Method of resistance spot welding of galvanized high-strength steel with good joint performance

Abstract

A resistance spot welding method of galvanized high-strength steel with good joint performance, in which three welding pulses are used within one spot welding schedule. The method includes applying a first welding pulse and a second welding pulse which are used for generating a nugget and suppressing the generation of liquid metal embrittlement (LME) cracks, respectively. The first welding pulse generates a nugget having a diameter of 3.75T.sup.1/2-4.25T.sup.1/2 in which T represents a plate thickness. The second welding pulse causes the nugget to grow at a rate less than a rate of growth during the first welding pulse. A third welding pulse, which is a tempering pulse, is applied for improving plasticity of a welding spot.

Claims

1. A resistance spot welding method of galvanized high-strength steel, characterized by that: three welding pulses are used within one spot welding schedule; a first welding pulse and a second welding puke are used for generating a nugget and suppressing the generation of liquid metal embrittlement (LME) cracks, wherein the first welding pulse has a first current amperage magnitude and a pulse duration time t1 that generates a nugget having a diameter of 3.75T.sup.1/2-4.25T.sup.1/2 in which T represents a plate thickness; the second welding pulse has a second current amperage magnitude and a pulse duration time t2 that causes the nugget to grow at a rate less than a rate of growth during the first welding pulse; and a third welding pulse has a third current amperage magnitude and a pulse duration time t3 which is a tempering pulse used for improving plasticity of a welding spot, wherein the second current amperage magnitude of the second welding pulse is greater than the first and third current amperage magnitudes of the respective first and third welding pulses and the pulse duration time t2 less than the pulse duration time t1.

2. The resistance spot welding method of galvanized high-strength steel according to claim 1, wherein the time t1 of the first welding pulse is set and a welding current I1 of the first welding pulse is obtained through tests, and the welding current I1 of the first welding pulse is a welding current upon generating the nugget having the diameter of 3.75T.sup.1/2-4.25T.sup.1/2; and a welding current I2 and the time t2 of the second welding pulse, and a welding current I3 and the time t3 of the third welding pulse are calculated by the welding current I1 and the time t1 of the first welding pulse.

3. The resistance spot welding method of galvanized high-strength steel according to claim 2, wherein for the plate thickness 0.9-1.2 mm, the time t1 of the first welding pulse is set as 8-12 cyc, wherein cyc represents a time unit, 1 cyc-0.02 seconds, and the welding current I1 of the first welding pulse is obtained through tests; or the plate thickness 1.3-1.6 mm, the time t1 of the first welding pulse is set as 0-15 cyc, and the welding current I1 of the first welding pulse is obtained through tests; for the plate thickness 1.7-2.0 mm, the time t1 of the first welding pulse is set as 12-18 cyc, and the welding current I1 of the first welding pulse is obtained through tests; correspondingly: for the plate thickness 0.9-1.2 mm, the time of the second welding pulse is set as t2=t¼; the time of the third welding pulse is set as t3=(t¼)+1; for the plate thickness 1.3-1.6 mm, the time of the second welding pulse is set as t2=(2t⅕)−2; the time of the third welding pulse is set as t3=(t⅕)+2; for the plate thickness 1.7-2.0 mm, the time of the second welding pulse is set as t2=t⅓; the time of the third welding pulse is set as t3=(t⅓)+1; according to the plate thickness, correspondingly, a specific, method of calculating I2 and I3 by I1 is as follows: a specific setting method of the current I2 of the second welding pulse is as follows: a lower limit of I2: I2 min=(1.3−0.05t2)I1, an upper limit of I2: I2 max=(2.2−0.1t 2)I1; a specific setting method of the current I3 of the third welding pulse current I3 is as follows: a lower limit of I3: I3 min=⅔I1, an upper limit of I3: I3 max=I1; an interval time between the first welding pulse and the second welding, pulse is C1 which is a first cooling time, an interval time between the second welding pulse and the third welding pulse is C2 which is a second cooling time, a holding time (HT) is a time after the third welding pulse, and for steel plates with different thicknesses, values of C1, C2 and HT are respectively set as follows: plate thickness 0.9-1.2 mm, C1=1 cyc, C2=8 cyc, HT=5 cyc; plate thickness 1.3-1.6 mm, C1=1 cyc, C2=10 cyc, HT=5 cyc; plate thickness 1.7-2.0 mm, C1=1 cyc, C2=12 cyc, HT=5 cyc.

4. The resistance spot welding method of galvanized high-strength steel according to claim 1, wherein the pulse duration time t2 is less than the pulse duration time t3.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) FIG. 1 is a schematic view of process parameters for suppressing LME cracks during spot welding of TWIP steel galvanized plates in the Document;

(2) FIG. 2 is a schematic view of a resistance spot welding method of galvanized high-strength steel with good joint performance according to the present invention;

(3) FIG. 3 is a schematic view of a section of resistance spot welding of galvanized high-strength steel;

(4) FIG. 4 is a schematic view of the relationship between a plate thickness and a welding pressure;

(5) FIG. 5 is a metallograph of a typical spot welding section with a process No. 1 (conventional spot welding process) in an embodiment;

(6) FIG. 6 is a metallograph of a typical spot welding section of a process No. 3 (the spot welding method of the present invention) in an embodiment.

DETAILED DESCRIPTION OF THE EMBODIMENTS

(7) The present invention will be further described below in conjunction with the accompanying drawings and a specific embodiment.

(8) The present invention discloses a resistance spot welding method of galvanized steel plates with a tensile strength no less than 590 Mpa. By the method, the plasticity of welding spot can be improved, and the probability of button pullout failure of the welding spots during broken testing can be increased while the generation of liquid metal embrittlement (LME) cracks during the spot welding of high-strength steel galvanized plates are suppressed.

(9) As shown in FIG. 2, in a resistance spot welding method of galvanized high-strength steel with good joint performance, three welding pulses are used within one spot welding schedule; a first welding pulse and a second welding pulse are used for generating a nugget and suppressing the generation of LME cracks, wherein the first welding pulse generates a nugget having a diameter of 3.75T.sup.1/2-4.25T.sup.1/2, and T represents a plate thickness; the second welding pulse causes the nugget to grow slowly; and a third welding pulse is a tempering pulse, which is used for improving the plasticity of a welding spot.

(10) A time t1 of the first welding pulse is set, and the welding current I1 of the first welding pulse is obtained through tests, and the welding current I1 of the first welding pulse is a welding current upon generating the nugget having the diameter of 3.75T.sup.1/2-4.25T.sup.1/2 (T=plate thickness). A welding current I2 and a time t2 of the second welding pulse and a welding current I3 and a time t3 of the third welding pulse are calculated by the welding current I1 and the time t1 of the first welding pulse.

(11) In the present invention, the welding current I2 and the time t2 of the second welding pulse and the welding current I3 and the time t3 of the third welding pulse can be conveniently calculated by the welding current I1 and the time t1 of the first welding pulse obtained through a few tests, so that the spot welding process, which can not only suppress the LME cracks during the spot welding of the high-strength steel galvanized plates, but also can improve the plasticity of the welding spot, is implemented.

(12) The working principle of the resistance spot welding method of galvanized high-strength steel with good joint performance of the present invention is as follows:

(13) A stress and a suitable temperature range (the range of the galvanized high-strength steel is 700° C. to 950° C.) are two necessary conditions for the generation of the LME cracks. The galvanized high-strength steel has the above two conditions in a spot welding process, and thus generates the LME cracks.

(14) The design idea of the present invention is to avoid the occurrence of the LME cracks by reducing the stress level of a spot welding LME crack sensitive region X, as shown in FIG. 3. The specific principle is as follows: with the increase of heat input during the spot welding, a diameter D and a height h of the nugget Y increase continuously. Since the high-strength steel, especially ultra-high-strength steel, has the addition of more alloy elements to a base material, it has high electrical resistivity, the heat generation speed during the spot welding is high, and the nugget grows at a high speed. The height h of the nugget grows too fast, so that the thickness T′ of the unmelted base material in a plate thickness direction is rapidly decreased, and the size of the thickness T′ of the unmelted base material directly affects the cross-sectional area under a load. Therefore, the smaller the thickness T′ of the unmelted base material is, the greater the stress is.

(15) In the present invention, the nugget having the diameter of 3.75T.sup.1/2-4.25T.sup.1/2 (T=the plate thickness) is generated by the first welding pulse. At this time, the nugget is relatively small, the thickness T′ of the unmelted base material is relatively large, and no LME crack of spot welding is generated. Then, the second welding pulse with a short time t2 is applied to slowly grow the nugget, thus reducing the decrease speed of the thickness T′ of the unmelted base material so as to reduce the stress level of the LME crack sensitive region and avoid the occurrence of the LME cracks.

(16) The improvement of the plasticity of the welding spot and the increased probability of button pullout failure of the welding spot during the broken testing are achieved by the third welding pulse. The pulse is the tempering pulse, which can effectively reduce the cooling speed of the region of the nugget and reduce the generation of a hardened structure of the joint, thereby improving the plasticity of the joint.

(17) Test Implementing Steps:

(18) 1 Basic parameter settings:

(19) 1.1 An electrode having andomed surface with 06 mm (plate thickness ≤1.4 mm) or ϕ8 mm (plate thickness >1.4 mm) is used.

(20) 1.2 The welding pressure is set within an enclosed region as shown in FIG. 4 according to the plate thickness. A specific method of setting a value of the welding pressure is as follows: the lower limit of the welding pressure Fmin=3.182T+0.0364 kN (wherein T represents the plate thickness, its unit is mm, and the range of T is 0.9 mm-2.0 mm); the upper limit of the welding pressure Fmax=4.091T-0.182 kN (wherein T represents the plate thickness, its unit is mm, and the range of T is 0.9 mm-2.0 mm).

(21) 1.3 Flow rate of cooling water: 2 L/min-4 L/min.

(22) 1.4 The time of C1, C2 and HT (holding time) in FIG. 2 is set according to Table 1. The interval time between the first welding pulse and the second welding pulse is C1, that is, a first cooling time C1, the interval time between the second welding pulse and the third welding pulse is C2, that is, a second cooling time C2, the holding time HT is a time after the third welding pulse, and their values for steel plates with different thicknesses are respectively set as follows:

(23) TABLE-US-00001 TABLE 1 Plate thickness/mm C1 C2 HT 0.9-1.2 1 cyc  8 cyc 5 cyc 1.3-1.6 10 cyc 1.7-2.0 12 cyc Wherein: cyc represents the time unit, which is a cycle, 1 cyc = 0.02 seconds;

(24) Wherein: cyc represents the time unit, which is a cycle, 1 cyc=0.02 seconds;

(25) 2 Setting of the first welding pulse:

(26) 2.1 The time t1 of the first welding pulse is set according to the plate thickness, and a specific setting method is as follows:

(27) Plate thickness 0.9-1.2 mm: t1: 8-12 cyc;

(28) Plate thickness 1.3-1.6 mm: t1: 10-15 cyc;

(29) Plate thickness 1.7-2.0 mm: t1: 12-18 cyc.

(30) 2.2 The welding current I1 of the first welding pulse is set. A nugget having a diameter of 3.75T.sup.1/2-4.25T.sup.1/2 (T=plate thickness) is generated. The setting steps of the welding current I1 of the first welding pulse are as follows:

(31) 2.2.1 The electrode, the pressure, the flow rate of cooling water and the HT are set according to “1 basic parameter setting”. C1 and C2 are set as 0.

(32) 2.2.2 t1 is set according to the method of “2.1”.

(33) 2.2.3 Starting from 4 kA, the welding current I1 of the first pulse is sequentially set with 400 A as a step length, and two spot welding samples are welded under each current.

(34) 2.2.4 The spot welding samples in 2.2.3 are destroyed by using a peeling method.

(35) 2.2.5 The diameter of the nugget of the welding spot of each spot welding sample that is destroyed in step 2.2.4 is measured by using a vernier caliper.

(36) 2.2.6 The diameters of the nuggets of the two welding spots under the same welding current is averaged, and the corresponding current when the averaged value is closest to the 3.75T.sup.1/2-4.25T.sup.1/2 (T=plate thickness) is the “welding current I1 of the first pulse”.

(37) 3 Setting of the time t2 of the second welding pulse and the time t3 of the third welding pulse:

(38) 3.1 The electrode, the pressure, the flow rate of cooling water, C1, C2 and HT are set according to “1 basic parameter setting”.

(39) 3.2 The t2 and t3 are set according to the plate thickness through the t1, and a specific method is as follows:

(40) Plate thickness 0.9-1.2 mm: t1: 8-12 cyc;

(41) $t2=\frac{t1}{4};t3=\frac{t1}{4}+1.$

(42) Plate thickness 1.3-1.6 mm: t1: 10-15 cyc;

(43) $t2=\frac{2t1}{5}-2;t3=\frac{t1}{5}+2.$

(44) Plate thickness 1.7-2.0 mm: t1: 12-18 cyc;

(45) $t2=\frac{t1}{3};t3=\frac{t1}{3}+1.$
4 Setting of the welding current I2 of the second welding pulse and the welding current I3 of the third welding pulse:

(46) 4.1 The welding current I2 of the second welding pulse is set according to the welding current I1 of the first welding pulse. The diameter of the nugget is caused to grow slowly, and it is ensured that no welding spatter occurs. A setting method of the welding current I2 of the second welding pulse is as follows:

(47) Lower limit of I2: I2 min=(1.3−0.05t2)I1, wherein t2 is the time of the second welding pulse (unit: cyc);

(48) Upper limit of I2: I2 max=(2.2−0.1t2)I1, wherein t2 is the time of the second welding pulse (unit: cyc).

(49) 4.2 The welding current I3 of the third welding pulse is set according to the welding current I1 of the first welding pulse. Slow cooling processing is performed on the welding spot to reduce the generation of the hardened structure of the nugget and to improve the plasticity of the welding spot. A setting method of the welding current I3 of the third welding pulse is as follows:

(50) Lower limit of I3: I3 min=⅔ I1

(51) Upper limit of I3: I3 max=I1.

Embodiment

(52) Spot welding is performed on 1.6 mm hot-dipped high-strength steel (the mechanical property and compositions are shown in table 2) by using three spot welding schedules No. 1, No. 2 and No. 3. The LME crack generations and the fracture modes of the welding spot during the broken testing are compared and evaluated. The characteristics and test results of the three spot welding schedules are shown in the Table 3.

(53) TABLE-US-00002 TABLE 2 Compositions and mechanical property of galvanized high-strength steel Mechanical property Plate Yield Tensile Elongation Chemical composition % thickness strength strength at fracture C Si Mn P S 1.6 715 1020 20% 0.2 1.5 1.8 0.01 0.002 mm Mpa Mpa

(54) TABLE-US-00003 TABLE 3 Characteristics and results of Spot welding processes No. 1, No. 2 and No. 3 Process serial number Process characteristics Test result No. 1 Conventional spot welding The welding spot generates process severe LME cracks No. 2 The third welding pulse is zero, The ratio of interfacial and the remaining processes are fracture at welding spot set according to the spot welding during the broken testing is method of the present invention high No. 3 The spot welding method No spot welding LME crack according to the present is generated, and the ratio invention is adopted of interfacial fracture at the welding spot during the broken testing is greatly reduced

(55) The detailed results are as follows:

(56) 1. Results by the Spot Welding Process No. 1:

(57) The spot welding process No. 1 is specifically as shown in Table 4:

(58) TABLE-US-00004 TABLE 4 Spot welding process No. 1 Diameter of end First Second Flow rate Plate surface of Welding First pulse cooling Second pulse cooling Third pulse Holding of cooling thickness electrode pressure Time Current time Time Current time Time Current time water 1.6 mm 6 mm 3.6 KN 6 cyc I.sub.1 1 cyc 6 cyc I.sub.2 1 cyc 6 cyc I.sub.3 5 cyc 2 L/min Note: I.sub.1 = 1.sub.2 = 1.sub.3 in the table

(59) Through the metallographic, severe liquid metal embrittlement (LME) cracks are found in the entire welded region. FIG. 5 is a typical metallograph thereof.

(60) 2. Results by the Spot Welding Process No. 2:

(61) The spot welding process No. 2 is as follows:

(62) TABLE-US-00005 TABLE 5 Spot welding process No. 2 Diameter of end First Second Flow rate Plate surface of Welding First pulse cooling Second pulse cooling Third pulse Holding of cooling thickness electrode pressure Time Current time Time Current time Time Current time water 1.6 mm 8 mm 5.5 kN 15 cyc 8.0 kA 1 cyc 4 cyc 8.8-14.4 kA 0 0 0 5 cyc 2 L/min

(63) By this welding method, during the broken testing, the fracture mode of the welding spot is mainly interfacial fracture. Although the tensile-shear strength (TSS) and cross tensile strength (CTS) of the welding spot meet the requirements, the welding spot after the TSS test is almost entirely with interfacial fracture, and the ratio of interfacial fracture after the CTS test is also less than 50%.

(64) 3. Results by the Spot Welding Process No. 3:

(65) The spot welding process No. 3 is as follows:

(66) TABLE-US-00006 TABLE 6 Spot welding process No. 3 Diameter of end First Second Flow rate Plate surface of Welding First pulse cooling Second pulse cooling Third pulse Holding of cooling thickness electrode pressure Time Current time Time Current time Time Current time water 1.6 mm 8 mm 5.5 kN 15 cyc 8.0 kA 1 cyc 4 cyc 8.8-14.4 kA 10 cyc 5 cyc 5.3 kA 5 cyc 2 L/min

(67) By this method, the liquid metal embrittlement (LME) crack is not found in the entire welded region through the metallographic. The typical metallograph thereof is as shown in FIG. 6.

(68) At the same time, by this process, the tensile-shear strength (TSS) and cross tensile strength (CTS) of the welding spot meet the requirements, the fracture mode detected after the CTS test is all button pullout failure, and the ratio of button pullout failure at the welding spot detected after the TSS detection is also above 70%, which is much better than the result when the slow cooling pulse is not applied.

(69) The above descriptions are only preferred embodiments of the present invention, and are not intended to limit the protection scope of the present invention. Therefore, any modifications, equivalents, improvements and the like made within the spirit and principle of the present invention should be encompassed within the protection scope of the present invention.