POROUS ELECTROCHROMIC NIOBIUM OXIDE FILMS AND METHODS OF MAKING AND USE THEREOF
20210340022 · 2021-11-04
Inventors
- Delia Milliron (Austin, TX, US)
- Gary ONG (Temecula, CA, US)
- Camila SAEZ CABEZAS (Austin, TX, US)
- Hsin-Che LU (Austin, TX, US)
Cpc classification
C01P2004/64
CHEMISTRY; METALLURGY
B82Y40/00
PERFORMING OPERATIONS; TRANSPORTING
C01P2004/16
CHEMISTRY; METALLURGY
C01P2002/77
CHEMISTRY; METALLURGY
C01P2004/54
CHEMISTRY; METALLURGY
C01P2002/72
CHEMISTRY; METALLURGY
C01P2004/24
CHEMISTRY; METALLURGY
C09K9/00
CHEMISTRY; METALLURGY
International classification
C09K9/00
CHEMISTRY; METALLURGY
Abstract
Disclosed herein are porous electrochromic niobium oxide films comprising a plurality of niobium oxide nanocrystals, wherein the plurality of niobium oxide nanocrystals comprise niobium oxide having a formula of NbO.sub.x where x represents the average Nb:O ratio in the niobium oxide and where x is from 2 to 2.6. Also disclosed herein are methods of making the porous electrochromic niobium oxide films, methods of use of the porous electrochromic niobium oxide films, and devices comprising the porous electrochromic niobium oxide films.
Claims
1. A porous electrochromic niobium oxide film comprising: a plurality of niobium oxide nanocrystals, wherein the plurality of niobium oxide nanocrystals comprise niobium oxide having a formula NbO.sub.x where x represents the average Nb:O ratio in the niobium oxide and where x is from 2 to 2.6, and wherein the plurality of niobium oxide crystals are: substantially rod-shaped such that the plurality of niobium oxide nanocrystals comprise a plurality of rod-shaped niobium oxide nanocrystals, substantially plate-shaped such that the plurality of niobium oxide nanocrystals comprise a plurality of plate-shaped niobium oxide nanocrystals, or a combination thereof.
2. The porous electrochromic niobium oxide film of claim 1, wherein x is from 2.3 to 2.5.
3. The porous electrochromic niobium oxide film of claim 1, wherein the plurality of niobium oxide nanocrystals comprise Nb.sub.2O.sub.5, Nb.sub.12O.sub.29, or a combination thereof.
4. (canceled)
5. (canceled)
6. The porous electrochromic niobium oxide film of claim 20, wherein the plurality of niobium oxide nanocrystals have an average particle shape that is anisotropic such that the plurality of niobium oxide crystals have an elongated axis and wherein the elongated axis is substantially parallel to the [001] direction of the crystal structure or the [011] direction of the crystal structure.
7. (canceled)
8. The porous electrochromic niobium oxide film of claim 1, wherein the plurality of niobium oxide nanocrystals are a plurality of rod-shaped niobium oxide nanocrystals and the plurality of rod-shaped niobium oxide nanocrystals have an average length of from 0.5 nm to 200 nm and an average width of from 0.5 nm to 20 nm.
9-14. (canceled)
15. The porous electrochromic niobium oxide film of claim 1, wherein the plurality of niobium oxide nanocrystals are a plurality of plate-shaped niobium oxide nanocrystals and the plurality of plate-shaped niobium oxide nanocrystals have an average length of from 0.5 nm to 200 nm, an average width of from 0.5 nm to 100 nm, and an average thickness of from 0.5 nm to 20 nm.
16-19. (canceled)
20. The porous electrochromic niobium oxide film of claim 1, wherein the plurality of niobium oxide nanocrystals have a crystal structure that is substantially orthorhombic, pseudo-hexagonal, substantially monoclinic, or a combination thereof.
21. (canceled)
22. The porous electrochromic niobium oxide film of claim 1, wherein the plurality of niobium oxide nanocrystals are substantially free of ligands and/or capping materials.
23. The porous electrochromic niobium oxide film of claim 1, wherein the porous electrochromic niobium oxide film has an average porosity of from 15% to 80%.
24. The porous electrochromic niobium oxide film of claim 1, wherein the porous electrochromic niobium oxide film has an average thickness of from 10 nm to 2 microns.
25-30. (canceled)
31. A method of making the porous electrochromic niobium oxide film of claim 1, the method comprising: making the plurality of niobium oxide nanocrystals, wherein making the niobium oxide nanocrystals comprises aminolysis-driven formation of a plurality of niobium oxo clusters, condensation of the plurality of niobium oxo clusters into a plurality of amorphous niobium oxide seeds, and crystallization and growth of the plurality of amorphous niobium oxide seeds to thereby form the plurality of niobium oxide nanocrystals; dispersing the plurality of niobium oxide nanocrystals in a first solvent, thereby forming a dispersion; and depositing the dispersion on a substrate; thereby forming the electrochromic niobium oxide film.
32-44. (canceled)
45. The method of claim 31, wherein the method of making the plurality of niobium oxide nanocrystals comprises: mixing a niobium salt with a ligand and a second solvent to form a solution comprising a niobium-ligand complex; mixing the solution comprising the niobium-ligand complex with an amine, an alcohol, or a combination thereof, and subsequently heating at a first temperature to form a solution comprising a plurality of niobium oxo clusters; and heating the solution comprising the plurality of niobium oxo clusters at a second temperature to crystallize and grow the plurality of niobium oxide nanocrystals.
46. The method of claim 45, wherein the first temperature is from 100° C. to 200° C. and the second temperature is from 200° C. to 320° C.
47. (canceled)
48. The method of claim 45, wherein the niobium salt comprises a niobium halide, a niobium ethoxide, a niobium oxalate, or a combination thereof.
49. (canceled)
50. (canceled)
51. (canceled)
52. The method of claim 45, wherein the ligand comprises an alkyl carboxylic acid, an alkylphosphonic acid, and alkylphosphinic acid, an alkylsulfonic acid, or combinations thereof.
53-58. (canceled)
59. The method of claim 45, wherein the niobium-ligand complex comprises a niobium oleate complex.
60-63. (canceled)
64. The method of claim 45, wherein the method is performed under an inert atmosphere.
65. The method of claim 45, further comprising stripping the ligands from the plurality of niobium oxide nanocrystals prior to forming the electrochromic niobium oxide film.
66. An electrochromic electrode comprising the porous electrochromic niobium oxide film of claim 1 deposited on a conducting layer.
67-79. (canceled)
80. An electrochromic device comprising the electrochromic film of claim 1, wherein the electrochromic device comprises an electronic device, an energy storage device, an energy conversion device, an optical device, an optoelectronic device, or a combination thereof.
81-86. (canceled)
Description
BRIEF DESCRIPTION OF THE FIGURES
[0034] The accompanying figures, which are incorporated in and constitute a part of this specification, illustrate several aspects of the disclosure, and together with the description, serve to explain the principles of the disclosure.
[0035]
[0036]
[0037]
[0038]
[0039]
[0040]
[0041]
[0042]
[0043]
[0044]
[0045]
[0046]
[0047]
[0048]
[0049]
[0050]
[0051]
[0052]
[0053]
[0054]
[0055]
[0056]
[0057]
[0058]
[0059]
[0060]
[0061]
[0062]
[0063]
[0064]
[0065]
[0066]
[0067]
[0068]
[0069]
[0070]
[0071]
[0072]
[0073]
[0074]
[0075]
[0076]
[0077]
[0078]
[0079]
[0080]
[0081]
[0082]
[0083]
[0084]
[0085]
[0086]
[0087]
[0088]
[0089]
[0090]
[0091]
[0092]
[0093]
[0094]
[0095]
[0096]
[0097]
[0098]
[0099]
[0100]
[0101]
[0102]
[0103]
[0104]
[0105]
[0106]
[0107]
[0108]
[0109]
[0110]
[0111]
[0112]
[0113]
[0114]
[0115]
[0116]
[0117]
[0118]
[0119]
[0120]
[0121]
[0122]
[0123]
[0124]
[0125]
[0126]
[0127]
[0128]
[0129]
[0130]
[0131]
[0132]
[0133]
[0134]
[0135]
[0136]
[0137]
[0138]
[0139]
[0140]
[0141]
[0142]
[0143]
[0144]
[0145]
[0146]
[0147]
[0148]
[0149]
[0150]
[0151]
[0152]
[0153]
[0154]
[0155]
[0156]
DETAILED DESCRIPTION
[0157] The compositions, devices, and methods described herein may be understood more readily by reference to the following detailed description of specific aspects of the disclosed subject matter and the Examples included therein.
[0158] Before the present compositions, devices, and methods are disclosed and described, it is to be understood that the aspects described below are not limited to specific synthetic methods or specific reagents, as such may, of course, vary. It is also to be understood that the terminology used herein is for the purpose of describing particular aspects only and is not intended to be limiting.
[0159] Also, throughout this specification, various publications are referenced. The disclosures of these publications in their entireties are hereby incorporated by reference into this application in order to more fully describe the state of the art to which the disclosed matter pertains. The references disclosed are also individually and specifically incorporated by reference herein for the material contained in them that is discussed in the sentence in which the reference is relied upon.
General Definitions
[0160] In this specification and in the claims that follow, reference will be made to a number of terms, which shall be defined to have the following meanings:
[0161] Throughout the description and claims of this specification the word “comprise” and other forms of the word, such as “comprising” and “comprises,” means including but not limited to, and is not intended to exclude, for example, other additives, components, integers, or steps.
[0162] As used in the description and the appended claims, the singular forms “a,” “an,” and “the” include plural referents unless the context clearly dictates otherwise. Thus, for example, reference to “a composition” includes mixtures of two or more such compositions, reference to “the compound” includes mixtures of two or more such compounds, reference to “an agent” includes mixture of two or more such agents, and the like.
[0163] “Optional” or “optionally” means that the subsequently described event or circumstance can or cannot occur, and that the description includes instances where the event or circumstance occurs and instances where it does not.
[0164] It is understood that throughout this specification the identifiers “first” and “second” are used solely to aid the reader in distinguishing the various components, features, or steps of the disclosed subject matter. The identifiers “first” and “second” are not intended to imply any particular order, amount, preference, or importance to the components or steps modified by these terms.
[0165] Porous Electrochromic Niobium Oxide Films
[0166] Disclosed herein are porous electrochromic niobium oxide films comprising a plurality of niobium oxide nanocrystals. The plurality of niobium oxide nanocrystals can be substantially free of ligands and/or capping materials. The plurality of niobium oxide nanocrystals can comprise niobium oxide having a formula NbO.sub.x, where x represents the average Nb:O ratio in the niobium oxide and where x is 2 or more (e.g., 2.05 or more, 2.1 or more, 2.15 or more, 2.2 or more, 2.25 or more, 2.3 or more, 2.35 or more, 2.4 or more, 2.45 or more, or 2.5 or more). In some examples, the plurality of niobium oxide nanocrystals can comprise niobium oxide having a formula NbO.sub.x where x is 2.6 or less (e.g., 2.55 or less, 2.5 or less, 2.45 or less, 2.4 or less, 2.35 or less, 2.3 or less, 2.25 or less, 2.2 or less, 2.15 or less, or 2.1 or less). The value of x in NbO.sub.x (e.g., the Nb:O ratio) of the niobium oxide comprising the plurality of niobium oxide nanocrystals can range from any of the minimum values described above to any of the maximum values described above. For example, the plurality of niobium oxide nanocrystals can comprise niobium oxide having a formula of NbO.sub.x where x represents the average Nb:O ratio in the niobium oxide and where x is from 2 to 2.6 (e.g., from 2.1 to 2.5, from 2.2 to 2.5, from 2.3 to 2.5, or from 2.4 to 2.5). In some examples, the plurality of niobium oxide nanocrystals can comprise Nb.sub.2O.sub.5, Nb.sub.12O.sub.29, or a combination thereof.
[0167] The plurality of niobium oxide nanocrystals can have a crystal structure that is substantially anisotropic. For example, the plurality of niobium oxide nanocrystals can have a crystal structure that is substantially orthorhombic, pseudo-hexagonal, substantially monoclinic, or a combination thereof. In some examples, the plurality of niobium oxide nanocrystals can have a crystal structure that is substantially orthorhombic, substantially monoclinic, or a combination thereof. In some examples, the plurality of niobium oxide nanocrystals can have a crystal structure that is substantially orthorhombic. In some examples, the plurality of niobium oxide nanocrystals can have a crystal structure that is substantially monoclinic.
[0168] The plurality of niobium oxide nanocrystals can comprise nanocrystals of any shape (e.g., a sphere, a rod, a quadrilateral, an ellipse, a triangle, a polygon, etc.). In some examples, the plurality of niobium oxide nanocrystals can have an isotropic shape. In some examples, the plurality of niobium oxide nanocrystals can have an anisotropic shape. In some examples, the plurality of niobium oxide nanocrystals can be substantially rod-shaped such that the plurality of niobium oxide nanocrystals comprise a plurality of rod-shaped niobium oxide nanocrystals.
[0169] The plurality of niobium oxide nanocrystals can have an average particle size. “Average particle size” and “mean particle size” are used interchangeably herein, and generally refer to the statistical mean particle size of the particles (or crystals) in a population of particles (or crystals). For example, the average particle size for a plurality of particles with a substantially spherical shape can comprise the average diameter of the plurality of particles. For a particle with a substantially spherical shape, the diameter of a particle can refer, for example, to the hydrodynamic diameter. As used herein, the hydrodynamic diameter of a particle can refer to the largest linear distance between two points on the surface of the particle. Mean particle size can be measured using methods known in the art, such as evaluation by scanning electron microscopy, transmission electron microscopy, and/or dynamic light scattering. As used herein, the average particle size is determined by electron microscopy.
[0170] In certain examples, where the plurality of niobium oxide nanocrystals have a substantially isotropic shape, the plurality of niobium oxide nanocrystals can have an average particle size of 0.5 nm or more (e.g., 1 nm or more, 1.5 nm or more, 2 nm or more, 2.5 nm or more, 3 nm or more, 3.5 nm or more, 4 nm or more, 4.5 nm or more, 5 nm or more, 6 nm or more, 7 nm or more, 8 nm or more, 9 nm or more, 10 nm or more, 11 nm or more, 12 nm or more, 13 nm or more, 14 nm or more, 15 nm or more, 16 nm or more, 17 nm or more, or 18 nm or more). In certain examples, where the plurality of niobium oxide nanocrystals have a substantially isotropic shape, the plurality of niobium oxide nanocrystals can have an average particle size of 20 nm or less (e.g., 19 nm or less, 18 nm or less, 17 nm or less, 16 nm or less, 15 nm or less, 14 nm or less, 13 nm or less, 12 nm or less, 11 nm or less, 10 nm or less, 9 nm or less, 8 nm or less, 7 nm or less, 6 nm or less, 5 nm or less, 4.5 nm or less, 4 nm or less, 3.5 nm or less, 3 nm or less, 2.5 nm or less, 2 nm or less, or 1.5 nm or less). The average particle size of the plurality of niobium oxide nanocrystals with a substantially isotropic shape can range from any of the minimum values described above to any of the maximum values described above. For example, the plurality of niobium oxide nanocrystals having a substantially isotropic shape can have an average particle size of from 0.5 nm to 20 nm (e.g., from 0.5 nm to 10 nm, from 2 nm to 10 nm, from 10 nm to 20 nm, from 0.5 nm to 8 nm, from 2 nm to 8 nm, from 8 nm to 14 nm, from 14 nm to 20 nm, from 1 nm to 20 nm, from 2 nm to 20 nm, or from 3 nm to 19 nm).
[0171] In some examples, the plurality of niobium oxide nanocrystals having a substantially isotropic shape can be substantially monodisperse. “Monodisperse” and “homogeneous size distribution,” as used herein, and generally describe a population of particles where all of the particles are the same or nearly the same size. As used herein, a monodisperse distribution refers to particle distributions in which 80% of the distribution (e.g., 85% of the distribution, 90% of the distribution, or 95% of the distribution) lies within 25% of the median particle size (e.g., within 20% of the average particle size, within 15% of the average particle size, within 10% of the average particle size, or within 5% of the average particle size).
[0172] In some examples, the plurality of niobium oxide nanocrystals are substantially rod-shaped such that the plurality of niobium oxide nanocrystals comprise a plurality of rod-shaped niobium oxide nanocrystals. The plurality of rod-shaped niobium oxide nanocrystals can have an average length and an average width. In some examples, the plurality of rod-shaped niobium oxide nanocrystals can have an average length of 0.5 nm or more (e.g., 1 nm or more, 1.5 nm or more, 2 nm or more, 2.5 nm or more, 3 nm or more, 3.5 nm or more, 4 nm or more, 4.5 nm or more, 5 nm or more, 6 nm or more, 7 nm or more, 8 nm or more, 9 nm or more, 10 nm or more, 15 nm or more, 20 nm or more, 25 nm or more, 30 nm or more, 35 nm or more, 40 nm or more, 45 nm or more, 50 nm or more, 60 nm or more, 70 nm or more, 80 nm or more, 90 nm or more, 100 nm or more, 110 nm or more, 120 nm or more, 130 nm or more, 140 nm or more, 150 nm or more, 160 nm or more, 170 nm or more, or 180 nm or more). In some examples, the plurality of rod-shaped niobium oxide nanocrystals can have an average length of 200 nm or less (e.g., 190 nm or less, 180 nm or less, 170 nm or less, 160 nm or less, 150 nm or less, 140 nm or less, 130 nm or less, 120 nm or less, 110 nm or less, 100 nm or less, 90 nm or less, 80 nm or less, 70 nm or less, 60 nm or less, 50 nm or less, 45 nm or less, 40 nm or less, 35 nm or less, 30 nm or less, 25 nm or less, 20 nm or less, 15 nm or less, 10 nm or less, 9 nm or less, 8 nm or less, 7 nm or less, 6 nm or less, 5 nm or less, 4.5 nm or less, 4 nm or less, 3.5 nm or less, 3 nm or less, 2.5 nm or less, 2 nm or less, or 1.5 nm or less). The average length of the plurality of rod-shaped niobium oxide nanocrystals can range from any of the minimum values described above to any of the maximum values described above. For example, the plurality of rod-shaped niobium oxide nanocrystals can have an average length of from 0.5 nm to 200 nm (e.g., from 0.5 nm to 100 nm, from 2 nm to 100 nm, from 100 nm to 200 nm, from 0.5 nm to 50 nm, from 2 nm to 50 nm, from 50 nm to 100 nm, from 100 nm to 150 nm, from 150 nm to 200 nm, from 1 nm to 200 nm, from 2 nm to 200 nm, from 1 nm to 100 nm, from 5 nm to 100 nm, from 10 nm to 90 nm, or from 20 nm to 80 nm).
[0173] The plurality of rod-shaped niobium oxide nanocrystals can, for example, have an average width of 0.5 nm or more (e.g., 1 nm or more, 1.5 nm or more, 2 nm or more, 2.5 nm or more, 3 nm or more, 3.5 nm or more, 4 nm or more, 4.5 nm or more, 5 nm or more, 6 nm or more, 7 nm or more, 8 nm or more, 9 nm or more, 10 nm or more, 11 nm or more, 12 nm or more, 13 nm or more, 14 nm or more, 15 nm or more, 16 nm or more, 17 nm or more, or 18 nm or more). In some examples, the plurality of rod-shaped niobium oxide nanocrystals can have an average width of 20 nm or less (e.g., 19 nm or less, 18 nm or less, 17 nm or less, 16 nm or less, 15 nm or less, 14 nm or less, 13 nm or less, 12 nm or less, 11 nm or less, 10 nm or less, 9 nm or less, 8 nm or less, 7 nm or less, 6 nm or less, 5 nm or less, 4.5 nm or less, 4 nm or less, 3.5 nm or less, 3 nm or less, 2.5 nm or less, 2 nm or less, or 1.5 nm or less). The average width of the plurality of rod-shaped niobium oxide nanocrystals can range from any of the minimum values described above to any of the maximum values described above. For example, the plurality of rod-shaped niobium oxide nanocrystals can have an average width of from 0.5 nm to 20 nm (e.g., from 0.5 nm to 10 nm, from 2 nm to 10 nm, from 10 nm to 20 nm, from 0.5 nm to 8 nm, from 2 nm to 8 nm, from 8 nm to 14 nm, from 14 nm to 20 nm, from 1 nm to 20 nm, from 2 nm to 20 nm, from 0.5 nm to 6 nm, from 1 nm to 6 nm, from 2 nm to 6 nm, from 0.5 nm to 4 nm, from 1 nm to 4 nm, from 0.5 nm to 2 nm, or from 2 nm to 4 nm). In some examples, the plurality of rod-shaped niobium oxide nanocrystals can be substantially monodisperse.
[0174] In some examples, the plurality of rod-shaped niobium oxide nanocrystals can be described by their aspect ratio, which, as used herein is the average length divided by the average width. For example, the plurality of rod-shaped niobium oxide nanocrystals can have an average aspect ratio of greater than 1 (e.g., 5 or more, 10 or more, 15 or more, 20 or more, 25 or more, 30 or more, 35 or more, 40 or more, 45 or more, 50 or more, 60 or more, 70 or more, or 80 or more). In some examples, the plurality of rod-shaped niobium oxide nanocrystals can have an average aspect ratio of 100 or less (e.g., 90 or less, 80 or less, 70 or less, 60 or less, 50 or less, 45 or less, 40 or less, 35 or less, 30 or less, 25 or less, 20 or less, 15 or less, or 10 or less). The average aspect ratio of the plurality of rod-shaped niobium oxide nanocrystals can range from any of the minimum values described above to any of the maximum values described above. For example, the plurality of rod-shaped niobium oxide nanocrystals can have an average aspect ratio of from greater than 1 to 100 (e.g., from 1 to 50, from 50 to 100, from 1 to 20, from 20 to 40, from 40 to 60, from 60 to 80, from 80 to 100, from 10 to 100, from 5 to 40, from 5 to 20, from 10 to 40, from 10 to 20, from 1 to 10, or from 5 to 10).
[0175] In some examples, the plurality of niobium oxide nanocrystals are substantially plate-shaped such that the plurality of niobium oxide nanocrystals comprise a plurality of plate-shaped niobium oxide nanocrystals. The plurality of plate-shaped niobium oxide nanocrystals can have an average length, an average width, and an average thickness. In some examples, the plurality of plate-shaped niobium oxide nanocrystals can have an average length of 0.5 nm or more (e.g., 1 nm or more, 1.5 nm or more, 2 nm or more, 2.5 nm or more, 3 nm or more, 3.5 nm or more, 4 nm or more, 4.5 nm or more, 5 nm or more, 6 nm or more, 7 nm or more, 8 nm or more, 9 nm or more, 10 nm or more, 15 nm or more, 20 nm or more, 25 nm or more, 30 nm or more, 35 nm or more, 40 nm or more, 45 nm or more, 50 nm or more, 60 nm or more, 70 nm or more, 80 nm or more, 90 nm or more, 100 nm or more, 110 nm or more, 120 nm or more, 130 nm or more, 140 nm or more, 150 nm or more, 160 nm or more, 170 nm or more, or 180 nm or more). In some examples, the plurality of plate-shaped niobium oxide nanocrystals can have an average length of 200 nm or less (e.g., 190 nm or less, 180 nm or less, 170 nm or less, 160 nm or less, 150 nm or less, 140 nm or less, 130 nm or less, 120 nm or less, 110 nm or less, 100 nm or less, 90 nm or less, 80 nm or less, 70 nm or less, 60 nm or less, 50 nm or less, 45 nm or less, 40 nm or less, 35 nm or less, 30 nm or less, 25 nm or less, 20 nm or less, 15 nm or less, 10 nm or less, 9 nm or less, 8 nm or less, 7 nm or less, 6 nm or less, 5 nm or less, 4.5 nm or less, 4 nm or less, 3.5 nm or less, 3 nm or less, 2.5 nm or less, 2 nm or less, or 1.5 nm or less). The average length of the plurality of plate-shaped niobium oxide nanocrystals can range from any of the minimum values described above to any of the maximum values described above. For example, the plurality of plate-shaped niobium oxide nanocrystals can have an average length of from 0.5 nm to 200 nm (e.g., from 0.5 nm to 100 nm, from 2 nm to 100 nm, from 100 nm to 200 nm, from 0.5 nm to 50 nm, from 2 nm to 50 nm, from 50 nm to 100 nm, from 100 nm to 150 nm, from 150 nm to 200 nm, from 50 nm to 150 nm, from 1 nm to 200 nm, from 2 nm to 200 nm, from 1 nm to 100 nm, from 2 nm to 100 nm, from 5 nm to 100 nm, from 10 nm to 90 nm, or from 20 nm to 80 nm).
[0176] The plurality of plate-shaped niobium oxide nanocrystals can, for example, have an average width of 0.5 nm or more (e.g., 1 nm or more, 1.5 nm or more, 2 nm or more, 2.5 nm or more, 3 nm or more, 3.5 nm or more, 4 nm or more, 4.5 nm or more, 5 nm or more, 6 nm or more, 7 nm or more, 8 nm or more, 9 nm or more, 10 nm or more, 15 nm or more, 20 nm or more, 25 nm or more, 30 nm or more, 35 nm or more, 40 nm or more, 45 nm or more, 50 nm or more, 60 nm or more, 70 nm or more, or 80 nm or more). In some examples, the plurality of plate-shaped niobium oxide nanocrystals can have an average width of 100 nm or less (e.g., 90 nm or less, 80 nm or less, 70 nm or less, 60 nm or less, 50 nm or less, 45 nm or less, 40 nm or less, 35 nm or less, 30 nm or less, 25 nm or less, 20 nm or less, 15 nm or less, 10 nm or less, 9 nm or less, 8 nm or less, 7 nm or less, 6 nm or less, 5 nm or less, 4.5 nm or less, 4 nm or less, 3.5 nm or less, 3 nm or less, 2.5 nm or less, 2 nm or less, or 1.5 nm or less). The average width of the plurality of plate-shaped niobium oxide nanocrystals can range from any of the minimum values described above to any of the maximum values described above. For example, the plurality of plate-shaped niobium oxide nanocrystals can have an average width of from 0.5 nm to 100 nm (e.g., from 0.5 nm to 50 nm, from 2 nm to 50 nm, from 50 nm to 100 nm, from 0.5 nm to 20 nm, from 2 nm to 20 nm, from 20 nm to 40 nm, from 40 nm to 60 nm, from 60 nm to 80 nm, from 80 nm to 100 nm, from 1 nm to 100 nm, from 2 nm to 100 nm, or from 5 nm to 95 nm).
[0177] The plurality of plate-shaped niobium oxide nanocrystals can, for example, have an average thickness of 0.5 nm or more (e.g., 1 nm or more, 1.5 nm or more, 2 nm or more, 2.5 nm or more, 3 nm or more, 3.5 nm or more, 4 nm or more, 4.5 nm or more, 5 nm or more, 6 nm or more, 7 nm or more, 8 nm or more, 9 nm or more, 10 nm or more, 11 nm or more, 12 nm or more, 13 nm or more, 14 nm or more, 15 nm or more, 16 nm or more, 17 nm or more, or 18 nm or more). In some examples, the plurality of plate-shaped niobium oxide nanocrystals can have an average thickness of 20 nm or less (e.g., 19 nm or less, 18 nm or less, 17 nm or less, 16 nm or less, 15 nm or less, 14 nm or less, 13 nm or less, 12 nm or less, 11 nm or less, 10 nm or less, 9 nm or less, 8 nm or less, 7 nm or less, 6 nm or less, 5 nm or less, 4.5 nm or less, 4 nm or less, 3.5 nm or less, 3 nm or less, 2.5 nm or less, 2 nm or less, or 1.5 nm or less). The average thickness of the plurality of plate-shaped niobium oxide nanocrystals can range from any of the minimum values described above to any of the maximum values described above. For example, the plurality of plate-shaped niobium oxide nanocrystals can have an average thickness of from 0.5 nm to 20 nm (e.g., from 0.5 nm to 10 nm, from 2 nm to 10 nm, from 10 nm to 20 nm, from 0.5 nm to 8 nm, from 2 nm to 8 nm, from 8 nm to 14 nm, from 14 nm to 20 nm, from 1 nm to 20 nm, from 2 nm to 20 nm, from 0.5 nm to 6 nm, from 1 nm to 6 nm, from 2 nm to 6 nm, from 0.5 nm to 4 nm, from 1 nm to 4 nm, or from 2 nm to 4 nm). In some examples, the plurality of plate-shaped niobium oxide nanocrystals can be substantially monodisperse.
[0178] In some examples, the plurality of plate-shaped niobium oxide nanocrystals can be described by their aspect ratio, which, as used herein is the average length divided by the average width. For example, the plurality of plate-shaped niobium oxide nanocrystals can have an average aspect ratio of greater than 1 (e.g., 5 or more, 10 or more, 15 or more, 20 or more, 25 or more, 30 or more, 35 or more, 40 or more, 45 or more, 50 or more, 60 or more, 70 or more, or 80 or more). In some examples, the plurality of plate-shaped niobium oxide nanocrystals can have an average aspect ratio of 100 or less (e.g., 90 or less, 80 or less, 70 or less, 60 or less, 50 or less, 45 or less, 40 or less, 35 or less, 30 or less, 25 or less, 20 or less, 15 or less, or 10 or less). The average aspect ratio of the plurality of plate-shaped niobium oxide nanocrystals can range from any of the minimum values described above to any of the maximum values described above. For example, the plurality of plate-shaped niobium oxide nanocrystals can have an average aspect ratio of from greater than 1 to 100 (e.g., from 1 to 50, from 50 to 100, from 1 to 20, from 20 to 40, from 40 to 60, from 60 to 80, from 80 to 100, from 10 to 100, from 5 to 40, from 5 to 20, from 10 to 40, from 10 to 20, from 1 to 10, or from 5 to 10). In some examples, the plurality of niobium oxide nanocrystals can comprise: a first population of nanocrystals comprising a first niobium oxide material and having a first particle shape having a first average particle size, a first average length, a first average width, a first average aspect ratio, or a combination thereof; and a second population of nanocrystals comprising a second niobium oxide material and having a second particle shape having a second set average particle size, a second average length, a second average width, a second average aspect ratio, or a combination thereof; wherein the first particle shape and the second particle shape are different, the first material and the second material are different, the first average particle size and the second average particle size are different, the first average length and the second average length are different, the first average width and the second average width are different, the first average aspect ratio and the second average aspect ratio are different, or a combination thereof. In some examples, the plurality of niobium oxide nanocrystals can comprise a mixture of a plurality of populations of nanocrystals, wherein each population of nanocrystals within the mixture is different with respect to shape, composition, size, length width, aspect ratio, or combinations thereof.
[0179] The porous electrochromic niobium oxide films can have an average porosity. The average porosity of the porous electrochromic niobium oxide films can be determined by methods known in the art, such as ellipsometric porosimetry. The porous electrochromic niobium oxide films can, for example, have an average porosity of 15% or more (e.g., 20% or more, 25% or more, 30% or more, 35% or more, 40% or more, 45% or more, 50% or more, 55% or more, 60% or more, 65% or more, or 70% or more). In some examples, the porous electrochromic niobium oxide films can have an average porosity of 80% or less (e.g., 75% or less, 70% or less, 65% or less, 60% or less, 55% or less, 50% or less, 45% or less, 40% or less, 35% or less, 30% or less, or 25% or less). The average porosity of the porous electrochromic niobium oxide films can range from any of the minimum values described above to any of the maximum values described above. For example, the porous electrochromic niobium oxide films can have an average porosity of from 15% to 80% (e.g., 15% to 50%, from 50% to 80%, from 15% to 25%, from 25% to 35%, from 25% to 45%, from 45% to 55%, from 55% to 65%, from 65% to 80%, from 15% to 75%, or from 15% to 60%). The average porosity of the porous electrochromic niobium oxide films can be selected in view of a variety of factors. In some examples, the shape, average size, average length, average width, average aspect ratio, or a combination thereof of the plurality of niobium oxide nanocrystals can be selected such that the electrochromic niobium oxide film has a desired porosity.
[0180] The porous electrochromic niobium oxide films can have an average thickness. The average thickness of the porous electrochromic niobium oxide films can be determined by methods known in the art, for example profilometry, cross-sectional electron microscopy, atomic force microscopy (AFM), ellipsometry, or combinations thereof. As used herein, the average thickness of the porous electrochromic niobium oxide films is determined by profilometry.
[0181] The porous electrochromic niobium oxide films can, for example, have an average thickness of 10 nanometers (nm) or more (e.g., 20 nm or more, 30 nm or more, 40 nm or more, 50 nm or more, 60 nm or more, 70 nm or more, 80 nm or more, 90 nm or more, 100 nm or more, 125 nm or more, 150 nm or more, 175 nm or more, 200 nm or more, 225 nm or more, 250 nm or more, 275 nm or more, 300 nm or more, 325 nm or more, 350 nm or more, 375 nm or more, 400 nm or more, 425 nm or more, 450 nm or more, 475 nm or more, 500 nm or more, 550 nm or more, 600 nm or more, 650 nm or more, 700 nm or more, 800 nm or more, 900 nm or more, 1 micrometer (micron, μm) or more, 1.25 μm or more, or 1.5 μm or more). In some example, the porous electrochromic niobium oxide films can have an average thickness of 2 μm or less (e.g., 1.75 μm or less, 1.5 μm or less, 1 μm or less, 900 nm or less, 800 nm or less, 700 nm or less, 650 nm or less, 600 nm or less, 550 nm or less, 500 nm or less, 475 nm or less, 450 nm or less, 425 nm or less, 400 nm or less, 375 nm or less, 350 nm or less, 325 nm or less, 300 nm or less, 275 nm or less, 250 nm or less, 225 nm or less, 200 nm or less, 175 nm or less, 150 nm or less, 125 nm or less, 100 nm or less, 90 nm or less, 80 nm or less, 70 nm or less, 60 nm or less, 50 nm or less, 40 nm or less, or 30 nm or less). The average thickness of the porous electrochromic niobium oxide films can range from any of the minimum values described above to any of the maximum values described above. For example, the porous electrochromic niobium oxide films can have an average thickness of from 10 nm to 2 μm (e.g., from 10 nm to 800 nm, from 800 nm to 2 μm, from 10 nm to 1.5 μm, from 10 nm to 1 μm, from 10 nm to 900 nm, from 20 nm to 700 nm, from 30 nm to 650 nm, from 40 nm to 600 nm, from 50 nm to 550 nm, from 60 nm to 500 nm, from 70 nm to 450 nm, or from 80 nm to 400 nm).
[0182] The porous electrochromic niobium oxide films can control optical properties such as optical transmission, absorption, reflectance, and/or emittance in a continual but reversible manner on application of a voltage. The porous electrochromic niobium oxide films can also be used to reduce near infrared transmission.
[0183] In some examples, the porous electrochromic niobium oxide films can transition from different optical states. These different states can be referred to herein as a first optical state and a second optical state. The use of the terms first and second here is not intended to imply that there are only two distinct optical states, but rather that the porous electrochromic niobium oxide films can change between different optical states.
[0184] In some examples, the porous electrochromic niobium oxide films can be switched from the first optical state to the second optical state and/or from the second optical state to the first optical state upon application of a potential to the porous electrochromic niobium oxide films. In some examples, the potential applied to the porous electrochromic niobium oxide film can be 1 volt (V) or more relative to Li/Li.sup.+ (e.g., 1.1 V or more, 1.2 V or more, 1.3 V or more, 1.4 V or more, 1.5 V or more, 1.75 V or more, 2 V or more, 2.25 V or more, 2.5 V or more, 2.75 V or more, 3 V or more, 3.25 V or more, or 3.5 V or more). In some examples, the potential applied to the porous electrochromic niobium oxide film can be 4 V or less relative to Li/Li.sup.+ (e.g., 3.75 V or less, 3.5 V or less, 3.25 V or less, 3 V or less, 2.75 V or less, 2.5 V or less, 2.25 V or less, 2 V or less, 1.75 V or less, or 1.5 V or less). The potential applied to the porous electrochromic niobium oxide film can range from any of the minimum values described above to any of the maximum values described above. For example, the potential applied to the porous electrochromic niobium oxide film can be from 1 V to 4 V relative to Li/Li.sup.+ (e.g., from 1 V to 2.5 V, from 2.5 V to 4 V, from 1 V to 2 V, from 2 V to 3 V, from 3 V to 4 V, from 1.2 V to 4 V, or from 1.5 V to 3.5 V).
[0185] In some examples, the porous electrochromic niobium oxide film can be switched from the first optical state to the second optical state and/or from the second optical state to the first optical state by applying the potential for an amount of time of 20 minutes or less (e.g., 15 minutes or less, 10 minutes or less, 5 minutes or less, 1 minute or less, 50 seconds or less, 40 seconds or less, 30 seconds or less, or 20 seconds or less). In some examples, the time the potential is applied to the porous electrochromic niobium oxide film to switch the porous electrochromic niobium oxide film from the first optical state to the second optical state can be referred to as the switching speed.
[0186] In some examples, the porous electrochromic niobium oxide films can be durable. As used herein, durability of the porous electrochromic niobium oxide films means that one or more properties of the porous electrochromic niobium oxide films (e.g., transmittance of the first optical state, transmittance of the second optical state) decreases by 5% or less (e.g., 4.75% or less, 4.5% or less, 4.25% or less, 4% or less, 3.75% or less, 3.5% or less, 3.25% or less, 3% or less, 2.75% or less, 2.5% or less, 2.25% or less, 2% or less, 1.75% or less, 1.5% or less, 1.25% or less, 1% or less, 0.75% or less, 0.5% or less, or 0.25% or less) over 200 cycles or more (e.g., 300 cycles or more, 400 cycles or more, 500 cycles or more, 600 cycles or more, 700 cycles or more, 800 cycles or more, 900 cycles or more, or 1000 cycles or more). As used herein, a cycle refers to the porous electrochromic niobium oxide film switching from the first optical state to the second optical state, and then back to the first optical state from the second optical state or switching from the second optical state to the first optical state and then back to the second optical state from the first optical state.
[0187] In certain examples, each of the first optical state and the second optical state can have an average transmittance at one or more wavelengths from 350 nm to 2500 nm and the average transmittance of the second optical state can be less than the average transmittance of the first optical state by 20% or more (e.g., 25% or more, 30% or more, 35% or more, 40% or more, 45% or more, 50% or more, 55% or more, 60% or more, 65% or more, 70% or more, 75% or more, 80% or more, 85% or more, 90% or more, or 95% or more) at one or more wavelengths from 350 nm to 2500 nm. For example, the first optical state can be substantially transparent at one or more wavelengths from 350 nm to 2500 nm and the second optical state can be substantially opaque at one or more wavelengths from 350 nm to 2500 nm.
[0188] In some examples, the porous electrochromic niobium oxide film has a coloration efficiency at one or more wavelengths from 350 nm to 2500 nm of 25 cm.sup.2/C or more (e.g. 30 cm.sup.2/C or more, 35 cm.sup.2/C or more, 40 cm.sup.2/C or more, 45 cm.sup.2/C or more, 50 cm.sup.2/C or more, 55 cm.sup.2/C or more, 60 cm.sup.2/C or more, 65 cm.sup.2/C or more, 70 cm.sup.2/C or more, 75 cm.sup.2/C or more, 80 cm.sup.2/C or more, 85 cm.sup.2/C or more, 90 cm.sup.2/C or more, 95 cm.sup.2/C or more, 100 cm.sup.2/C or more, 125 cm.sup.2/C or more, 150 cm.sup.2/C or more, 175 cm.sup.2/C or more, or 200 cm.sup.2/C or more). As used herein, the coloration efficiency refers to the change in optical density from the first optical state to the second optical state (e.g., the difference between the optical density of the first optical state and the optical density of the second optical state) relative to the charge density injected into the porous electrochromic niobium oxide film to switch the porous electrochromic niobium oxide film from the first optical state and the second optical state.
[0189] Methods of Making
[0190] Also disclosed herein are methods of making the porous electrochromic niobium oxide films described herein, the method comprising: dispersing the plurality of niobium oxide nanocrystals in a solvent, thereby forming a dispersion; and depositing the dispersion on a substrate; thereby forming the electrochromic niobium oxide film.
[0191] Depositing the plurality of nanocrystals can, for example, comprise printing, spin coating, drop-casting, zone casting, dip coating, blade coating, spraying, vacuum filtration, slot die coating, curtain coating, or combinations thereof.
[0192] Examples of solvents include, but are not limited to, tetrahydrofuran (THF), dimethylformamide (DMF), N-methylformamide, formamide, dichloromethane (CH.sub.2Cl.sub.2), ethylene glycol, ethanol, methanol, propanol, isopropanol, water, acetonitrile, chloroform, toluene, methyl acetate, ethyl acetate, acetone, hexane, heptane, tetraglyme, propylene carbonate, diglyme, dimethyl sulfoxide (DMSO), dimethoxyethane, xylene, and combinations thereof.
[0193] In some examples, the substrate can comprise glass, quartz, silicon, a transparent polymer, MgO, TiO.sub.2, TaO, or combinations thereof. In some examples, the substrate comprises a conducting layer. In some examples, the substrate comprises a conducting layer deposited on a non-conducting substrate such as glass, quartz, silicon, a transparent polymer, MgO, TiO.sub.2, TaO, or combinations thereof. The conducting layer can, for example, comprise a transparent conducting oxide, a carbon material, a nanostructured metal, or a combination thereof.
[0194] As used herein, “nanostructured” means any structure with one or more nanosized features. A nanosized feature can be any feature with at least one dimension less than 1 micrometer (μm) in size. For example, a nanosized feature can comprise a nanowire, nanotube, nanoparticle, nanopore, and the like, or combinations thereof. As such, the nanostructured metal can comprise, for example, a nanowire, nanotube, nanoparticle, nanopore, or a combination thereof. In some examples, the nanostructured metal can comprise a metal that is not nanosized but has been modified with a nanowire, nanotube, nanoparticle, nanopore, or a combination thereof. The nanostructured metal can comprise, for example, a metal selected from the group consisting of Be, Mg, Al, Ca, Sc, Ti, V, Cr, Mn, Fe, Co, Ni, Cu, Zn, Ga, Sr, Y, Zr, Nb, Mo, Tc, Ru, Rh, Pd, Ag, Cd, In, Sn, Ba, Hf, Ta, W, Re, Os, Ir, Pt, Au, Hg, Tl, Pb, Bi, La, Ce, Pr, Nd, Pm, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, and combinations thereof.
[0195] Examples of carbon materials include, but are not limited to, graphitic carbon and graphites, including pyrolytic graphite (e.g., highly ordered pyrolytic graphite (HOPG)) and isotropic graphite, amorphous carbon, carbon black, single- or multi-walled carbon nanotubes, graphene, glassy carbon, diamond-like carbon (DLC) or doped DLC, such as boron-doped diamond, pyrolyzed photoresist films, and others known in the art.
[0196] In some examples, the conducting layer can comprise a transparent conducting oxide. In some examples, the conducting layer can comprise a metal oxide. Examples of metal oxides include simple metal oxides (e.g., with a single metal element) and mixed metal oxides (e.g., with different metal elements). The metal oxide can, for example, comprise a metal selected from the group consisting of Cd, Cr, Cu, Ga, In, Ni, Sn, Ti, W, Zn, and combinations thereof. In some examples, the conducting layer can comprise CdO, CdIn.sub.2O.sub.4, Cd.sub.2SnO.sub.4, Cr.sub.2O.sub.3, CuCrO.sub.2, CuO.sub.2, Ga.sub.2O.sub.3, In.sub.2O.sub.3, NiO, SnO.sub.2, TiO.sub.2, ZnGa.sub.2O.sub.4, ZnO, InZnO, InGaZnO, InGaO, ZnSnO, Zn.sub.2SnO.sub.4, CdSnO, WO.sub.3, or combinations thereof.
[0197] In some examples, the conducting layer can further comprise a dopant. The dopant can comprise any suitable dopant for the conducting layer. The dopant can, for example, be selected to tune the optical and/or electronic properties of the nanostructured conducting film. In some examples, the dopant can comprise an n-type dopant. The dopant can, for example, comprise Al, B, Ca, Ce, Cl, Cs, Dy, Er, Eu, F, Ga, Gd, Ho, In, La, Mg, Mo, N, Nb, Nd, Rb, Sb, Sn, Sm, Ta, or combinations thereof.
[0198] In some examples, the conducting layer can comprise a transparent conducting oxide selected from indium doped tin oxide, tin doped indium oxide, fluorine doped tin oxide, and combinations thereof.
[0199] In some examples, the methods further comprise making the plurality of niobium oxide nanocrystals. For example, the method of making the plurality of niobium oxide nanocrystals can comprise formation of a plurality of niobium oxo clusters (e.g., via aminolysis or alcoholysis), condensation of the plurality of niobium oxo clusters into a plurality of amorphous niobium oxide seeds, and crystallization and growth of the plurality of amorphous niobium oxide seeds to thereby form the plurality of niobium oxide nanocrystals.
[0200] In some examples, the method of making the plurality of niobium oxide nanocrystals can comprise: mixing a niobium salt with a ligand and a solvent to form a solution comprising a niobium-ligand complex; mixing the solution comprising the niobium-ligand complex with an amine, an alcohol, or combination thereof, and subsequently heating at a first temperature to form a solution comprising a plurality of niobium oxo clusters; and heating the solution comprising the plurality of niobium oxo clusters at a second temperature to crystallize and grow the plurality of niobium oxide nanocrystals, wherein the second temperature is above the first temperature.
[0201] The niobium salt can, for example, comprise a niobium halide, a niobium ethoxide, a niobium oxalate, or a combination thereof. In some examples, the niobium salt san comprise a niobium halide, wherein the niobium halide can comprise a niobium chloride, a niobium bromide, a niobium iodide, a niobium fluoride, or combination thereof. In some examples, the niobium salt can comprise a niobium chloride, such as NbCl.sub.5.
[0202] The ligand can, for example, comprise any suitable ligand, such as those known in the art for nanocrystal synthesis. For example, the ligand can comprise an alkyl carboxylic acid, an alkylphosphonic acid, and alkylphosphinic acid, an alkylsulfonic acid, or combinations thereof.
[0203] In some examples, the ligand can comprise an alkyl carboxylic acid, such as mystiric acid, oleic acid, or combinations thereof. In some examples, the ligand can comprise oleic acid.
[0204] The amine can, for example, comprise a primary amine, a secondary amine, a tertiary amine, or a combination thereof. For example, the amine can comprise a primary alkyl amine, a secondary alkyl amine, a tertiary alkyl amine, or a combination thereof. In some examples, the amine can comprise a primary amine, such as oleylamine In some examples, the amine can comprise a tertiary amine, such as trioctylamine. The alcohol can, for example, comprise an alkyl alcohol, a diol, or a combination thereof. In some examples, the alcohol can comprise oleyl alcohol.
[0205] In some examples, the niobium-ligand complex can comprise a niobium oleate complex. In certain examples, the niobium-ligand complex can comprise a chloro oleyl niobium (V) complex.
[0206] The solvent can, for example, comprise any suitable solvent, such as those known in the art. For example, the solvent can comprise squalene, oleic acid, oleylamine, octadecene, dialkyl ether (e.g., dioctyl ether), diphenyl ether, dibenzyl ether, or a combination thereof. In some examples, the solvent can comprise octadecene.
[0207] The niobium salt, the ligand, and the primary amine can be provided in an appropriate amount. For example, the amount of the niobium salt, the amount of the ligand, and/or the amount of the primary amine can be selected in view of a variety of factors, such as the desired shape and/or size of the plurality of niobium oxide nanocrystals. In some examples, the niobium salt and the ligand can be provided in a molar ratio of 1:1 or less (e.g., 1:2 or less, 1:3 or less, 1:4 or less, 1:5 or less, 1:6 or less, 1:7 or less, 1:8 or less, 1:9 or less, or 1:10 or less). In some examples, the primary amine and the ligand can be provided in a molar ratio of 1:1 or less (e.g., 1:2 or less, 1:3 or less, 1:4 or less, 1:5 or less, 1:6 or less, 1:7 or less, 1:8 or less, 1:9 or less, or 1:10 or less).
[0208] The first temperature can, for example be 100° C. or more (e.g., 110° C. or more, 120° C. or more, 130° C. or more, 140° C. or more, 150° C. or more, 160° C. or more, 170° C. or more, or 180° C. or more). In some examples, the first temperature can be 200° C. or less (e.g., 190° C. or less, 180° C. or less, 170° C. or less, 160° C. or less, 150° C. or less, 140° C. or less, 130° C. or less, or 120° C. or less). The first temperature can range from any of the minimum values described above to any of the maximum values described above. For example, the first temperature can be from 100° C. to 200° C. (e.g., from 100° C. to 150° C., from 150° C. to 200° C., from 100° C. to 120° C., from 120° C. to 140° C., from 140° C. to 160° C., from 160° C. to 180° C., from 180° C. to 200° C., from 100° C. to 190° C., from 110° C. to 200° C., from 100° C. to 140° C., or from 110° C. to 130° C.).
[0209] The second temperature can, for example, the 200° C. or more (e.g., 210° C. or more, 220° C. or more, 230° C. or more, 240° C. or more, 250° C. or more, 260° C. or more, 270° C. or more, 280° C. or more, 290° C. or more, or 300° C. or more). In some examples, the second temperature can be 320° C. or less (e.g., 310° C. or less, 300° C. or less, 290° C. or less, 280° C. or less, 270° C. or less, 260° C. or less, 250° C. or less, 240° C. or less, 230° C. or less, or 220° C. or less). The second temperature can range from any of the minimum values described above to any of the maximum values described above. For example, the second temperature can be from 200° C. to 320° C. (e.g., from 200° C. to 260° C., from 260° C. to 300° C., from 200° C. to 220° C., from 220° C. to 240° C., from 240° C. to 260° C., from 260° C. to 280° C., from 280° C. to 300° C., from 300° C. to 320° C., from 200° C. to 300° C., from 210° C. to 320° C., or from 210° C. to 300° C.).
[0210] The method can, in some examples, be performed under an inert atmosphere (e.g., Ar, N2, etc.).
[0211] In some examples, the methods can further comprise stripping the ligands from the plurality of niobium oxide nanocrystals prior to forming the electrochromic niobium oxide film.
[0212] Electrodes and Devices
[0213] Also disclosed herein are electrochromic electrodes comprising any of the porous electrochromic niobium oxide films described herein, electrochromic devices comprising any of the porous electrochromic niobium oxide films described herein, and electrochromic devices comprising any of the electrochromic electrodes described herein.
[0214] Also disclosed herein are electrochromic electrodes comprising any of the porous electrochromic niobium oxide films described herein, wherein the electrochromic electrode comprises the porous electrochromic niobium oxide film deposited on a conducting layer.
[0215] The conducting layer can, for example, comprise a transparent conducting oxide, a carbon material, a nanostructured metal, or a combination thereof. As used herein, “nanostructured” means any structure with one or more nanosized features. A nanosized feature can be any feature with at least one dimension less than 1 micrometer (μm) in size. For example, a nanosized feature can comprise a nanowire, nanotube, nanoparticle, nanopore, and the like, or combinations thereof. As such, the nanostructured metal can comprise, for example, a nanowire, nanotube, nanoparticle, nanopore, or a combination thereof. In some examples, the nanostructured metal can comprise a metal that is not nanosized but has been modified with a nanowire, nanotube, nanoparticle, nanopore, or a combination thereof. The nanostructured metal can comprise, for example, a metal selected from the group consisting of Be, Mg, Al, Ca, Sc, Ti, V, Cr, Mn, Fe, Co, Ni, Cu, Zn, Ga, Sr, Y, Zr, Nb, Mo, Tc, Ru, Rh, Pd, Ag, Cd, In, Sn, Ba, Hf, Ta, W, Re, Os, Ir, Pt, Au, Hg, Tl, Pb, Bi, La, Ce, Pr, Nd, Pm, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, and combinations thereof.
[0216] Examples of carbon materials include, but are not limited to, graphitic carbon and graphites, including pyrolytic graphite (e.g., highly ordered pyrolytic graphite (HOPG)) and isotropic graphite, amorphous carbon, carbon black, single- or multi-walled carbon nanotubes, graphene, glassy carbon, diamond-like carbon (DLC) or doped DLC, such as boron-doped diamond, pyrolyzed photoresist films, and others known in the art.
[0217] In some examples, the conducting layer can comprise a transparent conducting oxide. In some examples, the conducting layer can comprise a metal oxide. Examples of metal oxides include simple metal oxides (e.g., with a single metal element) and mixed metal oxides (e.g., with different metal elements). The metal oxide can, for example, comprise a metal selected from the group consisting of Cd, Cr, Cu, Ga, In, Ni, Sn, Ti, W, Zn, and combinations thereof. In some examples, the conducting layer can comprise CdO, CdIn.sub.2O.sub.4, Cd.sub.2SnO.sub.4, Cr.sub.2O.sub.3, CuCrO.sub.2, CuO.sub.2, Ga.sub.2O.sub.3, In.sub.2O.sub.3, NiO, SnO.sub.2, TiO.sub.2, ZnGa.sub.2O.sub.4, ZnO, InZnO, InGaZnO, InGaO, ZnSnO, Zn.sub.2SnO.sub.4, CdSnO, WO.sub.3, or combinations thereof.
[0218] In some examples, the conducting layer can further comprise a dopant. The dopant can comprise any suitable dopant for the conducting layer. The dopant can, for example, be selected to tune the optical and/or electronic properties of the nanostructured conducting film. In some examples, the dopant can comprise an n-type dopant. The dopant can, for example, comprise Al, B, Ca, Ce, Cl, Cs, Dy, Er, Eu, F, Ga, Gd, Ho, In, La, Mg, Mo, N, Nb, Nd, Rb, Sb, Sn, Sm, Ta, or combinations thereof.
[0219] In some examples, the conducting layer can comprise a transparent conducting oxide selected from indium doped tin oxide, tin doped indium oxide, fluorine doped tin oxide, and combinations thereof.
[0220] In some example, the electrochromic electrode can be durable. As used herein, durability of the electrochromic electrode means that one or more properties (e.g., charge capacity, transmittance of the first optical state, transmittance of the second optical state) decreases by 5% or less (e.g., 4.75% or less, 4.5% or less, 4.25% or less, 4% or less, 3.75% or less, 3.5% or less, 3.25% or less, 3% or less, 2.75% or less, 2.5% or less, 2.25% or less, 2% or less, 1.75% or less, 1.5% or less, 1.25% or less, 1% or less, 0.75% or less, 0.5% or less, or 0.25% or less) over 200 cycles or more (e.g., 300 cycles or more, 400 cycles or more, 500 cycles or more, 600 cycles or more, 700 cycles or more, 800 cycles or more, 900 cycles or more, or 1000 cycles or more).
[0221] Also disclosed herein are electrochromic devices comprising the electrochromic electrodes described herein. The electrochromic devices can, for example, comprise any of the electrochromic electrodes described herein, an electrolyte, and a counter electrode, wherein the electrochromic electrode and the counter electrode are in electrochemical contact with the electrolyte. In response to electrical stimulus, electronic charge can move in or out of the electrochromic electrode and ionic charge from the electrolyte can migrate into or out of the electrochromic electrode, thus affecting the optical properties of the porous electrochromic niobium oxide film.
[0222] The electrolyte can comprise H.sup.+ ions, Li.sup.+ ions, Na.sup.+ ions, K.sup.+ ions, Mg.sup.2+ ions, Ca.sup.2+ ions, Al.sup.3+ ions, or combinations thereof. For example, the electrolyte can comprise a lithium ion salt selected from the group consisting of LiTFSI, LiI, LiPH.sub.6, LiPF.sub.6, LiBF.sub.4, LiClO.sub.4, and combinations thereof.
[0223] The concentration of the electrolyte can be, for example, 0.001 molar (M; mol/L) or more (e.g., 0.0025 M or more, 0.005 M or more, 0.0075 M or more, 0.01 M or more, 0.025 M or more, 0.05 M or more, 0.075 M or more, 0.1 M or more, 0.25 M or more, 0.5 M or more, 0.75 M or more, 1 M or more, 1.25 M or more, 1.5 M or more, 1.75 M or more, 2 M or more, 2.25 M or more, 2.5 M or more, or 2.75 M or more). In some examples, the concentration of the electrolyte can be 3 M or less (e.g., 2.75 M or more, 2.5 M or more, 2.25 M or more, 2 M or more, 1.75 M or more, 1.5 M or more, 1.25 M or more, 1 M or more, 0.75 M or more, 0.5 M or more, 0.25 M or more, 0.1 M or more, 0.075 M or more, 0.05 M or more, 0.025 M or more, 0.001 M or more, 0.0075 M or more, 0.005 M or more, or 0.0025 M or more). The concentration of the electrolyte can range from any of the minimum values described above to any of the maximum values described above. For example, the electrolyte can have a concentration of from 0.001 M to 3 M (e.g., from 0.001 M to 1.5 M, from 1.5 M to 3 M, from 0.001 M to 0.01 M, from 0.01 M to 0.1 M, from 0.1 M to 1 M, from 0.001 M to 1 M, from 0.025 M to 0.4 M, from 0.05 M to 0.3 M, or from 0.075 to 0.2 M).
[0224] The electrolyte can, in some examples, further comprise a solvent selected from the group consisting of tetraglyme, propylene carbonate, diglyme, dimethyl sulfoxide (DMSO), dimethyl formamide (DMF), dimethoxyethane, acetonitrile, ethylene carbonate, dimethyl carbonate, monoglyme (dimethoxyethane), and combinations thereof.
[0225] In some examples, the electrochromic devices described herein can be coupled to a power supply and optionally to one or more additional suitable features including, but not limited to, a voltmeter, an ammeter, a multimeter, an ohmmeter, a signal generator, a pulse generator, an oscilloscope, a frequency counter, a potentiostat, or a capacitance meter. For example, the electrochromic device can further comprise a power supply that is in electrical contact with the electrochromic electrode and the counter electrode. In some examples, the power supply is configured to apply a potential to the electrochromic electrode, the counter electrode, or a combination thereof.
[0226] In some examples, the electrochromic device can be durable. As used herein, durability of the electrochromic device means that one or more properties (e.g., charge capacity, transmittance of the first optical state, transmittance of the second optical state) decreases by 5% or less (e.g., 4.75% or less, 4.5% or less, 4.25% or less, 4% or less, 3.75% or less, 3.5% or less, 3.25% or less, 3% or less, 2.75% or less, 2.5% or less, 2.25% or less, 2% or less, 1.75% or less, 1.5% or less, 1.25% or less, 1% or less, 0.75% or less, 0.5% or less, or 0.25% or less) over 200 cycles or more (e.g., 300 cycles or more, 400 cycles or more, 500 cycles or more, 600 cycles or more, 700 cycles or more, 800 cycles or more, 900 cycles or more, or 1000 cycles or more).
[0227] The electrochromic devices described herein can, for example, comprise an electronic device, an energy storage device, an energy conversion device, an optical device, an optoelectronic device, or combinations thereof. In some examples, the electrochromic devices can comprise a touch panel, an electronic display, a transistor, a smart window, a solar cell, a fuel cell, a photovoltaic cell, a battery, a light emitting diode, or a combination thereof.
[0228] Methods of Use
[0229] Also provided herein are methods of use of the electrochromic devices, electrochromic electrodes, and porous electrochromic niobium oxide films described herein. For example, the electrochromic devices, electrochromic electrodes, and/or porous electrochromic niobium oxide films described herein can be used in, for example, an electronic device, an energy storage device, an energy conversion device, an optical device, an optoelectronic device, or combinations thereof. In some examples, the electrochromic devices, electrochromic electrodes, and/or porous electrochromic niobium oxide films described herein can be used in, for example, a touch panel, an electronic display, a transistor, a smart window, a solar cell, a fuel cell, a photovoltaic cell, a battery, a light emitting diode, or a combination thereof. Such devices can be fabricated by methods known in the art.
[0230] In some examples, the electrochromic devices, electrochromic electrodes, and/or porous electrochromic niobium oxide films described herein can be used in various articles of manufacture including electronic devices, energy storage devices, energy conversion devices, optical devices, optoelectronic devices, and combinations thereof. Examples of articles of manufacture (e.g., devices) using the electrochromic devices electrochromic electrodes, and/or porous electrochromic niobium oxide films described herein can include, but are not limited to touch panels, electronic displays, transistors, smart windows, solar cells, fuel cells, photovoltaic cells, batteries, light emitting diodes, and combinations thereof. Such articles of manufacture can be fabricated by methods known in the art.
[0231] The examples below are intended to further illustrate certain aspects of the methods and compounds described herein, and are not intended to limit the scope of the claims.
EXAMPLES
[0232] The following examples are set forth below to illustrate the methods and results according to the disclosed subject matter. These examples are not intended to be inclusive of all aspects of the subject matter disclosed herein, but rather to illustrate representative methods, compositions, and results. These examples are not intended to exclude equivalents and variations of the present invention, which are apparent to one skilled in the art.
[0233] Efforts have been made to ensure accuracy with respect to numbers (e.g., amounts, temperature, etc.) but some errors and deviations should be accounted for. Unless indicated otherwise, parts are parts by weight, temperature is in ° C. or is at ambient temperature, and pressure is at or near atmospheric. There are numerous variations and combinations of reaction conditions, e.g., component concentrations, temperatures, pressures, and other reaction ranges and conditions that can be used to optimize the product purity and yield obtained from the described process. Only reasonable and routine experimentation will be required to optimize such process conditions.
Example 1
[0234] Herein, an electrochromic coating designed from the bottom up based upon niobium oxide is described. By considering the many phases and stoichiometry of niobium oxide, it was determined that the desired phases are orthorhombic or pseudo-hexagonal niobium oxide with a stoichiometry of Nb.sub.2O.sub.5. Selection of stoichiometry was due to a necessary change in niobium oxidation state from +5 to +4 to achieve visible coloration. The choice of crystal structure on the other hand was motivated by studies suggesting preferential Li.sup.+ intercalation and fast diffusion pathways along different crystallographic planes, possibility decoupling the design for strain accommodation and fast kinetics. Next, nanocrystal morphology was considered. Strain accommodation in nanostructures, previously demonstrated for silicon nanowires, allows minimal structural damage upon electrochemical cycling when an anisotropic morphology has a long axis coincident with the preferred intercalation plane. Furthermore, selection of certain crystal planes on the side of the anisotropic structure can facilitate Li ion motion throughout the structure, allowing enhanced kinetics.
[0235] Beyond intrinsic properties of the nanocrystal (composition, crystal structure, and shape), the necessary microstructure for fast kinetics was also considered. Prior work in electrochemical systems has shown that porosity can be important and, generally, electrodes with structures that are more porous than just the random packing of spheres exhibit better performance. The use of templating agents was avoided herein to maintain ease of processability. Therefore, porosity was instead incorporated by using long-range electrostatic repulsion that disallows close packing in nanorod systems. Further, all processing for the structures described herein was limited to the use of only solution techniques, with no vacuum processes or severe heating steps, to enable scalable use in high or low temperature setups.
[0236] Having considered the aforementioned factors, the electrochromic response of orthorhombic niobium oxide nanorods dominantly in the near infrared (NIR) was investigated and was shown to exhibit high electrochemical durability coupled with fast kinetics enabled by fast Li.sup.+ transport pathways. Intercalative strain was preferentially accommodated by having nanorods with a [001] long axis for fast Li.sup.+ transport along with a generally porous structure of the nanocrystal films that further enables fast Li.sup.+ transport through the electrolyte.
[0237] Methods
[0238] Nanocrystal Synthesis
[0239] The synthesis of niobium oxide (Nb.sub.2O.sub.5) nanorods is based on established colloidal synthesis methods and was conducted in an air-free environment using a standard Schlenk line technique. Briefly, 0.545 g of niobium chloride (2 mmol, NbCl.sub.5, Aldrich 99.995%) was mixed with 3.127 g oleic acid (11 mmol, Aldrich 90%) and 10 g of octadecene (40 mmol, Aldrich, 90%) under an inert environment to form a niobium oleate complex. This solution was left to stir until the niobium chloride completely dissolved to form a blood red solution of niobium oleate and was then degassed at 120° C. under vacuum for 30 minutes. Then, 0.534 g of oleylamine (2 mmol, 90% Acros Organics) was mixed with 0.789 g of octadecene and the mixture was injected into the niobium oleate solution, after which the combination was degassed at 120° C. under vacuum for 15 minutes. Then, the solution was heated to and held at 240° C. for 30 minutes to nucleate and grow the Nb.sub.2O.sub.5 nanorods.
[0240] Ligand Stripping
[0241] For a typical ligand stripping procedure, 1 mL of a 5 mg/mL solution of niobium oxide nanorods in toluene was mixed with 1 mL of dimethylformamide (DMF) with 5 mg of nitrosonium tetrafluoroborate (Aldrich 95%). This solution was sonicated for thirty minutes and then left to settle to observe the clear precipitation of a nanocrystal pellet. Then, the nanocrystals and solution were centrifuged at 2000 rpm to separate the nanocrystals from the solution. The nanocrystals were then dispersed in 1 mL of DMF, mixed with an equal part of hexane, shaken, and the resultant phase separated hexane layer removed. This process was repeated 3 times. Then, the nanocrystals were subjected to five cycles of purification by flocculation and dispersion in a solvent combination of toluene, for flocculation, and DMF, for dispersion. The final ligand-stripped niobium oxide nanorod product was then dispersed in DMF.
[0242] Thin Film Deposition
[0243] Ligand-stripped Nb.sub.2O.sub.5 nanorods were dispersed in 1:1 mixture of DMF and acetonitrile (30 mg/ml) and spin-coated at 1250 rpm on FTO-coated glass substrates.
[0244] Scanning Electron Microscopy
[0245] Scanning electron microscopy was performed on a Hitachi 55500 SEM/STEM at a 30 kV accelerating voltage. Nanorods were imaged in bright-field scanning transmission electron microscopy mode. Samples were prepared by drop casting a dilute nanocrystal solution in toluene on Type-A ultrathin carbon (Ted Pella, 01822, 400 mesh) copper TEM grids. Nanorod films spin-coated on silicon substrates were images in scanning electron microscopy mode.
[0246] Spectroelectrochemical and Standard Electrochemical Measurements
[0247] Electrochemical charging and in-situ optical modulation measurements were performed using a spectroelectrochemical cell in an Ar glovebox. In a typical half-cell measurement, a three-electrode configuration was used to electrochemically charge the Nb.sub.2O.sub.5 nanorod films, in which Li foil acts as the counter and reference electrode and the nanorod film on FTO-coated glass is the working electrode. For these experiments, lithium bis(trifluoromethanesulfonyl)imide (Li-TFSI) in anhydrous tetraglyme electrolytes of varying concentrations (0.1 M, 1 M, and 3 M) were prepared. In-situ transmission data as a function of applied potential (Bio-logic VMP3 potentiostat) was collected using an ASD Quality Spec Pro spectrometer connected to the cell with fiber optic cables. This setup was also used to perform chronoamperometry (CA), cyclic voltammetry (CV), and cycling stability studies.
[0248] X-Ray Diffraction (XRD)
[0249] Powder diffraction patterns were collected on a Rigaku R-Axis Spider using Cu K.sub.α radiation (1.54 Å). Samples were mounted on a cryoloop using mineral oil.
[0250] Raman Spectroscopy
[0251] Raman spectroscopy was carried out on a LabRAM HR Evolution Raman instrument (Horiba). Samples were drop-casted on a glass substrate and spectra were collected using a 50× microscope objective with an acquisition time of 60 s at a 532 nm excitation wavelength (50 mW power laser source).
[0252] FTIR Spectroscopy
[0253] Fourier transform infrared spectroscopy was done on spin-coated thin films on undoped silicon substrates in transmission geometry with a 2 cm.sup.−1 wavenumber resolution and an average of 128 scans on a Bruker Vertex 70 spectrometer.
[0254] X-Ray Photoelectron Spectroscopy (XPS)
[0255] XPS was carried out with a Kratos X-ray photoelectron spectrometer-axis ultra DLD using Al K.sub.α source. Samples were identical to the nanorod films spin-coated on FTO for spectroelectrochemical and standard electrochemical measurements.
[0256] Results and Discussion
[0257] Nanocrystal Synthesis
[0258] Niobium oxide nanorods were synthesized via decomposition of a niobium oleate complex. The as-synthesized nanorods are in the orthorhombic phase and have approximate dimensions of 3 nm diameter and 40 nm length (
[0259] Formation of Porous Films
[0260] To fabricate the electrochromic films, the nanorods were first ligand stripped to simultaneously remove the insulating organic ligands and create a charged surface to introduce electrostatic repulsion. Herein, nitrosonium tetrafluoroborate was utilized for the ligand-stripping; successful ligand removal was confirmed with Fourier transform infrared spectroscopy by the disappearance of the C—H stretch and emergence of a broad hydroxyl peak, suggesting the oxide surface is now ligand free and —OH terminated (
[0261] Electrochromic Characterization
[0262] For electrochromic characterization, films were first spun on an FTO substrate from a ligand stripped Nb.sub.2O.sub.5 dispersion in a 1:1 DMF:ACN solution. The films were then tested in a half-cell configuration with a Li counter electrode by applying an oxidizing and reducing potential of 4 V and 1 V versus Li/Li′ in a 1 M Li-TFSI/tetraglyme electrolyte. The system exhibited fast electrochromic response with almost complete coloration within a minute (
[0263] Additional experiments with 3 M and 0.1 M electrolytes further demonstrated 20 second and 1-minute response times suggesting that, in this system, Li transport in the electrolyte is the primary bottleneck to switching kinetics (
[0264] X-ray photoelectron spectroscopic measurements were conducted on the orthorhombic Nb.sub.2O.sub.5 nanorod material before and after electrochemical reduction to investigate the nature of the electrochemically induced coloration. The results of the X-ray photoelectron spectroscopy measurements on the orthorhombic Nb.sub.2O.sub.5 nanorod material clarified the redox changes that underlie the coloration phenomena in both the visible and NIR regimes. Specifically, a reduction of Nb from a +5 to +4 state was observed, which is known to be responsible for visible coloration in niobium oxides upon lithiation (
[0265] Cyclic Stability
[0266] One of the key figure of merit for an electrochromic device is its cyclic stability upon subjugation to multiple cycles of charge and discharge. The prototypical electrochromic material, WO.sub.3, for instance, suffers from cyclic stability in the absence of specific surface modification to impart stability. Furthermore, previous attempts on engineering Nb.sub.2O.sub.5 electrochromics have also been hampered by the poor durability of this material upon multiple cycles of lithiation and delithiation. As shown in
Example 2
[0267] Existing niobium oxide electrochromic materials suffer from their sluggish lithiation rate and insulating-to-semiconducting nature, leading to slow electrochromic response. To facilitate the electronic and lithium transport of niobium oxides, appropriate design of their crystal structure and stoichiometry was considered. The electronic conductivity of niobium pentoxide can be increased upon introducing Nb.sup.4+ and oxygen vacancies into its crystal lattice (Cava et al. Phys. Rev. B 1991, 44, 6973-6981). Among the non-stoichiometric niobium pentoxide polymorphs, Nb.sub.12O.sub.29 (Nb.sup.4+.sub.2Nb.sup.5+.sub.10O.sub.29) shows the largest electronic conductivity with metallic property at room temperature. Furthermore, the monoclinic Nb.sub.12O.sub.29, its metastable phase at lower temperature, exhibits mostly vertex-shared niobium oxygen octahedra arranged into a Wadsley-Roth shear structure. The relatively open structural motifs in this crystal structure can serve as lithium sites and diffusion channels for fast lithiation upon switching. On the other hand, the electrochromic response of Nb.sub.12O.sub.29 can vary from the traditional Nb.sub.2O.sub.5 since the incorporation of Nb.sup.4+ with 4d.sup.1 valence electron can change the polaronic absorption of niobium oxides, or moreover, can show a plasmonic response due to the metallic property of Nb.sub.12O.sub.29. Strain accommodation in materials to withstand volume expansion upon lithium intercalation can be a necessary consideration for long-term operation for electrochromic devices. In this regard, an anisotropic morphology can be preferred for their potential to accommodate large volume expansion.
[0268] To utilize the above advantages of Nb.sub.12O.sub.29 in electrochromic applications, a colloidal synthesis showing control over crystal structure and stoichiometry was designed with monoclinic Nb.sub.12O.sub.29 nanoplates as the paradigm product. The films based on monoclinic Nb.sub.12O.sub.29 nanoplates exhibited porous morphology due to their anisotropic morphology and surface modification to introduce electrostatic repulsion. Fast and reversible electrochromic response upon lithiation was observed for the investigated films. Furthermore, these films showed strong modulation in both visible and NIR region, unlike other studied niobium oxides.
[0269] Methods
[0270] Nanocrystal Synthesis
[0271] The synthesis of niobium oxide (Nb.sub.12O.sub.29) nanoplates was designed based on colloidal synthesis method and conducted in an inert environment using Schlenk line technique. A hot-injection method was used to initiate the synthesis at designated temperature. In a typical synthesis, 0.405 g of NbCl.sub.5 powder (1.5 mmol, Aldrich 99.995%) and 4.237 g of oleic acid (15 mmol, Aldrich 90%) were mixed in a flask until the NbCl.sub.5 powder was dissolved, forming a blood red solution of niobium oleate complex. Afterwards, this solution was degassed at 120° C. for 30 min and the color gradually changed to orange during this process. In the meantime, 11.298 g of oleic acid (40 mmol, Aldrich 90%) and 2.140 g of oleylamine (8 mmol, Acros Organics) were mixed in another flask, degassed at 120° C. for 30 min, heated to 300° C. and kept at this temperature. Once the degassing procedure for the niobium oleate complex was finished, the orange solution was injected into the flask containing the mixture of oleic acid and oleylamine at 300° C., and the mixture reacted for 10 min to obtain the Nb.sub.12O.sub.29 nanoplates. After that, the nanocrystal solution was purified with a washing procedure using toluene as a solvent for dispersion and isopropanol as an anti-solvent for flocculation. The final product of Nb.sub.12O.sub.29 nanoplates was dispersed in toluene after washing.
[0272] Ligand Stripping
[0273] For the ligand-stripping procedure of Nb.sub.12O.sub.29 nanoplates, 30 mg of Nb.sub.12O.sub.29 nanoplates were dispersed in 3 ml of hexane; 30 mg of nitrosonium tetrafluoroborate (Aldrich 95%) was dissolved in 3 ml of DMF and this solution was gradually added into the nanoplate solution. The mixed solution was stirred for 30 min, after which the upper solution, comprising most of the ligand-capped nanoplates in hexane, was removed. The ligand-stripped nanoplates in DMF were purified with a washing process using DMF as a solvent and toluene as an anti-solvent. The final ligand-stripped nanoplates were dispersed in DMF at a concentration of 50 mg/ml.
[0274] Thin Film Deposition
[0275] Ligand-stripped Nb.sub.12O.sub.29 nanoplates (30 μl) were drop-cased onto FTO-coated glass substrates, which were then dried at 150° C. for 30 min. The active area was controlled using a razor blade to be 1.5×1.5 cm.sup.2. The same procedure was conducted on silicon substrates for imaging purposes.
[0276] Scanning Electron Microscopy
[0277] Scanning electron microscopy (SEM) and scanning transmission electron microscopy (STEM) images were collected using Hitachi 55500 SEM/STEM at 30 kV. Nanoplates were imaged in bright-field STEM mode by dropping the diluted nanoplate solution (before ligand stripping) on Type-A ultrathin carbon (Ted Pella, 01822, 400 mesh) copper TEM grids. Nanoplate thin films on silicon substrates were imaged in SEM mode.
[0278] X-Ray Diffraction (XRD)
[0279] Diffraction patterns of Nb.sub.12O.sub.29 nanoplates were collected on a Rigaku R-Axis Spider using Cu K.sub.α radiation (1.54 Å). Nanoplate solutions were dried into powder and mounted on a cryoloop using mineral oil.
[0280] Spectroelectrochemical and Standard Electrochemical Measurements
[0281] Electrochemical and in-situ optical measurements were performed in a spectroelectrochemical cell in an Ar glovebox. In a typical measurement, the nanoplate thin film on FTO-coated glass was immersed into the electrolyte as the working electrode, while Li foil was also immersed into the electrolyte serving as the counter electrode. Electrolyte was prepared in an Ar glovebox and comprised 1 M of lithium bis(trifluoromethanesulfonyl)imide (LiTFSI) in anhydrous tetraglyme. Electrochemical data were collected using an electrochemical workstation (Bio-logic VMP3 potentiostat); meanwhile, in-situ optical data were collected using an ASD Quality Spec Pro spectrometer. Potential was applied to the cell by chronoamperometry (CA).
[0282] Results and Discussion
[0283] Nanocrystal Synthesis and Characterization
[0284] Nb.sub.12O.sub.29 nanoplates were synthesized by injecting the preformed niobium oleate complex into a hot bath containing oleic acid and oleylamine. The STEM image in
[0285] Formation of Porous Films
[0286] The organic ligands on the Nb.sub.12O.sub.29 nanoplates were stripped from the surface and replaced by a charged surface stabilized in DMF. Electrostatic repulsion provided by DMF and nitrosonium tetrafluoroborate between the Nb.sub.12O.sub.29 nanoplates allows a porous film morphology to be generated using solution-based coating (Heo et al. Nano Lett. 2017, 17, 5756-5761). A SEM image of a Nb.sub.12O.sub.29 nanoplate film with a thickness of 170 nm is shown in
[0287] Electrochromic Characterization
[0288] A 170 nm thick film of ligand-stripped Nb.sub.12O.sub.29 nanoplates on FTO-coated glass was used throughout the electrochromic measurements as the working electrode in a three-electrode configuration with Li foil as the counter electrode. Potential applied to the system was referenced to Li/Li.sup.+ in a 1 M LiTFSI/tetraglyme electrolyte. As shown in
Example 3
[0289] Within the context of materials with tunable optical properties, particularly in the subfield of smart windows electrochromic materials are of interest for their ability to exhibit on-demand change in optical properties upon application of an electrochemical bias. These devices can be used to modulate light transmission through windows based on application of charge with full reversibility. Established electrochromic materials are largely based on tungsten oxide, which suffers from issues of electrochemical and photochemical stability as well as charging kinetics on top of issues of abundance.
[0290] Electrochromic devices are used to modulate light transmittance by electrochemical charging or discharging of an active material. Due to the electrochemical nature of the phenomenon, the process can be slow and lead to degradation of the material over time. In application however, an electrochromic material must exhibit fast switching characteristics that are reversible with durability over thousands of cycles.
[0291] Current electrochromic technologies rely primarily on variants of tungsten oxide (WO.sub.3-x) with only a small usage of niobium oxide, despite both materials having been explored as traditional electrochromic materials and niobium having a >10× abundance as a mineral resource (20 ppm vs 1.5 ppm in the Earth's crust). This is due to the latter's poor coloration kinetics and electrochemical durability prohibiting cyclic use. Current methods to synthesize niobium oxide usually rely on hydrothermal processes that yield micron-sized colloids or vacuum processes that yield thin films with limited control over porosity and crystal morphology. While the former allows tuning of crystal shape and dimensionality, the micrometer size prohibits film casting into films with high optical quality and low haze. The latter suffers from the inverse problem, with easy production of films of high optical quality, but difficult control of crystal shape and dimensionality.
[0292] Disclosed herein are colloidal niobium oxide nanocrystals that when deposited as a porous film act as an electrochromic layer with reversible coloration under applied bias, fast charging kinetics, and good electrochemical durability. The films described herein utilize deliberately nanostructured niobium oxide nanocrystals which predominantly present known planes for fast Li ion diffusion in a form factor that facilitates generation of intrinsic porosity and has inherent strain tolerance for good electrochemical durability.
[0293] By synthesizing colloidal nanocrystals of niobium oxide, colloids were generated that can yield films of high optical quality with two different niobium oxide crystals, Nb.sub.2O.sub.5 nanorods and monoclinic Nb.sub.12O.sub.29 nanoplates. The nanorod morphology of the Nb.sub.2O.sub.5 nanocrystals is tailored to take advantage of known fast Li ion diffusion pathways in the material and allow for fast kinetics and effective strain relaxation to avoid degradation, while introducing Nb.sup.4+ and oxygen vacancy into nanoplates enhances the electrical conductivity that also leads to fast kinetics with additional feature of unique optical response upon coloration. Specifically, the niobium oxide nanocrystals were engineered i) with a long axis along the planes of fast Li ion diffusion to allow fast switching kinetics, and ii) into an anisotropic morphology to provide intrinsic porosity in the film as well strain accommodation during Li ion intercalation to provide stable electrochemical durability. Coupled with the nanocrystal ink form of the material that can be adopted into roll-to-roll and other solution-based processes, this material offers new properties previously not observed for niobium oxide electrochromic films in a form factor that is scalable and useful for applications from smart windows and batteries to optical filters, displays and sensors.
[0294] The technology described herein is based on nanoengineered niobium oxide and can be tailored to deliver a high durability, fully reversible, ultra-fast charging electrochromic films with the additional benefit of compatibility with solution based processes and improved color neutrality. The system described is capable of ultrafast electrochromic response (sub-30 seconds for near complete switching or sub-10 seconds by conventional 75% optical range electrochromic standards), alongside ultra stable (flat charge capacity upon cycling) durability. Coloration is more neutral than tungsten oxide and no unintended photochromic effect is present under ultraviolet light exposure.
[0295] The resulting system makes niobium oxide a viable electrochromic material by removing previous material limitations of kinetics and durability. The resulting material is several times faster than the conventional systems (not only comparing to other strategies for niobium oxide, but considering all known electrochromic films), has the potential to meet code standards for 50-100 k electrochemical cycles, thermal cycles, and is made with a material that is also 10× more abundant than the incumbent tungsten oxide electrochromic material. Furthermore, this material circumvents the photochemical instability of tungsten oxide electrodes.
[0296] Electrochromic films composed of niobium oxide (Nb.sub.2O.sub.5) are one of the earliest electrochromic materials explored. However, the material was considered unsuitable for widespread use due to its slow kinetics of coloration and poor electrochemical durability. The nano-engineering niobium oxide materials described herein changes the overall ensemble properties of this material and imparts the necessary kinetics and durability into this ‘old’ electrochromic material to make it viable for actual usage.
[0297] Described herein is a form of colloidal niobium oxide nanocrystal ink that upon being coated to form films, acts as a fast switching and durable electrochromic material. Specifically, the nanocrystal morphology can be tuned to exploit pathways of fast lithium transport that is intrinsic to the orthorhombic niobium oxide crystal structure. The material design applied to this system allowed system specifics such as a 10 second coloration time and at least 500 electrochemical cycles with no signs of degradation. Coupled to the nanocrystal ink form of the material, the material is also suitable for solution deposition and even roll-to-roll processing of electrochromic films.
[0298] Besides the advantages listed above, compared to the established electrochromic material tungsten oxide, the niobium oxide nanocrystal electrochromic materials described herein have a more favorable color when charged and circumvent unwanted photoinduced coloration. In the first case, tungsten oxide has a deep blue color that is not preferred and must be compensated for by a brown coloration, usually accomplished with a brown coloring counter electrode film, such as NiO. However, a blue tint often remains, at least at some stages of coloration. Nb.sub.2O.sub.5 nanorod films have a more neutral color when charged, making it easier to achieve a visually pleasing, neutral tint at all stages of darkening. In addition, tungsten oxide is well-known to undergo a photodarkening effect under ultraviolet exposure, particularly when in contact with organic (e.g. solution, polymer, or gel) electrolytes. This photochromic process degrades the electrolyte, can lead to accumulation of an unwanted surface coating on the tungsten oxide, and can result in irreversible darkening of the electrochromic material over time. While this problem is even more severe for nanocrystal films of tungsten oxide, owing to their large surface area, niobium oxide nanocrystals, including both the Nb.sub.2O.sub.5 nanorods and Nb.sub.12O.sub.29 nanoplates described herein, are immune to this photochromic effect, thus resolving a major durability challenge facing electrochromic windows. In addition, Nb.sub.12O.sub.29 nanoplates can modulate a broad range of incident light across the visible and IR regions, which has not been reported in niobium oxide electrochromic materials before.
[0299] The coloration efficiency of Nb.sub.2O.sub.5 nanocrystals is lower than that typically reported for tungsten oxide. This parameter describes the extent of optical tinting achieved for a given amount of charge injected. To simply overcome this challenge, thicker films of Nb.sub.2O.sub.5 can be used to achieve the required extent of darkening. The porous nature of nanocrystal films means that ion transport should still readily occur through the film thickness. The niobium oxide materials described herein were synthesized from niobium chloride, which is highly refined form of niobium precursor thus making the synthetic pathway costly to scale up. However, other precursors such as metal acetates, metal acetylacetonates, nitrates and so forth can be used instead. For niobium in particular, other precursors include niobic acids, niobium oxalate, and niobium oxide.
[0300] Uses for the electrochromic films described herein include uses in batteries and/or supercapacitors. Other uses include use in electrochromic windows for automobiles, trains, airplanes, residential and commercial buildings.
Example 4
[0301] Niobium oxide (Nb.sub.2O.sub.5) is an active material of interest for various technologies, such as catalysis, sensors, energy storage and electrochromic devices, owing to its unique optical, electronic, and electrochemical properties. These properties vary between different phases and morphologies in the Nb.sub.2O.sub.5 system, but systematic studies that correlate properties to phase and morphology are limited by current synthetic methods, which require post-synthetic high temperature treatments and suffer from a lack of direct and precise control over morphology, crystal structure, and stoichiometry. Herein, a heat up colloidal synthesis method that produces orthorhombic Nb.sub.2O.sub.5 nanorods with an aspect ratio of 1 nm in width by 31 nm in length that preferentially grow along the [001] direction is described. The synthesis is based upon aminolysis of niobium oleate and nanorods are formed through three distinct steps: aminolysis-driven formation of niobium oxo clusters, condensation into amorphous Nb.sub.2O.sub.5 seeds below the reaction temperature, and crystallization and growth of Nb.sub.2O.sub.5 nanorods. The electrochromic behavior of nanorod thin films upon Li.sup.+ intercalation was investigated and predominantly near-infrared, fast switching kinetics, and durability for 500 charge-discharge cycles was observed.
[0302] Introduction
[0303] Niobium oxide has garnered significant interest in the recent decade as an active material in applications ranging from electrochemical devices like batteries (Kim et al. Adv. Energy Mater. 2012, 2(1), 141-148; Augustyn et al. Nat. Mater. 2013, 12(6), 518-522) and electrochromic windows (Fu et al. J. Electrochem. Soc. 1999, 10(146), 3914-3918; Llordes et al. Nature 2013, 500, 323-326; Heo et al. Nano Lett. 2017, 17 (9), 5756-5761; Kim et al. Nano Lett. 2015, 5574-5579; Llordes et al. Nat. Mater. 2016, 15 (12), 1267-1273) to solar devices (Le Viet et al. J. Phys. Chem. C 2010, 114(49), 21795-21800; Chen et al. Chem. Mater. 2001, 13(12), 4629-4634; Ou et al. ACS Nano 2012, 6(5), 4045-4053) and chemical sensors (Kadir et al. Sensors Actuators, B Chem. 2014, 202, 74-82; Dai et al. Adv. Mater. Interfaces 2015, 2(11), 1500167; Ab Kadir et al. ACS Appl. Mater. Interfaces 2015, 7(8), 4751-4758). The development of these technologies is enabled by the combination of optical, electronic, and electrochemical properties of niobium oxide such as a wide band gap, high dielectric constant, medium to high refractive index, and fast Li.sup.+ transport (Gotrik et al. ACS Nano 2012, 6 (9), 8052-8059; Rani et al. Journal of Materials Chemistry A 2014, 2(38), 15683-15703; Schafer et al. Angew. Chemie Int. Ed. English 1966, 5 (1), 40-52). As an electrochromic material, niobium oxides are one of the oldest known comparable to tungsten oxide. The coloration is attributed to the intercalation of Li.sup.+ into the niobium oxide lattice accompanied by the reduction of niobium oxide expressed in the formula below (Equation 1).
Nb.sub.2O.sub.5+xLi.sup.+═Li.sub.xNb.sub.2O.sub.5 Equation (1)
[0304] While the intercalative mechanism remains the same, the electrochromic properties of the various phases of niobium oxide and their amorphous counterpart varies significantly. The first observable distinction is a difference in coloration upon Li.sup.+ intercalation: brown for amorphous niobium oxide and blue for crystalline niobium oxide. This phenomenon can be because amorphous niobium oxide absorbs with two distinct bands at 440 and 620 nm while crystalline niobium oxide absorbs with just one absorption band at 700 nm (Fu et al. J. Electrochem. Soc. 1999, 146 (10), 3914). Additionally, the observable coloration transitions from the visible to the near-infrared when the crystallite size exceeded 30 nm (Schmitt et al. Electrochim. Acta 2001, 46 (13-14), 2105-2111). Beyond coloration, electrochromic parameters like the magnitude of optical modulation, coloration efficiency, durability, and kinetics also differ between crystalline and amorphous niobium oxide: crystalline niobium oxide switches faster and is more durable than amorphous niobium oxide (Fu et al. J. Electrochem. Soc. 1999, 10(146), 3914-3918: Yoshimura et al. J. Electrochem. Soc. 1997, 144 (9), 2982; Reichman et al. J. Electrochem. Soc. 1980, 127 (1), 241; Ohtani et al. J. Electrochem. Soc. 1994, 141 (9), 2439). However, systematic study of these phenomena for the niobium oxide system is impeded by the incongruence between typical heat up synthetic protocols and the complex niobium oxide phase diagram (Naito et al. Solid State Ionics 1984, 12, 125-134; Naito et al. J. Solid State Chem. 1980, 35 (3), 305-311): heat up processes can often yield trace impurity phases as thermal cycles transition across different regions of the phase diagram.
[0305] Colloidal nanocrystal synthesis is an effective way to impose strict dimensional and phase control on materials and has been applied extensively to a variety of nanocrystal systems including metal nanoparticles (Gilroy et al. Chem. Rev. 2016, 116 (18), 10414-10472), metal oxides (Wang et al. Chem. Mater. 2014, 26 (22), 6328-6332; Dinh et al. ACS Nano 2009, 3 (11), 3737-3743; Gordon e al. Nano Lett. 2013, 13 (6), 2857-2863), doped metal oxides, and metal chalcogenides (Felice Shieh et al. J Phys Chem B 2005, 109(18), 8538-8542). Specific to the niobium oxide system, a reported method has shown the potential to control shape and phase of the resultant nanocrystals using seeded growth and high temperature thermal decomposition of niobium oleate to synthesize niobium oxide (Jana et al. Nanoscale 2012, 4 (5), 1782). This is a step towards the development of colloidal synthesis methods that yield size controlled and phase pure niobium oxide materials. However, a mechanistic understanding of the synthetic process was not elucidated, and the influence of nanostructuring through colloidal synthesis on the resulting properties compared to bulk niobium oxide systems remains to be investigated.
[0306] A mechanistic study of the synthesis of niobium oxide nanorods that is derived from the aminolysis of niobium oleate is discussed herein and the utility of the nanorods as an electrochromic material is demonstrated. The synthesis was developed to promote nanorod formation at significantly lower temperatures to sidestep agglomeration difficulties present in prior syntheses thus enabling the solution-based processing of these nanorods into thin films. Using a combination of microscopy, X-ray diffraction, and infrared, nuclear magnetic resonance, and Raman spectroscopy analysis, the mechanism underlying the nanorod formation was elucidated; the mechanism starts with the in situ formation of a chloro oleyl niobium (V) complex followed by the formation of amorphous niobium oxide seeds that then crystallize into orthorhombic niobium oxide (Nb.sub.2O.sub.5) nanorods. The electrochromic properties of nanorod thin films was then investigated and core electrochromic characteristics of the nanorod thin films, such as their coloration behavior, cyclic stability, and kinetics, is discussed. Unlike prior reports on the electrochromism of niobium oxides that are centered on electrochromic modulation in the visible regime, these films exhibit electrochromism that is predominantly in the infrared with a significantly diminished visible electrochromic response. This difference can be attributed to the dimensional constraint of the nanorod shape in the radial direction inhibiting the polaronic coloration of niobium oxide in the visible regime while maintaining the infrared red polaronic response.
[0307] Experimental Section
[0308] Materials. All chemicals were used as received and without further purification. Niobium chloride (NbCl.sub.5, 99%), oleic acid (technical grade, 90%), 1-octadecene (technical grade, 90%), N,N-dimethylformamide (ACS reagent, ≥99.8%), nitrosonium tetraborofluorate (95%), acetonitrile (ACS reagent, ≥99.5%), tetraethylene glycol dimethyl ether (tetraglyme, ≥99%), tetrabutylammonium bistrifluoromethanesulfonimidate (TBATFSI, ≥99.0%) were purchased from Sigma Aldrich. Oleylamine (C-18 content 80-90%) was purchased from Acros Organics. Toluene (≥99.5%) and hexane (ACS reagent, various methylpentanes 4.2%, ≥98.5%) were purchased from Fisher Scientific. Lithium bis(trifluoromethanesulfonyl)imide (LiTFSI, 3M Fluorad) was purchased from 3M.
[0309] Nanorod synthesis. The synthesis of Nb.sub.2O.sub.5 nanorods is based on established colloidal synthesis methods. The reaction mixture was prepared in a nitrogen glovebox and kept in an air-free environment while it was transferred to the Schlenk line. Briefly, 0.545 g (2 mmol) NbCl.sub.5 was mixed with 3.127 g (11 mmol) of oleic acid and 10 g (40 mmol) of octadecene. The reagents were stirred at room temperature under nitrogen until NbCl.sub.5 was fully dissolved and a blood red solution of chloro oleyl niobium (V) was formed. This solution was degassed at 120° C. for 30 minutes. Then, a mixture of oleylamine (0.534 g or 2 mmol) and octadecene (0.789 g) was injected into the reaction flask at 120° C. under nitrogen. After the injection, the solution was degassed at 120° C. for 15 min, heated to 240° C., and allowed to react for 30 min under nitrogen. Once the solution cooled down to 70° C., 7.5 mL of toluene was injected into the flask to dilute the mixture. The nanorods were recovered and purified by precipitating with isopropanol, centrifuging at 3500 rpm for ten minutes, and re-dispersing in toluene. This step was repeated two more times.
[0310] Ligand-stripping. The native organic ligands on the nanorod surface were stripped following a method established previously (Dong et al. J. Am. Chem. Soc. 2011, 133 (4), 998-1006). In a typical procedure, 5 mg of nitrosonium tetrafluoroborate was added to a mixture containing 1 mL of a 5 mg/ml nanorod dispersion and 1 mL of N, N-dimethylformamide (DMF). This solution was sonicated for 30 min and then left to settle to allow the nanorods to precipitate. The nanorods were then dispersed in 1 mL of DMF. This dispersion was mixed with an equal volume of hexane, shaken, and left to settle to remove the top hexane layer. This step was repeated three times. Finally, the nanorods were purified by performing five cycles of flocculation with toluene, centrifugation at 4000 rpm for five minutes, and re-dispersion in DMF.
[0311] Thin film deposition. Ligand-stripped nanorods were dispersed in 1:1 mixture of DMF and acetonitrile (30 mg/ml) and spin-coated at 1250 rpm on fluorine-doped tin oxide (FTO)-coated glass substrates.
[0312] Electron microscopy. Electron microscopy was performed on a Hitachi 55500 SEM/STEM instrument. Nanorods were imaged in bright-field scanning transmission electron (STEM) mode at a 30 kV accelerating voltage. Samples were dropcasted on Type-A ultrathin carbon copper TEM grids (Ted Pella, 01822, 400 mesh) from dilute nanorod dispersions in toluene. Nanorod films deposited on silicon substrates were imaged in scanning electron (SEM) mode at a 30 kV accelerating voltage.
[0313] X-ray diffraction (XRD). Powder diffraction patterns were collected on a Rigaku R-Axis Spider using Cu K.sub.α radiation (1.54 Å). Powders were obtained by precipitation from solution with isopropanol, centrifugation at 7000 rpm for five minutes, and drying under vacuum for 24 hours. Samples were mounted on a cryoloop using mineral oil.
[0314] Raman spectroscopy Raman spectroscopy was performed with a Horiba LabRAM HR Evolution instrument equipped with a confocal microscope. Spectra were collected using a 532 nm laser source, 50 mW power, 50× objective, and 1 μm laser spot size. Powder samples were identical to the ones prepared for X-ray diffraction measurements. The bulk orthorhombic Nb.sub.2O.sub.5 powder used as a reference in
[0315] Fourier transform infrared spectroscopy (FTIR). FTIR spectroscopy was carried out in transmission geometry with a 4 cm.sup.−1 resolution and an average of 128 scans on a Bruker Vertex 70 spectrometer. Chloro oleyl niobium (V) samples were transferred into a sealed liquid cell with KBr windows and a 0.0125 mm path length under inert conditions. Ligand-capped and ligand-stripped nanorod films were spin-coated on 1×1 cm undoped silicon substrates.
[0316] Nuclear magnetic resonance spectroscopy (NMR). NMR spectroscopy was performed on an Agilent 400 MHz instrument using a OneNMR probe with Protune accessory. The .sup.1H NMR was taken in a range of −2 to 14 ppm with 128 scans and a relaxation delay of 2 secs with a pulse angle of 30 degrees. The samples were prepared under an inert atmosphere and diluted into d-DMSO (10 μL, 600 μL).
[0317] Spectroelectrochemical Modulation. In situ spectroelectrochemical measurements were performed using a custom-built cell in an Ar glovebox connected to a potentiostat (Bio-logic VMP3) and a spectrometer (ASD Quality Spec Pro). A three-electrode configuration was used in a typical experiment: Li foil (MTI) was both the counter and reference electrode, and the nanorod film on FTO-coated glass was the working electrode. The transmittance of the nanorod film immersed in Li-TFSI in anhydrous tetraglyme electrolytes of varying concentrations (0.1 M, 1 M, and 3 M) was recorded as a function of wavelength at each applied potential (1.2 and 4.0 V vs. Li/Li.sup.+ for charging and discharging, respectively). This setup was also used to conduct cyclic voltammetry, cycling stability, and coloration efficiency experiments, Spectroelectrochemical experiments with the nonintercalating 1 M TBATFSI in tetraglyme electrolyte were also performed using a three-electrode configuration, but in this case, Pt foil was the counter electrode, non-aqueous Ag/Ag.sup.+ was the reference electrode, and the nanorod film on FTO-coated glass was the working electrode.
[0318] X-ray Photoelectron Spectroscopy (XPS). XPS was carried out with a Kratos X-ray photoelectron spectrometer-axis ultra DLD using Al Kα source. Samples were identical to the nanorod films spin-coated on FTO for spectroelectrochemical modulation.
[0319] Zeta potential. Zeta potential measurements of the ligand-stripped Nb.sub.2O.sub.5 nanorods dispersed in dimethylformamide (˜1 mg/ml) were conducted on a Malvern Zetasizer Nano ZS. A dip cell (ZEN1002, Malvern) was immersed in the dispersion, which was contained in a glass cuvette.
[0320] Galvanostatic intermittent titration technique (GITT). The same custom-built cell and three-electrode configuration described above was used to perform the galvanostatic intermittent titration technique experiment. Briefly, Li foil (counter and reference electrode) and the Nb.sub.2O.sub.5 nanorod film on fluorine-doped tin oxide (FTO)-coated glass (working electrode) were immersed in 1 M LiTFSI in tetraglyme electrolyte in a near-infrared quartz cuvette. Before performing the galvanostatic intermittent titration technique experiment, the film was bleached by applying 4.0 V for 5 min, colored by applying 1.2 V for min, and allowed to rest at open circuit voltage (OCV) for 5 min to determine the leakage current (−5 μA). The first galvanostatic intermittent titration technique sequence consisted of gradually discharging the film by withdrawing +15 μA every 1 s for 1 min and equilibrating at open circuit voltage for 44 min. This step was repeated until the working electrode potential reached 4.0 V (
[0321] Reflection measurement of Nb.sub.2O.sub.5 nanorod film. In situ reflectance and transmittance measurements were carried out in the same custom-built spectroelectrochemical cell and with the same three-electrode configuration described above. Briefly, Li foil (counter and reference electrode) and the Nb.sub.2O.sub.5 nanorod film on fluorine-doped tin oxide (FTO)-coated glass (working electrode) were immersed in 1 M LiTFSI in tetraglyme electrolyte in a near-infrared quartz cuvette. A constant potential was applied using a 5200 Biologic potentiostat while the film was illuminated with a white light source at a 75° incident angle. Reflectance and transmittance spectra were obtained by changing the detector position relative to the incident light and keeping the light source and film positions fixed. In the reflection configuration, the detector was placed at a 30° angle while in the transmission configuration, the detector was placed at a 180° angle. A bare glass substrate was used as the background in the transmission configuration while a silver mirror (Thorlabs, PFR10-P01) was used as the background in the reflection configuration. First, the film was bleached by applying 4.0 V for 5 min, then colored by applying 1.2 V for 10 min, and finally bleached again by applying 4.0 V for 5 min.
[0322] Optical spectra of colored Nb.sub.2O.sub.5 nanorods in different dielectric environment. First, the nanorod film was bleached by applying 4.0 V for 5 min and subsequently charged by applying 1.2 V for 5 min using the same custom-built cell and three-electrode configuration described above. Then, the colored nanorod film was rinsed with dimethylcarbonate to remove excess 1M LiTFSI in tetraglyme electrolyte. The colored film and bare glass substrate were clipped to the near-infrared quartz cuvette using binder clips covered with insulating and solvent-resistant kapton tape to avoid discharging the film and to ensure consistent backgrounding after each solvent exchange. Solvent was dripped onto the colored film and the cuvette three times to fully exchange the dielectric environment before recording transmittance spectra in the pure solvent.
[0323] Results and Discussion
[0324] The design of the one-pot colloidal synthesis of niobium oxide began with a well-established starting point for the synthesis of many metal oxides: the decomposition of a metal carboxylate, specifically a metal oleate (Yu et al. Chem. Commun. 2004, 356 (20), 2306; Kim et al. J. Am. Chem. Soc. 2011, 133 (32), 12624-12631; Park et al. Nat. Mater. 2004, 3 (12), 891-895). Thermal decomposition of the metal oleate, formed in situ through a reaction of niobium (V) chloride with oleic acid, required high temperatures exceeding 270° C. (Jana et al. Nanoscale 2012, 4 (5), 1782). The synthesis yielded nanorods that were, however, irreversibly aggregated (
[0325] To uncover the underlying synthetic mechanism, an aliquot study was performed on the reaction starting from the formation of the metal oleate complex to the final formation of the nanorods at the end of the synthesis: the results were analyzed with a combination of electron microscopy (STEM), Raman, XRD, NMR, and FTIR spectroscopy. True to the synthetic design, FTIR and NMR show formation of a metal oleate complex upon mixing of niobium (V) chloride and oleic acid in octadecene (
[0326] After the limited aminolysis reaction, the mechanism progresses through three distinct steps (
[0327] One benefit of this lower temperature aminolysis-based synthesis of niobium oxide nanorods is their colloidal stability for the casting of functional thin films. In order to process the nanorods into switchable electrochromic thin films, a strategy similar to that used on tungsten oxide nanorods was employed to yield ligand-free colloidal dispersions that can be spin coated as films on transparent conducting oxide FTO coated glass (Heo et al. Nano Lett. 2017, 17 (9), 5756-5761). Briefly, the as-synthesized nanorods were ligand stripped in solution with a nitrosonium tetrafluoroborate procedure that leaves the surface positively charged and free of its native insulating layer. This electrostatically stabilized surface enables repulsion between nanorods to promote disordered packing and yield porous thin films. The procedure was discussed in detail in the previous paper and is summarized in the Experimental section. The step-by-step characterization of the process is described above (
[0328] Unlike prior reports of crystalline niobium oxide electrochromism that extends from the visible regime to the near-infrared, these niobium oxide nanorod films exhibit an electrochromic response that is predominantly in the infrared upon application of a reducing potential (
[0329] One finding in this study is the anomalous electrochromic behavior of these nanorod films. Unlike prior reports on niobium oxide electrochromism where amorphous systems demonstrate a predominantly visible response and crystalline systems demonstrate a response across the visible and infrared regime, these nanorod films show an electrochromic response predominantly in the near infrared. Prior studies have suggested that the visible response is dependent on polaronic coloration intrinsic to the niobium oxide system while the infrared response may arise from Drude reflection upon electrochemical reduction of the system (Schmitt et al. Electrochim. Acta 2001, 46 (13-14), 2105-2111). To shed light on the origins of coloration, a series of experiments were performed to test i) the role of Li.sup.+ intercalation and reduction of Nb.sup.5+, ii) the emergence of Drude reflection or a local surface plasmon resonance upon charging, and iii) the possible extinguishing of the polaronic visible mode due to dimensional constraint.
[0330] First, films of niobium oxide nanorods were tested with a different electrolyte of non-intercalating TBA-TFSI in tetraglyme. As shown in
[0331] Next, air-free XPS was conducted on as-prepared niobium oxide films and Li.sup.+ intercalated films to determine the oxidation state of niobium in the film post-electrochemical charging. Shown in
[0332] Next, the second possibility that an increase in free electrons in the system contributes a metallic Drude reflection in the infrared regime or a localized plasmon resonance in the case of a nanocrystal film was investigated. To test these hypotheses, the transmission spectra was deconvoluted into its constitutive reflection and absorption components.
[0333] Finally, it is only by deconvoluting the Raman spectra of the niobium oxide nanorods and comparing it to the bulk counterpart that a plausible explanation for this anomalous behavior was obtained (
TABLE-US-00001 TABLE 1 Results of fitting for Niobium oxide nanorod Raman Amp Area FWHM Peak Type Location Amplitude Sigma Area Sigma FWHM Sigma 0.00 Gauss 132.93 5927.93 61.38 126332 1334.28 20.02 0.24 1.00 Gauss 232.18 2186.85 49.51 148936 4591.97 63.98 1.38 2.00 Gauss 293.05 3554.11 37.12 490427 10018.90 129.63 1.83 3.00 Gauss 687.77 13245.9 48.00 1934940 7668.62 137.23 0.42 4.00 Gauss 559.03 5047.70 29.17 1441820 12471.40 268.34 2.92 5.00 Gauss 718.45 23557.20 48.11 1311040 4353.65 52.28 0.13 6.00 Gauss 805.47 4992.78 33.29 1427970 7292.39 268.69 1.53
TABLE-US-00002 TABLE 2 Results of fitting for Niobium oxide reference Raman Amp Area FWHM Peak Type Location Amplitude Sigma Area Sigma FWHM Sigma 0.00 Gauss 123.87 5273.41 54.17 234795 2693.50 41.83 0.59 1.00 Gauss 232.18 10927.70 49.61 638831 3285.79 54.92 0.29 2.00 Gauss 305.52 6673.86 41.62 506858 3814.52 71.35 0.63 3.00 Gauss 388.04 842.51 60.34 26742.5 2211.23 29.82 2.75 4.00 Gauss 463.59 1662.10 72.43 86213.7 5352.46 48.73 2.04 5.00 Gauss 536.20 4894.44 53.53 448384 10129.50 86.06 1.86 6.00 Gauss 616.89 12140.90 113.35 1058110 12224.00 81.87 0.59 7.00 Gauss 687.76 29102.6 117.58 2563090 17259.70 82.74 0.30 8.00 Gauss 718.82 6578.66 123.87 505271 12855.10 72.15 0.83 9.00 Gauss 805.47 7794.93 39.24 1098970 10372.60 132.45 1.34 10.00 Gauss 925.03 2110.20 50.19 223553 6320.48 99.52 2.05
[0334] From the comparison (
[0335] Conclusion
[0336] In summary, the colloidal synthesis of niobium oxide nanorods through the aminolysis of a chloro oleyl niobium (V) complex was demonstrated to yield colloidally stable nanorods that can be further processed into electrochromic thin films. The synthesis proceeds through the initial formation of niobium oxo clusters through the aminolysis of chloro oleyl niobium (V) species, condensation to form small amorphous niobium oxide seeds, and final crystallization at elevated temperatures to yield high aspect ratio nanorods. These materials, when tested as solution deposited films, exhibit properties comparable to sputter coated niobium oxide thin films with the exception of electrochromic coloration that is predominantly in the near infrared. Further investigation of this phenomenon revealed that both the visible and infrared coloration for orthorhombic niobium pentoxide are triggered by polaronic responses that are associated strongly to specific crystalline directions. The synthesis of an anisotropic nanocrystal, that has a width approximately equal to or smaller than the a and b dimensions of one unit cell, can affect the accessibility of phonon modes that support polaronic absorption in the visible range upon charging. Further studies to elucidate the specific link between various phonon modes and coloration behavior in niobium oxide systems are in preparation. More broadly, this study demonstrates how the dimensional control through colloidal nanocrystal synthesis can be exploited to tune the properties of traditional electrochromic materials, such as niobium oxide, as well as open a new opportunity to study the physics that underlie the optical response of these materials.
Example 5
[0337] The colloidal synthesis of anisotropic niobium oxide nanocrystals (Nb.sub.2O.sub.5-x NCs), enabling phase control between their monoclinic and orthorhombic phases, is discussed herein. The anisotropic monoclinic Nb.sub.12O.sub.29 nanocrystals (am-Nb.sub.12O.sub.29 NCs), possessing a two-dimensional nanoplatelet morphology with ˜95 nm in long axis and ˜9 nm in short axis, are the first successful synthesis of monoclinic Nb.sub.2O.sub.5-x nanocrystals. X-ray diffraction and simulations confirmed the anisotropic monoclinic Nb.sub.12O.sub.29 nanocrystals are monolayer materials with preferential elongation along the [011] crystallographic direction. The anisotropic nature of the anisotropic monoclinic Nb.sub.12O.sub.29 nanocrystals led to reduced abundance of Nb═O terminal bonds in their local structure, as indicated by both experimental and simulated Raman spectra. Phase control was achieved by manipulating the chemistry of the niobium precursors used to initiate the nanocrystal growth, with niobium chloro oleate favoring the growth of the orthorhombic phase, while the niobium oxo clusters favored the growth of the monoclinic phase. The anisotropic monoclinic Nb.sub.12O.sub.29 nanocrystals showed a dual-mode electrochromism: the first step was dominated by capacitive charging, leading to increased concentration of delocalized electrons and absorption in near-infrared region, and the second step was dominated by ion intercalation, leading to generation of localized electrons and absorption in visible region. These results can promote the synthetic development and applications of Nb.sub.2O.sub.5-x nanocrystals, as shown in the dual-mode electrochromism of anisotropic monoclinic Nb.sub.12O.sub.29 nanocrystals for independently controlling the solar spectrum in electrochromic smart windows.
[0338] Introduction
[0339] Niobium(V) oxide (Nb.sub.2O.sub.5-x) displays rich polymorphic forms with diverse electronic and optical properties which have made it attractive for applications in catalysts, electrochromics, batteries, and sensors (Nowak et al. Chem. Rev. 1999, 99 (12), 3603-3624; Rani et al. J. Mater. Chem. A 2014, 2 (38), 15683-15703). Especially in electrochromics (materials modulating their optical properties electrochemically in response to an external potential), bulk Nb.sub.2O.sub.5-x crystals have drawn interest due to their tunable optical modulation across visible and near-infrared (NIR) regions (Yoshimura et al. Thin Solid Films 1996, 281-282, 235-238; Schmitt et al. Sol. Energy Mater. Sol. Cells 1998, 54 (1), 9-17), as well as because of their stability, which can be due to minimal change in their crystal structure during ion intercalation and their large band gap (˜3.8 eV) (Kumagai et al. J. Electrochem. Soc. 1999, 146 (9), 3203-3210; Le Viet et al. J. Phys. Chem. C 2010, 114 (49), 21795-21800).
[0340] Upon being coated on windows, electrochromics can be used to modulate the incident solar spectrum to gain better energy management (Wang et al. Annu. Rev. Chem. Biomol. Eng. 2016, 7 (1), 283-304). However, bulk Nb.sub.2O.sub.5-x crystals have had limited success when compared to the state-of-the-art electrochromics, tungsten oxide nanocrystals (WO.sub.3-x NCs), due to their relatively poor coloration efficiency and switching kinetics (Wang et al. Annu. Rev. Chem. Biomol. Eng. 2016, 7 (1), 283-304; Runnerstrom et al. Chem. Commun. 2014, 50 (73), 10555-10572; Mjejri et al. ACS Appl. Energy Mater. 2018, 1 (8), 4359-4366; Yao et al. J. Phys. Chem. C 2014, 118 (1), 476-481). Nanostructuring of WO.sub.3-x has benefited its switching kinetics and yielded the ability to support both ion intercalation electrochromism, associated with polaronic absorption, and capacitive charging electrochromism, associated with localized surface plasmon resonance (LSPR) (Runnerstrom et al. Chem. Commun. 2014, 50 (73), 10555-10572). Nanostructuring of WO.sub.3-x has also given rise to instability due to irreversible ion intercalation and their small band gap (˜2.6 eV) (Balaji et al. Chem. Mater. 2009, 21 (7), 1381-1389; Wang et al. Chem. Mater. 2016, 28 (20), 7198-7202). In this regard, the synthesis of Nb.sub.2O.sub.5-x nanocrystals, which has been treated in various techniques but only obtained limited control, is explored herein for the purpose of promoting Nb.sub.2O.sub.5-x nanocrystals as an alternative material for electrochromics to access the stability in their bulk form and the benefits of nanostructuring. The common phases of crystalline Nb.sub.2O.sub.5-x are pseudohexagonal, orthorhombic, and monoclinic, which can be obtained by crystallizing amorphous Nb.sub.2O.sub.5-x in an elevated temperature (Nowak et al. Chem. Rev. 1999, 99 (12), 3603-3624). The first two phases are structurally similar, with the pseudohexagonal phase being less crystalline. In the monoclinic phase, niobium oxygen octahedra (NbO.sub.6 octahedra) sharing vertex are arranged in blocks (or shears) and share edges with NbO.sub.6 octahedra in other blocks at different levels, which is also referred as a Wadsley-Roth structure with parallel crystallographic shear planes (Wadsley et al. Eds.; John Wiley & Sons: Chichester, 1970; Vol. 3, p 14). This structure forms a variety of compounds that have attracted interest due to their large capacity in storing Li.sup.+ ions (Cava et al. J. Electrochem. Soc. 1983, 130 (12), 2345-2351; Griffith et al. Nature 2018, 559 (7715), 556-563; Li et al. Chem. Mater. 2011, 23 (9), 2292-2294). In particular, the change of electronic properties when stoichiometric monoclinic Nb.sub.2O.sub.5 (m-Nb.sub.2O.sub.5) is chemically reduced into nonstoichiometric monoclinic Nb.sub.12O.sub.29 (m-Nb.sub.12O.sub.29), with additional electrons being populated into the conduction band of monoclinic Nb.sub.12O.sub.29 giving rise to its metallic conduction, are of interest (Cava et al. Phys. Rev. B 1991, 44 (13), 6973-6981; Koçer et al. Phys. Rev. B 2019, 99 (7), 075151). This triggers attention to whether the nanocrystals of monoclinic Nb.sub.12O.sub.29 are able to accommodate electrons in their conduction band during electrochemical reduction to instigate the capacitive charging electrochromism that was not reported for Nb.sub.2O.sub.5-x electrochromics.
[0341] Crystalline Nb.sub.2O.sub.5-x has been prepared by sol-gel methods (Özer et al. Thin Solid Films 1996, 277 (1), 162-168), solvothermal methods (Ali et al. Cryst. Growth Des. 2017, 17 (9), 4637-4646; Lopes et al. Appl. Catal. B: Environ. 2014, 144, 800-808), and vapor deposition methods (Yoshimura et al. Thin Solid Films 1996, 281-282, 235-238; Masse et al. Thin Solid Films 2006, 515 (4), 1674-1682). In the sol-gel method, amorphous Nb.sub.2O.sub.5-x sols are crystallized by high temperature annealing; the sol-gel method is widely used in preparing Nb.sub.2O.sub.5-x electrochromics but lacks precise control and the accessibility of monoclinic phase that only stabilizes at ˜1100° C. (Nowak et al. Chem. Rev. 1999, 99 (12), 3603-3624). In contrast, solvothermal synthesis involves the direct crystallization of Nb.sub.2O.sub.5-x using various Nb ions and solvents to interact with in a moderate temperature to obtain different nanostructures, thus circumventing the high temperature annealing. However, these solvothermal syntheses include a wide range of procedures without systematic investigation to understand the synthetic mechanism. In addition, most crystals made using these solvothermal syntheses are polydisperse with submicron size and arranged only into pseudohexagonal and orthorhombic phases.
[0342] Colloidal synthesis has met great success in synthesizing monodisperse and phase pure colloidal nanocrystals with tight control over their morphology, stoichiometry, and crystal phase (Agrawal et al. Chem. Rev. 2018, 118 (6), 3121-3207; Rosi et al. Chem. Rev. 2005, 105 (4), 1547-1562; Tao et al. Small 2008, 4 (3), 310-325). This method involves direct crystallization of colloidal nanocrystals in a nonaqueous environment by controlling the nucleation and growth of metal ions down to near-atomic precision, therefore enabling an incremental investigation of how metal ions progress into clusters, then eventually into nanocrystals (Hyeon et al. J. Am. Chem. Soc. 2001, 123 (51), 12798-12801). In the field of colloidal metal oxide nanocrystals, the syntheses of iron, titanium, and indium oxides have reached excellent control and synthetic understanding using a route wherein a metal oleate is used as a precursor and subsequent alcoholysis or aminolysis reactions produce nanocrystals (Agrawal et al. Chem. Rev. 2018, 118 (6), 3121-3207; Hyeon et al. J. Am. Chem. Soc. 2001, 123 (51), 12798-12801; Jansons et al. ACS Nano 2016, 10 (7), 6942-6951; Buonsanti et al. J. Am. Chem. Soc. 2008, 130 (33), 11223-11233). Variation in the crystal structure and morphology of nanocrystals can be achieved by synthetic control, for instance, the phase control between anatase and brookite TiO.sub.2 nanocrystals (Buonsanti et al. J. Am. Chem. Soc. 2008, 130 (33), 11223-11233). Colloidal synthesis of Nb.sub.2O.sub.5-x nanocrystals is not well established, with only one example demonstrating the synthesis of tetragonal NbO.sub.2 nanorods and tetragonal Nb.sub.2O.sub.5 nanoplatelets using amorphous niobium oxide seeds to initiate nanocrystal growth at different temperatures (Jana et al. Nanoscale 2012, 4 (5), 1782-1788). Hence, development of a colloidal synthesis to produce Nb.sub.2O.sub.5-x nanocrystals and understanding of the synthetic mechanism as a general guide for the synthetic development of Nb.sub.2O.sub.5-x nanocrystals is needed.
[0343] Herein, the colloidal synthesis of Nb.sub.2O.sub.5-x nanocrystals enabling direct crystallization and phase control between the anisotropic monoclinic Nb.sub.12O.sub.29 nanocrystals (am-Nb.sub.12O.sub.29 NCs) and the anisotropic orthorhombic Nb.sub.2O.sub.5 nanocrystals (ao-Nb.sub.2O.sub.5 NCs) is demonstrated. The anisotropic monoclinic Nb.sub.12O.sub.29 nanocrystals, being the first reported monoclinic Nb.sub.2O.sub.5-x nanocrystals, were characterized by electron microscopy, X-ray diffraction, and Raman spectroscopy to demonstrate their anisotropy, which brings structural anomaly as compared to their bulk counterparts, along with simulations to support this argument. Investigation of the synthetic mechanism revealed that the chemistry of the niobium precursors used to initiate nanocrystal growth, which varied between niobium chloro oleate and niobium oxo clusters, determined the crystal phase of the nanocrystals. In terms of electrochromism, the anisotropic monoclinic Nb.sub.12O.sub.29 nanocrystals exhibited dual-mode electrochromism: a capacitive charging process that leads to the absorption of near-infrared (NIR) light and an ion intercalation process that leads to the absorption of visible light, as investigated by the presence of localized electrons following electrochemical charging in ex situ X-ray photoelectron spectroscopy together with observations of electrochemical kinetics in determining whether ion intercalation occurs.
[0344] Experimental Section
[0345] Materials. Toluene (>99.5%), hexane (>99%), isopropanol (>99.5%), N,N-dimethylformamide (DMF, anhydrous 99.8%), nitrosonium tetrafluoroborate (NOBF.sub.4, 95%), tetrabutylammonium bis(trifluoromethanesulfonyl)imide (TBA-TFSI, >99.0%), oleic acid (OA, 90%), niobium chloride (NbCl.sub.5, anhydrous, 99.995%), tetraethylene glycol dimethyl ether (TG, >99%), 1-octadecene (ODE, 90%) and chloroform-d (CDCl.sub.3, 99.96 atom % D) were purchased from Sigma-Aldrich. Oleylamine (OM, 90%) was purchased from Acros Organics. Lithium bis(trifluoromethanesulfonyl)imide (Li-TFSI, HQ-115) was purchased from 3M. oleic acid and oleylamine were degassed under vacuum at 120° C. before use.
[0346] Synthesis. All reactions were carried out using standard Schlenk line techniques under a N2 atmosphere. In a typical synthesis for anisotropic monoclinic Nb.sub.12O.sub.29 nanocrystals, 0.405 g of NbCl.sub.5 (1.5 mmol) and 4.237 g of oleic acid (15 mmol) were mixed in a three-neck flask in a N2 glove box and transferred to a Schlenk line. After NbCl.sub.5 was completely dissolved and formed a blood-red solution, the mixture was then degassed under vacuum at 120° C. for 30 min. During the heating at 120° C., the blood-red color disappeared and turned into an orange solution of niobium precursor (NbP-120). Meanwhile, 11.298 g of oleic acid (40 mmol) and 2.140 g of oleylamine (8 mmol) were mixed in another three-neck flask and degassed under vacuum at 120° C. for 30 min, then heated to 300° C. Once the first flask was done degassing, the 120° C.-niobium precursor was injected into the second flask and reacted at 300° C. for 10 min Afterwards, the solution containing the nanocrystals was cooled to room temperature and washed using toluene as a solvent for dispersion and isopropanol as an antisolvent for flocculation. After being washed 3 times, the nanocrystals were dispersed in toluene at a concentration of 15 mg/ml, which is referred to as a ligand-capped nanocrystal dispersion throughout and was used throughout the characterizations if not otherwise specified. Illustration of the anisotropic monoclinic Nb.sub.12O.sub.29 nanocrystal synthesis is shown in
[0347] The synthesis that produced a mixture of both anisotropic orthorhombic Nb.sub.2O.sub.5 and anisotropic monoclinic Nb.sub.12O.sub.29 nanocrystals was performed using the same protocol as above, except the preparation of the niobium precursor was degassed at 40° C., in which a blood-red color is still remained before injection (NbP-40). Aliquots for tracking the reaction progression were collected at 2, 4, 6, 8, and 10 min after the injection, quenched in toluene, and washed as in the original synthesis.
[0348] The synthesis that produced anisotropic orthorhombic Nb.sub.2O.sub.5 nanocrystals was performed based on a previous report using a heat-up method. In brief, 0.540 g of NbCl.sub.5 (2 mmol), 3.107 g of oleic acid (11 mmol), 0.535 g of oleylamine (2 mmol) and 10.10 g of 1-octadecene (40 mmol) were mixed in a flask, degassed at 120° C., heated to 240° C. and reacted for 30 min.
[0349] Bulk monoclinic Nb.sub.2O.sub.5 crystals were prepared by annealing the 120° C.-niobium precursor at 1100° C. for 8 hr in a tube furnace under ambient condition.
[0350] X-ray Diffraction (XRD) Analysis. Nanocrystal dispersions were dried, re-dispersed in mineral oil, and mounted on a cryoloop for XRD analysis. XRD patterns were collected using a Rigaku R-Axis Spider with Cu Kα radiation with wavelength of 1.54 Å.
[0351] X-ray Diffraction (XRD) Simulation. A crystallographic information file for monoclinic Nb.sub.12O.sub.29 documented by Waldron et al. was used in the simulations herein (Waldron et al. J. Am. Chem. Soc. 2001, 123 (24), 5833-5834). The X-ray diffraction pattern of the bulk monoclinic Nb.sub.12O.sub.29 crystals was simulated using a RIETAN-FP package based on Rietveld refinement at a wavelength condition of 1.54 Å to match the experimental X-ray diffraction pattern of bulk monoclinic Nb.sub.12O.sub.29 crystals (PDF #01-073-1610).
[0352] X-ray diffraction patterns of the finite crystals were simulated based on a Debye scattering formula, in which:
where I is the scattering intensity, q (q=4π sin θ/λ) is the scattering vector, λ (1.54 Å) is the wavelength of the incident X-ray, θ is the diffraction half angle, i and j stand for the ions in the finite crystals that scatter X-ray, r.sub.ij is the distance between ions i and j, and f.sub.i and f.sub.j is the scattering factors calculated from the tabulated Cromer-Mann coefficients (Murray et al. Annu. Rev. Mater. Sci. 2000, 30 (1), 545-610).
[0353] A 3D crystal visualization program was used to obtain the position of every ion in the finite crystals, and the scattering intensity was calculated based on the scattering of all individual pairs of ions using the above equation. To simulate the anisotropy, supercells expanded along different crystallographic directions were made and named as [a×b×c]. For instance, the unit cell of monoclinic Nb.sub.12O.sub.29 was named [1×1×1], and a supercell expanded 2 times in the [100] direction (or a axis), 2 times in the [010] direction (or b axis), and 1 time in the [001] direction (or c axis) was named [2×2×1].
[0354] Raman Spectroscopy Analysis. Nanocrystal dispersions were drop-casted on microscope slides and dried for Raman analysis. Raman spectra were collected using a Horiba LabRAM Aramis instrument. Raman measurements were carried out using a ×50 microscope objective and a laser powered at a wavelength of 532 nm with acquisition time of 5 s.
[0355] Raman Spectroscopy Simulation. Simulated Raman spectra of anisotropic monoclinic Nb.sub.12O.sub.29 nanocrystals, bulk monoclinic Nb.sub.12O.sub.29 crystals, and several related structures were performed using vasp_raman.py, which utilizes the electronic structure optimization methods implemented in Vienna Ab-initio Simulation Package (VASP) (Kresse et al. Phys. Rev. B 1993, 47 (1), 558-561; Fonari et al. vasp_raman.py. https://github.com/raman-scNASP/: 2013). Structure minimization was performed with a Perdew-Burke-Ernzerhof (PBE) functional within generalized gradient approximation with on-site coulombic correction on niobium using simplified rotationally invariant approach in VASP (Perdew et al. Phys. Rev. Lett. 1996, 77 (18), 3865-3868; Dudarev et al. Phys. Rev. B 1998, 57 (3), 1505-1509). The minimized structures were studied computationally for Raman spectra by exploiting the derivatives of polarizability along each phonon mode (Llordés et al. Nat. Mater. 2016, 15, 1267). The following structures taken from Materials project were used for simulations: Nb.sub.12O.sub.29 (mp-510554), Nb.sub.2O.sub.5 (mp-776896), Nb.sub.2O.sub.5 (mp-604), and Nb.sub.2O.sub.5 (mp-1101660) (Jain et al. APL Materials 2013, 1 (1), 011002).
[0356] Spectroelectrochemical Analysis for Electrochromic Applications. Electrochemical and in situ optical properties of the nanocrystal films on FTO glass (70 S2/sq) were measured in an argon glove box using an electrochemical workstation (Bio-logic VMP3 potentiostat) and an ASD Quality Spec Pro spectrometer. In a typical measurement, a homemade two-electrode cell comprising a nanocrystal film as the working electrode, a Li foil serving as both the counter and reference electrodes, and 1 M Li-TFSI/tetraethylene glycol dimethyl ether as the electrolyte was used. The capacitive charging experiments were conducted in a homemade three-electrode cell comprising a nanocrystal film as the working electrode, a Pt foil as the counter electrode, a commercial fritted Ag/Ag.sup.+ cell as the reference electrode, and 0.1 M TBA-TFSI/tetraethylene glycol dimethyl ether as the electrolyte. The potentials (vs. Ag/Ag.sup.+) measured in the three-electrode cell were converted to the potentials (vs. Li/Li.sup.+) in the two-electrode cell by calibrating the two different cells using the same nanocrystal film. Upon dipping the nanocrystal film into the electrolytes, open-circuit potentials (OCPs) of 2.6 V (vs. Li/Li.sup.+) and −1.0 V (vs. Ag/Ag.sup.+) were recorded respectively in the two different cells.
[0357] Electron Microscopy Analysis. Nanocrystal dispersions were dropped onto carbon-coated 400 mesh copper grids (TedPella) and dried in vacuum for electron microscopy analysis. Scanning transmission electron microscopy (STEM) images were obtained using a Hitachi 55500 microscope in STEM mode. High-resolution transmission electron microscopy (HRTEM) images were obtained using a JEOL 2010F microscope. Scanning electron microscopy (SEM) images of the nanocrystal films on silicon substrates were obtained using a Hitachi 55500 microscope in SEM mode.
[0358] Ultraviolet-Visible-Near-Infrared (UV-Vis-NIR) Spectroscopy Analysis. UV-VIS-NIR spectra of the niobium precursors diluted in hexane (1:50 in volume ratio) were measured using an Agilent Cary series UV/Vis-NIR spectrophotometer.
[0359] Proton nuclear magnetic resonance (H-NMR) Spectroscopy Analysis. Niobium precursors were diluted in CDCl.sub.3 in special screw-capped NMR tubes (Norell) in a N2 glove box. H-NMR spectra were obtained in an Agilent/Varian MR-400 spectrometer operating at a field strength of 400 MHz.
[0360] Ligand Stripping of the Ligand-Capped Nanocrystals. In a typical ligand-stripping procedure, 30 mg of the ligand-capped anisotropic monoclinic Nb.sub.12O.sub.29 nanocrystals were dispersed in 3 ml of hexane and a solution of 30 mg NOBF.sub.4 dissolved in DMF was gradually added to the nanocrystal dispersion. After 30 min of stirring, the ligand-capped nanocrystals in the upper hexane layer were removed, and the ligand-stripped nanocrystals in the DMF layer were purified by performing a washing procedure 6 times using DMF as a solvent for dispersion and toluene as an antisolvent for flocculation. The ligand-stripped nanocrystals were subsequently dispersed in DMF at a concentration of 50 mg/ml and used for thin film deposition.
[0361] Fourier Transform Infrared Spectroscopy (FT-IR) Analysis. IR spectra were measured using a Bruker Vertex 70 FTIR at 4 cm.sup.−1 resolution. Samples of oleic acid and niobium precursors were drop-casted on CaF.sub.2 windows and samples of the ligand-capped and ligand-stripped nanocrystal dispersions were drop-casted on silicon substrates and dried. The measurement chamber was purged by N2 for 5 min prior to measuring to eliminate any signal from air.
[0362] Thin Film Deposition. To clean the FTO glass and silicon substrates for thin film deposition, sequential sonication was carried out in a solution of 2 vol % Hellmanex in deionized water, acetone, and isopropanol, for 30 min, respectively. After cleaning, UV-ozone treatment was performed to create a hydrophilic surface for deposition. The ligand-stripped nanocrystal dispersion (20 μl) was spin-coated at 250 rpm on the cleaned hydrophilic FTO glass. For comparison, 20 μl of the ligand-capped nanocrystal dispersion was spin-coated at 250 rpm on the cleaned hydrophobic FTO glass. Afterwards, films were dried at 150° C. for 30 min before spectroelectrochemical measurements. The resulting ligand-stripped nanocrystal films had an average thickness of 350 nm as measured by a Veeco Dektak 150 profilometer. The same deposition conditions were performed on silicon substrates for scanning electron microscopy imaging.
[0363] X-ray Photoelectron Spectroscopy (XPS) Analysis. Ligand-stripped nanocrystal films on FTO glass were immersed in 1 M Li-TFSI/tetraethylene glycol dimethyl ether and no potential (e.g., in which the sample was kept at open-circuit potential) or potentials at 2.0 V and 1.5 V were applied to different films for 5 min After that, samples were transferred in an argon-filled condition for analysis. Spectra were collected using a Kratos Axis Ultra DLD spectrometer with a monochromatic Al K.sub.α source (1486.6 eV). Wide survey scans were measured at a pass energy of 80 eV and the high-resolution scans were measured at a pass energy of 20 eV with steps of 0.1 eV. The binding energy of the spectra was referenced to the C is peak at 284.8 eV.
[0364] Results and Discussion
[0365] Morphological Characterization by Electron Microscopy. Synthetic techniques employed herein are: the hot injection of 120° C.-niobium precursor and 40° C.-niobium precursor to initiate nanocrystal growth at 300° C., and the heat-up method in which nanocrystals grow gradually during ramping temperature. The injection of 120° C.-niobium precursor lead to the formation of nanocrystals with a two-dimensional nanoplatelet morphology, as shown in scanning transmission electron microscopy (STEM) imaging (
[0366] Structural Characterization by X-ray Diffraction. The crystal structure of the as-synthesized nanocrystals was investigated by X-ray diffraction analysis, along with simulations for both bulk crystals and finite crystals. As seen in
[0367] The nanoplatelets were therefore proposed to be an anisotropic case of monoclinic Nb.sub.12O.sub.29, abbreviated as anisotropic monoclinic Nb.sub.12O.sub.29 nanocrystals (am-Nb.sub.12O.sub.29 NCs).
[0368] To investigate the anisotropy of the anisotropic monoclinic Nb.sub.12O.sub.29 nanocrystals, simulations were performed based on the Debye scattering formula, in which the intensity of the incident X-ray being scattered by every pair of ions within a finite crystal is calculated (Murray et al. Annu. Rev. Mater. Sci. 2000, 30 (1), 545-610). In
[0369] The simulations of anisotropic finite crystals were used to approach the experimental X-ray diffraction pattern of anisotropic monoclinic Nb.sub.12O.sub.29 nanocrystals (
[0370] The atomic models of the [1×1×1] unit cell and the [1×250×4] supercell used in the simulations are shown in
[0371] Structural Characterization by Raman Spectroscopy. Raman spectroscopy was used to study the structural features of niobium oxygen bonds in the as-synthesized nanocrystals, which have different Raman shifts depending on their bond order and angle. According to previous reports, these bonds can be classified in a descending bond order into Nb═O terminal bonds (950-1050 cm.sup.−1), Nb—O—Nb collinear bonds (800-900 cm.sup.−1), Nb—O—Nb bridging bonds (550-750 cm.sup.−1), ONb.sub.3 bonds (350-500 cm.sup.−1), and Nb—O—Nb angle deformation bonds (150-350 cm.sup.−1) (Llordés et al. Nat. Mater. 2016, 15, 1267; Orel et al. J. Solid State Electrochem. 1998, 2 (4), 221-236; Ikeya et al. Non-Cryst. Solids 1988, 105 (3), 243-250). In terms of structure, previous simulations demonstrated that the Nb═O terminal bonds and Nb—O—Nb collinear bonds are exclusively contributed by the vertex-shared NbO.sub.6 octahedra, while the other three modes can be either from vertex-shared NbO.sub.6 octahedra or edge-shared NbO.sub.6 octahedra (Llordés et al. Nat. Mater. 2016, 15, 1267).
[0372] In
[0373] Simulations of Raman spectra were used to identify the missing bonds in the anisotropic monoclinic Nb.sub.12O.sub.29 nanocrystals. To begin with, the simulations were performed for several structures of Nb.sub.2O.sub.5 (X—
[0374] Having assigned the structural features in the Raman spectra, the simulations were performed using the structure present in the “Simulated bulk m-Nb.sub.12O.sub.29 crystals” block in
[0375] Synthetic Mechanism Investigation. The choice of niobium precursor injected into the same reaction environment led to diverse results: the 120° C.-niobium precursor led to pure anisotropic monoclinic Nb.sub.12O.sub.29 nanocrystals, while the 40° C.-niobium precursor led to a mixture of anisotropic orthorhombic Nb.sub.2O.sub.5 and anisotropic monoclinic Nb.sub.12O.sub.29 nanocrystals. To investigate this result further, ultraviolet-visible-near-infrared spectra of the niobium precursors were recorded.
[0376] The results show that the blood-red color of 40° C.-niobium precursor is from an absorption peak centered at 445 nm (
[0377] On the other hand, the 120° C.-niobium precursor shows weak absorption in the visible and an orange color (
[0378] IR spectroscopy is useful for identifying the structure of metal ions coordinating to oleic acid molecules, namely the metal oleate, and the chemistry leading to diverse results (Buonsanti et al. J. Am. Chem. Soc. 2008, 130 (33), 11223-11233; Bronstein et al. Chem. Mater. 2007, 19 (15), 3624-3632; Cho et al. Chem. Mater. 2019, 31 (7), 2661-2676). Upon the COO.sup.− ions coordinating to metal ions, several peaks of coordinated COO.sup.− stretches (v COO) can be observed mostly located between 1480 cm.sup.−1 and 1650 cm.sup.−1 compared to the non-coordinated COO.sup.− stretches (Bronstein et al. Chem. Mater. 2007, 19 (15), 3624-3632; Cho et al. Chem. Mater. 2019, 31 (7), 2661-2676). In the FT-IR spectrum of non-coordinated oleic acid (
[0379] The formation of byproduct in both precursors were studied by IR and .sup.1H-NMR spectroscopies (
[0380] Based on the above observations, the mechanisms accounting for the formation of niobium oxo clusters in 120° C.-niobium precursor and the other byproducts shown in
[0381] Upon injecting the metal precursors into a high temperature environment, they undergo lysis and react with the protic moieties, presumably the oleylamine and the aminolysis reaction (Agrawal et al. Chem. Rev. 2018, 118 (6), 3121-3207). The bond between COO.sup.− ions and Nb.sup.5+ ions, either in the form of coordination or tightly bound onto niobium oxo clusters, will be cleaved by oleylamine, form niobium hydroxide, and subsequently condense into nanocrystals. The mechanism of nanocrystal growth was investigated by tracking the reaction progression using aliquots during the hot-injection synthesis. In the Raman spectra (
[0382] The mechanism was also investigated using scanning transmission electron microscopy images and experimental X-ray diffraction patterns of the reaction aliquots in the synthesis injecting the 40° C.-niobium precursor (
[0383] Controlling the complex of metal oleate to vary the preferred facet during nanocrystal growth was extensively investigated, with finest examples from iron oxide and titanium oxide nanocrystals (Feld et al. ACS Nano 2019, 13 (1), 152-162; Chang et al. J. Am. Chem. Soc. 2019, 141 (17), 7037-7045; Gordon et al. J. Am. Chem. Soc. 2012, 134 (15), 6751-6761). In this report, the chemistry of niobium precursors was investigated and showed that the niobium chloro oleate will preferentially deposit on the {001} facet of orthorhombic Nb.sub.2O.sub.5, and the niobium oxo clusters will preferentially deposit on the {011} facet of monoclinic Nb.sub.12O.sub.29.
[0384] Influence of Ligand Stripping. The presence of bulky capping ligands on the surface of nanocrystals are considered to block the ion/electron transport at the nanocrystal-to-nanocrystal or nanocrystal-to-electrolyte interfaces (Dong et al. J. Am. Chem. Soc. 2011, 133 (4), 998-1006; Kim et al. ACS Nano 2018, 12 (4), 3200-3208). In this regard, a method for stripping the oleic acid molecules capped on the anisotropic monoclinic Nb.sub.12O.sub.29 nanocrystals was developed based on a reported protocol using NOBF.sub.4 (Dong et al. J. Am. Chem. Soc. 2011, 133 (4), 998-1006). The FT-IR spectra of the ligand-capped and ligand-stripped anisotropic monoclinic Nb.sub.12O.sub.29 nanocrystals show that the intensity of C—H stretches are significantly reduced after ligand stripping (
[0385] Spectroelectrochemical Characterization. The anisotropic monoclinic Nb.sub.12O.sub.29 nanocrystals were ligand-stripped to remove the insulating oleic acid molecules on their surface before electrochemical measurement. The ligand-stripped anisotropic monoclinic Nb.sub.12O.sub.29 nanocrystal films were electrochemically reduced by using two different cations for charge balance, small Li.sup.+ ions for both ions intercalating into the nanocrystal lattice and being adsorbed on the nanocrystal surface as electrical double layer capacitance, and bulky TBA.sup.+ ions for only the adsorbed process (Dahlman et al. J. Am. Chem. Soc. 2015, 137 (28), 9160-9166). In
[0386] In a previous report using Li.sup.+ ions for charge balance, the reduction of Nb-doped TiO.sub.2 nanocrystal films populates both delocalized electrons into the conduction band of nanocrystals and localized electrons into the self-trapped states between the valence and conduction band, referred to as polarons, while using a TBA-based electrolyte will contribute to delocalized electrons only (Dahlman et al. J. Am. Chem. Soc. 2015, 137 (28), 9160-9166). These two processes were distinguished by the optical response of nanocrystal films: delocalized electrons will give rise to the plasmonic absorption residing in NIR region, and the localized electrons will give rise to the polaronic absorption in visible region. It was hypothesized for the optical modulation in anisotropic monoclinic Nb.sub.12O.sub.29 nanocrystal films in a Li-based electrolyte that the first mode, ranging from open-circuit potential to 2.0 V, is a capacitive charging process with increasing concentration of delocalized electrons that gives rise to the plasmonic absorption in NIR region. The second mode, ranging from 2.0 V to 1.5 V, involves both the ion intercalation process with electrons being localized and giving rise to the polaronic absorption in visible region, and the previous capacitive charging process as well. When using TBA.sup.+ ions for charge balance, ions intercalating into the nanocrystal lattice is forbidden due to their bulky nature, and therefore the absorption mostly resides in NIR region because of capacitive charging and shares the same peak position with the first mode in Li-based electrolyte. The involvement of both capacitive charging and ion intercalation electrochromisms were investigated previously in Nb-doped TiO.sub.2 for their metallic nature and finite scale that are able to support capacitive charging electrochromism (Dahlman et al. J. Am. Chem. Soc. 2015, 137 (28), 9160-9166), whereas the ion intercalation is present when the metal ions are reduced. The metallic nature of bulk monoclinic Nb.sub.12O.sub.29 crystals reported in literature is proposed to have led to the observation of capacitive charging electrochromism (Li et al. Chem. Mater. 2011, 23 (9), 2292-2294; Cava et al. Phys. Rev. B 1991, 44 (13), 6973-6981; Kocer et al. Phys. Rev. B 2019, 99 (7), 075151), and the ion intercalation electrochromism is from the Nb.sup.5+ ions being reduced into Nb.sup.4+ ion (Özer et al. Sol. Energy Mater. Sol. Cells 1996, 40 (4), 285-296; Macek et al. J. Electrochem. Soc. 1997, 144 (9), 3002-3010). In terms of where the Li.sup.+ ions located during ion intercalation, possible candidates are the cavities within four vertex-shared NbO.sub.6 octahedra in the basic building block (Li et al. Chem. Mater. 2011, 23 (9), 2292-2294).
[0387] The nature of localized electrons can be observed by the change of oxidation state of the metal ions being reduced (Özer et al. Sol. Energy Mater. Sol. Cells 1996, 40 (4), 285-296). For Nb.sub.2O.sub.5-x, decrease in the binding energy of Nb 3d.sub.3/2 and Nb 3d.sub.5/2 bands is considered as the result of Nb.sup.5+ being reducing to Nb.sup.4+ and balanced by Li.sup.+ ion intercalation. In
[0388] The electrochemical nature of ligand-stripped anisotropic monoclinic Nb.sub.12O.sub.29 nanocrystal films were further investigated by analyzing the dependence of current on the sweep rate in cyclic voltammograms. The so called b-value test is a method for determining the extent to which the electrochemical process is limited by diffusion, in which:
log(i)=log(a)+b*log(v)
where i is the current density in cyclic voltammogram, v is the sweep rate, a is a constant determined by the testing environment, and b is a constant determining the kinetics of the electrochemical reaction (Lindstrom et al. J. Phys. Chem. B 1997, 101 (39), 7717-7722; Augustyn et al. Nat. Mater. 2013, 12, 518). A b value of 0.5 indicates a purely diffusion-limited reaction controlled by the boundary condition of semi-infinite linear diffusion, and a b value of 1 indicates that the reaction behaves similarly to a capacitor, equivalently a non-diffusion-limited reaction with no apparent concentration gradient in the system.
[0389] In this case, the diffusion of Li.sup.+ ions in the nanocrystal lattice during ion intercalation may limit the reaction kinetics. Cyclic voltammograms of the nanocrystal films at various sweep rate ranging from 4 mV/s to 80 mV/s were recorded, with the results from 1 mV/s to 10 mV/s presented in
[0390] The optical density changes (ΔOD) at different charge densities (Q) injected into the nanocrystal films were measured by cathodically charging the films at 10 μA/cm.sup.2 using chronopotentiometry (
[0391]
CONCLUSION
[0392] Phase control in the colloidal synthesis of Nb.sub.2O.sub.5-x nanocrystals was developed, varying between pure anisotropic orthorhombic Nb.sub.2O.sub.5 nanocrystals, pure anisotropic monoclinic Nb.sub.12O.sub.29 nanocrystals, and a mixture of both. Among them, the anisotropic monoclinic Nb.sub.12O.sub.29 nanocrystals are the first successful synthesis of monoclinic Nb.sub.2O.sub.5-x nanocrystals using a colloidal approach without high temperature annealing. The anisotropic monoclinic Nb.sub.12O.sub.29 nanocrystals have a nanoplatelet morphology, monolayer feature with elongation only in the direction, and reduced abundance of Nb═O terminal bonds due to their anisotropy. In terms of enabling phase control, two niobium precursors for hot-injection synthesis were synthesized, the niobium chloro oleate leading to the nanocrystal mixture with anisotropic orthorhombic Nb.sub.2O.sub.5 nanocrystals being the main product, and the niobium oxo clusters leading to pure anisotropic monoclinic Nb.sub.12O.sub.29 nanocrystals. As a complementary synthesis, heat-up synthesis using niobium chloro oleate leads to pure anisotropic orthorhombic Nb.sub.2O.sub.5 nanocrystals. Thin films based on ligand-stripped anisotropic monoclinic Nb.sub.12O.sub.29 nanocrystals demonstrate dual-mode electrochromism: the first step is dominated by capacitive charging that generates delocalized electrons and absorbs NIR light, and the second step is dominated by ion intercalation that generates localized electrons and absorbs visible light. Electrochemical kinetics of the films were investigated by b-value test, showing that the described capacitive charging process is a non-diffusion-limited process, while the ion intercalation process is limited by the diffusion of Li.sup.+ ions in the nanocrystal lattice.
[0393] Electrochromic properties of anisotropic monoclinic Nb.sub.12O.sub.29 nanocrystals demonstrate the first case of capacitive charging electrochromic process existing in Nb.sub.2O.sub.5-x, usually considered unavailable in bulk Nb.sub.2O.sub.5-x materials, and also the independent control of solar spectrum utilizing the two different processes. The optical and chemical evidence of these two processes was presented along with an approach to distinguish them, using b-value test to track whether Li.sup.+ ion diffusion is occurring in the crystal lattice, a concomitant process with the generation of localized electrons as polarons. The ability of anisotropic monoclinic Nb.sub.12O.sub.29 nanocrystals to independently control NIR and visible light can promote their usage in electrochromic smart windows.
[0394] The compositions, devices, and methods of the appended claims are not limited in scope by the specific devices and methods described herein, which are intended as illustrations of a few aspects of the claims and any devices and methods that are functionally equivalent are within the scope of this disclosure. Various modifications of the compositions, devices, and methods in addition to those shown and described herein are intended to fall within the scope of the appended claims. Further, while only certain representative compositions, devices, and methods, and aspects of these compositions, devices, and methods are specifically described, other compositions, devices, and methods and combinations of various features of the compositions, devices, and methods are intended to fall within the scope of the appended claims, even if not specifically recited. Thus a combination of steps, elements, components, or constituents can be explicitly mentioned herein; however, all other combinations of steps, elements, components, and constituents are included, even though not explicitly stated.