Method for enhancing tensile strength of carbon nanotube fiber aggregate

Abstract

The present invention relates to a method for enhancing tensile strength of a carbon nanotube (CNT) fiber aggregate, comprising dispersing a CNT fiber aggregate with chlorosulfonic acid (CSA), followed by thermal treatment, wherein a particular magnitude of tension is applied upon the thermal treatment, whereby the CNT fiber aggregate is increased in alignment level and tensile strength.

Claims

1. A method for improving tensile strength of an aggregate of carbon nanotube (CNT) fibers, comprising the steps of: 1) dispersing the aggregate of CNT fibers in chlorosulfonic acid (CSA); 2) treating the aggregate of CNT fibers dispersed in the CSA with a solvent for removing the CSA, thereby removing the CSA; and 3) treating by heating the aggregate of CNT fibers from which the CSA has been removed at 200 to 400° C. for 5 minutes to 2 hours; wherein tension is applied to at least one of the steps 1) to 3), and the tension/tex is applied in an amount of 2 to 50 cN/tex, and the ratio of the aggregate of CNT fibers to 100 parts by weight of the CSA in the step 1) is 0.01 to 1.0 parts by weight.

2. The method for improving tensile strength of the aggregate of CNT fibers according to claim 1, wherein tension is applied simultaneously with each of at least one of the steps 1) to 3).

3. The method for improving tensile strength of the aggregate of CNT fibers according to claim 1, wherein tensile is applied successively after the end of at least one of the steps 1) to 3).

4. The method for improving tensile strength of the aggregate of CNT fibers according to claim 1, wherein the solvent for removing the CSA in the step 2) is selected from the group consisting of acetone, ethanol and water.

5. The method for improving tensile strength of the aggregate of CNT fibers according to claim 1, wherein the heat treatment in the step 3) is performed under an atmosphere containing oxygen and an inert gas atmosphere.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) FIG. 1 is an illustration of an example of a process for improving tensile strength of an aggregate of CNT fibers according to the present invention.

(2) FIG. 2 is a result of the scanning electron microscope (SEM) analysis of shrinkage and alignment of an aggregate of CNT fibers according to the dispersion or non-dispersion of an aggregate of CNT fibers in CSA in Comparative Examples 1 to 5 and Examples 1 to 13.

(3) FIG. 3 is a graph showing relative tensile strength according to tension/tex applied to an aggregate of CNT fibers in Examples 1 to 13.

DETAILED DESCRIPTION

(4) The terms and words used in the present specification and claims should not be construed as limited to ordinary or dictionary meanings and should be interpreted with the meaning and concept consistent with the technical idea of the present invention based on the principle that the inventors can appropriately define the concepts of the terms to describe their invention in the best way.

(5) The method for improving tensile strength of an aggregate of CNT fibers according to the present invention comprises the steps of:

(6) 1) dispersing the aggregate of CNT fibers in chlorosulfonic acid (CSA);

(7) 2) treating the aggregate of CNT fibers dispersed in the CSA with a solvent for removing the CSA, thereby removing the CSA; and

(8) 3) treating by heating the aggregate of CNT fibers from which the CSA has been removed,

(9) wherein tension is applied simultaneously with each of at least one of the steps 1) to 3), or tension is applied successively after the end of at least one of the steps 1) to 3), and wherein the tension/tex is applied in an amount of 2 to 50 cN/tex or 3 to 40 cN/tex, or 3 to 40 cN/tex, or 5 to 35 cN/tex, or 10 to 30 cN/tex.

(10) Furthermore, the method for improving tensile strength of an aggregate of CNT fibers according to the present invention comprises the steps of:

(11) 1) treating the aggregate of CNT fibers with chlorosulfonic acid (CSA) to disperse CNTs constituting the aggregate of CNT fibers, thereby loosening the aggregate;

(12) 2) applying tension to the aggregate of CNT fibers dispersed in the CSA wherein the tension is applied in an amount of 2 to 50 cN/tex;

(13) 3) treating the aggregate of CNT fibers with a solvent for removing the CSA in order to wash and shrink the aggregate of CNT fibers; and

(14) 4) treating by heating the aggregate of CNT fibers.

(15) The method of the present invention will be described in detail in accordance with the respective steps as follows:

(16) Step 1): Dispersing of CNT

(17) CSA is added to disperse an aggregate of CNT fibers. Due to this treatment, the CNTs constituting the aggregate of CNT fibers are not entangled and dispersed well, and the aggregate is loosened. At this stage, the tension/tex can be applied to the aggregate of CNT fibers in an amount of 2 to 50 cN/tex.

(18) Step 2): Removal of CSA and shrinking of CNTs

(19) The loosened aggregate of CNT fibers is aligned. The aligned aggregate of CNT fibers is washed with a solvent for removing CSA such as acetone, ethanol or water. As a result, the dispersed aggregate of CNT fibers can be shrunk to maintain the aggregate shape. At this stage, the tension/tex can be applied to the aggregate of CNT fibers in an amount of 2 to 50 cN/tex.

(20) Step 3): Heat treatment

(21) The aggregate of CNT fibers is heat-treated to remove residual CSA or solvent for removing remained CSA in the aggregate of CNT fibers thereby further shrinking the aggregate of CNT fibers. The heat treatment may be performed under an atmosphere containing oxygen and an inert gas atmosphere, for example, under an air atmosphere at 200 to 400° C. for 5 minutes to 2 hours, for example at 300° C. for 30 minutes. At this stage, the tension/tex can be applied to the aggregate of CNT fibers in an amount of 2 to 50 cN/tex.

(22) An example of a process including the above steps is shown in FIG. 1 as an illustration of a process for improving tensile strength of an aggregate of CNT fibers.

(23) Hereinafter, the present invention will be described in more detail with reference to Examples. It will be apparent to those skilled in the art that the following examples are merely intended to be illustrative of the present invention and not to be construed as limiting the scope of the invention.

Examples 1 to 13

(24) As shown in FIG. 1, one end of an aggregate of CNT fibers (0.007 mg) was fixed to a glass rod and the other end of the aggregate of CNT fibers was connected to the weights, and the aggregate of CNT fibers was set so that the tension/tex was applied thereto in an amount of 3 to 40 cN/tex by controlling the weights in order to perform each of Examples 1 to 13. CSA (0.01 mL) as a CNT dispersant was sprinkled on the aggregates of CNT fibers by a spuit. When the CSA treatment was finished, acetone (1 mL) was sprinkled onto the aggregates of CNT fibers by a spuit to remove residual CSA and to shrink the aggregates of CNT fibers. The aggregates of CNT fibers was heat-treated at 300° C. for 30 minutes in an air atmosphere to remove remained CSA and acetone in the aggregates of CNT fibers. The relative tensile strength of the heat-treated aggregates of CNT fibers was measured at a speed of 2 mm/min using FAVIMAT+ instrument of Textechno, Germany (load cell range: 210 cN, gauge length: 2.0 cm). The measurement results are shown in Table 1 below. In addition, the relative tensile strength obtained according to the tension/tex applied to the aggregates of CNT fibers is shown as a graph in FIG. 3.

Comparative Examples 1 to 3

(25) Aggregates of CNT fibers were tested in the same manner as in the above examples except that tension was not applied to the aggregates of CNT fibers, and neither heat treatment nor CSA treatment were performed. The measurement results of the tensile strength are shown in Table 2 below.

Comparative Examples 4 and 5

(26) Aggregates of CNT fibers were tested in the same manner as in the above examples except that neither tension was applied to the aggregates of CNT fibers nor CSA treatment was performed. The measurement results of the tensile strength are shown in Table 2 below.

Comparative Examples 6 and 7

(27) Aggregates of CNT fibers were tested in the same manner as in the above examples except that tension was not applied to the aggregates. The measurement results of the tensile strength are shown in Table 2 below.

(28) TABLE-US-00001 TABLE 1 CSA Relative CSA removing Heat Tension/tex Tensile Example Treatment solvent Treatment [cN/tex] Strength [%] 1 ◯ Acetone Air, 300° C. 3.4 138.4 2 30 min 5.2 142.9 3 5.6 147.5 4 8.3 151.7 5 10.5 151.1 6 16.7 160.1 7 17.4 155.1 8 18.9 165.7 9 20.6 160.7 10 20.6 161.8 11 32.8 125.3 12 35.1 118.0 13 36.4 130.9

(29) TABLE-US-00002 TABLE 2 Avg. Comp. CSA CSA Tension/ Relative Relative Ex- Treat- removing Heat tex Tensile Tensile ample ment solvent Treatment [cN/tex] Strength strength 1 X X X 0 100.0 100.3 (Base) 2 0 100.0 3 0 101.1 4 X X Air, 300° C. 0 115.3 114.3 5 30 min 0 113.3 6 ◯ Acetone Air, 300° C. 0 117.3 117.1 7 30 min 0 116.8

(30) In the Tables 1 and 2 above, “Relative Tensile Strength” represents the tensile strength of the CNT fibers in Examples and Comp. Examples when the tensile strength of the CNT fibers without any treatment is taken as 100 (based on Comparative Example 1).

(31) As shown in the above Tables 1 and 2, the average relative tensile strength of the aggregates of CNT fibers from Comparative Examples 1 to 3 (untreated with CSA, tension not applied and no heat treatment) was 100.3, the average relative tensile strength of the aggregates of CNT fibers from Comparative Examples 4 and 5 (untreated with CSA, tension not applied and heat treatment) was 114.3, and the average relative tensile strength of the aggregates of CNT fibers from Comparative Examples 6 and 7 (tension not applied, treated with CSA and heat treatment) was 117.1. In contrast, the average relative tensile strength of CNT aggregates from Examples 1 to 13 (CSA treatment, acetone solvent, tension/tex of 3.4 to 36.4 cN/tex applied and heat treatment) according to the present invention is 146.9. From this, it is calculated that the average relative tensile strength of Examples 1 to 13 according to the present invention was increased by 46.5%, by 28.5%, and by 25.4%, respectively, as compared with the average relative tensile strength of Comparative Examples 1 to 3, Comparative Examples 4 and 5, and Comparative Examples 6 and 7.

(32) Furthermore, from FIG. 2, which shows the results of SEM analysis of the aggregates of CNT fibers of Comparative Examples 1 to 5, which are not treated with CSA, and the aggregates of CNT fibers of Examples 1 to 13 according to the present invention, which are treated with CSA, it is found that aggregates of CNT fibers are further shrunk and the degree of alignment of the aggregates is improved after treatment with CSA.

(33) Therefore, it can be seen that the aggregates of CNT fibers obtained by dispersing in CSA with application of specific range of tensile force and heat treatment according to the present invention, are better aligned and have the improved tensile strength, compared with the aggregates of CNT fibers having no CSA treatment, no tension application and no heat treatment, the aggregates of CNT fibers having no tension application and no CSA treatment and having heat treatment, and aggregates of CNT fibers having no tension application and having CSA treatment and heat treatment.

(34) While the present invention has been particularly shown and described with reference to figures and embodiments thereof, it will be understood by those of ordinary skill in the art that the scope of the present invention is not limited thereby and that various changes and modifications may be made therein. Therefore, the actual scope of the present invention will be defined by the appended claims and their equivalents.