Novel Polyglycolic Acid and Preparation Method Thereof by Polycondensation

Abstract

The invention relates a novel polyglycolic acid. The polyglycolic acid comprises branched repeating units and linear repeating units. The polyglycolic acid may be produced from methyl glycolate by polycondensation in the presence of structure regulators, and exhibit excellent melt strength and thermal stability while maintaining good flowability and suitability for use in melt blow molding.

Claims

1. A polyglycolic acid comprising first repeating units of formula (I) and second repeating units of E-R.sub.2—F, wherein formula (I) is wherein: ##STR00005## R.sub.1 and R.sub.2 are each an aliphatic or aromatic group; G.sub.1, G.sub.2 . . . G.sub.i is ##STR00006## respectively; i is greater than or equal to 3; X1, X2 . . . Xi, E and F are each —NH—C(O)—, —O—, —NH— or —C(O)— except: (a) when each of X1, X2 . . . Xi is —O— or —NH—, E and F are each —NH—C(O)— or —C(O)— and (b) when each of X1, X2 . . . Xi is —NH—C(O)— or —C(O)—, E and F are each —O— or —NH—.

2. The polyglycolic acid of claim 1, wherein X.sub.1 is —O— or —NH—, X.sub.2 is —C(O)—, and E and F are each —NH—, —NH—C(O)—, —O—, or —C(O)—.

3. The polyglycolic acid of claim 1, wherein each of X.sub.1, X.sub.2 . . . X.sub.i is —O— or —NH—, and E and F are the same and are —NH—C(O)— or —C(O)—.

4. The polyglycolic acid of claim 1, wherein each of X.sub.1, X.sub.2 . . . X.sub.i is —C(O)— or —NH—C(O)—, and E and F are each —O— or —NH—.

5. The polyglycolic acid of claim 1, wherein the polyglycolic acid is prepared from methyl glycolate by polycondensation in the presence of a structure regulator.

6. The polyglycolic acid of claim 1, wherein the polyglycolic acid is prepared according to a three-stage process comprising: (a) esterifying methyl glycolate in the presence of an esterification catalyst and a structure regulator A in an esterification reactor, whereby a melted pre-esterified polymer is formed; (b) polycondensing the melted pre-esterified polymer in the presence of a polycondensation catalyst in a polycondensation reactor, whereby a polyglycolic acid based polymer is formed; and (c) optimizing the polyglycolic acid based polymer in the presence of a structure regulator B in a devolatilization reactor at 200-250° C., under an absolute pressure of not more than 1000 Pa for 10 min to 4 h, whereby the polyglycolic acid is formed.

7. The polyglycolic acid of claim 6, wherein the esterification catalyst comprises a tin salt, a zinc salt, a titanium salt, a sulfonium salt, a tin oxide, a zinc oxide, a titanium oxide, a sulfonium oxide, or a combination thereof.

8. The polyglycolic acid of claim 6, wherein the polycondensation catalyst comprises an oxide, compound or complex of a rare earth element selected from the group consisting of cerium (Ce), dysprosium (Dy), erbium (Er), europium (Eu), gadolinium (Gd), holmium (Ho), lanthanum (La), lutetium (Lu), neodymium (Nd), praseodymium (Pr), promethium (Pm), samarium (Sm), scandium (Sc), terbium (Tb), thulium (Tm), ytterbium (Yb), and yttrium (Y), or a combination thereof

9. The polyglycolic acid of claim 6, wherein the esterification catalyst is tin dichloride dihydrate and the polycondensation catalyst is a rare earth catalyst.

10. The polyglycolic acid of claim 6, wherein the structure regulator A is C1m-R1-D1n (m+n≥3), wherein the structure regulator B is C2-R2-D2, wherein C1, C2, D1 and D2 are each —OH, —COOH, —NH.sub.2, —N═C═O or —COOR5, and wherein R1, R2 and R5 are each an aliphatic or aromatic group.

11. The polyglycolic acid of claim 10, wherein m+n is in the range of 3-8, wherein C1 and D1 are each —OH, —COOH, —NH.sub.2 or —COOR5, wherein R5 is an aliphatic or aromatic group, and wherein C2 and D2 are each —OH, —COOH, —NH.sub.2, —N═C═O.

12. The polyglycolic acid of claim 10, wherein m+n is 3.

13. The polyglycolic acid of claim 6, wherein the structure regulator A is selected from the group consisting of a polyol, a polycarboxylic acid, a polyhydroxypolycarboxyl compound, a polyhydroxypolyester compound, a polyaminopolycarboxyl compound, and a polyaminopolyhydroxy compound.

14. The polyglycolic acid of claim 6, wherein the structure regulator B is a diisocyanate, a dibasic acid, a diamine or a diol.

15. The polyglycolic acid of claim 1, wherein the polyglycolic acid has a property selected from the group consisting of: (a) a melt index of 5-30 g/10 min at 230° C. and a load of 2.16 g; (b) a melt strength of 50-300 mN at 230° C. and an acceleration rate at about 1.2 cm/s.sup.2; (c) a temperature of 270° C. or higher when a weight loss rate reaches 3% after being heated starting from room temperature at a heating rate of 2° C./min under a nitrogen atmosphere; and (d) a combination thereof.

16. The polyglycolic acid of claim 15, wherein the polyglycolic acid is molded by blowing.

17. A process of preparing the polyglycolic acid of claim 1, comprising polycondensing methyl glycolate in the presence of a structure regulator.

18. A process of preparing the polyglycolic acid of claim 1, comprising (a) esterifying methyl glycolate in the presence of an esterification catalyst and a structure regulator A in an esterification reactor, whereby a melted pre-esterified polymer is formed; (b) polycondensing the melted pre-esterified polymer in the presence of a polycondensation catalyst in a polycondensation reactor, whereby a polyglycolic acid based polymer is formed; and (c) optimizing the polyglycolic acid based polymer in the presence of a structure regulator B in a devolatilization reactor at 200-250° C., under an absolute pressure of not more than 1000 Pa for 10 min to 4 h, whereby the polyglycolic acid is formed.

19. The process of claim 18, wherein the esterification catalyst comprises a tin salt, a zinc salt, a titanium salt, a sulfonium salt, a tin oxide, a zinc oxide, a titanium oxide, a sulfonium oxide, or a combination thereof.

20. The process of claim 18, wherein the polycondensation catalyst comprises an oxide, compound or complex of a rare earth element selected from the group consisting of cerium (Ce), dysprosium (Dy), erbium (Er), europium (Eu), gadolinium (Gd), holmium (Ho), lanthanum (La), lutetium (Lu), neodymium (Nd), praseodymium (Pr), promethium (Pm), samarium (Sm), scandium (Sc), terbium (Tb), thulium (Tm), ytterbium (Yb), and yttrium (Y), or a combination thereof.

21. The process of claim 18, wherein the esterification catalyst is tin dichloride dihydrate and the polycondensation catalyst is a rare earth catalyst.

22. The process of claim 18, wherein the structure regulator A is C1m-R1-D1n (m+n≥3), wherein the structure regulator B is C2-R2-D2, wherein C1, C2, D1 and D2 are each —NH.sub.2, —OH, —COOH, —N═C═O or —COOR5, and wherein R1, R2 and R5 are each an aliphatic or aromatic group.

23. The process of claim 18, wherein m+n is in the range of 3-8, wherein C1 and D1 are each —OH, —COOH—, —NH.sub.2, or —COOR5, wherein R5 is an aliphatic or aromatic group, and wherein C2 and D2 are each —OH, —NH.sub.2, —COOH or —N═C═O.

24. The process of claim 22, wherein m+n is 3.

25. The process of claim 18, wherein the structure regulator A is selected from the group consisting of a polyol, a polycarboxylic acid, a polyhydroxypolycarboxyl compound, a polyhydroxypolyester compound, a polyaminopolycarboxyl compound, and a polyaminopolyhydroxy compound.

26. The process of claim 18, wherein the structure regulator B is a diisocyanate, a dibasic acid, diamine or a diol.

Description

DETAILED DESCRIPTION OF THE INVENTION

[0026] The invention provides a polyglycolic acid (PGA) having a novel structure prepared by a polycondensation method. The invention was made based on the inventor's surprising discovery of a PGA having a novel branched structure prepared from methyl glycolate by polycondensation in the presence of a structure regulator showed excellent melt strength and thermal stability while maintaining good flowability and is suitable for use in melt blow molding.

[0027] The PGA of the invention has a branched structure, which has a large molecular volume, the branched molecules having a larger molecular volume are further connected via a linear structure, and the molecular volume is further increased. That is to say, the novel structure which is formed by chemical bonding of the branched structures via a linear structure results in a satisfactory molecular volume, which in turn exhibits excellent melt strength. The thermal decomposition temperature of the PGA increases, thereby exhibiting better thermal stability. The melt index is regarded as an index of flowability in processing of a polymer. It is not only limited by the molecular weight of the polymer, but also affected by the molecular structure of the polymer. The PGA of the present invention has shown a similar melt index and a similar flowability but better melt strength and better thermal stability than a linear PGA obtained by ring-opening polymerization of glycolide or polycondensation of methyl glycolate.

[0028] The PGA of the present invention can be used for melt blow molding. When melt blow molding under the same conditions for example, a processing temperature of about 230° C. and a mold temperature of about 10-150° C. The blow ratio was 2, and the draw ratio was 2 and the PGA of this invention produced a well molded article, which is defined as an article without collapse and damage and free of surface defects, while a linear PGA having a similar melt index was found incapable of producing a well molded article.

[0029] The terms “polyglycolic acid (PGA),” “poly(glycolic acid) (PGA)” and “polyglycolide” are used herein interchangeably and refer to a biodegradable, thermoplastic polymer composed of monomer glycolic acid. A polyglycolide may be prepared by polycondensation or ring-opening polymerization. An additive may be added to the PGA to achieve a desirable property.

[0030] The term “structure regulator” used herein refers to an agent used in making the PGA to change the structure of the resulting PGA. One or more structure regulators may be used in the same or different steps of the PGA preparation process.

[0031] A polyglycolic acid is provided. The polyglycolic acid comprises first repeating units of formula (I) and second repeating units of E-R.sub.2—F. Formula (I) is

##STR00003##

R.sub.1 and R.sub.2 are each an aliphatic or aromatic group; G.sub.1, G.sub.2 . . . G.sub.i are

##STR00004##

respectively; i is greater than 3; and X1, X2 . . . Xi, E and F are each —NH—C(O)—, —O—, —NH— or —C(O)— except:

[0032] (a) when each of X1, X2 . . . Xi is —O— or —NH—, E and F are each —NH—C(O)— or —C(O)—; and

[0033] (b) when each of X1, X2 . . . Xi is —NH—C(O)— or —C(O)—, E and F are each —O— or —NH—.

[0034] In one embodiment of the polyglycolic acid, X.sub.1 is —O— or —NH—, X.sub.2 is —C(O)—, and E and F are each —NH—, —NH—C(O)—, —O—, or —C(O)—.

[0035] In another embodiment of the polyglycolic acid, each of X.sub.1, X.sub.2 . . . X.sub.i is —O— or —NH—, and E and F are the same and are either —NH—C(O)— or —C(O)—.

[0036] In yet another embodiment of the polyglycolic acid, each of X.sub.1, X.sub.2 . . . X.sub.i is —C(O)— or —NH—C(O)—, and E and F are each —O— or —NH—.

[0037] The PGA of the present invention may be prepared from methyl glycolate by polycondensation in the presence of a structure regulator. For example, the PGA may be obtained by a three-stage reaction process: esterification reaction, polycondensation reaction, and optimization reaction.

[0038] In the first step, methyl glycolate is esterified in the presence of an esterification catalyst and a structure regulator A in an esterification reaction to form a branched esterification mixture. The esterification catalyst may be present in an amount of about 0.0001-5.0000 wt % or 0.0001-0.01 wt % of the methyl glycolate. The structure regulator A may be present in an amount no more than about 5 wt % of the methyl glycolate. The esterification reaction may carried out under esterification conditions, including a mixing speed (Rotation Speed A) of about 1-100 rpm, a gauge pressure (PaG.sub.A) of about 0-0.5 MPa, a reaction temperature (T.sub.A) of about 120-200° C., and a reaction time (t.sub.A) about 30 min to about 4 h.

[0039] In the second step, the esterification mixture is polycondensated in the presence of a polycondensation catalyst in a polycondensation reactor to form a polycondensation mixture. The polycondensation catalyst may be present in an amount of about 10.sup.−6-10.sup.−3 parts of the methyl glycolate. The polycondensation catalyst may be a rare earth catalyst. The polycondensation reaction may be carried out under polycondensation conditions, including a mixing speed (Rotation Speed B) of about 1-100 rpm, an absolute pressure (PaA.sub.B) of about 1-1000 Pa, a reaction temperature (T.sub.B) of about 190-240° C., and a reaction time (t.sub.B) of about 2-10 h.

[0040] In the third step, the polycondensation mixture is optimized in the presence of structure regulator B in a devolatilization reactor to form the PGA. The structure regulator B may be present in an amount not more than about 5 wt % of the methyl glycolate. The optimization may be carried out under optimization conditions, including a mixing speed (Rotation Speed C) of about 1-400 or 1-100 rpm, an absolute pressure (PaA.sub.C) of about 1-1000 Pa, a temperature (T.sub.C) of about 200-250° C. and a reaction time (t.sub.C) from about 10 min to about 4 h.

[0041] The PGA produced by polycondensation may be extruded from the end of the devolatilization reactor. The polymer may be cooled from the polycondensation temperature in a molten state, and pulverized into a freezing pulverizer to obtain particles having a mesh number of about 2-300 mesh for detection and processing.

[0042] The methyl glycolate may be a coal-based methyl glycolate or any commercially available methyl glycolate obtained by other methods. The methyl glycolate may be substituted by a monomer of

HO—R3-COOR4

wherein R3 and R4 are each an alkyl group, for example, methyl glycolate, ethyl glycolate, propyl glycolate, isopropyl glycolate, butyl glycolate, methyl lactate, propyl lactate, and isopropyl lactate, preferably methyl glycolate.

[0043] The use of one or more structure regulators is the key to the synthesis of a PGA having both high strength and excellent flowability. The structure regulator may be in the form of Cx-R-Dy (2≤x+y), in which C and D are each —OH, —NH.sub.2, —COOH, —COOR5, —N═C═O, or a combination thereof. R and R5 are each an aliphatic or aromatic group.

[0044] The structure regulator A may be added in the first step. The structure regulator A may be in the form of C1m-R1-D1n (35m+n). C1 and D1 are each —OH, —NH.sub.2, —COOH, —COOR5 or a combination thereof. R1 and R5 are each an aliphatic or aromatic group. The structure regulator A may be a polyhydroxypolycarboxyl compound, such as dimethylolpropionic acid, dimethylolbutanoic acid, 4,5-dihydroxy-2-(hydroxymethyl)pentanoic acid, gluconic acid, hydroxysuccinic acid, hydroxymalonic acid 2-hydroxyglutaric acid, hydroxypropionic acid, or 3-hydroxy-1,3, 5-pentanetricarboxylic acid. The structure regulator A may be a polyol such as 1, 1, 1-trimethylol ethane, 1, 1, 1-trimethylol propane, hexanetriol, butyl alcohol, glycerol, ninhydrin, cyclohexanetriol, heptanetriol, octanetriol, pentaerythritol, butyltetraol, dipentaerythritol, glycerol, xylitol, mannitol, sorbitol, cyclohexanol. The structure regulator A may be a polycarboxylic acid (e.g., propionic acid). The structure regulator A may be a polyhydroxypolyester compound, (e.g., glycerol propionate, glycerol acetate, glycerol butyrate, glycerol diacetate, and dibutyrin). The structure regulator A may be a polyaminopolycarboxyl compound (e.g., 2, 6-diaminocaproic acid, 2, 4-diaminobutyric acid, and glutamic acid). The structure regulator A may be a polyaminopolyhydroxy compound (e.g., 2,6-diamino-1-hexanol, (3R)-2-amino-1,3-butanediol, 2-amino-2-methyl-1,3-propanediol).

[0045] The structure regulator A is preferably a trifunctional compound. More preferably, the structure regulator A is 1, 1, 1-trimethylol propane, dibutyrin, dimethylolpropionic acid or hydroxymalonic acid.

[0046] The structure regulator B may be added during the third step. The structure regulator B may be in the form of C2-R2-D2. C2 and D2 are each —OH, —NH.sub.2, —COOH, —N═C═O, or a combination thereof. R2 is an aliphatic or aromatic group. The structure regulator B may be a diisocyanate, a dibasic acid, a diamine or a diol. Examples of the structure regulator B include hexamethylene diisocyanate, isophorone diisocyanate, diphenylmethane diisocyanate, xylylene diisocyanate, toluene diisocyanate, adipic acid, glutaric acid, itaconic acid, ethylene glycol, propylene glycol and octanediol, Propanediamine, butanediamine, 1, 5-pentanediamine, 2-methyl-1, 5-pentanediamine, and preferablydiisocyanate. Preferably, the structural regulator B is hexamethylene diisocyanate.

[0047] The term “about” as used herein when referring to a measurable value such as an amount, a percentage, and the like, is meant to encompass variations of ±20% or ±10%, more preferably ±5%, even more preferably ±1%, and still more preferably ±0.1% from the specified value, as such variations are appropriate.

Example 1

[0048] Polymers 1-32 and Comparative 1 were prepared and evaluated for their melt strength, melt index, thermal stability, mean square radius of gyration and blow molding.

[0049] Polymer 1 was prepared from methyl glycolate. Methyl glycolate, stannous chloride dichloride (esterification catalyst) at 0.01 wt % of the methyl glycolate, dimethylolpropionic acid (structure regulator A) at 1 wt % of the methyl glycolate were mixed in an esterification reactor at 30 rpm, 0.1 MPa (gauge pressure), 180° C. for 90 min. The materials in the esterification reactor material were transferred into a polycondensation reactor. Ce (HCO.sub.3).sub.4 (polycondensation catalyst) at 5×10.sup.−5 parts of the methyl glycolate was added into the polycondensation reactor. The polycondensation reaction was carried out at 80 rpm and 215° C. for 240 min under an absolute pressure of 100 Pa. The material in the polycondensation reactor was transferred into an optimized reactor and hexamethylene diisocyanate (structure regulator B) at 1 wt % of the methyl glycolate was added. The reaction was carried out at 225° C. for 120 min under an absolute pressure of 50 Pa. Polymers 2 and 3 were prepared in the same way as that for Polymer 1 except that structure regulator A was added at 2 wt % for Polymer 2 or 0.5 wt % for Polymer 3.

[0050] Polymer 4 was prepared from methyl glycolate. Methyl glycolate, stannous chloride dichloride (esterification catalyst) at 0.01 wt % of the methyl glycolate, hydroxymalonic acid (structure regulator A) at 1 wt % of the methyl glycolate were mixed in an esterification reactor at 30 rpm, 0.1 MPa (gauge pressure), 175° C. for 75 min. The materials in the esterification reactor material were transferred into a polycondensation reactor. Ce (HCO.sub.3).sub.4 (polycondensation catalyst) at 5×10.sup.−5 parts of the methyl glycolate was added into the polycondensation reactor. The polycondensation reaction was carried out at 80 rpm and 215° C. for 240 min under an absolute pressure of 100 Pa. The material in the polycondensation reactor was transferred into an optimized reactor and hexamethylene diisocyanate (structure regulator B) at 1 wt % of the methyl glycolate was added. The reaction was carried out at 225° C. for 120 min under an absolute pressure of 50 Pa. Polymers 5 and 6 were prepared in the same way as that for Polymer 1 except that structure regulator A was added at 0.5 wt % for Polymer 5 or 2 wt % for Polymer 6.

[0051] Polymer 7 was prepared from methyl glycolate. Methyl glycolate, stannous chloride dichloride (esterification catalyst) at 0.01 wt % of the methyl glycolate, 1, 1, 1-trimethylol propane (structure regulator A) at 1 wt % of the methyl glycolate were mixed in an esterification reactor at 30 rpm, 0.1 MPa (gauge pressure), 180° C. for 100 min. The materials in the esterification reactor material were transferred into a polycondensation reactor. Ce (HCO.sub.3).sub.4 (polycondensation catalyst) at 5×10.sup.−5 parts of the methyl glycolate was added into the polycondensation reactor. The polycondensation reaction was carried out at 80 rpm and 215° C. for 240 min under an absolute pressure of 100 Pa. The material in the polycondensation reactor was transferred into an optimized reactor and hexamethylene diisocyanate (structure regulator B) at 1 wt % of the methyl glycolate was added. The reaction was carried out at 225° C. for 120 min under an absolute pressure of 50 Pa.

[0052] Polymer 8 was prepared from methyl glycolate. Methyl glycolate, stannous chloride dichloride (esterification catalyst) at 0.01 wt % of the methyl glycolate, dibutyrin (structure regulator A) at 1 wt % of the methyl glycolate were mixed in an esterification reactor at 30 rpm, 0.1 MPa (gauge pressure), 180° C. for 100 min. The materials in the esterification reactor material were transferred into a polycondensation reactor. Ce (HCO.sub.3).sub.4 (polycondensation catalyst) at 5×10.sup.−5 parts of the methyl glycolate was added into the polycondensation reactor. The polycondensation reaction was carried out at 80 rpm and 215° C. for 240 min under an absolute pressure of 100 Pa. The material in the polycondensation reactor was transferred into an optimized reactor and hexamethylene diisocyanate (structure regulator B) at 1 wt % of the methyl glycolate was added. The reaction was carried out at 225° C. for 120 min under an absolute pressure of 50 Pa.

[0053] Polymers 9-32 were prepared in the same way as that for Example 1 except that some process parameters were changed. The parameters are shown in Table 1.

[0054] Comparative example 1 was a linear polyglycolic acid was obtained from a glycolide by ring-opening polymerization without a structure regulator.

[0055] Polymers 1-32 and Comparative 1 were evaluated in the following tests and the results are shown in Table 2.

[0056] 1. Melt Index Test

[0057] The melt index (MFR) of a sample was tested according to the following: 1) drying a test sample in a vacuum drying oven at 105° C.; 2) setting the test temperature of the melt index test instrument to 230° C. and preheating the instrument; 3) loading 4 g of the dried sample into a barrel through a funnel and inserting a plunger into the barrel to compact the dried sample into a rod; 4) keeping the dried sample in the rod for 1 min with a weight of 2.16 kg pressing on top of the rod, and then cutting a segment every 30s to obtain a total of five segments; 5) weighing the mass of each sample MFR=600 W/t (g/10 min), where W is the average mass per segment of the sample and t is the cutting time gap for each segment.

[0058] 2. Melt Strength Test

[0059] The melt strength of a sample was measured using an Italian CEAST Rheologic 5000 capillary rheometer and a “Haul-off” melt strength test module. The sample was extruded at a constant speed by a plunger and fall through a capillary outlet into a set of counter-rotating clamps with a vertical distance of 195 mm from the outlet. The pinch rolls rotated at a constant acceleration to stretch the melt strip. The tensile force increases continuously until the melt breaks. The force at this time is the “melt strength,” and is reported as mN. The test parameters: a temperature at about 230° C., and an acceleration rate at about 1.2 cm/s.sup.2.

[0060] 3. Thermal Stability

[0061] The thermal stability of a sample was measured using the NETZSCH TG 209 F3 thermogravimetric analyzer of NETZSCH ATST. 10 mg of a powder sample was used. The temperature was raised from about 25° C. at a heating rate of about 2° C./min under the conditions of a nitrogen flow rate of 10 mL/min. The temperature was measured when a 3 wt % loss was measured.

[0062] 4. Mean Square Radius of Gyration

[0063] A mean square radius of gyration was determined by using a laser light scattering instrument (helium/neon laser generator power: 22 mW) of the German ALV company CGS-5022F type to measure the mean square radius of gyration of the polymer. A polymer sample was dried to a constant weight in a vacuum oven at 50° C. Hexafluoroisopropanol (HPLC grade) was used as a solvent at 25° C. to prepare a polymer having a concentration of C.sub.0=0.001 g/g polymer/hexafluoroisopropanol solution. Four concentrations C.sub.0, 3/4C.sub.0, 1/2C.sub.0 and 1/4C.sub.0 of the polymer/hexafluoroisopropanol solution were prepared by dilution and filtering through a 0.2 μm filter. The test wavelength was 632.8 nm; the scattering angle range was 15-150 degrees; and the test temperature was 25 f 0.1° C.

[0064] 5. Blow Molding

[0065] A hollow container was prepared by molding in a blowing mold apparatus at a thermoplastic processing temperature of about 230° C. and a mold temperature of about 10-150° C. The blow ratio was 2, and the draw ratio was 2. The processing performance was evaluated according to the following criteria:

[0066] A: Very good blow molding when the sample could form a defect-free article continuously for a long period of time.

[0067] B: Blow molding can be performed, but the surface is defective or shark skin phenomenon occurs.

[0068] C: Unable to blow molding when it was impossible to blow out a complete article because it may be broken or collapsed.

TABLE-US-00001 TABLE 1 Synthesis parameters structure Rotation structure Rotation Rotation stannous structure regulator Speed structure regulator Speed Speed methyl chloride regulator A A PaG.sub.A/ T.sub.A/ t.sub.A/ Ce regulator B B/ PaA.sub.B/ T.sub.B/ t.sub.B/ C/ PaA.sub.C/ T.sub.C/ t.sub.C/ NO glycolate dichloride A dosage RPM MPa ° C. min (HCO.sub.3).sub.4 B dosage RPM Pa ° C. min RPM Pa ° C. min Polymer1 1 10.sup.−4 dimethylol 0.01 30 0.1 180 90 5*10.sup.−5 hexamethylene 0.01 80 100 215 240 180 50 225 120 propionic acid diisocyanate Polymer2 1 10.sup.−4 dimethylol 0.02 30 0.1 180 90 5*10.sup.−5 hexamethylene 0.01 80 100 215 240 180 50 225 120 propionic acid diisocyanate Polymer3 1 10.sup.−4 dimethylol 0.005 30 0.1 180 90 5*10.sup.−5 hexamethylene 0.01 80 100 215 240 180 50 225 120 propionic acid diisocyanate Polymer4 1 10.sup.−4 hydroxymalonic 0.01 30 0.1 175 75 5*10.sup.−5 hexamethylene 0.01 80 100 215 240 180 50 225 120 acid diisocyanate Polymer5 1 10.sup.−4 hydroxymalonic 0.005 30 0.1 175 75 5*10.sup.−5 hexamethylene 0.01 80 100 215 240 180 50 225 120 acid diisocyanate Polymer6 1 10.sup.−4 hydroxymalonic 0.02 30 0.1 175 75 5*10.sup.−5 hexamethylene 0.01 80 100 215 240 180 50 225 120 acid diisocyanate Polymer7 1 10.sup.−4 1,1,1- 0.01 30 0.1 180 100 5*10.sup.−5 hexamethylene 0.01 80 100 215 240 180 50 225 120 trimethylolpropane diisocyanate Polymer8 1 10.sup.−4 dibutyrin 0.0 30 0.1 180 10 5*10.sup.−5 hexamethylene 0.01 80 100 215 240 180 50 225 120 diisocyanate Polymer9 1 10.sup.−4 dimethylol 0.01 1 0.1 180 90 5*10.sup.−5 hexamethylene 0.01 80 100 215 240 180 50 225 120 propionic acid diisocyanate Polymer10 1 10.sup.−4 dimethylol 0.01 100 0.1 180 90 5*10.sup.−5 hexamethylene 0.01 80 100 215 240 180 50 225 120 propionic acid diisocyanate Polymer11 1 10.sup.−4 dimethylol 0.01 30 0 180 90 5*10.sup.−5 hexamethylene 0.01 80 100 215 240 180 50 225 120 propionic acid diisocyanate Polymer12 1 10.sup.−4 dimethylol 0.01 30 0.5 180 90 5*10.sup.−5 hexamethylene 0.01 80 100 215 240 180 50 225 120 propionic acid diisocyanate Polymer13 1 10.sup.−4 dimethylol 0.01 30 0.1 120 90 5*10.sup.−5 hexamethylene 0.01 80 100 215 240 180 50 225 120 propionic acid diisocyanate Polymer14 1 10.sup.−4 dimethylol 0.01 30 0.1 200 90 5*10.sup.−5 hexamethylene 0.01 80 100 215 240 180 50 225 120 propionic acid diisocyanate Polymer15 1 10.sup.−4 dimethylol 0.01 30 0.1 180 30 5*10.sup.−5 hexamethylene 0.01 80 100 215 240 180 50 225 120 propionic acid diisocyanate Polymer16 1 10.sup.−4 dimethylol 0.01 30 0.1 180 240 5*10.sup.−5 hexamethylene 0.01 80 100 215 240 180 50 225 120 propionic acid diisocyanate Polymer17 1 10.sup.−4 dimethylol 0.01 30 0.1 180 90 5*10.sup.−5 hexamethylene 0.01 1 100 215 240 180 50 225 120 propionic acid diisocyanate Polymer18 1 10.sup.−4 dimethylol 0.01 30 0.1 180 90 5*10.sup.−5 hexamethylene 0.01 200 100 215 240 180 50 225 120 propionic acid diisocyanate Polymer19 1 10.sup.−4 dimethylol 0.01 30 0.1 180 90 5*10.sup.−5 hexamethylene 0.01 80 1 215 240 180 50 225 120 propionic acid diisocyanate Polymer20 1 10.sup.−4 dimethylol 0.01 30 0.1 180 90 5*10.sup.−5 hexamethylene 0.01 80 1000 215 240 180 50 225 120 propionic acid diisocyanate Polymer21 1 10.sup.−4 dimethylol 0.01 30 0.1 180 90 5*10.sup.−5 hexamethylene 0.01 80 100 190 240 180 50 225 120 propionic acid diisocyanate Polymer22 1 10.sup.−4 dimethylol 0.01 30 0.1 180 90 5*10.sup.−5 hexamethylene 0.01 80 100 240 240 180 50 225 120 propionic acid diisocyanate Polymer23 1 10.sup.−4 dimethylol 0.01 30 0.1 180 90 5*10.sup.−5 hexamethylene 0.01 80 100 215 120 180 50 225 120 propionic acid diisocyanate Polymer24 1 10.sup.−4 dimethylol 0.01 30 0.1 180 90 5*10.sup.−5 hexamethylene 0.01 80 100 215 600 180 50 225 120 propionic acid diisocyanate Polymer25 1 10.sup.−4 dimethylol 0.01 30 0.1 180 90 5*10.sup.−5 hexamethylene 0.01 80 100 215 240 1 50 225 120 propionic acid diisocyanate Polymer26 1 10.sup.−4 dimethylol 0.01 30 0.1 180 90 5*10.sup.−5 hexamethylene 0.01 80 100 215 240 400 50 225 120 propionic acid diisocyanate Polymer27 1 10.sup.−4 dimethylol 0.01 30 0.1 180 90 5*10.sup.−5 hexamethylene 0.01 80 100 215 240 180 1 225 120 propionic acid diisocyanate Polymer28 1 10.sup.−4 dimethylol 0.01 30 0.1 180 90 5*10.sup.−5 hexamethylene 0.01 80 100 215 240 180 1000 225 120 propionic acid diisocyanate Polymer29 1 10.sup.−4 dimethylol 0.01 30 0.1 180 90 5*10.sup.−5 hexamethylene 0.01 80 100 215 240 180 50 200 120 propionic acid diisocyanate Polymer30 1 10.sup.−4 dimethylol 0.0 30 0.1 180 90 5*10.sup.−5 hexamethylene 0.01 80 100 215 240 180 50 250 120 propionic acid diisocyanate Polymer31 1 10.sup.−4 dimethylol 0.01 30 0.1 180 90 5*10.sup.−5 hexamethylene 0.01 80 100 215 240 180 50 225 10 propionic acid diisocyanate Polymer32 1 10.sup.−4 dimethylol 0.01 30 0.1 180 90 5*10.sup.−5 hexamethylene 0.01 80 100 215 240 180 50 225 240 propionic acid diisocyanate

TABLE-US-00002 TABLE 2 Polymer properties Mean Square Melt Thermal Radius of Strength Melt Index Stability Gyration Blow (mN) (g/10 min) (° C.) (nm) molding Polymer1 130 14 293 30 A Polymer2 70 28 284 22 C Polymer3 220 8 295 35 B Polymer4 120 15 290 27 A Polymer5 80 27 280 19 C Polymer6 200 9 298 32 B Polymer7 142 13 290 29 A Polymer8 137 17 295 29 A Polymer9 73 28 286 23 C Polymer10 135 15 289 29 A Polymer11 141 16 290 28 A Polymer12 126 17 291 26 A Polymer13 145 13 297 30 A Polymer14 138 14 293 29 A Polymer15 153 12 294 30 A Polymer16 137 14 296 29 A Polymer17 105 19 287 23 A Polymer18 102 20 285 25 A Polymer19 123 16 290 28 A Polymer20 52 30 285 20 C Polymer21 50 31 283 21 C Polymer22 80 27 281 22 C Polymer23 131 15 294 27 A Polymer24 128 16 296 29 A Polymer25 130 15 293 28 A Polymer26 146 14 289 30 A Polymer27 280 7 292 37 B Polymer28 121 16 298 28 A Polymer29 120 18 289 26 A Polymer30 115 18 293 25 A Polymer31 75 27 285 23 C Polymer32 118 18 292 26 A Comparative 1 50 15 275 20 C
As shown in Table 2, the polyglycolic acid (PGA) obtained by using a structure regulator has higher melt strength, better thermal stability and better stability than a comparative linear PGA ring-opening polymerization having a similar melt index and more fit for blow molding.

[0069] Although the invention is illustrated and described herein with reference to specific embodiments, the invention is not intended to be limited to the details shown. Rather, various modifications may be made in the details within the scope and range of equivalents of the claims without departing from the invention.