Heat transfer label

Abstract

The present invention relates to heat transfers that include silicone based heat transfer inks and digitally printed toner images, particularly for use on fabrics, apparel items, garments and accessories. The present subject matter is especially suitable for use in heat-transferable labeling or creating embellishments on polyester fabrics and garments.

Claims

1. A heat transfer label comprising: a support portion having a label carrier and a release layer; wherein the label carrier comprises at least one of cellulosic film and polymeric film; and wherein the release layer comprises polymer wax; and a transfer portion, said transfer portion being positioned over the support portion release layer for transfer of the transfer portion from the support portion to a fabric substrate under conditions of heat and pressure, the transfer portion comprising: a heat transfer silicone ink layer having a first surface and a second surface, the first surface being exposed to permit direct contact with a fabric substrate to be labeled; an image layer comprising a printed toner layer; and a compatibility layer in contact with the second surface of the heat transfer silicone ink layer, wherein the compatibility layer adheres the toner layer to the heat transfer silicone ink layer, and wherein the compatibility layer is formed from a composition comprising decamethyltetrasiloxane, tetraethyl orthosilicate and Titanium (IV) butoxide.

2. The heat transfer label of claim 1, wherein the heat transfer silicone ink layer comprises: silicone ink base composition; a pigment; and a heat-transfer adhesion promoter being one or more of the group comprising: a hydrogen bonded silicon; an organosilane; and a metal chelate.

3. The heat transfer label of claim 2, wherein the heat transfer silicone ink layer further comprises at least one heat transfer adhesive.

4. The heat transfer label of claim 2, wherein the compatibility layer is transparent.

5. The heat transfer label of claim 2, wherein the compatibility layer is up to 1 gsm.

6. The heat transfer label of claim 2, wherein the image layer further comprises a printed water based ink layer.

7. The heat transfer label of claim 1, wherein the compatibility layer is configured to crosslink the polymers of the toner image layer.

8. The heat transfer label of claim 1, wherein the compatibility layer further comprises ante silica precursor.

9. The heat transfer label of claim 1, wherein the compatibility layer further comprises silanes.

10. The heat transfer label of claim 1, wherein the compatibility layer further comprises colloidal silica dispersed in fluid.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) FIG. 1 is a schematic section view of a first embodiment of a heat transfer label assembly according to the present disclosure;

(2) FIG. 2 is a schematic section view of a second embodiment of a heat transfer label assembly that further includes a water-based ink layer according to the present disclosure;

(3) FIG. 2A provides a further schematic section view of a further embodiment of the heat transfer label shown in FIG. 2;

(4) FIG. 2B illustrates a further schematic section view of a further embodiment of the heat transfer label shown in FIG. 2;

DETAILED DESCRIPTION

(5) Detailed embodiments of the present invention are disclosed herein; however, it is to be understood that the disclosed embodiments are merely exemplary of the invention, which may be embodied in various forms. Therefore, specific details disclosed herein are not to be interpreted as limiting, but merely as a basis for the claims and as a representative basis for teaching one skilled in the art to variously employ the present invention in virtually any appropriate manner.

(6) FIG. 1 is a schematic representation of a heat transfer label construction and illustrates a first embodiment that achieves secure transfer of a desired image, design and/or indicia to a fabric substrate. The label construction 10 includes a support portion 20 and a transfer portion 30. Support portion 20 includes a label carrier 22 and a release layer or coating 24.

(7) The support portion 20 typically has the function of providing mechanical strength to the label assembly, allowing handling such as being wound up in a roll for storage, stacking, and as a label feed for mechanized operations. Typical label carrier sheets are cellulosic or polymeric film, such as heat stabilized polyethylene terephthalate (PET). The back of the film may be coated against static build up and blocking when the films are stacked against each other. In one embodiment, the thickness of the carrier is 4 mil (100 μm). Thinner films, such as those having a thickness of 50 to 75 μm, may also be used. Label carrier 22 may also be coated with one or more layers to provide a matting effect.

(8) Release layer 24 is coated or printed on carrier 22. In one embodiment, a release layer is coated on both sides of the carrier 22. The release layer also functions as a thermal release to permit the separation of the transfer portion 30 from the support portion 20 after the heat transfer. The release layer may be based on polymer waxes that manifest affinity for the toners used in commercial digital printing, such as the digital printing process of HP® Indigo® printers. Examples of suitable polymeric waxes for the release layer include polyethylene acrylic and methacrylic acids (EAA and EMA), polyolefin waxes that are made polar by an oxidationprocess. The release layer may also contain anti-blocking additives, which facilitate the release layer detaching from the carrier when the latter is peeled during the heat transfer process. Examples of release additives are polar waxes compatible with EAA, such as carnauba and montan waxes. Other release additives include polytetrafluoroethylene particles either in neat form or as composite particulates with other polyolefins. In one embodiment, the preferred coat weight of the release layer is in the range of 0.5 to 5 gsm.

(9) Transfer portion 30 generally includes a toner image layer 32, compatibility layer 34 overlying the toner image layer 32, and a heat transfer silicone ink layer 36. The release layer 24 receives the toner image layer 32. Toner image layer 32 is generally digitally printed using a liquid electrophotographic process by which electrically-charged liquid inks, i.e., toners, are dried and applied to the release layer via a thermal blanket. Liquid toners typically include pigments, binder, carrier solvent, dispersing agents and charge additives. The toner image layer 32 may be printed using HP® Indigo® digital machines in sheet-fed format. It should be understood that other printing technologies, including a continuous or roll-to-roll format may be used.

(10) Overlying toner image layer 32 is compatibility layer 34, which fixes the toner image and provides an interface for the subsequently applied heat transfer silicone based ink layer 36. In one embodiment, the compatibility layer includes the following components:

(11) TABLE-US-00001 Component Weight % Silicone fluid: decamethyltetrasiloxane 99.4% (Dow Corning OS 30) Tetraethyl orthosilicate (TEOS, Aldrich) 0.5% Titanium (IV) butoxide 0.1%

(12) The compatibility layer 34 may interact with the polymers of the underlying toner image layer 32 to strengthen the toner layer against water and abrasion. For example, the compatibility layer could crosslink the polymers of the toner image layer if the polymers of the toner image layer contain chemical moieties such as hydroxyl or carboxyl groups. In addition, the compatibility layer may block and restrict possible migration of contaminants originating in the release layer from reaching the overlying heat transfer silicone ink layer 36. Contaminants such as amines species could poison and render inactive the Pt hydrosilylation catalyst used in curing the silicone inks.

(13) The compatibility layer could also include silica precursors such as organic silicates (tetraethyl orthosilicate and similar, organic silanes that possess chemical moieties capable to reach with potential chemical toner functionality (hydroxyl, carboxyl). Examples of these reactive silanes include (3-Glycidyloxypropyl)trimethoxysilane, 2-(3,4-Epoxycyclohexyl)ethyltriethoxysilane). The compatibility layer also could include silanes that are able to participate in the in hydrosililation chemical curing of the silicone ink they are interfacing. One example of such molecule is a Trimethoxy(vinyl)silane coupling agent.

(14) The compatibility 34 layer may also contain colloidal silica dispersed in a fluid (solvent or water with solvent). Preferred are the silica known to exhibit elongated or string like particles. Examples of such colloidal silicas are Nissan Chemical's ORGANOSILICASOL: IPA-ST-UP and MEK-ST-UP.

(15) The compatibility layer 34 may be coated onto the toner image layer using a Meyer Rod (numbers 6-10) and dried in an oven at 100° C. for 1 minute, resulting in a thin transparent compatibility layer that is 1 gsm or less.

(16) Overlying the compatibility layer 34 is a heat transfer silicone ink layer 36. In most applications, the heat transfer silicone ink layer 36 is a white layer. In one embodiment, the heat transfer silicone ink layer is prepared in accordance with the composition described in US Patent Publication US 2015/0004336, the contents of which are incorporated herein by reference.

(17) In one embodiment, the heat transfer silicone ink layer 36 is a heat-transfer textile ink that includes: (a) a silicone ink base composition; (b) a pigment; and (c) a heat-transfer adhesion promoter being one or more of the group that includes: (i) a hydrogen bonded silicon; (ii) an organosilane; and (iii) a metal chelate.

(18) Suitable pigments are known in the art, and are not further discussed in detail. They include all types of pigments, inks, tinctures, dyes, colorants and “colors”, and are included in the relevant proportions known in the art to provide the required image quantity and quality. Suitable pigments and dyes include but are not limited to carbon black, titanium dioxide, chromium oxide, bismuth vanadium oxide and the like. The pigments may be dispersed in the heat-transfer textile ink composition at the ratio of 25:75 to 70:30 to the silicone ink base.

(19) The heat transfer silicone ink may include any proportions and/or ratios of the heat transfer adhesion promoters listed above, such as in the amount of 0.1 wt % to 10 wt %, alternatively in the range 0.5 wt % to 5 wt %.

(20) The hydrogen bonded silicon of group (c) (i) may include

(21) ##STR00001##

(22) wherein m is in the range 0 and 120, and n is in the range 1 to 120. Alternatively, one or more different hydrogen bonded silicones may be included as the adhesion promoter.

(23) The organosilane of group (c) (ii) may be a silane, an oligomeric reaction product of the silane, or a combination thereof, in particular an alkoxysilane. Alternatively, the organosilane may include either: (i) the formula R3bSiR4; (4-b), where each is independently a monovalent organic group; each R4 is an alkoxy group; and b is 0, 1, 2, or 3; or (ii) the formula R5cR6dSi(OR5)4-(c+d) where each R5 is independently a substituted or unsubstituted, monovalent hydrocarbon group having at least 1 carbon atom and each R6 contains at least one SiC bonded group having an adhesion-promoting group, such as amino, epoxy, mercapto or acrylate groups, c is 0, 1 or 2, d is 1 or 2, and the sum of c+d is not greater than 3, or a partial condensate thereof.

(24) The organosilane may include an alkoxysilane exemplified by a dialkoxysilane, such as dialkyldialkoxysilane or a trialkoxysilane, such as an alkyltrialkoxysilane or alkenyltrialkoxysilane, or partial or full hydrolysis products thereof, or another combination thereof.

(25) The metal chelate of group (c)(iii) may include any suitable metal (such as zirconium (IV) or titanium), in the form of suitable chelate complexes such as tetraacetylacetonate, hexafluoracetylacetonate, trifluoroacetylacetonate, tetrakis (ethyltrifluoroacetylacetonate), tetrakis (2,2,6,6-tetramethyl-heptanedionato), dibutoxy bis(ethylacetonate), diisopropoxy bis(2,2,6,6-tetramethyl-heptanedionato), or β-diketone complexes, including alkyl-substituted and fluoro-substituted forms thereof. Alternatively, the metal chelate is a zirconium chelate, optionally zirconium acetyl acetonate, such as zirconium tetrakisacetylacetonate (also termed “Zr(AcAc)4”), (including alkyl-substituted and fluoro-substituted forms thereof).

(26) The silicone ink base composition may include one or more silicone ink base compositions known in the art, and the invention is not limited thereto. Alternatively, the silicone ink base is as defined in US Patent Publication US 2007/141250, incorporated herein by reference. Alternatively, the silicone ink base composition for the heat transfer textile ink may include:

(27) (A) 100 parts by weight of a liquid polydiorganosiloxane containing at least two alkenyl radicals in each molecule,

(28) (B) an organohydrogenpolysiloxane containing at least three silicon-bonded hydrogen atoms in each molecule, in an amount that the molar ratio of the total number of the silicon bonded hydrogen atoms in this ingredient to the total quantity of all alkenyl radicals in ingredient (A) is from 0.5:1 to 20:1,

(29) (C) from 5 to 50 parts by weight of a reinforcing filler, based on the amount of ingredient (A),

(30) (D) from 0.05 to 4.5 parts by weight of a polydiorganosiloxane-polyether copolymer containing from 5 to 50 percent by mole of the polyether, based on 100 parts by weight of the combined weight of ingredients (A), (B), and (C), and

(31) (E) a hydrosilylation catalyst.

(32) In one embodiment, the heat transfer silicone ink layer further includes one or more heat transfer adhesives. Such adhesives are well known for this purpose. For example, the heat transfer adhesive may include a thermoplastic polymer resin.

(33) Curing of the heat transfer silicone ink layer is catalyzed by ingredient (E), which may be a metal selected from the platinum group of the periodic table, or a compound of such metal. The metals include platinum, palladium and rhodium. Platinum and platinum compounds are preferred due to the high activity of these catalysts in hydrosilylation reaction.

(34) The label of FIG. 1 may be transferred to a substrate such as a fabric or textile by placing the label assembly over the substrate, applying heat, and removing the support structure to leave the transfer portion as a lasting image on the substrate.

(35) FIG. 2 is a schematic representation of another heat transfer label construction that includes a water-based image layer in addition to a toner image layer. The label construction 110 includes a support portion 120 and a transfer portion 130. Support portion 120 includes a label carrier 122 and a release layer or coating 124.

(36) Transfer portion 130 is similar in most respects to transfer portion 30, the principal difference between the two is that a water based image layer 133 is included in the construction. The water based ink layer 133 may be printed directly onto release liner 124 such that it does not overlap toner image layer 132. Alternatively, water based ink layer 133 may overlap portions of toner image layer 132. Alternatively, water based ink layer 133 may cover completely the toner layer 132. In this case the water based ink will contain the reactive ingredients need to fixate chemically the toner image. Water based ink layer 133 may be formed by screen printing, ink jet printing, gravure printing, flexographic printing, or the like.

(37) Compatibility layer 134 overlies toner image layer 132 and water based ink layer 133 to block and restrict possible migration of contaminants originating in the release layer or the water based ink from reaching the overlying heat transfer silicone ink layer 136. Contaminants such as amines species could poison and render inactive the Pt hydrosilylation catalyst used in curing the silicone inks. Not only are there volatiles amines used in producing the water based anionic polymer dispersions, there may also be amino group containing polymers in either the polymer backbone or at the polymer end (i.e., polyamides, polyurethanes, etc.)

(38) Overlying the compatibility layer 134 is heat transfer silicone ink layer 136. The label of FIG. 2 may be transferred to a substrate such as a fabric or textile by placing the label assembly over the substrate, applying heat, and removing the support structure to leave the transfer portion as a lasting image on the substrate.

(39) Attention is directed to FIG. 2A which shows an alternate embodiment of FIG. 2 in which the water based ink layer 133 substantially covers the image toner layer 132.

(40) FIG. 2B is a further embodiment of the heat transfer label of the present invention in which the water based ink layer 133 resides on top of the carrier and/or release layer 122, 124.

(41) In another embodiment of the heat transfer label construction, a compatibility additive is incorporated into a heat transfer silicone ink layer. The label construction includes a support portion and a transfer portion. Support portion includes a label carrier and a release layer or coating.

(42) Toner layer is printed onto release layer. Overlying toner layer is heat transfer silicone ink layer, which is formed from a composition that includes a compatibility additive and a silicone based heat transfer ink. In one embodiment, the silicone based heat transfer ink is prepared in accordance with the composition described in US Patent Publication US 2015/0004336, which is described in more detail above. In one embodiment, the compatibility additive includes the following components:

(43) TABLE-US-00002 Component Weight %* Silicone fluid: decamethyltetrasiloxane 10.0% (Dow Corning OS 30) Tetraethyl orthosilicate (TEOS, Aldrich) 0.5% Titanium (IV) butoxide 0.1% *based on the total weight of the heat transfer silicone ink layer

(44) The compatibility additive when incorporated into the silicone based heat transfer ink provides similar advantages as a separate compatibility layer, and does not interfere with the silicone crosslinking chemistry of the silicone based heat transfer ink.

(45) Other embodiments, besides those illustrated herein, may also be employed without departing from the scope of the present disclosure. For example, the label can be of a perimeter shape desired for a particular purpose other than the generally circular or cylindrical labels associated with a patch or insignia, for example, taking the form of a decorative embellishment, company logo, or artwork. Other options include enhancing the flexibility of the label or the like by minimizing the thickness and area covered by the second barrier layer, thereby providing improved label performance in terms of being able to better follow bendability or flow of the substrate to which the label is attached, such as fabric or clothing.

(46) It will be understood that the embodiments described above are illustrative of some of the applications of the principles of the present subject matter. Numerous modifications may be made by those skilled in the art without departing from the spirit and scope of the claimed subject matter, including those combinations of features that are individually disclosed or claimed herein. For these reasons, the scope hereof is not limited to the above description but is as set forth in the following claims, and it is understood that claims may be directed to the features hereof, including as combinations of features that are individually disclosed or claimed herein.