High-strength and corrosion-resistant sucker rod and preparation process thereof

Abstract

A high-strength and corrosion-resistant sucker rod and a preparation process thereof are disclosed. Raw materials for preparing the high-strength and corrosion-resistant sucker rod include, by weight percent, Mn: 0.70% to 1.20%, Cr: 9.50% to 13.50%, Ni: 0.65% to 1.10%, Mo: 0.10% to 0.90%, Cu: 0.28% to 0.56%, C: ≤0.07%, Si: ≤0.50%, P: ≤0.08%, and S: ≤0.005%, the balance is Fe and unavoidable impurities. The sucker rod prepared by the new process has an actual grain size equal to or greater than grade 8, excellent mechanical properties that meet the standard of grade HL specified in SY/T5029 Sucker Rods, and excellent corrosion fatigue resistance. The preparation process is simple and easy for operation, and suitable for large-scale promotion.

Claims

1. A preparation process of a sucker rod, comprising the following steps: step S10; weighing raw materials for preparing the sucker rod according to a weight percentage, wherein the raw materials for preparing the sucker rod comprise: by weight percent, Mn: 0.80% to 1.00%, Cr: 11.00% to 12.50%, Ni: 0.70% to 1.00%, Mo: 0.25% to 0.65%, Cu: 0.30% to 0.50%, V: ≤0.50%, Nb: ≤0.30%, C: ≤0.07%, Si: ≤0.50%, P: ≤0.02%, S: ≤0.005%, and a balance is Fe and unavoidable impurities; A step S20: subjecting the raw materials for preparing the sucker rod with the weight percentage to a primary refining in an electric arc furnace to obtain a first refined product, followed by a second refining of the first refined product in an argon oxygen decarburization furnace to obtain a second refined product, a third refining on the second refined product outside a ladle furnace to obtain a third refined product, and casting the third refined product to obtain a steel ingot; step S30: first heating the steel ingot obtained in step S20 to 550° C. to 580° C., keeping the steel ingot at 550° C. to 580° C. for 40 minutes to 80 minutes, heating the steel ingot to 850° C. to 920° C., keeping the steel ingot at 850° C. to 920° C. for 50 minutes to 90 minutes, then heating the steel ingot to a final temperature of 1,160° C. to 1,200° C., and keeping the final temperature of the steel ingot for 1 hour to 2.5 hours to obtain a heated steel ingot, and then taking the heated steel ingot out from a heating furnace for a rolling to obtain a sucker rod bar, and step S40: putting the sucker rod bar obtained in step S30 into a sodium chloride aqueous solution with a concentration of 8 wt %-12 wt % for a quenching treatment to obtain a treated sucker rod bar, and then performing a tempering treatment on the treated sucker rod bar to obtain the sucker rod.

2. The preparation process according to claim 1, wherein in step S30, the final temperature is 1,170° C.

3. The preparation process according to claim 1, wherein in step S40, a quenching temperature of the quenching treatment is controlled to be 905° C.-918° C., and the quenching temperature is kept for 20 minutes to 40 minutes.

4. The preparation process according to claim 1, wherein in step S40, a tempering temperature of the tempering treatment is controlled to be 550° C.-595° C., and the tempering temperature is kept for 42 minutes to 52 minutes.

5. The preparation process according to claim 1, wherein the raw materials for preparing the sucker rod comprise: by weight percent, Mn: 0.90%, Cr: 12.00%, Ni: 0.85%, Mo: 0.35%, Cu: 0.40%, V: ≤0.32%, Nb: ≤0.25%, C: ≤0.07%, Si: ≤0.50%, P: ≤0.002%, S: ≤0.005%, and the balance is Fe and unavoidable impurities.

6. The preparation process according to claim 1, wherein the raw materials for preparing the sucker rod comprise: by weight percent, Mn: 0.85%, Cr: 11.80%, Ni: 0.90%, Mo: 0.35%, Cu: 0.35%, V: ≤0.20%, Nb: ≤0.12%, C: ≤0.07%, Si: ≤0.20%, P: ≤0.02%, S: ≤0.005%, and the balance is Fe and unavoidable impurities.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) The drawings constituting a part of the present specification for further understanding of the present invention show the implementation modes of the present invention, and are used together with the specification to illustrate the preparation process of the present invention. In the drawings:

(2) FIG. 1A is a diagram showing commercially available 1Cr13 steel before a hydrogen-induced cracking (HIC) experiment;

(3) FIG. 1B is a diagram showing commercially available 1Cr13 steel after the HIC experiment;

(4) FIG. 2A is a diagram showing the sucker rod prepared in embodiment 6 of the present invention before the HIC experiment;

(5) FIG. 2B is a diagram showing the sucker rod prepared in embodiment 6 of the present invention after the HIC experiment;

(6) FIG. 3 is a diagram showing a test surface of the commercially available 1Cr13 steel in the HIC experiment;

(7) FIG. 4 is a diagram showing a test surface of the sucker rod prepared in embodiment 6 of the present invention in the HIC experiment;

(8) FIG. 5A is a diagram showing an appearance of a corrosion inhibitor for an oilfield produced water treatment before a property testing to comparative example 1;

(9) FIG. 5B is a diagram showing an appearance of the corrosion inhibitor for the oilfield produced water treatment before the property testing to embodiment 6;

(10) FIG. 6A is a diagram showing an appearance of the corrosion inhibitor for the oilfield produced water treatment after the property testing to comparative example 1; and

(11) FIG. 6B is a diagram showing an appearance of the corrosion inhibitor for the oilfield produced water treatment after the property testing to embodiment 6.

DETAILED DESCRIPTION OF THE EMBODIMENTS

(12) The embodiments of the present invention are described in detail below with reference to the drawings, but the present invention can be implemented in a variety of different ways claimed and covered by the claims.

Embodiment 1

(13) High-Strength and Corrosion-Resistant Sucker Rod and Preparation Process Thereof.

(14) The raw materials for preparing the high-strength and corrosion-resistant sucker rod include: by weight percent, Mn: 0.70%, Cr: 11.00%, Ni: 1.00%, Mo: 0.90%, Cu: 0.30%, V: 0.50%, Nb: 0.30%, C: 0.07%, Si: 0.30%, P: 0.08%, S: 0.005%, and the balance is Fe and unavoidable impurities.

(15) The high-strength and corrosion-resistant sucker rod is prepared by the process as follows.

(16) Step S10, the raw materials of the high-strength and corrosion-resistant sucker rod are weighed according to the above-mentioned weight percentage.

(17) Step S20, the raw materials for preparing the high-strength and corrosion-resistant sucker rod with the above weight percentage is subjected to a primary refining in an electric arc furnace, followed by refining in an argon oxygen decarburization (AOD) furnace, and further refining outside a ladle furnace (LF), and then casting to obtain a steel ingot.

(18) Step S30, the steel ingot obtained in step S20 is first heated to 550° C. and kept for 50 minutes, heated to 900° C. and kept for 90 minutes, then heated to a final temperature of 1,160° C. and kept for 1 hour, and then the heated steel ingot is taken out of the furnace for rolling to obtain a high-strength sucker rod bar.

(19) Step S40: the high-strength sucker rod bar obtained in step S30 is put into a sodium chloride aqueous solution with a concentration of 9 wt % for a quenching treatment at 905° C. for 25 minutes, and then a tempering treatment is performed at 580° C. for 50 minutes to obtain the high-strength and corrosion-resistant sucker rod.

Embodiment 2

(20) High-Strength and Corrosion-Resistant Sucker Rod and Preparation Process Thereof.

(21) The raw materials for preparing the high-strength and corrosion-resistant sucker rod include: by weight percent, Mn: 0.80%, Cr: 12.50%, Ni: 0.65%, Mo: 0.35%, Cu: 0.56%, V: 0.40%, Nb: 0.18%, C: 0.06%, Si: 0.30%, P: 0.035%, S: 0.004%, and the balance is Fe and unavoidable impurities.

(22) The high-strength and corrosion-resistant sucker rod is prepared by the process as follows.

(23) Step S10, the raw materials of the high-strength and corrosion-resistant sucker rod are weighed according to the above-mentioned weight percentage.

(24) Step S20, the raw materials for preparing the high-strength and corrosion-resistant sucker rod with the above weight percentage is subjected to a primary refining in an electric arc furnace, followed by refining in an AOD furnace, and further refining outside a LF furnace, and then casting to obtain a steel ingot.

(25) Step S30, the steel ingot obtained in step S20 is first heated to 560° C. and kept for 40 minutes, heated to 920° C. and kept for 60 minutes, then heated to a final temperature of 1,170° C. and kept for 1.5 hours, and then the heated steel ingot is taken out of the furnace for rolling to obtain a high-strength sucker rod bar.

(26) Step S40: the high-strength sucker rod bar obtained in step S30 is put into a sodium chloride aqueous solution with a concentration of 8 wt % for a quenching treatment at 910° C. for 40 minutes, and then a tempering treatment is performed at 590° C. for 52 minutes to obtain the high-strength and corrosion-resistant sucker rod.

Embodiment 3

(27) High-Strength and Corrosion-Resistant Sucker Rod and Preparation Process Thereof.

(28) The raw materials for preparing the high-strength and corrosion-resistant sucker rod include: by weight percent, Mn: 1.20%, Cr: 9.50%, Ni: 0.70%, Mo: 0.65%, Cu: 0.28%, V: 0.15%, Nb: 0.10%, C: 0.06%, Si: 0.40%, P: 0.01%, S: 0.005%, and the balance is Fe and unavoidable impurities.

(29) The high-strength and corrosion-resistant sucker rod is prepared by the process as follows.

(30) Step S10, the raw materials of the high-strength and corrosion-resistant sucker rod are weighed according to the above-mentioned weight percentage.

(31) Step S20, the raw materials for preparing the high-strength and corrosion-resistant sucker rod with the above weight percentage is subjected to a primary refining in an electric arc furnace, followed by refining in an AOD furnace, and further refining outside a LF furnace, and then casting to obtain a steel ingot.

(32) Step S30, the steel ingot obtained in step S20 is first heated to 580° C. and kept for 70 minutes, heated to 860° C. and kept for 50 minutes, then heated to a final temperature of 1,180° C. and kept for 2.5 hours, and then the heated steel ingot is taken out of the furnace for rolling to obtain a high-strength sucker rod bar.

(33) Step S40: the high-strength sucker rod bar obtained in step S30 is put into a sodium chloride aqueous solution with a concentration of 11 wt % for a quenching treatment at 918° C. for 35 minutes, and then a tempering treatment is performed at 560° C. for 42 minutes to obtain the high-strength and corrosion-resistant sucker rod.

Embodiment 4

(34) High-Strength and Corrosion-Resistant Sucker Rod and Preparation Process Thereof.

(35) The raw materials for preparing the high-strength and corrosion-resistant sucker rod include: by weight percent, Mn: 1.00%, Cr: 13.50%, Ni: 1.10%, Mo: 0.10%, Cu: 0.50%, V: 0.12%, Nb: 0.08%, C: 0.07%, Si: 0.50%, P: 0.015%, S: 0.003%, and the balance is Fe and unavoidable impurities.

(36) The high-strength and corrosion-resistant sucker rod is prepared by the process as follows.

(37) Step S10, the raw materials of the high-strength and corrosion-resistant sucker rod are weighed according to the above-mentioned weight percentage.

(38) Step S20, the raw materials for preparing the high-strength and corrosion-resistant sucker rod with the above weight percentage is subjected to a primary refining in an electric arc furnace, followed by refining in an AOD furnace, and further refining outside a LF furnace, and then casting to obtain a steel ingot.

(39) Step S30, the steel ingot obtained in step S20 is first heated to 570° C. and kept for 80 minutes, heated to 850° C. and kept for 80 minutes, then heated to a final temperature of 1,200° C. and kept for 2.0 hours, and then the heated steel ingot is taken out of the furnace for a rolling to obtain a high-strength sucker rod bar.

(40) Step S40: the high-strength sucker rod bar obtained in step S30 is put into a sodium chloride aqueous solution with a concentration of 12 wt % for a quenching treatment at 915° C. for 20 minutes, and then a tempering treatment is performed at 550° C. for 45 minutes to obtain the high-strength and corrosion-resistant sucker rod.

Embodiment 5

(41) High-Strength and Corrosion-Resistant Sucker Rod and Preparation Process Thereof.

(42) The raw materials for preparing the high-strength and corrosion-resistant sucker rod include: by weight percent, Mn: 0.85%, Cr: 11.80%, Ni: 0.90%, Mo: 0.35%, Cu: 0.35%, V: 0.20%, Nb: 0.12%, C: 0.07%, Si: 0.20%, P: 0.065%, S: 0.005%, and the balance is Fe and unavoidable impurities.

(43) The high-strength and corrosion-resistant sucker rod is prepared by the process as follows.

(44) Step S10, the raw materials of the high-strength and corrosion-resistant sucker rod are weighed according to the above-mentioned weight percentage.

(45) Step S20, the raw materials for preparing the high-strength and corrosion-resistant sucker rod with the above weight percentage is subjected to a primary refining in an electric arc furnace, followed by refining in an AOD furnace, and further refining outside a LF furnace, and then casting to obtain a steel ingot.

(46) Step S30, the steel ingot obtained in step S20 is first heated to 580° C. and kept for 20 minutes, heated to 900° C. and kept for 60 minutes, then heated to a final temperature of 1,180° C. and kept for 1.0 hour, and then the heated steel ingot is taken out of the furnace for rolling to obtain a high-strength sucker rod bar.

(47) Step S40: the high-strength sucker rod bar obtained in step S30 is put into a sodium chloride aqueous solution with a concentration of 8 wt % for a quenching treatment at 915° C. for 30 minutes, and then a tempering treatment is performed at 565° C. for 50 minutes to obtain the high-strength and corrosion-resistant sucker rod.

Embodiment 6

(48) High-Strength and Corrosion-Resistant Sucker Rod and Preparation Process Thereof.

(49) The raw materials for preparing the high-strength and corrosion-resistant sucker rod include: by weight percent, Mn: 0.90%, Cr: 12.00%, Ni: 0.85%, Mo: 0.35%, Cu: 0.40%, V: 0.32%, Nb: 0.23%, C: 0.07%, Si: 0.50%, P: 0.035%, S: 0.004%, and the balance is Fe and unavoidable impurities.

(50) The high-strength and corrosion-resistant sucker rod is prepared by the process as follows.

(51) Step S10, the raw materials of the high-strength and corrosion-resistant sucker rod are weighed according to the above-mentioned weight percentage.

(52) Step S20, the raw materials for preparing the high-strength and corrosion-resistant sucker rod with the above weight percentage is subjected to a primary refining in an electric arc furnace, followed by refining in an AOD furnace, and further refining outside a LF furnace, and then casting to obtain a steel ingot.

(53) Step S30, the steel ingot obtained in step S20 is first heated to 570° C. and kept for 60 minutes, heated to 880° C. and kept for 70 minutes, then heated to a final temperature of 1,170° C. and kept for 2.0 hour, and then the heated steel ingot is taken out of the furnace for rolling to obtain a high-strength sucker rod bar.

(54) Step S40: the high-strength sucker rod bar obtained in step S30 is put into a sodium chloride aqueous solution with a concentration of 10 wt % for a quenching treatment at 910° C. for 30 minutes, and then a tempering treatment is performed at 570° C. for 48 minutes to obtain the high-strength and corrosion-resistant sucker rod.

Comparative Example 1

(55) High-Strength and Corrosion-Resistant Sucker Rod and Preparation Process Thereof.

(56) The raw materials for preparing the high-strength and corrosion-resistant sucker rod include: by weight percent, Mn: 0.80%, Cr: 9.00%, Ni: 0.60%, Mo: 0.35%, Cu: 0.45%, V: 0.12%, Nb: 0.08%, C: 0.06%, Si: 0.30%, P: 0.01%, S: 0.004%, and the balance is Fe and unavoidable impurities.

(57) The high-strength and corrosion-resistant sucker rod is prepared by the process as follows.

(58) Step S10, the raw materials of the high-strength and corrosion-resistant sucker rod are weighed according to the above-mentioned weight percentage.

(59) Step S20, the raw materials for preparing the high-strength and corrosion-resistant sucker rod with the above weight percentage is subjected to a primary refining in an electric arc furnace, followed by refining in an AOD furnace, and further refining outside a LF furnace, and then casting to obtain a steel ingot.

(60) Step S30, the steel ingot obtained in step S20 is first heated to 570° C. and kept for 60 minutes, heated to 880° C. and kept for 70 minutes, then heated to a final temperature of 1,180° C. and kept for 2.0 hour, and then the heated steel ingot is taken out of the furnace for rolling to obtain a high-strength sucker rod bar.

(61) Step S40: the high-strength sucker rod bar obtained in step S30 is put into a sodium chloride aqueous solution with a concentration of 10 wt % for a quenching treatment at 908° C. for 30 minutes, and then a tempering treatment is performed at 570° C. for 48 minutes to obtain the high-strength and corrosion-resistant sucker rod.

Comparative Example 2

(62) High-Strength and Corrosion-Resistant Sucker Rod and Preparation Process Thereof.

(63) The raw materials for preparing the high-strength and corrosion-resistant sucker rod include: by weight percent, Mn: 0.80%, Cr: 9.00%, Ni: 0.60%, Mo: 0.35%, Cu: 0.45%, V: 0.22%, Nb: 0.18%, C: 0.06%, Si: 0.30%, P: 0.01%, S: 0.004%, and the balance is Fe and unavoidable impurities.

(64) The high-strength and corrosion-resistant sucker rod is prepared by the process as follows.

(65) Step S10, the raw materials of the high-strength and corrosion-resistant sucker rod are weighed according to the above-mentioned weight percentage.

(66) Step S20, the raw materials for preparing the high-strength and corrosion-resistant sucker rod with the above weight percentage is subjected to a primary refining in an electric arc furnace, followed by refining in an AOD furnace, and further refining outside a LF furnace, and then casting to obtain a steel ingot.

(67) Step S30, the steel ingot obtained in step S20 is first heated to 570° C. and kept for 60 minutes, heated to 880° C. and kept for 70 minutes, then heated to a final temperature of 1,160° C. and kept for 2.0 hour, and then the heated steel ingot is taken out of the furnace for rolling to obtain a high-strength sucker rod bar.

(68) Step S40: the high-strength sucker rod bar obtained in step S30 is put into a sodium chloride aqueous solution with a concentration of 10 wt % for a quenching treatment at 918° C. for 30 minutes, and then a tempering treatment is performed at 570° C. for 48 minutes to obtain the high-strength and corrosion-resistant sucker rod.

Experimental Example

(69) To further illustrate the technological advancement of the present invention, experiments are presented hereinafter to further illustrate.

(70) 1. Mechanical Property Testing

(71) The high-strength and corrosion-resistant sucker rods prepared in embodiments 5 and 6 and comparative examples 1 and 2 of the present invention are selected for mechanical performance testing. Among them, the high-strength corrosion-resistant rods in comparative examples 1 and 2 are obtained by rolling with a lower Cr content, and the data are shown in Table 1.

(72) TABLE-US-00001 TABLE 1 Test material Test item Unit Test results Test method Embodiment R.sub.p0.2 MPa 947 944 947 GB/T228.1-2010 5 Rm MPa 1256 1263 1266 A124 A % 20.0 19.5 17.0 Z % 72 72 71 KU.sub.2 J 234, 257, 230 Grain size Grade 8.0 GB/T6394-2002A method Microstructure / Tempered martensite GB/T13320-2007 Rockwell hardness HRC 41.1 41.2 40.6 GB/T230.1-2009 Embodiment R.sub.p0.2 MPa 961 987 955 GB/T228.1-2010 6 Rm MPa 1260 1221 1230 A124 A % 18.0 17.0 16.5 Z % 73 72 73 KU.sub.2 J 237, 232, 249 Grain size Grade 8.0 GB/T6394-2002A method Microstructure / Tempered martensite GB/T13320-2007 Rockwell hardness HRC 39.1 38.3 38.2 GB/T230.1-2009 Comparative R.sub.p0.2 MPa 872 832 828 GB/T228.1-2010 Example 1 Rm MPa 1,057 1,019 1,007 A124 A % 15.5 16.5 15.0 Z % 46.0 47.0 52.0 KU.sub.2 J 40, 34, 33 Grain size Grade 6.5 GB/T6394-2002A method Microstructure / Tempered torsite GB/T13320-2007 Rockwell hardness HRC 33.3 35.4 33.8 GB/T230.1-2009 Comparative R.sub.p0.2 MPa / 1,149 1,130 GB/T228.1-2010 Example 2 Rm MPa 1,180 1,187 1,175 A124 A % 14.5 15.5 15.5 Z % 47.0 54.0 55.0 KU.sub.2 J 72, 75, 72 Grain size Grade 6.5 GB/T6394-2002A method Microstructure / Tempered torsite GB/T13320-2007 Rockwell hardness HRC 35.9 36.3 35.2 GB/T230.1-2009

(73) 2. Corrosion Resistance Testing

(74) (1) Sulfuric Acid Corrosion Resistance Testing

(75) Experimental samples: high-strength and corrosion-resistant sucker rods (sample size: 50×10×3 mm) prepared in embodiments 5 and 6 of the present invention, as well as commercially available 4330M steel (4330 modified steel) and 4138 steel, and five samples of each type are selected.

(76) Corrosion solution: H.sub.2SO.sub.4 mixed solution (n % H.sub.2SO.sub.4+5% NaCl+0.5% CH.sub.3COOH+H.sub.2O) 500 mL.

(77) Experimental conditions: placed at normal pressure and temperature (NPT) for 168 h, and the experimental results are shown in Table 2.

(78) TABLE-US-00002 TABLE 2 Test results of corrosion resistance of the high-strength and corrosion-resistant sucker rods prepared in embodiments 5 and 6 of the present invention, and commercially available 4330M steel and 4138 steel to sulfuric acid mixed solution Weight Weight after Weight before corrosion Weight loss rate Corrosion Material H.sub.2SO.sub.4 mixed solution corrosion (g) (g) loss (%) rate (mm/a) Embodiment 1.0 + 5.0 + 0.5 12242.8 11018.3 1224.5 10.00 10.096 5 0.5 + 5.0 + 0.5 9574.8 8231.8 1343.0 14.03 13.036 0.1 + 5.0 + 0.5 11071.2 10604.1 467.1 4.22 4.116 0.05 + 5.0 + 0.5 9072.5 8992.4 80.1 0.88 0.810 0.01 + 5.0 + 0.5 9591.1 9550.1 41.0 0.43 0.398 Embodiment 1.0 + 5.0 + 0.5 12041.2 10793.7 1247.5 10.36 10.392 6 0.5 + 5.0 + 0.5 10766.7 9200.2 1566.5 14.55 14.078 0.1 + 5.0 + 0.5 9393.3 8941.7 451.6 4.81 4.441 0.05 + 5.0 + 0.5 9337.5 9242.8 94.7 1.01 0.935 0.01 + 5.0 + 0.5 9428.7 9357.0 71.7 0.76 0.704 4138 steel 1.0 + 5.0 + 0.5 12239.9 8600.3 3639.6 29.74 30.058 0.5 + 5.0 + 0.5 8654.2 5881.1 2773.1 32.04 28.861 0.1 + 5.0 + 0.5 11258.5 9899.7 1358.8 12.07 11.866 0.5 + 5.0 + 0.5 10481.9 9470.9 741.0 7.07 6.791 0.01 + 05.0 + 0.5 9646.5 8963.0 683.5 7.09 6.619 4330M steel 1.0 + 5.0 + 0.5 12017.9 9143.3 2874.6 23.91 23.850 0.5 + 5.0 + 0.5 9372.8 9372.8 2682.5 28.62 26.468 0.1 + 5.0 + 0.5 10388.4 9071.1 1317.3 12.68 12.139 0.05 + 5.0 + 0.5 9801.5 8748.6 1052.9 10.74 10.083 0.01 + 5.0 + 300.5 9904.4 9034.4 870.0 8.78 8.270

(79) (2) Resistance Testing to Hydrogen-Induced Cracking (HIC)

(80) According to the NACETM0284-2016 “Evaluation of Pipelines and Pressure Vessel Steels for Resistance to HIC”, the high-strength and corrosion-resistant sucker rod prepared in embodiment 6 of the present invention is subjected to the resistance testing to HIC, the commercially available 1Cr13 steel is used as a test sample of the comparative example 3, and three samples are selected for each type. The test information is shown in Table 3, the test results are shown in Tables 4 and 5, the diagrams of the samples before and after the experiment are shown in FIGS. 1A-B and FIGS. 2A-B, and the diagrams of the test surfaces are shown in FIG. 3 and FIG. 4.

(81) TABLE-US-00003 TABLE 3 Test information of resistance testing to HIC of the high-strength and corrosion-resistant sucker rod prepared in embodiment 6 of the present invention and commercially available 1Cr13 steel pH H.sub.2S content Solution at in the Saturated the end of saturated Experiment Experiment Experiment H.sub.2S the H.sub.2S Debinding temperature time solution Initial solution solution experiment solution method 25 ± 3° C. 96 h A solution 2.70 2.83 3.77 2,680 Acetone mg/L Note: 1. Solution A is a distilled water solution with mass fraction of 5% sodium chloride and 0.5% glacial acetic acid. 2. The experiment process include the following steps: (1) preparing samples; (2) putting each of the samples into a test container, respectively; (3) preparing solution; (4) measuring the pH of the initial solution; (5) deoxidizing with nitrogen gas at a rate of 100 mL/min for two hours; (6) feeding H.sub.2S at a rate of 100 mL/min for at least one hour until the solution is saturated; (7) measuring the pH value and H.sub.2S content of the saturated H.sub.2S solution; (8) maintaining the positive H.sub.2S pressure until the end of the experiment; (9) measuring the pH value of the solution at the end of the experiment; and (10) verifying the experimental results.

(82) TABLE-US-00004 TABLE 4 Test results 1 of resistance testing to HIC of the high-strength and corrosion-resistant sucker rod prepared in embodiment 6 of the present invention and commercially available 1Cr13 steel Crack length Crack thickness Crack sensitivity ratio ratio ratio (CLR, %) (CTR, %) (CSR, %) Average Average Average value of value of value of Test Measured each Measured each Measured each Test material surface value sample value sample value sample Embodiment 6 001 0 0 0 0 0 0 002 0 0 0 003 0 0 0 Comparative 001  8.307% 6.796%  5.629% 7.251% 0.05984% 0.07952% Example 3 002 12.081% 16.125% 0.17872% 003 0 0 0

(83) Under this test conditions, the HIC resistance of the sample of comparative example 3 cannot simultaneously meet the performance requirements of CLR≤15%, CSR≤2%/and CTR≤5%, and the CTR value is higher than the required value.

(84) TABLE-US-00005 TABLE 5 Test results 2 of resistance testing to HIC of the high-strength and corrosion-resistant sucker rod prepared in embodiment 6 of the present invention and commercially available 1Cr13 steel Weight Weight Corrosion Weight Corrosion before after test rate after rate Material test (g) (g) (mm/a) pickling (g) (mm/a) Comparative 129.5170 129.4310 0.275 / / Example 3-1 Comparative 125.7703 125.6880 0.263 125.3737 0.281 Example 3-2 Comparative 126.1680 126.0811 0.277 126.0744 0.285 Example 3-3 Embodiment 203.9933 203.9205 0.122 / / 6-1 Embodiment 204.0848 204.0284 0.090 204.0265 0.097 6-2 Embodiment 203.9710 203.9118 0.101 203.9103 0.101 6-3

(85) (3) Property Testing of Corrosion Inhibitor for Oilfield Produced Water Treatment

(86) According to SY/T5273-2014 “Technical Specifications and Evaluating Methods of Corrosion-inhibitors for Oilfield Produced Water”, the high-strength and corrosion-resistant sucker rods (with a sample size of 50×10×3 mm) prepared in embodiments 5 and 6 of the present invention are is subjected to the property testing.

(87) Experimental process: a coupon experiment is carried out in a Wang 26-1 corrosive medium. The specific corrosion conditions are: the mineralization of water is 30,665 ppm, hydrogen sulfide is 200 ppm, carbon dioxide is 200 ppm, the temperature is 60° C., and the time is 7 days.

(88) Test results: after the coupon experiment, the results are shown in Table 6, and the appearance views before and after the experiment are shown in FIGS. 5A-B and FIGS. 6A-B.

(89) TABLE-US-00006 TABLE 6 Corrosion resistance test results of high-strength and corrosion-resistant sucker rods prepared in embodiments 5 and 6 of the present invention Mass Mass after Total mass loss Annual Temperature/ Corrosion before film after film corrosion rate Material ° C. rate/% corrosion/g removal/g removal/g mm/a Embodiment 60 0.0065995 10.6068 10.6061 0.0007 0.003399263 5 Embodiment 60 0.0056397 10.6388 10.6382 0.0006 0.002913654 6

(90) Test conclusion: the high-strength and corrosion-resistant sucker rod of the present invention has a smooth surface without obvious corrosion product film after corrosion, and the corrosion rate is far less than the SY/T5329-2012 standard of 0.076 mm/a, which belongs to a light corrosion of <0.001 mm/a according to the standard of NACERP-0775-91 on the average corrosion level.

(91) (4) Metal Stress Corrosion Test (Cracking)

(92) Under the conditions of simulated operating conditions of water P.sub.H.sub.2.sub.S=0.25 MPa, P.sub.CO.sub.2=3.63 MPa and test temperature of 152° C., stress corrosion cracking (SCC) test is carried out on the high-strength and corrosion-resistant sucker rods prepared in embodiments 5 and 6 of the present invention. Three samples are selected for each type, and the test results are shown in Table 7.

(93) TABLE-US-00007 TABLE 7 SCC test results of high-strength and corrosion-resistant sucker rods prepared in embodiments 5 and 6 of the present invention Test time (h) Test results Embodiment 5-1 24 × 30 0.0135 mm/a Embodiment 5-2 0.0045 mm/a Embodiment 5-3 0.0192 mm/a Embodiment 6-1 24 × 60 0.0260 mm/a Embodiment 6-2 0.0136 mm/a Embodiment 6-3 0.0109 mm/a

(94) The results show that the corrosion of each sample is uniform corrosion without local corrosion such as pitting corrosion. The corrosion rate is relatively low, and lower than the corrosion rate at 150° C. in CO.sub.2 environment, which belongs to the slight corrosion in the NACE standard. The corrosion products on the sample surface are densely distributed, and the main components in the corrosion products of embodiments 5 and 6 are FeS, Fe.sub.7S.sub.8 and FeS.sub.2.

(95) The foregoing descriptions are merely preferred embodiments of the present invention, which are not used to limit the present invention. For those skilled in the art, the present invention may have various modifications and variations. Any modifications, equivalent substitutions, improvements within the spirit and principle of the present invention shall fall within the protective scope of the present invention.