Abstract

A fatigue-resistant layered elastomer (3) which is extruded into the long linear structure by using thermoplastic polyester elastomer as raw materials, then is curled and bonded to form a layered body of a certain thickness. The contact parts of adjacent linear structures are fused together to form continuously bonded points (1) or intermittently bonded points (2), among which, the proportion of continuously bonded points (1) is over 20%. When the proportion of continuously bonded points (1) is greater than 20%, the hardness loss rate after fatigue-resistant cyclic compression is less than 23%. The larger the proportion of continuously bonded points (1), the better the cyclic compression durability. Therefore, by increasing the proportion of continuously bonded points (1) of layered elastomers (3), it enables us to obtain products with cyclic compression durability.

Claims

1. It relates to a fatigue-resistant layered elastomer which is extruded into the long linear structure by using thermoplastic polyester elastomer as raw materials, then is curled and bonded to form a layered body of a certain thickness, and its characteristics are that: The contact parts of adjacent linear structures are fused together to form continuously bonded points (1) or intermittently bonded points (2), among which, the proportion of continuously bonded points (1) is over 20%.

2. For fatigue-resistant layered elastomer according to claims 1, its characteristics are that: The melt index of the raw material of the above-mentioned thermoplastic polyester elastomer is 15-25 g/10 min.

3. For fatigue-resistant layered elastomer according to claims 1, its characteristics are that: The melting point of the above-mentioned raw material of thermoplastic polyester elastomer is below 180° C.;

4. For fatigue-resistant layered elastomer according to claims 1, its characteristics are that: The continuously bonded point (1) mentioned is a fusing part of ≥5 mm long.

5. For fatigue-resistant layered elastomer according to claims 1, its characteristics are that: After the layered elastomer (3) mentioned is cyclically compressed for 80,000 times under the compression force of 750N, the hardness loss rate will be less than 25%.

6. For fatigue-resistant layered elastomer according to claims 1, its characteristics are that: The 40% indentation hardness of the layered elastomer (3) mentioned is 100N-350N.

7. For fatigue-resistant layered elastomer according to claims 1, its characteristics are that: The thickness of the layered elastomer (3) mentioned is 20 mm-200 mm and the density is 30-100 kg/m.sup.3.

8. For fatigue-resistant layered elastomer according to claims 1, its characteristics are that: The continuous filaments of the layered elastomer (3) mentioned are round solid filaments, special-shaped filaments or hollow filaments.

9. For fatigue-resistant layered elastomer according to claims 1, its characteristics are that: The soft block of the raw material of thermoplastic polyester elastomer mentioned is polytetramethylene ether glycol.

10. For fatigue-resistant layered elastomer according to claims 1, its characteristics are that: The content of polytetramethylene ether glycol soft block contained in the raw material of the thermoplastic polyester elastomer mentioned is 70%, melting point of the raw material is 171° C., and the melt index is 20 g/10 min.

Description

DESCRIPTION OF FIGURES

[0020] FIG. 1 is a structural diagram of layered elastomer products, with 1. Continuously bonded point; 2. Intermittently bonded point, and 3. Layered elastomer.

[0021] FIGS. 2 and 3 illustrates Table 1 and 2 respectively.

DETAILED DESCRIPTION OF EMBODIMENTS

[0022] Specific embodiments of the invention will be described combined with the following figures.

[0023] As the polyester thermoplastic elastomer, dimethyl terephthalate (DMT), 1,4-butanediol (1,4-BD), polytetramethylene glycol (PTMG), tetrabutyl titanate (TBT) catalyst and stabilizer Irganox 1010 shall undergo the esterification reaction at 230° C., and after the removal amount of by-product methanol reaches more than 98% of the theoretical value, it shall heat up to 245° C. and reduce pressure to 100 Pa in vacuum for polycondensation, and after being polymerized to a desired viscosity, it shall form grains and finally generate the polyether-ester block copolymer elastomers. The formula of the obtained thermoplastic elastomer material is recorded in Table 1, wherein, the melt index is controlled by means of controlling manufacturing condition parameters such as polymerization time.

[0024] Table 1 is illustrated in FIG. 2

The specific test method is as follows: [0025] 1. Thickness: Randomly take 3 samples, measure the thickness of products using the thickness gauge, and calculate the average value. [0026] 2. Density: Put the product in the drying oven, and set the oven at 80° C.*3 hr. After removal of moisture, measure the length, width and height of the product and calculate the volume of the product, and use precision balance to get the weight which is corrected to three decimal places, then divide the weight by the volume to calculate the density. [0027] 3. Wire diameter: Randomly take 5 fibers from the three-dimensional network structure, and use 20-fold optical microscope and scale to measure the diameters of 3 positions, calculate the average diameter of each fiber, then calculate the average value of 5 fibers; [0028] 4. 40% indentation hardness test: At the constant temperature of 23° C., put the product between the upper and lower compression plates, and compress the product to reach the strain 40% at a test speed of 100 mm/min. By using the upper compression plate to compress the product downwards, the load cell at the upper end will sense the pressure, convert the pressure into the voltage signal and send the voltage signal to the display for analysis. Meanwhile, display pressure value on the screen, and take average value of three tests. [0029] 5. Hardness loss rate after fatigue-resistant cyclic compression: At the constant temperature of 23° C., put the product on the lower platform of the cyclic compression tester, compress the product cyclically at the compression force of 750N and a frequency of 70 time/minute, then evaluate the performance of the product after 80,000 times of compression. Hardness loss rate after fatigue-resistant cyclic compression=(40% indentation hardness before product test-40% indentation hardness after product test)/40% indentation hardness before product test*100%, measure 3 samples and take average value. [0030] 6. Bonded point: Take the 5 cm*5 cm sample and use precision balance to get the weight which is corrected to the first decimal place, as shown in FIG. 1, define the intersection point with a length <5 mm at the fusing part between the linear structures of the layered elastomer 3 as the intermittently bonded point 2 and define the intersection point with a length ≥5 mm at the fusing part between the linear structures as the continuously bonded point 1; The counter shall carefully strip the intersection parts between linear structures , carefully observe and calculate the quantity of intermittently bonded point 2 and continuously bonded point 1, and after the quantity of obtained bonded points is divided by the sample weight, it can obtain the quantity of intermittently bonded points and continuously bonded points per unit volume (unit: pcs./g). Proportion of continuously bonded points=quantity of continuously bonded points/(quantity of continuously bonded points+quantity of intermittently bonded points).

Embodiment 1

[0031] By sending the raw materials of polyester elastomer A1 into the extruder, the materials shall be heated up to a molten state of 225° C. in the extruder and conveyed to the spinning die through the metering pump, the continuous linear structure fibers are sprayed from the spinning die into the water and are bent into a ring. The contact parts between the linear structures are fused together, the traction rate is 0.4 m/min, infrared insulation method is adopted between the spinning die and the lower water tank, the well-woven continuous linear structure fibers are compressed by a mold in 30° C. warm water to make both sides flat, and finally, the three-dimensional layered elastomer 3 is formed. The above method is used to test the layered elastomer, thus obtaining the physical parameters as shown in Table 2. The network structure density of the layered elastomer 3 is 60 kg/m.sup.3, and the proportion of continuously bonded points of the layered elastomer 3 obtained is 26%, the 40% indentation hardness is 189N, and the hardness loss rate after fatigue-resistant cyclic compression is 22%.

Embodiment 2

[0032] The specific implementation method is same as that of embodiment 1, however, the raw material adopted is changed to polyester elastomer B1, and the proportion of continuously bonded points of layered elastomer 3 obtained is 31%, the 40% indentation hardness is 133N, and the hardness loss rate after fatigue-resistant cyclic compression is 15%.

Comparison Example 1

[0033] The specific implementation method is same as that of embodiment 1, however, the raw material adopted is changed to polyester elastomer A2, and the proportion of continuously bonded points of three-dimensional network structure is 17%, the 40% indentation hardness is 171N, and the hardness loss rate after fatigue-resistant cyclic compression is 31%.

Comparison Example 2

[0034] The specific implementation method is same as that of embodiment 1, however, the raw material adopted is changed to polyester elastomer B2, and the proportion of continuously bonded points of three-dimensional network structure is 13%, the 40% indentation hardness is 123N, and the hardness loss rate after fatigue-resistant cyclic compression is 26%.

Comparison Example 3

[0035] The specific implementation method is same as that of embodiment 1, however, the raw material adopted is changed to polyester elastomer C1, and the proportion of continuously bonded points of three-dimensional network structure is 14%, the 40% indentation hardness is 244N, and the hardness loss rate after fatigue-resistant cyclic compression is 33%.

[0036] Table 2 is illustrated in FIG. 3. By comparing Embodiment 1-3 and comparison examples 1-3, it can be seen that when the proportion of continuously bonded points is less than 20%, the hardness loss rate after fatigue-resistant cyclic compression will exceed 25%, and the less the continuously bonded points 1, the worse the cyclic compression durability. Therefore, by increasing the proportion of continuously bonded points of layered elastomer 3, it enables us to obtain products with cyclic compression durability. When the proportion of continuously bonded points is 31%, the hardness loss rate after fatigue-resistant cyclic compression is only 15%, and the fatigue durability of product is the optimal.

[0037] By comparing embodiment 1 and comparison example 1, when the melt index is 35 g/10 min, the proportion of continuously bonded points of the layered elastomer 3 is only 17%. At this time, although the 40% indentation hardness can reach 171N, the hardness loss rate after fatigue-resistant cyclic compression can rise to 31%. It can be seen that when the melt index is greater than 25 g/10 min, the proportion of continuously bonded points decreases and the compression durability of the product becomes worse. It is probably because that the larger the melt index, the better the processing flowability of the materials, the quicker the speed of the continuous linear structure outflowing from the spinning die; When the traction rate is controlled as constant, the wire diameter of the continuous linear structure will be thinner, and when the wire diameter is thinner, there will be a lower probability of forming continuously bonded point 1 at the fusing position, and therefore, the proportion of continuously bonded points of the final product will be decreased.

[0038] By comparing embodiment 2 and comparison example 2, when the melt index is 8 g/10 min, the proportion of continuously bonded points of the layered elastomer 3 is only 13%. At this time, although the 40% indentation hardness can reach 123N, the hardness loss rate after fatigue-resistant cyclic compression can rise to 26%. It can be seen that when the melt index is less than 15 g/10 min, the proportion of continuously bonded points decreases and the compression durability of the product becomes worse. It is probably because that the smaller the melt index, the worse the processing flowability of the materials, the slower the speed of the continuous linear structure outflowing from the spinning die; When the traction rate is controlled as constant, the wire diameter of the continuous linear structure will be thicker, and although the wire diameter is thicker, it is because of relatively low flow speed of the continuous linear structure, thus causing decrease in temperature earlier in the falling process; therefore, fusing parts formed after being put into water become less as well as there is a lower probability of forming continuously bonded point 1 at the fusing position, and finally, the proportion of continuously bonded points of the final product will be decreased.

[0039] By comparing embodiment 1 and comparison example 3, when the melting point of polyester elastomer is 207° C., although the melt index is same, the proportion of continuously bonded points of the layered elastomer 3 obtained in comparison example 3 is only 14%. At this time, although the 40% indentation hardness can reach 244N, the hardness loss rate after fatigue-resistant cyclic compression can rise to 33%. It can be seen that when the melting point of polyester elastomer is greater than 180° C., the proportion of continuously bonded points decreases and the compression durability of the product becomes worse. It is probably because that the melting point is higher. After it is extruded out at 225° C. at the molten state, the continuous linear structures are not easy to be bonded together, fusing parts of products formed become less and there is a lower probability of forming continuously bonded point 1 at the fusing position. Although the products with certain hardness can be obtained at high melting point, the proportion of continuously bonded points is not high, eventually leading to poor cyclic compression durability.

[0040] The above-mentioned description is an explanation of the invention but not the restriction over the invention, and the invention can be modified in any form without going against the spirit of the invention. For example, the filaments of the layered elastomer 3 are round solid filaments in the above-mentioned embodiments and the comparison examples, or the special-shaped filaments or hollow filaments in other modes of implementation.