphere for 2 hours with a nitrogen flow rate of 100 mL/min.

(49) 1 wt % Ag-1 wt % Ga/HZSM-5(23:1) catalyst (MAC3) was prepared in the following manner. An NH.sub.4-ZSM-5 (SiO.sub.2:Al.sub.2O.sub.3 molar ratio of 23:1) support structure in powder form obtained from Zeolyst USA was calcined in static air at 600° C. for 3 hours. The following metal salts were dissolved in deionized water to form a metal precursor solution: Ga(NO.sub.3).sub.3.9H.sub.2O and AgNO.sub.3. The HZSM-5 support was impregnated with the metal precursor solution to achieve a suitable metal weight loading. The obtained wet powder was first dried in an oven at 100° C. overnight, followed by calcination at 550° C. for 4 hours in static air.

(50) 1 g dibenzothiophene (DBT), which is a model compound representing thiophenic sulfur species in diesel oil, was put in a 100 mL batch reactor. The 10 wt % Mo-1.25 wt % Ni—TiO.sub.2—S catalyst and the 1 wt % Ag-1 wt % Ga/HZSM-5(23:1) catalyst were added and mechanical mixing was practiced. The reaction was carried out under 400° C. and a gas atmosphere of 32 atm CH.sub.4 and 3 atm N.sub.2. The weight ratio of DBT to each catalyst was 5:1 and the reaction lasted 1 hour. The gas product was collected in air bags, and the soluble product was extracted by solvent 1,1,2,2-tetrachloroethane and separated from the solid product through filtration. DBT conversion, methane conversion, gas yield, soluble yield, coke yield and overall mass balance were measured and listed in Table 1. Besides, the composition of gas products is listed in Table 2. Moreover, soluble products were also analyzed and the product distribution is listed in Table 3.

Example 12

(51) 10 wt % Mo-1.25 wt % Ni—TiO.sub.2—S catalyst (MDS1) was prepared in the following manner. A TiO.sub.2 (P25, average particle size 21 nm) support structure in powder form obtained from Sigma-Aldrich was used without further treatment. The metal salts nickel nitrate (Ni(NO.sub.3).sub.2.6H.sub.2O) and ammonium tetrathiomolybdate ((NH.sub.4).sub.2MoS.sub.4) was dissolved in deionized water to form a precursor solution. The TiO.sub.2 support was impregnated with the metal precursor solution to achieve a suitable metal weight loading. The obtained wet powder was first dried in an oven at 100° C. overnight, followed by calcination at 350° C. in a nitrogen atmosphere for 2 hours with a nitrogen flow rate of 100 mL/min.

(52) 1 wt % Ag-5 wt % Ce/HZSM-5(23:1) catalyst (MAC4) was prepared in the following manner. An NH.sub.4-ZSM-5 (SiO.sub.2:Al.sub.2O.sub.3 molar ratio of 23:1) support structure in powder form obtained from Zeolyst USA was calcined in static air at 600° C. for 3 hours. The following metal salts were dissolved in deionized water to form a metal precursor solution: Ce(NO.sub.3).sub.3.6H.sub.2O and AgNO.sub.3. The HZSM-5 support was impregnated with the metal precursor solution to achieve a suitable metal weight loading. The obtained wet powder was first dried in an oven at 100° C. overnight, followed by calcination at 550° C. for 4 hours in static air.

(53) 1 g dibenzothiophene (DBT), which is a model compound representing thiophenic sulfur species in diesel oil, was put in a 100 mL batch reactor. The 10 wt % Mo-1.25 wt % Ni—TiO.sub.2—S catalyst and the 1 wt % Ag-5 wt % Ce/HZSM-5(23:1) catalyst were added and mechanical mixing was practiced. The reaction was carried out under 400° C. and a gas atmosphere of 32 atm CH.sub.4 and 3 atm N.sub.2. The weight ratio of DBT to each catalyst was 5:1 and the reaction lasted 1 hour. The gas product was collected in air bags, and the soluble product was extracted by solvent 1,1,2,2-tetrachloroethane and separated from the solid product through filtration. DBT conversion, methane conversion, gas yield, soluble yield, coke yield and overall mass balance were measured and listed in Table 1. Besides, the composition of gas products is listed in Table 2. Moreover, soluble products were also analyzed and the product distribution is listed in Table 3.

Example 13

(54) 10 wt % Mo-1.25 wt % Ni—TiO.sub.2—S catalyst (MDS1) was prepared in the following manner. A TiO.sub.2 (P25, average particle size 21 nm) support structure in powder form obtained from Sigma-Aldrich was used without further treatment. The metal salts nickel nitrate (Ni(NO.sub.3).sub.2.6H.sub.2O) and ammonium tetrathiomolybdate ((NH.sub.4).sub.2MoS.sub.4) was dissolved in deionized water to form a precursor solution. The TiO.sub.2 support was impregnated with the metal precursor solution to achieve a suitable metal weight loading. The obtained wet powder was first dried in an oven at 100° C. overnight, followed by calcination at 350° C. in a nitrogen atmosphere for 2 hours with a nitrogen flow rate of 100 mL/min.

(55) 1 wt % Ag-1 wt % Ga-5 wt % Ce/HZSM-5(23:1) catalyst (MAC1) was prepared in the following manner. An NH.sub.4-ZSM-5 (SiO.sub.2:Al.sub.2O.sub.3 molar ratio of 23:1) support structure in powder form obtained from Zeolyst USA was calcined in static air at 600° C. for 3 hours. The following metal salts were dissolved in deionized water to form a metal precursor solution: Ce(NO.sub.3).sub.3.6H.sub.2O, Ga(NO.sub.3).sub.3.9H.sub.2O and AgNO.sub.3. The HZSM-5 support was impregnated with the metal precursor solution to achieve a suitable metal weight loading. The obtained wet powder was first dried in an oven at 100° C. overnight, followed by calcination at 550° C. for 4 hours in static air.

(56) 1 g 4-methyldibenzothiophene (4-mDBT), which is a model compound representing thiophenic sulfur species in diesel oil, was put in a 100 mL batch reactor. The 10 wt % Mo-1.25 wt % Ni—TiO.sub.2—S catalyst and the 1 wt % Ag-1 wt % Ga-5 wt % Ce/HZSM-5(23:1) catalyst were added and mechanical mixing was practiced. The reaction was carried out under 400° C. and a gas atmosphere of 32 atm CH.sub.4 and 3 atm N.sub.2. The weight ratio of 4-mDBT to each catalyst was 5:1 and the reaction lasted 1 hour. The gas product was collected in air bags, and the soluble product was extracted by solvent 1,1,2,2-tetrachloroethane and separated from the solid product through filtration. DBT conversion, methane conversion, gas yield, soluble yield, coke yield and overall mass balance were measured and listed in Table 1. Besides, the composition of gas products is listed in Table 2. Moreover, soluble products were also analyzed and the product distribution is listed in Table 3.

Example 14

(57) 10 wt % Mo-1.25 wt % Ni—TiO.sub.2—S catalyst (MDS1) was prepared in the following manner. A TiO.sub.2 (P25, average particle size 21 nm) support structure in powder form obtained from Sigma-Aldrich was used without further treatment. The metal salts nickel nitrate (Ni(NO.sub.3).sub.2.6H.sub.2O) and ammonium tetrathiomolybdate ((NH.sub.4).sub.2MoS.sub.4) was dissolved in deionized water to form a precursor solution. The TiO.sub.2 support was impregnated with the metal precursor solution to achieve a suitable metal weight loading. The obtained wet powder was first dried in an oven at 100° C. overnight, followed by calcination at 350° C. in a nitrogen atmosphere for 2 hours with a nitrogen flow rate of 100 mL/min.

(58) 1 wt % Ag-1 wt % Ga-5 wt % Ce/HZSM-5(23:1) catalyst (MAC1) was prepared in the following manner. An NH.sub.4-ZSM-5 (SiO.sub.2:Al.sub.2O.sub.3 molar ratio of 23:1) support structure in powder form obtained from Zeolyst USA was calcined in static air at 600° C. for 3 hours. The following metal salts were dissolved in deionized water to form a metal precursor solution: Ce(NO.sub.3).sub.3.6H.sub.2O, Ga(NO.sub.3).sub.3.9H.sub.2O and AgNO.sub.3. The HZSM-5 support was impregnated with the metal precursor solution to achieve a suitable metal weight loading. The obtained wet powder was first dried in an oven at 100° C. overnight, followed by calcination at 550° C. for 4 hours in static air.

(59) 1 g 4,6-dimethyldibenzothiophene (4,6-dmDBT), which is a model compound representing thiophenic sulfur species in diesel oil, was put in a 100 mL batch reactor. The 10 wt % Mo-1.25 wt % Ni—TiO.sub.2—S catalyst and the 1 wt % Ag-1 wt % Ga-5 wt % Ce/HZSM-5(23:1) catalyst were added and mechanical mixing was practiced. The reaction was carried out under 400° C. and a gas atmosphere of 32 atm CH.sub.4 and 3 atm N.sub.2. The weight ratio of 4,6-dmDBT to each catalyst was 5:1 and the reaction lasted 1 hour. The gas product was collected in air bags, and the soluble product was extracted by solvent 1,1,2,2-tetrachloroethane and separated from the solid product through filtration. DBT conversion, methane conversion, gas yield, soluble yield, coke yield and overall mass balance were measured and listed in Table 1. Besides, the composition of gas products is listed in Table 2. Moreover, soluble products were also analyzed and the product distribution is listed in Table 3.

(60) TABLE-US-00001 TABLE 1 Overall analysis results in Example 1-14 Overall Gas Soluble Coke mass DBT yield yield yield balance Example Catalyst Gas conv. (%) (wt %) (wt %) (wt %) (%)  1 MDS1 32 bar CH.sub.4, 1.4 ± 0.6 2 ± 5 97 ± 5  1.3 ± 0.2 100 ± 5   3 bar N.sub.2  2 MAC1 32 bar CH.sub.4, 6.5 ± 0.6 7 ± 5 90 ± 5  2.1 ± 0.2 99 ± 5  3 bar N.sub.2  3 MDSl + MAC1 32 bar CH.sub.4, 14.0 ± 0.6  2 ± 5 92 ± 5  4.8 ± 0.2 99 ± 5  3 bar N.sub.2  4 MDS1 + MAC1 35 bar N.sub.2 8.3 ± 0.6 3 ± 5 94 ± 5  3.3 ± 0.2 100 ± 5    5 SiC 32 bar CH.sub.4, 0.0 ± 0.6 1 ± 5 96 ± 5  0.0 ± 0.1 97 ± 5  3 bar N.sub.2  6 MDS1-O + MAC1 32 bar CH.sub.4, 5.1 ± 0.6 8 ± 5 89 ± 5  2.8 ± 0.2 100 ± 5   3 bar N.sub.2  7 MDS2 + MAC1 32 bar CH.sub.4, 9.2 ± 0.6 6 ± 5 90 ± 5  2.3 ± 0.2 98 ± 5  3 bar N.sub.2  8 MDS3 + MAC1 32 bar CH.sub.4, 26.6 ± 0.6  2 ± 5 95 ± 5  2.5 ± 0.2 100 ± 5   3 bar N.sub.2  9 MDS4 + MAC1 32 bar CH.sub.4, 10.8 ± 0.6  2 ± 5 95 ± 5  3.0 ± 0.2 100 ± 5   3 bar N.sub.2 10 MDS1 + MAC2 32 bar CH.sub.4, 14.1 ± 0.6  3 ± 5 96 ± 5  3.5 ± 0.2 100 ± 5   3 bar N.sub.2 11 MDS1 + MAC3 32 bar CH.sub.4, 13.5 ± 0.6  0 ± 5 94 ± 5  4.1 ± 0.2 98 ± 5  3 bar N.sub.2 12 MDS1 + MAC4 32 bar CH.sub.4, 9.0 ± 0.6 4 ± 5 96 ± 5  2.4 ± 0.2 98 ± 5  3 bar N.sub.2 13 MDSl + MAC1 32 bar CH.sub.4, 6.9 ± 1.0 1 ± 5 92 ± 10 6.7 ± 0.2 100 ± 5   3 bar N.sub.2 (4-mDBT) MDS1 + MAC1 32 bar CH.sub.4, 5.5 ± 1.5 30 ± 50 46 ± 50 9.5 ± 2   95 ± 50 14 3 bar N.sub.2 (4,6-dmDBT)

(61) TABLE-US-00002 TABLE 2 Gas analysis of products in Example 1-14 CH.sub.4 CS.sub.2 Ex- conv. H.sub.2 yield C2 yield yield ample Catalyst Gas (wt %) (wt %) (wt %) (wt %)  1 MDS1 32 bar CH.sub.4, 1.0 ± 1.0 0.07 ± 0.05 0 0 3 bar N.sub.2  2 MAC1 32 bar CH.sub.4, 2.2 ± 1.0 0.10 ± 0.01 6.8 ± 1.0 0 3 bar N.sub.2  3 MDS1 + 32 bar CH.sub.4, 1.4 ± 1.0 0.10 ± 0.03 1.1 ± 0.2 0 MAC1 3 bar N.sub.2  4 MDS1 + 35 bar N.sub.2 N.A. 0.05 ± 0.04 0 0 MAC1  5 SiC 32 bar CH.sub.4, 0.8 ± 1.0 0.06 ± 0.04 0 0 3 bar N.sub.2  6 MDS1- 32 bar CH.sub.4, 2.4 ± 1.0 0.10 ± 0.01 6.2 ± 2.7 0 O + MAC1 3 bar N.sub.2  7 MDS2 + 32 bar CH.sub.4, 1.4 ± 1.0 0.21 ± 0.05 2.3 ± 0.4 0 MAC1 3 bar N.sub.2  8 MDS3 + 32 bar CH.sub.4, 2.0 ± 1.0 0.24 ± 0.06 1.6 ± 0.3 0 MAC1 3 bar N.sub.2  9 MDS4 + 32 bar CH.sub.4, 0.6 ± 1.0 0.09 ± 0.02 1.1 ± 0.2 0 MAC1 3 bar N.sub.2 10 MDS1 + 32 bar CH.sub.4, 1.6 ± 1.0 0.09 ± 0.01 1.0 ± 0.2 0 MAC2 3 bar N.sub.2 11 MDS1 + 32 bar CH.sub.4, 1.9 ± 1.0 0.10 ± 0.02 0.8 ± 0.2 0 MAC3 3 bar N.sub.2 12 MDS1 + 32 bar CH.sub.4, 0.1 ± 1.0 0.09 ± 0.02 0.3 ± 0.2 0 MAC4 3 bar N.sub.2 13 MDS1 + 32 bar CH.sub.4, 1.2 ± 1.0 0.17 ± 0.05 0.7 ± 0.2 0 MAC1 3 bar N.sub.2 14 MDS1 + 32 bar CH.sub.4, 0.9 ± 1.0 0.05 ± 0.02 0.9 ± 0.2 0 MAC1 3 bar N.sub.2

(62) TABLE-US-00003 TABLE 3 Product yield distribution in Example 1-14, unit: wt % Bi Other High b.p. Example C2 CS.sub.2 Benzene Toluene Xylene phenyl aromatics solubles Coke Total  1 0 0 0 0.2 0 0 0 2.9 1.3 4.4  2 6.8 0 0.5 0.2 0 0 1.6 4.0 2.1 15.2  3 1.1 0.5 0.5 1.2 0.6 1.7 1.1 4.6 4.8 16.1  4 0 0 0.2 0.1 0 0 0.2 5.4 3.3 9.2  5 0 0 0 0 0 0 0 0 0 0  6 6.2 0 0.1 0.1 0 0.1 0.5 4.0 2.8 13.8  7 2.3 0.24 0.3 0.6 0.4 1.6 1.0 4.9 2.3 13.6  8 1.6 Trace 1.4 3.8 1.6 7.0 5.5 7.1 2.5 30.5  9 1.1 0.09 0.3 0.7 0.4 1.2 0.8 6.0 3.0 13.6 10 1.0 0.001 0.4 0.6 0.4 1.6 0.8 5.0 3.5 13.3 11 0.8 Trace 0.2 0.6 0.3 1.4 1.3 4.9 4.1 13.6 12 0.3 0 0 0.1 0 0.1 0.2 4.8 2.4 7.9 13 0.7 0.02 0.2 0.3 0.2 0.2 0.8 5.0 6.7 14.1 14 0.9 0 0.2 0.3 0.2 0.04 0.1 5.1 9.5 16.3

(63) As indicated by the data provided in Tables 1, 2 and 3 (based upon Examples 1-14), the use of MDS catalyst structures (comprising Mo and Ni loaded in a TiSO.sub.2—S support structure), MAC catalyst structures (comprising two or more of Ag, Ga and Ce loaded in an HZSM-5 support structure), and further combinations of MDS with MAC catalyst structures, provides effective DBT conversion as well as effective production of BTX and/or other desirable aromatic compounds, clearly indicating the effectiveness of such catalyst structures in the desulfurization of light oils and upgrading conversion into desirable end products.

Example 15

(64) 1 wt % Ag-1 wt % Ga-10 wt % Mo/HZSM-5(23:1) catalyst was prepared in the following manner. An NH.sub.4-ZSM-5 (SiO.sub.2:Al.sub.2O.sub.3 molar ratio of 23:1) support structure in powder form obtained from Zeolyst USA was calcined in static air at 600° C. for 3 hours. The following metal salts were dissolved in deionized water to form a metal precursor solution: AgNO.sub.3, Ga(NO.sub.3).sub.3.9H.sub.2O and ((NH.sub.4).sub.6Mo.sub.7O.sub.24.4H.sub.2O. The HZSM-5 support was impregnated with the metal precursor solution to achieve a suitable metal weight loading. The obtained wet powder was first dried in an oven at 100° C. overnight, followed by calcination at 550° C. for 4 hours in static air.

(65) 1 g 1 wt % Ag-1 wt % Ga-10 wt % Mo/HZSM-5(23:1) catalyst was put in a 300 mL batch reactor together with 50 g marine diesel oil with continuous mechanical mixing. The reaction was carried out under 400° C. and a gas atmosphere of 30 atm CH.sub.4 and 5 atm N.sub.2. The weight ratio of feed to catalyst was 50:1 and the reaction lasted 1 hour. The liquid product was collected and liquid yield was calculated based on the feed. Meanwhile, the sulfur content in the liquid product was measured and the sulfur removal rate was calculated. The results were listed in Table 4.

Example 16

(66) Shaped catalyst with the formula of 1 wt % Ag-1 wt % Ga-10 wt % Mo/HZSM-5(23:1) was prepared in the following manner. First, an NH.sub.4-ZSM-5 (SiO.sub.2:Al.sub.2O.sub.3 molar ratio of 23:1) support structure in powder form obtained from Zeolyst USA was calcined in static air at 600° C. for 3 hours. The zeolite was then extruded into pellet form with the following recipe: catalyst:colloidal silica:methylcellulose:acetic acid solution=1:0.5:0.2:0.1. After all components were added and suitably mixed, the extrusion was conducted with an extruder at room temperature. After extrusion, the wet catalyst pellets were dried at 95° C. overnight (e.g., about 8-12 hours), followed by calcination at 300° C. for 12 hours. The following metal salts were dissolved in deionized water to form a metal precursor solution: AgNO.sub.3, Ga(NO.sub.3).sub.3.9H.sub.2O and ((NH.sub.4).sub.6Mo.sub.7O.sub.24.4H.sub.2O. The HZSM-5 support was impregnated with the metal precursor solution to achieve a suitable metal weight loading. The obtained wet powder was first dried in an oven at 100° C. overnight, followed by calcination at 550° C. for 4 hours in static air.

(67) 5 mL 1 wt % Ag-1 wt % Ga-10 wt % Mo/HZSM-5(23:1) catalyst was put in a small fixed bed reactor and marine diesel oil was used as the feed. The reaction was carried out under 400° C. and a gas atmosphere of 30 atm CH.sub.4 and 5 atm N.sub.2. The LHSV was controlled to be 1 h.sup.−1 and the time on stream was set to be 6 h. After the reactor, the liquid product was collected and liquid yield was calculated based on the feed. Meanwhile, the sulfur content in the liquid product was measured and the sulfur removal rate was calculated. The results were listed in Table 4.

Example 17

(68) 1 wt % Ag-1 wt % Ga-10 wt % Mo/HZSM-5(23:1) catalyst was prepared in the following manner. An NH.sub.4-ZSM-5 (SiO.sub.2:Al.sub.2O.sub.3 molar ratio of 23:1) support structure in powder form obtained from Zeolyst USA was calcined in static air at 600° C. for 3 hours. The following metal salts were dissolved in deionized water to form a metal precursor solution: AgNO.sub.3, Ga(NO.sub.3).sub.3.9H.sub.2O and ((NH.sub.4).sub.6Mo.sub.7O.sub.24.4H.sub.2O. The HZSM-5 support was impregnated with the metal precursor solution to achieve a suitable metal weight loading. The obtained wet powder was first dried in an oven at 100° C. overnight, followed by calcination at 550° C. for 4 hours in static air.

(69) 1 g catalyst was put in a 300 mL batch reactor together with 50 g marine diesel oil with continuous mechanical mixing. The reaction was carried out under 350° C. and a gas atmosphere of 50 atm natural gas. The weight ratio of feed to catalyst was 1:10 and the reaction lasted 1 hour. The liquid product was collected and liquid yield was calculated based on the feed. Meanwhile, the sulfur content in the liquid product was measured and the sulfur removal rate was calculated. The results were listed in Table 4.

Example 18

(70) 1 wt % Ag-1 wt % Ga-10 wt % Mo/HZSM-5(23:1) catalyst was prepared in the following manner. An NH.sub.4-ZSM-5 (SiO.sub.2:Al.sub.2O.sub.3 molar ratio of 23:1) support structure in powder form obtained from Zeolyst USA was calcined in static air at 600° C. for 3 hours. The following metal salts were dissolved in deionized water to form a metal precursor solution: AgNO.sub.3, Ga(NO.sub.3).sub.3.9H.sub.2O and ((NH.sub.4).sub.6Mo.sub.7O.sub.24.4H.sub.2O. The HZSM-5 support was impregnated with the metal precursor solution to achieve a suitable metal weight loading. The obtained wet powder was first dried in an oven at 100° C. overnight, followed by calcination at 550° C. for 4 hours in static air.

(71) 1 g catalyst was put in a 300 mL batch reactor together with 50 g marine diesel oil with continuous mechanical mixing. The reaction was carried out under 450° C. and a gas atmosphere of 1 atm natural gas. The weight ratio of feed to catalyst was 50:1 and the reaction lasted 1 hour. The liquid product was collected and liquid yield was calculated based on the feed. Meanwhile, the sulfur content in the liquid product was measured and the sulfur removal rate was calculated. The results were listed in Table 4.

Example 19

(72) Shaped catalyst with the formula of 1 wt % Ag-1 wt % Ga-10 wt % Mo/HZSM-5(23:1) was prepared in the following manner. First, an NH.sub.4-ZSM-5 (SiO.sub.2:Al.sub.2O.sub.3 molar ratio of 23:1) support structure in powder form obtained from Zeolyst USA was calcined in static air at 600° C. for 3 hours. The zeolite was then extruded into pellet form with the following recipe: catalyst:colloidal silica:methylcellulose:acetic acid solution=1:0.5:0.2:0.1. After all components were added and suitably mixed, the extrusion was conducted with an extruder at room temperature. After extrusion, the wet catalyst pellets were dried at 95° C. overnight (e.g., about 8-12 hours), followed by calcination at 300° C. for 12 hours. The following metal salts were dissolved in deionized water to form a metal precursor solution: AgNO.sub.3, Ga(NO.sub.3).sub.3.9H.sub.2O and ((NH.sub.4).sub.6Mo.sub.7O.sub.24.4H.sub.2O. The HZSM-5 support was impregnated with the metal precursor solution to achieve a suitable metal weight loading. The obtained wet powder was first dried in an oven at 100° C. overnight, followed by calcination at 550° C. for 4 hours in static air.

(73) 5 mL catalyst was put in a small fixed bed reactor and FCC diesel oil was used as the feed. The reaction was carried out under 400° C. and a gas atmosphere of 30 atm CH.sub.4 and 5 atm N.sub.2. The LHSV was controlled to be 0.1 h.sup.−1 and the time on stream was set to be 6 h. After the reactor, the liquid product was collected and liquid yield was calculated based on the feed. Meanwhile, the sulfur content in the liquid product was measured and the sulfur removal rate was calculated. The results were listed in Table 4.

Example 20

(74) Shaped catalyst with the formula of 1 wt % Ag-1 wt % Ga-10 wt % Mo/HZSM-5(23:1) was prepared in the following manner. First, an NH.sub.4-ZSM-5 (SiO.sub.2:Al.sub.2O.sub.3 molar ratio of 23:1) support structure in powder form obtained from Zeolyst USA was calcined in static air at 600° C. for 3 hours. The zeolite was then extruded into pellet form with the following recipe: catalyst:colloidal silica:methylcellulose:acetic acid solution=1:0.5:0.2:0.1. After all components were added and suitably mixed, the extrusion was conducted with an extruder at room temperature. After extrusion, the wet catalyst pellets were dried at 95° C. overnight (e.g., about 8-12 hours), followed by calcination at 300° C. for 12 hours. The following metal salts were dissolved in deionized water to form a metal precursor solution: AgNO.sub.3, Ga(NO.sub.3).sub.3.9H.sub.2O and ((NH.sub.4).sub.6Mo.sub.7O.sub.24.4H.sub.2O. The HZSM-5 support was impregnated with the metal precursor solution to achieve a suitable metal weight loading. The obtained wet powder was first dried in an oven at 100° C. overnight, followed by calcination at 550° C. for 4 hours in static air.

(75) 5 mL catalyst was put in a small fixed bed reactor and FCC gasoline oil was used as the feed. The reaction was carried out under 400° C. and a gas atmosphere of 30 atm CH.sub.4 and 5 atm N.sub.2. The LHSV was controlled to be 10 h.sup.−1 and the time on stream was set to be 6 h. After the reactor, the liquid product was collected and liquid yield was calculated based on the feed. Meanwhile, the sulfur content in the liquid product was measured and the sulfur removal rate was calculated. The results were listed in Table 4.

Example 21

(76) 10 wt % Mo-1.25 wt % Ni—TiO.sub.2—S catalyst (MDS1) was prepared in the following manner. A TiO.sub.2 (P25, average particle size 21 nm) support structure in powder form obtained from Sigma-Aldrich was used without further treatment. The metal salts nickel nitrate (Ni(NO.sub.3).sub.2.6H.sub.2O) and ammonium tetrathiomolybdate ((NH.sub.4).sub.2MoS.sub.4) was dissolved in deionized water to form a precursor solution. The TiO.sub.2 support was impregnated with the metal precursor solution to achieve a suitable metal weight loading. The obtained wet powder was first dried in an oven at 100° C. overnight, followed by calcination at 350° C. in a nitrogen atmosphere for 2 hours with a nitrogen flow rate of 100 mL/min.

(77) 1 wt % Ag-1 wt % Ga-5 wt % Ce/HZSM-5(23:1) (MAC1) catalyst was prepared in the following manner. An NH.sub.4-ZSM-5 (SiO.sub.2:Al.sub.2O.sub.3 molar ratio of 23:1) support structure in powder form obtained from Zeolyst USA was calcined in static air at 600° C. for 3 hours. The following metal salts were dissolved in deionized water to form a metal precursor solution: Ce(NO.sub.3).sub.3.6H.sub.2O, Ga(NO.sub.3).sub.3.9H.sub.2O and AgNO.sub.3. The HZSM-5 support was impregnated with the metal precursor solution to achieve a suitable metal weight loading. The obtained wet powder was first dried in an oven at 100° C. overnight, followed by calcination at 550° C. for 4 hours in static air.

(78) 0.2 g MDS1 catalyst and 0.2 g MAC1 catalyst were put in a 100 mL batch reactor together with 2 g marine diesel oil. The reaction was carried out under 400° C. with continuous mechanical mixing and a gas atmosphere of 30 atm CH.sub.4 and 5 atm N.sub.2. The weight ratio of feed to catalyst was 10:1 and the reaction lasted 1 hour. The liquid product was collected and liquid yield was calculated based on the feed. Meanwhile, the sulfur content in the liquid product was measured and the sulfur removal rate was calculated. The results were listed in Table 4.

Example 22

(79) 10 wt % Mo-1.25 wt % Ni—TiO.sub.2—S catalyst (MDS1) was prepared in the following manner. A TiO.sub.2 (P25, average particle size 21 nm) support structure in powder form obtained from Sigma-Aldrich was used without further treatment. The metal salts nickel nitrate (Ni(NO.sub.3).sub.2.6H.sub.2O) and ammonium tetrathiomolybdate ((NH.sub.4).sub.2MoS.sub.4) was dissolved in deionized water to form a precursor solution. The TiO.sub.2 support was impregnated with the metal precursor solution to achieve a suitable metal weight loading. The obtained wet powder was first dried in an oven at 100° C. overnight, followed by calcination at 350° C. in a nitrogen atmosphere for 2 hours with a nitrogen flow rate of 100 mL/min.

(80) 1 wt % Ag-1 wt % Ga-5 wt % Ce/HZSM-5(23:1) (MAC1) catalyst was prepared in the following manner. An NH.sub.4-ZSM-5 (SiO.sub.2:Al.sub.2O.sub.3 molar ratio of 23:1) support structure in powder form obtained from Zeolyst USA was calcined in static air at 600° C. for 3 hours. The following metal salts were dissolved in deionized water to form a metal precursor solution: Ce(NO.sub.3).sub.3.6H.sub.2O, Ga(NO.sub.3).sub.3.9H.sub.2O and AgNO.sub.3. The HZSM-5 support was impregnated with the metal precursor solution to achieve a suitable metal weight loading. The obtained wet powder was first dried in an oven at 100° C. overnight, followed by calcination at 550° C. for 4 hours in static air.

(81) 0.2 g MDS1 catalyst and 0.2 g MAC1 catalyst were put in a 100 mL batch reactor together with 2 g renewable diesel oil. The reaction was carried out under 400° C. with continuous mechanical mixing and a gas atmosphere of 30 atm CH.sub.4 and 5 atm N.sub.2. The weight ratio of feed to catalyst was 10:1 and the reaction lasted 1 hour. The liquid product was collected and liquid yield was calculated based on the feed. Meanwhile, the sulfur content in the liquid product was measured and the sulfur removal rate was calculated. The results were listed in Table 4.

Example 23

(82) 10 wt % Mo-1.25 wt % Ni—TiO.sub.2—S catalyst (MDS1) was prepared in the following manner. A TiO.sub.2 (P25, average particle size 21 nm) support structure in powder form obtained from Sigma-Aldrich was used without further treatment. The metal salts nickel nitrate (Ni(NO.sub.3).sub.2.6H.sub.2O) and ammonium tetrathiomolybdate ((NH.sub.4).sub.2MoS.sub.4) was dissolved in deionized water to form a precursor solution. The TiO.sub.2 support was impregnated with the metal precursor solution to achieve a suitable metal weight loading. The obtained wet powder was first dried in an oven at 100° C. overnight, followed by calcination at 350° C. in a nitrogen atmosphere for 2 hours with a nitrogen flow rate of 100 mL/min.

(83) 1 wt % Ag-1 wt % Ga-5 wt % Ce/HZSM-5(23:1) (MAC1) catalyst was prepared in the following manner. An NH.sub.4-ZSM-5 (SiO.sub.2:Al.sub.2O.sub.3 molar ratio of 23:1) support structure in powder form obtained from Zeolyst USA was calcined in static air at 600° C. for 3 hours. The following metal salts were dissolved in deionized water to form a metal precursor solution: Ce(NO.sub.3).sub.3.6H.sub.2O, Ga(NO.sub.3).sub.3.9H.sub.2O and AgNO.sub.3. The HZSM-5 support was impregnated with the metal precursor solution to achieve a suitable metal weight loading. The obtained wet powder was first dried in an oven at 100° C. overnight, followed by calcination at 550° C. for 4 hours in static air.

(84) 0.2 g MDS1 catalyst and 0.2 g MAC1 catalyst were put in a 100 mL batch reactor together with 2 g heavy crude oil. The reaction was carried out under 400° C. with continuous mechanical mixing and a gas atmosphere of 30 atm CH.sub.4 and 5 atm N.sub.2. The weight ratio of feed to catalyst was 10:1 and the reaction lasted 1 hour. The liquid product was collected and liquid yield was calculated based on the feed. Meanwhile, the sulfur content in the liquid product was measured and the sulfur removal rate was calculated. The results were listed in Table 4.

Example 24

(85) 10 wt % Mo-1.25 wt % Ni—TiO.sub.2—S catalyst (MDS1) was prepared in the following manner. A TiO.sub.2 (P25, average particle size 21 nm) support structure in powder form obtained from Sigma-Aldrich was used without further treatment. The metal salts nickel nitrate (Ni(NO.sub.3).sub.2.6H.sub.2O) and ammonium tetrathiomolybdate ((NH.sub.4).sub.2MoS.sub.4) was dissolved in deionized water to form a precursor solution. The TiO.sub.2 support was impregnated with the metal precursor solution to achieve a suitable metal weight loading. The obtained wet powder was first dried in an oven at 100° C. overnight, followed by calcination at 350° C. in a nitrogen atmosphere for 2 hours with a nitrogen flow rate of 100 mL/min.

(86) 1 wt % Ag-1 wt % Ga-5 wt % Ce/HZSM-5(23:1) (MAC1) catalyst was prepared in the following manner. An NH.sub.4-ZSM-5 (SiO.sub.2:Al.sub.2O.sub.3 molar ratio of 23:1) support structure in powder form obtained from Zeolyst USA was calcined in static air at 600° C. for 3 hours. The following metal salts were dissolved in deionized water to form a metal precursor solution: Ce(NO.sub.3).sub.3.6H.sub.2O, Ga(NO.sub.3).sub.3.9H.sub.2O and AgNO.sub.3. The HZSM-5 support was impregnated with the metal precursor solution to achieve a suitable metal weight loading. The obtained wet powder was first dried in an oven at 100° C. overnight, followed by calcination at 550° C. for 4 hours in static air.

(87) 0.2 g MDS1 catalyst and 0.2 g MAC1 catalyst were put in a 100 mL batch reactor together with 2 g coker naphtha. The reaction was carried out under 400° C. with continuous mechanical mixing and a gas atmosphere of 30 atm CH.sub.4 and 5 atm N.sub.2. The weight ratio of feed to catalyst was 10:1 and the reaction lasted 1 hour. The liquid product was collected and liquid yield was calculated based on the feed. Meanwhile, the sulfur content in the liquid product was measured and the sulfur removal rate was calculated. The results were listed in Table 4.

Example 25

(88) 10 wt % Mo-1.25 wt % Ni—TiO.sub.2—S catalyst (MDS1) was prepared in the following manner. A TiO.sub.2 (P25, average particle size 21 nm) support structure in powder form obtained from Sigma-Aldrich was used without further treatment. The metal salts nickel nitrate (Ni(NO.sub.3).sub.2.6H.sub.2O) and ammonium tetrathiomolybdate ((NH.sub.4).sub.2MoS.sub.4) was dissolved in deionized water to form a precursor solution. The TiO.sub.2 support was impregnated with the metal precursor solution to achieve a suitable metal weight loading. The obtained wet powder was first dried in an oven at 100° C. overnight, followed by calcination at 350° C. in a nitrogen atmosphere for 2 hours with a nitrogen flow rate of 100 mL/min.

(89) 1 wt % Ag-1 wt % Ga-5 wt % Ce/HZSM-5(23:1) (MAC1) catalyst was prepared in the following manner. An NH.sub.4-ZSM-5 (SiO.sub.2:Al.sub.2O.sub.3 molar ratio of 23:1) support structure in powder form obtained from Zeolyst USA was calcined in static air at 600° C. for 3 hours. The following metal salts were dissolved in deionized water to form a metal precursor solution: Ce(NO.sub.3).sub.3.6H.sub.2O, Ga(NO.sub.3).sub.3.9H.sub.2O and AgNO.sub.3. The HZSM-5 support was impregnated with the metal precursor solution to achieve a suitable metal weight loading. The obtained wet powder was first dried in an oven at 100° C. overnight, followed by calcination at 550° C. for 4 hours in static air.

(90) 0.2 g MDS1 catalyst and 0.2 g MAC1 catalyst were put in a 100 mL batch reactor together with 2 g coker naphtha. The reaction was carried out under 400° C. with continuous mechanical mixing and a gas atmosphere of 35 atm N.sub.2. The weight ratio of feed to catalyst was 10:1 and the reaction lasted 1 hour. The liquid product was collected and liquid yield was calculated based on the feed. Meanwhile, the sulfur content in the liquid product was measured and the sulfur removal rate was calculated. The results were listed in Table 4.

Example 26

(91) A commercial silicon carbide (SiC) from Sigma-Aldrich with a specific surface area of 10 m.sup.2/g was used as the catalyst without further purification. 0.2 g SiC catalyst was put in a 100 mL batch reactor together with 2 g coker naphtha. The reaction was carried out under 400° C. with continuous mechanical mixing and a gas atmosphere of 30 atm CH.sub.4 and 5 atm N.sub.2. The weight ratio of feed to catalyst was 10:1 and the reaction lasted 1 hour. The liquid product was collected and liquid yield was calculated based on the feed. Meanwhile, the sulfur content in the liquid product was measured and the sulfur removal rate was calculated. The results were listed in Table 4.

Example 27

(92) 10 wt % Mo-1.25 wt % Ni—TiO.sub.2—S catalyst (MDS1) was prepared in the following manner. A TiO.sub.2 (P25, average particle size 21 nm) support structure in powder form obtained from Sigma-Aldrich was used without further treatment. The metal salts nickel nitrate (Ni(NO.sub.3).sub.2.6H.sub.2O) and ammonium tetrathiomolybdate ((NH.sub.4).sub.2MoS.sub.4) was dissolved in deionized water to form a precursor solution. The TiO.sub.2 support was impregnated with the metal precursor solution to achieve a suitable metal weight loading. The obtained wet powder was first dried in an oven at 100° C. overnight, followed by calcination at 350° C. in a nitrogen atmosphere for 2 hours with a nitrogen flow rate of 100 mL/min.

(93) 1 wt % Ag-1 wt % Ga-5 wt % Ce/HZSM-5(23:1) (MAC1) catalyst was prepared in the following manner. An NH.sub.4-ZSM-5 (SiO.sub.2:Al.sub.2O.sub.3 molar ratio of 23:1) support structure in powder form obtained from Zeolyst USA was calcined in static air at 600° C. for 3 hours. The following metal salts were dissolved in deionized water to form a metal precursor solution: Ce(NO.sub.3).sub.3.6H.sub.2O, Ga(NO.sub.3).sub.3.9H.sub.2O and AgNO.sub.3. The HZSM-5 support was impregnated with the metal precursor solution to achieve a suitable metal weight loading. The obtained wet powder was first dried in an oven at 100° C. overnight, followed by calcination at 550° C. for 4 hours in static air.

(94) 2.1 mL MDS1 catalyst and 2.1 mL MAC1 catalyst were put in a fixed bed reactor and coker naphtha was used as the feed. The reaction was carried out under 400° C. and a gas atmosphere of 30 atm CH.sub.4 and 5 atm N.sub.2. The LHSV was controlled to be 1 h.sup.−1 and the time on stream was set to be 72 h. After the reactor, the liquid product was collected and liquid yield was calculated based on the feed. Meanwhile, the sulfur content in the liquid product was measured and the sulfur removal rate (removal degree, e.g., percentage of the amount of sulfur removed based upon the amount of sulfur in the original composition) was calculated. The results are listed in Table 4.

(95) TABLE-US-00004 TABLE 4 Overall analysis results in Example 15-27 Sulfur Liquid Gas removal yield Example Catalyst Feed Reactor atmosphere degree (%) (wt%) 15 1 wt % Ag-1 wt % Ga- Marine Batch 30 atm CH.sub.4 + 62 98 10 wt % Mo/ZSM-5 diesel oil 5 atm N.sub.2 16 1 wt % Ag-1 wt % Ga- Marine Fixed bed 30 atm CH.sub.4 + 78 96 10 wt % ± Mo/ZSM-5 diesel oil 5 atm N.sub.2 17 1 wt ± Ag-1 wt ± Ga- Marine Batch 50 atm natural 58 91 10 wt % ± Mo/ZSM-5 diesel oil gas 18 1 wt % ± Ag-1 wt % Ga- Marine Batch 1 atm natural 65 97 10 wt % ± Mo/ZSM-5 diesel oil gas 19 1 wt % Ag-1 wt % Ga- FCC diesel Fixed bed 30 atm CH.sub.4 + 74 91 10 wt ± Mo/Z S M-5 5 atm N.sub.2 20 1 wt % Ag-1 wt % Ga- FCC Fixed bed 30 atm CH.sub.4 + 52 94 10 wt ± Mo/ZSM-5 gasoline 5 atm N.sub.2 21 MDS1 + MAC1 Marine Batch 30 atm CH.sub.4 + 32 79 diesel oil 5 atm N.sub.2 22 MDS1 + MAC1 Renewable Batch 30 atm CH.sub.4 + 56 67 diesel oil 5 atm N.sub.2 23 MDS1 + MAC1 Heavy Batch 30 atm CH.sub.4 + 61 93 crude oil 5 atm N.sub.2 24 MDS1 + MAC1 Coker Batch 30 atm CH.sub.4 + 98 73 naphtha 5 atm N.sub.2 25 MDS1 + MAC1 Coker Batch 35 atm N.sub.2 87 70 naphtha 26 SiC Coker Batch 30 atm CH.sub.4 + 33 81 naphtha 5 atm N.sub.2 27 MDS1 + MAC1 Coker Fixed bed 30 atm CH.sub.4 + 60 60 naphtha 5 atm N.sub.2

(96) The data presented in Table 4 (based upon Examples 15-27) clearly shows the effectiveness of utilizing combinations of MDS and MAC catalyst structures or catalyst structures comprising Ag, Ga and Mo loaded in an HZSM-5 support structure with regard to desulfurization/sulfur removal from light oils.

(97) It is evident that the sulfur-containing species can be effectively converted to valuable products including benzene, xylene, toluene and other aromatics with the presence of methane environment and catalyst structure disclosed in the embodiments. In addition, a new sulfur-containing product CS.sub.2 can be formed, which is not observed in hydrodesulfurization processes. Therefore, the methods and catalyst structures described herein provide an alternative way for the oil desulfurization process, which is innovative and transformational in the petroleum industry.

(98) While the invention has been described in detail and with reference to specific embodiments thereof, it will be apparent to one skilled in the art that various changes and modifications can be made therein without departing from the spirit and scope thereof. Thus, it is intended that the present invention covers the modifications and variations of this invention provided they come within the scope of the appended claims and their equivalents.