Method for making steel or titanium products containing a precipitation-hardening nickel-base alloy, and part

Abstract

Combining a precipitation-hardening nickel-base alloy with a steel or titanium substrate makes it very easy to repair parts, the nickel-base alloy having good erosion-resistant properties. A method for producing is disclosed. In particular for repairing, a component having a substrate, in particular turbine blades made of steel or titanium, in particular made of martensitic or precipitation-hardening chromium-rich steels, with a localized deposition weld or with an affixed shaped part, in which a precipitation-hardening nickel-based alloy is used as the localized deposition weld or as the shaped part, in which a laser powder deposition weld or an arc deposition weld is performed.

Claims

1. A method for repairing a leading edge of a turbine blade component, comprising: providing the turbine blade component as a substrate, wherein the substrate is made of martensitic or precipitation-hardening chromium-rich steels, wherein the substrate is not a nickel-based alloy or a nickel-based superalloy, and wherein the substrate is X.sub.5CrNiCuNb.sub.16.sup.−4, and connecting a precipitation-hardening nickel-based alloy to the substrate proximate the leading edge of the turbine blade component, with a localized deposition weld or with an affixed shaped part, wherein the localized deposition weld is formed by a laser powder deposition weld or an arc deposition weld, wherein the precipitation-hardening nickel-based alloy has a chromium content of 10 wt % to 13.75 wt % and/or a molybdenum content of 0.1 wt % to 2.5 wt %.

2. The method as claimed in claim 1, in which the shaped part made of a precipitation-hardening nickel-based alloy is connected to the substrate.

3. The method as claimed in claim 1, in which the shaped part made of a precipitation-hardening nickel-based alloy is brazed into or onto the substrate.

4. The method as claimed in claim 1, having a γ′ fraction≤30%, for the precipitation-hardening nickel-based alloy.

5. The method as claimed in claim 1, in which the deposition weld has just one layer.

6. The method as claimed in claim 1, wherein the precipitation-hardening nickel-based alloy is corrosion-resistant, nickel chromium alloy.

7. A component, comprising: a substrate, wherein the substrate is a turbine blade made of martensitic or precipitation-hardening chromium-rich steel, wherein the substrate is not a nickel-based alloy or a nickel-based superalloy, and wherein the substrate is X.sub.5CrNiCuNb.sub.16.sup.−4, and a precipitation-hardening nickel-based alloy, wherein the precipitation-hardening nickel-based alloy is present only locally on a leading edge of the turbine blade as a deposition weld or as a shaped part, further wherein the deposition weld is formed by a laser powder deposition weld or an arc deposition weld, wherein the precipitation-hardening nickel-based alloy has a chromium content of 10 wt % to 13.75 wt % and/or a molybdenum content of 0.1 wt % to 2.5 wt %.

8. A turbine blade component, the turbine blade component comprising: a substrate, wherein the substrate is not a nickel-based alloy or a nickel-based superalloy, and wherein the substrate is TiAl.sub.6V.sub.4; and a precipitation-hardening nickel-based alloy having a chromium content of 10 wt % to 13.75 wt % and/or a molybdenum content of 0.1 wt % to 2.5 wt %; wherein the precipitation-hardening nickel-based alloy comprises at least one of: a shaped part, located only locally on the substrate in a leading edge region of the turbine blade component, wherein the shaped part is brazed to the substrate; and a deposition weld located only locally on the substrate in the leading edge region of the turbine blade component.

Description

DESCRIPTION OF THE DRAWINGS

(1) Some of the embodiments will be described in detail, with reference to the following figures, wherein like designations denote like members, wherein:

(2) FIG. 1 shows an exemplary embodiment of the invention;

(3) FIG. 2 shows another exemplary embodiments of the invention.

DETAILED DESCRIPTION

(4) A method is disclosed for producing, in particular for repairing, a component (1′, 1″) having a substrate (4), in particular turbine blades made of steel or titanium, in particular made of martensitic or precipitation-hardening chromium-rich steels, with a localized deposition weld (7) or with an affixed shaped part (10), in which a precipitation-hardening nickel-based alloy is used as the localized deposition weld (7) or as the shaped part (10), in which a laser powder deposition weld or an arc deposition weld is performed.

(5) A component (1′, 1″) is disclosed, in particular produced having a substrate (4) made of steel or titanium, in particular made of martensitic or precipitation-hardening chromium-rich steels, and having only locally material of a precipitation-hardening nickel-based alloy, in which a laser powder deposition weld or an arc deposition weld is performed.

(6) Nickel-based materials, in the precipitation-hardened state after suitable heat treatment, can be very resistant to water droplet erosion and moreover are distinguished by their good weldability in comparison to the cobalt-based group of materials. An onerous primer is not required.

(7) The welding can preferably be performed using suitable methods such as laser welding or arc welding.

(8) The deposition weld can advantageously have just one layer.

(9) Another possibility is to braze in place shaped parts (inserts).

(10) Nickel-based superalloys with the precipitation hardening on the basis of γ′ are known from gas turbine engineering, in which precipitation-hardening nickel-based alloys are also again used to repair these alloys (like-for-like repair).

(11) Unexpectedly, the combination of precipitation-hardening nickel-based alloys and substrate 4 made of steel or titanium, this meaning titanium and titanium alloys as material, (FIGS. 1 and 2) achieved very good results which a person skilled in the art would on one hand not have expected and would also never have used, since substrates are always welded with identical or similar materials.

(12) The shaped part 10 (insert) which is welded or brazed in or on is then also made of a precipitation-hardening nickel-based alloy.

(13) The shaped part 10 or the deposition weld is heat-treated prior to or after connection. The insert 10 and the substrate 4 are joined by simple material bonding and then have a connection layer or brazing layer 13 (FIG. 2).

(14) When a shaped part 10 is brazed in place for the new production or repair of a component 1″, it is possible to use any desired brazing material, wherein the shaped part 10 also has a precipitation-hardening nickel-based alloy.

(15) Preferably, the method is used to produce or repair leading edges of turbine blades, in particular of steam turbines.

(16) The nickel-based alloy as a deposition weld 7 or as a shaped part 10 is preferably present only locally in or on the substrate 4 of the component 1′, 1″.

(17) Deposition welding 7 is performed in particular by laser powder deposition welding or by arc deposition welding.

(18) The precipitation-hardening nickel-based alloy preferably has the following composition:

(19) a chromium content (Cr) of 10 wt % to 21 wt %

(20) and/or

(21) a niobium content (Nb) of 0.1 wt % to 5.5 wt %

(22) and/or

(23) a molybdenum content of 0.1 wt % to 3.3 wt %,

(24) in particular IN 718.

(25) The nickel-based alloy that is used preferably has a γ′ fraction≤50%, in particular ≤40%, most particularly ≤30%.

(26) The deposition weld 7 preferably has just one layer.

(27) X.sub.20Cr.sub.13, X.sub.5CrNiCuNb.sub.16.sup.−4 or TiAl.sub.6V.sub.4 are preferably used as the material for the substrate 4.

(28) Although the present invention has been disclosed in the form of preferred embodiments and variations thereon, it will be understood that numerous additional modifications and variations could be made thereto without departing from the scope of the invention.

(29) For the sake of clarity, it is to be understood that the use of “a” or “an” throughout this application does not exclude a plurality, and “comprising” does not exclude other steps or elements.