A METHOD OF MANUFACTURING A COMPOSITE BLADE

Abstract

There is disclosed a method of manufacturing a composite blade, and the composite blade. The method comprises a lay-up operation comprising laying up fibre reinforcement material on an untwisted lay-up surface to make a blade pre-form and a forming operation comprising forming the blade pre-form to introduce twist in the blade pre-form.

Claims

1. A method of manufacturing a composite blade, the method comprising: a lay-up operation comprising laying up fibre reinforcement material on an untwisted lay-up surface to make a blade pre-form; and a forming operation comprising forming the blade pre-form to introduce twist in the blade pre-form.

2. The method according to claim 1, wherein the lay-up operation comprises laying-up two or more portions of the blade pre-form onto the lay-up surface and subsequently combining the two or more portions together at an interface to form the blade pre-form.

3. The method according to claim 2, wherein the interface between the two or more portions corresponds to a camber line of the composite blade.

4. The method according to claim 1, wherein the lay-up operation comprises laying-up unitary ply sheets, such that at least some ply layers of the pre-form consist of a respective portion of a unitary ply sheet.

5. The method according to claim 1, wherein the lay-up operation comprises laying-up fibre reinforcement material to provide a multi-blade pre-form, wherein the multi-blade pre-form is cut into individual blade pre-forms before individually forming each of the blade pre-forms in respective forming operations.

6. The method according to claim 4, wherein the lay-up operation comprises laying-up fibre reinforcement material to provide a multi-blade pre-form, wherein the multi-blade pre-form is cut into individual blade pre-forms before individually forming each of the blade pre-forms in respective forming operations, and wherein at least some of the unitary ply sheets of the multi-blade pre-form extend over a region corresponding to at least two of the individual blade pre-forms.

7. The method according to claim 1, wherein the blade pre-form is twisted by at least 15 degrees around a span-wise axis of the blade pre-form in the forming operation.

8. The method according to claim 1, wherein the lay-up surface is curved in only one dimension.

9. The method according to claim 8, wherein the lay-up surface is curved about a chord-wise axis of the blade.

10. The method according to claim 1, wherein an aerofoil region of the lay-up surface corresponding to an aerofoil portion of the blade pre-form is substantially flat, and a root region of the lay-up surface corresponding to a root portion of the blade pre-form departs from the plane of the aerofoil region of the lay-up surface.

11. The method according to claim 1, wherein the lay-up surface is substantially flat in a region corresponding to a root to a tip of the blade pre-form.

12. The composite blade manufactured by a method in accordance with claim 1.

Description

DESCRIPTION OF THE DRAWINGS

[0027] Embodiments will now be described by way of example only, with reference to the Figures, in which:

[0028] FIG. 1 is a sectional side view of a gas turbine engine;

[0029] FIG. 2 shows a side view of a composite fan blade;

[0030] FIG. 3 shows a sectional side view of an apparatus laying-up a portion of a blade pre-form;

[0031] FIG. 4 shows a sectional side view of a blade pre-form made from two portions;

[0032] FIG. 5 is a flow chart of a method of manufacturing a composite blade;

[0033] FIG. 6 is a flow chart of a method of manufacturing multiple composite blades at once; and

[0034] FIG. 7 shows a plan view of a lay-up surface having a multi-blade pre-form.

DETAILED DESCRIPTION

[0035] FIG. 1 illustrates a gas turbine engine 10 having a principal rotational axis 9. The engine 10 comprises an air intake 12 and a propulsive fan 23 that generates two airflows: a core airflow A and a bypass airflow B. The gas turbine engine 10 comprises a core 11 that receives the core airflow A. The engine core 11 comprises, in axial flow series, a low pressure compressor 14, a high-pressure compressor 15, combustion equipment 16, a high-pressure turbine 17, a low pressure turbine 19 and a core exhaust nozzle 20. A nacelle 21 surrounds the gas turbine engine 10 and defines a bypass duct 22 and a bypass exhaust nozzle 18. The bypass airflow B flows through the bypass duct 22. The fan 23 is attached to and driven by the low pressure turbine 19 via a shaft 26 and an epicyclic gearbox 30.

[0036] In use, the core airflow A is accelerated and compressed by the low pressure compressor 14 and directed into the high pressure compressor 15 where further compression takes place. The compressed air exhausted from the high pressure compressor 15 is directed into the combustion equipment 16 where it is mixed with fuel and the mixture is combusted. The resultant hot combustion products then expand through, and thereby drive, the high pressure and low pressure turbines 17, 19 before being exhausted through the nozzle 20 to provide some propulsive thrust. The high pressure turbine 17 drives the high pressure compressor 15 by a suitable interconnecting shaft 27. The fan 23 generally provides the majority of the propulsive thrust. The epicyclic gearbox 30 is a reduction gearbox.

[0037] Other gas turbine engines to which the present disclosure may be applied may have alternative configurations. For example, such engines may have an alternative number of compressors and/or turbines and/or an alternative number of interconnecting shafts. By way of further example, the gas turbine engine shown in FIG. 1 has a split flow nozzle 20, 22 meaning that the flow through the bypass duct 22 has its own nozzle that is separate to and radially outside the core engine nozzle 20. However, this is not limiting, and any aspect of the present disclosure may also apply to engines in which the flow through the bypass duct 22 and the flow through the core 11 are mixed, or combined, before (or upstream of) a single nozzle, which may be referred to as a mixed flow nozzle. One or both nozzles (whether mixed or split flow) may have a fixed or variable area. Whilst the described example relates to a turbofan engine, the disclosure may apply, for example, to any type of gas turbine engine, such as an open rotor (in which the fan stage is not surrounded by a nacelle) or turboprop engine, for example. In some arrangements, the gas turbine engine 10 may not comprise a gearbox 30.

[0038] The geometry of the gas turbine engine 100, and components thereof, is defined by a conventional axis system, comprising an axial direction (which is aligned with the rotational axis 9), a radial direction (in the bottom-to-top direction in FIG. 1), and a circumferential direction (perpendicular to the page in the FIG. 1 view). The axial, radial and circumferential directions are mutually perpendicular.

[0039] FIG. 2 shows a side view of a composite blade 100. In this example, the blade 100 is a fan blade having a modern twisted shape and comprises a root portion 102 and an aerofoil portion 104. The fan blade 100 extends from a root base 106 on the root portion 102 to a tip 108 on the aerofoil portion 104 along a span-wise axis 20. The aerofoil portion 104 is twisted with respect to the root portion 102 about the span-wise axis 110. The root portion 102 is configured to be retained in a hub of an engine.

[0040] FIG. 3 shows a side sectional view of a lay-up apparatus 130 for laying-up a portion 132 of a blade pre-form 150 (shown in FIG. 4). The lay-up apparatus 130 comprises a lay-up surface 134 and a lay-up head 136 which, in this example, is configured to apply layers of fibre reinforcement material 138 in the form of tape or tows to the lay-up surface 134 or on composite material already on the lay-up surface 134. In other examples, the lay-up head may be configured to pick up and place unitary sheets of fibre reinforcement material on the lay-up surface as will be described below.

[0041] In this example, the portion 132 of the blade pre-form 150 corresponds to one half of the blade pre-form 150. In other examples, the portion of the blade pre-form 150 may comprise more or less than 50% of the blade pre-form.

[0042] FIG. 4 shows a corresponding blade pre-form 150 which, in this simplified example, comprises two identical portions 132 made with the apparatus 130 which are joined along an interface 160. The interface 160 corresponds to the camber line of the composite blade 100 when the blade pre-form 150 is cured. In other words, the interface 160 corresponds to an equal thickness distribution on each side of the interface 160.

[0043] In some examples, the portions of the blade pre-form may not be identical. In other examples the interface may be any line through the blade pre-form and the thickness distribution on either side of the interface may be unequal. In some examples, there may be more than two portions combined to make the blade pre-form or the blade pre-form may be made in a single portion on a lay-up apparatus.

[0044] The blade pre-form 150 comprises an aerofoil portion 152 and a root portion 154 and extends from a root base 156 to a tip 158, which correspond to the root base 106 and the tip 108 respectively of the composite blade 100.

[0045] Referring back to FIG. 3, the lay-up surface 134 has a flat surface profile, and is untwisted. In some examples, the lay-up surface may be curved along only one dimension, such as along a span-wise direction of the blade pre-form 150 (i.e. curved about a line corresponding to a chord-wise direction). In other examples, the lay-up surface may be flat in an aerofoil region corresponding to the aerofoil portion of the blade portion 132, and the lay-up surface may depart from the plane of the aerofoil region of the lay-up surface in a root region of the lay-up surface corresponding to the root portion of the blade portion 132. This may be particularly useful when the blade pre-form is laid-up in a single portion, as it may permit the maximum displacement in the root portion to be minimised by offsetting the lay-up surface from the relatively thicker root below the lay-up surface for the relatively thinner aerofoil.

[0046] FIG. 5 is a flow chart showing steps of a method 200 of manufacturing the composite blade 100, which will be described by way of example with reference to the above examples. In step 202, fibre reinforcement material such as pre-impregnated carbon fibre reinforced resin, is laid-up on an untwisted lay-up surface in a lay-up operation to make a portion 132 of the blade pre-form 150.

[0047] The portion 132 may be made by laying-up tows or tapes of fibre reinforcement material. In other examples, the portions may be laid up by picking up and placing unitary ply sheets of fibre reinforcement material on top of one another (or upon one or more layers of tows or tapes) so that at least some of the ply layers of the blade pre-form consist of a respective unitary ply sheet. In some examples, the unitary ply sheets may be placed such that all of the ply layers in the blade pre-form consist of the respective unitary ply sheets.

[0048] Whether forming layers of a pre-form by tows, tapes or unitary ply sheets, in order to form a complex geometry it is typically necessary to form the layer to have a curved boundary (i.e. curved within the plane of the layer). For unitary ply sheets, this may be done by cutting the ply sheet to size. When laying up a pre-form using tows or tapes, the boundary may be formed by an applicator head cutting the tows or tapes at an appropriate location. This may result in a saw-tooth profile in the edge of the boundary, the effects of which can be mitigated by using relative narrow tows or tapes.

[0049] In step 204, portions 132 of the blade pre-form 150 are combined at an interface 160 to form the blade pre-form 150. As described above, in some examples, two identical portions may be joined together to form the blade pre-form. In other examples, there may be two different portions which are joined together to form the blade pre-form. In further examples, there may be more than two portions combined to form the blade pre-form.

[0050] As explained above with reference to FIG. 4, the blade pre-form may alternatively be laid-up in one part in step 1202. In this case, step 204 is omitted as it is not necessary to combine more than one portion to form the blade pre-form.

[0051] Since the lay-up surface 134 of the apparatus 130 is untwisted, when the blade pre-form 150 is made, it requires further processing in order to form the desired shape of the composite blade 100. Therefore, in step 206, the blade pre-form 150 is formed in a forming operation to introduce a twist along the aerofoil portion 152 of the blade pre-form 150 relative to the root portion 154 of the blade pre-form 150.

[0052] In this example, the forming operation comprises a double diaphragm forming process in which the blade pre-form 150 is placed between two diaphragms. The area between the diaphragms is evacuated to compress the blade pre-form 150 between the diaphragms. The diaphragms and blade pre-form 50 are driven against a mould surface. The blade pre-form may be driven against a mould surface by applying pressure to an opposing side of the blade pre-form and/or by evacuating the area between the mould surface and the diaphragm and blade pre-form 150. The blade pre-form 150 therefore adopts the shape of the mould surface.

[0053] In other examples, the forming operation may comprise any type of diaphragm forming process, or forming between two mould surfaces.

[0054] In this example, the forming operation twists the aerofoil portion 152 by up to 60 degrees relative the root portion 154 when it is driven against the mould surface, for example at least 15 degrees. In other examples, the angle of twisting introduced to the aerofoil portion 152 relative the root portion 154 may be different, and may be more than 60 degrees, for example up to 90 degrees. Such twisting during forming has been found to reduce wrinkling in the pre-form as the twisting applies tension to the fibres in the blade pre-form 150.

[0055] In step 208, pressure and heat is applied to the blade pre-form 150 to cure it, to form the composite blade 100. The pressure and heat may be provided by an autoclave, for example. Once cured the composite blade 100 may require machining to finish.

[0056] FIG. 6 is a flow chart showing steps of a method 300 for forming multiple composite blades 100 at once.

[0057] In step 302 fibre reinforcement material is laid-up on an untwisted lay-up surface 234 in a lay-up operation to make a multi-blade pre-form 250. The multi-blade pre-form 250 is a pre-form corresponding to more than one blade pre-form 150, as shown by way of example in FIG. 7.

[0058] In some examples, the lay-up operation comprises laying up tows or tapes of fibre reinforcement material such as pre-impregnated carbon fibre reinforced resin. In other examples, the lay-up operation may comprise picking up and placing unitary ply sheets of fibre reinforcement material on top of one another so that at least some of the unitary ply sheets of the multi-blade pre-form extend over a region corresponding to at least two blades.

[0059] The multi-blade pre-form may also be laid-up in portions in a similar manner to step 202 of the method 200 described with reference to FIG. 5. In such examples, the portions of the multi-blade pre-form are combined to make the multi-blade pre-form before proceeding to step 304, or each set of pre-form portions for a respective blade are combined after step 304 to make multiple blade pre-forms 150.

[0060] In step 304, the multi-blade pre-form is cut into individual blade pre-forms 150.

[0061] In step 306, the individual blade pre-forms 150 are formed in a forming operation to introduce a twist in the same manner as described in step 206 for the single blade pre-form 150 method.

[0062] In step 308, pressure and heat is applied to each of the blade pre-forms 150 to cure them in a similar manner as described in step 208 of the method 200. Once cured, the composite blades 100 may require machining to finish.

[0063] By laying-up on an untwisted lay-up surface, the lay-up operation is more efficient than laying-up on a twisted lay-up surface. The simplified geometry of the lay-up surface allows tows or tapes of material to be applied much more quickly, with less complex machinery.

[0064] In previously known lay-up operations for blades, the complex geometry of a near net shape lay-up surface limits the width of tows which can be used without bridging occurring during lay-up. Furthermore, traversing over a complex geometry limits the rate at which tows can be laid up. Due to the simplified geometry of the lay-up surface 134, tows or tapes 138 for laying-up the blade or portions of the blade may be wider than for a twisted lay-up surface, or a unitary sheet or broadgood ply may be applied to form a layer of the pre-form. By using wider tows or tapes or broadgood plies, it may be faster to lay-up a layer of the preform (e.g. by covering more surface area in one pass of the lay-up head 136 than previous methods, thereby improving the speed and efficiency of lay-up of a blade pre-form, or by simply applying a broadgood ply). Further, since the lay-up head 136 does not need to traverse over a complex geometry, the speed of the lay-up head 136 itself can also be increased.

[0065] Further, equipment may require fewer degrees of freedom to navigate the contours of the geometry without intersecting the lay-up surface or partially laid-up pre-form (e.g. only translational movement, without rotational movement).

[0066] If the lay-up surface is untwisted, whole sheets of fibre reinforcement material may be applied to the lay-up surface in one go, thereby further simplifying the machinery required for laying-up the fibre reinforcement material, as well as improving the speed of the lay-up operation.

[0067] With a flat lay-up surface, or a lay-up surface having a curve in one dimension, an alternative method of making multiple blades at once includes using a lay-up machine having multiple lay-up heads side-by-side which move together and each simultaneously lay-up a blade or portions of a blade pre-form. Once the blade pre-forms are provided, the method proceeds to step 306 of the method 300 for making multiple composite blades 100.

[0068] It will be understood that the invention is not limited to the embodiments above-described and various modifications and improvements can be made without departing from the concepts described herein. Except where mutually exclusive, any of the features may be employed separately or in combination with any other features and the disclosure extends to and includes all combinations and sub-combinations of one or more features described herein.