Abstract

The invention relates to an electrically conductive film (10) having an electrically nonconductive substrate layer (12), and an electrically conductive metal layer (14) that has a structure produced by material removal and that on a first side is joined, at least in sections, to the substrate layer (12).

Claims

1. An electrically conductive film for a cell contacting unit for a battery, the electrically conductive film having: an electrically nonconductive substrate layer; an electrically conductive metal layer that has a structure produced by material removal and that on a first side is joined, at least in sections, to the electrically nonconductive substrate layer; and an electrically nonconductive cover layer having a structure that is produced by material removal; wherein the electrically conductive metal layer is located on a second side and is joined, at least in sections, to the electrically nonconductive cover layer; wherein a material of which the electrically nonconductive substrate layer is made has a modulus of elasticity in the range of 10 to 100 megapascals; wherein the material of which the electrically nonconductive substrate layer is made has a lower modulus of elasticity than a material of which the electrically nonconductive cover layer is made; and wherein a difference between the modulus of elasticity of the material of which the electrically nonconductive substrate layer is made and the modulus of elasticity of the material of which the electrically nonconductive cover layer is made is at least 20 megapascals.

2. The electrically conductive film according to claim 1, wherein the electrically conductive film has contacting sections that are configured to be electroconductively connected to contact poles of unit cells.

3. The electrically conductive film according to claim 1, wherein the battery is a vehicle battery.

4. The electrically conductive film according to claim 1, wherein the electrically conductive metal layer includes multiple strip conductors.

5. The electrically conductive film according to claim 4, wherein the multiple strip conductors have a plurality of bent sections, where the strip conductors change of direction.

6. The electrically conductive film according to claim 5, wherein the multiple strip conductors have widths that differ from one another.

7. The electrically conductive film according to claim 6, wherein the widths range between 5 millimeters and 1 millimeter.

8. The electrically conductive film according to claim 1, wherein the electrically conductive film is an integral part of a cell voltage tap system.

9. The electrically conductive film according to claim 1, wherein the electrically conductive film has a protective film on a side facing unit cells.

10. The electrically conductive film according to claim 2, wherein the electrically conductive film is an integral part of a cell voltage tap system, the electrically conductive film has a protective film on a side facing unit cells.

11. The electrically conductive film according to claim 10, wherein the electrically conductive film has a protective film on a side facing the unit cells.

12. The electrically conductive film according to claim 1, wherein the electrically nonconductive substrate layer is made of a thermoplastic plastic, polyethylene naphthalate, or polyethylene terephthalate.

13. The electrically conductive film according to claim 1, wherein the electrically nonconductive substrate layer is made of a thermoplastic elastomer or a thermoplastic polyurethane.

14. The electrically conductive film according to claim 1, wherein the electrically conductive metal layer is made of copper, a copper alloy, aluminum, copper-clad aluminum (CCA), and/or an aluminum alloy.

15. The electrically conductive film according to claim 1, wherein the electrically nonconductive substrate layer is made of a thermoplastic plastic, polyethylene naphthalate, or polyethylene terephthalate, and the electrically conductive metal layer is made of copper, a copper alloy, aluminum, copper-clad aluminum (CCA), and/or an aluminum alloy.

16. The electrically conductive film according to claim 1, wherein the electrically nonconductive substrate layer is made of a thermoplastic elastomer or a thermoplastic polyurethane, and the electrically conductive metal layer is made of copper, a copper alloy, aluminum, copper-clad aluminum (CCA), and/or an aluminum alloy.

17. The electrically conductive film according to claim 1, wherein the electrically nonconductive substrate layer has an elastically deformable design.

18. The electrically conductive film according to claim 1, wherein the electrically conductive metal layer includes multiple strip conductors, the multiple strip conductors have a plurality of bent sections, the bent ections are arranged between the contacting sections.

19. The electrically conductive film according to claim 1, wherein the electrically conductive metal layer includes multiple strip conductors, the multiple strip conductors have a plurality of bent sections, wherein two bent sections are arranged in between two adjacent contacting sections.

20. The electrically conductive film according to claim 1, wherein the electrically conductive metal layer comprises strip conductors that are heating conductors that extend in a meandering manner.

Description

(1) Preferred embodiments of the invention are explained and described in greater detail below with reference to the appended drawings, which show the following:

(2) FIG. 1 shows the manufacture of an electrically conductive film according to the invention in a schematic illustration;

(3) FIG. 2 shows the manufacture of an electrically conductive film according to the invention in a schematic illustration;

(4) FIG. 3 shows the manufacture of an electrically conductive film according to the invention in a schematic illustration;

(5) FIG. 4 shows the manufacture of an electrically conductive film according to the invention in a schematic illustration;

(6) FIG. 5 shows one exemplary embodiment of the electrical heating device according to the invention in a schematic illustration;

(7) FIG. 6 shows one exemplary embodiment of the cell contacting unit according to the invention in a schematic illustration;

(8) FIG. 7 shows one exemplary embodiment of the manufacturing method according to the invention in a block diagram;

(9) FIG. 8 shows the width profile of multiple strip conductors of a metal layer of an electrically conductive film according to the invention; and

(10) FIG. 9 shows one exemplary embodiment of the electrical heating device according to the invention in a schematic illustration.

(11) FIG. 1 on the left side shows an electrically conductive film 10 having an electrically nonconductive substrate layer 12 and an electrically conductive metal layer 14.

(12) The substrate layer 12 is made of a material that has a modulus of elasticity in the range of 120 to 1200 megapascals. For example, the substrate layer 12 may be made of polyethylene naphthalate or polyethylene terephthalate.

(13) The metal layer 14 is made of copper and aluminum, for example copper-clad aluminum, and on a first side is joined to the substrate layer 12.

(14) The right side of FIG. 1 shows the film 10 illustrated on the left side of FIG. 1, after material removal from the metal layer 14 has taken place. The produced structure of the metal layer 14 has a strip conductor 20 having a bent section (concealed).

(15) FIG. 2 on the left side shows an electrically conductive film 10 having an electrically nonconductive substrate layer 12, an electrically conductive metal layer 14, and an electrically nonconductive cover layer 16.

(16) The substrate layer 12 is made of a material that has a modulus of elasticity in the range of 120 to 1200 megapascals. For example, the substrate layer 12 may be made of polyethylene naphthalate or polyethylene terephthalate.

(17) The metal layer 14 is made of copper and aluminum, for example copper-clad aluminum, and on a first side is joined to the substrate layer 12 and on a second side is joined to the cover layer 16.

(18) The cover layer 16 is made of a material that has a modulus of elasticity in the range of 120 to 1200 megapascals. For example, the cover layer 16 may be made of polyethylene naphthalate or polyethylene terephthalate.

(19) The right side of FIG. 2 shows the film 10 illustrated on the left side of FIG. 2, after material removal from the metal layer 14 and the cover layer 16 has taken place. The produced structure of the metal layer 14 is different from the produced structure of the cover layer 16.

(20) FIG. 3 on the left side shows an electrically conductive film 10 having an electrically nonconductive substrate layer 12, an electrically conductive metal layer 14, an electrically nonconductive cover layer 16, and an electrically nonconductive supporting layer 18.

(21) The substrate layer 12 is made of a material that has a modulus of elasticity in the range of 10 to 100 megapascals. For example, the substrate layer 12 may be made of a thermoplastic elastomer such as a thermoplastic polyurethane.

(22) The metal layer 14 is made of copper and aluminum, for example copper-clad aluminum, and on a first side is joined to the substrate layer 12 and on a second side is joined to the cover layer 16.

(23) The cover layer 16 is made of a material that has a modulus of elasticity in the range of 120 to 1200 megapascals. For example, the cover layer 16 may be made of polyethylene naphthalate or polyethylene terephthalate. The material of which the substrate layer 12 is made thus has a lower modulus of elasticity than the material of which the cover layer 16 is made. In addition, the difference between the modulus of elasticity of the material of which the substrate layer 12 is made and the modulus of elasticity of the material of the material of which the cover layer 16 is made is greater than 20 megapascals.

(24) The supporting layer 18 is made of a material that has a modulus of elasticity in the range of 120 to 1200 megapascals. For example, the supporting layer 18 may be made of polyethylene naphthalate or polyethylene terephthalate, wherein the material thickness of the supporting layer 18 is greater than the respective material thicknesses of the other layers 12, 14, 16. In addition, the supporting layer 18 is joined to the side of the substrate layer 12 opposite from the metal layer 14, wherein the adhesion of the supporting layer 18 to the substrate layer 12 allows damage-free detachment of the supporting layer 18 from the substrate layer 12.

(25) The right side of FIG. 3 shows the film 10 illustrated on the left side of FIG. 3, after material removal from the metal layer 14 and the cover layer 16 on the one hand, and detachment of the supporting layer 18 from the substrate layer 12 on the other hand, have taken place. The produced structure of the metal layer 14 differs from the produced structure of the cover layer 16. However, it is also conceivable for the material removal to take place in such a way that the produced structure of the cover layer 16 is the same, in its entirety or in sections, as the produced structure of the metal layer 14.

(26) FIG. 4 on the left side shows an electrically conductive film 10 having an electrically nonconductive substrate layer 12, an electrically conductive metal layer 14, and an electrically nonconductive supporting layer 18.

(27) The substrate layer 12 is made of a material that has a modulus of elasticity in the range of 120 to 1200 megapascals. For example, the substrate layer 12 may be made of polyethylene naphthalate or polyethylene terephthalate.

(28) The metal layer 14 is made of copper and aluminum, for example copper-clad aluminum, and on a first side is joined to the substrate layer 12.

(29) The supporting layer 18 is made of a material that has a modulus of elasticity in the range of 120 to 1200 megapascals. For example, the supporting layer 18 may be made of polyethylene naphthalate or polyethylene terephthalate, wherein the material thickness of the supporting layer 18 is greater than the respective material thicknesses of the other layers 12, 14. In addition, the supporting layer 18 is joined to the metal layer 14, wherein the adhesion of the supporting layer 18 to the metal layer 14 allows damage-free detachment of the supporting layer 18 from the metal layer 14.

(30) The right side of FIG. 4 shows the film 10 illustrated on the left side of FIG. 4, after material removal from the metal layer 14 and the substrate layer 12 on the one hand, and detachment of the supporting layer 18 from the metal layer 14 on the other hand, have taken place. The produced structure of the metal layer 14 and the produced structure of the substrate layer 12 are the same.

(31) FIG. 5 shows an electrical heating device 100 having an electrically conductive film 10. The electrically conductive film 10 has an electrically nonconductive substrate layer 12 and an electrically conductive metal layer 14.

(32) The metal layer 14 includes a structure that is produced by material removal, and on a first side is joined to the substrate layer 12. The structure of the metal layer 14 has a strip conductor 20 that is designed as a heating conductor and that in the sections 24a-24e extends in a meandering manner and thus includes a plurality of bent sections 22. A contact section 26a, 26b is situated in each case at the ends of the heating conductor, wherein the heating conductor of the heating device 100 is suppliable with electrical energy via the contacting sections 26a, 26b.

(33) FIG. 6 shows a cell contacting unit 200 for a battery, namely, a vehicle battery. The cell contacting unit 200 has an electrically conductive film 10 that includes an electrically nonconductive substrate layer 12 and an electrically conductive metal layer 14.

(34) The metal layer 14 has a structure that is produced by material removal, wherein the structure of the metal layer 14 includes multiple strip conductors 20 that have a plurality of bent sections 22.

(35) The electrically conductive film 10 also includes contacting sections 26a-26d that are electroconductively connected to contact poles 204a-204d of unit cells 202a-202d.

(36) FIG. 7 shows a manufacturing method for an electrically conductive film 10. The manufacturing method is initiated by the following step: 300) providing a film 10 having an electrically nonconductive substrate layer 12, an electrically conductive metal layer 14, and an electrically nonconductive cover layer 16.

(37) After the film 10 has been provided, the following steps may be carried out: 302) producing a structure of the metal layer 14 by means of a machining process; and 308) producing a structure of the cover layer 16 by means of a machining process.

(38) During production of the structure of the metal layer 14, multiple strip conductors 20 are created, wherein the production of the structure of the metal layer 14 by means of a machining process comprises the following two steps: 304) producing material elevations in the metal layer 14 by means of an embossing roller; and 306) removing the material elevations in the metal layer 14 by means of a milling wheel.

(39) The product ion of the structure of the cover layer 16 by means of a machining process analogously comprises the following two steps: 310) producing material elevations in the cover layer 16 by means of the embossing roller; and 312) removing the material elevations in the cover layer 16 by means of the milling wheel.

(40) The production of the structure of the metal layer 14 and the production of the structure of the cover layer 16 take place at the same time, namely, by the embossing roller producing sufficiently projecting material elevations in the metal layer 14 and the cover layer 16 so that the material elevations in the metal layer 14 and the cover layer 16 produced by the embossing roller may at the same time be removed by the milling wheel. The produced structure of the cover layer 16 is thus the same as the produced structure of the metal layer 14. Alternatively, however, by using an embossing roller that has embossing sections with different heights, it is also possible to produce electrically conductive films 10 whose various layers have different structural patterns.

(41) FIG. 8 shows the structure of multiple strip conductors 20 of a metal layer 14. All strip conductors 20 in each case have multiple strip conductor sections 28a-28e having strip conductor widths B1-B5 that are different from one another. The strip conductor sections 28a-28e of the strip conductors 20 extend in an offset manner and in parallel to one another. The strip conductor width B1-B5 of successive strip conductor sections 28a-28e increases along the course of the strip conductor. The strip conductor section 28a has a strip conductor width B1 of 4.2 millimeters. The strip conductor section 28b has a strip conductor width B2 of 3.8 millimeters. The strip conductor section 28c has a strip conductor width B3 of 3.2 millimeters. The strip conductor section 28d has a strip conductor width B4 of 2.3 millimeters. The strip conductor section 28e likewise has a strip conductor width B5 of 2.3 millimeters. Bent transition sections 30a-30d are situated between the strip conductor sections 28a-28e. The ends of the individual strip conductors 20 are positioned on one side, laterally offset relative to one another.

(42) FIG. 9 shows an electrical heating device 100 having an electrically conductive film 10. The electrically conductive film 10 has an electrically nonconductive substrate layer 12 and an electrically conductive metal layer 14.

(43) The metal layer 14 includes a structure that is produced by material removal, and on a first side is joined to the substrate layer 12. The structure of the metal layer 14 has two strip conductors 20 that are designed as heating conductors, and that extend continuously in a meandering manner and thus include a plurality of bent heating conductor sections 22. The two heating conductors that extend in a meandering manner each have a nonuniformly bent design in sections, wherein the proportion of bent heating conductor sections is greater than 90%. Contacting sections 26a, 26b are situated on the respective ends of the heating conductors, wherein the heating conductors of the heating device 100 are suppliable with electrical energy via the contacting sections 26a, 26b.

(44) The invention preferably relates to a heating element having an elastically and/or plastically deformable substrate, a strip conductor that is situated on the substrate, and a cover layer whose base area is congruent with the base area of the strip conductor, and whose tensile strength is at least twice that of the strip conductor.

(45) The invention further preferably relates to a connection conductor having at least one machined electrically nonconductive nonconductor zone, and at least one strip conductor that has a bent course, at least in sections, within the conductor level.

LIST OF REFERENCE NUMERALS

(46) 10 electrically conductive film 12 substrate layer 14 metal layer 16 cover layer 18 supporting layer 20 strip conductor 22 bent sections 24a-24e meandering sections 26a-26d contacting sections 28a-28e strip conductor sections 30a-30d transition sections 100 electrical heating device 200 cell contacting unit 202a-202d unit cells 204a-204d contact poles 300-312 method steps B1-B5 strip conductor widths