TWO-COMPONENT PLATINUM CONTENTED LIQUID SILICONE AND THE METHOD FOR MANUFACTURING OF STORAGE BOX LID

Abstract

The present application provides a storage box lid, a storage box and a method for manufacturing the same. The storage box lid comprises a flexible thin film and a plastic rigid frame. The flexible thin film is prepared from a two-component platinum contented liquid silicone. In the present invention, the storage box, formed by using the storage box lid with the flexible thin film, in combination with a matching box body, can significantly improve the capacity for storing food, so that it can effectively store food larger than the box body. Moreover, the storage box of the present invention does not significantly squeeze the stored food, and the effect is distinctive.

Claims

1. A two-component platinum contented liquid silicone for preparing a storage box lid, the two-component platinum contented liquid silicone comprising a component A and a component B, wherein the content of component A are 100% by weight, the following components by weight: TABLE-US-00008 Vinyl Terminated Polydimethylsiloxane 60-78%, Silicone Dioxide 18-38%, Platinum(0)-1,3-divinyl-1,1,3,3-tetramethyldisiloxane  2-4%; and, wherein the content of component B are 100% by weight, the following components by weight: TABLE-US-00009 Vinyl Terminated Polydimethylsiloxane 60-78%, Silicone Dioxide 18-38%, Dimethyhydrogensiloxane  2-4%.

2. The two-component platinum contented liquid silicone for preparing a storage box lid according to claim 1, characterized in that: the mass ratio of the component A and the component B is 1:1 to 1.08:1.

3. A preparation method of a storage box lid, the storage box lid comprising a flexible thin film and a plastic rigid frame, the preparation method of the storage box lid comprises: S1. transfer a Primer to the plastic rigid frame at room temperature in a clean room; S2. cure the Primer at a temperature of 120° C. to 150° C. for 15 minutes to 20 minutes; S3. heating a mold to 125-145° C., the mold having a mold cavity; S4. put the plastic rigid frame with the Primer into the mold cavity, and then close the mold; S5. inject two-component platinum contented liquid silicone into the mold cavity, cure for 150s to 200s, and form a flexible thin film in the plastic rigid frame; the two-component platinum contented liquid silicone formed by mixing component A and component B by weight as set forth in claim 1; S6. open the mold to obtain the storage box lid.

4. The method for preparing a storage box lid of claim 3, wherein, in step S1, the clean room complies with at least one of: the standard FDA ISO 7 or better, and the standard EU level B or better.

5. The method for preparing a storage box lid of claim 3, wherein in step S1, the Primer comprising a Primer A and a Primer B, comprising a Primer A are 100% by weight, the following components by weight: TABLE-US-00010 Butyl acetate 97%, Triethoxyvinylsilane  3%; comprising a Primer B are 100% by weight, the following components by weight: TABLE-US-00011 Butyl acetate 95%, Tetraethoxysilane  5%.

6. The method for preparing a storage box lid of claim 5, wherein the mixing mass ratio of Primer A and Primer B is 1:1-1.03:1.

7. The method for preparing a storage box lid of claim 6, wherein the mixing mass ratio of Primer A and Primer B is 1.0:1-1.02:1.

8. A storage box comprising: a lid prepared by claim 3, comprising a flexible thin film and a plastic rigid frame, the outer periphery of the flexible thin film and the inner periphery of the plastic rigid frame being connected with a primer; a box body; clips movably connected with the outer periphery of the plastic rigid frame, the number of the clips is more than two, and the clips are used for realizing fixed connection between the storage box lid and the box body; a groove is provided in the lower portion of the plastic rigid frame, the groove is provided in the circumferential direction of the plastic rigid frame; and a sealing ring, located in the groove, configured to realize sealing between the storage box lid and the box body.

9. The storage box lid of claim 8, wherein the clips are connected with the plastic rigid frame through pivot shafts, and the clips can rotate in the rotation direction of the pivot shafts.

10. The storage box of claim 8, wherein the lid is provided above the box body, a convex extending horizontally outward is provided on the box body, and the fixed connection between the box body and the storage box lid is realized by fitting connection of the clips and the convex.

11. The storage box lid of claim 8, wherein the box body is any one of a glass box body, a plastic box body and a ceramic box body.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0037] In order to explain the embodiments of the present application more clearly, the related drawings will be briefly described below. It will be understood that the drawings in the following description are only intended to illustrate some embodiments of the present application, and many other technical features, connection relationships, etc. not mentioned herein may be obtained by those of ordinary skill in the art from these drawings.

[0038] FIG. 1 is a structural schematic view of a storage box provided by the present application.

[0039] FIG. 2 is a horizontal view of a storage box, with silicone film being extended by interior content, provided by the present application.

[0040] The reference numerals and names in the appended drawing are as follows: [0041] 1 flexible thin film; [0042] 2 clip; [0043] 3 plastic rigid frame; [0044] 4 silicone rubber sealing ring; [0045] 5 box body; [0046] 6 primer.

DETAILED DESCRIPTION OF EMBODIMENTS

[0047] The present invention is described in detail below in conjunction with specific embodiments. The following embodiments will facilitate a further understanding of the present invention by those skilled in the art without limiting the present invention in any form. It should be noted that for those skilled in the art, several modifications and improvements can be made without departing from the concept of the present invention. All these belong to the scope of protection of the present invention.

Embodiment 1

[0048] The embodiment provides a storage box lid, and as shown in FIG. 1, the storage box lid comprises a flexible thin film 1 and a plastic rigid frame 3, the outer periphery of the flexible thin film 1 and the inner periphery of the plastic rigid frame 3 are connected with a primer 6.

[0049] The outer periphery of the plastic rigid frame 3 is connected with clips 2 through pivot shafts, and the clips 2 are able to rotate in the rotation direction of the pivot shafts. In this embodiment, the plastic rigid frame 3 is square, 4 clips 2 are adopted and are symmetrically provided at four sides of the plastic rigid frame 3, and the clips 2 are used for realizing fixed connection between the storage box lid and a matching box body 5. Food in the box body can be effectively sealed and preserved though the tight fitting of the clips 2 and the box body 5.

[0050] A groove is provided in the lower portion of the plastic rigid frame 3, the groove is provided in the circumferential direction of the plastic rigid frame 3, and a silicone rubber sealing ring 4 which is configured to realize further sealing between the storage box lid and the matching box body 5 and able to withstand high temperature (which up to 220° C.) is placed in the groove.

[0051] The plastic rigid frame 3 and the clips 2 in this embodiment are all manufactured from polyamide resin.

[0052] The preparation method of the storage box lid in the present embodiment comprises the following steps:

[0053] S1. Transfer the primer to the plastic rigid frame at room temperature in a clean room;

[0054] The primer comprising a Primer A and a Primer B, comprising a Primer A are 100% by weight, the following components by weight show in Table 1; comprising a Primer B are 100% by weight, the following components by weight shown in Table 1.

TABLE-US-00005 Raw material Usage composition CAS NO. Percentage Ratio Primer A Butyl acetate 123-86-4 97% 1.03 Triethoxyvinylsilane 78-08-0  3% Primer B Butyl acetate 123-86-4 95% 1 Tetraethoxysilane 78-10-4  5%

[0055] S2. Curing the primer at a temperature of 120° C. for 20 minutes;

[0056] S3. Heating the mold to 125° C.;

[0057] S4. Put the plastic rigid frame with primer into the mold cavity and position it, and then close the mold;

[0058] S5. Inject two-component platinum contented liquid silicone into the mold cavity, cure for 150s, and form a flexible thin film in the plastic rigid frame; the two-component platinum contented liquid silicone is formed by component A and component B in a certain proportion shown in Table 2;

[0059] S6. Open the mold to obtain the storage box lid.

[0060] The embodiment further provides a storage box comprising the above-mentioned lid and a box body as shown in FIG. 1 and FIG. 2, wherein the lid is provided above the box body, a convex extending horizontally outward is provided on the box body and extending in the direction of the bottom of the box body, and the fixed connection between the box body and the lid is realized by fitting connection of the clips and the convex. Although the box body described in this embodiment is a plastic box body, the present invention is not limited thereto, the same effect can be achieved by replacing it with a glass box body, a ceramic box body, etc.

[0061] The storage box prepared in this embodiment can place and store foods with irregular shapes. The thickness of the flexible thin film prepared by using two-component platinum contented liquid silicone is less than 1 mm, the hardness is Shore A30, and the tensile limit is 5 cm; the tensile strength of the flexible thin film is 11 MPa, so that when irregular food is placed in the storage box, its ability to withstand pressure to stretch can be effectively extended up to twice; the elongation at break of the flexible thin film is 1050%, so that it can also provide a large amount of stretching without breaking under the condition of force stretching, thereby increasing the plasticity of the storage box; the tear strength of the flexible thin film reaches 23 KN/M, so that even if it encounters sharp food for storage, such as bones, chicken wings, etc., it will not be easily pierced like conventional films, but because of its high tear strength, even if it encounters the above There is no puncture and tear in sharp food; the compression set ratio of this flexible thin film is low, in the test JIS K6249, when it reaches 175 degrees and compresses for 22 hours, its deformation ratio remained at 21%.

Embodiment 2-3

[0062] Embodiment 2-3 provides a method for preparing a storage box lid, which is basically the same as the method in Embodiment 1, with the only difference that: Embodiment 2-3 prepares the raw material of the two-component platinum contented liquid silicone for the flexible thin film.

[0063] The composition is shown in Table 2.

TABLE-US-00006 TABLE 2 Usage Raw material composition CAS NO. Embodiment 1 Embodiment 2 Embodiment 3 Ratio Liquid Vinyl Terminated 68083-19-2 60% 70% 78% 1.05 Silicone Polydimethylsiloxane A Silicone Dioxide 14464-46-1 38% 27% 18% Platinum(0)-1,3-divinyl- 68478-92-2  2%  3%  4% 1,1,3,3- tetramethyldisiloxane Liquid Vinyl Terminated 68083-19-2 60% 70% 78% 1 Silicone Polydimethylsiloxane B Silicone Dioxide 14464-46-1 38% 27% 18% Dimethyhydrogensiloxane 68037-59-2  2%  3%  4%

Embodiment 4

[0064] The present embodiment provides a method for preparing a storage box lid, comprising the following steps:

[0065] The preparation method of the storage box lid in the present embodiment comprises the following steps:

[0066] S1. Transfer the primer to the plastic rigid frame at room temperature in a clean room; The primer is the same as in Embodiment 1.

[0067] S2. Curing the primer at a temperature of 140° C. for 18 minutes;

[0068] S3. Heating the mold to 135° C.;

[0069] S4. Put the plastic rigid frame with primer into the mold cavity and position it, and then close the mold;

[0070] S5. Inject two-component platinum contented liquid silicone into the mold cavity, cure for 180s, and form a flexible thin film in the plastic rigid frame; the two-component platinum contented liquid silicone is formed by mixing component A and component B in a ratio of 1:1; The two-component platinum contented liquid silicone includes the components shown in Embodiment 1 in Table 1 below.

[0071] S6. Open the mold to obtain the storage box lid.

Embodiment 5

[0072] The present embodiment provides a method for preparing a storage box lid, comprising the following steps:

[0073] The preparation method of the storage box lid in the present embodiment comprises the following steps:

[0074] S1. Transfer the primer to the plastic rigid frame at room temperature in a clean room; The primer is the same as in Embodiment 1.

[0075] S2. Curing the primer at a temperature of 150° C. for 15 minutes;

[0076] S3. Heating the mold to 145° C.;

[0077] S4. Put the plastic rigid frame with primer into the mold cavity and position it, and then close the mold;

[0078] S5. Inject two-component platinum contented liquid silicone into the mold cavity, cure for 200s, and form a flexible thin film in the plastic rigid frame; the two-component platinum contented liquid silicone is formed by mixing component A and component B in a ratio of 1:1.08; The two-component platinum contented liquid silicone includes the components shown in Embodiment 1 in Table 1 below.

[0079] S6. Open the mold to obtain the storage box lid.

[0080] The present invention further compares the performance of the flexible thin film prepared by using the two-component platinum contented liquid silicone described in the embodiment of the present invention and the flexible thin film prepared by the existing general grade silicone produced by other brands. The results are shown in Table 3.

TABLE-US-00007 TABLE 3 Physical Properties Comparison Table The two-component platinum contented liquid silicone Other brands Physical Properties used in the present invention of silicone Tensile Strength 10.0-13.0 Mpa 5.5-8.0 Mpa Elongation at break 900-1100% 150%-700% Tear Strength 20-25 KN/M 10-15 Kn/M Compression   20-25% 30% and above Deformation Rate

[0081] It will be apparent to those skilled in the art that the present application is not limited to the details of the above exemplary embodiments and that the present application can be embodied in other specific forms without departing from the spirit or essential features of the present application. Thus, the embodiments are to be regarded as exemplary and non-limiting from any point of view, and the scope of the present application is defined by the appended claims rather than the above description, so that all variations falling within the meaning and scope of the equivalent requirements of the claims are intended to be included in the present application. No reference numerals in the claims shall be construed as limiting the claims to which they relate.