Flexible porous metal foil and manufacturing method for flexible porous metal foil

Abstract

A flexible porous metal foil sheet made of a metal porous material which use a solid solution alloy, a metal element of a face-centered cubic structure or a metal element of a body-centered cubic structure as the matrix phase, wherein the thickness of the sheet is greater than 200 μm and less than or equal to 1500 μm, the average aperture is 0.05˜100 μm, and the porosity is 15%˜70%. The method for making the flexible porous metal foil comprises: (1) making viscous suspension or muddy paste of raw material powder that will form the metal porous material using a dispersing agent and a binding agent; (2) injecting the suspension or paste into a mold for making membrane, and drying the suspension or paste to form a homogeneous membrane; (3) pressing the membrane to improve the stacking density of the powder particles; and (4) sintering the pressed membrane to obtain the flexible porous metal foil. The flexible porous metal foil has more uniform aperture distribution, and better flatness of the foil.

Claims

1. A method of making a flexible porous metal foil characterized as a sheet having a matrix phase made of a metal porous material, wherein the metal porous material is a solid solution alloy, a face-centered cubic metal element, or a body-centered cubic metal element, wherein the thickness of the sheet is more than 200 μm and less than or equal to 1500 μm, average aperture of the sheet is 0.05˜100 μm, and porosity of the sheet is 15˜70%, the method comprising: (1) cleaning a Cu foil having purity exceeding 99% and thickness of 10 μm; (2) preparing a paste using dispersing agent, binding agent, and raw material powder that will form the metal porous material; (3) sticking the Cu foil to a surface of a mold for making a membrane; (4) injecting the paste into the mold after sticking the Cu foil to the surface of the mold and leaving the paste to dry into a homogeneous membrane; (5) pressing the homogenous membrane to improve stacking density of powder particles in the membrane, thus forming a pressed membrane; and (6) sintering the pressed membrane to obtain the flexible porous metal foil, wherein the raw material powder consists of Ni; and a mass of the Cu foil is approximately equal to a mass of the raw material powder in the paste injected into the mold.

2. The method of making a flexible porous metal foil of claim 1, wherein the dispersing agent is ethanol and the binding agent is PVB in a ratio of 4:100 (PVB:ethanol), and the paste consists of 25 g of Ni powder per 100 ml of ethanol.

3. A method of making a flexible porous metal foil characterized as a sheet having a matrix phase made of a metal porous material, wherein the metal porous material is a solid solution alloy, a face-centered cubic metal element, or a body-centered cubic metal element, wherein the thickness of the sheet is more than 200 μm and less than or equal to 1500 μm, average aperture of the sheet is 0.05˜100 μm, and porosity of the sheet is 15˜70%, the method comprising: (1) preparing a paste using dispersing agent, binding agent, and raw material powder that will form the metal porous material; (2) injecting the paste into a mold for making membrane and leaving the paste to dry into a homogeneous membrane; (3) pressing the homogenous membrane to improve stacking density of powder particles in the membrane, thus forming a pressed membrane; and (4) sintering the pressed membrane to obtain the flexible porous metal foil, and wherein the mold comprises: a mold frame for forming an edge of the flexible metal foil; a template matched to the mold frame and adjustable in a depth direction within the mold frame to set a thickness of the flexible metal foil; and a scraper to set a top surface of the paste flush with a top edge of the mold frame.

4. A method of making a flexible porous metal foil characterized as a sheet having a matrix phase made of a metal porous material, wherein the metal porous material is a solid solution alloy, a face-centered cubic metal element, or a body-centered cubic metal element, wherein the thickness of the sheet is more than 200 μm and less than or equal to 1500 μm, average aperture of the sheet is 0.05˜100 μm, and porosity of the sheet is 15˜70%, the method comprising: (1) preparing a paste using dispersing agent, binding agent, and raw material powder that will form the metal porous material; (2) injecting the paste into a mold for making membrane and leaving the paste to dry into a homogeneous membrane; (3) pressing the homogenous membrane to improve stacking density of powder particles in the membrane, thus forming a pressed membrane; and (4) sintering the pressed membrane to obtain the flexible porous metal foil, and wherein the mold comprises: an upper mold; a lower mold; a side mold; and at least three layers of clamping plates so that a plurality of pressed membranes can be sintered simultaneously.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) FIG. 1 is an appearance schematic diagram of a rectangular flexible porous metal foil in a specific embodiment of the present invention.

(2) FIG. 2 is a schematic diagram of a three-dimensional structure of a membrane making fixture for preparing the flexible porous metal foil shown in FIG. 1.

(3) FIG. 3 is a section view of FIG. 2 in the I-I direction.

(4) FIG. 4 is a structural schematic diagram of a membrane sintering fixture for preparing the flexible porous metal foil shown in FIG. 1.

(5) FIG. 5 is a section view of FIG. 4 in the II-II direction.

DETAILED DESCRIPTION OF THE INVENTION

(6) A flexible porous metal foil 100 shown in FIG. 1 is a sheet made of a metal porous material using a solid solution alloy, a face-centered cubic metal element or a body-centered cubic metal element as the matrix phase, the thickness H of the sheet is 5˜1500 μm, the average aperture is 0.05˜100 μm, and the porosity is 15˜70%. The sheet may be rectangular as shown in FIG. 1, and may also be circular, elliptical or in other plane shape.

(7) A preparation method (method 1) of the above flexible porous metal foil 100 includes the steps of: (1) preparing a viscous suspension from raw material powder constituting a metal porous material by using a dispersing agent and a binding agent; (2) injecting the suspension into a mold cavity of a membrane making fixture, and drying the suspension to form a homogeneous membrane; and (3) charging the membrane into a sintering fixture matched with the membrane in shape, then performing constrained sintering, and taking the flexible porous metal foil 100 out of the sintering fixture and obtaining the foil after sintering.

(8) In the above method, the dispersing agent may be an organic solvent which has small surface tension and is quick to volatilize and easy to dry, such as ethanol, methyl ethyl ketone, toluene, etc.; and the binding agent may be PVB (Polyvinyl Butyral), PVA (Polyvinyl Acetate), PVC (Polyvinyl Chloride), polyvinyl alcohol, polyethylene glycol (low molecular wax), paraffin, fatty acid, aliphatic amide, ester, etc.

(9) In the above method, the proportion of the raw material powder and the dispersing agent can be determined according to the specific components of the raw material powder in order to ensure the surface quality of the dried membrane. Generally, if the content of the raw material powder is too high, the surface quality of the dried membrane is poor, and the phenomena of cracking and the like easily occur; and if the content of the raw material powder is too low, the number of injecting the suspension into the mold cavity of the membrane making fixture later is increased, and the preparation cycle of the flexible porous metal foil is prolonged.

(10) In the above method, the proportion of the binding agent and the dispersing agent can be determined according to the specific components of the raw material powder in order to ensure the surface quality of the dried membrane and the strength of the membrane. Generally, if the content of the binding agent is too high, the flowability of the suspension is poor, the defects of pore shrinkage and the like are easily produced after drying, and the de-molding after sintering is difficult; and if the content of the binding agent is too low, the powder particles of the raw material powder cannot be effectively adhered, and the membrane is poor in molding property, low in strength and difficult to be taken out.

(11) In the above method, the constrained sintering means sintering on the premise that the sintering fixture keeps the shape of the membrane, thus preventing the membrane from being deformed in the sintering process. The specific sintering process shall be determined according to the specific components of the raw material powder and the achieved pore structure.

(12) As an improvement on the above method, a step can be added between step (2) and step (3), i.e., pressing the membrane to improve the stacking density of powder particles in the membrane, and then sintering is performed. Specifically, the pressing operation can be realized by adopting a roll mill, a mold press, an isostatic press or the like. The pressing can improve the stacking density of powder particles in the membrane, so that the average aperture of the final prepared flexible porous metal foil can be smaller and more uniform; and the average aperture of the flexible porous metal foil can be controlled by selecting the pressure.

(13) The membrane making fixture as shown in FIG. 2 and FIG. 3 is used in step 2 of the above method. Specifically, the membrane making fixture includes a fixing portion 210, an adjusting portion 220 and a movable portion 230, wherein the fixing portion 210 includes a mold frame 211 for forming the edge of the membrane, and the mold frame 211 is installed on a supporting base 212 for supporting the mold frame 211 (of course, the mold frame 211 may also be fixed in other manner); the adjusting portion 220 includes a template 221 matched with the mold frame 211 and used for forming the bottom of the membrane, and the template 221 is connected with adjusting devices 222 enabling the template 221 to move in the depth direction of the mold frame 211; and the movable portion 230 includes a scraper 231 positioned at the top surface of the mold frame 211 and having the cutting edge flush with the top surface of the mold frame 211 in the working process. When the flexible porous metal foil 100 is rectangular as shown in FIG. 1, the inner cavity of the mold frame 211 is also rectangular, and the template 221 is located in the inner cavity and matched with the rectangular inner cavity. In addition, each adjusting device 222 specifically can include a height adjusting mechanism 222a (e.g., a spiral lifting mechanism below each of four corners of the bottom of the template 221) which is fixed relative to the mold frame 211 and connected with one of four corners of the bottom of the template 221 and works independently. To facilitate the installation of the height adjusting mechanisms 222a, supporting structures 211a extending inwards are also arranged at the bottom of the mold frame 211, and the height adjusting mechanisms 222a are installed on the supporting structures 211a.

(14) A using method of the membrane making fixture includes: adjusting the template 221 to a set height and to parallel to the top surface of the mold frame 211 by adjusting each height adjusting mechanism 222a, then laying a PET plastic film on the molding surface of the mold frame 211 and the molding surface of the template 221 respectively, injecting the suspension obtained in step (1) into the mold cavity formed by the mold frame 211 and the template 221, next, moving the scraper 231 while ensuring its cutting edge is flush with the top surface of the mold frame 211 to scrape off the suspension on the top surface of the mold frame 211, drying the suspension to form a membrane having uniform thickness, and finally taking the membrane out of the membrane making fixture. The membrane making fixture can accurately control the thickness of the membrane, and ensures the thickness uniformity and surface flatness of the membrane.

(15) The membrane sintering fixture as shown in FIG. 4 and FIG. 5 is used in step 3 of the above method. Specifically, the membrane sintering fixture includes an upper mold 310a, a lower mold 310b and a side mold 320 made of graphite, and the upper mold 310a and the lower mold 310b are respectively matched with the side mold 320 to form the mold cavity matched with the internal membrane 100′; wherein, the side mold 320 is specifically a mask 321, the upper mold 310a and the lower mold 310b are respectively clamping plates 310, multiple layers of clamping plates 310 are installed in the mask 321, and the mold cavity is formed between any two adjacent layers of clamping plates 310; besides, a fit clearance for emitting sintered volatile matters is reserved at the fit part of each clamping plate 310 and the mask 321. When the flexible porous metal foil 100 is rectangular as shown in FIG. 1, the side of the mask 321 is of a rectangular structure formed by a front plate 321a, a rear plate 321b, a left plate 321c and a right plate 321d.

(16) A using method of the membrane sintering fixture includes: arranging an alumina coating on the inner wall of the mask 321 and two side walls of each clamping plate 310 (mixing ethanol, PVB and alumina powder to prepare a viscous alumina powder suspension, and then coating the inner wall of the mask 321 and two side walls of each clamping plate 310 with the alumina powder suspension to form the alumina coating), then laying a bottom clamping plate 310 at the bottom of the mask 321, placing a membrane 100′ on the clamping plate 310, laying a second layer of clamping plate 310 on the membrane 100′, laying all the remaining clamping plates 310 like this while ensuring a membrane 100′ is sandwiched between any two adjacent layers of clamping plates 310, feeding the assembled membrane sintering fixture into a sintering furnace for sintering, and taking the flexible porous metal foil 100 out of the membrane sintering fixture after sintering. The membrane sintering fixture realizes simultaneous constrained sintering of a plurality of membranes 100′, thus improving the production efficiency and simultaneously ensuring the sintering consistency.

(17) Another preparation method (method 2) of the above flexible porous metal foil includes the steps of: (1) preparing a carrier, wherein the carrier is a foil formed by a certain element or a few elements in a metal porous material for forming the flexible porous metal foil; (2) preparing a viscous suspension from raw material powder of the remaining elements constituting the metal porous material by using a dispersing agent and a binding agent; (3) coating the surface of the carrier with the suspension, and drying the suspension to form a membrane attached to the surface of the carrier; and (4) charging the carrier carrying the membrane into a sintering fixture matched with the carrier in shape, then performing constrained sintering, and taking the flexible porous metal foil out of the sintering fixture. As an improvement on the method, a step can also be added between step (3) and step (4), i.e., pressing the carrier carrying the membrane to improve the stacking density of powder particles in the membrane, and then sintering is performed. Specifically, the pressing operation can be realized by adopting a roll mill, a mold press, an isostatic press or the like. The pressing can improve the stacking density of powder particles in the membrane, so that the average aperture of the final prepared flexible porous metal foil can be smaller and more uniform; and the average aperture of the flexible porous metal foil can be controlled by selecting the pressure.

(18) In the above method, the dispersing agent may be an organic solvent which has small surface tension and is quick to volatilize and easy to dry, such as ethanol, methyl ethyl ketone, toluene, etc.; and the binding agent may be PVB, PVA, PVC, polyvinyl alcohol, polyethylene glycol (low molecular wax), paraffin, fatty acid, aliphatic amide, ester, etc.

(19) In the above method, the proportion of the raw material powder and the dispersing agent can be determined according to the specific components of the raw material powder in order to ensure the surface quality of the dried membrane. Generally, if the content of the raw material powder is too high, the surface quality of the dried membrane is poor, and the phenomena of cracking and the like easily occur; and if the content of the raw material powder is too low, the number of injecting the suspension into the mold cavity of the membrane making fixture later is increased, and the preparation cycle of the flexible porous metal foil is prolonged.

(20) In the above method, the proportion of the binding agent and the dispersing agent can be determined according to the specific components of the raw material powder in order to ensure the surface quality of the dried membrane and the strength of the membrane. Generally, if the content of the binding agent is too high, the flowability of the suspension is poor, the defects of pore shrinkage and the like are easily produced after drying, and the de-molding after sintering is difficult; and if the content of the binding agent is too low, the powder particles of the raw material powder cannot be effectively adhered, and the membrane is poor in molding property, low in strength and difficult to be taken out.

(21) In the above method, the constrained sintering means sintering on the premise that the sintering fixture keeps the shape of the membrane, thus preventing the membrane from being deformed in the sintering process. The specific sintering process shall be determined according to the specific components of the raw material powder and the achieved pore structure. This method still uses the membrane sintering fixture in “method 1”.

(22) The suspension can be attached to the surface of the carrier by coating or the like in step 3 of the above method, but it is suggested that the suspension is attached to the surface of the carrier by using the membrane making fixture shown in FIG. 2 and FIG. 3. The specific method includes: adjusting the template 221 to a set height and to parallel to the top surface of the mold frame 211 by adjusting each height adjusting mechanism 222a, then laying a carrier on the template 221, injecting the suspension obtained in step (2) into the mold cavity between the mold frame 211 and the carrier, next, moving the scraper 231 while ensuring its cutting edge is flush with the top surface of the mold frame 211 to scrape off the suspension on the top surface of the mold frame 211, drying the suspension to form a membrane having uniform thickness, and finally taking the carrier carrying the membrane out of the membrane making fixture.

(23) A further preparation method (method 3) of the above flexible porous metal foil includes the steps of: (1) preparing muddy paste from raw material powder constituting the metal porous material by using a dispersing agent and a binding agent; (2) pressing the paste to form a homogeneous membrane; and (3) sintering the pressed membrane to obtain the flexible porous metal foil. In this method, the dispersing agent may be an organic solvent which has small surface tension and is quick to volatilize and easy to dry, such as ethanol, methyl ethyl ketone, toluene, etc.; and the binding agent may be PVB, PVA, PVC, polyvinyl alcohol, polyethylene glycol (low molecular wax), paraffin, fatty acid, aliphatic amide, ester, etc. The steps of “method 3” are fewer than those of “method 1” and “method 2”, so the production efficiency is high, and the quality of the prepared flexible porous metal foil is very ideal. Specifically, the pressing operation can be realized by adopting a roll mill, a mold press, an isostatic press or the like. The pressing can improve the stacking density of powder particles in the membrane, so that the average aperture of the final prepared flexible porous metal foil is smaller and more uniform; and the average aperture of the flexible porous metal foil can be controlled by selecting the pressure. This method also uses the membrane sintering fixture in “method 1”.

Embodiment 1

(24) The flexible porous metal foil 100 is a rectangular sheet made of a Ni—Cu solid solution alloy porous material, the thickness H of the sheet is 10 μm, the length is 160 mm, the width is 125 mm, the average aperture is 18.4 μm, and the porosity is 58.37%. A preparation method of the flexible porous metal foil 100 includes the steps of: firstly, mixing Ni powder and Cu powder uniformly to form raw material powder, wherein the mass of the Cu powder is 30% of the mass of the raw material powder; then taking ethanol as a dispersing agent and PVB as a binding agent, adding the PVB into the ethanol in a mass ratio of 2.5:100 to form a PVB solution, adding the raw material powder into the PVB solution according to a proportion of adding 25 g of raw material powder into per 100 ml of ethanol, and dispersing the raw material powder uniformly by stirring to obtain a viscous suspension; secondly, injecting the suspension into the mold cavity of the membrane making fixture shown in FIG. 2 and FIG. 3, and drying the suspension to form a homogeneous membrane 100′; and finally, charging the membrane 100′ into the membrane sintering fixture shown in FIG. 4 and FIG. 5, performing a specific sintering process of gradually raising the sintering temperature to 550° C. and holding 90 mins (this process is mainly used for removing the binding agent, Vaseline, etc.), then directly raising the temperature to 1130° C. at the heating rate of 6° C./min and holding 180 mins (when the temperature is quickly raised to 1170° C. and exceeds the melting point of Cu, the Ni powder can be driven by using the flowability after the Cu is melted, so that the Ni powder is sufficiently combined, and the integrity and flexibility of the flexible porous metal foil 100 are ensured), and taking the flexible porous metal foil 100 out of the sintering fixture after sintering.

Embodiment 2

(25) The flexible porous metal foil 100 is a rectangular sheet made of a Ni—Cu solid solution alloy porous material, the thickness H of the sheet is 100 μm, the length is 200 mm, the width is 130 mm, the average aperture is 30 μm, and the porosity is 61.68%. A preparation method of the flexible porous metal foil 100 includes the steps of: firstly, mixing Ni powder and Cu powder uniformly to form raw material powder, wherein the mass of the Cu powder is 60% of the mass of the raw material powder; then taking ethanol as a dispersing agent and PVB as a binding agent, adding the PVB into the ethanol in a mass ratio of 4:100 to form a PVB solution, adding the raw material powder into the PVB solution according to a proportion of adding 40 g of raw material powder into per 100 ml of ethanol, and dispersing the raw material powder uniformly by stirring to obtain a viscous suspension; secondly, injecting the suspension into the mold cavity of the membrane making fixture shown in FIG. 2 and FIG. 3, and drying the suspension to form a homogeneous membrane 100′; and finally, charging the membrane 100′ into the membrane sintering fixture shown in FIG. 4 and FIG. 5, performing a specific sintering process of gradually raising the sintering temperature to 550° C. and holding 90 min, then directly raising the temperature to 1180° C. at the heating rate of 8° C./min and holding 180 min, and taking the flexible porous metal foil 100 out of the sintering fixture after sintering.

Embodiment 3

(26) The flexible porous metal foil is a rectangular sheet made of a Ni—Cu solid solution alloy porous material, the thickness H of the sheet is 60 μm, the length is 150 mm, the width is 100 mm, the average aperture is 54.1 μm, and the porosity is 40.16%. A preparation method of the flexible porous metal foil includes the steps of: firstly, performing surface treatment on a Cu foil (carrier) having the purity more than 99% and the thickness of 10 μm: cleaning impurities such as oil stains and the like on the surface of the Cu foil by adopting 10% NaOH solution, and then performing acid washing on the Cu foil in 10% H.sub.2SO.sub.4 solution for 2 mins to remove oxides and rust stains on the surface of the Cu foil; secondly, soaking the Cu foil after alkali washing and acid washing into an acetone solution, cleaning the Cu foil with ultrasonic for 8 mins, drying the Cu foil in a vacuum oven, and recording the mass of the Cu foil; thirdly, taking elemental Ni powder as a raw material, ethanol as a dispersing agent and PVB as a binding agent, adding the PVB into the ethanol in a mass ratio of 4:100 to prepare a PVB solution, then adding Ni powder into the PVB solution according to a proportion of adding 25 g of Ni powder into per 100 ml of ethanol, and dispersing the Ni powder uniformly by stirring to obtain a viscous suspension; and finally, sticking the Cu foil to the surface of the template 221 of the membrane making fixture, controlling the membrane laminating thickness by adjusting the height of the top surface of the template 221, then injecting the suspension into the mold cavity of the membrane making fixture, controlling the mass ratio of Ni to Cu to about 1:1, drying the suspension, charging the dried blank into the membrane sintering fixture shown in FIG. 4 and FIG. 5, and sintering the blank according to the same sintering process of embodiment 1.

Embodiment 4

(27) The flexible porous metal foil 100 is a rectangular sheet made of a Ni—Cu solid solution alloy porous material, the thickness H of the sheet is 10 μm, the length is 160 mm, the width is 125 mm, the average aperture is 1.2 μm, and the porosity is 42.5%. A preparation method of the flexible porous metal foil 100 includes the steps of: firstly, mixing Ni powder and Cu powder uniformly to form raw material powder, wherein the mass of the Cu powder is 30% of the mass of the raw material powder; then taking ethanol as a dispersing agent and PVB as a binding agent, adding the PVB into the ethanol in a mass ratio of 2.5:100 to form a PVB solution, adding the raw material powder into the PVB solution according to a proportion of adding 25 g of raw material powder into per 100 ml of ethanol, and dispersing the raw material powder uniformly by stirring to obtain a viscous suspension; secondly, injecting the suspension into the mold cavity of the membrane making fixture shown in FIG. 2 and FIG. 3, and drying the suspension to form a homogeneous membrane 100′; thirdly, putting the membrane 100′ onto a roll mill and rolling the membrane 100′ under 10 MPa at the rolling speed of 600 r/min (revolving speed of a roll); and finally, charging the rolled membrane 100′ into the membrane sintering fixture shown in FIG. 4 and FIG. 5, performing a specific sintering process of gradually raising the sintering temperature to 550° C. and holding 90 mins (this process is mainly used for removing the binding agent, Vaseline, etc.), then directly raising the temperature to 1130° C. at the heating rate of 6° C./min and holding 180 mins (when the temperature is quickly raised to 1170° C. and exceeds the melting point of Cu, the Ni powder can be driven by using the flowability after the Cu is melted, so that the Ni powder is sufficiently combined, and the integrity and flexibility of the flexible porous metal foil 100 are ensured), and taking the flexible porous metal foil 100 out of the sintering fixture after sintering.

Embodiment 5

(28) The flexible porous metal foil is a rectangular sheet made of a Ni—Cu solid solution alloy porous material, the thickness H of the sheet is 60 μm, the length is 150 mm, the width is 100 mm, the average aperture is 25 μm, and the porosity is 37%. A preparation method of the flexible porous metal foil includes the steps of: firstly, performing surface treatment on a Cu foil (carrier) having the purity more than 99% and the thickness of 10 μm: cleaning impurities such as oil stains and the like on the surface of the Cu foil by adopting 10% NaOH solution, and then performing acid washing on the Cu foil in 10% H.sub.2SO.sub.4 solution for 2 mins to remove oxides and rust stains on the surface of the Cu foil; secondly, soaking the Cu foil after alkali washing and acid washing into an acetone solution, cleaning the Cu foil with ultrasonic for 8 min, drying the Cu foil in a vacuum oven, and recording the mass of the Cu foil; thirdly, taking elemental Ni powder as a raw material, ethanol as a dispersing agent and PVB as a binding agent, adding the PVB into the ethanol in a mass ratio of 4:100 to prepare a PVB solution, then adding Ni powder into the PVB solution according to a proportion of adding 25 g of Ni powder into per 100 ml of ethanol, and dispersing the Ni powder uniformly by stirring to obtain a viscous suspension; and finally, sticking the Cu foil to the surface of the template 221 of the membrane making fixture, controlling the membrane laminating thickness by adjusting the height of the top surface of the template 221, then injecting the suspension into the mold cavity of the membrane making fixture, controlling the mass ratio of Ni to Cu to about 1:1, drying the suspension, putting the dried blank onto a roll mill, rolling the blank under 15 MPa at the rolling speed of 300 r/min (revolving speed of a roll), then charging the blank into the membrane sintering fixture shown in FIG. 4 and FIG. 5, and performing sintering according to the same sintering process of embodiment 1.

Embodiment 6

(29) The flexible porous metal foil 100 is a rectangular sheet made of a Ni—Cu solid solution alloy porous material, the thickness H of the sheet is 500 μm, the length is 160 mm, the width is 125 mm, the average aperture is 15.2 μm, and the porosity is 51%. A preparation method of the flexible porous metal foil 100 includes the steps of: firstly, mixing Ni powder and Cu powder uniformly to form raw material powder, wherein the mass of the Cu powder is 30% of the mass of the raw material powder; then taking ethanol as a dispersing agent and PVB as a binding agent, preparing a muddy paste according to a proportion of 30 g of PVB and 500 g of raw material powder per 100 ml of ethanol; secondly, putting the paste onto a roll mill and rolling the paste under 25 MPa at the rolling speed of 200 r/min (revolving speed of a roll); and finally, charging the rolled membrane 100′ into the membrane sintering fixture shown in FIG. 4 and FIG. 5, performing a specific sintering process of gradually raising the sintering temperature to 550° C. and holding 90 min, then directly raising the temperature to 1130° C. at the heating rate of 6° C./min and holding 180 mins (when the temperature is quickly raised to 1170° C. and exceeds the melting point of Cu, the Ni powder can be driven by using the flowability after the Cu is melted, so that the Ni powder is sufficiently combined, and the integrity and flexibility of the flexible porous metal foil 100 are ensured), and taking the flexible porous metal foil 100 out of the sintering fixture after sintering.

Embodiment 7

(30) Based on embodiment 1, the thickness H of the sheet is increased to 300 μm in embodiment 7.

Embodiment 8

(31) Based on embodiment 4, the thickness H of the sheet is increased to 500 μm in embodiment 8.

Embodiment 9

(32) Based on embodiment 5, the thickness H of the sheet is increased to 800 μm in embodiment 9.

(33) The performance comparison results of the flexible porous metal foils of embodiments 1-9 are shown as Table 1.

(34) TABLE-US-00001 TABLE 1 Performance Comparison Results of Flexible Porous Metal Foils Embodiment Embodiment Embodiment Embodiment Embodiment Embodiment Embodiment Embodiment Embodiment Item 1 2 3 4 5 6 7 8 9 Surface plane ≤0.36 μm ≤0.56 μm ≤5 μm ≤0.09 μm ≤0.15 μm ≤0.06 μm ≤9.38 ≤1.64 ≤2.24 runout of foil (flatness) Aperture X ≤ 10 μm 15% 15% 10% 7% 11% 5% 8% 6% distribution 10 μm < X < 85% 70% 50% 91%  86% 93%  87%  92%  80 μm X ≥ 80 μm  5% 15% 40% 2%  3% 2% 5% 2% Folding Folded 16 Folded 14 Folded 7 Folded 25 Folded 21 Folded 28 Folded 7 Folded 12 Folded 10 endurance times times times times times times times times times of foil