METHOD FOR MANUFACTURING A TURBOMACHINE COMPOSITE PART

Abstract

Methods for manufacturing a turbomachine composite part, such as a fan blade, are provided. The composite part has a fibrous structure with a three-dimensional fibrous preform coated with a surface fibrous web, and which is embedded in a polymer matrix The methods include: forming the surface web in a cavity of a mold in order to shape it, wetting and forming the preform on the surface web in order to shape it, and closing the mold, drying the fibrous structure, and injecting thermosetting resin into the mold in order to form said polymer matrix. The surface web is wetted before and/or during the forming thereof.

Claims

1. A method for manufacturing a turbomachine composite part comprising a fibrous structure which comprises a three-dimensional fibrous preform coated with at least one surface fibrous web, and which is embedded in a thermosetting resin-based matrix, the method comprising: shaping a surface fibrous web in a cavity of a mold, wherein the surface fibrous web has been wetted; wetting and forming a three-dimensional fibrous preform directly on the surface fibrous web in the cavity of the mold, thereby forming a fibrous structure comprising the surface fibrous web and the three-dimensional fibrous preform; and closing the mold, drying the fibrous structure, and injecting a thermosetting resin into the mold, thereby forming a thermosetting resin-based matrix.

2. The method according to claim 1, wherein the surface fibrous web is wetted and oven-dried before its shaping.

3. The method according to claim 2, wherein the surface fibrous web is coated with a handling fabric, covered with a vacuum bag, and then subjected to a partial vacuum while the surface fibrous web is oven-dried.

4. The method according to claim 3, wherein the handling fabric is used to position the oven-dried surface fibrous web in the cavity of the mold.

5. The method according to claim 2, wherein, before its wetting, the surface fibrous web is immobilized on a support by an adhesive.

6. The method according to claim 2, wherein the surface fibrous web is rewetted during its shaping.

7. The method according to claim 6, wherein the surface fibrous web is cut before its wetting.

8. The method according to claim 7, wherein the three-dimensional fibrous preform and the surface fibrous web are wetted with at least one of a water or a tackifier.

9. The method according to claim 1, wherein the mold is closed by attaching a counter mold comprising a second cavity in which a further surface fibrous web is formed.

10. The method according to claim 1, wherein the surface fibrous web is formed of woven tapes, or by two bidirectional layers superimposed and sewn together.

11. The method according to claim 6, wherein the surface fibrous web is cut after its wetting.

12. The method according to claim 6, wherein the surface fibrous web is cut during its shaping.

13. The method according to claim 7, wherein the surface fibrous web is cut after its wetting.

14. The method according to claim 13, wherein the surface fibrous web is cut during its shaping.

15. The method according to claim 8, wherein, the cavity of the mold is wetted with at least one of the water or the tackifier before shaping the surface fibrous web.

Description

DESCRIPTION OF THE FIGURES

[0033] The invention will be better understood and other details, characteristics and advantages of the invention will appear more clearly when reading the following description made as a non-limitative example and with reference to the appended drawings in which:

[0034] FIG. 1 is a block diagram illustrating steps of a method according to the invention,

[0035] FIGS. 2 and 3 are schematic perspective views of a preform before and after forming,

[0036] FIG. 4 is a schematic perspective view of a mold for manufacturing a composite part,

[0037] FIGS. 5a, 5b and 5c represent in a very schematic way different surface webs that can be used in the method according to the invention,

[0038] FIGS. 6 and 7 are block diagrams illustrating variants of embodiments of the method according to the invention,

[0039] FIGS. 8 to 26 illustrate steps of the method of FIG. 6, and

[0040] FIGS. 27 to 40 illustrate steps of the method of FIG. 7.

DETAILED DESCRIPTION

[0041] FIG. 1 is a block diagram illustrating the steps of a method according to the invention of manufacturing a turbomachine composite part 10 such as a fan blade visible in FIG. 4.

[0042] This part comprises a fibrous structure which comprises on the one hand a three-dimensional fibrous preform 12 visible in FIG. 3 and on the other hand at least one surface fibrous web 14 covering at least a portion of the preform. The fibrous structure is embedded in a thermosetting resin-based polymer matrix so as to obtain a rigid part.

[0043] As mentioned above, the preform 12 is produced by three-dimensional weaving of yarns using a loom, and has a generally flat shape visible in FIG. 2 at the exit of the loom. This fan blade preform 12 comprises a portion 12a intended to extend into the vane of the blade, and a portion 12b intended to extend into the blade root.

[0044] The surface web 14 comprises fibers such as carbon fibers and can be: [0045] a fabric 14a visible in FIG. 5a, obtained by weaving tapes 14a1, oriented for example in perpendicular directions, [0046] a Uni-Directional (UD) layer 14b as shown in FIG. 5b, obtained by sewing unidirectional fibres 14b1 together, [0047] a fabric 14c comprising two Uni-Directional (UD) layers 14b superimposed and sewn together, the fibres 14b1 of the two layers 14b being oriented in different directions, for example perpendicular, [0048] etc.

[0049] The surface state of a preform 12 (FIGS. 2 and 3) is very irregular and a surface web 14 is generally deposited on both sides of the portion 12a, intended to be located respectively on the pressure and suction sides of the vane, to improve this surface state (FIG. 4). Each web 14 can extend to the portion 12b of the preform 12.

[0050] The method in FIG. 1 comprises steps of: [0051] (I) forming the surface web 14, [0052] (II) forming the preform 12, and [0053] (III) injecting thermosetting resin into the fibrous structure formed by the web 14 and the preform 12.

[0054] Advantageously, the forming (I) of the surface web 14 is carried out by positioning the web in a cavity 16a of a mold 16 (FIG. 4) and deforming it to fit the shape of this cavity. This allows the web 14 to be shaped before the actual shaping of the preform 12 (II). The preform is also shaped by positioning the preform in the cavity 16a of the mold 16, directly on the web 14, and deforming it to match the shape of the cavity.

[0055] The mold 16 is then closed by placing a counter mold on the mold, the fibrous structure is dried and the thermosetting resin is injected into the mold to impregnate the fibrous structure.

[0056] It is known to (ii) wet the preform 12 during its forming (II). To facilitate the handling of the web 14 and in particular to avoid its deterioration, the invention proposes to (i) also wet the web before and/or during its forming (I).

[0057] FIGS. 6 and 7 illustrate two variants of embodiment of the method.

[0058] The method of FIG. 6, which is also illustrated in FIGS. 8 to 26, uses a woven tape fabric 14a (FIG. 5a).

[0059] The method of FIG. 6 comprises a first step i, consisting in wetting the web 14a, here before its forming, which takes place in step I.

[0060] FIG. 8 illustrates this first step i during which an operator can spray, for example water, on the web 14 and in particular on each of the two webs 14 of the composite part to be manufactured. The spraying of the water is carried out using an appropriate tool 18.

[0061] Prior to this step i, the webs 14 can be pre-cut and can therefore undergo a cutting step D to set them at predetermined sides. In addition, the webs 14 can be immobilized on a support 20 such as the upper surface of a workbench, before the wetting. This immobilization can simply be achieved by using a strip adhesive 22 which is placed on two opposite sides of each web 14 for example.

[0062] The next step i′ consists of drying the web 14 before shaping it. Drying gives the web an additional stiffness which makes it much less prone to deformation. For this purpose, and as shown in FIG. 9, the web 14 is covered with a handling fabric 24 which will facilitate the transfer of the web from the support 20 to the mold 16. The fabric 24 is advantageously made of a permeable material so that air and moisture can be sucked through it. The web 14 and the fabric 24 are then covered with a vacuum bag 26 which allows the web to be subjected to a partial vacuum. The whole is put in the oven and thus under partial vacuum, e.g. at a temperature of 110° C. or less, and for a sufficient time to obtain a dry web 14.

[0063] The step i′ can be followed by a new step D of cutting the web 14, for example by means of a template 28 placed directly on the web, and possibly immobilized on the web by an strip adhesive 22 (FIG. 10). The cutting of the web can simultaneously lead to the cutting of the handling fabric 24 located here under the web. This cut D, as well as the previous cut, can be performed with any suitable tool, e.g. a pair of scissors, a knurl 30, a blade, etc.

[0064] The next step shown in FIGS. 11 to 13 consists then to transfer the web 14 from the support 20 to the mold 16. Prior to this transfer, water may possibly be sprayed into the mold (step E in FIG. 6). The handling fabric 24 enables the web 14 to be grasped more easily without damaging it and facilitates its positioning in the cavity of the mold 16. Once the web is positioned, the fabric 24 is removed. The same operation is performed with the second web 14 which is positioned in the cavity of the counter mold 32, as shown in FIGS. 14 to 16.

[0065] The next step I consists in shaping the web 14 in the cavity of the mold 16, preferably by wetting it again using the tool 18 to make it more flexible (FIG. 17). The shaping is carried out manually (FIG. 18) and may require an additional operation to cut the edges of the web, for example using a pair of scissors 34 (FIG. 19), to prevent the web from having bulges 36 (FIG. 20) and to ensure that it completely covers the bottom of the cavity of the mold 16 (FIG. 21). The same step I is carried out on the two webs 14, and thus on the mold 16 and the counter mold 24.

[0066] The next step II consists in shaping the preform 12 in the mold 16, directly on the previously installed web 14, by wetting it (step ii) also with water for example (FIG. 22). The shaping is carried out manually (FIG. 23) and ensures that the preform is wedged in the cavity and perfectly fits the shape of the cavity (FIG. 24).

[0067] The counter mold 32 is then added and fixed to the mold (FIGS. 25 and 26), which allows the second web 14 to be applied to the still bare face of the preform 12. The tooling thus assembled is then placed in an oven in order to be dried (for example by heating it to a temperature less than or equal to 120° C.) and before undergoing the resin injection operation (step III).

[0068] The method in FIG. 7, which is also illustrated in FIGS. 27 to 40, uses a fabric 14c with sewn layers (FIG. 5c).

[0069] This fabric 14c has a better hold than the fabric 14a used in the previous embodiment and can be cut directly (without prior wetting and drying). For example, the cut D of the web 14 is made with a blade 38 of the cutter type and a ruler 40, on a support 20 (FIG. 27). The two webs 14 of the workpiece are thus cut (FIG. 28).

[0070] Prior to the transfer of the web 14 into the mold 16, water or a tackifier can optionally be sprayed into the mold 16 (step E in FIG. 7). For example, the tackifier is sprayed using a container 42 containing tackifier under pressure (FIGS. 29 and 30). A tackifier is a sticky substance, in this case for example water-based.

[0071] The next step shown in FIGS. 30 to 33 then consists in shaping (step I) a first web 14 in the cavity of the mold 16, optionally wetting it (step i) with the tool 18 to make it more flexible. This wetting may be optional if the prior wetting of the mold 16 is sufficient to wet and soften the web during its shaping. Shaping is carried out manually (FIGS. 30 and 31) and may require an additional operation to cut the edges of the web, for example using a pair of scissors 34 (FIG. 32), to ensure that the web completely covers the bottom of the cavity of the mold 16 (FIG. 33). Similar operations are carried out with the second web 14 in the counter mold 32, as shown in FIGS. 34 to 37.

[0072] The next step II consists in shaping the preform 12 in the mold 16, directly on the previously installed web 14, by wetting it (step ii) also with the water or the tackifier, for example. The shaping is carried out manually and ensures that the preform is wedged in the cavity and perfectly fits the shape thereof (FIGS. 38 and 39).

[0073] The counter mold 32 is then added and fixed to the mold (FIG. 40), which allows the second web 14 to be applied to the still bare side of the preform 12. The tooling thus assembled is then placed in an oven in order to be dried (for example by heating it to a temperature less than or equal to 120° C.) and before undergoing the resin injection operation (step III).