RADIOLYTIC METHOD OF PREPARING GELS

Abstract

In certain aspects and embodiments, the present invention provides a radiolytic polymerization/gelation method for the synthesis of gels and their subsequent activated carbon derivatives. In certain exemplary embodiments, resorcinol-formaldehyde gels are produced from resorcinol and formaldehyde without additives, catalysts, buffers, initiators or other species. In certain embodiments, ionizing γ-type radiation from .sup.60Co is used as a radiation source in the gel crosslinking process. Different compositions of resorcinol/formaldehyde and a wide range of irradiation doses were examined. Various techniques are used to characterize the outcome product, either the gels or their derived carbon gels or activated carbon.

Claims

1. A method of making a phenolic compound-formaldehyde gel, the method comprising: preparing a reaction mixture comprising a phenolic compound and formaldehyde; and irradiating the reaction mixture with ionizing radiation, thereby producing the phenolic compound-formaldehyde gel.

2. The method of claim 1, wherein the phenolic compound is selected from the group consisting of a dihydroxybenzene, a trihydroxybenzen, and mixtures thereof.

3. The method of claim 2, wherein the phenolic compound is selected from the group consisting of resorcinol, catechol, hydroquinone, and mixtures thereof

4. The method of claim 3, wherein the phenolic compound is resorcinol.

5. The method of claim 1, wherein the ionizing radiation is gamma irradiation.

6. The method of claim 5, wherein the gamma irradiation is a dose from about 10 to 70 kGy.

7. The method of claim 6, wherein the ionizing radiation is produced by a radiation source comprising radioactive .sup.60Co.

8. The method of claim 1, wherein the reaction mixture does not comprise a polymerization initiator, a polymerization catalyst, an acid, a base, or a buffer.

9. The method of claim 1, wherein the reaction mixture does not comprise a solvent.

10. The method of claim 1, wherein the phenolic compound-formaldehyde gel is a xerogel, an aerogel, or a cryogel.

11. The method of claim 1, further comprising: waiting for gelation of the reaction mixture.

12. The method of claim 10, wherein gelation of the reaction mixture comprises crosslinking of the phenolic compound during irradiating of the reaction mixture.

13. The method of claim 1, further comprising: curing the phenolic compound-formaldehyde gel.

14. The method of claim 1, further comprising: converting the phenolic compound-formaldehyde gel to a carbon gel.

15. The method of claim 14, wherein converting the resorcinol-formaldehyde gel to a carbon gel comprises heating up to 500° C. for 3 hours while purging with nitrogen gas.

16. The method of claim 15, wherein the purging with nitrogen is at a gas flow rate of about 100 cm.sup.3/min.

17. The method of claim 14, wherein converting the resorcinol-formaldehyde gel to a carbon gel comprises heating up to 700° C. for 1 hour while purging with carbon dioxide gas.

18. The method of claim 17, wherein the purging with carbon dioxide is at a gas flow rate of about 150 cm.sup.3/min.

19. The method of claim 1, wherein the reaction mixture's ratio of phenolic compound to formaldehyde is at least about 1:9.

20. The method of claim 1, wherein the gel activated carbon has an average pore size of from about 1.0 to 2.1 nm.

21. The method of claim 1, wherein the gel activated carbon has an average area of micropores of from about 0.3 to 1.1% of the total area.

22. The method of claim 1, wherein the gel activated carbon has an average area of mesopores of from about 11 to 35% of the total area.

23. The method of claim 1, wherein the gel activated carbon has an average area of macropores of from about 63 to 88% of the total area.

24. The method of claim 1, wherein the gel activated carbon has an average particle size of from about 0.2 to 6.6 μm.

25. The method of claim 1, wherein the I.sub.D/I.sub.G ratio of activated carbons is from about 0.82 to 0.90.

26. The method of claim 1, wherein the gel activated carbon has an activated carbon % of at least about 14 to 60% in studying the composition effect.

27. The method of claim 26, wherein the gel activated carbon has an activated carbon % of at least about 32 to 56% in studying the dose irradiation dose effect.

Description

BRIEF DESCRIPTION OF THE FIGURES

[0035] FIG. 1A illustrates a proposed radiolytic reaction mechanism of water.

[0036] FIG. 1B suggested a radiolytic reaction mechanism of RF gels.

[0037] FIG. 1C shows the irradiation processing using gamma-rays cell of .sup.60Co as main source.

[0038] FIG. 2 shows FTIR spectra of RFG1 through RFG9 crosslinked at 40 kGy with a dose rate of 0.34 kGy/h.

[0039] FIG. 3 shows Raman spectra of RFG1 through RFG9 crosslinked at 40 kGy with a dose rate of 0.34 kGy/h.

[0040] FIG. 4 shows Raman intensity ratios (I.sub.D/I.sub.G) of RFG1 through RFG9 crosslinked at 40 kGy with a dose rate of 0.34 kGy/h.

[0041] FIGS. 5A and 5B show TGA thermograms (FIG. 5A) and DTG thermograms (FIG. 5B) of RFG1 through RFG9 crosslinked at 40 kGy with a dose rate of 0.34 kGy/h.

[0042] FIG. 6 shows XRD patterns of RFG1 through RFG9 crosslinked at 40 kGy with a dose rate of 0.34 kGy/h.

[0043] FIG. 7 shows SEM photomicrographs of RFG1 through RFG9 crosslinked at 40 kGy with a dose rate of 0.34 kGy/h. The scale bar size is 10 μm.

[0044] FIG. 8 shows optical photos of RFG1 through RFG9 crosslinked at 40 kGy with a dose rate of 0.34 kGy/h.

[0045] FIG. 9 shows N.sub.2 adsorption/desorption isotherms at −196° C. onto RFG1-AC through RFG9-AC.

[0046] FIG. 10 shows the cumulative pore volume versus pore width for RFG1-AC through RFG9-AC.

[0047] FIGS. 11A, 11B, and 11C show the full x-axis scale of incremental pore volume versus pore width and x-axis in log scale (FIG. 11A), truncated x-axis and zoomed-in scale of 0.6-1.8 nm (FIG. 11B), and truncated x-axis and zoomed-in scale of 2-280 nm (FIG. 11C). Samples are RFG1-AC through RFG9-AC from corresponding gels that were prepared at 40 kGy with a dose rate of 0.34 kGy/h.

[0048] FIG. 12 shows the cumulative surface areas versus pore width of RFG1-AC through RFG9-AC from corresponding gels that were prepared at 40 kGy with a dose rate of 0.34 kGy/h.

[0049] FIGS. 13A and 13B show the full x-axis scale of incremental surface area versus pore width and x-axis in log scale (FIG. 13A) and truncated x-axis (FIG. 13B) and zoomed-in scale of 0.6-1.8 nm of RFG1-AC through RFG9-AC from gels that were prepared at 40 kGy with a dose rate of 0.34 kGy/h.

DETAILED DESCRIPTION

[0050] Provided herein are radiolytic methods for the synthesis of phenolic compound-formaldehyde gels and their derivatives.

Definitions

[0051] When referring to the compounds provided herein, the following terms have the following meanings unless indicated otherwise. Unless defined otherwise, all technical and scientific terms used herein have the same meaning as is commonly understood by one of ordinary skill in the art. In the event that there is a plurality of definitions for a term herein, those in this section prevail unless stated otherwise.

[0052] The term “aerogel” as used herein includes a gel in which the liquid component has largely or entirely been replaced by a gas phase. In certain embodiments, the aerogel has very low density and low thermal conductivity.

[0053] The term “xerogel” as used herein as type of solid-formed gels, which are being prepared through drying slowly at the room temperature with an unconstrained shrinkage. In certain embodiments, the xerogel has high surface area and small pore size.

[0054] The term “carbon gel” as used herein includes a porous, three-dimensional form of carbon produced from a gel (e.g., by pyrolysis of the gel).

[0055] The term “cryogel” as used herein includes a gel formed in a partially frozen solution.

[0056] The term “gel” as used herein includes a porous, three-dimensional network of polymeric compounds. In certain embodiments, a gel is formed by a polymerization reaction in which the monomers react to form a network of interlinking or interconnected chains. In certain embodiments, the pores incorporate a liquid phase (e.g., the solvent used for gel formation).

[0057] The term “phenolic compound” as used herein includes di- and trihydroxyaryl groups (preferably, di- and trihydroxybenzenes, such as resorcinol) and mixtures thereof. In certain embodiments, a mixture of di- and trihydroxy compounds are used (e.g., to influence the degree of crosslinking in the final gel).

Reaction Mechanism of Water Radiolysis

[0058] The free radicals formed during water radiolysis are highly reactive, for the HO. radical is the most powerful oxidant known to occur in water, while the same is true for the hydrated electron as reductant. Without intending to be bound by theory, the radiolytic process occurs in three main stages taking place on different typical time scales:

[0059] 1. Physical stage, which is achieved in about 1 fs (10-15 s) after the initial matter-ionizing radiation interaction, consists in energy deposition followed by fast relaxation processes. This leads to the formation of ionized water molecules (H.sub.2O.sup.+), excited water molecules (H.sub.2O*) and subexcitation electrons (e.sup.−).

[0060] 2. Physico-chemical stage (10-15-10-12 s), in which numerous processes occur, including ion-molecule reaction (1), dissociative relaxation (2), auto-ionization of excited states, thermalization of sub-excitation electrons (solvation of electrons) (3), hole diffusion, and the like.

[0061] 3. Chemical stage (10-12-10-6 s), in which the species react in the tracks and then diffuse in solution. They can thus react with each other and also with surrounding molecules in the solute. The track of the particles expands because of the diffusion of radicals and their subsequent chemical reactions. Recombination becomes unimportant after ca. 1 μs for low linear energy transfer radiation.

[0062] Without intending to be bound by theory, FIG. 1 shows a suggested radiolytic process of H.sub.2O molecule radiolysis that is induced by the ionizing radiation of γ-rays using ° Co as a main source of γ-radiation.

[0063] The principal idea depends basically on chemical stage of H.sub.2O radiolysis as shown in Eq.(4):

##STR00001##

[0064] The radiolytic yield (labeled as G-value) for water decomposition products using γ-ray irradiation at room temperature are 2.7, 0.6, 2.8, 0.45, 0.72, 3.2 0.5 for e.sub.aq, H., HO., HO..sub.2, H.sub.3O.sup.+, OH.sup.−, H.sub.2O.sub.2, and H.sub.2, respectively. The G-value represents the number of produced or decomposed molecules per 100 eV energy absorbed (or, if the G-values are multiplied by 0.010364, in the SI unit μmol/J).

Reaction Mechanism of Methanol Radiolysis

[0065] The products formed when liquid methanol is irradiated are e.sub.aq, H., HO., CH.sub.3., CH.sub.3OH, H.sub.2, (CH.sub.2OH).sub.2, HCHO, CH.sub.4, and CO, respectively and some other minor species. It was reported that the salvation in alcohol is lower than in water. In a methanolic system, the above species are generated primarily as shown in Eq. (5). The G-values of these species are 0.21, 0.11, 0.02, 0.02, 0.28, 0.58, 0.185, 0.043 and 0.013 (μvalue-1), respectively.

##STR00002##

[0066] The reaction of resorcinol with formaldehyde needs a catalyst, such as an acid or base catalyst, to initiate the reaction. Therefore, the presence of OH.sup.− and H.sub.3O.sup.+ in Eq. (4) as radiolysis products of H.sub.2O due to exposure to γ-rays, and presence of these radicals in Eq. (4), can change the pH level in the range of 3 to 11. These conditions are enough to initiate the reaction of resorcinol and formaldehyde reactants to produce gels. Further, the produced species in Eq. (5) may change the pH level of resorcinol and formaldehyde reaction media to reach the desired value of initiation for polymerization and gelation reaction.

[0067] The existing technology and current practices depend on conventional methods that comprise the main reactants in addition to extra components, such as catalyst, buffer, acid or base to control pH level, and additives. These additives or initiators of reaction can contaminate and poison the final gel products if seeded into the gel structure. In some embodiments, these contaminating materials restrict the applications of the obtained gels such pharmaceuticals, biomaterials, biomaterials, cosmetics, and the like. Moreover, these contaminating materials can have non-environmental-friendly effects. Furthermore, the conventional process requires a relatively long time to complete the polymerization and gelation reactions of the gels.

[0068] In certain aspects, the present invention provides one or more advantages over existing technologies and current practices in using only the main reactants without additional chemical species, as are used in the conventional methods. In certain aspects, the present invention provides sterilized and clean gel products, which widens the scope of possible applications and allows better conformity to green chemistry principles. The absence of extra chemical components make the final gel product more suitable for sensitive applications such as biomaterials, biomedical materials, cosmetics, pharmaceutics, and the like, because some of these applications require highly pure and clean final raw materials. Furthermore, the polymerization and crosslinking reactions in this novel method can be significantly faster than the conventional method if a high irradiation rate is used.

[0069] In certain aspects and embodiments, the present invention provides a method of making a phenolic compound-formaldehyde gel (e.g., a resorcinol-formaldehyde gel), the method comprising:

[0070] preparing a reaction mixture comprising a phenolic compound and formaldehyde; and

[0071] irradiating the reaction mixture with ionizing radiation, thereby producing the phenolic compound-formaldehyde gel.

[0072] In certain aspects and embodiments, the phenolic compound is selected from the group including a dihydroxybenzene (e.g., 1,3-dihydroxybenzene or resorcinol; 2,4-dimethylresorcinol; 2,4-di(hydroxymethyl)resorcinol; 1-methoxy-2,4-dihydroxybenzene), a trihydroxybenzene (e.g., 1,3,5-trihydroxybenzene; 1,2,4-trihydroxybenzene), and mixtures thereof. In certain aspects and embodiments, the phenolic compound is selected from the group including resorcinol, catechol, hydroquinone, and mixtures thereof. In certain aspects and embodiments, the phenolic compound is resorcinol.

[0073] In certain aspects and embodiments, the ionizing radiation is gamma radiation. In certain aspects and embodiments, the dose of gamma irradiation ranges from about 10 to 70 kGy (e.g., about 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, or 70 kGy).

[0074] In certain aspects and embodiments, the ionizing radiation is produced by a radiation source comprising radioactive .sup.60Co (for example) as the main source.

[0075] In certain aspects and embodiments, the reaction mixture (i.e., for gel formation or polymerization) does not comprise a polymerization initiator, a polymerization catalyst, an acid, a base, or a buffer. In certain aspects and embodiments, the reaction mixture is substantially free of a polymerization initiator or a polymerization catalyst. In certain aspects and embodiments, the reaction mixture is substantially free of an acid, a base, or a buffer.

[0076] In certain aspects and embodiments, the reaction mixture does not include a solvent (e.g., is substantially free of a solvent). In certain aspects and embodiments, the reaction mixture for the gel formation or polymerization comprises resorcinol and formaldehyde solution.

[0077] In certain aspects and embodiments, the reaction mixture for the gel formation or polymerization comprises water, resorcinol, and formaldehyde. In certain aspects and embodiments, wherein the reaction mixture for the gel formation or polymerization consists essentially of resorcinol, and formaldehyde.

[0078] In certain aspects and embodiments, the reaction mixture's ratio of phenolic compound to formaldehyde ranges from about 1:9 to 9:1 (e.g., about 1:9, 1:8, 1:7, 1:6, 1:5, 1:4, 1:3, 1:2, 1:1, 2:1, 3:1, 4:1, 5:1, 6:1, 7:1, 8:1, and 9:1).

[0079] In certain aspects and embodiments, the phenolic compound-formaldehyde gel is a xerogel, an aerogel, or a cryogel. In certain aspects and embodiments, the phenolic compound-formaldehyde gel is a xerogel. In certain aspects and embodiments, the phenolic compound-formaldehyde gel is an aerogel. In certain aspects and embodiments, the phenolic compound-formaldehyde gel is a cryogel.

[0080] In certain aspects and embodiments, the method further comprises:

waiting for gelation of the reaction mixture (e.g., for 30 min, 1 h, 2 h, or 3 h, depending on the irradiation rate along with the applied dose of irradiation).

[0081] In certain aspects and embodiments, gelation of the reaction mixture comprises crosslinking of the phenolic compounds (including resorcinol, catechol, hydroquinone, and mixtures thereof) during the irradiating of the reaction mixture (e.g., 1,3-dihydroxybenzene or resorcinol; 2,4-dimethylresorcinol; 2,4-di(hydroxymethyl)resorcinol; 1-methoxy-2,4-dihydroxybenzene), a trihydroxybenzene (e.g., 1,3,5-trihydroxybenzene; 1,2,4-trihydroxybenzene), and mixtures thereof).

[0082] In certain aspects and embodiments, the method further comprises:

[0083] curing the phenolic compound-formaldehyde gel (e.g., by heating).

[0084] In certain aspects and embodiments, curing the phenolic compound-formaldehyde gel comprises heat drying the phenolic compound-formaldehyde gel at about 50° C. for 3 days. In certain aspects and embodiments, the heat drying of the phenolic compound-formaldehyde gel is at about 50° C. (e.g., at about 40, 45, 50, 55, 60, or 65° C.). In certain aspects and embodiments, the heat drying of the phenolic compound-formaldehyde gel is at about 3 days (e.g., 36 h, 48 h, 60 h, 72 h, 84 h, 96 h, or 108 h).

[0085] The method of any one of the preceding claims, further comprising: converting the phenolic compound-formaldehyde gel to a carbon gel.

[0086] In certain aspects and embodiments, converting the resorcinol-formaldehyde gel to a carbon gel comprises heating up to 500° C. (e.g., 350, 375, 400, 425, 450, 475, 500, 525, or 550° C.), keeping this temperature constant for about 3 hours, and then cooling spontaneously to room temperature while purging with an inert gas (e.g., nitrogen gas) throughout the process. In certain aspects and embodiments, the purging with an inert gas (e.g., nitrogen) is at a gas flow rate of about 100 cm.sup.3/min.

[0087] In certain aspects and embodiments, converting the carbonized resorcinol-formaldehyde gel to an activated carbon gel comprises heating up to 700° C. (e.g., 550, 575, 600, 625, 650, 675, 700, 725, or 750° C.), keeping this temperature constant for 1 hour and then cooling spontaneously to room temperature while purging with carbon dioxide gas (for example) throughout the process. In certain aspects and embodiments, the purging with carbon dioxide gas is at a gas flow rate of about 150 cm.sup.3/min.

[0088] In certain aspects and embodiments, the activated carbon gel has an average pore size of from about 1.0 to 2.1 nm (e.g., about 0.8, 0.9, 1.0, 1.1, 1.2, 1.3, 1.4, 1.5, 1.6, 1.7, 1.8, 1.9, 2.0, 2.1, 2.2, 2, 3, or 2.4 nm).

[0089] In certain aspects and embodiments, the activated carbon gel has an average area of micropores of from about 0.3 to 1.1% of the total area (e.g., about 0.3, 0.4, 0.5, 0.6, 0.7, 0.8, 0.9, 1.0, or 1.1%).

[0090] In certain aspects and embodiments, the activated carbon gel has an average area of mesopores of from about 11 to 35% of the total area (e.g., about 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, 20, 21, 22, 23, 24, 25, 26, 27, 28, 29, 30, 31, 32, 33, 34, 35, 36, 38, 39, or 40%).

[0091] In certain aspects and embodiments, the activated carbon gel has an average area of macropores of from about 63 to 88% of the total area (e.g., about 58, 59, 60, 61, 62, 63, 64, 65, 66, 67, 68, 69, 70, 71, 72, 73, 74, 75, 76, 77, 78, 79, 80, 81, 82, 83, 84, 85, 86, 87, 88, 89, or 90%).

[0092] In certain aspects and embodiments, the activated carbon gel has an average particle size of from about 0.20 to 6.60 μm (e.g., about 0.15, 0.18, 0.20, 0.25, 0.30, 0.35, 0.40, 0.45, 0.50, 0.55, 0.60, 0.65, 0.70, 0.75, 0.80, 0.85, 0.9, 1.1, 1.15, 1.20, 1.25, 1.3, 1.4, 1.5, 1.6, 1.7, 1.8, 1.9, 2.0, 2.1, 2.2, 2.3, 2.4, 2.5, 2.6, 2.7, 2.8, 2.9, 3.0, 3.2, 3.4, 3.6, 3.8. 4.0, 4.2, 4.4, 4.6, 4.8, 5.0, 5.2, 5.4, 5.6, 5.8, 6.0, 6.2, 6.4, 6.6, 6.8, or 7.0 μm).

[0093] In certain aspects and embodiments, the I.sub.D/I.sub.G ratio of activated carbons is from about 0.82 to 0.90 (e.g., about 0.80, 0.81, 0.82, 0.83, 0.84, 0.85, 0.86, 0.87, 0.88, 0.89, 0.90, 0.91, or 0.92).

[0094] In certain aspects and embodiments, the activated carbon gel has an activated carbon % of at least about 14 to 60% (e.g., depending on the applied composition and at an irradiation dose of 40 kGy) (e.g., about 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, 20, 21, 22, 23, 24, 25, 26, 27, 28, 29, 30, 31, 32, 33, 34, 35, 36, 38, 39, 40, 41, 42, 43, 44, 45, 46, 47, 48, 49, 50, 51, 52, 53, 54, 55, 56, 57, 58, 59, 60, 61, 62, 63, 64, or 65%).

[0095] In certain aspects and embodiments, the activated carbon gel has an activated carbon % of at least about 32 to 56% (e.g., depending on the irradiation dose at a fixed composition) (e.g., about 27, 28, 29, 30, 31, 32, 33, 34, 35, 36, 38, 39, 40, 41, 42, 43, 44, 45, 46, 47, 48, 49, 50, 51, 52, 53, 54, 55, 56, 57, 58, 59, 60, 61, or 62%).

[0096] In certain aspects and embodiments, the present invention is useful for the preparation of resorcinol/formaldehyde gels. More broadly, this novel technique can be applied in the synthesis of xerogels, aerogels and cryogels from resorcinol/formaldehyde or their related family of main reactants, which widens the scale of gel products and their applications.

EXAMPLES

[0097] As used herein, the symbols and conventions used in these processes, schemes and examples, regardless of whether a particular abbreviation is specifically defined, are consistent with those used in the contemporary scientific literature, for example, the Journal of the American Chemical Society or the Journal of Biological Chemistry. Specifically, but without limitation, the following abbreviations may be used in the examples and throughout the specification: g (grams); mg (milligrams); mL (milliliters); μL (microliters); mM (millimolar); μM (micromolar); Hz (Hertz); MHz (megahertz); mmol (millimoles); hr or hrs (hours); min (minutes); MS (mass spectrometry); ESI (electrospray ionization); TLC (thin layer chromatography); HPLC (high pressure liquid chromatography); THE (tetrahydrofuran); CDCl.sub.3 (deuterated chloroform); AcOH (acetic acid); DCM (dichloromethane); DMSO (dimethyl sulfoxide); DMSO-d.sub.6 (deuterated dimethyl sulfoxide); EtOAc (ethyl acetate); MeOH (methanol); and BOC (t-butyloxycarbonyl).

[0098] For all of the following examples, standard work-up and purification methods known to those skilled in the art can be utilized. Unless otherwise indicated, all temperatures are expressed in ° C. (degrees Centigrade). All reactions are conducted at room temperature unless otherwise noted. Synthetic methodologies illustrated herein are intended to illustrate the applicable chemistry through the use of specific examples, not to restrict the full scope of the disclosure.

Example 1: Preparation of Compounds 1, 1a and 1b

[0099] This example provides a method of synthesis for Compounds 1, 1a, and 1b.

Proposed Reaction Mechanism of Resorcinol/Formaldehyde Gel

[0100] Without intending to be limited by theory, FIG. 1A illustrates a proposed reaction mechanism of resorcinol with formaldehyde reactants in the presence of radiolysis species that initiate the polymerization and gelation reaction processes.

Preparation of Gels

[0101] The synthesis of resorcinol-formaldehyde gels (RFGs) is carried out via the exposure to γ-rays in the range of 10 to 70 kGy with a dose rate of 0.34 kGy/h at room temperature (e.g., 40 kGy for Table 2). A Gamma cell .sup.60Co apparatus (e.g., supplied from Atomic Energy of Canada LTD, Kanata, Ontario-Canada, Model GC-220, Serial No 234, Type B(U)) was used to generate the γ-rays. A schematic of the apparatus and sample location is shown in FIG. 1C. The effects of irradiation dose and RFG composition on the produced RFG samples were evaluated. After irradiation the extracted gels were put in an oven at 50±1° C. for 3 days to dry.

[0102] The synthesis details regarding the effect of radiation dose and the effect of reactants' composition on the product RFGs are listed in Tables 1 and 2, respectively.

TABLE-US-00001 TABLE 1 Effect of radiation dose (at dose rate 0.34 kGy/h) on RFGs and RFG-ACs. R F Dose RFG RFG-AC R:F R:W (g) (mL) (kGy) Product RFG1 RFG1-AC 0.90 0.40 12.44 10.19 10 high viscous gel RFG1 RFG1-AC 0.90 0.40 12.44 10.19 20 solid gel RFG1 RFG1-AC 0.90 0.40 12.44 10.19 30 solid gel RFG1 RFG1-AC 0.90 0.40 12.44 10.19 40 solid gel RFG1 RFG1-AC 0.90 0.40 12.44 10.19 50 solid gel RFG1 RFG1-AC 0.90 0.40 12.44 10.19 60 solid gel RFG1 RFG1-AC 0.90 0.40 12.44 10.19 70 solid gel RFG5 RFG5-AC 0.50 0.24 12.44 17.40 10 low viscous gel RFG5 RFG5-AC 0.50 0.24 12.44 17.40 20 high viscous gel RFG5 RFG5-AC 0.50 0.24 12.44 17.40 30 solid gel RFG5 RFG5-AC 0.50 0.24 12.44 17.40 40 solid gel RFG5 RFG5-AC 0.50 0.24 12.44 17.40 50 solid gel RFG5 RFG5-AC 0.50 0.24 12.44 17.40 60 solid gel RFG5 RFG5-AC 0.50 0.24 12.44 17.40 70 solid gel RFG9 RFG9-AC 0.10 0.04 12.44 91.68 10 liquid solution RFG9 RFG9-AC 0.10 0.04 12.44 91.68 20 low viscous gel RFG9 RFG9-AC 0.10 0.04 12.44 91.68 30 high viscous gel RFG9 RFG9-AC 0.10 0.04 12.44 91.68 40 solid gel RFG9 RFG9-AC 0.10 0.04 12.44 91.68 50 solid gel RFG9 RFG9-AC 0.10 0.04 12.44 91.68 60 solid gel RFG9 RFG9-AC 0.10 0.04 12.44 91.68 70 solid gel

TABLE-US-00002 TABLE 2 Effect of reactants composition of RFGs and their consequent RFG-ACs. Dose RFG RFG-AC R:F R:W R(g) F(mL) (kGy) Product RFG1 RFG1-AC 0.90 0.40 12.44 10.19 40 solid gel RFG2 RFG2-AC 0.80 0.35 12.44 11.46 40 solid gel RFG3 RFG3-AC 0.70 0.31 12.44 13.10 40 solid gel RFG4 RFG4-AC 0.60 0.26 12.44 15.28 40 solid gel RFG5 RFG5-AC 0.50 0.24 12.44 17.40 40 solid gel RFG6 RFG6-AC 0.40 0.19 12.44 21.74 40 solid gel RFG7 RFG7-AC 0.30 0.14 12.44 28.99 40 solid gel RFG8 RFG8-AC 0.20 0.09 12.44 45.84 40 solid gel RFG9 RFG9-AC 0.10 0.04 12.44 91.68 40 solid gel Radiolytic gelation was made at 40 kGy with a dose rate of 0.34 kGy/h.

Carbonization and Activation Processes

[0103] The dried RFG sample was placed in a ceramic boat inside a programmable electric-heated tube furnace (Nabertherm GmbH, Germany), through which nitrogen gas was passed with a continuous flow rate of 100 cm.sup.3/min at 0.3 bar. The tube furnace was first kept at room temperature for 40 minutes to guarantee that air is fully purged with the flowing N.sub.2 gas in presence of the RFG sample. Then, the furnace was heated up to a temperature of 500° C. at a heating rate of 10° C./minute. The furnace was maintained at 500° C. for 3 h and then allowed to cool spontaneously to room temperature under flowing nitrogen.

[0104] After cleaning the tube furnace comprehensively from carbonization process remains, the carbonized gel was activated in the same tube furnace with a carbon dioxide gas flow of 150 cm.sup.3/min at 0.3 bar, instead of nitrogen gas flow. The sample was again heated up to 700° C. at a rate of 10° C./minute, maintained at 700° C. for 1 h, and then allowed to cool to room temperature while still flowing carbon dioxide.

[0105] After the carbonization and activation processes, the activated products were designated RFG activated carbons and denoted as RFG-AC with a corresponding code number related to the used recipe (see, e.g., Tables 1 and 2).

Characterization

[0106] FT-Raman spectra were measured by utilizing a Bruker FT-Raman spectrometer of type RFS 100/S that is attached to a Bruker-IFS 66/S spectrometer. Fourier transform infrared (FTIR) spectroscopy (NICOLET, iS10, Thermo-Scientific) was used to examine the structure of the synthesized samples. X-ray diffraction (XRD) measurements were proceeded by Miniflex II Benchtop XRD apparatus, manufactured by Rigaku Corporation, Japan. The 2θ scan data were collected at 0.05° intervals over the range of 5 to 80 at a scan rate of 0.05°/min. The morphology of RFG and RFG-AC samples were scanned by SEM FEI Nova™ nanoscanning electron microscopy 450 (Nova NanoSEM). The chemical compositions of RFG and RFG-AC samples were studied by energy-dispersive X-ray spectroscopy (EDX) connected to Nova NanoSEM. Thermogravimetric analyses (TGA) were conducted by a PerkinElmer Pyris6 TGA analyzer under nitrogen gas in the range of 30 to 800° C. with heating rate 10° C./min. A Micromeritics ASAP2420® Accelerated Surface Area and Porosimetry Analyzer System, with an enhanced micropore capability (utilizing 1-Torr pressure transducer), was utilized to investigate the pore structures of RFG-AC samples through the adsorption/desorption isotherms of nitrogen at −196° C. Before the adsorption measurements, RFG-AC samples were degassed in-situ for 24 h at 150° C. and 200° C., respectively under vacuum (1×10.sup.−4 Pa). The pore structures of RFG-AC samples were attained by built-in calculations depending on the density functional theory (DFT).

[0107] The instant inventive disclosure is fully different from those already reported in the literature on synthesis of resorcinol/formaldehyde gels or their derivative reactants and their subsequent carbons either in literature or in commercial products. The resorcinol/formaldehyde gels or their derivative family found in literature or global market (as commercial products) are manufactured by conventional methods that contain catalyst, initiators, additives, buffer, etc. These initiators or additives prohibit and restrict the applications especially in sensitive fields such as biomaterials, pharmaceutics, biomaterials, biomedical applications, cosmetics, etc., which require materials that are highly pure and clean from initiators or additives that might be trapped in their structure. This novel approach is characterized by using only the main reactants required and thus producing highly pure, clean, and sterilized gel products. The process of synthesis is environmentally friendly. Further, the manufactured gels and their subsequent carbons are unique and may widen the range of their applications.

[0108] A detailed technical description of the process used in this invention has been provided in the previous section.

[0109] FIG. 2 shows the FTIR spectra of RFGs of different gel samples, in which the broadband at 3250 cm.sup.−1 is a characteristic of OH stretching vibrations in phenol. Absorption bands at 2939 and 1440 cm.sup.−1 are associated with CH.sub.2 stretching. The absorption band at 1608 cm.sup.−1 was assigned to the aromatic ring stretching vibrations. The bands at 1280 and 1090 cm.sup.−1 confirm the methylene ether C—O—C linkage stretching between resorcinol molecules (phenyl rings), as expected in the polycondensation reaction between resorcinol and formaldehyde.

[0110] FIG. 3 describes the Raman spectra of RFG samples crosslinked radiolytically using γ-rays at two main bands. The first band at 1355 cm.sup.−1, named as ‘disorder-induced’ (I.sub.D) band, commonly ascribes the lack of long-range translation symmetry in disordered carbons atoms (see Gholipour-Ranjbar H., M. R. Ganjali, P. Norouzi, and H. R. Naderi, “Functionalized graphene aerogel with p-phenylenediamine and its composite with porous MnO.sub.2: investigating the effect of functionalizing agent on supercapacitive performance,” J. Mater. Sci. Mater. Electron., 27 (2016), pp. 10163-10172). The second (graphitic) band appearing at 1591 cm.sup.−1 is named as (I.sub.G). It is ascribed to a Raman-allowed E.sub.2g resulting from ‘in plane’ displacement of carbons strongly coupled in the hexagonal sheets, and is characteristic of sp.sup.2-hybridized C—C bonds in a two-dimensional hexagonal lattice (see M. Zafra, P. Lavela, C. Macias, G. Rasines “Electrosorption of environmental concerning anions on a highly porous carbon aerogel,” J. Electroanal. Chem., 708 (2013), pp. 80-86).

[0111] FIG. 4 exposes the Raman intensity ratio of the I.sub.D and I.sub.G bands (denoted by I.sub.D/I.sub.G). This I.sub.D/I.sub.G ratio can be used to evaluate the graphitic nature of the gel sample. It was seen from the results that the RFG6 represents the highest graphic order (lowest I.sub.D/I.sub.G ratio) among samples whereas RFG9 represents the lowest graphic order (highest I.sub.D/I.sub.G ratio) among samples. Further, the sequential order of these gel samples are RFG6>RFG3≈RFG8>RFG4>RFG1>RFG2≈RFG5≈RFG7>RFG9. Overall, the I.sub.D/I.sub.G ratio was almost constant in the range from 0.70 to 0.80. Without intending to be bound by theory, this small fluctuation in I.sub.D/I.sub.G values may be due to the competition between the two processes of high degradation and crosslinking. Further, this may be due to the random effect of γ-rays.

[0112] FIG. 5A exhibits TGA thermograms of RFG1 through RFG9 samples crosslinked at 40 kGy with a of dose rate of 0.34 kGy/h. The TGA curves were collected in the range from room temperature to 847° C. Overall, there are three major stages of weight losses, these ranges were at temperatures between 40-172° C., 172-439° C. and 439-793° C. The derivative thermogravimetric (DTG) (see FIG. 5B) exposed these three stages of thermal decompositions for all RFG samples. The peaks of weight losses in the first stage occurred at 101, 125, 101, 93, 84, 70, 89, 90 and 85° C., for RFG1 through RFG9, respectively. The weight loss peaks in the second stage are at 380, 347, 380, 380, 380, 385, 371, 383 and 383° C., for RFG1 through RFG9, respectively. Further, the weight loss peaks in the third stage are at 612, 620, 612, 603, 609, 576, 598, 602 and 602° C., for RFG1 through RFG9, respectively. The peaks at these three stages correspond, respectively, to the removal of adsorbed moisture, solvent removal/decomposition, and carbonization of gels. Without intending to be bound by theory, the gels' decomposition include the breakage of C—O and C—H bonds at 347-385° C. and 603-612° C., respectively. Briefly, it can be concluded that the differences in thermal stability are due the differences in the ratio between resorcinol and formaldehyde as main reactants.

[0113] FIG. 6 exhibits the XRD patterns of RFG1 through RFG9 crosslinked at 40 kGy with a dose rate of 0.34 kGy/h. All samples displayed similar patterns with a broad peak at 20=20°. This indicates that these gel samples have an amorphous structure. Further, the intensities of these peaks differ from one gel sample to another. Overall, the highest and lowest intensities are 1814 and 1379 cps for the corresponding RFG2 and RFG6 samples, respectively. Moreover, the intensity order of these gel samples are as RFG2>RFG1>RFG5>RFG7>RFG9>RFG3>RFG8>RFG4>RFG6.

[0114] FIG. 7 shows the SEM photomicrographs of RFG1 through RFG9 crosslinked at an irradiation dose of 40 kGy with a dose rate of 0.34 kGy/h. The morphologies of RFG1 and RFG2 samples indicate porous structures, where the pore sizes in RFG1 are larger than those in RFG2. Overall, the morphologies of all RFG samples are different and unique from each other.

[0115] FIG. 8 shows the optical photos of RFG1 through RFG9 crosslinked at 40 kGy with a dose rate of 0.34 kGy/h. The shapes of all gel samples tested are monolithic, and the colours of samples are red-brown. The volumes of samples decrease (due to shrinkage upon drying) by increasing the sample number (i.e., by decreasing the R:F ratio).

Elemental Analysis

[0116] The elemental analysis values listed in Table 3 indicate that the percentages of carbon and oxygen vary slightly from RFG1 to RFG9. On the other hand, while the percentage of activated carbons (i.e., the mass of activated carbon produced relative to the mass of the starting gel) decreases significantly by increasing the formaldehyde in the feeding solution of reaction (i.e., by increasing the sample number).

TABLE-US-00003 TABLE 3 EDX elemental analyses and percentage of conversion (to activated carbon) for the samples RFG1 through RFG9 crosslinked at 40 kGy with a dose rate of 0.34 kGy/h. Elemental analysis Activated Sample Carbon (wt. %) Oxygen (wt. %) carbon (%) RFG1 88.0 12.0 60.4 RFG2 87.5 12.6 58.4 RFG3 86.7 13.3 57.9 RFG4 84.4 15.6 42.0 RFG5 84.5 15.5 49.1 RFG6 84.8 15.2 48.6 RFG7 84.6 15.4 45.6 RFG8 85.4 14.6 28.8 RFG9 85.2 14.8 13.8

[0117] Table 4 shows the effect of the irradiation dose an reaction composition on the percentage of outcome activated carbons. Overall, the percentage of activated carbon of RFG1 decreases by increasing radiation dose, as in both RFG5 and RFG9 the percentage of activated carbons decreases by increasing the radiation dose. Furthermore, the percentage of activated carbons decreases by increasing formaldehyde solution into the reaction media (i.e., increasing sample number), especially at high radiation dose.

TABLE-US-00004 TABLE 4 Effect of irradiation dose on the percentage of conversion (to activated carbon) for selected RFG samples. Activated carbon (%) Radiation Dose (kGy) Sample 20 30 40 50 60 70 RFG1 41.1 43.7 46.0 31.7 57.6 49.1 RFG5 55.5 46.3 46.0 45.7 45.4 40.9 RFG9 NA NA 45.7 36.0 35.3 34.6

[0118] Table 4 shows the effect of the irradiation dose and reaction composition on the percentage of outcome activated carbons. Overall, the percentage of activated carbon of RFG1 decreases by increasing radiation dose, as in both RFG5 and RFG9 the percentage of activated carbons decreases by increasing the radiation dose. Furthermore, the percentage of activated carbons decreases by increasing formaldehyde solution into the reaction media (i.e., increasing sample number), especially at high radiation dose.

[0119] FIG. 9 shows the adsorption/desorption isotherms of N2 at −196° C. onto RFG1-AC through RFG9-AC. The isotherms on all samples are of type-IV due to the presence of hysteresis loops that indicate the presence of mesopores and macropores. According to the IUPAC classification, the isotherms fall under Type-IV with an H4-type hysteresis. A steep increase of volume adsorbed at low relative pressure (P/PO) is an indication of microporous structure.

[0120] Without intending to be bound by theory, this is due to the pore condensation process in which gas condenses to a liquid-like phase in pores at a pressure less than the saturation pressure P/PO of the bulk fluid. The nature of the adsorption process in these samples is monolayer/multilayer adsorption. The monolayer of the adsorbate is formed at low pressure, while the low slope region in the middle of the isotherm refers to the formation of the first few multilayers. The isotherms show lower adsorption capacity at low pressure, which afterwards increase with increasing pressure. Therefore, these results indicate to that the RFG1-AC through RFG9-AC samples have little micro-porosity and more of mesopores and macropores.

[0121] This conclusion agrees with the results listed in Table 5, which shows that for all samples in the table, mesopores are in the order of ˜10-30% and macropores in the order of ˜70 to 90%. Table 5 also shows that both the total pore volume and total surface area increase slightly by increasing the amount of formaldehyde in the matrix of the RFG used to produce the activated carbon (i.e., with increasing sample number). The average pore width increases slightly by increasing the amount of formaldehyde in the structure of obtained activated carbon. There is a general trend that the percentages of micropores increase slightly by increasing the amount of formaldehyde, but it remains up to ˜1%. The mesopores increase when increasing the amount of formaldehyde, where they increase from 11% to 28% when comparing RFG1-AC to RFG9-AC. On the other hand, macropores decreased when increasing the amount of formaldehyde where they drop from 88% to 71% when comparing RFG1-AC to RFG9-AC. Consequently, the data suggest that the structures of these activated carbon samples forms three types of pores, which have a majority of macropores followed by mesopores and a minimal extent of micropores.

[0122] FIG. 10 exhibits the relationship between the pore widths and cumulative pore volumes of RFG1-AC through RFG9-AC samples. Overall, it is seen that the cumulative pore volume increases by increasing the pore widths. The cumulative pore volume of RFG1-AC increases up to 0.134 cm.sup.3/g for the corresponding pore width of 1.8 nm and then then levels off. The cumulative pore volume of RFG2-AC increases up to 0.141 cm.sup.3/g for the corresponding pore width of 1.29 nm and then levels off. The cumulative pore volume of RFG3-AC increases up to 0.130 cm.sup.3/g for corresponding pore width of 1.1 nm and then levels off. The cumulative pore volume of RFG4-AC increases up to 0.179 cm.sup.3/g for the corresponding pore width of 1.3 nm then levels off. The cumulative pore volume of RFG5-AC increases up to 0.088 cm.sup.3/g for the corresponding pore width of 1.4 nm and then levels off. The cumulative pore volume of RFG6-AC increases through the whole range up to 0.216 cm.sup.3/g for the corresponding pore width up to 252.6 nm. The cumulative pore volume of RFG7-AC increases through the whole range up to 0.359 cm.sup.3/g for the corresponding pore width up to 172.1 nm. The cumulative pore volume of RFG8-AC increases through the whole range up to 0.217 cm.sup.3/g for the corresponding pore width up to 117.2 nm. The cumulative pore volume of RFG9-AC increases through the whole range up to 0.295 cm.sup.3/g for the corresponding pore width of 159.4 nm.

[0123] FIGS. 11A, 11B, and 11C display the relationship between the incremental pore volume and pore width of RFG1-AC through RFG9-AC. FIG. 11A represents the full scale of incremental pore volume against pore size, while FIGS. 11B and 11C are presented with more convenient scales for clarity and to avoid overcrowding. FIG. 11B shows that RFG1-AC has two peaks at 0.8 and 1.1 nm for the corresponding incremental pore volumes of 0.009 and 0.058 cm.sup.3/g and with no peaks seen in FIG. 11C. RFG2-AC has only one peak at ˜1 nm for the corresponding incremental pore volume of 0.084 cm.sup.3/g as shown in FIG. 11B and with no peaks seen in FIG. 11C. RFG3-AC has only one peak at 1.1 nm for the corresponding incremental pore volume of 0.105 cm.sup.3/g and with no peaks seen in FIG. 11C. FIG. 11B shows that RFG4-AC has three peaks at 0.8, 1.0 and 1.2 nm for the corresponding incremental pore volumes of 0.020, 0.027, 0.037 and 0.054 cm.sup.3/g, respectively. Further, a small peak was observed in FIG. 11C for RFG4-AC at 14.8 nm with the corresponding incremental pore volume of 0.008 cm.sup.3/g. RG5-AC shows two peaks at 1.1 and 1.3 nm for the corresponding incremental pore volumes of 0.021, 0.017 and 0.020 cm.sup.3/g, respectively. FIG. 11C shows that the RFG5-AC shows two other peaks at 13.7 and 216.0 nm for the corresponding incremental pore volumes of 0.004 and 0.002 cm.sup.3/g, respectively. RFG6-AC has two peaks observed from FIG. 11B at 1.2 and 1.5 nm with the corresponding incremental pore volumes of 0.052 and 0.028 cm.sup.3/g, respectively. It also shows two peaks in FIG. 11C, one of them is broad peaking at 50.4 nm and the other is at 117.2 nm with the corresponding incremental pore volumes of 0.003 and 0.029 cm.sup.3/g, respectively. RFG7-AC presents three peaks in FIG. 11B at 0.7, 1.1 and 1.3 nm with the corresponding incremental pore volumes of 0.039, 0.084 and 0.022 cm.sup.3/g, respectively. In FIG. 11C, RFG7-AC reveals five peaks at 21.6, 68.5, 93.1, 117.1, 147.6 nm with the corresponding incremental pore volumes of 0.006, 0.007, 0.006, 0.003 and 0.002 cm.sup.3/g, respectively. It exhibits two peaks at 0.8 and 1.1 nm with the corresponding incremental pore volumes of 0.014 and 0.084 cm.sup.3/g, respectively. Further, FIG. 11C shows that RFG8-AC presents seven peaks are at 23.4, 31.8, 40.0, 50.4, 68.5, 79.9 and 108.6 nm with the corresponding incremental pore volumes of 0.019, 0.002, 0.004, 0.003, 0.002, 0.003 and 0.002 cm.sup.3/g, respectively. RGF9-AC refers to four peaks in FIG. 11B at 0.7, 0.8, 1.1 and 1.3 nm with the corresponding incremental pore volumes of 0.043, 0.012, 0.05 and 0.028 cm.sup.3/g, respectively. Moreover, the same sample of RFG9-AC in FIG. 11C shows six peaks at 31.8, 50.4, 68.5, 79.9, 117.2 and 147.6 nm with the corresponding incremental pore volumes of 0.004, 0.007, 0.0037, 0.004, 0.003 and 0.003 cm.sup.3/g, respectively.

[0124] FIG. 12 shows the effect of pore width on the cumulative surface area of RFG1-AC through RFG9-AC. Overall, the cumulative surface area increases by increasing pore width. The cumulative surface area of RFG1-AC increases by increasing pore width up to 31.4 m.sup.2/g for the corresponding pore size of 0.8 nm, then levels off, and then increases again up to 254.9 m.sup.2/g with the corresponding pore width of 1.1 nm until it saturates at that value. The cumulative surface area of RFG2-AC increases with increasing pore width up to 270.8 m.sup.2/g at the corresponding pore width of 1.1 nm and then levels off at the same value. The cumulative surface area of RFG3-AC increases with increasing pore width up to 241 m.sup.2/g at the corresponding pore width of 1.1 nm and then levels off at the same value. The cumulative surface area of RFG4-AC increases with increasing pore width up to 83 m.sup.2/g at the corresponding pore width of 0.8 nm, levels off, and then increases again up to 321 m.sup.2/g at the corresponding pore width of 1.3 nm until it again levels off. The cumulative surface area of RFG5-AC increases with increasing pore width up to 122.4 m.sup.2/g at the corresponding pore width of 1.3 nm and then levels off. The cumulative surface area of RFG6-AC increases with increasing pore width up to 180.3 m.sup.2/g at the corresponding pore width of 1.2 nm, followed by an increase up to 245.4 m.sup.2/g for the corresponding pore width of 1.5 nm until it again levels off. The cumulative surface area of RFG7-AC increases with increasing pore width up to 339.5 m.sup.2/g for the corresponding pore width of 1.4 nm and then levels off. The cumulative surface area of RFG8-AC increases with increasing pore width up to 50.4 m.sup.2/g for the corresponding pore width of 0.8 nm, increases again up to 335 m.sup.2/g at the corresponding pore width of 1.2 nm, and then levels off. The cumulative surface area of RFG9-AC increases with increasing pore width up to 211 m.sup.2/g at the corresponding pore width of 0.8 nm, followed by another increase again up to 417 m.sup.2/g at the corresponding pore width of 3.4 nm, and then levels off.

[0125] FIGS. 13A and 13B show the incremental surface area versus pore width of RFG1-AC through RFG9-AC. FIG. 13A displays the full scale of pore width (0-500 nm), while FIG. 13B shows data only in the range from 0.6 to 1.8 nm for clarity and for avoiding the overcrowding of curves into one graph. FIG. 13B also shows that incremental surface areas of RFG1-AC exposes two main peaks at 24.4 and 106.8 m.sup.2/g at the corresponding pore widths of 0.8 and 1.1 nm, respectively. The incremental surface areas of RFG2-AC exposes one main peak at 122.2 m.sup.2/g at the corresponding pore width 1.1 nm. RFG3-AC shows only one main peak at 194.03 m.sup.2/g for the corresponding pore width 1.1 nm. RFG4-AC shows three peaks at 50.5, 54.2 and 92.8 m.sup.2/g for the corresponding pore width 0.8, 1.0, and 1.2 nm, respectively. RFG5-AC indicates to two peaks at 38.6 and 32.1 m.sup.2/g for the corresponding pore width 1.1 and 1.3 nm, respectively. RFG6-AC indicates to two peaks at 89.14 and 37.8 m.sup.2/g for the corresponding pore width 1.2 and 1.5 nm, respectively. RFG7-AC has three peaks at 10.8, 155.3 and 35.7 m.sup.2/g for the corresponding pore width 0.7, 1.1 and 1.3 nm, respectively. RFG8-AC shows two peaks at 35 and 157.1 m.sup.2/g for the corresponding pore width 0.8 and 1.1 nm, respectively. RFG9-AC exposes four peaks at 128.2, 31.2, 95.2 and 45.3 m.sup.2/g for the corresponding pore widths of 0.7, 0.8, 1.1 and 1.3 nm, respectively.

[0126] The results listed in Table 5 show that I.sub.D/I.sub.G tends to increase with increased formaldehyde in the preparation reaction media. A detailed analysis indicates that I.sub.D/I.sub.G increases for RFG2-AC and varies for RFG6-AC to RFG9-AC. This extent of distortion behaviour in the sample is due to the random reaction with γ-rays, which affects the formation of structure during the synthesis process.

TABLE-US-00005 TABLE 5 Pore characteristics and elemental analysis of RFG1-AC through RFG9-AC samples. Average.sup.b Average.sup.b Average.sup.b Average.sup.b V.sub.Total.sup.a S.sub.total.sup.a pore size micropore size mesopore size macropore size sample (cm.sup.3/g) (m.sup.2/g) (nm) (%) (%) (%) RFG1-AC 0.134 254.9 1.0 0.3 11.2 88.4 RFG2-AC 0.141 270.8 1.0 0.5 16.5 83.0 RFG3-AC 0.130 241.0 1.1 0.3 11.2 88.4 RFG4-AC 0.179 321.0 1.1 0.5 16.5 83.0 RFG5-AC 0.088 122.4 1.4 0.4 17.8 81.8 RFG6-AC 0.216 245.4 1.8 0.6 17.8 81.7 RFG7-AC 0.359 339.5 2.1 0.8 26.1 73.1 RFG8-AC 0.217 334.9 1.3 1.1 35.5 63.4 RFG9-AC 0.295 417.2 1.4 0.9 28.2 70.9 Average N.sub.2 particle size.sup.c adsorption capacity .sup.d I.sub.D/I.sub.G EDX elemental analysis Sample (μm) (mmol/g) ratio Carbon (wt. %) Oxygen (wt. %) RFG1-AC 6.6 4.6 0.84 98.2 1.8 RFG2-AC 0.4 5.1 0.86 98.9 1.1 RFG3-AC 1.4 4.6 0.82 99.0 1.1 RFG4-AC 0.4 6.2 0.83 98.1 1.9 RFG5-AC 0.7 2.9 0.86 98.9 1.1 RFG6-AC 0.3 7.1 0.87 99.0 1.0 RFG7-AC 0.2 12.0 0.85 99.0 1.1 RFG8-AC 0.3 7.7 0.90 96.8 3.2 RFG9-AC 0.2 10.2 0.87 96.9 3.1 .sup.aValues derived from DFT, .sup.bcalculated based on incremental surface area, .sup.csnatched from Micromeritics summary sheet, and .sup.d Maximum amount of N.sub.2 gas adsorbed at −196° C.

CONCLUSIONS

[0127] In certain embodiments, this invention presents a novel route to synthesize gels (e.g., resorcinol/formaldehyde gels and their gel derivatives) and their subsequent carbons by using the gamma-irradiation technique of .sup.60Co as the main source of γ-rays. This novel route is featured by using only the main reactants, without any additives such as catalysts or buffers, in a fast reaction process that depends on the rate of irradiation dose and can be used in synthesis of other gels. This makes this process friendlier to the environment and results in uncontaminated products that can be very useful in sensitive applications such as biomaterials, pharmaceuticals, biomedical materials, cosmetics, and the like. Furthermore, this route is easy to be up-scaled for mass production. Different compositions of resorcinol and formaldehyde reactants were used to synthesize the corresponding gels via exposing these reactants to different irradiation doses. Moreover, the activated carbon derivatives of these gels were prepared. Various characterization techniques were used to characterize the outcome products (both gels and activated carbons). The techniques confirmed that resorcinol/formaldehyde gels and their subsequent activated carbons were successfully prepared in a wide range of irradiation doses and ingredient compositions. Consequently, the use of γ-rays to produce resorcinol/formaldehyde gels (e.g., xerogels, aerogels, cryogels, and their related starting materials of same family) and their subsequent activated carbon are possible.

[0128] All publications, patents, and patent applications cited in this specification are herein incorporated by reference as if each individual publication, patent, or patent application were specifically and individually indicated to be incorporated by reference. While the claimed subject matter has been described in terms of various embodiments, the skilled artisan will appreciate that various modifications, substitutions, omissions, and changes may be made without departing from the spirit thereof. Accordingly, it is intended that the scope of the subject matter limited solely by the scope of the following claims, including equivalents thereof.