OPTICAL FIBER WITH AN ATTENUATION REDUCTION REFRACTIVE INDEX (RI) PROFILE

Abstract

The present invention relates to an optical fiber having a core extending parallelly along a central axis of the optical fiber, an inner cladding surrounding the core and an outer cladding surrounding the inner cladding. In particular, the core is up-doped with first and second up-dopants and the inner cladding is up-doped with the second up-dopant. Moreover, the outer cladding is un-doped. Further, the optical fiber has an attenuation of less than 0.2 at a wavelength of 1625 nanometres (nm), the attenuation of less than 0.18 at a wavelength of 1550 nm, or the attenuation of less than 0.32 at a wavelength of 1310 nm and a cable cutoff in a range of 1186 nanometres (nm) to 1194 nm.

Claims

1. An optical fiber, comprising: a core extending along a central axis of the optical fiber, wherein the core is up-doped with at least a first up-dopant and a second up-dopant; an inner cladding surrounding the core, wherein the inner cladding is up-doped with at least the second up-dopant; and an outer cladding surrounding the inner cladding, wherein the outer cladding is un-doped.

2. The optical fiber of claim 1, wherein the core, the inner cladding, and the outer cladding has a refractive index Δ1, a refractive index Δ2, and a refractive index Δ3, respectively, such that the refractive index Δ1 is greater than the refractive index Δ2 and the refractive index Δ2 is greater than the refractive index Δ3.

3. The optical fiber of claim 1, wherein the core has a relative refractive index Δ1% that is in range 0.2% to 0.4%, wherein the inner cladding has a relative refractive index Δ2% that is in range 0.01% to 0.05%, and wherein the outer cladding has a relative refractive index Δ3% that is equal to 0%.

4. The optical fiber of claim 1, wherein the core up-doped with first and second up-dopants, the inner cladding up-doped with the second up-dopant, and the un-doped outer cladding 106 generates a Refractive Index (RI) profile that is defined by a core peak and an inner cladding peak, wherein the core peak is greater than the inner cladding peak.

5. The optical fiber of claim 4, wherein the core peak and the inner cladding peak has a peak radial distance therebetween, wherein the radial distance is in a range of 9 micrometres (μm) to 10 μm.

6. The optical fiber of claim 1, wherein the core and the inner cladding has the second up-dopant in first and second concentrations, respectively, wherein the first concentration is less than the second concentration.

7. The optical fiber of claim 8, wherein the first concentration of the second up-dopant in the core is in a range of 41% to 43% and the second concentration of the second up-dopant in the inner cladding 104 is in a range of 57% to 59%.

8. The optical fiber of claim 1, wherein concentration of the first up-dopant in the core is in a range of 0.25% to 0.3%.

9. The optical fiber of claim 1, wherein the core and the inner cladding has the second up-dopant in a first and second volumes, wherein the first volume is less than the second volume.

10. The optical fiber of claim 9, wherein the first volume of the second up-dopant in the core is in a range of 1850 ppm to 2100 ppm and the second volume of the second up-dopant in the inner cladding is in a range of 2490 ppm to 2800 ppm.

11. The optical fiber of claim 9, wherein the volume of the first up-dopant (i.e., Ge) in the core may be in a range of 2500 Parts Per Million (ppm) to 3000 ppm.

12. The optical fiber of claim 1, wherein the relative refractive index Δ2% of the inner cladding is radially distributed with a maximum value Δ2max and a minimum value Δ2 min, wherein the maximum value Δ2max is 0.03 and the minimum value Δ2 min is 0.02.

13. The optical fiber of claim 1, wherein (i) an attenuation of the optical fiber at a wavelength of 1625 nanometres (nm) is less than 0.2, wherein the attenuation of the optical fiber at a wavelength of 1550 nm is less than 0.18.

14. The optical fiber of claim 1, wherein the attenuation of the optical fiber at a wavelength of 1310 nm is less than 0.32, (ii) a macro bend loss of the optical fiber for 10 turns, 30 mm Mandrel diameter and at a wavelength of 1625 nm is less than 0.3 db/km.

15. The optical fiber of claim 1, wherein the macro bend loss in the optical fiber for 1 turn, 20 mm Mandrel diameter at the wavelength of 1625 nm is less than 1.5 db/km,

16. The optical fiber of claim 1, wherein the macro bend loss of the optical fiber for 10 turn, 30 mm Mandrel diameter at a wavelength of 1550 nm is less than 0.1 db/km,

17. The optical fiber of claim 1, wherein the macro bend loss of the optical fiber for 1 turns, 20 mm Mandrel diameter at the wavelength of 1550 nm is less than 0.5 db/km, and (iii) a cable cutoff of the optical fiber is in a range of 1186 nm to 1194 nm.

18. The optical fiber of claim 1, wherein the core has a radius R1 that is in range of 4 μm to 4.5 μm, wherein the inner cladding has a radius R2 that is in a range of 14 μm to 15 μm, and wherein the outer cladding has a radius R3 that is in range 61.5 μm to 62.5 μm.

19. The optical fiber of claim 13, wherein the radius R1, the radius R2, and the radius R3 is given by an average ratio (R3−R1)/(R2−R1), wherein the average ratio is in a range of 5.52 μm to 5.75 μm.

20. The optical fiber of claim 1, wherein the core has a thickness T1 and the inner cladding has a thickness T2 such that the thickness T2 is greater that the thickness T1.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0027] So that the manner in which the above recited features of the present invention is understood in detail, a more particular description of the invention, briefly summarized above, may be had by reference to embodiments, some of which are illustrated in the appended drawings. It is to be noted, however, that the appended drawings illustrate only typical embodiments of this invention and are therefore not to be considered limiting of its scope, for the invention may admit to other equally effective embodiments.

[0028] The invention herein will be better understood from the following description with reference to the drawings, in which:

[0029] FIG. 1 is a snapshot illustrating a cross-sectional view of an optical fiber in accordance with an embodiment of the present invention;

[0030] FIG. 2 is a graphical representation illustrating a Refractive Index (RI) profile of the optical fiber in accordance with an embodiment of the present invention;

[0031] FIG. 3 is a snapshot illustrating the concentration profiles of first up dopant and second up dopant in the core, inner cladding, and the outer cladding along with a resultant refractive index profile in accordance with another aspect of the present invention.

ELEMENT LIST

[0032] Optical fiber—100 [0033] Core—102 [0034] Inner cladding—104 [0035] Outer cladding—106 [0036] Central axis—108 [0037] Graph—200 [0038] Curve—202 [0039] Core peak—204 [0040] Inner cladding peak—206 [0041] Graph—300 [0042] First curve—302 [0043] Second curve—304 [0044] Third curve—306 [0045] Transition point—308

[0046] The optical fiber cable illustrated in the accompanying drawings, which like reference letters indicate corresponding parts in the various figures. It should be noted that the accompanying figure is intended to present illustrations of exemplary embodiments of the present invention. This figure is not intended to limit the scope of the present invention. It should also be noted that the accompanying figure is not necessarily drawn to scale.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0047] The principles of the present invention and their advantages are best understood by referring to FIGS. 1 to FIG. 3. In the following detailed description numerous specific details are set forth in order to provide a thorough understanding of the embodiment of invention as illustrative or exemplary embodiments of the invention, specific embodiments in which the invention may be practiced are described in sufficient detail to enable those skilled in the art to practice the disclosed embodiments. However, it will be obvious to a person skilled in the art that the embodiments of the invention may be practiced with or without these specific details. In other instances, well known methods, procedures and components have not been described in detail so as not to unnecessarily obscure aspects of the embodiments of the invention.

[0048] The following detailed description is, therefore, not to be taken in a limiting sense, and the scope of the present invention is defined by the appended claims and equivalents thereof. The terms “comprising,” “including,” “having,” and the like are synonymous and are used inclusively, in an open-ended fashion, and do not exclude additional elements, features, acts, operations, and so forth. Also, the term “or” is used in its inclusive sense (and not in its exclusive sense) so that when used, for example, to connect a list of elements, the term “or” means one, some, or all of the elements in the list. References within the specification to “one embodiment,” “an embodiment,” “embodiments,” or “one or more embodiments” are intended to indicate that a particular feature, structure, or characteristic described in connection with the embodiment is included in at least one embodiment of the present invention.

[0049] Although the terms first, second, etc. may be used herein to describe various elements, these elements should not be limited by these terms. These terms are generally only used to distinguish one element from another and do not denote any order, ranking, quantity, or importance, but rather are used to distinguish one element from another. Further, the terms “a” and “an” herein do not denote a limitation of quantity, but rather denote the presence of at least one of the referenced items.

[0050] Conditional language used herein, such as, among others, “can,” “may,” “might,” “may,” “e.g.,” and the like, unless specifically stated otherwise, or otherwise understood within the context as used, is generally intended to convey that certain embodiments include, while other embodiments do not include, certain features, elements and/or steps.

[0051] Disjunctive language such as the phrase “at least one of X, Y, Z,” unless specifically stated otherwise, is otherwise understood with the context as used in general to present that an item, term, etc., may be either X, Y, or Z, or any combination thereof (e.g., X, Y, and/or Z). Thus, such disjunctive language is not generally intended to, and should not, imply that certain embodiments require at least one of X, at least one of Y, or at least one of Z to each be present.

[0052] The Following Brief Definition of Terms Shall Apply Throughout the Present Invention:

[0053] The term “core” of an optical fiber as used herein is referred to as the inner most cylindrical structure present in the center of the optical fiber, that is configured to guide the light rays inside the optical fiber.

[0054] The term “Cladding” of an optical fiber as used herein is referred to as one or more layered structure covering the core of an optical fiber from the outside, that is configured to possess a lower refractive index than the refractive index of the core to facilitate total internal reflection of light rays inside the optical fiber. Further, the cladding of the optical fiber may include an inner cladding layer coupled to the outer surface of the core of the optical fiber and an outer cladding layer coupled to the inner cladding from the outside.

[0055] The term “refractive index” as used herein is referred to as the measure of change of speed of light from one medium to another and is particularly measured in reference to speed of light in vacuum. More specifically, the refractive index facilitates measurement of bending of light from one medium to another medium.

[0056] The term “relative refractive index” as used herein is referred to as the ratio of refractive index of one medium to the refractive index of other medium.

[0057] The term refractive index profile” of the optical fiber as used herein is referred to as the distribution of refractive indexes in the optical fiber from the core to the outmost cladding layer of the optical fiber. Based on the refractive index profile, the optical fiber may be configured as a step index fiber. The refractive index of the core of the optical fiber is constant throughout the fiber and is higher than the refractive index of the cladding. Further, the optical fiber may be configured as a graded index fiber, wherein the refractive index of the core gradually varies as a function of the radial distance from the center of the core.

[0058] The term “core peak” as used herein is referred to as the maximum refractive index value of the core of the optical fiber. The core peak is more significant in the graded index fiber as for the step index fiber, the refractive index of the core is same throughout.

[0059] The term “Cladding peak” as used herein is referred to as the maximum value of the refractive index of the one or more layers of cladding of the optical fiber.

[0060] The term “up-doping” as used herein is referred to as adding doping materials to facilitate increase in the refractive index of a particular layer or part of optical fiber. The materials configured to facilitate up-doping are known as up-dopants.

[0061] The term “down-doping” as used herein is referred to as adding doping materials to facilitate decrease in the refractive index of a particular layer or part of optical fiber. The materials configured to facilitate down-doping are known as down-dopants.

[0062] Concentration of Up Dopant:

[0063] The term “first concentration” as used herein is referred to as the percentage of the up-dopant materials present in the core that facilitate an increase in refractive index of the core of the optical fiber.

[0064] The term “second concentration” as used herein is referred to as the percentage of the up-dopant material present in the inner cladding that is configured to facilitate an increase in the refractive index of the inner cladding of the optical fiber.

[0065] The term “first volume” as used herein is referred to as the count of the up-dopant present per million of the elements of the core, i.e., concentration of the up-dopant in the core in (ppm), that is configured to facilitate an increase in refractive index of the core of the optical fiber.

[0066] The term “second volume” as used herein is referred to as the count of the up-dopant present per million of the elements of the inner cladding i.e., concentration of the up-dopant in the inner cladding in (ppm), that is configured to facilitate an increase in refractive index of the core of the optical fiber.

[0067] FIG. 1 is a snapshot illustrating a cross-sectional view of an optical fiber in accordance with an embodiment of the present invention. The optical fiber 100 may be fabricated to have reduced attenuation without increasing macro bend losses. In particular, the optical fiber 100 may have a core 102, an inner cladding 104, and an outer cladding 106. Moreover, the optical fiber 100 may have a central axis 108 such that the core 102 may be arranged along the central axis 108 running longitudinally, i.e., generally parallel to the central axis 108. The optical fiber 100 may have a Refractive Index (RI) profile (shown in FIG. 2) that may be generated by virtue of the core 102 being up doped with Germanium (Ge) and Chlorine (Cl), the inner cladding 104 being up doped with Cl and the outer cladding being undoped and made up of pure silica. Specifically, by up doping the core 102 and the inner cladding 104 with Cl, the RI profile having an upward peak in the inner cladding region may be generated, that may further facilitate the optical fiber 100 to have reduced attenuation without increasing macro bend losses.

[0068] The core 102 may be a cylindrical fiber that may run along a length of the optical fiber 100 and may be configured to guide an optical signal. In particular, the core 102 may be made up of a material selected from at least one of, a pure silica glass, Silicon tetrachloride (SiCl.sub.4), Germanium tetrachloride (GeCl.sub.4), Chlorine gas (Cl.sub.2), and the like. Preferably, the core 100 may be made up of a silica glass doped with a first up-dopant and a second up-dopant. Alternatively, the present invention is intended to include and/or otherwise cover any type of the material for the core 102, including known, related, and later developed materials.

[0069] Specifically, the core 102 may be up-doped with the first and second up-dopants that may increase values of net refractive index of the optical fiber 100 facilitating to control macro bend losses. The first and second up-dopants may be Germanium (Ge), and Cl.sub.2, respectively.

[0070] In some aspects of the present invention, a concentration (i.e., a weight percentage (wt. %)) of the first up-dopant in the core 102 may be in a range of 0.25% to 0.3%. Preferably, the concentration of the first up-dopant in the core 102 may be 0.3%.

[0071] The second up-dopant may have a first concentration in the core 102. The first concentration (i.e., a weight percentage (wt. %)) of the second up-dopant in the core 102 may be in a range of 41% to 43%. Preferably, the first concentration of the second up-dopant in the core 102 may be 42%.

[0072] In some aspects of the present invention, a volume of the first up-dopant (i.e., Ge) in the core 102 may be in a range of 2500 Parts Per Million (ppm) to 3000 ppm. Particularly, the volume of the first up-dopant (i.e., Ge) in the core 102 may be 3000 ppm. And, the second up-dopant may have a first volume in the core 102. The first volume of the second up-dopant may be in a range of 1850 ppm to 2100 ppm and the first volume of the second up-dopant (i.e., Cl.sub.2) in the core 102 may be 1950 ppm. Further, the second up-dopant may have a second volume in the inner cladding 104. The second volume of the second up-dopant may be in a range of 2490 ppm to 2800 ppm and the second volume of the second up-dopant (i.e., Cl.sub.2) in the inner cladding 104 may be 2680 ppm.

[0073] In accordance with an embodiment of the present invention, the second up-dopant (i.e., Cl.sub.2) may be used to up dope the core 102 as Cl.sub.2 and facilitate in reduction of stress in an optical fiber preform and in the optical fiber 100. In other words, the second up-dopant (i.e., Cl.sub.2) may act as a core viscosity reduction agent such that the core 102 becomes softer (i.e., easy to flow to provide relaxation and ease in releasing of stress from the hot optical fiber preform and resultant optical fiber.

[0074] The core 102 may have a radius R1 a thickness T1, and a refractive index Δ1. The radius R1 may be in a range of 4 micrometres (μm) to 4.5 μm. Preferably, the radius R1 may be 4 μm and the thickness T1 may be less than 4.5 μm. Preferably, the thickness T1 may be equal to the radius R1.

[0075] In some aspects of the present invention, the refractive index Δ1 may be in a range of 4.4 to 5.4 The core 102 may have a core alpha in a range of 3 to 5. Further, the core 102 may have a Mode Field Diameter (MFD) in a range of 8.85 to 9.2. Particularly, the refractive index Δ.sub.1 in the range of 4.4 to 5.4, the core alpha in the range of 3 to 5, and the MFD in the range of 8.85 to 9.2 may facilitate the optical fiber 100 to demonstrate desirable parameters such as, but not limited to, low attenuation, low MFD, high cutoff, low dispersion, and low macro bending loss, and the like.

[0076] When the core 102 has the refractive index Δ.sub.1 that is not within the range of 4.4 to 5.4, the core alpha that is not in the range of 3 to 5, and the MFD that is not in the range of 8.85 to 9.2, then optical fiber 100 may demonstrate undesirable parameters such as high attenuation, high MFD, less power in a core region, low cutoff, high macro bending loss, high dispersion, and poor lightening in confined space.

[0077] In accordance with an embodiment of the present invention, the inner cladding 104 may be made up of a material selected from at least one of, a pure silica glass, a doped silica glass, and the like. Alternatively, the inner cladding 104 may be made up of a combination of SiCl.sub.4 and Cl.sub.2. The inner cladding 104 may be made up of a silica glass doped with the second up-dopant.

[0078] Aspects of the present invention are intended to include and/or otherwise cover any type of the material for the inner cladding 104, including known, related, and later developed materials. The inner cladding 104 may be up-doped with the second up-dopant increasing values of net refractive index of the optical fiber 100 and facilitates control macro bend losses in the optical fiber 100. Additionally, the core 102 and the inner cladding 104 may be doped with the second up-dopant (i.e., Cl.sub.2) to avoid generation of stress in the optical fiber 100.

[0079] In some aspects of the present invention, the inner cladding 104 may have the second up-dopant (i.e., Cl.sub.2) in a second concentration (i.e., a weight percentage (wt. %)) may be in a range of 57% to 59%. Preferably, the second concentration of the second up-dopant (i.e., Cl.sub.2) in the inner cladding 104 may be 58%. Further, the inner cladding 104 may have the second up-dopant in a second volume in a range of 2490 ppm to 2800 ppm. Preferably, the second volume of the second up-dopant in the inner cladding 104 may be 2680 ppm.

[0080] In some aspects of the present invention, the first concentration may be lower than the second concentration. Particularly, the second concentration may be higher as compared to the first concentration to accommodate the consolidation of the inner cladding 104 that happens prior to the consolidation of the core 102. The addition of the second up-dopant (i.e., Cl.sub.2) in the core 102 and in the inner cladding 104 may further reduce the stress in the optical fiber preform and hence in the optical fiber 100, thus generating a peak surrounding an inner clad region. Specifically, the addition of the second up-dopant may reduce viscosity that may facilitate to avoid causing stresses between the core 102 and the inner cladding 104 of the optical fiber 100. Further, the addition of the second up-dopant in the core 102 and the inner cladding 104 may increase the value of net refractive index of the optical fiber 100 that may further facilitate control of the macro-bend loss of the optical fiber 100. Specifically, the addition of the second up-dopant may facilitate to control the macro-bend loss to less than 0.1 Decibel/Kilometres (dB/Km) at a wavelength of 1550 nanometres (nm) at 30 mm Mandrel diameter for 10 turns and the macro-bend loss may be controlled to less than 0.3 dB/Km at a wavelength of 1625 nm for 30 mm Mandrel diameter for 10 turns.

[0081] In accordance with an embodiment of the present invention, the addition of the first dopant in the core 102 facilitates the increase of the refractive index of the core 102. However, a concentration of the first dopant is not increased in the optical fiber 100 to control attenuation. Thus, the attenuation in the optical fiber 100 may be controlled only through the addition of the first and second up-dopants in the core 102 and the addition of the second up-dopant in the inner cladding 104 and keeping the overall concentration of the first up-dopant in the optical fiber 100 consistent.

[0082] In some aspects of the present invention, at a wavelength of 1310, the attenuation of the optical fiber 100 may be controlled to a value that may be in a range of 0.32 to 0.324. Alternatively, at a wavelength of 1550, the attenuation of the optical fiber 100 may be controlled to a value that may be in a range of 0.179 to 0.184.

[0083] In accordance with an embodiment of the present invention, the inner cladding 104 may have a radius R2, a thickness T2, and a refractive index Δ2. Specifically, the radius R2 of the inner cladding 104 may be in a range of 14 μm to 15 μm. Preferably, the radius R2 of the inner cladding 104 may be 14.5 um.

[0084] In some aspects of the present invention, the second up-dopant may be doped in the inner cladding 104 in a way such that the concentration of the second up-dopant in the inner cladding 104 varies along the radius R2 of the inner cladding 104. Further, the thickness T2 of the inner cladding 104 may be equal to a difference between a numerical value of the radius R2 of the inner cladding 104 and a numerical value of the radius R1 of the core 102 (i.e., T2=R2−R1). Additionally, the thickness T2 of the inner cladding 104 may be greater than the thickness T1 of the core 102. The thickness T2 of the inner cladding 104 may be in a range of 10 μm to 10.5 μm.

[0085] The inner cladding 104 may have a relative refractive index Δ2% that may be in a range of 0.01 to 0.05. The relative refractive index Δ2% of the inner cladding 104 may be radially distributed along the central axis 108 of the optical fiber 100. Particularly, the relative refractive index Δ2% of the inner cladding 104 may have a maximum value Δ2max and a minimum value Δ2 min (as shown later in FIG. 2). Moreover, the relative refractive index Δ2% may be less than the relative refractive index Δ1% of the core 102. Further, the refractive index Δ2 of the inner cladding 104 may be less than the refractive index Δ1 of the core 102. In other words, the refractive index Δ1 of the core 102 may be higher than the refractive index Δ2 of the inner cladding 104 such that the optical signal that propagates through the core 102 and that strikes a boundary between the core 102 and the inner cladding 104 at an angle that may be smaller than a critical angle will reflect into the core 102 by total internal reflection.

[0086] In accordance with an embodiment of the present invention, the outer cladding 106 may surround the inner cladding 104 may be made up of a material selected from at least one of, a pure silica glass, and the like. In particular, the outer cladding 106 may be made up of a silica glass that may be undoped and have a radius R3, a thickness T3, and a refractive index Δ3. Moreover, the radius R3 may be in a range of 61.5 μm to 62.5 μm, the thickness T3 of the outer cladding 106 may be in a range of 46.5 μm to 48.5 μm. And, the refractive index Δ3 may be equal to 0 such that the refractive index Δ1 of the core 102 may be greater than the refractive index Δ2 of the inner cladding 104 and the refractive index Δ2 of the inner cladding 104 may be greater than the refractive index Δ3 of the outer cladding 106. Further, the radius R1, the radius R2, and the radius R3 may have a predefined ratio in a range of 5.52 μm to 5.75 μm and may be given by the equation (R3−R1)/(R2−R1).

[0087] In an exemplary example, when the radius R1 is 4 μm, the radius R2 is 14 μm, and the radius R3 is 62.5 μm.

[0088] In one aspect of the present invention, the core 102 may have the refractive index Δ1 that is between 4.4 to 5.4, relative refractive index Δ1% between 0.33 to 0.36, radius R1 between 4.4 to 4.6, the core alpha between 3.58 to 4.65, and the MFD between 8.85 to 9.2. Particularly, the inner cladding 104 may have the relative refractive index Δ2% between 0.02 to 0.03 and the radius R2 between 14 μm to 15 μm. Moreover, the outer cladding 106 may have the relative refractive index Δ3% of 0 and the radius R3 between 61.5 μm to 62.5 am. Further, the optical fiber 100 may be fabricated based on the above numerical values and may have a cable cutoff between 1186 nm to 1194 nm.

[0089] For example, an optical fiber with the refractive index Δ1 of 4.4, the relative refractive index Δ1% of 0.33, the radius R1 of 4.5, the core alpha of 3.7, the MFD of core 102 of 9.2, the relative refractive index Δ2% of 0.02, the radius R2 14 μm, the relative refractive index Δ3% of 0 may demonstrate a cable cutoff of 1186 nm.

[0090] In another aspect of the present invention, the optical fiber 100 may be fabricated based on the above numerical values. The numerical values may demonstrate an attenuation of 0.321 Decibel/Kilometers (dB/km) at a wavelength of 1310 nm, an attenuation of 0.182 dB/km at a wavelength of 1550 nm, and an attenuation of 0.202 dB/km at a wavelength of 1625 nm. Moreover, the optical fiber 100 fabricated based on the above numerical values may demonstrate a MFD of 8.89 μm at a wavelength of 1310 nm. Further, the optical fiber 100 fabricated based on the above numerical values may have a cutoff wavelength of 1295 nm.

[0091] In yet another aspect of the present invention, the optical fiber 100 may be fabricated based on the above numerical values may demonstrate a MFD in a range of 8.7 to 9.5, a cutoff wavelength in a range of 1160 nm to 1360 nm, and a zero-dispersion in a range of 1300 nm to 1323 nm. For example, when the MFD is 8.9, the optical fiber 100 demonstrates the cutoff of 1294 nm and the zero-dispersion of 1317 nm. Alternatively, when the MFD is 8.92, the optical fiber 100 demonstrates the cutoff of 1286 nm and the zero-dispersion of 1316 nm.

[0092] In yet another aspect of the present invention, the optical fiber 100 may be fabricated based on the above numerical values and may experience a macro bend loss of less than 0.3 db/Km for 10 turns, 30 mm Mandrel diameter at a wavelength of 1625 nm. Particularly, the optical fiber 100 may experience the macro bend loss of less than 0.1 db/km for 10 turns, 30 mm Mandrel diameter at the wavelength of 1550 nm. Moreover, the optical fiber 100 fabricated based on the above numerical values may experience the macro bend loss of less than 1.5 db/km for 1 turn, 20 mm Mandrel diameter at a wavelength of 1625 nm. Further, the optical fiber 100 may experience the macro bend loss of less than 0.5 db/km for 1 turn, 20 mm Mandrel diameter, at the wavelength of 1550 nm. Furthermore, the optical fiber 100 fabricated based on the above numerical values may experience the macro bend loss of less than 0.1 db/km for 10 turns, 30 mm Mandrel diameter at a wavelength of 1550 nm.

[0093] The optical fiber 100 may experience the macro bend loss of less than 0.1 db/km for 10 turns, 30 mm Mandrel diameter at the wavelength of 1550 nm.

[0094] Alternatively, the optical fiber 100 fabricated based on the above numerical values may experience the macro bend loss of less than 0.5 db/km for 1 turns, 20 mm Mandrel diameter at the wavelength of 1550 nm. Specifically, the optical fiber 100 may experience the macro bend loss of less than 0.5 db/km for 1 turns, 20 mm Mandrel diameter at the wavelength of 1550 nm.

[0095] FIG. 2 is a graphical representation illustrating a Refractive Index (RI) profile of the optical fiber in accordance with an embodiment of the present invention. The graph 200 has a curve 202 that represents the RI profile of the optical fiber 100. In the radius versus relative refractive index graph x-axis of the graph 200 represents values of the radius R1, the radius R2, and the radius R3 of the core 102, the inner cladding 104, and the outer cladding 106, respectively, and a y-axis of the graph 200 represents values of the relative refractive index Δ1%, the relative refractive index Δ2%, and the relative refractive index Δ3% of the core 102, the inner cladding 104, and the outer cladding 106, respectively.

[0096] As depicted in FIG. 2, the core 102 doped with the first and second up-dopants, the inner cladding 104 doped with the second up-dopant, and the undoped outer cladding 106 generates the RI profile. The refractive index Δ1 of the core 102 has a maximum value that is given by Δ1max. In particular, the core 102 defines a core region such that the refractive index Δ1 of the core 102 is realized in the core region (i.e., within the radius R1 of the core 102). Moreover, the inner cladding 104 defines an inner cladding region such that the refractive index Δ2 of the inner cladding 104 is realized in the inner cladding region (i.e., within the radius R2 of the inner cladding 104). Further, the outer cladding 106 may define an outer cladding region such that the refractive index Δ3 of the outer cladding 106 is realized in the outer cladding region (i.e., within the radius R3 of the outer cladding 104).

[0097] The curve 202 transitions from the core region to the inner cladding region, thus generating the RI profile that is defined by a core peak 204 and an inner cladding peak 206. As shown by the curve 202, the core peak 204 is greater than the inner cladding peak 206. And, a peak radial distance R.sub.d between the core peak 204 and the inner cladding peak 206 may be in a range of 9 μm to 10 μm. The peak radial distance R.sub.d between the core peak 204 and the inner cladding peak 206 may be between (T1min+T2min) to (T1max+T2max).

[0098] For example, when T1min is 4.4 μm, T2min is 4.6 μm, T1max is 4.6 μm, and T2max is 5.4 μm, the radial distance between the core peak 204 and the inner cladding peak 206 is 4.4+4.6 to 4.6+5.4 i.e., 9 μm to 10 μm. Specifically, a low numerical value of the peak radial distance R.sub.d (i.e., 9 μm to 10 μm) and the difference in the refractive indexes Δ1 and Δ2 may facilitate in reduction of attenuation due to reduction in the relative refractive index between the core 102 and the inner cladding 104.

[0099] The refractive index Δ2 of the inner cladding 104 may have the maximum value i.e., Δ2max and the minimum value i.e., Δ2 min. Particularly, the curve 202 may transition from the core region to the inner cladding region when the refractive index Δ2 of the inner cladding 104 is at the minimum value i.e., Δ2 min. Moreover, the curve 202 may transition from the inner cladding region to the outer cladding region when the refractive index Δ2 of the inner cladding 104 is at the maximum value i.e., Δ2max.

[0100] In some aspects of the present invention, the maximum value i.e., Δ2max of the refractive index Δ2 is 0.03 and the minimum value i.e., Δ2 min of the refractive index Δ2 is 0.02. Further, as shown by the curve 202, the refractive index Δ3 of the outer cladding 106 is 0 along the thickness T3.

[0101] FIG. 3 is a snapshot illustrating a graphical representation depicting concentration profiles of first up dopant and second up dopant in the core 102, inner cladding 104, and the outer cladding 106 along with a resultant refractive index profile in accordance with another aspect of the present invention. The graph 300 may include a first curve 302, a second curve 304, and a third curve 306. In particular, the first curve 302 may depict a concentration profile of the first up dopant in the core 102, the inner cladding 104, and the outer cladding 106. Moreover, the first curve 302 depicts the core peak 204 that may be realized due to the up doping of the core 102 with the first up dopant (i.e., Cl) that may further facilitate the optical fiber 100 to have reduced attenuation without increasing macro bend losses. Further, the first curve 302 depicts that at a transition point 308 when the concentration profile transitions from the core 102 to the inner cladding 104, a first diffusion zone is formed that includes traces of the first up dopant diffusing from the core 102 to the inner cladding 104.

[0102] The second curve 304 may depict the inner cladding peak 206 that may be realized due to the up doping of the inner cladding 104 with the first up dopant (i.e., Cl). In particular, up doping may further facilitate the optical fiber 100 to have reduced attenuation without increasing macro bend losses. Moreover, the second curve 304 depicts that at a transition point 310 when the concentration profile transitions from the inner cladding 104 to the outer cladding 106, a second diffusion zone is formed that includes traces of the first up dopant diffusing from the inner cladding 104 to the outer cladding 106.

[0103] The third curve 306 may depict a resultant refractive index profile in the core 102, the inner cladding 104, and the outer cladding 106. The third curve 306 may be an actual resultant refractive index profile generated due to the up doping of the core 102 and the inner cladding 104 with the first and second up dopants.

[0104] An ideal refractive index profile is shown in FIG. 3 that depicts a step function.

[0105] Advantageously, the optical fiber 100 of the present invention may demonstrate reduced stresses and reduction in the attenuation. And, the up doping of the core 102 with Ge and Cl.sub.2 and the up doping of the inner cladding 104 with Cl.sub.2 may facilitate control of the microbend losses and macro-bend loss in the optical fiber 100. Moreover, the up doping of the core 102 with the first up-dopant (i.e., Ge) and the second up-dopant (i.e. Cl.sub.2) and the up doping of the inner cladding 104 with the second up-dopant (i.e. Cl.sub.2) may result in a net increase in the refractive index of the optical fiber 100 and thus facilitates the attenuation in the optical fiber 100 without causing hindrance in microbending. Further, the up doping of the inner cladding 104 with the second up-dopant (i.e., Cl.sub.2) may reduce stresses in the optical fiber 100 due to reducing viscosity facilitating stress reduction between the core and the inner cladding 104. Furthermore, the up doping of the core 102 with the first and second up-dopants and the up doping of the inner cladding 104 with the second up-dopant (i.e., Cl.sub.2) may facilitate the traveling of the optical signal within the optical fiber 100.

[0106] The foregoing descriptions of specific embodiments of the present technology have been presented for purposes of illustration and description. They are not intended to be exhaustive or to limit the present technology to the precise forms disclosed, and obviously many modifications and variations are possible in light of the above teaching. The embodiments were chosen and described in order to best explain the principles of the present technology and its practical application, to thereby enable others skilled in the art to best utilize the present technology and various embodiments with various modifications as are suited to the particular use contemplated. It is understood that various omissions and substitutions of equivalents are contemplated as circumstance may suggest or render expedient, but such are intended to cover the application or implementation without departing from the spirit or scope of the claims of the present technology.

[0107] While several possible embodiments of the invention have been described above and illustrated in some cases, it should be interpreted and understood as to have been presented only by way of illustration and example, but not by limitation. Thus, the breadth and scope of a preferred embodiment should not be limited by any of the above-described exemplary embodiments.

[0108] It will be apparent to those skilled in the art that other embodiments of the invention will be apparent to those skilled in the art from consideration of the specification and practice of the invention. While the foregoing written description of the invention enables one of ordinary skill to make and use what is considered presently to be the best mode thereof, those of ordinary skill will understand and appreciate the existence of variations, combinations, and equivalents of the specific embodiment, method, and examples herein. The invention should therefore not be limited by the above described embodiment, method, and examples, but by all embodiments and methods within the scope of the invention. It is intended that the specification and examples be considered as exemplary, with the true scope of the invention being indicated by the claims.