ELECTROLYTE MATERIALS FOR SOLID OXIDE ELECTROLYZER CELLS

20210359324 ยท 2021-11-18

    Inventors

    Cpc classification

    International classification

    Abstract

    A solid oxide electrolyzer electrolyte composition includes a scandia and ceria stabilized zirconia, containing 5 to 12 mol % scandia, 1 to 7 mol % ceria, and 80 to 94 mol % zirconia, or a yttria and ceria stabilized zirconia containing 3 to 10 mol % yttria, 1 to 6 mol % ceria, and 84 to 96 mol % zirconia.

    Claims

    1. A solid oxide electrolyzer electrolyte composition comprising a scandia and ceria stabilized zirconia, comprising: 5 to 12 mol % scandia; 1 to 7 mol % ceria; and 80 to 94 mol % zirconia.

    2. The electrolyte composition of claim 1, comprising: 5 to 10 mol % scandia; 1 to 5 mol % ceria; and 84 to 94 mol % zirconia.

    3. The electrolyte composition of claim 1, comprising: 5 to 10 mol % scandia; 2 to 5 mol % ceria; and 84 to 94 mol % zirconia.

    4. The electrolyte composition of claims 1, 2 or 3, further comprising 0.5 to 3 mol % ytterbia.

    5. A solid oxide electrolyzer electrolyte composition comprising a yttria and ceria stabilized zirconia comprising: 3 to 10 mol % yttria; 1 to 6 mol % ceria; and 84 to 96 mol % zirconia.

    6. The electrolyte composition of claim 5, wherein the electrolyte composition comprises: 3 mol % yttria; 1 to 5 mol % ceria; and 92 to 96 mol % zirconia.

    7. The electrolyte composition of claim 5, wherein the electrolyte composition comprises: 8 mol % yttria; 2 to 6 mol % ceria; and 86 to 90 mol % zirconia.

    8. The electrolyte composition of claim 5, wherein the electrolyte composition comprises: 10 mol % yttria; 1 to 4 mol % ceria; and 86 to 89 mol % zirconia.

    9. A solid oxide electrolyzer cell comprising: the electrolyte composition of claim 1; an air electrode; and a fuel electrode.

    10. A solid oxide electrolyzer cell comprising: the electrolyte composition of claim 2; an air electrode; and a fuel electrode.

    11. A solid oxide electrolyzer cell comprising: the electrolyte composition of claim 3; an air electrode; and a fuel electrode.

    12. A solid oxide electrolyzer cell comprising: the electrolyte composition of claim 4; an air electrode; and a fuel electrode.

    13. A solid oxide electrolyzer cell comprising: the electrolyte composition of claim 5; an air electrode; and a fuel electrode.

    14. A solid oxide electrolyzer cell comprising: the electrolyte composition of claim 6; an air electrode; and a fuel electrode.

    15. A solid oxide electrolyzer cell comprising: the electrolyte composition of claim 7; an air electrode; and a fuel electrode.

    16. A solid oxide electrolyzer cell comprising: the electrolyte composition of claim 8; an air electrode; and a fuel electrode.

    17. A solid oxide electrolyzer stack, comprising: a plurality of solid oxide electrolyzer cells of claim 9; and a plurality of interconnects separating the plurality of solid oxide electrolyzer cells.

    18. A solid oxide electrolyzer stack, comprising: a plurality of solid oxide electrolyzer cells of claim 13; and a plurality of interconnects separating the plurality of solid oxide electrolyzer cells.

    Description

    FIGURES

    [0007] FIG. 1A is a perspective view of a solid oxide electrolyzer cell (SOEC) stack, and FIG. 1B is a side cross-sectional view of a portion of the stack of FIG. 1A.

    [0008] FIG. 2 is a plot of voltage at different current for different electrolyzer cells. The figure shows cell voltage of two electrolyte compositions (A and B) operated for extended periods of time at various currents.

    DETAILED DESCRIPTION

    [0009] FIG. 1A is a perspective view of a solid oxide electrolyzer cell (SOEC) stack 20, and FIG. 1B is a side cross-sectional view of a portion of the stack 20 of FIG. 1A. Referring to FIGS. 1A and 1B, the stack 20 includes multiple electrolyzer cells 1 that are separated by interconnects 9, which may also be referred to as gas flow separator plates or bipolar plates. Each electrolyzer cell 1 includes an air electrode 3, a solid oxide electrolyte 5, and a fuel electrode 7. The stack 20 also includes internal fuel riser channels 22.

    [0010] Each interconnect 9 electrically connects adjacent electrolyzer cells 1 in the stack 20. In particular, an interconnect 9 may electrically connect the fuel electrode 7 of one electrolyzer cell 1 to the air electrode 3 of an adjacent electrolyzer cell 1. FIG. 1B shows that the lower electrolyzer cell 1 is located between two interconnects 9.

    [0011] Each interconnect 9 includes ribs 10 that at least partially define fuel channels 8 and air channels 8 on opposite sides of the interconnect The interconnect 9 may operate as a gas-fuel separator that separates a fuel, such as a water vapor, flowing to the fuel electrode 7 of one cell 1 in the stack 20 from oxidant, such as air, flowing to the air electrode 3 of an adjacent cell 1 in the stack 20. At either end of the stack 20, there may be an air end plate or fuel end plate (not shown) for providing air or fuel, respectively, to the end electrode. The end plates are electrically connected to a power source (e.g., voltage or current source) which provides electrical power to the stack 20 for the electrolysis reaction in which water provided to the fuel electrode 7 is separated into hydrogen on the fuel side and oxygen which are transported from the fuel electrode 7 to the air electrode 3 through the electrolyte 5.

    [0012] The air electrode 3 may comprise a mixture of an electrically conductive material and an electrically insulating ceramic material. The electrically conductive material may comprise a perovskite electrically conductive material, such as lanthanum strontium manganate, or a metal, such as platinum. The electrically insulating ceramic material may comprise an ionically conductive stabilized or partially stabilized zirconia (ZrO.sub.2) material, such as a rare earth stabilized (e.g., doped) zirconia, such as scandia (Sc.sub.2O.sub.3) stabilized zirconia (SSZ), yttria (Y.sub.2O.sub.3) stabilized zirconia (YSZ), and/or ytterbia (Yb.sub.2O.sub.3) stabilized zirconia (YbSZ). The fuel electrode 7 may comprise a cermet material, such as a nickel and a stabilized zirconia and/or doped ceria cermet.

    [0013] Without wishing to be bound by a particular theory, the delamination of the air electrode 3 may be caused by the precipitation of oxygen at the electrolyte/air electrode interface which can lead to high pressures resulting in air electrode delamination.

    [0014] Embodiments of the invention provide electrolyte 5 materials that help mitigate the air electrode delamination and allow SOEC to operate at higher current densities. It has been found that increasing the amount of ceria in a Scandia-Ceria doped Zirconia fluorite material helps mitigate air electrode delamination. For example, SOEC's were tested with two different electrolyte materials with one having approximately twice the amount of ceria as the other. The electrolytes were A) 88 mol % ZrO.sub.2-10 mol % Sc.sub.2O.sub.3-2 mol % CeO.sub.2, which can written as Zr.sub.0.8Sc.sub.0.182Ce.sub.0.018O.sub.2-x, and B) 88 mol % ZrO.sub.2-10 mol % Sc.sub.2O.sub.3-1 mol % CeO.sub.2-1 mol % Yb.sub.2O.sub.3, which can be written as Zr.sub.0.793Sc.sub.0.180Ce.sub.0.009Yb.sub.0.018O.sub.2-x. The SOEC stack consisted of cells numbered 1-5 with electrolyte A and cells numbered 6-10 with electrolyte B, and was operated for extended periods of time at the different currents, 1 A, 2 A, 4 A, 10 A, 15 A, and 20 A. At low currents (1-4 A), cells with both electrolyte compositions behaved well and similarly, as shown in the FIG. 2.

    [0015] However, at higher currents (10A and above), the cells with electrolyte composition B (lower ceria content) exhibited a higher voltage increase during operation, indicating higher resistance and cell over potential. The two type of cells have the same air and fuel electrodes and the only difference is the electrolyte composition. Without wishing to be bound by a particular theory, the inventor believes that the higher ceria content in the electrolyte increases the electronic conductivity in the electrolyte, which mitigates the precipitation of oxygen at the electrolyte/cathode interface.

    [0016] Based on these results, the following compositions of doped zirconia are provided for SOEC electrolyte 5 materials.

    [0017] 10 mol % scandia doped zirconia with 1 to 5 mol % CeO.sub.2 doping as shown below: [0018] 89 mol % ZrO.sub.2-10 mol % Sc.sub.2O.sub.3-1 mol % CeO.sub.2; [0019] 88 mol % ZrO.sub.2-10 mol % Sc.sub.2O.sub.3-2 mol % CeO.sub.2; [0020] 87 mol % ZrO.sub.2-10 mol % Sc.sub.2O.sub.3-3 mol % CeO.sub.2; [0021] 86 mol % ZrO.sub.2-10 mol % Sc.sub.2O.sub.3-4 mol % CeO.sub.2; [0022] 85 mol % ZrO.sub.2-10 mol % Sc.sub.2O.sub.3-5 mol % CeO.sub.2.

    [0023] 9 mol % scandia doped zirconia with 1-5 mol % CeO.sub.2 doping, as shown below: [0024] 90 mol % ZrO.sub.2-9 mol % Sc.sub.2O.sub.3-1 mol % CeO.sub.2 to 86 mol % ZrO.sub.2-9 mol % Sc.sub.2O.sub.3-5 mol % CeO.sub.2; [0025] 8 mol % Scandia doped zirconia with 1-5 mol % CeO.sub.2 doping; [0026] 7 mol % Scandia doped zirconia with 1-5 mol % CeO.sub.2 doping; [0027] 6 mol % Scandia doped zirconia with 1-5 mol % CeO.sub.2 doping; [0028] 5 mol % Scandia doped zirconia with 1-5 mol % CeO.sub.2 doping.

    [0029] Ytterbia may also be added to the scandia and ceria stabilized zirconia at 0.5 to 3 mol %, such as 0.75 to 1.5 mol %, as shown below: [0030] 10 mol % Scandia-1 mol % Yb.sub.2O.sub.3 doped zirconia with 1-5 mol % CeO.sub.2 doping; [0031] 88 mol Zr.sub.2O.sub.2-10 mol % Sc.sub.2O.sub.3-1 mol % Yb.sub.2O.sub.3-1 mol % CeO.sub.2; [0032] 87 mol Zr.sub.2O.sub.2-10 mol % Sc.sub.2O.sub.3-1 mol % Yb.sub.2O.sub.3-2 mol % CeO.sub.2; [0033] 86 mol Zr.sub.2O.sub.2-10 mol % Sc.sub.2O.sub.3-1 mol % Yb.sub.2O.sub.3-3 mol % CeO.sub.2; [0034] 85 mol Zr.sub.2O.sub.2-10 mol % Sc.sub.2O.sub.3-1 mol % Yb.sub.2O.sub.3-4 mol % CeO.sub.2; [0035] 84 mol Zr.sub.2O.sub.2-10 mol % Sc.sub.2O.sub.3-1 mol % Yb.sub.2O.sub.3-5 mol % CeO.sub.2.

    [0036] As above: 5-9 mol % Scandia doped zirconia-1 mol % Yb.sub.2O.sub.3-(1-5 mol % CeO.sub.2).

    [0037] Thus, compositions with at least 2 mol % ceria, such as 2 to 7 mol %, including 2 to 5 mol % ceria, are preferred based on FIG. 2.

    [0038] In another embodiment, the electrolyte compositions may comprise yttria and ceria stabilized zirconia. The compositions may comprise 3 to 10 mol % yttria, 1 to 6 mol % ceria, and 84 to 96 mol % zirconia.

    [0039] In one embodiment, the electrolyte composition comprises 3 mol % yttria, 1 to 5 mol % ceria, (such as 1, 2, 3, 4 or 5 mol % ceria), and 92 to 96 mol % zirconia. In another embodiment, the electrolyte composition comprises 8 mol % yttria, 2 to 6 mol % ceria, (such as 2, 3, 4, 5 or 6 mol % ceria,) and 86 to 90 mol % zirconia. In another embodiment, the electrolyte composition comprises 10 mol % yttria, 1 to 4 mol % ceria, (such as 1, 2, 3 or 4 mol % ceria), and 86 to 89 mol % zirconia.

    [0040] The yttria and ceria stabilized zirconia may be formed by mixing yttria stabilized zirconia powder and ceria powder followed by sintering the powder blends into the electrolyte composition. Alternatively, the yttria and ceria stabilized zirconia may be formed by mixing yttria powder, zirconia powder and ceria powder followed by sintering the synthesized powders into the electrolyte composition.

    [0041] 8YSZ (8 mol % yttria stabilized zirconia) and CeO.sub.2 powder blends may be formed as follows: mix (100-x) mol % 8YSZ powder with x mol % CeO.sub.2 powder, where x ranges from 2 to 6, as shown in the Table 1 below.

    TABLE-US-00001 TABLE 18 8YSZ + 2CeO.sub.2 8YSZ + 3CeO.sub.2 8YSZ + 4CeO.sub.2 8YSZ + 5CeO.sub.2 8YSZ + 6CeO.sub.2

    [0042] 8YSZ and CeO.sub.2 synthesized powders may be formed as follows: mix 8 mol % (Y.sub.2O.sub.3) with x mol % (CeO.sub.2) and (92-x) mol % (ZrO.sub.2) powders, where x ranges from 2 to 5, as shown in the Table 2 below.

    TABLE-US-00002 TABLE 2 8YSZ + 2 CeO.sub.2: synthesize 8 mol %(Y.sub.2O.sub.3) + 2 mol %(CeO.sub.2) + 90 mol %(ZrO.sub.2) 8YSZ + 3 CeO.sub.2: synthesize 8 mol %(Y.sub.2O.sub.3) + 3 mol %(CeO.sub.2) + 89 mol %(ZrO.sub.2) 8YSZ + 4 CeO.sub.2: synthesize 8 mol %(Y.sub.2O.sub.3) + 4 mol %(CeO.sub.2) + 88 mol %(ZrO.sub.2) 8YSZ + 5 CeO.sub.2: synthesize 8 mol %(Y.sub.2O.sub.3) + 5 mol %(CeO.sub.2) + 87 mol %(ZrO.sub.2)

    [0043] 3YSZ and CeO.sub.2 powder blends may be formed as follows: mix (100-x) mol % 3YSZ powder with x mol % CeO.sub.2 powder, where x ranges from 1 to 5.

    [0044] 3YSZ and CeO.sub.2 synthesized powders may be formed as follows: mix 3 mol % (Y.sub.2O.sub.3) with x mol % (CeO.sub.2) and (97-x) mol % (ZrO.sub.2) powders, where x ranges from 1 to 5.

    [0045] 10YSZ and CeO.sub.2 powder blends may be formed as follows: mix (100-x) mol % 10YSZ powder with x mol % CeO.sub.2 powder, where x ranges from 1 to 4.

    [0046] 10YSZ and CeO.sub.2 synthesized powders may be formed as follows: mix 10 mol % (Y.sub.2O.sub.3) with x mol % (CeO.sub.2) and (90-x) mol % (ZrO.sub.2) powders, where x ranges from 1 to 4.

    [0047] The preceding description of the disclosed aspects is provided to enable any person skilled in the art to make or use the present invention. Various modifications to these aspects will be readily apparent to those skilled in the art, and the generic principles defined herein may be applied to other aspects without departing from the scope of the invention. Thus, the present invention is not intended to be limited to the aspects shown herein but is to be accorded the widest scope consistent with the principles and novel features disclosed herein.