INTERLOCKING INFILL FOR ADDITIVE MANUFACTURING PRODUCTS

Abstract

The present invention provides a method improving the shear strength of a 3D manufactured product by inserting infill into the interstices between the bead layers.

Claims

1. A method for increasing the shear strength of an additive manufactured product comprising: lowering the axis to be strengthened by reducing the bead height of alternating beads on the uppermost layer and lowermost layer.

2. A method for increasing the shear strength of a molded additive manufactured product comprising: (a) creating a wall from a series of at least three layers of beads of suitable material, the layers having alternating widths to create an interstitial gap between the first and third layers, the first layer having a width greater than the width of the second layer; (b) depositing a layer of infill into the gap between the first and third layers; (c) repeating steps (b) and (c) sequentially to create gaps between the alternating greater width layers; and (d) depositing a layer of strengthening infill in the respective gaps; and wherein the strengthening infill extends into abutment with the wall of the lesser width bead layers.

3. The method of claim 2 wherein the bead height of the beads in the lowermost layer and the uppermost layer alternate between a first height H1 and a second height H.

4. The method of claim 2 which further comprises: repeating steps (b) and (c) sequentially to create gaps between the alternating greater width layers.

Description

BRIEF DESCRIPTION OF THE DRAWING

[0011] FIGS. 1A and 1B are perspective views illustrating a typical grid configuration according to the prior art;

[0012] FIG. 2 is a plan view of a grid with various percentages of infill in an additive manufactured product;

[0013] FIG. 3 is a side view of a typical prior art printed object;

[0014] FIG. 4A is a perspective view showing the utilization of the interlocking infill in accordance with the present invention in a standard bead configuration;

[0015] FIG. 4B is a side view showing the utilization of the interlocking infill in accordance with the present invention in a standard bead configuration; and

[0016] FIG. 5 is a view similar to FIG. 4A but using an offset bead arrangement.

DESCRIPTION OF THE INVENTION

[0017] By way of background and with reference to FIGS. 1, 1A and 2 there is depicted therein a standard mold configuration utilized during a 3D printing or additive manufacturing process.

[0018] As is known to the skilled artisan a typical additive manufactured product, generally denoted at 10, includes a base or platform 12 and a plurality of upstanding walls 14, 14′, etc. which are configured to the shape of the product to be manufactured. Ordinarily, the walls are substantially non-porous and terminate near an upper perimetral top surface 16. The walls typically comprise a plurality of adjacent layers 18, 18′, which for illustration purposes, extend in the direction of the arrow A (FIG. 1B).

[0019] Typically, infill is deposited in layers of beads 19, 19′, etc. in a direction B, and, depending on the nature of the product or object to be produced, can have various porous densities such as those shown in FIG. 2. As noted, the innermost layers which define the wall create abutments for the infill below.

[0020] In any event, though, the products being manufactured are created by the layers 18, 18′, etc. being deposited atop one another with one or more sequential series of beads being created adjacent thereto as to create a wall of the printed object.

[0021] However, as noted above, using present printing processes gaps 22, 22′ are created in the spaces or interstices between the infill layers along both the length and width thereof, which diminishes the shear strength of the so-produced product.

[0022] According to the present invention and with reference to FIGS. 4A and 4B and in a first embodiment hereof, a plurality of bead layers 40, 40′, etc. are deposited to create a wall 30. The layers 40, 42, 44′,etc. have alternating widths W and W1, respectively.

[0023] Infill strengthening bead layers 50, 52′, etc. each substantially perpendicular or normal or otherwise angularly disposed with respect to an associated layer 40, 42, 44, etc., extend toward the wall(s) and into abutment with the innermost layers and terminal walls along the extent thereof into the gaps between overlying layers 22, 22′, etc.

[0024] The strengthening infill layer 50, 52, are substantially parallel to each other and abut with an associated portion of the bead layer wall.

[0025] The strengthening infill 50, 52′, 54, etc., abuts against a wall portion 26 of the innermost terminal wall of the layers created between the layers of width W.

[0026] The strengthening infill 50, 52, 54, etc., can have any desired configuration such as the U-shape shown herein.

[0027] The process hereof generally comprises depositing a first bead layer 40 from beads 17 generally along an X-axis and having the width W. A second layer 41 of beads 17′ is then deposited thereatop and having the width W1. Thereafter, a third layer 44 is deposited atop the second layer 42 and has the width W. This process is repeated until the desired height of the wall is achieved. As shown, the innermost beads of the layers each have wall a terminus or wall 26. Due to the difference in widths of the layers, the gaps 22, 22′ etc. are created therebetween, as shown.

[0028] Abutting strengthening infill layers 50, 52 are then deposited to extend laterally into abutment with the walls of the innermost layers having Width W1 at least intermittently along the extent thereof.

[0029] As shown in the drawing the gap which is associated with the alternating terminal walls between the first, third, fifth, etc. layers is filled with the infill strengthening material 50, 52′, etc.

[0030] By having the interstitial infill hereof disposed within the gaps 22, 22′, etc., created by the layering, the shear and tensile strength of the object is further improved.

[0031] As shown in FIGS. 4 and 4B, the interstitial infill layers 50, 52 are complementary to the abutting layers and thus are alternating therewith as well as the balance of the bead layers.

[0032] According to a second embodiment hereof and with reference to FIG. 5, the present invention has particular utility with the offset bead figuration disclosed and claimed in the aforesaid co-pending application. According to the disclosure thereof, the beads 110, 112 on the top and bottom layers are deposited in alternating heights of H and H1 such that every other bead in the top and bottom layer is of a first height and the beads therebetween are of a second height which is less than that of the height of the first beads. As a result, there is a lack of parallelism in the various intermediate layers which, thereby, improves the shear strength of the so-manufactured product.

[0033] In either embodiment hereof, the interstitial strengthening infill layers are formed from any of the suitable infill materials referenced above including, for example, glass fiber-filled carbonate, PEKK, PEEK and ABS, ASA, PLA, PETG, polypropylene, TPU, nylon, polycarbonate, PSU, PPSU, PESU, PEI, as well as metals, ceramics, sand or cement.

[0034] In either embodiment the layers of the interlocking infill layers provide improved strength to the object.

[0035] In carrying out the process a conventional extruder such as that sold under the mask Titan may be used herein. This is an extruder which deposits either infill filaments or beads vertically and which moves in the X, Y and Z axes in response to computer controls in the manner well known to the skilled artisans.

[0036] Having, thus, described the invention, what is claimed is: