TRANSPARENT TRIAZINE COPOLYMER BASED TRANSPARENT GEL-POLYMER ELECTROLYTES

Abstract

Method for manufacturing optically transparent gel-polymer electrolytes includes reaction of copolymerization of melamine and formaldehyde or melamine and glyoxal with one or several polyols and/or with one or several monosaccharides, oligosaccharides or polysaccharides and adding of a concentrated acid to form an optically transparent gel-polymer. The electrolyte according to the invention can be used in electrochromic devices and other optical-electrochemical devices as well as in devices for storing electrical energy (such as batteries, supercapacitors and hybrid power storage devices), thus replacing conventional water-based electrolytes.

Claims

1. A method of manufacturing proton-conducting gel-polymer electrolytes, the method comprising: providing copolymerization reaction of melamine and formaldehyde or melamine and glyoxal with one or more polyols; and adding a concentrated acid to form an optically transparent gel-polymer.

2. The method of claim 1, wherein the polyol is selected from the following group: glycerol, ethylene glycol, propylene glycol, polyethylene glycol, polypropylene glycol, polyethylene oxide, polyvinyl alcohol.

3. The method of claim 1, wherein the acid is an organic acid.

4. The method of claim 1, wherein the acid is an inorganic acid.

5. A method of manufacturing proton-conducting gel-polymer electrolytes, the method comprising: providing copolymerization reaction of melamine and formaldehyde with one or several monosaccharides, oligosaccharides or polysaccharides and/or their derivatives; and adding a concentrated acid to form an optically transparent gel-polymer.

6. The method of claim 5, wherein the polysaccharide is selected from the following group: starch, cellulose, chitin.

7. The method of claim 6, wherein the polysaccharide derivatives are carboxylate compounds.

8. The method of claim 6, wherein the polysaccharide derivatives are esters.

9. The method of claim 5, wherein the acid is an organic acid.

10. The method of claim 5, wherein the acid is an inorganic acid.

11. A method of manufacturing proton-conducting gel-polymer electrolytes, the method comprising: providing copolymerization reaction of melamine and formaldehyde or melamine and glyoxal with one or several polyols and with one or several monosaccharides, oligosaccharides or polysaccharides and/or their derivatives; and adding a concentrated acid to form an optically transparent gel-polymer.

12. The method of claim 11, wherein the polyol is selected from the group consisting of: glycerol, ethylene glycol, propylene glycol, polyethylene glycol, polypropylene glycol, polyethylene oxide, polyvinyl alcohol.

13. The method of claim 11, wherein the polysaccharide is selected from the group consisting of: starch, cellulose, chitin.

14. The method of claim 13, wherein the polysaccharide derivatives are carboxylate compounds.

15. The method of claim 13, wherein the polysaccharide derivatives are esters.

16. The method of claim 11, wherein the acid is an organic acid.

17. The method of claim 11, wherein the acid is an inorganic acid.

Description

BRIEF DESCRIPTION OF DRAWINGS

[0027] The accompanying drawings, which are included to provide a further understanding of the invention and are incorporated in and constitute a part of this specification, illustrate embodiments of the invention and, together with the description, serve to explain the principles of the invention.

[0028] In the drawings:

[0029] FIG. 1 shows a schematic diagram of first stage of gel-polymer electrolyte synthesis that is formation of trimethylol melamine.

[0030] FIG. 2 shows a schematic diagram of second stage of optically transparent melamine-formaldehyde gel-polymer electrolyte synthesis by reaction of trimethylol melamine with polyols, monosaccharides, oligosaccharides, polysaccharides and any of their derivatives containing more than one free OH— group.

[0031] FIG. 3 shows a schematic diagram for measuring ionic conductivity of a gel electrolyte by impedance spectroscopy between two platinum electrodes.

[0032] FIG. 4 shows a schematic diagram of an electrochromic device. The process of coloring (a) occurs when protons move towards the electrochromic electrode and process of bleaching (b) is achieved after polarity inversion.

[0033] FIG. 5 shows a schematic diagram of a secondary electrochromic cell. It illustrates motion of protons and anions during discharge (a) and charge (b), and it also shows schematically faradic processes at the electrodes.

[0034] FIG. 6 shows a schematic diagram of a symmetrical supercapacitor with an electrical double layer and a gel-polymer electrolyte with proton conductivity.

DETAILED DESCRIPTION OF EMBODIMENTS OF THE INVENTION

[0035] Reference will now be made in detail to the preferred embodiments of the present invention, examples of which are illustrated in the accompanying drawings.

[0036] The main drawbacks of melamine-based polymers are their fragility and tendency to shrinkage. To overcome them, the inventor of the present invention developed a method of obtaining more elastic melamine derivatives by copolymerization of trimethylol melamine (FIG. 1) with polyols, sugars, starch and cellulose derivatives. Copolymerization occurs with relatively long polymer chains and hydroxyl-terminated groups (FIG. 2), which contributes to elasticity of the resulting polymer. In addition, hydroxyl-containing groups in the final melamine copolymers are quite voluminous and significantly reduce shrinkage of these copolymers.

[0037] It should be noted that the copolymers obtained in this manner represent transparent or translucent liquids of various viscosities. Some of them can be stored for up to 12 months (usually from 30 days to 8 months) without significant change in their physical properties. Further, by adding strong mineral or organic acids to melamine copolymers, proton-conducting gels are obtained.

[0038] Immediately after adding a strong acid, the solution remains liquid and retains transparency, but after a while, the process of deeper polymerization begins and the polymer solution turns into a ion-conducting gel-electrolyte. At the same time, the process of conversion of the solution into gel can take quite a long time and its duration depends both on concentration of the acid and on presence of hydrophobic groups in the polyol chain. The stronger the acid and the higher its concentration, the slower the gel formation process. Hydrophobic groups in polyols also significantly reduce rate of gel formation. For example, when using propylene glycol and its derivatives, in particular, poloxamers [24], the gel formation process may take up to 72 hours or more.

[0039] Unexpectedly, when very large amounts of strong concentrated acids (for example, concentrated sulfuric acid) were added to copolymer solutions in ratio of 1:1 or even 1.5:1 (in terms of polymer) there was no instant polymerization with formation of a solid phase (gel-polymer), but a slow (up to 10 hours) thickening of the initial copolymer occurred with formation of very elastic and completely transparent gel-polymers without separation of the liquid phase.

[0040] In addition, it should be noted that dependence of transparency of the proton-conducting gel on the concentration of an acid is not linear. With increase in the acid content, at least two values of content ratio between the acid and the melamine copolymer are observed, at which the gel electrolyte becomes transparent. Transparent gel-polymer electrolytes are developed at acid concentration from 3.0% to 7.5% and from 10.0% to 40.0% in a copolymer solution. Between these values, the gel can be in a very hazy state, opalescent, or even completely white and opaque.

[0041] Ionic conductivity of melamine electrolytes was measured in a cell containing two platinum electrodes with a working surface area (a) of 17.2 cm.sup.2. The distance (1) between the electrodes was 1 mm (see FIG. 3). The impedance of the cell was measured by Electrochemical Impedance Spectroscopy (EIS) in frequency range of 1 kHz to 0.5 MHz with a voltage amplitude between 50 mV and 150 mV. As a result, a frequency response was obtained for each gel-polymer electrolyte (Nyquist plot). To determine the impedance value (Z), the minimum value was selected along the ReZ (Ohm) axis and along the ImZ (Ohm) axis. The conductivity was determined by formula (1) [25].

[00001]$\begin{array}{cc}\sigma =\left(\frac{1}{Z}\right).Math.\left(\frac{l}{a}\right)& \left(1\right)\end{array}$

[0042] Ionic conductivity of all gel-polymer electrolytes obtained by the method described herein was in range of 1.2.Math.10.sup.−1 to 2.56.Math.10.sup.−1 S/cm. Such high conductivity makes it possible to achieve good characteristics of electrochromic and other galvanic devices.

[0043] The electrochromic devices were manufactured by the inventor of the present invention with use of the proposed gel-polymer electrolytes to verify their operability experimentally. A generalized schematic diagram of these devices is shown in FIG. 4. Tungsten oxide-based material was used for the electrochromic electrode, and doped cerium oxide CeO.sub.2:M (M is a transition metal) was used for the counter electrode. Both materials were magnetron sputtered to a glass substrate with applied layer of Fluorine doped Tin Oxide (FTO). Operational voltage in such an electrochemical cell, which provides change of coloring, did not exceed 1.0 V. This voltage value should be considered acceptable due to limitation of voltammetric window of aqueous electrolytes, at which their premature degradation does not occur (<1.23 V).

[0044] Owing to high conductivity of the electrolyte, speed of switching from bleached state to the colored state is very high in such a cell, usually 5 to 20 seconds with a distance between the electrodes of 1 mm. At the same time, with decrease in the distance between the electrodes, there is no significant increase in speed. Apparently, operation of the electrochemical cell in such conditions is limited by speed of electrochemical processes occurring directly on the electrodes, not conductivity of the gel-polymer electrolyte.

[0045] The schematic diagram of the electrochromic device in FIG. 4 proposes the use of inorganic materials as an electrochromic electrode and a counter electrode. Nevertheless, it should be obvious that the gel-polymer electrolytes developed by the inventor can also be successfully used in devices based on suitable organic electrochromic materials.

[0046] Also, the inventor has manufactured electrochemical current sources (batteries) using melamine copolymer-based gel-polymer electrolytes to check the present invention experimentally. A generalized schematic diagram of these devices is shown in FIG. 5. An electrochemical system of a lead-acid battery was used as an example. Sulfuric acid solution was replaced with a gel-polymer electrolyte that was obtained by adding H.sub.2SO.sub.4 of a similar concentration to the initial copolymer. Thus, all electrochemical processes in this device were similar to processes in the well-known lead-acid battery.

[0047] Due to the fact that ionic conductivity of gel-polymer melamine electrolytes used in the device is not as high as that of a conventional sulfuric acid solution, the power output of the battery was slightly lower than that of cells assembled according to the classical scheme. However, the battery capacity remained unchanged, and its service life increased significantly. Owing to absence of the liquid phase, operating safety of the battery and its resistance to mechanical stress increase. In addition, such a battery does not require a separator between the electrodes, since the elastic gel-polymer electrolyte ideally performs as a separator and a membrane, thus eliminating incorrect operation of the electric current source.

[0048] It should be clear that a schematic diagram similar to the one shown in FIG. 5 can be used to manufacture any power sources (including primary ones) using proton-conducting electrolytes.

[0049] The inventor also manufactured supercapacitors comprising melamine copolymer-based gel-polymer electrolytes to test the invention experimentally. As an example, basic symmetrical supercapacitors with an electrical double layer were used [24], [26], [27]. A generalized schematic diagram of these devices is shown in FIG. 6. The electrodes were made of carbon paper and a gel-polymer with H.sub.2SO.sub.4 concentration of approximately 0.5-2.0 M was used as an electrolyte. Use of a separator in this case is not required. The device operated normally in the voltage range of 0-1.2 V, and its characteristics were very close to those of similar devices comprising acid electrolytes. Specific capacity of the supercapacitors strongly depended on porosity of carbon paper. There was no decrease in capacity during 10 000 charge-discharge cycles.

[0050] The following are examples of implementation of the invention.

Example 1. Synthesis of Ethylene Glycol Melamine Formaldehyde Concentrate EMFC-3-5 (50%)

[0051] 31.53 g (0.25 mol) of melamine, 15.52 g (0.25 mol) of ethylene glycol, 4.86 g of butanol-1, 22.43 g of water and 5.00 g of 2% NaOH solution were placed in a three-neck flask equipped with a stirrer, reflux condenser and thermometer. The contents were mixed and heated up to 85-90° C., after that 56.76 g (0.70 mol) of 37% formalin solution preheated to 50° C. was added, while ensuring that temperature of the reaction mixture did not fall below 70° C. Melamine dissolved within 1-2 minutes and the reaction mixture became completely transparent. The reaction was conducted for 5 hours at a temperature of 80-85° C. Further, the reaction mixture was quickly cooled (in less than 10 minutes) to room temperature. The prepared 50% solution of melamine copolymer and ethylene glycol was mixed with concentrated hydrochloric acid at ratio of 5 ml of the solution to 0.8-1.1 ml of the acid while cooling with ice and vigorous stirring. The obtained transparent solution was placed in an electrochromic cell as electrolyte. It took 7 to 24 hours to form a proton-conducting transparent gel-polymer.

[0052] Conductivity of the obtained gel-polymer electrolyte was in range of 15.6.Math.10.sup.−1 to 1.5.Math.10.sup.−1 S cm.sup.−1, depending on amount of the added acid. Transparency in visible wavelength range was T.sub.380-780=99.8% for polymer layer thickness of 1 mm.

Example 2. Synthesis of Glycerol Melamine Formaldehyde Concentrate GMFC-3-5 (50%)

[0053] 31.53 g (0.25 mol) of melamine, 23.02 g (0.25 mol) of glycerol, 4.86 g of butanol-1, 29.93 g of water and 5.00 g of 2% NaOH solution were placed in a three-neck flask equipped with a stirrer, reflux condenser and thermometer. The contents were heated while mixing to 85-90° C., after that 56.76 g (0.70 mol) of 37% formalin solution preheated to 50° C. was added, while ensuring that temperature of the reaction mixture did not fall below 70° C. Melamine dissolved within 1-2 minutes and the reaction mixture became completely transparent. The reaction was conducted for 5 hours at a temperature of 80-85° C. Then the reaction mixture was quickly cooled (in less than 10 minutes) to room temperature. The obtained 50% solution of the melamine copolymer and glycerol was mixed with concentrated hydrochloric acid at ratio of 5.0 ml of the solution to 0.7-1.3 ml of the acid while cooling with ice and vigorous stirring. The obtained transparent solution was placed in an electrochromic cell as electrolyte. It took 7 to 48 hours to form a proton conducting transparent gel-polymer.

[0054] Conductivity of the obtained gel-polymer electrolyte was in range of 1.56.Math.10.sup.−1 to 1.48.Math.10.sup.−1 S/cm, depending on amount of the added acid. Transparency in visible wavelength range was T.sub.380-780=99.9% for polymer layer thickness of 1 mm.

Example 3. Synthesis of Glycerol Melamine Formaldehyde Concentrate GMFC-3-5 (60%)

[0055] 31.53 g (0.25 mol) of melamine, 23.02 g (0.25 mol) of glycerol, 4.86 g of butanol-1, 4.75 g of water and 5 g of 2% NaOH solution were placed in a three-neck flask equipped with a stirrer, reflux condenser and thermometer. The contents were heated while mixing to 85-90° C., after that 56.76 g (0.70 mol) of 37% formalin solution preheated to 50° C. was added, while ensuring that temperature of the reaction mixture did not fall below 70° C. Melamine was dissolved within 0.5-2 minutes and the reaction mixture became completely transparent. The reaction was conducted for 5 hours at a temperature of 80-85° C. Further, the reaction mixture was quickly cooled (in less than 10 minutes) to room temperature. The obtained 60% solution of the melamine copolymer with glycerol was mixed with concentrated hydrochloric acid at ratio of 5.0 ml of the solution to 0.7-1.3 ml of the acid. The obtained transparent solution was placed in an electrochromic cell as electrolyte. It took 5 to 48 hours to form a transparent and flexible gel-polymer with proton conductivity.

[0056] Conductivity of the obtained gel-polymer electrolyte was in range of 1.55.Math.10.sup.−1 to 1.59.Math.10.sup.−1 S/cm, depending on amount of the added acid. Transparency in visible wavelength range was T.sub.380-780=99.8% for polymer layer thickness of 1 mm.

Example 4. Synthesis of Glycerol Melamine Formaldehyde Concentrate GMFC-3-5 (65%)

[0057] 31.53 g (0.25 mol) of melamine, 23.02 g (0.25 mol) of glycerol, 4.86 g of butanol-1 and 0.20 g of NaOH were placed in a three-neck flask equipped with a stirrer, reflux condenser and thermometer. The contents were heated while mixing to 85-90° C., after that 56.76 g (0.70 mol) of 37% formalin solution preheated to 50° C. was added, while ensuring that temperature of the reaction mixture did not fall below 70° C. Melamine was dissolved within 0.5-2 minutes and the reaction mixture became completely transparent. It took 5 hours to conduct the reaction at a temperature of 80-85° C. Further, the reaction mixture was quickly cooled (in less than 10 minutes) to room temperature. The obtained 65% melamine copolymer with glycerol was mixed under ice cooling and vigorous stirring with concentrated hydrochloric acid at ratio of 5.0 ml of solution to 0.7-1.3 ml of acid. The obtained transparent solution was placed in an electrochromic cell as electrolyte. It took 5 to 36 hours to form a transparent and flexible gel-polymer with proton conductivity.

[0058] Conductivity of the obtained gel-polymer electrolyte was in range of 1.35.Math.10.sup.−1 to 1.50.Math.10.sup.−1 S cm.sup.−1, depending on amount of the added acid. Transparency in visible wavelength range was T.sub.380-780=99.8% for polymer layer thickness of 1 mm.

Example 5. Synthesis of Polyethylene Glycol (400) Glycerol Melamine Formaldehyde Concentrate PEG-GMFC-3-5 (50%)

[0059] 31.53 g (0.25 mol) of melamine, 21.87 g (0.24 mol) of glycerol, 5.00 g (0.05 mol) of PEG-400, 4.86 g of butanol-1, 33.78 g of water and 5.00 g of 2% NaOH solution were placed in a three-neck flask equipped with a stirrer, reflux condenser and thermometer. The contents were heated while mixing to 85-90° C., after that 56.76 g (0.70 mol) of 37% formalin solution preheated to 50° C. was added, while ensuring that temperature of the reaction mixture did not fall below 70° C. Melamine dissolved within 1-2 minutes and the reaction mixture became completely transparent. The reaction was conducted for 5 hours at a temperature of 80-85° C. Further, the reaction mixture was quickly cooled (in less than 10 minutes) to room temperature. The obtained 50% solution of melamine copolymer with glycerol and PEG-400 was mixed with concentrated hydrochloric acid in ratio of 5.0 ml of the solution to 0.7-1.3 ml of the acid under ice cooling and vigorous stirring. The obtained transparent solution was placed in an electrochromic cell as electrolyte. It took 5 to 72 hours to form a transparent gel-polymer with proton conductivity.

[0060] Conductivity of the obtained gel-polymer electrolyte was in range of 1.64.Math.10.sup.−1 to 2.00.Math.10.sup.−1 S/cm, depending on amount of the added acid. Transparency in visible wavelength range was T.sub.380-780=99.5% for polymer layer thickness of 1 mm.

Example 6. Synthesis Propylene Glycol Melamine Formaldehyde Concentrate PG-MFC-3-5 (50%)

[0061] 31.53 g (0.25 mol) of melamine, 19.02 g (0.25 mol) of propylene glycol, 4.86 g of butanol-1, 26.94 g of water and 5.00 g of 2% NaOH solution were placed in a three-neck flask equipped with a stirrer, reflux condenser and thermometer. The contents were mixed while heated to 85-90° C., after that 56.76 g (0.70 mol) of 37% formalin solution preheated to 50° C. was added, while ensuring that temperature of the reaction mixture did not fall below 70° C. Melamine dissolved within 1-2 minutes and the reaction mixture became completely transparent. The reaction was conducted for 5 hours at a temperature of 80-85° C. Further, the reaction mixture was quickly cooled (in less than 10 minutes) to room temperature. The obtained 50% solution of melamine copolymer with propylene glycol was mixed with concentrated hydrochloric acid at ratio of 5.0 ml of the solution to 0.7-1.4 ml of the acid under ice cooling and vigorous stirring. The obtained transparent solution was placed in an electrochromic cell as electrolyte. It took 12 to 120 hours to form a transparent gel-polymer with proton conductivity.

[0062] Conductivity of the obtained gel-polymer electrolyte was in range of 1.2.Math.10.sup.−1 to 1.7.Math.10.sup.−1 S/cm, depending on amount of the added acid. Transparency in visible wavelength range was T.sub.380-780=99.5% for polymer layer thickness of 1 mm.

Example 7. Synthesis of Polyethylene Glycol (400) Melamine Formaldehyde Concentrate PEG-MFC-3-7 (70%)

[0063] 31.53 g (0.25 mol) of melamine, 100 g (0.25 mol) of PEG-400, 4.86 g of butanol-1, 19.75 g of water and 5.00 g of 2% NaOH solution were placed in a three-neck flask equipped with a stirrer, reflux condenser and thermometer. The contents were mixed while heating up to 85-90° C., after that 56.76 g (0.70 mol) of 37% formalin solution preheated to 50° C. was added, while ensuring that temperature of the reaction mixture did not fall below 70° C. Melamine dissolved within 1-2 minutes and the reaction mixture became completely transparent. The reaction was conducted for 7 hours at a temperature of 80-85° C. Further, the reaction mixture was quickly cooled (in less than 10 minutes) to room temperature. The obtained 50% melamine copolymer solution with PEG-400 was mixed under cooling and vigorous stirring with concentrated hydrochloric acid at ratio of 5.0 ml of the solution to 0.8-1.2 ml of the acid. The obtained transparent solution was placed in an electrochromic cell as electrolyte. It took 48 to 120 hours to form a transparent gel-polymer with proton conductivity.

[0064] Conductivity of the obtained gel-polymer electrolyte was in range of 1.51.Math.10.sup.−1 to 1.62.Math.10.sup.−1 S/cm, depending on amount of the added acid. Transparency in visible wavelength range was T.sub.380-780=99.3% for polymer layer thickness of 1 mm.

Example 8. Synthesis of Polyethylene Glycol (400) Polypropylene Glycol Starch Formaldehyde Concentrate PEG-PPG-Starch-MFC-3-5 (61%)

[0065] 32.46 g (0.26 mol) of melamine, 13 g (0.03 mol) of PEG-400, 11.67 g (0.13 mol) of propylene glycol, 1.19 g of cationic starch, 4.86 g of butanol-1 and 0.10 g of NaOH were placed in a three-neck flask equipped with a stirrer, reflux condenser and thermometer. The contents were mixed and heated to 85-90° C., after that 56.76 g (0.70 mol) of 37% formalin solution preheated to 50° C. was added, while ensuring that temperature of the reaction mixture did not fall below 70° C. Melamine dissolved within 1-2 minutes and the reaction mixture became transparent with a slight opalescence. The reaction was conducted for 5 hours at a temperature of 80-85° C. Further, the reaction mixture was quickly cooled (in less than 10 minutes) to room temperature. The obtained 61% copolymer solution was mixed with concentrated hydrochloric acid at ratio of 5.0 ml of the solution to 0.5-2.0 ml of the acid under ice cooling and vigorous stirring. The obtained transparent solution was placed in an electrochromic cell as electrolyte. It took 48 to 120 hours to form a transparent gel-polymer with proton conductivity.

[0066] Conductivity of the obtained gel-polymer electrolyte was in range of 1.38.Math.10.sup.−1 to 1.80.Math.10.sup.−1 S/cm, depending on amount of the added acid. Transparency in visible wavelength range was T.sub.380-780=98.5% for polymer layer thickness of 1 mm. The resulting gel had an observable opalescence.

Example 9. Synthesis of Saccharose Ethylene Glycol Melamine Formaldehyde Concentrate Succharose-EMFC-3-5 (60%)

[0067] 31.53 g (0.25 mol) of melamine, 11.15 g (0.2 mol) of ethylene glycol, 17.1 g (0.05 mol) of saccharose, 4.86 g of butanol-1, 9.05 ml of H.sub.2O and 5.00 g of 2% NaOH solution were placed in a three-neck flask equipped with a stirrer, reflux condenser and thermometer. The contents were mixed and heated to 85-90° C., after that 56.76 g (0.70 mol) of 37% formalin solution preheated to 50° C. was added, while ensuring that temperature of the reaction mixture did not fall below 70° C. Melamine dissolved within 1-2 minutes and the reaction mixture became transparent. The reaction was conducted for 5 hours at a temperature of 80-85° C. Further, the reaction mixture was quickly cooled (in less than 10 minutes) to room temperature. The obtained 60% polymer solution was mixed under ice cooling and vigorous stirring with concentrated hydrochloric acid at ratio of 5.0 ml of the solution to 0.7-1.5 ml of the acid. The obtained transparent solution was placed in an electrochromic cell as electrolyte. It took 12 to 48 hours to form a gel-polymer with proton conductivity.

[0068] Conductivity of the obtained gel-polymer electrolyte was in range of 1.55.Math.10.sup.−1 to 1.80 .Math.10.sup.−1 S/cm, depending on amount of the added acid. Transparency in visible wavelength range was T.sub.380-780=99.0% for polymer layer thickness of 1 mm.

Example 10. Synthesis of Carboxymethyl Cellulose Ethylene Glycol Melamine Formaldehyde Concentrate CMC-EMFC-3-3 (18%)

[0069] 31.53 g (0.25 mol) of melamine, 11.17 g (0.18 mol) of ethylene glycol, 16.81 g (0.07 mol) of sodium carboxymethyl cellulose (CMC), 4.86 g of butanol-1 and 453.90 ml of H.sub.2O were placed in a three-neck flask equipped with a stirrer, reflux condenser and thermometer. The contents were mixed and heated to 85-90° C., after that 56.76 g (0.70 mol) of 37% formalin solution preheated to 50° C. was added, while ensuring that temperature of the reaction mixture did not fall below 70° C. Melamine dissolved within 1-2 minutes and the reaction mixture became transparent. The reaction was conducted for 3 hours at a temperature of 80-85° C. Further, the reaction mixture was quickly cooled (in less than 10 minutes) to room temperature. The obtained 18% polymer solution was mixed under cooling and vigorous stirring with concentrated hydrochloric acid at ratio of 5.0 ml of the solution to 0.7-3.5 ml of the acid. The obtained transparent solution was placed in an electrochromic cell as electrolyte. It took 12 to 160 h to form a gel-polymer with proton conductivity.

[0070] Conductivity of the obtained gel-polymer electrolyte was in range of 1.60.Math.10.sup.−1 to 2.40.Math.10.sup.−1 S/cm, depending on amount of the added acid. Transparency in visible wavelength range was T.sub.380-780=99.3% for polymer layer thickness of 1 mm.

Example 11. Synthesis of Saccharose Hydroxyethyl Cellulose Ethylene Glycol Melamine Formaldehyde Concentrate Saccharose-HEC-EMFC-3-3 (25%)

[0071] 31.53 g (0.25 mol) of melamine, 9.31 g (0.15 mol) of ethylene glycol, 23.94 g (0.07 mol) of saccharose, 2.00 g of hydroxyethyl cellulose (HEC), 4.86 g of butanol-1, 217.69 ml of H.sub.2O and 5.00 g of 2% NaOH solution were placed in a three-neck flask equipped with a stirrer, reflux condenser and thermometer. The contents were mixed and heated to 85-90° C., after that 56.76 g (0.70 mol) of 37% formalin solution preheated to 50° C. was added, while ensuring that temperature of the reaction mixture did not fall below 70° C. Melamine dissolved within 1-2 minutes and the reaction mixture became transparent. The reaction was conducted for 3 hours at a temperature of 80-85° C. Further, the reaction mixture was quickly cooled (in less than 10 minutes) to room temperature. The obtained 25% polymer solution was mixed under ice cooling and vigorous stirring with concentrated hydrochloric acid at ratio of 5.0 ml of the solution to 0.5-3.5 ml of the acid. The obtained transparent solution was placed in an electrochromic cell as electrolyte. It took 12 to 160 h to form a transparent gel-polymer with proton conductivity.

[0072] Conductivity of the obtained gel-polymer electrolyte was in range of 1.35.Math.10.sup.−1 to 2.50.Math.10.sup.−1 S/cm, depending on amount of the added acid. Transparency in visible wavelength range was T.sub.380-780=99.6% for polymer layer thickness of 1 mm.

Example 12. Synthesis of Saccharose Polyvinyl Alcohol Ethylene Glycol Melamine Formaldehyde Concentrate Saccharose-PVA-EMFC-3-5 (60%)

[0073] 31.53 g (0.25 mol) of melamine, 9.31 g (0.15 mol) of ethylene glycol, 23.94 g (0.07 mol) of saccharose, 4.86 g of butanol-1, 3.50 g of polyvinyl alcohol (PVA), 217.69 ml of H.sub.2O and 5.00 g of 2% NaOH solution were placed in a three-neck flask equipped with a stirrer, reflux condenser and thermometer. The contents were mixed and heated to 85-90° C., after that 56.76 g (0.70 mol) of 37% formalin solution preheated to 50° C. was added, while ensuring that temperature of the reaction mixture did not fall below 70° C. Melamine dissolved within 1-2 minutes and the reaction mixture became transparent. The reaction was conducted for 5 hours at a temperature of 80-85° C. Further, the reaction mixture was quickly cooled (in less than 10 minutes) to room temperature. The obtained 60% polymer solution was mixed under ice cooling and vigorous stirring with concentrated hydrochloric acid at ratio of 5.0 ml of the solution to 0.5-2.0 ml of the acid. The obtained transparent solution was placed in an electrochromic cell as electrolyte. It took 12 to 78 hours to form a gel-polymer with proton conductivity.

[0074] Conductivity of the obtained gel-polymer electrolyte was in range of 1.44.Math.10.sup.−1 to 1.60.Math.10.sup.−1 S/cm, depending on amount of the added acid. Transparency in visible wavelength range was T.sub.380-780=99.8% for polymer layer thickness of 1 mm.

Example 13. Synthesis of Glyoxal Ethylene Glycol Melamine Formaldehyde Concentrate Glyoxal-EMFC-3-5 (50%)

[0075] 31.53 g (0.25 mol) of melamine, 15.52 g (0.25 mol) of ethylene glycol, 36.28 g (0.25 mol) of glyoxal, 4.86 g of butanol-1, 10.17 g of water and 10.00 g of 2% NaOH solution were placed in a three-neck flask equipped with a stirrer, reflux condenser and thermometer. The contents were mixed and heated to 85-90° C., after that 56.76 g (0.70 mol) of 37% formalin solution preheated to 50° C. was added, while ensuring that temperature of the reaction mixture did not fall below 70° C. Melamine dissolved within 1-2 minutes and the reaction mixture became completely transparent. The reaction was conducted for 5 hours at a temperature of 80-85° C. Further, the reaction mixture was quickly cooled (in less than 10 minutes) to room temperature. The obtained 50% copolymer solution was mixed with concentrated hydrochloric acid at ratio of 5.0 ml of the solution to 0.7-1.5 ml of the acid under ice cooling and vigorous stirring. The obtained transparent solution was placed in an electrochromic cell as electrolyte. It took 7 to 48 hours to form a proton-conducting gel-polymer.

[0076] Conductivity of the obtained gel-polymer electrolyte was in range of 1.53.Math.10.sup.−1 to 1.55.Math.10.sup.−1 S/cm, depending on amount of the added acid. Transparency in the visible wavelength range was T.sub.380-780=99.5% for polymer layer thickness of 1 mm.

[0077] The theoretical analysis and experiments carried out by the inventor have shown that it is possible to use other strong proton acids, for instance, such inorganic acids as H.sub.2SO.sub.4, H.sub.3PO.sub.4, HBr, HF, HBF.sub.4, CF.sub.3SO.sub.3H, or such organic acids as CH.sub.2ClCOOH, CCl.sub.3COOH, CF.sub.3COOH, for obtaining transparent proton-conducting polymer electrolytes.

[0078] The first stage of the reaction results in formation of trimethylol (A) (FIG. 1) that is a product of interaction of melamine with three moles of formalin. Trimethylol is highly reactive and therefore it easily reacts with almost any compounds containing hydroxyl and amino groups (organic amines, alcohols, polyols, monosaccharides, oligosaccharides and polysaccharides, as well as with any multi-base organic acids or their anhydrides), forming the corresponding copolymers, graft polymers and their blends, which, upon interaction with acids, turn into gel-polymer electrolytes (B) (FIG. 2).

[0079] In the examples above, polyols are represented by glycerin, ethylene glycol, polyethylene glycol and polyvinyl alcohol. At the same time, it is possible to use other polyatomic alcohols, for example, propylene glycol, polypropylene glycol, polyethylene oxide, etc. The inventor is not physically able to conduct experiments with all polyols existing in nature. However, it should be apparent to those skilled in the art that possibility of their use in this invention follows from the common chemical properties of polyols.

[0080] In the examples above, monosaccharides and oligosaccharides are generally represented by sucrose. In this case, it is also possible to use other short saccharides-monosaccharides (for example, glucose, fructose), disaccharides (for example, lactose, maltose, isomaltose), trisaccharides (for example, glyceraldehyde, maltotriose, raffinose), tetrasaccharides (for example, stachyose, lichyose, maltotetraose), etc. As noted above with respect to polyols, the inventor is not physically able to conduct experiments with all monosaccharides and oligosaccharides existing in nature, however, possibility of their use in this invention follows from the common chemical properties of monosaccharides and oligosaccharides, which should be apparent to those skilled in the art.

[0081] In the examples above, polysaccharides and their derivatives are represented by sodium carboxymethyl cellulose (a representative of carboxylate compounds) and hydroxyethyl cellulose. In this case, it is possible to use other derivatives of polysaccharides, for example, hydroxypropyl, hydroxymethyl and methyl cellulose. As noted above with respect to polyols and saccharides, the inventor is not physically able to conduct experiments with all naturally occurring polysaccharides and their derivatives, in particular, those derived from cellulose, starch or chitin, however, a possibility of their use in this invention follows from the common chemical properties of polysaccharides and their derivatives, which should be apparent to those skilled in the art.

Example 14. Electrochromic Device with W029:Al:C:N and Ceo.SUB.2.:Zr-Based Electrodes

[0082] WO.sub.2.Math.9:Al:C:N-based electrochromic electrode material, 500 nm thick layer and CeO.sub.2:Zr-based counter electrode material, 300 nm thick layer were deposited on FTO-glass substrates by magnetron sputtering.

[0083] A freshly prepared melamine copolymer solution of Example 12 was blended with concentrated sulfuric acid and placed between the electrodes. The appeared reaction of further polymerization of the melamine copolymer resulted in formation of an elastic transparent gel-polymer electrolyte. The electrochromic cell developed in this way was operable at potential of ±1.0 V. When a negative potential was applied to the electrochromic electrode, it became colored and when the polarity is reversed, it became bleached. Maximum transmission capacity in visible wavelength range for the colored and discolored states was ΔT.sub.380-780=40%.

Example 15. Lead-Acid Battery with Gel-Polymer Electrolyte

[0084] A freshly prepared melamine copolymer solution of Example 9 was blended with concentrated sulfuric acid and placed into a conventional lead-acid battery with rated voltage of 12 V without electrolyte. The H.sub.2SO.sub.4 concentration was at least 37%. The reaction resulted in a deeper polymerization of the original copolymer that happened immediately in the battery, and elastic transparent gel-polymer between two electrodes made of lead and lead oxide (PbO2) was obtained. The process of transition to the state of a conductive gel took 10 to 12 hours. The lead-acid battery was operable under normal conditions with cell voltage in range from 1.80 V in the discharged state to 2.25 V in the fully charged state (immediately after charging). Capacity of the battery corresponded to its nominal capacity specified in its technical certificate with the usual electrolyte containing 37-40% of sulfuric acid, which originally was intended for it.

Example 16. Symmetrical Supercapacitor with Proton Gel-Polymer Electrolyte

[0085] A freshly prepared melamine copolymer solution of Example 9 was blended with concentrated sulfuric acid and placed between two sheets of special carbon paper having highly porous surface of activated carbon. Concentration of H.sub.2SO.sub.4 was 0.5-2.0 M. The deeper polymerization reaction launched in this way produced an elastic transparent gel-polymer electrolyte that was located between the carbon electrodes. The developed symmetrical supercapacitor demonstrated operability in range of 0-1.2 V and had capacitance values usual for this type of double electric layer capacitors.

[0086] Having thus described a preferred embodiment, it should be apparent to those skilled in the art that certain advantages of the described method and apparatus have been achieved. It should also be appreciated that various modifications, adaptations, and alternative embodiments thereof may be made within the scope and spirit of the present invention.

NON-PATENT REFERENCES (ALL INCORPORATED BY REFERENCE IN THEIR ENTIRETY)

[0087] [1] Ayushi Choudhary, Eswara Prasad. Electrochromic glass market by application (windows, mirror, and display) and end-user industry (construction, automotive, aerospace, and others): Global Opportunity Analysis and Industry Forecast, 2020-2027, Allied Market Research, June 2020. [0088] [2] Smart glass and smart window market report 2019-2029, Visiongain, July 2019. [0089] [3] H. Iwahara. Oxide-ionic and protonic conductors based on perovskite-type oxides and their possible applications. Solid State Ionics, vol. 52, no. 1-3, pp. 99-104, May 1992. [0090] [4] S. Oukassi, C. Giroud-Garampon, C. Dubarry, C. Ducros, R. Salot. All inorganic thin film electrochromic device using LiPON as the ion conductor. Solar Energy Materials and Solar Cells, vol. 145, pp. 2-7, July 2015. [0091] [5] Y. Wang et al. Design principles for solid-state lithium superionic conductors. Nature Materials, vol. 14, no. 10, pp. 1026-1031, August 2015. [0092] [6] F. Alloina, C. Iojoiu. Composite polymer electrolytes for electrochemical devices. Polymer Electrolytes. Fundamentals and Applications, 2010, pp. 129-175. [0093] [7] N. A. Choudhury, A. K. Shukla, S. Sampath, S. Pitchumani. Cross-linked polymer hydrogel electrolytes for electrochemical capacitors. Journal of Electrochemical Society, vol. 153, no. 3, 2006. [0094] [8] J. B. Kerr. Polymeric electrolytes: an overview. Lithium Batteries: Science and Technology, G.-A. Nazri, G. Pistoia, Eds. Boston, MA: Springer US, 2003, pp. 575-622. [0095] [9] K. S. Ngai, S. Ramesh, K. Ramesh, J. C. Juan. A review of polymer electrolytes: fundamental, approaches and applications. Ionics, vol. 22, pp. 1259-1279, 2016. [0096] [10] W. Wang, P. Alexandridis. Composite polymer electrolytes: nanoparticles affect structure and properties. Polymers, vol. 8, no. 11, 2016. [0097] [11] P. Ghosh, C. K. Dhole, S. Ganguly, D. Banerjee, K. Kargupta. Portable smart highly proton conductive all inorganic gel paste electrolyte with optimum phosphorous to silicon ratio for enhanced durable operation of a fuel cell. Sustainable Energy & Fuels, 2018, no. 2, pp. 1737-1748. [0098] [12] V. K. Thakur, G. Ding, J. Ma, P. S. Lee, X. Lu. Hybrid materials and polymer electrolytes for electrochromic device applications. Advanced Materials., vol. 24, no. 30, pp. 4071-4096, 2012. [0099] [13] W. Ma et al. Cross-linked aromatic cationic polymer electrolytes with enhanced stability for high temperature fuel cell applications. Energy & Environmental Science, vol. 5, no. 6, pp. 7617-7625, 2012. [0100] [14] G. Wang et al. Gel polymer electrolytes based on polyacrylonitrile and a novel quaternary ammonium salt for dye-sensitized solar cells. Materials Research Bulletin, vol. 39, no. 13, pp. 2113-2118, 2004. [0101] [15] U.S. Pat. No. 2,345,543A Cationic melamine-formaldehyde resin solution, 1942. [0102] [16] B. Bann, S. A. Miller. Melamine and Derivatives of Melamine. Chemical Reviews, vol. 58, no. 1, pp. 131-172, 1958. [0103] [17] D. J. Merline, S. Vukusic, A. A. Abdala. Melamine formaldehyde: curing studies and reaction mechanism. Polymer Journal, vol. 45, no. 4, pp. 413-419, 2013. [0104] [18] J. K. Fink. Melamine Resins. In: Reactive Polymers: Fundamentals and Applications. A Concise Guide to Industrial Polymers. Second edition, pp. 193-201, 2013. [0105] [19] K. Bretterbauer, C. Schwarzinger. Melamine derivatives—a review on synthesis and application. Current Organic Synthesis, 9(3):342, pp. 342-356, 2012. [0106] [20] C. Du Fresne Von Hohenesche, D. F. Schmidt, V. Schödler. Nanoporous melamine-formaldehyde gels by microemulsion templating. Chemical Materials, vol. 20, no. 19, pp. 6124-6129, 2008. [0107] [21] K. Shijina et al. Melamine formaldehyde-metal organic gel interpenetrating polymer network derived intrinsic Fe-N-doped porous graphitic carbon electrocatalysts for oxygen reduction reaction. New Journal of Chemistry, vol. 42, no. 23, pp. 18690-18701, 2018. [0108] [22] K. Mishra, S. A. Hashmi, D. K. Rai. Studies on a proton battery using gel polymer electrolyte. High Performance Polymers, vol. 26, no. 6, pp. 672-676, 2014. [0109] [23] C. Zhong, Y. Deng, W. Hu, J. Qiao, L. Zhang, J. Zhang. A review of electrolyte materials and compositions for electrochemical supercapacitors. Chemical Society Reviews, vol. 44, no. 21, pp. 7484-7539, 2015. [0110] [24] Abraham J. Domb, Joseph Kost, David M. Wiseman. Handbook of Biodegradable Polymers. First Edition. CRC Press, 2019. [0111] [25] W. Chen et al. A novel ionically crosslinked gel polymer electrolyte as an ion transport layer for high-performance electrochromic devices. Journal of Materials Chemistry C, vol. 7, no. 13, pp. 3744-3750, 2019. [0112] [26] L. N. Han, X. Wei, Q. C. Zhu, S. M. Xu, K. X. Wang, J. S. Chen. Nitrogen-doped carbon nets with micro/mesoporous structures as electrodes for high-performance supercapacitors. Journal of Materials Chemistry A, vol. 4, no. 42, pp. 16698-16705, 2016. [0113] [27] J. A. Fernandez, T. Morishita, M. Toyoda, M. Inagaki, F. Stoeckli, T. A. Centeno. Performance of mesoporous carbons derived from poly(vinyl alcohol) in electrochemical capacitors. Journal of Power Sources, vol. 175, no. 1-3, pp. 675-679, 2008.