ZONAL TRABECULA FEMORAL CONDYLAR COMPONENT CONTAINING ZIRCONIUM-NIOBIUM ALLOY ON OXIDATION LAYER AND PREPARATION METHOD THEREOF

Abstract

The present invention discloses the zonal trabecular femoral condylar component containing zirconium-niobium alloy on oxidation layer and its preparation method. The preparation method is as follows: using zirconium-niobium alloy powder as a raw material, conducting a 3D printing for one-piece molding, and obtaining intermediate products of the zonal trabecular femoral condylar component containing zirconium-niobium alloy on oxidation layer, after Sinter-HIP, cryogenic cooling and surface oxidation, the zonal trabecular femoral condylar component containing zirconium-niobium alloy on oxidation layer is prepared. Partial of the zonal trabecular femoral condylar component containing zirconium-niobium alloy on oxidation layer is provided with Zonal trabecula. The present invention achieves that the micro-strain in most areas of the bone tissue on the femoral condylar component is between the minimum effective strain threshold and the super-physiological strain threshold, which is conducive to bone ingrowth, thereby improving long-term stability.

Claims

1. A preparation method of the zonal trabecular femoral condylar component containing zirconium-niobium alloy on oxidation layer includes the following steps: 1) using zirconium-niobium alloy powder as a raw material, conducting a 3D printing for one-piece molding, and obtaining a first intermediate product of the zonal trabecular femoral condylar component containing zirconium-niobium alloy on oxidation layer, putting the first intermediate product into a Sinter-HIP furnace, heating to 1250° C.-1400° C. under inert gas protection, and placing at a constant pressure of 140 MPa-180 MPa for 1 h to 3 h, and reducing to a normal pressure, cooling to below 200° C. with the furnace, taking it out, and obtaining a second intermediate product; 2) putting the second intermediate product into a programmed thermostat, cooling to −80° C. to −120° C. at a rate of 1° C./min, keeping it at a constant temperature for 5 h to 10 h, and taking it out of the programmed thermostat; and putting it into a liquid nitrogen for 16 h to 36 h, and adjusting the temperature to a room temperature so as to obtain a third intermediate product; 3) putting the third intermediate product in a programmed thermostat, cooling to −80° C. to −120° C. at a rate of 1° C./min, and placing it at a constant temperature for 5 h to 10 h, taking it out of the programmed thermostat, and putting it into the liquid nitrogen for 16 h to 36 h, and adjusting the temperature to room temperature so as to obtain a fourth intermediate product; 4) machining, finishing, polishing, cleaning, and drying the fourth intermediate product, and obtaining a fifth intermediate product, where articular surface roughness of the fifth intermediate product is Ra≤0.050 μm; 5) putting the fifth intermediate product into a tube furnace, introducing the normal-pressure inert gas containing 5% to 15% of oxygen in percentage by mass, heating to 500° C. to 700° C. at 5° C./min to 20° C./min, and cooling to 400° C. to 495° C. at 0.4° C./min to 0.9° C./min, and cooling to be below 200° C. sequentially, taking it out to obtain the zonal trabecular femoral condylar component containing zirconium-niobium alloy on oxidation layer; for the zonal trabecular femoral condylar component containing zirconium-niobium alloy on oxidation layer, its structure is the same as its first intermediate product, second intermediate product, third intermediate product, fourth intermediate product, and fifth intermediate product; and the inert gas is helium or argon; the structure of the zonal trabecular femoral condylar component containing zirconium-niobium alloy on oxidation layer includes a medial condyle (11) and a lateral condyle (12) which are arranged in the left and right direction; a medial condyle anterior end (1101) of the medial condyle (11) is integrated with a lateral condyle anterior end (1102) of the lateral condyle (12); a posterior end of the medial condyle (11) is connected with a posterior end of the lateral condyle (12) by a stopper (15); a lateral wall of the medial condyle (11) and a lateral wall of the lateral condyle (12) are both provided with a holding slot (16); the medial condyle (11) is provided with a medial condyle fixation surface (110); the lateral condyle is provided with a lateral condyle fixation surface (120); the medial condyle fixation surface (110) includes a first fixation surface (111), a second fixation surface (112), a third fixation surfaces (113), a fourth fixation surface (114) and a fifth fixation surface (115) which are connected sequentially; the lateral condyle fixation surface (120) includes a sixth fixation surface (121), a seventh fixation surface (122), an eighth fixation surface (123), a ninth fixation surface (124), and a tenth fixing surface (125) which are connected sequentially; a mounting hole (17) is formed in the middle of the third fixation surface (113) and the eighth fixation surface (123); the first fixation surface (111) is intersected with the second fixation surface (112) to form a first intersecting line (181); the second fixation surface (112) is intersected with the third fixation surface (113) to form a second intersecting line (182); the third fixation surface (113) is intersected with the fourth fixation surface (114) to form a third intersecting line (183); the fourth fixation surface (114) is intersected with the fifth fixation surface (115) to form a fourth intersecting line (184); an intersecting line of the sixth fixation surface (121) and the seventh fixation surface (122) is collinear with the first intersecting line (181); an intersecting line of the seventh fixation surface (122) and the eighth fixation surface (123) is collinear with the second intersecting line (182); an intersecting line of the eighth fixation surface (123) and the ninth fixation surface (124) is collinear with the third intersecting line (183); an intersecting line of the ninth fixation surface (124) and the tenth fixation surface (125) is collinear with the fourth intersecting line (184); and the first Intersecting line (181), the second intersecting line (182), the third intersecting line (183), and fourth intersecting line (184) are parallel to each other; an included angle between the first fixation surface (111) and the second fixation surface (112) is 130° to 140°, equal to an included angle between the sixth fixation surface (121) and the seventh fixation surface (122); an included angle between the second fixation surface (112) and the third fixation surface (113) is 130° to 140°, equal to the included angle between the seventh fixation surface (122) and the eighth fixation surface (123); an included angle between the third fixation surface (113) and the fourth fixation surface (114) is 130° to 140°, equal to the included angle between the eighth fixation surface (123) and the ninth fixation surface (124); an included angle between the fourth fixation surface (114) and the fifth fixation surface (115) is 130° to 140°, equal to the included angle between the ninth fixation surface (124) and the tenth fixation surface (125); the first fixation surface (111), the fifth fixation surface (115), the sixth fixation surface (121) and the tenth fixation surface (125) are provided with a first bone trabecula (191); the second fixation surface (112), the fourth fixation surface (114), the seventh fixation surface (122) and the ninth fixation surface (124) are provided with a second bone trabecula (192); the third fixation surface (113) and the eighth fixation surface (123) are provided with a third bone trabecula (193). a pore diameter and porosity of the first bone trabecula (191) are smaller than those of the second bone trabecula (192) and the third bone trabecula (193) in sequence.

2. The method according to claim 1, wherein the chemical composition of the zirconium-niobium alloy powder in percentage by mass is respectively 85.6%-96.5% of Zr, 1.0%-12.5% of Nb, and the rest are unavoidable impurities; where a particle size of the zirconium-niobium alloy powder ranges from 45 to 150 μm.

3. The method according to claim 1, wherein the specific steps for adjusting the temperature in steps 2) and 3) are: increasing the temperature to −120° C. to −80° C. and keeping the constant temperature for 3 h to 5 h; then increasing the temperature to −40° C. to −20° C. and keeping the constant temperature for 3 h to 5 h; then increasing the temperature to 4° C. to 8° C. and keeping the constant temperature for 1 h to 3 h and then increasing the temperature.

4. The method according to claim 1, wherein the pore diameter of the first bone trabecula (191) ranges from 0.74 mm to 0.85 mm, the porosity ranges from 70.0% to 74.7%, and the through-hole ratio of 100%; the pore diameter of the second bone trabecula (192) ranges from 0.86 mm to 0.99 mm, a porosity ranges from 74.8% to 77.5%, and a through-hole ratio of 100%; the pore diameter of the third bone trabecula (193) ranges from 1.00 mm to 1.10 mm mm, a porosity ranges from 77.6% to 85%, and a through-hole ratio of 100%.

5. The method according to claim 1, wherein the thickness of the first bone trabecula (191), the second trabecular bone (192) and the third bone trabecula (193) are 0.5 mm to 3 mm.

6. The method according to claim 1, wherein a rectangular first solid structure (21) is provided at a junction of the second fixation surface and the seventh fixation surface; a semicircular second solid structure (20) is provided at a junction of the first fixation surface and the sixth fixation surface; the thickness of the first solid structure (21) and the second solid structure (20) is equal to the thickness of the bone trabecula, ranging from 0.5 mm to 3 mm.

7. The method according to claim 1, wherein a side wall (22) is provided on an edge of a fixation surface formed by the medial condyle fixation surface (110), the lateral condyle fixation surface (120) and the stopper (15).

8. A zonal trabecular femoral condylar component containing zirconium-niobium alloy on oxidation layer prepared in the method according to claim 1.

9. The zonal trabecular femoral condylar component according to claim 8, wherein the chemical composition of the zirconium-niobium alloy powder in percentage by mass is respectively 85.6%-96.5% of Zr, 1.0%-12.5% of Nb, and the rest are unavoidable impurities; where a particle size of the zirconium-niobium alloy powder ranges from 45 to 150 μm.

10. The zonal trabecular femoral condylar component according to claim 8, wherein the specific steps for adjusting the temperature in steps 2) and 3) are: increasing the temperature to −120° C. to −80° C. and keeping the constant temperature for 3 h to 5 h; then increasing the temperature to −40° C. to −20° C. and keeping the constant temperature for 3 h to 5 h; then increasing the temperature to 4° C. to 8° C. and keeping the constant temperature for 1 h to 3 h and then increasing the temperature.

11. The zonal trabecular femoral condylar component according to claim 8, wherein the pore diameter of the first bone trabecula (191) ranges from 0.74 mm to 0.85 mm, the porosity ranges from 70.0% to 74.7%, and the through-hole ratio of 100%; the pore diameter of the second bone trabecula (192) ranges from 0.86 mm to 0.99 mm, a porosity ranges from 74.8% to 77.5%, and a through-hole ratio of 100%; the pore diameter of the third bone trabecula (193) ranges from 1.00 mm to 1.10 mm mm, a porosity ranges from 77.6% to 85%, and a through-hole ratio of 100%.

12. The zonal trabecular femoral condylar component according to claim 8, wherein the thickness of the first bone trabecula (191), the second trabecular bone (192) and the third bone trabecula (193) are 0.5 mm to 3 mm.

13. The zonal trabecular femoral condylar component according to claim 8, wherein the rectangular first solid structure (21) is provided at the junction of the second fixation surface and the seventh fixation surface; a semicircular second solid structure (20) is provided at the junction of the first fixation surface and the sixth fixation surface; the thickness of the first solid structure (21) and the second solid structure (20) is equal to the thickness of the bone trabecula, ranging from 0.5 mm to 3 mm.

14. The zonal trabecular femoral condylar component according to claim 8, wherein a side wall (22) is provided on an edge of a fixation surface formed by the medial condyle fixation surface (110), the lateral condyle fixation surface (120) and the stopper (15).

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0038] FIG. 1 shows an axonometric drawing of the zonal trabecular femoral condylar component containing zirconium-niobium alloy on oxidation layer observed from the lateral condyle.

[0039] FIG. 2 shows an axonometric drawing of the zonal trabecular femoral condylar component containing zirconium-niobium alloy on oxidation layer (including the first solid structure and the second solid structure) observed from the medial condyle.

[0040] FIG. 3 shows an axonometric drawing of the zonal trabecular femoral condylar component containing zirconium-niobium alloy onoxidation layer observed from the anterior of the femoral condyle.

[0041] FIG. 4 shows a finite element analysis strain cloud chart of the zonal trabecular femoral condylar component containing zirconium-niobium alloy on oxidation layer observed from the anterior of the femoral condyle in Embodiment 1.

[0042] FIG. 5 shows a finite element analysis strain cloud chart of the zonal trabecular femoral condylar component containing zirconium-niobium alloy on oxidation layer observed from the posterior of the femoral condyle in Embodiment 1.

[0043] FIG. 6 shows a metallographic microstructure diagram of the solid part of Control Group 1 (A is for observation at a magnification of 50 times; B is for observation at a magnification of 500 times).

[0044] FIG. 7 shows a metallographic microstructure diagram of the solid part that has not been prepared with steps 4) and 5) of the preparation method in Embodiment 1 (A is for observation at a magnification of 50 times; B is for observation at a magnification of 500 times).

[0045] FIG. 8 shows SEM images of trabecula in Control Group 1.

[0046] FIG. 9 shows SEM images of trabecula that has not been prepared with steps 4) and 5) of the preparation method in Embodiment 1.

[0047] FIG. 10 shows the SEM of cross-section between the oxidation layer and the matrix in Embodiment 1.

[0048] FIG. 11 shows the XRD curve of the oxidation layer surface in Embodiment 1.

DETAILED DESCRIPTION OF THE EMBODIMENTS

[0049] The zonal trabecular femoral condylar component containing zirconium-niobium alloy on oxidation layer of the present invention is subjected to a 3D printing for one-piece molding.

[0050] The present invention will be further described below with the drawings and embodiments.

Embodiment 1

[0051] The preparation method of the zonal trabecular femoral condylar component containing zirconium-niobium alloy on oxidation layer includes the following steps:

[0052] 1) Using zirconium-niobium alloy powder as a raw material, the first intermediate product of the zonal trabecular femoral condylar component containing zirconium-niobium alloy on oxidation layer is integrally formed by 3D printing, and the first intermediate product is put into the Sinter-HIP furnace, heated to 1250° C. under helium gas protection, and placed at a constant pressure of 180 MPa for 3 h, and the furnace is depressurized to a normal pressure, the first intermediate product is cooled to below 200° C. with the furnace and taken out to obtain a second intermediate product.

[0053] 2) Place the second intermediate product in a programmed thermostat to cool to −80° C. at a rate of 1° C./min, keep it at a constant temperature for 10 h, and take it out of the programmed thermostat, and place the second intermediate product in liquid nitrogen for another 16 h, and adjust the temperature to room temperature to obtain a third intermediate product.

[0054] 3) Place the third intermediate product in a programmed thermostat to cool to −80° C. at a rate of 1° C./min, and place the third intermediate product at a constant temperature for 10 h, take it out of the programmed thermostat, place it in liquid nitrogen for another 16 h and adjust the temperature to room temperature to obtain a fourth intermediate product.

[0055] The specific steps for adjusting the temperature in steps 2) and 3) are: increase the temperature to −120° C. and keep the constant temperature for 5 h, then increase the temperature to −40° C. and keep the constant temperature for 5 h, then increase the temperature to 4° C. and keep the constant temperature for 3 h and then increase the temperature.

[0056] 4) The fourth intermediate product is machined, finished, polished, cleaned and dried to obtain a fifth intermediate product. The articular surface roughness of the fifth intermediate product is Ra=0.012 μm.

[0057] 5) Place the fifth intermediate product in a tube furnace, introduce normal pressure helium gas containing 5% oxygen in percentage by mass, heat it to 500° C. at 5° C./min, and cool it down to 400° C. at 0.4° C./min. Under natural cooling to below 200° C., take it out to obtain the zonal trabecular femoral condylar component containing zirconium-niobium alloy on oxidation layer.

[0058] For the zonal trabecular femoral condylar component containing zirconium-niobium alloy on oxidation layer, its structure is the same as its first intermediate product, second intermediate product, third intermediate product, fourth intermediate product, and fifth intermediate product.

[0059] The chemical composition of the zirconium-niobium alloy powder is respectively 85.6% of Zr, 12.5% of Nb by mass percentage, and the rest are unavoidable impurities. The zirconium-niobium alloy powder has a particle size of 45-150 μm and is purchased from Xi'an Sailong Metal Materials Co., Ltd.

[0060] The structure of the above-mentioned zonal trabecular femoral condylar component containing zirconium-niobium alloy on oxidation layer (see FIGS. 1-3) includes a medial condyle 11 and a lateral condyle 12 which are arranged in a left and right direction. A medial condyle anterior end 1101 is integrated with a lateral condyle anterior end 1102; a posterior end of the medial condyle 11 is connected with a posterior end of the lateral condyle 12 by a stopper 15. The lateral wall of the medial condyle 11 and the lateral wall of the lateral condyle 12 are both provided with a holding slot 16. The medial condyle 11 is provided with a medial condyle fixation surface 110; the lateral condyle is provided with a lateral condyle fixation surface 120. The medial condyle fixation surface 110 includes a first fixation surface 111, a second fixation surface 112, a third fixation surfaces 113, a fourth fixation surface 114 and a fifth fixation surface 115 connected in sequence; the lateral condyle fixation surface 120 includes a sixth fixation surface 121, a seventh fixation surface 122, an eighth fixation surface 123, a ninth fixation surface 124, and a tenth fixing surface 125 connected in sequence. A mounting hole 17 is formed in the middle of the third fixation surface 113 and the eighth fixation surface 123. The first fixation surface 111 and the second fixation surface 112 intersect to form a first intersecting line 181; the second fixation surface 112 and the third fixation surface 113 intersect to form a second intersecting line 182; the third fixation surface 113 and the fourth fixation surface 114 intersect to form a third intersecting line 183; the fourth fixation surface 114 and the fifth fixation surface 115 form a fourth intersecting line 184; an intersecting line of the sixth fixation surface 121 and the seventh fixation surface 122 is collinear with the first intersecting line 181; an intersecting line of the seventh fixation surface 122 and the eighth fixation surface 123 is collinear with the second intersecting line 182; an intersecting line of the eighth fixation surface 123 and the ninth fixation surface 124 is collinear with the third intersecting line 183; an intersecting line of the ninth fixation surface 124 and the tenth fixation surface 125 is collinear with the fourth intersecting line 184. The first Intersecting line 181, the second intersecting line 182, the third intersecting line 183, and fourth intersecting line 184 are parallel to each other.

[0061] An included angle between the first fixation surface 111 and the second fixation surface 112 is 135°, equal to the included angle between the sixth fixation surface 121 and the seventh fixation surface 122. The included angle between the second fixation surface 112 and the third fixation surface 113 is 135°, equal to the included angle between the seventh fixation surface 122 and the eighth fixation surface 123. The included angle between the third fixation surface 113 and the fourth fixation surface 114 is 135°, equal to the included angle between the eighth fixation surface 123 and the ninth fixation surface 124. The included angle between the fourth fixation surface 114 and the fifth fixation surface 115 is 135°, equal to the included angle between the ninth fixation surface 124 and the tenth fixation surface 125.

[0062] The first fixation surface 111, the fifth fixation surface 115, the sixth fixation surface 121 and the tenth fixation surface 125 are provided with a first bone trabecula 191.

[0063] The second fixation surface 112, the fourth fixation surface 114, the seventh fixation surface 122 and the ninth fixation surface 124 are provided with a second bone trabecula 192.

[0064] The third fixation surface 113 and the eighth fixation surface 123 are provided with a third bone trabecula 193.

[0065] The pore diameter and a porosity of the first bone trabecula 191 are smaller than those of the second bone trabecula 192 and the third bone trabecula 193 in sequence.

[0066] The first bone trabecula 191 has a pore diameter of 0.80 mm, a porosity of 72%, and a through-hole ratio of 100%.

[0067] The second bone trabecula 192 has a pore diameter of 0.93 mm, a porosity of 76%, and a through-hole ratio of 100%.

[0068] The third bone trabecula 193 has a pore diameter of 1.05 mm, a porosity of 80%, and a through-hole ratio of 100%.

[0069] The thickness of the first trabecular bone 191, the second trabecular bone 192, and the third trabecular bone 193 are 1.5 mm.

[0070] It is also possible to provide a rectangular first solid structure 21 at the junction of the second fixation surface and the seventh fixation surface, and provide a semicircular second solid structure 20 at the junction of the first fixation surface and the sixth fixation surface. The thickness of the first solid structure 21 and the second solid structure 20 are equal to the thickness of the bone trabecula, which are either 1 mm or arbitrary value selected from 0.5 mm-3 mm, such as 0.5, 0.6, 0.7, 0.9, 1.1, 1.5, 2.0, 2.5 or 3 mm.

[0071] A side wall 22 is provided on the edge of the fixation surface formed by the medial condyle fixation surface 110, the lateral condyle fixation surface 120, and the stopper 15.

Embodiment 2

[0072] The preparation method of the zonal trabecular femoral condylar component containing zirconium-niobium alloy on oxidation layer includes the following steps:

[0073] 1) Using zirconium-niobium alloy powder as the raw material, a 3D printing is conducted for one-piece molding, a first intermediate product of the zonal trabecular femoral condylar component containing zirconium-niobium alloy on oxidation layer is obtained, and the first intermediate product is put into the Sinter-HIP furnace, heated to 1325° C. under helium gas protection, placed at a constant pressure of 160 MPa for 2 h, and the furnace is depressurized to a normal pressure, the first intermediate product is cooled to below 200° C. with the furnace and taken out to obtain a second intermediate product.

[0074] 2) Place the second intermediate product in a programmed thermostat to cool to −100° C. at a rate of 1° C./min, keep it at a constant temperature for 7 h, and take it out of the programmed thermostat, place it in liquid nitrogen for another 24 h, and adjust the temperature to room temperature to obtain a third intermediate product.

[0075] 3) Place the third intermediate product in a programmed thermostat to cool to −100° C. at a rate of 1° C./min, and place it at a constant temperature for 7 h, take it out of the programmed thermostat, place it in liquid nitrogen for another 24 h and adjust the temperature to room temperature to obtain a fourth intermediate product.

[0076] The specific steps for adjusting the temperature in steps 2) and 3) are: increase the temperature to −100° C. and keep the constant temperature for 4 h, then increase the temperature to −30° C. and keep the constant temperature for 4 h, then increase the temperature to 6° C. and keep the constant temperature for 2 h and then increase the temperature.

[0077] 4) The fourth intermediate product is machined, finished, polished, cleaned and dried to obtain a fifth intermediate product. The articular surface roughness of the fifth intermediate product is Ra=0.035 μm.

[0078] 5) Place the fifth intermediate product in a tube furnace, introduce the normal-pressure helium gas with 10% of oxygen in percentage by mass, heat it to 600° C. at 15° C./min, and cool it down to 450° C. at 0.7° C./min. Under natural cooling to below 200° C., take it out to obtain the zonal trabecular femoral condylar component containing zirconium-niobium alloy on oxidation layer.

[0079] For the zonal trabecular femoral condylar component containing zirconium-niobium alloy on oxidation layer, its structure is the same as its first intermediate product, second intermediate product, third intermediate product, fourth intermediate product, and fifth intermediate product.

[0080] The chemical composition of the zirconium-niobium alloy powder is respectively 93.4% of Zr, 5.1% of Nb by mass percentage, and the rest are unavoidable impurities. The zirconium-niobium alloy powder has a particle size of 45-150 μm and is purchased from Xi'an Sailong Metal Materials Co., Ltd.

[0081] The structure of the zonal trabecular femoral condylar component containing zirconium-niobium alloy on oxidation layer is same as that of the structure in the Embodiment 1, with a difference as follows:

[0082] An included angle between the first fixation surface 111 and the second fixation surface 112 is 130°, equal to the included angle between the sixth fixation surface 121 and the seventh fixation surface 122. The included angle between the second fixation surface 112 and the third fixation surface 113 is 130°, equal to the included angle between the seventh fixation surface 122 and the eighth fixation surface 123. The included angle between the third fixation surface 113 and the fourth fixation surface 114 is 130°, equal to the included angle between the eighth fixation surface 123 and the ninth fixation surface 124. The included angle between the fourth fixation surface 114 and the fifth fixation surface 115 is 130°, equal to the included angle between the ninth fixation surface 124 and the tenth fixation surface 125.

[0083] The first fixation surface 111, the fifth fixation surface 115, the sixth fixation surface 121 and the tenth fixation surface 125 are provided with a first bone trabecula 191.

[0084] The second fixation surface 112, the fourth fixation surface 114, the seventh fixation surface 122 and the ninth fixation surface 124 are provided with a second bone trabecula 192.

[0085] The third fixation surface 113 and the eighth fixation surface 123 are provided with a third bone trabecula 193.

[0086] The pore diameter and a porosity of the first bone trabecula 191 are smaller than those of the second bone trabecula 192 and the third bone trabecula 193 in sequence.

[0087] The first bone trabecula 191 has a pore diameter of 0.74 mm, a porosity of 70.0%, and a through-hole ratio of 100%.

[0088] The second bone trabecula 192 has a pore diameter of 0.86 mm, a porosity of 74.8%, and a through-hole ratio of 100%.

[0089] The third bone trabecula 193 has a pore diameter of 1.00 mm, a porosity of 77.6%, and a through-hole ratio of 100%.

[0090] The thickness of the first trabecular bone 191, the second trabecular bone 192, and the third trabecular bone 193 are 0.5 mm.

Embodiment 3

[0091] The preparation method of the zonal trabecular femoral condylar component containing zirconium-niobium alloy on oxidation layer includes the following steps:

[0092] 1) Using zirconium-niobium alloy powder as the raw material, a 3D printing is conducted for one-piece molding, a first intermediate product of the zonal trabecular femoral condylar component containing zirconium-niobium alloy on oxidation layer is obtained, and the first intermediate product is put into the Sinter-HIP furnace, heated to 1400° C. under argon gas protection, placed at a constant pressure of 140 MPa for 1 h, and the furnace is depressurized to a normal pressure, the first intermediate product is cooled to below 200° C. with the furnace and taken out to obtain a second intermediate product.

[0093] 2) Place the second intermediate product in a programmed thermostat to cool to −120° C. at a rate of 1° C./min, keep it at a constant temperature for 5 h, and take it out of the programmed thermostat, place it in liquid nitrogen for another 36 h, and adjust the temperature to room temperature to obtain a third intermediate product.

[0094] 3) Place the third intermediate product in a programmed thermostat to cool to −120° C. at a rate of 1° C./min, and place it at a constant temperature for 5 h, take it out of the programmed thermostat, place it in liquid nitrogen for another 36 h and adjust the temperature to room temperature to obtain a fourth intermediate product.

[0095] The specific steps for adjusting the temperature in steps 2) and 3) are: increase the temperature to −80° C. and keep the constant temperature for 3 h, then increase the temperature to −20° C. and keep the constant temperature for 3 h, then increase the temperature to 8° C. and keep the constant temperature for 1 h and then increase the temperature.

[0096] 4) The fourth intermediate product is machined, finished, polished, cleaned and dried to obtain a fifth intermediate product. The articular surface roughness of the fifth intermediate product is Ra=0.050 μm.

[0097] 5) Place the fifth intermediate product in a tube furnace, introduce the normal-pressure helium gas with 15% of oxygen in percentage by mass, heat it to 700° C. at 20° C./min, and cool it down to 495° C. at 0.9° C./min. Under natural cooling to below 200° C., take it out to obtain the zonal trabecular femoral condylar component containing zirconium-niobium alloy on oxidation layer.

[0098] For the zonal trabecular femoral condylar component containing zirconium-niobium alloy on oxidation layer, its structure is the same as its first intermediate product, second intermediate product, third intermediate product, fourth intermediate product, and fifth intermediate product.

[0099] The chemical composition of the zirconium-niobium alloy powder is respectively 96.5% of Zr, 1% of Nb by mass percentage, and the rest are unavoidable impurities. The zirconium-niobium alloy powder has a particle size of 45-150 μm and is purchased from Xi'an Sailong Metal Materials Co., Ltd.

[0100] The structure of the zonal trabecular femoral condylar component containing zirconium-niobium alloy on oxide layer is from the same as that of the structure in the Embodiment 1, with a difference as follows:

[0101] An included angle between the first fixation surface 111 and the second fixation surface 112 is 140°, equal to the included angle between the sixth fixation surface 121 and the seventh fixation surface 122. The included angle between the second fixation surface 112 and the third fixation surface 113 is 140°, equal to the included angle between the seventh fixation surface 122 and the eighth fixation surface 123. The included angle between the third fixation surface 113 and the fourth fixation surface 114 is 140°, equal to the included angle between the eighth fixation surface 123 and the ninth fixation surface 124. The included angle between the fourth fixation surface 114 and the fifth fixation surface 115 is 140°, equal to the included angle between the ninth fixation surface 124 and the tenth fixation surface 125.

[0102] The first fixation surface 111, the fifth fixation surface 115, the sixth fixation surface 121 and the tenth fixation surface 125 are provided with a first bone trabecula 191.

[0103] The second fixation surface 112, the fourth fixation surface 114, the seventh fixation surface 122 and the ninth fixation surface 124 are provided with a second bone trabecula 192.

[0104] The third fixation surface 113 and the eighth fixation surface 123 are provided with a third bone trabecula 193.

[0105] The pore diameter and porosity of the first bone trabecula 191 are smaller than those of the second bone trabecula 192 and the third bone trabecula 193 in sequence.

[0106] The first bone trabecula 191 has a pore diameter of 0.85 mm, a porosity of 74.7%, and a through-hole ratio of 100%.

[0107] The second bone trabecula 192 has a pore diameter of 0.99 mm, a porosity of 77.5%, and a through-hole ratio of 100%.

[0108] The third bone trabecula 193 has a pore diameter of 1.10 mm, a porosity of 85%, and a through-hole ratio of 100%.

[0109] The thickness of the first trabecular bone 191, the second trabecular bone 192, and the third trabecular bone 193 are 3 mm.

[0110] Control Group 1

[0111] Using zirconium-niobium alloy powder (same as Embodiment 1) as a raw material, a 3D printing is conducted for one-piece molding, a femoral condylar component with the same structure as that of Embodiment 1 is obtained.

[0112] Experiment Verification

[0113] Finite element analysis on the finite element model of Embodiment 1 of the present invention is shown in FIGS. 4-5. The strain cloud chart only shows micro-strains (shaded areas) ranging from 1000 to 3000, and the 1000-3000 micro-strain area accounts for 65.2% of the entire femoral condylar component bone tissue finite element model. The strain cloud chart suggests that the micro-strains in most area of the zonal trabecular femoral condylar component containing zirconium-niobium alloy on oxidation layer of the present invention is between the minimum effective strain threshold and the super-physiological strain threshold, which allows excellent bone ingrowth performance.

[0114] Metallographic microstructures of a solid part in the control group 1 and a solid part of the Embodiment 1 that has not been prepared with steps 4) and 5) in the preparation method were observed by an inverted universal material microscope (Axio Vert.A1, Zeiss, and Germany). As shown in FIGS. 6-7, a metallograph in the control group 1 showed a fine alpha martensite, a tissue was fine, a stress concentration was easy to cause, and a plasticity was poor; and a metallographic phase in the embodiment 1 was displayed as an alpha phase, which showed a mesh basket structure, and crystalline grains were refined. The results showed that base part of the femoral condylar component (without oxidation layer) of the present invention has excellent strength and plasticity.

[0115] A bone trabecula in the control group 1 and a bone trabecula that has not been prepared with step 4) and 5) in the preparation method in the embodiment 1 were observed and analyzed by a scanning electron microscope (Crossbeam340/550, Zeiss, and Germany), and results were shown in FIGS. 8-9. Compared with the control group 1, the zirconium-niobium alloy powder in a bone trabecular structure in the embodiment 1 was further sintered, indicating that a combination property of the bone trabecula was improved.

[0116] A physical compression test piece (size: 8*8*10 mm.sup.3) that has not been prepared with step 4) and 5) in the preparation method in the embodiment 1 and a physical compression test piece (size: 8*8*10 mm.sup.3) in the control group 1 were subjected to a compression performance test by an electronic universal testing machine (UTM5105, Shenzhen SUNS Technology Co., Ltd., and China). There were 5 physical compression test pieces respectively in the embodiment 1 and the control group 1. Results were shown in Table 1. The compressive yield strength of embodiment 1 is 546.72 MPa, better than that of Control Group 1 (P<0.05), suggesting that the solid part of the zonal trabecular femoral condylar component containing zirconium-niobium alloy on oxidation layer prepared by the present invention has excellent anti-compression performance.

TABLE-US-00001 TABLE 1 Anti-compression experiment results of the solid specimens of Control Group 1 and Embodiment 1 (x ± S, n = 5, *P < 0.05, compared with Control Group 1) Cross-sectional Yield Load Yield Strength Group Area (mm.sup.2) (kN) (MPa) Embodiment 1 64 34.99 ± 4.04* 546.72 ± 63.19* Control Group 1 64 23.59 ± 2.30  368.63 ± 35.92 

[0117] A bone trabecula compression specimens with pore diameter of 0.80 mm, porosity of 72%, through-hole rate of 100% of the Control Group 1 and the bone trabecula compression specimens with pore diameter of 0.80 mm, porosity of 72%, through-hole rate of 100% of Embodiment 1 (specimen size: 8*8*10 mm.sup.3) that has not been prepared with step 4) and step 5) of the above-mentioned preparation method, were subjected to a compression test by the electronic universal testing machine (UTM5105, Shenzhen SUNS Technology Co., Ltd., and China). Bone trabecula compression specimens of the Control Group 1 and the Embodiment 1 were 5 pieces each. The results are shown in Table 2. The compressive yield strength of Embodiment 1 is 18.39 MPa, significantly better than that of Control Group 1 (P<0.05), suggesting that the bone trabecula part of the zonal trabecular femoral condylar component containing zirconium-niobium alloy on oxidation layer prepared by the present invention has excellent anti-compression performance.

TABLE-US-00002 TABLE 2 Anti-compression experiment results of the bone trabecula specimens of Control Group 1 and Example 1 (x ± S, n = 5, *P < 0.05, compared with Control Group 1) Cross-sectional Yield Load Yield Strength Group Area (mm.sup.2) (N) (MPa) Embodiment 1 64 1177.24 ± 91.66* 18.39 ± 1.43* Control Group 1 64  926.12 ± 106.13 14.47 ± 1.66 

[0118] A cross-section of the zirconium-niobium alloy base and oxidation layer of the femoral condylar component of Embodiment 1, Embodiments 2 and 3 were observed by the scanning electron microscope (Crossbeam340/550, Zeiss, and Germany) (see FIG. 10). The oxidation layer thicknesses were 10.3 μm, 17.2 μm and 20.6 μm, and an oxygen-rich layer was positioned between the oxidation layer and the zirconium-niobium metal base to enhance the bonding force between the zirconium-niobium alloy base and the oxidation layer.

[0119] XRD (D8DISCOVER, Bruker, Germany) analyzed the oxidation layer of the femoral condylar component of Embodiment 1 (see FIG. 11). The oxidation layer contained monoclinic phase zirconia and tetragonal phase zirconia.

[0120] The microhardness measurement on the zonal trabecular femoral condylar component containing zirconium-niobium alloy on oxidation layer of Embodiments 1-3 was determined by a microhardness tester (MHVS-1000 PLUS, Shanghai AolongXingdi Testing Equipment Co., Ltd., and China), in which the load was 0.05 kg, the load time of the specimens was 20 s, and 8 points were taken for each specimen. The average hardness values measured in Embodiments 1-3 were 1948.6Hv, 1923.7Hv, and 1967.2Hv, suggesting that the oxidation layer of the zonal trabecular femoral condylar component containing zirconium-niobium alloy on oxidation layer of the present invention has high hardness.

[0121] Experiments have proved that the zirconium-niobium alloy powder fusion degree, anti-compression performance, anti-compression performance of the solid part, and metallographic organization, the oxidation layer's crystal structure, thickness and hardness for the bone trabecular part of the zonal trabecular femoral condylar component containing zirconium-niobium alloy on oxidation layer prepared in Embodiments 2 and 3, are similar to that prepared in Embodiments 1.

[0122] Experiments have proved that, for the bone trabecular part of the zonal trabecular femoral condylar component containing zirconium-niobium alloy on oxidation layer prepared in Embodiments 2 and 3, its zirconium-niobium alloy powder fusion degree, anti-compression performance, anti-compression performance of the solid part, and metallographic organization, the oxidation layer's crystal structure, thickness and hardness, are similar to that prepared in Embodiments 1.