NICKEL-BASED SUPERALLOY HAVING HIGH MECHANICAL AND ENVIRONMENTAL STRENGTH AT HIGH TEMPERATURES AND LOW DENSITY

Abstract

A nickel-based superalloy includes, in weight percent, 5.9 to 6.5% aluminum, 9.5 to 10.5% cobalt, 4 to 5% chromium, 0.1 to 0.2% hafnium, 0.3 to 0.7% molybdenum, 3.7 to 4.5% rhenium, 7.5 to 8.5% tantalum, 0.2 to 0.7% titanium, 3.2 to 4% tungsten, 0 to 0.1% silicon, the balance being nickel and unavoidable impurities.

Claims

1. A nickel-based superalloy comprising, in weight percent, 5.9 to 6.5% aluminum, 9.5 to 10.5% cobalt, 4 to 5% chromium, 0.1 to 0.2% hafnium, 0.3 to 0.7% molybdenum, 3.7 to 4.5% rhenium, 7.5 to 8.5% tantalum, 0.2 to 0.7% titanium, 3.2 to 4% tungsten, 0 to 0.1% silicon, the balance consisting of nickel and unavoidable impurities.

2. The superalloy as claimed in claim 1, wherein said superalloy comprises, in weight percent, 6.1 to 6.5% aluminum, 9.5 to 10.5% cobalt, 4 to 5% chromium, 0.1 to 0.2% hafnium, 0.3 to 0.7% molybdenum, 3.7 to 4.5% rhenium, 7.5 to 8.5% tantalum, 0.2 to 0.7% titanium, 3.2 to 4% tungsten, 0 to 0.1% silicon, the balance being nickel and unavoidable impurities.

3. The superalloy as claimed in claim 1, wherein said superalloy comprises, in weight percent, 5.9 to 6.5% aluminum, 9.5 to 10.5% cobalt, 4 to 5% chromium, 0.1 to 0.2% hafnium, 0.3 to 0.7% molybdenum, 3.7 to 4.5% rhenium, 7.5 to 7.9% tantalum, 0.2 to 0.7% titanium, 3.2 to 4% tungsten, 0 to 0.1% silicon, the balance being nickel and unavoidable impurities.

4. The superalloy as claimed in claim 2, wherein said superalloy comprises, in weight percent, 6.1 to 6.5% aluminum, 9.5 to 10.5% cobalt, 4 to 5% chromium, 0.1 to 0.2% hafnium, 0.3 to 0.7% molybdenum, 3.7 to 4.5% rhenium, 7.5 to 7.9% tantalum, 0.2 to 0.7% titanium, 3.2 to 4% tungsten, 0 to 0.1% silicon, the balance consisting of nickel and unavoidable impurities.

5. The superalloy as claimed in claim 4, wherein said superalloy comprises, in weight percent, 6.1 to 6.5% aluminum, 9.5 to 10% cobalt, 4 to 5% chromium, 0.1 to 0.2% hafnium, 0.3 to 0.7% molybdenum, 3.7 to 4.5% rhenium, 7.5 to 7.9% tantalum, 0.2 to 0.7% titanium, 3.2 to 4% tungsten, 0 to 0.1% silicon, the balance being nickel and unavoidable impurities.

6. The superalloy as claimed in claim 5, wherein said superalloy comprises, in weight percent, 6.1 to 6.3% aluminum, 9.5 to 10% cobalt, 4 to 5% chromium, 0.1 to 0.2% hafnium, 0.3 to 0.7% molybdenum, 3.7 to 4.5% rhenium, 7.5 to 7.9% tantalum, 0.2 to 0.7% titanium, 3.2 to 4% tungsten, 0 to 0.1% silicon, the balance being nickel and unavoidable impurities.

7. The superalloy as claimed in claim 6, wherein said superalloy comprises, in weight percent, 6.1 to 6.3% aluminum, 9.5 to 10% cobalt, 4 to 5% chromium, 0.1 to 0.2% hafnium, 0.3 to 0.7% molybdenum, 3.7 to 4.5% rhenium, 7.5 to 7.9% tantalum, 0.3 to 0.6% titanium, 3.2 to 4% tungsten, 0 to 0.1% silicon, the balance being nickel and unavoidable impurities.

8. The superalloy as claimed in claim 5, wherein said superalloy comprises, in weight percent, 6.1 to 6.5% aluminum, 9.5 to 10% cobalt, 4 to 5% chromium, 0.1 to 0.2% hafnium, 0.3 to 0.7% molybdenum, 3.7 to 4.5% rhenium, 7.5 to 7.9% tantalum, 0.3 to 0.6% titanium, 3.2 to 4% tungsten, 0 to 0.1% silicon, the balance being nickel and unavoidable impurities.

9. The superalloy as claimed in claim 7, wherein said superalloy comprises, in weight percent, 6.1 to 6.3% aluminum, 9.5 to 10% cobalt, 4 to 5% chromium, 0.1 to 0.2% hafnium, 0.3 to 0.7% molybdenum, 3.7 to 4.5% rhenium, 7.5 to 7.9% tantalum, 0.3 to 0.6% titanium, 3.4 to 3.8% tungsten, 0 to 0.1% silicon, the balance consisting of nickel and unavoidable impurities.

10. The superalloy as claimed in claim 9, wherein said superalloy comprises, in weight percent, 6.1 to 6.3% aluminum, 9.5 to 10% cobalt, 4 to 5% chromium, 0.1 to 0.2% hafnium, 0.3 to 0.7% molybdenum, 3.8 to 4.5% rhenium, 7.5 to 7.9% tantalum, 0.3 to 0.6% titanium, 3.4 to 3.8% tungsten, 0 to 0.1% silicon, the balance being nickel and unavoidable impurities.

11. The superalloy as claimed in claim 10, wherein said superalloy comprises, in weight percent, 6.1 to 6.3% aluminum, 9.5 to 10% cobalt, 4.5 to 4.7% chromium, 0.1 to 0.2% hafnium, 0.3 to 0.7% molybdenum, 3.8 to 4.5% rhenium, 7.6 to 7.9% tantalum, 0.35 to 0.55% titanium, 3.4 to 3.8% tungsten, 0 to 0.1% silicon, the balance consisting of nickel and unavoidable impurities.

12. The superalloy as claimed in claim 1, wherein the superalloy comprises a sulfur content of less than or equal to 2 ppm by weight.

13. A turbomachinery part made of nickel-based superalloy as claimed in claim 1.

14. The part as claimed in claim 13, wherein said part is single-crystal.

15. A process for manufacturing a turbomachinery part made of nickel-based superalloy as claimed in claim 1 by casting.

Description

DESCRIPTION OF THE EMBODIMENTS

[0043] The superalloy in accordance with the invention comprises a nickel base with associated major additive elements.

[0044] Major addition elements comprise: cobalt Co, chromium Cr, molybdenum Mo, tungsten W, aluminum Al, tantalum Ta, titanium Ti, and rhenium Re.

[0045] The superalloy may also comprise minor additive elements, which are additive elements whose maximum percentage in the superalloy does not exceed 1% by weight.

[0046] Minor additive elements comprise: hafnium Hf and silicon Si.

[0047] The nickel-based superalloy comprises, in weight percent, 5.9 to 6.5% aluminum, 9.5 to 10.5% cobalt, 4 to 5% chromium, 0.1 to 0.2% hafnium, 0.3 to 0.7% molybdenum, 3.7 to 4.5% rhenium, 7.5 to 8.5% tantalum, 0.2 to 0.7% titanium, 3.2 to 4% tungsten, 0 to 0.1% silicon, the balance consisting of nickel and unavoidable impurities.

[0048] The nickel-based superalloy may also advantageously comprise, in weight percent, 6.1 to 6.5% aluminum, 9.5 to 10.5% cobalt, 4 to 5% chromium, 0.1 to 0.2% hafnium, 0.3 to 0.7% molybdenum, 3.7 to 4.5% rhenium, 7.5 to 8.5% tantalum, 0.2 to 0.7% titanium, 3.2 to 4% tungsten, 0 to 0.1% silicon, the balance being nickel and unavoidable impurities.

[0049] The nickel-based superalloy may also advantageously comprise, in weight percent, 5.9 to 6.5% aluminum, 9.5 to 10.5% cobalt, 4 to 5% chromium, 0.1 to 0.2% hafnium, 0.3 to 0.7% molybdenum, 3.7 to 4.5% rhenium, 7.5 to 7.9% tantalum, 0.2 to 0.7% titanium, 3.2 to 4% tungsten, 0 to 0.1% silicon, the balance being nickel and unavoidable impurities.

[0050] The nickel-based superalloy may also advantageously comprise, in weight percent, 6.1 to 6.5% aluminum, 9.5 to 10.5% cobalt, 4 to 5% chromium, 0.1 to 0.2% hafnium, 0.3 to 0.7% molybdenum, 3.7 to 4.5% rhenium, 7.5 to 7.9% tantalum, 0.2 to 0.7% titanium, 3.2 to 4% tungsten, 0 to 0.1% silicon, the balance being nickel and unavoidable impurities.

[0051] The nickel-based superalloy may also advantageously comprise, in weight percent, 6.1 to 6.5% aluminum, 9.5 to 10.5% cobalt, 4 to 5% chromium, 0.1 to 0.2% hafnium, 0.3 to 0.7% molybdenum, 3.7 to 4.5% rhenium, 7.5 to 7.9% tantalum, 0.2 to 0.7% titanium, 3.2 to 4% tungsten, the balance being nickel and unavoidable impurities.

[0052] The superalloy may also advantageously comprise, in weight percent, 6.1 to 6.5% aluminum, 9.5 to 10% cobalt, 4 to 5% chromium, 0.1 to 0.2% hafnium, 0.3 to 0.7% molybdenum, 3.7 to 4.5% rhenium, 7.5 to 7.9% tantalum, 0.2 to 0.7% titanium, 3.2 to 4% tungsten, 0 to 0.1% silicon, the balance being nickel and unavoidable impurities.

[0053] The superalloy may also advantageously comprise, in weight percent, 6.1 to 6.3% aluminum, 9.5 to 10.5% cobalt, 4 to 5% chromium, 0.1 to 0.2% hafnium, 0.3 to 0.7% molybdenum, 3.7 to 4.5% rhenium, 7.5 to 7.9% tantalum, 0.2 to 0.7% titanium, 3.2 to 4% tungsten, 0 to 0.1% silicon, the balance being nickel and unavoidable impurities.

[0054] The superalloy may also advantageously comprise, in weight percent, 6.1 to 6.5% aluminum, 9.5 to 10.5% cobalt, 4 to 5% chromium, 0.1 to 0.2% hafnium, 0.3 to 0.7% molybdenum, 3.7 to 4.5% rhenium, 7.5 to 7.9% tantalum, 0.3 to 0.6% titanium, 3.2 to 4% tungsten, 0 to 0.1% silicon, the balance being nickel and unavoidable impurities.

[0055] The superalloy may also advantageously comprise, in weight percent, 6.1 to 6.3% aluminum, 9.5 to 10.5% cobalt, 4 to 5% chromium, 0.1 to 0.2% hafnium, 0.3 to 0.7% molybdenum, 3.7 to 4.5% rhenium, 7.5 to 7.9% tantalum, 0.3 to 0.6% titanium, 3.2 to 4% tungsten, 0 to 0.1% silicon, the balance being nickel and unavoidable impurities.

[0056] Advantageously, the superalloy may comprise, in weight percent, 6.1 to 6.5% aluminum, 9.5 to 10% cobalt, 4 to 5% chromium, 0.1 to 0.2% hafnium, 0.3 to 0.7% molybdenum, 3.7 to 4.5% rhenium, 7.5 to 7.9% tantalum, 0.3 to 0.6% titanium, 3.2 to 4% tungsten, 0 to 0.1% silicon, the balance consisting of nickel and unavoidable impurities.

[0057] Advantageously, the superalloy may comprise, in weight percent, 6.1 to 6.3% aluminum, 9.5 to 10% cobalt, 4 to 5% chromium, 0.1 to 0.2% hafnium, 0.3 to 0.7% molybdenum, 3.7 to 4.5% rhenium, 7.5 to 7.9% tantalum, 0.3 to 0.6% titanium, 3.4 to 3.8% tungsten, 0 to 0.1% silicon, the balance consisting of nickel and unavoidable impurities.

[0058] The superalloy may also comprise, in weight percent, 6.1 to 6.3% aluminum, 9.5 to 10% cobalt, 4 to 5% chromium, 0.1 to 0.2% hafnium, 0.3 to 0.7% molybdenum, 3.7 to 4.5% rhenium, 7.5 to 7.9% tantalum, 0.3 to 0.6% titanium, 3.2 to 4% tungsten, 0 to 0.1% silicon, the balance consisting of nickel and unavoidable impurities.

[0059] The superalloy may also comprise, in weight percent, 6.1 to 6.3% aluminum, 9.5 to 10% cobalt, 4 to 5% chromium, 0.1 to 0.2% hafnium, 0.3 to 0.7% molybdenum, 3.7 to 4.5% rhenium, 7.5 to 7.9% tantalum, 0.3 to 0.6% titanium, 3.4 to 3.8% tungsten, 0 to 0.1% silicon, the balance consisting of nickel and unavoidable impurities.

[0060] The superalloy may also comprise, in weight percent, 6.1 to 6.3% aluminum, 9.5 to 10% cobalt, 4 to 5% chromium, 0.1 to 0.2% hafnium, 0.3 to 0.7% molybdenum, 3.8 to 4.5% rhenium, 7.5 to 7.9% tantalum, 0.3 to 0.6% titanium, 3.4 to 3.8% tungsten, 0 to 0.1% silicon, the balance consisting of nickel and unavoidable impurities.

[0061] The superalloy may also comprise, in weight percent, 6.1 to 6.3% aluminum, 9.5 to 10% cobalt, 4 to 5% chromium, 0.1 to 0.2% hafnium, 0.3 to 0.7% molybdenum, 3.8 to 4.5% rhenium, 7.6 to 7.9% tantalum, 0.3 to 0.6% titanium, 3.4 to 3.8% tungsten, 0 to 0.1% silicon, the balance consisting of nickel and unavoidable impurities.

[0062] The superalloy may also comprise, in weight percent, 6.1 to 6.3% aluminum, 9.5 to 10% cobalt, 4.5 to 5% chromium, 0.1 to 0.2% hafnium, 0.3 to 0.7% molybdenum, 3.8 to 4.5% rhenium, 7.6 to 7.9% tantalum, 0.3 to 0.6% titanium, 3.4 to 3.8% tungsten, 0 to 0.1% silicon, the balance consisting of nickel and unavoidable impurities.

[0063] The superalloy may also comprise, in weight percent, 6.1 to 6.3% aluminum, 9.5 to 10% cobalt, 4.5 to 4.7% chromium, 0.1 to 0.2% hafnium, 0.3 to 0.7% molybdenum, 3.8 to 4.5% rhenium, 7.6 to 7.9% tantalum, 0.3 to 0.6% titanium, 3.4 to 3.8% tungsten, 0 to 0.1% silicon, the balance consisting of nickel and unavoidable impurities.

[0064] The superalloy may also comprise, in weight percent, 6.1 to 6.3% aluminum, 9.5 to 10% cobalt, 4.5 to 4.7% chromium, 0.1 to 0.2% hafnium, 0.3 to 0.7% molybdenum, 3.8 to 4.5% rhenium, 7.6 to 7.9% tantalum, 0.35 to 0.55% titanium, 3.4 to 3.8% tungsten, 0 to 0.1% silicon, the balance consisting of nickel and unavoidable impurities.

[0065] The superalloy may also comprise, in weight percent, 6.1 to 6.3% aluminum, 9.5 to 10% cobalt, 4.5 to 4.7% chromium, 0.1 to 0.2% hafnium, 0.3 to 0.7% molybdenum, 3.8 to 4.5% rhenium, 7.8 to 7.9% tantalum, 0.35 to 0.55% titanium, 3.4 to 3.8% tungsten, 0 to 0.1% silicon, the balance consisting of nickel and unavoidable impurities.

[0066] The superalloy may also comprise, in weight percent, 6.1 to 6.3% aluminum, 9.5 to 10% cobalt, 4.5 to 4.7% chromium, 0.1 to 0.2% hafnium, 0.4 to 0.6% molybdenum, 3.8 to 4.5% rhenium, 7.8 to 7.9% tantalum, 0.35 to 0.55% titanium, 3.4 to 3.8% tungsten, 0 to 0.1% silicon, the balance consisting of nickel and unavoidable impurities.

[0067] The superalloy may also comprise, in weight percent, 6.1 to 6.3% aluminum, 9.5 to 10% cobalt, 4.5 to 4.7% chromium, 0.1 to 0.2% hafnium, 0.4 to 0.6% molybdenum, 3.8 to 4.3% rhenium, 7.8 to 7.9% tantalum, 0.35 to 0.55% titanium, 3.4 to 3.8% tungsten, 0 to 0.1% silicon, the balance consisting of nickel and unavoidable impurities.

[0068] The superalloy may also comprise, in weight percent, 6.1 to 6.3% aluminum, 9.5 to 10% cobalt, 4.5 to 4.7% chromium, 0.1 to 0.2% hafnium, 0.4 to 0.6% molybdenum, 3.8 to 4.3% rhenium, 7.8 to 7.9% tantalum, 0.35 to 0.55% titanium, 3.4 to 3.8% tungsten, the balance consisting of nickel and unavoidable impurities.

[0069] The superalloy may also comprise, in weight percent, 6.2% aluminum, 9.75% cobalt, 4.6% chromium, 0.14% hafnium, 0.5% molybdenum, 4.1% rhenium, 7.9% tantalum, 0.45% titanium, 3.6% tungsten, the balance consisting of nickel and unavoidable impurities.

[0070] Cobalt, chromium, tungsten, molybdenum and rhenium are mainly involved in the hardening of the γ phase, the austenitic matrix of FCC structure.

[0071] Aluminum, titanium, and tantalum promote the precipitation of the γ′ phase, the hardening Ni.sub.3 (Al, Ti, Ta) phase with an L1.sub.2 ordered cubic structure.

[0072] Furthermore, rhenium slows down the diffusive processes and limits the coalescence of the γ′ phase, thus improving the creep resistance at high temperature. However, the rhenium content should not be too high in order not to negatively impact the mechanical properties of the superalloy part.

[0073] The refractory elements molybdenum, tungsten, rhenium and tantalum also slow down the diffusion-controlled mechanisms, thus improving the creep resistance of the superalloy part.

[0074] In addition, chromium and aluminum improve resistance to oxidation and corrosion at high temperatures, especially around 900° C. for corrosion and around 1100° C. for oxidation.

[0075] The addition of silicon and hafnium also optimizes the hot oxidation resistance of the superalloy by increasing the adhesion of the Al.sub.2O.sub.3 alumina layer that forms on the surface of the superalloy at high temperature in an oxidizing environment.

[0076] Furthermore, chromium and cobalt help to decrease the γ′ solvus temperature of the superalloy.

[0077] Cobalt is an element chemically related to nickel that partially substitutes for nickel to form a solid solution in the γ phase, thereby strengthening the γ matrix, reducing the susceptibility to precipitation of topologically close-packed phases, in particular the μ, P, R, and a phases, and Laves phases, and reducing the susceptibility to secondary reaction zone (SRZ) formation.

[0078] Furthermore, a very low sulfur content of the nickel-based superalloy makes it possible to significantly increase the resistance to oxidation and corrosion when hot, as well as the resistance to spalling of the thermal barrier when the superalloy is used to form a part coated with a thermal barrier (for example a turbine blade). By very low sulfur content is meant here a content of less than or equal to 2 ppm by weight, preferably less than or equal to 1 ppm by weight, and even more preferentially less than or equal to 0.5 ppm by weight. Such a sulfur concentration can be obtained by preparing a low-sulfur mother liquor or by using a post-casting desulfurization process. Such a sulfur concentration can also be obtained by preparing a low-sulfur mother liquor and then using a post-casting desulfurization process.

[0079] Such a superalloy composition allows to improve the mechanical properties at high temperature (650° C.-1200° C.) of the parts manufactured from said superalloy.

[0080] In addition, such a superalloy composition allows for improved manufacturing by reducing the risk of defect formation during the manufacture of the part, and in particular the formation of “freckle”-type parasitic grains during directional solidification.

[0081] Indeed, the superalloy composition reduces the susceptibility of the part to the formation of “freckle” parasitic grains. The susceptibility of the part to the formation of “freckle” parasitic grains is evaluated using the criterion of Konter, denoted NFP, which is given by the following equation (1):

[00001]$\begin{array}{cc}\left[\mathrm{Math}.1\right]& \\ \mathrm{NFP}=\frac{\left[\%\mathrm{Ta}+1.5\%\mathrm{Hf}+0.5\%\mathrm{Mo}-0.5\%\mathrm{Ti}\right]}{\left[\%W+1.2\mathrm{Re}\right]}& \left(1\right)\end{array}$

[0082] Where % Ta is the tantalum content of the superalloy, in weight percent; where % Hf is the hafnium content of the superalloy, in weight percent; where % Mo is the molybdenum content of the superalloy, in weight percent; where % Ti is the titanium content in the superalloy, in weight percent; where % W is the tungsten content in the superalloy, in weight percent; and where % Re is the rhenium content in the superalloy, in weight percent.

[0083] The superalloy composition makes it possible to obtain an NFP parameter greater than or equal to 0.7, a value above which the formation of “freckle” parasitic grains is greatly reduced.

[0084] Furthermore, such a superalloy composition allows for a reduced density, in particular a density below 8.4 g/cm.sup.3.

[0085] Table 1 below shows the composition, in weight percent, of three examples of superalloys in accordance with the invention, Examples 1 to 3, as well as commercial or reference superalloys, Examples 4 to 9. Example 4 corresponds to the AM1 superalloy, Example 5 corresponds to the PWA 1484 superalloy, Example 6 corresponds to the CMSX-4 superalloy, Example 7 corresponds to the CMSX-4 Plus® Mod C superalloy, Example 8 corresponds to René® N6 superalloy, and Example 9 corresponds to CMSX-10 K® superalloy.

TABLE-US-00001 TABLE 1 Alloys Ni Al Ta Ti Co Cr Mo W Re Hf Others Ex 1 Balance 6.2 7.9 0.45 9.75 4.6 0.5 3.6 4.1 0.17 Ex 2 Balance 6.2 7.9 0.45 9.75 4.6 0.5 3.6 4.1 0.12 Ex 3 Balance 6.2 7.9 0.45 9.75 4.6 0.5 3.6 4.1 0.12 Si 0.1 Ex 4 Balance 5.3 8 1.2 6.5 7.5 2 5.5 0 00.5 Ex 5 Balance 5.65 8.7 0 10 5 1.9 5.9 3 0.1 Ex 6 Balance 5.6 6.5 1 9.6 6.6 0.6 6.4 3 0.1 Ex 7 Balance 5.7 8 0.85 10 3.5 0.6 6 4.8 0.1 Ex 8 Balance 6 7.5 0 12.2 4.4 1.1 5.7 5.3 0.03 0.05 C + 0.004 B + 0.01 Y Ex 9 Balance 5.7 8 0.2 3 2 0.4 5 6 0.15 0.1 Nb + 0.01 Si

[0086] Table 2 gives estimated characteristics of the superalloys listed in Table 1. The characteristics given in Table 2 are density, different transformation temperatures (solvus, solidus and liquidus), mole fraction of the γ′ phase at 700° C., 900° C., at 1050° C. and at 1200° C., mole fraction of the topologically close-packed (TPC) phases at 900° C. and at 1050° C.

TABLE-US-00002 TABLE 2 Transformation TCP volume temperatures (° C.) γ′ phase mole fraction (% mol) fraction (% mol) Alloys Density Solvus Solidus Liquidus 700° C. 900° C. 1050° C. 1200° C. 900° C. 1050° C. Ex 1 8.73 1317 1326 1399 75 68 57 34 0 0 Ex 2 8.73 1313 1332 1399 75 68 57 33 0 0 Ex 3 8.74 1315 1327 1397 74 67 57 34 0.4 0 Ex 4 8.63 1291 1301 1366 69 63 53 29 0.1 0 Ex 5 8.89 1295 1337 1394 77 66 50 26 0.2 0 Ex 6 8.76 1270 1310 1385 70 63 52 23 1.1 0 Ex 7 8.95 1308 1319 1398 73 68 58 35 1.6 0.8 Ex 8 8.92 1285 1335 1400 75 66 51 25 1.7 0.4 Ex 9 8.96 1372 1382 1400 69 68 61 46 0.5 0.4

[0087] The γ′ phase mole fractions of the alloys of the invention (Examples 1 to 3) are very high at 1200° C., about 34% mol, reflecting high stability of the hardening precipitates, which ensures high mechanical properties at temperature. The mole fractions of the superalloys in accordance with the invention are higher than those of the reference superalloys of Examples 4, 5, 6 and 8 and similar to that of the superalloy of Example 7, the superalloy of Example 7 being known for its very good creep properties at high temperature.

[0088] The volume fraction of embrittling (TPC) phases which is present in the alloys in accordance with the invention (Examples 1 to 3) is negligible or zero at 900° C., and zero at 1050° C., contrary to the reference alloys of Examples 7, 8 and 9, thus reflecting a high stability of the microstructure at the target temperatures of use.

[0089] Table 3 gives estimated characteristics of the superalloys listed in Table 1. The characteristics given in Table 3 are the activity of chromium in the γ phase at 900° C., and the activity of aluminum in the γ phase at 1100° C. The activities of chromium and aluminum in the γ matrix are an indication of the corrosion and oxidation resistance, the higher the chromium activity and aluminum activity in the matrix, the higher the corrosion and oxidation resistance.

TABLE-US-00003 TABLE 3 γ phase Cr activity γ phase Al activity Alloys 900° C. 1100° C. Ex 1 1.92E−3 1.10E−07 Ex 2 1.89E−3 1.08E−07 Ex 3 1.91E−3 1.15E−07 Ex 4 3.78E−3 9.96E−08 Ex 5 2.19E−3 1.20E−07 Ex 6 3.05E−3 1.28E−07 Ex 7 1.51E−3 1.02E−07 Ex 8 1.80E−3 1.48E−07 Ex 9 5.18E−4 4.22E−08

[0090] The superalloys in accordance with the invention (Examples 1 to 3) have higher chromium activities at 900° C. than the reference alloys of Examples 5 and 7, which are known to have poor corrosion resistance.

[0091] As illustrated in Tables 2 and 3, the superalloys in accordance with the invention have mechanical properties at least equivalent to and even superior at high temperatures to the alloys of the prior art, while exhibiting lower density and superior resistance to corrosion and oxidation.

[0092] The properties given in Tables 2 and 3 are estimated using the CALP HAD (CALculation of PHAse Diagrams) method.

[0093] The nickel-based superalloy part can be made by casting.

[0094] The casting of the part is made by melting the superalloy, the liquid superalloy being poured into a mold to be cooled and solidified. The casting of the part can for example be made by the lost wax technique, in particular to make a blade.

[0095] Furthermore, in order to produce a single-crystal part, in particular a blade, the process can comprise a directional solidification step. The directional solidification is performed by controlling the thermal gradient and the solidification rate of the superalloy, and by introducing a single-crystal grain or by using a grain selector, in order to avoid the appearance of new grains in front of the solidification front.

[0096] In particular, directional solidification can allow the manufacture of a single-crystal blade whose crystal structure is oriented along a crystallographic direction <001> that is parallel to the longitudinal direction of the blade, i.e., along the radial direction of the turbomachine, such an orientation providing better mechanical properties.