Systems and methods for implementing tailored metallic glass-based strain wave gears and strain wave gear components
11168776 · 2021-11-09
Assignee
Inventors
Cpc classification
Y10T29/49462
GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
F16H2049/003
MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
F16H49/001
MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
Y10T29/4948
GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
International classification
F16H49/00
MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
C22C45/10
CHEMISTRY; METALLURGY
Abstract
Systems and methods in accordance with embodiments of the invention implement tailored metallic glass-based strain wave gears and strain wave gear components. In one embodiment, a method of fabricating a flexspline of a strain wave gear includes: forming a MG-based composition into a flexspline using one of a thermoplastic forming technique and a casting technique; where the forming of the MG-based composition results in a formed MG-based material; where the formed flexspline is characterized by: a minimum thickness of greater than approximately 1 mm and a major diameter of less than approximately 4 inches.
Claims
1. A method of fabricating a flexspline of a strain wave gear comprising: providing a mold having a shape of a flexspline; forming a MG-based composition into the flexspline using a forming technique comprising: heating an MG-based composition to a temperature greater than the glass transition temperature of the MG-based composition, depositing the MG-based composition into the mold, conforming the MG-based composition to the shape of the mold while the temperature of the MG-based composition within the first region is greater than its respective glass transition temperature of the MG-based composition, quenching the MG-based composition sufficiently rapidly to maintain at least some amorphous structure in the MG-composition, removing the MG-based composition from the mold, and wherein the forming of the MG-based composition results in a formed flexspline comprising a MG-based material; and wherein the formed flexspline is characterized by: at least a portion having a thickness of greater than approximately 1 mm and a major diameter of less than approximately 4 inches.
2. The method of claim 1, wherein the mold is an outer mold defining the final shape of the flexspline, and wherein the MG-based composition is poured into and forcibly pressed against the mold.
3. The method of claim 1, wherein the formed MG-based material has an entirely amorphous structure.
4. The method of claim 1, wherein the formed MG-based material is a metallic glass matrix composite.
5. The method of claim 1, wherein the formed MG-based material is further characterized by the inclusion of at least one set of gear teeth.
6. The method of claim 5, wherein the gear teeth have a non-linear tooth profile.
7. The method of claim 1, wherein the MG-based composition is a MG-based composition comprising at least one material selected from the group of Cu, Ti and Zr.
8. The method of claim 1, wherein the selected MG-based composition is a composite material that includes at least one of one of V, Nb, Ta, Mo, and Sn.
9. The method of claim 1, wherein the formation of the flexspline is a net shape process.
10. The method of claim 9, wherein the flexspline comprises plurality of gear teeth formed to a near-net shape, and further comprising finishing the plurality of gear teeth to form the plurality of gear teeth into a net shape.
11. The method of claim 1, wherein the formed flexspline has a wall characterized by a maximum thickness of less than approximately 3 mm.
12. The method of claim 1, wherein the heating technique is one of: a capacitive discharge forming technique and a frictional heating technique.
13. The method of claim 1, wherein the conforming technique is one of: spin forming, blow molding, and centrifugal casting.
14. The method of claim 1, wherein the MG-composition is powderized and then fused during the heating.
15. The method of claim 1, further comprising finishing the MG-material.
16. The method of claim 1, wherein the flexspline comprises at least one groove configured to contain at least one spherical body.
17. The method of claim 1, wherein the MG-composition is initially provided as a feedstock formed as one or more sheets, wherein the sheet is at least partially amorphous and has sufficient volume to form the flexspline after forming.
18. The method of claim 17, wherein more than one sheet is used to form the flexspline, and wherein the MG-composition forming each sheet has insufficient glass forming ability to form a single sheet of sufficient thickness to form the flexspline.
19. The method of claim 18, wherein the more than one sheet collectively has sufficient thickness to form the flexspline.
20. The method of claim 18, wherein the flexspline is formed of a plurality of materials at least one of which is the MG-composition and at least one of which is a MG composite material.
Description
BRIEF DESCRIPTION OF THE DRAWINGS
(1)
(2)
(3)
(4)
(5)
(6)
(7)
(8)
(9)
(10)
(11)
(12)
(13)
(14)
(15)
(16)
(17)
(18)
(19)
(20)
(21)
(22)
(23)
(24)
DETAILED DESCRIPTION
(25) Turning now to the drawings, systems and methods for implementing tailored metallic glass-based strain wave gears and strain wave gear components are illustrated.
(26) Metallic glasses, also known as amorphous alloys (or alternatively amorphous metals), are characterized by their disordered atomic-scale structure in spite of their metallic constituent elements—i.e., whereas conventional metallic materials typically possess a highly ordered atomic structure, metallic glass materials are characterized by their disordered atomic structure. Notably, metallic glasses typically possess a number of useful material properties that can allow them to be implemented as highly effective engineering materials. For example, metallic glasses are generally much harder than conventional metals, and are generally tougher than ceramic materials. They are also relatively corrosion resistant, and, unlike conventional glass, they can have good electrical conductivity. Importantly, the manufacture of metallic glass materials lends itself to relatively easy processing. In particular, the manufacture of a metallic glass can be compatible with an injection molding process, or any similar casting process.
(27) Nonetheless, the manufacture of metallic glasses presents challenges that limit their viability as engineering materials. In particular, metallic glasses are typically formed by raising a metallic alloy above its melting temperature, and rapidly cooling the melt to solidify it in a way such that its crystallization is avoided, thereby forming the metallic glass. The first metallic glasses required extraordinary cooing rates, e.g., on the order of 10.sup.6 K/s, and were thereby limited in the thickness with which they could be formed. Indeed, because of this limitation in thickness, metallic glasses were initially limited to applications that involved coatings. Since then, however, particular alloy compositions that are more resistant to crystallization have been developed, which can thereby form metallic glasses at much lower cooling rates, and can therefore be made to be much thicker (e.g., greater than 1 mm). These thicker metallic glasses are known as ‘bulk metallic glasses’ (“BMGs”.)
(28) In addition to the development of BMGs, ‘bulk metallic glass matrix composites’ (BMGMCs) have also been developed. BMGMCs are characterized in that they possess the amorphous structure of BMGs, but they also include crystalline phases of material within the matrix of the amorphous structure. For example the crystalline phases can exist in the form of dendrites. The crystalline phases can allow the material to have enhanced ductility, compared to where the material is entirely constituted of the amorphous structure. BMGs and BMGMCs can be referred to collectively as BMG-based materials. Similarly, metallic glasses, metallic glasses that include crystalline phase inclusions, BMGs, and BMGMCs can be referred to collectively as metallic glass-based materials or MG-based materials.
(29) Even with these developments, the current state of the art has yet to fully appreciate the advantageous materials properties of MG-based materials. As a consequence, MG-based materials have seen limited use in engineering applications. For example, various publications have concluded, and it is largely established, that the viability of MG-based materials is mostly limited to microscale structures. (See e.g., G. Kumar et al., Adv. Mater. 2011, 23, 461-476, and M. Ashby et al., Scripta Materialia 54 (2006) 321-326, the disclosures of which are hereby incorporated by reference.) This is in part because the material properties, including the fracture mechanics, of MG-based materials are correlated with the specimen size. For example, it has been observed that the ductility of a MG material is inversely correlated with its thickness. (See e.g., Conner, Journal of Applied Physics, Volume 94, Number 2, Jul. 15, 2003, pgs. 904-911, the disclosure of which is hereby incorporated by reference.) Essentially, as component dimensions become greater, they become more and more prone to brittle failure. Thus, for these reasons and others, those skilled in the art have generally counseled that although MG-based materials may make for excellent materials for microscale structures, e.g. MEMS devices, they generally should not be used for macroscale components. (See e.g., G. Kumar et al., Adv. Mater. 2011, 23, 461-476.) Indeed, G. Kumar et al. have related brittle failure to the plastic zone size, and have generalized that a specimen thickness of approximately 10 times the plastic zone radius can exhibit 5% bending plasticity. (Id.) Thus, G. Kumar et al. conclude that a 1 mm thick specimen of Vitreloy can exhibit 5% bend plasticity. (Id.)
(30) While the conventional understanding has suggested limited applications for MG-based materials, it has also touted the wear-resistant aspects of MG-based materials. (see e.g., Wu, Trans. Nonferrous Met. Soc. China 22 (2012), 585-589; Wu, Intermetallics 25 (2012) 115-125; Kong, Tribal Lett (2009) 35:151-158; Zenebe, Tribol Lett (2012) 47:131-138; Chen, J. Mater. Res., Vol. 26, No. 20, Oct. 28, 2011; Liu, Tribol Lett (2012) 46:131-138; the disclosures of which are hereby incorporated by reference.) To be clear, “wear” conventionally refers to the displacement of the surface of a material as a direct result of its mechanical interaction with another material. It is generally understood that a material's resistance to wear generally increases with its hardness, i.e. the harder a material is, the less susceptible it is to wear. (See e.g., I. L. Singer, Wear, Volume 195, Issues 1-2, July 1996, Pages 7-20.) Based on these understandings, it has been suggested that the predicted wear-resistance characteristics of MGs may make them excellent candidates for materials from which to fabricate miniature gears, given that gears are subject to extensive mechanical interaction and are thereby subject to wear. (See e.g., Chen, J. Mater. Res., Vol. 26, No. 20, Oct. 28, 2011; Huang, Intermetallics 19 (2011) 1385-1389; Liu, Tribol Lett (2009) 33:205-210; Zhang, Materials Science and Engineering A, 475 (2008) 124-127; Ishida, Materials Science and Engineering A, 449-451 (2007) 149-154; the disclosures of which are hereby incorporated by reference.) Thus, in accordance with the above-described insights, gears on a microscale have been fabricated (See e.g., Ishida, Materials Science and Engineering A, 449-451 (2007) 149-154, the disclosure of which is hereby incorporated by reference.)
(31) However, contrary to the above-described conventional wisdom, Hofmann et al. have demonstrated that MG-based materials can be beneficially implemented in a variety of other applications. For example, U.S. patent application Ser. No. 13/928,109 to Hofmann et al. describes how MG-based materials can be developed for the fabrication of gears on a macroscale. In particular, U.S. patent application Ser. No. 13/928,109 explains that while Ishida demonstrated the fabrication of MG-based gears, the demonstration was limited inasmuch as the fabricated gears were of smaller dimensions (and thereby weren't subjected to the same modes of failure as macroscopic engineering component) and the gears operated using lubricant, which can mitigate tendencies for brittle fracture. (Id.) Generally, Hofmann et al. explain that the prior art has been principally concerned with harnessing the wear resistance properties of MG-based materials, and consequently focused on implementing the hardest MG-based materials. (Id.) This design methodology is limiting insofar as the hardest materials are more prone to other modes of failure. (Id.) Indeed, Hofmann et al. demonstrate that implementing the hardest MG-based materials in the fabrication of macroscale gears generally yields gears that fracture during operation. (Id.) Accordingly, Hofmann et al. disclose that MG-based materials can be developed to have favorable properties with respect to fracture toughness, and thereby can be made to fabricate macroscale gears that do not necessarily require lubricant to function. (Id.) The disclosure of U.S. patent application Ser. No. 13/928,109 is hereby incorporated by reference in its entirety, especially as it pertains to metallic glass-based materials, and their implementation in macroscale gears. Moreover, U.S. patent application Ser. No. 13/942,932 to Hofmann et al. discloses that MG-based materials possess other favorable materials properties that can also allow them to be used in the fabrication of macroscale compliant mechanisms. The disclosure of U.S. patent application Ser. No. 13/942,932 is hereby incorporated by reference in its entirety, especially as it pertains to metallic glass-based materials, and their implementation in macroscale compliant mechanisms.
(32) The potential of metallic glass-based materials continues to be explored, and developments continue to emerge. For example, in U.S. patent application Ser. No. 14/060,478, D. Hofmann et al. disclose techniques for depositing layers of metallic glass-based materials to form objects. The disclosure of U.S. patent application Ser. No. 14/060,478 is hereby incorporated by reference especially as it pertains to metallic glass-based materials, and techniques for depositing them to form objects. Furthermore, in U.S. patent application Ser. No. 14/163,936, D. Hofmann et al., disclose techniques for additively manufacturing objects so that they include metallic glass-based materials. The disclosure of U.S. patent application Ser. No. 14/163,936 is hereby incorporated by reference in its entirety, especially as it pertains to metallic glass-based materials, and additive manufacturing techniques for manufacturing objects so that they include metallic glass-based materials. Additionally, in U.S. patent application Ser. No. 14/177,608, D. Hofmann et al. disclose techniques for fabricating strain wave gears using metallic glass-based materials. The disclosure of U.S. patent application Ser. No. 14/177,608 is hereby incorporated by reference in its entirety, especially as it pertains to metallic glass-based materials, and their implementation in strain wave gears. Moreover, in U.S. patent application Ser. No. 14/178,098, D. Hofmann et al., disclose selectively developing equilibrium inclusions within an object constituted from a metallic glass-based material. The disclosure of U.S. patent application Ser. No. 14/178,098 is hereby incorporated by reference, especially as it pertains to metallic glass-based materials, and the tailored development of equilibrium inclusions within them. Furthermore, in U.S. patent application Ser. No. 14/252,585, D. Hofmann et al. disclose techniques for shaping sheet materials that include metallic glass-based materials. The disclosure of U.S. patent application Ser. No. 14/252,585 is hereby incorporated by reference in its entirety, especially as it pertains to metallic glass-based materials and techniques for shaping sheet materials that include metallic glass-based materials. Additionally, in U.S. patent application Ser. No. 14/259,608, D. Hofmann et al. disclose techniques for fabricating structures including metallic glass-based materials using ultrasonic welding. The disclosure of U.S. patent application Ser. No. 14/259,608 is hereby incorporated by reference in its entirety, especially as it pertains to metallic glass-based materials and techniques for fabricating structures including metallic glass-based materials using ultrasonic welding. Moreover, in U.S. patent application Ser. No. 14/491,618, D. Hofmann et al. disclose techniques for fabricating structures including metallic glass-based materials using low pressure casting. The disclosure of U.S. patent application Ser. No. 14/491,618 is hereby incorporated by reference in its entirety, especially as it pertains to metallic glass-based materials and techniques for fabricating structures including metallic glass-based materials using low pressure casting. Furthermore, in U.S. patent application Ser. No. 14/660,730, Hofmann et al. disclose metallic glass-based fiber metal laminates. The disclosure of U.S. patent application Ser. No. 14/660,730 is hereby incorporated by reference in its entirety, especially as it pertains to metallic glass-based fiber metal laminates. Additionally, in U.S. patent application Ser. No. 14/971,848, Kennett et al. disclose fabricating gearbox housings from metallic glass-based materials. The disclosure of U.S. patent application Ser. No. 14/971,848 is hereby incorporated by reference in its entirety, especially as it pertains to fabricating gearbox housings from metallic glass-based materials and also as it pertains to casting metallic glass-based materials around a solid body to form useful objects.
(33) Notwithstanding all of these developments, the vast potential of metallic glass-based materials has yet to be fully appreciated. The instant application discloses how MG-based materials can be implemented in the creation of highly customized and/or robust strain wave gears and strain wave gear components. Note that MG-based materials can be developed so that they have high fatigue resistance, high fracture toughness, excellent sliding friction properties, a low density, and a high elasticity. Moreover, these and other characteristics can be largely tunable, e.g. by alloying a given MG-based material or else applying some other processing (e.g. heat treating) to a MG-based material. This versatility can enable the implementation of highly customized and efficacious strain wave gears and/or strain wave gearing components; e.g. they can be made to sustain greater operating loads, be lighter, and/or have longer life cycles. Notably, the characteristics that MG-based materials can offer can give rise to unique design considerations that can enable the implementation of more robust configurations relative to those seen in conventional strain wave gears. The general operation of strain wave gears is now discussed in detail below.
(34) Strain Wave Gear Operation
(35) In many embodiments of the invention, strain wave gears and strain wave gear components are provided that incorporate MG-based materials and thereby have improved performance characteristics. To provide context, the basic operating principles of strain wave gears are now reviewed.
(36)
(37)
(38) Of course, it should be understood that while an example of a strain wave gear design is illustrated and discussed above, any suitable strain wave gear design and any suitable strain wave gear components can be fabricated from MG-based materials in accordance with embodiments of the invention. For example, the flexspline can take any suitable shape, and is not required to be ‘cup-shaped.’ Similarly, any type of bearing can be implemented—not just a ball bearing. For example, needle roller bearings may be implemented. To be clear, the instant application is not meant to be limited to any particular strain wave gear design or strain wave gear component design. It is now discussed how MG-based materials can be implemented within strain wave gear components to enhance the performance of strain wave gears in accordance with embodiments of the invention.
(39) Metallic Glass-Based Strain Wave Gears and Strain Wave Gear Components
(40) In many embodiments of the invention, MG-based materials are incorporated within strain wave gears and/or strain wave gear components. In many instances, MG-based materials can be developed to possess desired materials properties that can make them very-well suited for the fabrication of the constituent components of a strain wave gear. For example, from the above-described strain wave gear operating principles, it is evident that the ball bearing and the flexspline deflect in a periodic fashion with the rotation of the wave generator plug. As a result, it would be desirable that those components be fabricated from materials that have high fatigue strength. For example,
(41) Generally, the fatigue limit of a material is defined by the number of times that the material can be stressed at a particular level before the material permanently deforms. Assuming the same cyclic load is applied many times, the lower the load, the longer the materials will last before it deforms. The cyclic load at which a material can survive 10.sup.7 cycles is generally referred to as the fatigue limit of the material. If the material is cyclically loaded at its yield strength, it would presumably fail in one cycle. Thus, fatigue limits are generally reported as a percentage of their yield strength (to normalize their performance). As an illustration, a 300M steel has a fatigue limit which is 20% of its yield strength. If one assumes a fixed geometry of a part being fatigued, as with a flexspline, incorporating a more flexible material results in a lower stress per cycle, which can result in a much longer fatigue life.
(42) Accordingly, MG-based materials can be favorably incorporated within a flexspline of a strain wave gear to provide enhanced fatigue performance. For example, MG-based materials can have an elastic limit as high as 2%, and can also have a stiffness about 3 times lower than steel-based materials. Typically, many MG-based materials can demonstrate elastic limits that are greater than approximately 1%, and it is these MG-based materials that can be particularly well-suited for implementation within strain wave gear components. Many MG-based materials can demonstrate elastic limits that are greater than approximately 1.5%. By contrast, 304 stainless steel has been reported to have an elastic limit of 0.1%. Generally, this implies that a flexspline fabricated from a MG-based material can experience lower stress per unit of deformation relative to a steel-based flexspline having an identical geometry (e.g. as measured by a respective material's yield strength). Correspondingly, the MG-based material can have much more favorable fatigue properties, e.g. a material that is subjected to less relative stress tends to be capable of withstanding more loading cycles. Importantly, whereas MG-based materials are often considered to be brittle and susceptible to fatigue failure by other measures, they can demonstrate great fatigue resistance when the applied stresses that they are subjected to are relatively less.
(43) Note also that the differing stiffness values impact the geometries of the fabricated components. Thus, because MG-based materials can have relatively lower stiffness values (e.g. relative to steel), they can allow for strain wave gear components that have more favorable geometries. For example, a relatively lower stiffness can enable the implementation of a thicker flexspline, which can be advantageous. Indeed, the materials properties profile of MG-based materials generally can enable the development of more favorable geometries—i.e. in addition to stiffness, the other materials properties of MG-based materials can also contribute to the development of advantageous geometries.
(44) Moreover, as is understood from the prior art, MG-based materials can have higher hardness values, and correspondingly demonstrate improved wear performance relative to heritage engineering materials. Materials with high hardness values can be particularly advantageous in strain wave gears, as the constituent components of strain wave gears are in continuous contact with one another and are subject to, for example, sliding friction. Generally, when gear teeth are subjected to a constant load and accompanying friction, the resulting associated elastic deformation and wear can precipitate ‘ratcheting’. That MG-based materials can have a high hardness value, good resistance to wear (including a good resistance to galling), and high elasticity—even when subjected to high loads—can make them well-suited to be implemented within a strain wave gear. For example, the implementation of MG-based materials within the gear teeth of a strain wave gear can deter ratcheting. Furthermore, MG-based materials can be made to have a high hardness value throughout a broad temperature range. For example, MG-based materials can have a hardness value that does not vary as a function of temperature by more than 20% within the temperature range of 100K to 300K. Indeed, MG-based materials can have a strength that does not vary as a function of temperature by more than 20% within a temperature range of 100K to 300K. In general, the implementation of MG-based materials within strain wave gears can be favorable on many levels. Table 1 below illustrates how the materials properties of certain MG-based materials possess improved materials properties relative to heritage engineering materials in many respects.
(45) TABLE-US-00001 TABLE 1 Material Properties of MG-Based Materials relative to Heritage Engineering Materials Density Stiffness, E Tensile Yield Tensile UTS Elastic Limit Specific Hardness Material (g/cc) (GPa) (MPa) (MPa) (%) Strength (HRC) SS 15500 H1024 7.8 200 1140 1170 <1 146 36 Ti—6Al—4V STA 4.4 114 965 1035 <1 219 41 Ti—6Al—6V—4Sn STA 4.5 112 1035 1100 <1 230 42 Nitronic 60 CW 7.6 179 1241 1379 <1 163 40 Vascomax C300 8.0 190 1897 1966 <1 237 50 Zr-BMG 6.1 97 1737 1737 >1.8 285 60 Ti-BMGMC 5.2 94 1362 1429 >1.4 262 51 Zr-BMGMC 5.8 75 1096 1210 >1.4 189 48
(46) Importantly, materials properties of MG-based materials are a function of the relative ratios of the constituent components and are also a function of the crystalline structure. As a result, the materials properties of a MG-based material can be tailored by varying the composition and varying the ratio of crystalline structure to amorphous structure. For example, in many embodiments it may be desirable to implement MG-based materials having a particular materials profile within a particular component of a strain wave gear. In these instances, an appropriate MG-based material may be developed and/or selected from which to fabricate a respective strain wave gear component. Tables 2, 3, and 4 depict how materials properties of MG-based materials can vary based on composition and crystalline structure.
(47) TABLE-US-00002 TABLE 2 Material Properties of Select MG-Based Materials as a function of Composition BMG bcc ρ σ.sub.y σ.sub.max ε.sub.y E T.sub.s name atomic % weight % (%) (%) (g/cm.sup.2) (g/cm.sup.3) (MPa) (%) (GPa) (K) DV2 Ti.sub.44Zr.sub.20V.sub.12Cu.sub.5Be.sub.19 Ti.sub.41.9Zr.sub.36.3V.sub.12.1Cu.sub.6.3Be.sub.3.4 70 30 5.13 1597 1614 2.1 94.5 956 DV1 Ti.sub.48Zr.sub.20V.sub.12Cu.sub.5Be.sub.15 Ti.sub.44.3Zr.sub.35.2V.sub.11.8Cu.sub.6.1Be.sub.2.6 53 47 5.15 1362 1429 2.3 94.2 955 DV3 Ti.sub.56Zr.sub.18V.sub.10Cu.sub.4Be.sub.12 Ti.sub.51.6Zr.sub.31.6V.sub.9.8Cu.sub.4.9Be.sub.2.1 46 54 5.08 1308 1309 2.2 84.0 951 DV4 Ti.sub.62Zr.sub.15V.sub.10Cu.sub.4Be.sub.9 Ti.sub.57.3Zr.sub.26.4V.sub.9.8Cu.sub.4.9Be.sub.1.6 40 60 5.03 1086 1089 2.1 83.7 940 DVAI1 Ti.sub.60Zr.sub.16V.sub.9Cu.sub.3Al.sub.3Be.sub.9 Ti.sub.55.8Zr.sub.28.4V.sub.8.9Cu.sub.3.7Al.sub.1.6Be.sub.1.6 31 69 4.97 1166 1189 2.0 84.2 901 DVAI2 Ti.sub.67Zr.sub.11V.sub.10Cu.sub.5Al.sub.2Be.sub.5 Ti.sub.62.4Zr.sub.19.5V.sub.9.9Cu.sub.6.2Al.sub.1Be.sub.0.9 20 80 4.97 990 1000 2.0 78.7 998 Ti-6-4a Ti.sub.86.1Al.sub.10.3V.sub.3.6 Ti.sub.90Al.sub.6V.sub.4(Grade 5 Annealed) na na 4.43 754 882 1.0 113.8 1877 Ti-6-4s Ti.sub.86.1Al.sub.10.3V.sub.3.6[Ref] Ti.sub.90Al.sub.6V.sub.4(Grade 5 STA) na na 4.43 1100 1170 ~1 114.0 1877 CP-Ti Ti.sub.100 Ti.sub.100 (Grade 2) na na 4.51 380 409 0.7 105.0 ~1930
(48) TABLE-US-00003 TABLE 3 Material Properties of Select MG-Based Materials as a function of Composition σ.sub.max ε.sub.tot σ.sub.y ε.sub.y E ρ G CIT RoA Alloy (MPa) (%) (MPa) (%) (GPa) (g/cm.sup.3) (GPa) (J) (%) ν Zr.sub.36.6Ti.sub.31.4Nb.sub.7Cu.sub.5.9Be.sub.19.1 (DH1) 1512 9.58 1474 1.98 84.3 5.6 30.7 26 44 0.371 Zr.sub.38.3Ti.sub.32.9Nb.sub.7.3Cu.sub.6.2Be.sub.15.3 (DH2) 1411 10.8 1367 1.92 79.2 5.7 28.8 40 50 0.373 Zr.sub.39.6Ti.sub.33.9Nb.sub.7.6Cu.sub.6.4Be.sub.12.6 (DH3) 1210 13.10 1096 1.62 75.3 5.8 27.3 45 46 0.376 Zr.sub.41.2Ti.sub.13.8Cu.sub.12.5Ni.sub.10Be.sub.22.5 (Vitreloy 1) 1737 1.98 — — 97.2 6.1 35.9 8 0 0.355 Zr.sub.56.2Ti.sub.13.8Nb.sub.5.0Cu.sub.6.9Ni.sub.5.6Be.sub.12.5 (LM 2) 1302 5.49 1046 1.48 78.8 6.2 28.6 24 22 0.375
(49) TABLE-US-00004 TABLE 4 Material Properties as a Function of Composition and Structure, where A is Amorphous, X, is Crystalline, and C is Composite A/X/C 2.0 Hv E (GPa) (CuZr42Al7Be10)Nb3 A 626.5 108.5 (CuZr46Al5Y2)Nb3 A 407.4 76.9 (CuZrAl7Be5)Nb3 A 544.4 97.8 (CuZrAl7Be7)Nb3 A 523.9 102.3 Cu40Zr40Al10Be10 A 604.3 114.2 Cu41Zr40Al7Be7Co5 C 589.9 103.5 Cu42Zr41Al7Be7Co3 A 532.4 101.3 Cu47,5Zr48Al4Co0.5 X 381.9 79.6 Cu47Zr45Al5Y2 A 409.8 75.3 CuSOZrB0 X 325.9 81.3 CuZr41AlBe7Cr3 A 575.1 106.5 CuZrAl5Be5Y2 A 511.1 88.5 CuZrAl5Ni3Be4 A 504.3 95.5 CuZrAl7 X 510.5 101.4 CuZrAl7Ag7 C 496.1 90.6 CuZrAl7Ni5 X 570.0 99.2 Ni40Zr28.5Ti16.5Be15 C 715.2 128.4 Ni40Zr8.5Ti16.5Cu5Al10 X 627.2 99.3 Ni40Zr28.5Ti16.5Cu5Be10 C 668.2 112.0 Ni56Zr17Ti13Si2Sn3Be9 X 562.5 141.1 Ni57Zr18Ti14Si2Sn3Be6 X 637.3 139.4 Ti33.18Zr30.51Ni5.33Be22.88Cu8.1 A 486.1 96.9 Ti40Zr25Be30Cr5 A 465.4 97.5 Ti40Zr25Ni8Cu9Be18 A 544.4 101.1 Ti45Zr16Ni9Cu10Be20 A 523.1 104.2 Vit 1 A 530.4 95.2 Vit105 (Zr52.5Ti5Cu17.9Ni14.6Al10) A 474.4 88.5 Vit 106 A 439.7 83.3 Zr55Cu30Al10NiS A 520.8 87.2 Zr65Cu17.5Al7.5Ni10 A 463.3 116.9 DH1 C 391.1 84.7 GHDT (Ti30Zr35Cu8.28Be26.8) A 461.8 90.5
(50)
(51) Tables 5 and 6 below list reported data as to how fatigue characteristics with MG-based materials vary as a function of composition.
(52) TABLE-US-00005 TABLE 5 Fatigue Characteristics as a Function of Composition Fracture Fatigue Strength Geometry Loading Frequency R- limit Fatigue Material (MPa) (mm) mode (Hz) ratio (MPa) ratio Zr.sub.56.2Cu.sub.6.9Ni.sub.5.6Ti.sub.13.8Nb.sub.5.0Be.sub.12.5 1480 3 × 3 × 30 4PB 25 0.1 −296 0.200 Composites Zr.sub.41.2Cu.sub.12.5Ni.sub.10Ti.sub.13.8Nb.sub.5.0Be.sub.22.5 1900 3 × 3 × 50 4PB 25 0.1 −152 0.080 Zr.sub.41.2Cu.sub.12.5Ni.sub.10Ti.sub.13.8Nb.sub.5.0Be.sub.22.5 1900 2 × 2 × 60 3PB 10 0.1 768 0.404 Zr.sub.41.2Cu.sub.12.5Ni.sub.10Ti.sub.13.8Nb.sub.5.0Be.sub.22.5 1900 2 × 2 × 60 3PB 10 0.1 359 0.189 Zr.sub.44Ti.sub.11Ni.sub.10Cu.sub.10Be.sub.25 1900 2.3 × 2.0 × 85 4PB 5-20 0.3 550 0.289 Zr.sub.44T.sub.11Ni.sub.10Cu.sub.10Be.sub.25 1900 2.3 × 2.0 × 85 4PB 5-20 0.3 390 0.205 Zr.sub.52.5Cu.sub.17.9Al.sub.10Ni.sub.14.6Ti.sub.5 1700 3.5 × 3.5 × 30 4PB 10 0.1 850 0.500 (Zr.sub.58Ni.sub.13.6Cu.sub.18Al.sub.10.4).sub.99Nb.sub.1 1700 2 × 2 × 25 4PB 10 0.1 559 0.329 Zr.sub.55Cu.sub.30Ni.sub.5Al.sub.10 1560 2 × 20 × 50 Plate 40 0.1 410 0.263 bend
(53) TABLE-US-00006 TABLE 6 Fatigue Characteristics as a Function of Composition Fracture Fatigue Strength Geometry Loading Frequency R- limit Fatigue Material (MPa) (mm) mode (Hz) ratio (MPa) ratio Zr.sub.56.2Cu.sub.6.9Ni.sub.5.6Ti.sub.13.8Nb.sub.5.0Be.sub.12.5 1480 Ø2.98 TT 10 0.1 239 0.161 Composites Zr.sub.55Cu.sub.30Ni.sub.5Al.sub.10 Nano 1700 2 × 4 × 70 TT 10 0.1 −340 0.200 Zr.sub.41.2Cu.sub.12.5Ni.sub.10Ti.sub.13.8Nb.sub.5.0Be.sub.22.5 1850 Ø2.98 TT 10 0.1 703 0.380 Zr.sub.41.2Cu.sub.12.5Ni.sub.10Ti.sub.13.8Nb.sub.5.0Be.sub.22.5 1850 Ø2.98 TT 10 0.1 615 0.332 Zr.sub.41.2Cu.sub.12.5Ni.sub.10Ti.sub.13.8Nb.sub.5.0Be.sub.22.5 1850 Ø2.98 TT 10 0.1 567 0.306 Zr.sub.41.2Cu.sub.12.5Ni.sub.10Ti.sub.13.8Nb.sub.5.0Be.sub.22.5 1900 — CC 5 0.1 −1050 0.553 Zr.sub.41.2Cu.sub.12.5Ni.sub.10Ti.sub.13.8Nb.sub.5.0Be.sub.22.5 1900 — TC 5 −1 −150 0.079 Zr.sub.50Cu.sub.40Al.sub.10 1821 Ø2.98 TT 10 0.1 752 0.413 Zr.sub.50Cu.sub.30Al.sub.10Ni.sub.10 1900 Ø2.98 TT 10 0.1 865 0.455 Zr.sub.50Cu.sub.37Al.sub.10Pd.sub.3 1899 Ø2.98 TT 10 0.1 983 0.518 Zr.sub.50Cu.sub.37Al.sub.10Pd.sub.3 1899 Ø5.33 TT 10 0.1 −900 0.474 Zr.sub.52.5Cu.sub.17.9Al.sub.10Ni.sub.14.6Ti.sub.5 1660 6 × 3 × 1.5 TT 1 0.1 — — Zr.sub.52.5Cu.sub.17.9Al.sub.10Ni.sub.14.6Ti.sub.5 1700 Ø2.98 TT 10 0.1 907 0.534 Zr.sub.59Cu.sub.20Al.sub.10Ni.sub.8Ti.sub.3 1580 6 × 3 × 1.5 TT 1 0.1 — — Zr.sub.65Cu.sub.15Al.sub.10Ni.sub.10 1300 3 × 4 × 16 TT 20 0.1 −280 0.215 Zr.sub.65Cu.sub.30Al.sub.10Ni.sub.5 1560 1 × 2 × 5 TT 0.13 0.5 — —
(54) Although the data in tables 5 and 6 has been reported, one of the inventors of the instant application conducted independent fatigue tests, which to some extent contradict the reported values.
(55) In particular,
(56) Similarly,
(57) In general,
(58) From the above, it is clear that MG-based materials can possess advantageous materials properties that can make them very well-suited for implementation within strain wave gear components. Any of the listed MG-based materials can be implemented within strain wave gear components in accordance with certain embodiments of the invention. More generally, MG-based materials can be tailored (e.g. via alloying and/or heat treating) to obtain a material having the desired materials profile for implementation within a strain wave gear in accordance with embodiments of the invention. Generally, a desired material property profile can be determined for a respective strain wave gear component, and a MG-based material conforming to the material property profile can be developed and implemented.
(59) For example, in many embodiments where a less stiff material is desired, the relative ratios of B, Si, Al, Cr, Co, and/or Fe within a MG-based composition is reduced. Similarly, in many embodiments where a less stiff material is desired, the volume fraction of soft, ductile dendrites is increased; or alternatively, the amount of beta stabilizing elements, e.g. V, Nb, Ta, Mo, and/or Sn, are increased. Generally, in metallic glass matrix composites, the stiffness of a material changes in accordance with the rule of mixtures, e.g., where there are relatively more dendrites, the stiffness decreases, and where there are relatively less dendrites, the stiffness increases. Note that, generally speaking, when modifying the stiffness of MG-based materials, the stiffness is modified largely without overly influencing other properties, e.g. elastic strain limit or the processability of the MG-based material. The ability to tune the stiffness independent of other material properties or influencing processability is greatly advantageous in designing strain wave gears and strain wave gear components.
(60) Moreover, just as the stiffness of MG-based materials can be tuned, the resistance to fatigue failure can also be tuned in accordance with embodiments of the invention. The alloying elements used to improve resistance to fatigue failure are largely experimentally determined. However, it has been observed that the same processing techniques that are used to enhance fracture toughness also tend to beneficially influence resistance to fatigue failure. More generally, any of a variety of materials characteristics can be altered by appropriately alloying base materials. For instance, the hardness, toughness, fatigue life, corrosion resistance, etc., can be modified by appropriate alloying. In many instances, these characteristics can be independently tuned. This can enable great customizability for parts to be fabricated.
(61) In any case, as should be clear from the above, any of the above-listed and described MG-based materials can be incorporated within strain wave gears and strain wave gear components in accordance with embodiments of the invention. More generally, any MG-based material can be implemented within strain wave gears and strain wave gear components in accordance with embodiments of the invention. For example, in many embodiments the implemented MG-based material is based in Fe, Zr, Ti, Ni, Hf, or Cu (i.e. those respective elements are present in the material in greater amounts than any other element). In some embodiments, a MG-based material that is implemented within a strain wave gear component is a Cu—Zr—Al—X composition, where X can be one or more element, including for example: Y, Be, Ag, Co, Fe, Cr, C, Si, B, Mo, Ta, Ti, V, Nb, Ni, P, Zn, and Pd. In several embodiments, a MG-based material that is implemented within a strain wave gear component is a Ni—Zr—Ti—X composition, where X can be one or more element, including for example Co, Al, Cu, B, P, Si, Be, and Fe. In a number of embodiments, a MG-based material that is implemented within a strain wave gear component is a Zr—Ti—Be—X composition, where X can be one or more element, including for example Y, Be, Ag, Co, Fe, Cr, C, Si, B, Mo, Ta, Ti, V, Nb, Ni, P, Zn, and Pd. In some embodiments, a strain wave gear component includes a MG-based material that is Ni.sub.40Zr.sub.28.5Ti.sub.16.5Al.sub.10Cu.sub.5 (atomic percent). In several embodiments a strain wave gear component includes a MG-based material that is (Cu.sub.50Zr.sub.50).sub.xAl.sub.1-12Be.sub.1-20Co.sub.0.5-5. In many embodiments, a desired materials profile is determined for a given strain wave gear component, and a MG-based material that possess the desired characteristics is used to construct the strain wave gear component. As MG-based materials can possess many advantageous traits, their implementation within strain wave gear components can result in much more robust strain wave gears. The design methodology and fabrication of MG-based strain wave gears is now discussed in greater detail below.
(62) Fabrication of Metallic Glass-Based Strain Wave Gears and Strain Wave Gear Components
(63) In many embodiments of the invention, strain wave gear components are fabricated from MG-based materials using casting or thermoplastic forming techniques. Using casting or thermoplastic forming techniques can greatly enhance the efficiency by which strain wave gears and strain wave gear components are fabricated. For example, steel-based strain wave gear components are typically machined; because of the intricacy of the constituent components, the machining costs can be fairly expensive. By contrast, using casting or thermoplastic forming techniques in the development of strain wave gear components can circumvent excessive costly machining processes.
(64) A method of fabricating a strain wave gear component that incorporates casting or thermoplastic forming techniques is illustrated in
(65) Note that any constituent component of a strain wave gear can be fabricated in accordance with embodiments of the invention. As alluded to above, because the flexspline and the ball bearing are subject to periodic deformation, it may be particularly advantageous that they be formed from a material having a high resistance to fatigue failure. Moreover, flexsplines and ball bearings may also benefit from being formed from a material that possesses excellent resistance to wear, since those components experience constant contact and relative motion during the normal operation of a strain wave gear (the gear teeth of the flexspline are subject to wear and the balls and inner and outer races of the ball bearing may experience wear). In some embodiments the balls of the ball bearing are fabricated from MG-based materials—in this way, the balls of the ball bearing can benefit from the enhanced wear resistance that MG-based materials can offer.
(66) But it should be clear that any of the components of a strain wave gear can be fabricated from MG-based materials in accordance with embodiments of the invention. In some embodiments, the gear teeth of the circular spline are fabricated from MG-based materials. In this way, the gear teeth of the circular spline can benefit from the enhanced wear-performance characteristics that MG-based materials can offer. In some embodiments, the gear teeth of the circular spline that are fabricated from a MG-based material are thereafter press-fit into a different, stiffer material—for example beryllium and titanium—to form the circular spline, bearing in mind that it would be beneficial for the circular spline to be relatively rigid to support the motion of the flexspline and the wave generator. In this way, MG-based materials are implemented in the gear teeth of the circular spline where they can offer enhanced wear performance, and a stiffer material can form the remainder of the circular spline where it can offer enhanced structural support.
(67) In many embodiments, the majority of the constituent components of a strain wave gear are fabricated from the same MG-based materials—in this way, the respective strain wave gear can have a more uniform coefficient of thermal expansion. In any case, it should be clear that any of the constituent components of a strain wave gear can be fabricated from a MG-based material in accordance with embodiments of the invention.
(68) Returning to
(69) The selected 620 MG-based material is formed into the desired shape (e.g. the shape of the component to be fabricated), for example thermoplastically or using a casting technique. While the fabrication of gear-type components from MG-based materials via casting and/or thermoplastic techniques is not currently widespread, the inventors of the instant application have demonstrated the viability of such techniques for this purpose. For example,
(70) As an example,
(71)
(72) As mentioned above, the heating of the MG-based material so that it is capable of thermoplastic forming can be achieved in any suitable way in accordance with embodiments of the invention. For example,
(73) Note that although the above descriptions regard mechanically conforming MG-based material to mold, MG-based material can be formed into a mold in any suitable way in accordance with embodiments of the invention. In many embodiments, the MG-based material is made to conform to the mold using one of: a forging technique, a vacuum-based technique, a squeezing technique, and a magnetic forming technique. Of course, the MG-based material can be made to conform to a mold in any suitable fashion in accordance with embodiments of the invention.
(74)
(75)
(76)
(77) In general, it should be clear that any suitable technique for thermoplastically forming or casting the MG-based material can be implemented in accordance with embodiments of the invention. The above-described examples are meant to be illustrative and not comprehensive. Even more generally, any suitable technique for forming a strain wave gear component that constitutes a MG-based material can be implemented in accordance with embodiments of the invention.
(78) Referring back to
(79)
(80) Note that the formation techniques are extremely sensitive to process control. In general, it is beneficial to have precise control over the fluid flow, venting, temperature, and cooling when forming the part. For example,
(81)
(82) It should be understood that although
(83) The above-described fabrication techniques can be used to efficiently fabricate strain wave gears and strain wave gear components. For example, as alluded to above, expenses associated with machining the components can be avoided using these techniques. Accordingly, the cost for fabricating a given strain wave gear component becomes principally a function of the cost of the raw material, and this can be the case irrespective of the size of the component. By contrast, when steel-based strain wave gear components are formed, the cost of manufacturing the part may increase with a reduction in size beyond some critical value. This is because it becomes difficult to machine parts of a smaller size.
(84) By way of example,
(85) Customized Manufacturing Processes for the Fabrication of Tailored Metallic Glass-Based Materials
(86) As can be appreciated from the above discussion, the implementation of MG-based materials into strain wave gears and strain wave gearing components can confer a host of advantages. For example, as already alluded to above, the implementation of metallic glass-based materials can result in the creation of more robust strain wave gears and strain wave gearing components. Moreover, as also alluded to above, metallic glass-based materials are amenable to casting and other thermoplastic manufacturing strategies, which can be much more efficient manufacturing techniques relative to conventional techniques typically employed in constructing conventional steel-based strain wave gears (e.g. machining). In many embodiments of the invention, the information discussed above is used to implement unique manufacturing strategies to produce highly customized strain wave gears. For example, MG-based materials can be made to possess unique materials property profiles, and these materials profiles can influence design considerations.
(87) For instance, in many embodiments, robust metallic glass-based strain wave gears having a relatively smaller dimension—e.g. having flexsplines characterized by a major diameter of less than approximately 4 inches—are implemented using MG-based materials. In a number of embodiments, robust metallic glass-based strain wave gears having flexsplines characterized by a major diameter of less than approximately 2 inches are implemented using MG-based materials. Conventionally, the manufacture of strain wave gears from steel at such small dimensions can be challenging. In particular, in order for steel to be made to achieve the requisite level of flexibility for suitable flexspline operation at such small dimensions, it generally has to be made in the form of a relatively thin walled structure. However, because the flexspline has to be made to conform to this thin shape, it can be undesirably fragile. By contrast, metallic glass-based materials can be relatively much thicker and still possess the requisite level of flexibility. This is because metallic glass-based materials can be made to be much less stiff than steel-based materials. Accordingly, the thicker flexsplines made from metallic glass-based materials can be much more durable. Moreover, it can be much easier to cast thicker metallic glass-based as opposed to thinner metallic glass-based materials.
(88)
(89) Subsequent to forming processes, as before, any post-forming operations can be performed 2140. In many instances, the formed 2130 flexsplines are “net shape” and do not require any appreciable post-forming processing. In a number of embodiments, the formed 2130 flexsplines are ‘near net shape’ and require minimal post-forming processing to finish the part. For instance, surface finishes can be implemented. Any suitable post-forming processing can be implemented in accordance with embodiments of the invention, including any of the processes mentioned previously with respect to
(90)
(91) As an example,
(92) While
(93) Notably, the ability to rely on casting and thermoplastic manufacturing techniques can greatly enhance the customizability of the manufacture of strain wave gears. For example, strain wave gearing components can be more readily cast in non-traditional shapes. Thus for example, in many embodiments of the invention, flexsplines and/or circular splines are cast so that they include “S-shaped” teeth. Conventional gear teeth geometries can result in excessive and unwanted contact known as backlash between intermeshing teeth. By contrast, gear teeth characterized by S-shaped geometries can allow for minimized backlash and therefore smoother operation.
(94) While the above-discussion has regarded the implementation of MG-based materials by utilizing them as the bulk material within respective strain wave gear components, in many embodiments, MG-based materials are coated onto strain wave gears fabricated from more conventional materials (e.g. steel and/or plastics). In this way, the wear-resistant properties of any of a variety of MG-based materials can be harnessed.
(95) As can be seen, the described manufacturing methods can enable the implementation of highly customized strain wave gears. They can be made to possess any of a variety of intrinsic materials properties based on the implemented metallic glass-based materials. And they can also readily be made to conform to unconventional, but advantageous, geometries. This level of customization is generally not feasible with conventional steel manufacturing methodologies.
(96) As can be inferred from the above discussion, the above-mentioned concepts can be implemented in a variety of arrangements in accordance with embodiments of the invention. For example, in some embodiments, strain wave gear components are cast from polymeric materials, and subsequently coated with bulk metallic glass-based materials. In this way, the wear resistant properties of bulk metallic glass-based materials can be harnessed. Accordingly, although the present invention has been described in certain specific aspects, many additional modifications and variations would be apparent to those skilled in the art. It is therefore to be understood that the present invention may be practiced otherwise than specifically described. Thus, embodiments of the present invention should be considered in all respects as illustrative and not restrictive.