Abstract
The method of curing reinforced concrete uses a liquid membrane-forming curing compound for the curing of reinforced concrete, but without fully coating the reinforced concrete with the curing compound, thus allowing for oxygen permeation through the reinforced concrete to effect passive layer formation on steel rebar embedded in the reinforced concrete. Prior to curing, a mask is applied to at least one surface of a slab of reinforced concrete, such that the mask covers about 10% of the surface area of the at least one surface. The at least one surface of the slab of reinforced concrete is then coated with a liquid membrane-forming curing compound. The liquid membrane-forming curing compound is allowed to dry, thus forming a curing compound layer on the at least one surface of the slab of reinforced concrete. The mask is then removed to form at least one uncoated region.
Claims
1. A method of curing reinforced concrete, comprising the steps of: applying a mask to at least one surface of a slab of reinforced concrete, the mask covering about 10% of the surface area of the at least one surface; coating the at least one surface of the slab of reinforced concrete with a liquid membrane-forming curing compound; drying the liquid membrane-forming curing compound to form a curing compound layer on the about 90% unmasked area of the at least one surface of the slab of reinforced concrete; and removing the mask from the at least one surface of the slab of reinforced concrete to form at least one uncoated region on the at least one surface of a slab of reinforced concrete.
2. The method of curing reinforced concrete as recited in claim 1, wherein the step of applying a mask to the at least one surface of the slab of reinforced concrete comprises partially covering the at least one surface of the slab of reinforced concrete with adhesive tape.
3. The method of curing reinforced concrete as recited in claim 1, wherein the liquid membrane-forming compound comprises a curing compound selected from the group consisting of a paraffin emulsion-based liquid membrane-forming curing compound, a bitumen-based liquid membrane-forming curing compound, and a wax-based liquid membrane-forming curing compound.
4. Reinforced concrete made according to the method of claim 1.
Description
BRIEF DESCRIPTION OF THE DRAWINGS
[0011] FIG. 1A, FIG. 1B, FIG. 1C, FIG. 1D, and FIG. 1E are diagrammatic perspective views showing successive steps of curing a block or slab of reinforced concrete in a method of curing reinforced concrete.
[0012] FIG. 1F is a diagrammatic perspective views showing an alternative mask configuration in the method of curing reinforced concrete.
[0013] FIG. 2A is a plot of corrosion current as a function of time (in days) for reinforced concrete samples treated by the method of curing reinforced concrete, including samples using different curing compounds, samples fully coated with the different curing compounds, for an entirely sealed sample, for a sample submerged in water, and for a completely uncoated control sample, where each reinforced concrete sample has a water-to-cement (W/C) ratio of 0.3 and was subjected to an admixed threshold total chloride content of 0.4%.
[0014] FIG. 2B is a plot of corrosion current as a function of time (in days) for reinforced concrete samples treated by the method of curing reinforced concrete, including samples using different curing compounds, samples fully coated with the different curing compounds, for an entirely sealed sample, for a sample submerged in water, and for a completely uncoated control sample, where each reinforced concrete sample has a water-to-cement (W/C) ratio of 0.45 and was subjected to an admixed threshold total chloride content of 0.4%.
[0015] FIG. 2C is a plot of corrosion current as a function of time (in days) for reinforced concrete samples treated by the method of curing reinforced concrete, including samples using different curing compounds, samples fully coated with the different curing compounds, for an entirely sealed sample, for a sample submerged in water, and for a completely uncoated control sample, where each reinforced concrete sample has a water-to-cement (W/C) ratio of 0.6 and was subjected to an admixed threshold total chloride content of 0.4%.
[0016] FIG. 3A is a plot of corrosion potential as a function of time (in days) for reinforced concrete samples treated by the method of curing reinforced concrete, including samples using different curing compounds, samples fully coated with the different curing compounds, for an entirely sealed sample, for a sample submerged in water, and for a completely uncoated control sample, where each reinforced concrete sample has a water-to-cement (W/C) ratio of 0.3 and was subjected to an admixed threshold total chloride content of 0.4%.
[0017] FIG. 3B is a plot of corrosion potential as a function of time (in days) for reinforced concrete samples treated by the method of curing reinforced concrete, including samples using different curing compounds, samples fully coated with the different curing compounds, for an entirely sealed sample, for a sample submerged in water, and for a completely uncoated control sample, where each reinforced concrete sample has a water-to-cement (W/C) ratio of 0.45 and was subjected to an admixed threshold total chloride content of 0.4%.
[0018] FIG. 3C is a plot of corrosion potential as a function of time (in days) for reinforced concrete samples treated by the method of curing reinforced concrete, including samples using different curing compounds, samples fully coated with the different curing compounds, for an entirely sealed sample, for a sample submerged in water, and for a completely uncoated control sample, where each reinforced concrete sample has a water-to-cement (W/C) ratio of 0.6 and was subjected to an admixed threshold total chloride content of 0.4%.
[0019] FIG. 4A is a plot of corrosion potential as a function of time (in days) for reinforced concrete samples treated by the method of curing reinforced concrete, including samples using different curing compounds, samples fully coated with the different curing compounds, for an entirely sealed sample, for a sample submerged in water, and for a completely uncoated control sample, where each reinforced concrete sample has a water-to-cement (W/C) ratio of 0.6 and was immersed in 5% NaCl brine solution.
[0020] FIG. 4B is a plot of corrosion current as a function of time (in days) for reinforced concrete samples treated by the method of curing reinforced concrete, including samples using different curing compounds, samples fully coated with the different curing compounds, for an entirely sealed sample, for a sample submerged in water, and for a completely uncoated control sample, where each reinforced concrete sample has a water-to-cement (W/C) ratio of 0.6 and was immersed in 5% NaCl brine solution.
[0021] FIG. 4C is a plot showing the chloride penetration profile into the concrete of the samples of FIGS. 4A and 4B.
[0022] FIG. 5A is a chart showing the results of gravimetric mass loss analysis for the steel rebars of the samples of FIGS. 2A-3C.
[0023] FIG. 5B is a chart showing the results of gravimetric mass loss analysis for the steel rebars of the samples of FIGS. 4A and 4B.
[0024] Similar reference characters denote corresponding features consistently throughout the attached drawings.
DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS
[0025] The method of curing reinforced concrete uses a liquid membrane-forming curing compound for the curing of reinforced concrete, but without fully coating the reinforced concrete with the curing compound, thus allowing for oxygen permeation through the reinforced concrete to effect passive layer formation on steel rebar embedded in the reinforced concrete. It should be understood that the configuration and relative dimensions of the reinforced concrete slab RC shown in FIG. 1A are shown for exemplary purposes only. It should be further understood that the method of curing reinforced concrete is not limited to any particular concrete mixture.
[0026] As shown in FIG. 1B, prior to curing, a mask is applied to at least one surface of the slab of reinforced concrete RC, such that the mask covers about 10% of the surface area of the at least one surface. In the non-limiting example of FIG. 1B, a plurality of squares of adhesive tape T are applied to multiple surfaces of the slab of reinforced concrete RC, such that about 10% of the surface area of the slab of reinforced concrete RC is covered. It should be understood that the square shape of the pieces of tape T and the particular arrangement of tape T are shown for exemplary purposes only in FIG. 1B. Another example is shown in FIG. 1F, in which the tape T is applied in multiple strips wrapped around the slab of reinforced concrete RC. It should be further understood that the use of adhesive tape T is only one example of a mask material, and that any suitable type of mask may be used. It should also be understood that any desired number of surfaces of the slab of reinforced concrete RC may be masked, and that the coverage of all surfaces in FIGS. 1B and 1F is shown for exemplary purposes only.
[0027] As shown in FIG. 1C, following application of the mask, the at least one surface of the slab of reinforced concrete RC is coated with a liquid membrane-forming curing compound CC. In FIG. 1C, the liquid membrane-forming curing compound CC is shown being sprayed on the slab of reinforced concrete RC. However, it should be understood that the spraying is shown for exemplary purposes only and that any other suitable method of application, such as painting, dipping, or the like may be used. The liquid membrane-forming curing compound CC is allowed to dry, thus forming a curing compound layer CC on the at least one surface of the slab of reinforced concrete RC. In FIG. 1D, the curing compound layer CC is shown as being transparent. However, it should be understood that the choice of a transparent curing compound is shown in FIG. 1D for exemplary purposes only, and that any suitable type of curing compound, including opaque curing compounds, may be used. As shown in FIG. 1E, the mask is then removed to form at least one uncoated region U on the at least one surface of a slab of reinforced concrete RC. The at least one uncoated region U allows environmental oxygen to permeate into the concrete to effect passive layer formation on the steel rebar embedded in the reinforced concrete RC.
[0028] As will be explained in detail below, in order to test the method of curing reinforced concrete, reinforced concrete slabs were prepared, including (a) control specimens, which were completely uncoated and unsealed, and which were cured using the wet burlap water-sprinkling method (indicated as “Unsealed” in FIGS. 2A-4B); (b) specimens that were fully sealed within a wrapping of plastic (indicated as “Sealed” in FIGS. 2A-4B); (c) specimens that were completely submerged in water (indicated as “Sub” in FIGS. 2A-4B); (d) specimens that were fully coated with a paraffin emulsion-based liquid membrane-forming curing compound (indicated as “C1” in FIGS. 2A-4B); (e) specimens that were fully coated with a bitumen-based liquid membrane-forming curing compound (indicated as “C2” in FIGS. 2A-4B); (f) specimens that were fully coated with a wax-based liquid membrane-forming curing compound (indicated as “C3” in FIGS. 2A-4B); (g) specimens that were 90% coated with the paraffin emulsion-based liquid membrane-forming curing compound (indicated as “C1 90%” in FIGS. 2A-4B); (h) specimens that were 90% coated with the bitumen-based liquid membrane-forming curing compound (indicated as “C2 90%” in FIGS. 2A-4B); and (i) specimens that were 90% coated with the wax-based liquid membrane-forming curing compound (indicated as “C3 90%” in FIGS. 2A-4B).
[0029] For the results of FIGS. 2A-3C, each reinforced concrete specimen was shaped as a rectangular prism with dimensions of 200 mm×200 mm×100 mm, with a total chloride content of 0.4%, which is considered the typical chloride threshold value for corrosion in reinforced concrete (RC) structures. As shown in FIGS. 2A and 3A, the corrosion current and potential are highest in the completely sealed specimens due to the complete unavailability of oxygen. This resulted in the poor formation of a passive layer, thus leading to the expected highest corrosion rates. This was followed by the bitumen-based curing compound (C2) yielding the second highest corrosion rate due to the nature of this curing compound being based on bitumen. This was followed by the wax-based curing compound (C3) and the paraffin emulsion-based curing compound (C1), which show intermixing in the graphs as a function of time, leading to a lack of clarity regarding which curing compound may perform better. However, it can be clearly seen that the 90% application of the curing compounds yielded a relatively better passage of oxygen, which produced lower corrosion rates. The specimens submerged under water during the curing period produced the second lowest corrosion rates due the availability of dissolved oxygen in the curing water tanks. The unsealed specimens produced the lowest corrosion current and potential due to the availability of sufficient quantities of oxygen throughout the curing period.
[0030] FIGS. 2B, 2C, 3B and 3C show an increasing trend in the corrosion current and potential with a reduced effect of the curing compounds on the blockage of oxygen reaching the rebars embedded in the concrete through the curing compound. This indicates that the effect of the curing compounds on the oxygen-based deprivation of the passive layer is more prone in the case of lower water-to-cement (W/C) ratios, since they have reduced porosity and increased tortuosity of capillary pores. This indicates the desirability of the present method, which allows for increased oxygen penetration coupled with the preservation of moisture in the concrete.
[0031] For the results of FIGS. 4A-4C, each reinforced concrete specimen was shaped as a rectangular slab with dimensions of 300 mm×300 mm×100 mm, and the samples were further immersed in 5% NaCl brine solution. With regard to FIGS. 4A-4C, it can be seen that the corrosion current and potential increased significantly (FIGS. 4A and 4B) with the ingress of chloride ions into the concrete specimens (FIG. 4C). The hierarchy of corrosion profiles was found to be similar to that of the admixed chloride specimens of FIGS. 2A-3C. The expected blockage of chloride ions due to the curing compound application on the concrete surface was not observed, and the results show an increase in corrosion rates with time, contrary to expectations. A possible reason for these results is the dissolution of the curing compound in the brine solution, allowing the chloride ions to penetrate into the concrete and reach the rebar surfaces. Additionally, the difference in the magnitude of corrosion for various cases was less than what was observed in the case of admixed chloride specimens (FIGS. 2A-3C). This also strengthens the dissolution of the curing compound into the brine. However, the trend between various cases was found to be similar to what was observed in the samples of FIGS. 2A-3C, thus providing further support for the desirability of the present method, which allows for increased oxygen penetration coupled with the preservation of moisture in the concrete.
[0032] After 6 months of testing, the prism-shaped specimens of FIGS. 2A-3C were broken, and after 9 months of testing, the slabs of FIGS. 4A-4C were broken, allowing gravimetric corrosion analysis to be performed on the steel rebars embedded in the respective samples. Gravimetric mass loss analysis is considered to be the most reliable source of data for corrosion experimentation. FIGS. 5A and 5B show the mass loss data obtained by chemical cleaning of the corroded rebars. It can be seen in FIG. 5A that the highest corrosion mass loss was obtained in the case of the completely sealed specimens, followed by the curing compound C2 specimens with admixed threshold total chloride content of 0.4% (i.e., the specimens of FIGS. 2A-3C). It is noted that the curing compound C2 appeared to block the penetration of oxygen, similar to the non-porous plastic sheet used to seal the completely sealed specimen. This makes the curing compound C2 the worst selection when there is a choice available to select from the three available curing compounds.
[0033] The effect of the three W/C ratios was found to influence the sealed specimens and the specimens coated with the C2 curing compound in a similar way. The curing compounds C3 and C1 showed relatively lower corrosion rates than curing compound C2 and behaved similar to each other. However, the effect of W/C variation was obvious and greatly affected all of the curing compounds.
[0034] The 90% application of all three curing compounds C1, C2 and C3 appeared to allow the same amount of oxygen into the concrete to reach the rebar surface. The submerged and unsealed specimens showed relatively lower corrosion mass loss, with the unsealed specimen producing the lowest mass loss due to sufficient amounts of availability of oxygen for the formation of a quality passive layer.
[0035] FIG. 5B shows an unexpected trend for the corrosion mass loss results for the case of the specimens immersed in 5% brine solution (i.e., the specimens of FIGS. 4A-4C). It can be seen that the curing compound C2 showed the lowest corrosion mass loss, even less than that of the sealed specimen. One possibility for this result is that the bituminous layer in this curing compound provides limited penetration to the chloride ions in the brine solution. The curing compounds C1 and C3 showed higher mass loss, thus showing that the dissolution of these compounds in water was relatively higher than that of curing compound C2. All of the 90% surface application specimens showed a similar trend to those of the specimens of FIGS. 2A-3C (i.e., the specimens having admixed chloride concentrations). The submerged and sealed specimens showed a similar mass loss, showing sufficient availability of oxygen at the surface of the rebar. This indicates that a higher W/C ratio in the range of 0.6 can provide enough dissolved oxygen to reach the rebar surface through the larger capillary pores and with less tortuosity. Thus, the choice of curing compound and its method of application is more critical in relation to the quality of passive layer formation and successive corrosion rate when lower W/C ratios are used in RC structures.
[0036] It is to be understood that the method of curing reinforced concrete is not limited to the specific embodiments described above, but encompasses any and all embodiments within the scope of the generic language of the following claims enabled by the embodiments described herein, or otherwise shown in the drawings or described above in terms sufficient to enable one of ordinary skill in the art to make and use the claimed subject matter.