THERMAL BARRIER COATING COMPOSITIONS, METHODS OF MANUFACTURE THEREOF AND ARTICLES COMPRISING THE SAME

Abstract

Disclosed herein is a process for coating a component, comprising applying a bond coat on a substrate of a component; applying a thermal barrier material to the bond coat; and applying a coating containing polynuclear aluminum oxide/hydroxide clusters, to the thermal barrier material. Disclosed herein too is a gas turbine engine component, comprising a superalloy substrate; a bond coat on the substrate; a thermal barrier material on the bond coat; and a coating containing polynuclear aluminum oxide/hydroxide clusters on the thermal barrier material.

Claims

1. A gas turbine engine component, comprising: a superalloy substrate; a bond coat on the substrate; a thermal barrier material on the bond coat; and a coating containing polynuclear aluminum oxide/hydroxide clusters on the thermal barrier material.

2. The component of claim 1, wherein the polynuclear aluminum oxide/hydroxide clusters are Al.sub.13 Keggin clusters having the formula [AlO.sub.4Al.sub.12(OH).sub.24(H.sub.2O).sub.12].sup.7+, or are salts of the Al.sub.13 Keggin clusters called Al.sub.13 Keggin complexes.

3. The component of claim 1, wherein the coating further comprises a hydroxy aluminosilicate compound formed by coagulating the Al.sub.13 Keggin clusters and/or the Al.sub.13 Keggin complexes with an aqueous solution of sodium silicate, where the sodium silicate is present in an amount of about 0.01 to about 0.1 moles/liter in a solution that contains the Al.sub.13 Keggin clusters and/or the Al.sub.13 Keggin complexes, where the sodium silicates comprise sodium meta-silicate, sodium orthosilicate, disodium disilicate, or a combination thereof.

4. The component of claim 1, wherein the coating comprises the Al.sub.13 Keggin clusters and/or the Al.sub.13 Keggin complexes in an amount of 0.007 to 0.07 moles/liter.

5. The component of claim 1, wherein the Al.sub.13 Keggin clusters and/or the Al.sub.13 Keggin complexes are dried to form a pre-condensed coating of hydrated pseudo-boehmite (AlOOH*H.sub.2O), aluminum trihydroxide, or a combination thereof.

6. The component of claim 5, further comprising heat treating the coating to form a fully dense transition alumina coating selected from the group consisting of χ-Al.sub.2O.sub.3, η-Al.sub.2O.sub.3 or γ-Al.sub.2O.sub.3, and where the coating thickness is about 1 to about 1000 nanometers.

7. The component of claim 2, wherein the Al.sub.13 Keggin complex has the formula {[AlO.sub.4Al.sub.12(OH).sub.24(H.sub.2O).sub.12].sup.7+*7NO.sub.3.sup.−}.

8. The component of claim 2, further comprising obtaining the Al.sub.13 Keggin clusters and/or the Al.sub.13 Keggin complexes by base neutralization of an aluminum salt solution, where the salt solution comprises a total aluminum concentration of about 0.02 to about 2.0 moles/liter, to obtain an (OH.sup.−/Al) mole ratio of about 2.1 to about 2.6.

9. The component of claim 2, further comprising obtaining the Al.sub.13 Keggin clusters and/or the Al.sub.13 Keggin complexes by base neutralization of an aluminum salt solution, where the salt solution comprises a total aluminum concentration of about 0.02 to about 2.0 moles/liter, to obtain an (OH.sup.−/Al) mole ratio of about 2.2 to about 2.4.

10. The component of claim 2, further comprising preparing the coating from a solution that comprises the Al.sub.13 Keggin clusters and/or the Al.sub.13 Keggin complexes in an amount of about 0.007 to about 0.07 moles/liter of the solution; where the solution comprises water or an organic solvent.

11. The component of claim 10, further comprising precipitating the Al.sub.13 Keggin clusters and/or the Al.sub.13 Keggin complexes from a solution and collecting the Al.sub.13 Keggin clusters and/or the Al.sub.13 Keggin complexes by filtration, and drying the solution to form Al.sub.13 Keggin cluster and/or Al.sub.13 Keggin complex powder.

12. The component of claim 11, further comprising redissolving the Al.sub.13 Keggin cluster and/or Al.sub.13 Keggin complex powder in water with a polymeric binder to form the coating.

13. The component of claim 2, wherein the coating is applied by painting, spraying, electrostatic spraying, or spin-coating.

14. The component of claim 2, further comprising drying the Al.sub.13 Keggin clusters to form a pre-condensed coating of hydrated pseudo-boehmite (AlOOH*H.sub.2O), aluminum trihydroxide, or a combination thereof.

15. The component of claim 2, further comprising heat treating the coating to form a fully dense transition alumina coating selected from the group consisting of χ-Al.sub.2O.sub.3, η-Al.sub.2O.sub.3 and γ-Al.sub.2O.sub.3 that has a thickness of about 1 to about 1000 nanometers.

16. The component of claim 2, further comprising coagulating the Al.sub.13 Keggin clusters and/or the Al.sub.13 Keggin complexes with an aqueous solution of sodium silicate, where the sodium silicate is present in an amount of about 0.01 to about 0.1 moles/liter to form a hydroxy aluminosilicate compound, where the sodium silicates comprise sodium meta-silicate, sodium orthosilicate, disodium disilicate, or a combination thereof.

17. The component of claim 12, wherein an Al/Si atomic ratio ranges from about 5:1 to 15:1.

18. The component of claim 12, wherein the coating comprises the Al.sub.13 Keggin cluster and the hydroxy aluminosilicate compound and wherein the coating is applied by dipping, painting, spraying, electrostatic spraying, spin-coating, or a combination thereof.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0029] Various features will become apparent to those skilled in the art from the following detailed description of the disclosed non-limiting embodiment. The drawings that accompany the detailed description can be briefly described as follows:

[0030] FIG. 1 is a schematic cross-section of an example gas turbine engine architecture;

[0031] FIG. 2 is a flowchart of a process according to one disclosed non-limiting embodiment for application of a coating system to a component;

[0032] FIG. 3 is a cross-section through a component with an alumina/aluminosilicate compound layer that promotes CMAS crystallization to form a protective glass-ceramic seal;

[0033] FIG. 4 is a cross-section through the component showing the coating formulation containing polynuclear aluminum oxide/hydroxide complex, referred to as ‘Al.sub.13 Keggin complex,’ and silica oxide/hydroxide co-coagulant precursors;

[0034] FIG. 5 is a cross-section through the component showing the mixed Al and Si oxide/hydroxide coating application and drying;

[0035] FIG. 6 is a cross-section through the component showing the coating heat treatment and precursor transformation to alumina/aluminosilicate compound layer; and

[0036] FIG. 7 is a cross-section through the component showing the alumina/aluminosilicate compound resistant to CMAS dissolution.

DETAILED DESCRIPTION

[0037] FIG. 1 schematically illustrates a gas turbine engine 20. The gas turbine engine 20 is disclosed herein as a two-spool turbofan that generally incorporates a fan section 22, a compressor section 24, a combustor section 26 and a turbine section 28. The fan section 22 drives air along a bypass flowpath while the compressor section 24 drives air along a core flowpath for compression and communication into the combustor section 26 then expansion through the turbine section 28. Although depicted as a turbofan in the disclosed non-limiting embodiment, it should be understood that the concepts described herein are not limited to use with turbofans as the teachings may be applied to other types of turbomachinery to include, but not be limited to, low bypass augmented turbofans, turbojets, turboshafts, three-spool (plus fan) turbofans and industrial gas turbines.

[0038] With reference to FIG. 2, a process 100 according to one disclosed non-limiting embodiment for application of a coating 40 to a component 42 (FIG. 3) subjected to high temperatures is schematically represented. The steps of the process 100 are schematically disclosed in terms of functional block diagrams as a flowchart. It should be appreciated that alternative of additional steps may be provided without departing from the teaching herein.

[0039] Representative examples of the component 42 include but are not limited to combustor section 26 and/or turbine section 28 hardware, such as, augmentor components, combustor liners, blades, vanes, and blade outer air seals. The coating 40 as described herein is suitable for protection of a substrate 44 such as a nickel superalloy but while being described with reference to such superalloy gas turbine engine components, the teachings herein are generally applicable to any component on which a TBC may be used to protect the component from a high temperature environment, particularly environments containing CMAS.

Definitions

[0040] The polynuclear aluminum oxide/hydroxide cluster [AlO.sub.4Al.sub.12(OH).sub.24(H.sub.2O).sub.12].sup.7+ is referred to as an Al.sub.13 Keggin cluster.

[0041] The polynuclear aluminum oxide/hydroxide complex with NO.sub.3.sup.− counter-ions, {[AlO.sub.4Al.sub.12(OH).sub.24(H.sub.2O).sub.12].sup.7+*7NO.sub.3.sup.−}, is referred to as an Al.sub.13 Keggin complex.

[0042] A liquid coating formulation formed from Al.sub.13 and sodium silicate forms the polynuclear Al and Si oxide/hydroxide precursors.

[0043] A pre-condensed Al or Al—Si oxide/hydroxide layer is formed from a dried coating of polynuclear Al and Si oxide/hydroxide precursors.

[0044] A condensed alumina/aluminosilicate compound layer is formed by heat-treating the pre-condensed Al or Al—Si oxide/hydroxide layer.

[0045] A glass-ceramic layer is formed from the reaction of alumina/aluminosilicate coating with CMAS.

[0046] The process 100 initially includes the application of a bond coat 46 to a substrate 44 (see step 102 in the FIG. 3). The substrate 44 is subjected to cleaning and preparation prior to disposing the bond coat 46 on it. (See 106 in FIG. 2) FIG. 3 is a cross-section through a component with an alumina/aluminosilicate compound layer that promotes CMAS crystallization to form a protective glass-ceramic seal. The bond coat 46 may include an aluminum-rich composition, such as an overlay coating or a diffusion coating such as a diffusion aluminide or a diffusion platinum aluminide having formulas such as MCrAlY, MCrAlY+Hf, and MCrAlY+Hf+Si, in which M denotes nickel, cobalt, iron, platinum or mixtures thereof; Cr denotes chromium; Al denotes aluminum; Y denotes yttrium; Hf denotes hafnium; and Si denotes silicon. MCrAlY materials are often referred to as overlay coatings because they are applied in a predetermined composition and do not interact significantly with the substrate 44 during the deposition process. One exemplary preferred MCrAlY+Hf+Si bond coat composition has a weight percent compositional range of about 5 to about 40 Cr, about 8 to about 35 Al, about 0.1 to about 2.0 Y, about 0.1 to about 2.0 Hf, about 0.1 to about 7 Si, with the balance being selected from the group consisting of Ni, Co and mixtures thereof. Alternatively, or in addition, the bond coat material may include Al, PtAl, and the like, that are often referred to as diffusion coatings. Alternatively, or in addition, the bond coat material may also include Al, PtAl, MCrAlY as described above, and the like, that are often referred to as cathodic arc coatings.

[0047] The bond coat 46 may be applied by any method operable to produce a dense, uniform, adherent coating of the desired composition, such as, but not limited to, an overlay bond coat, diffusion bond coat, cathodic arc bond coat, and the like. Such techniques may include, but are not limited to, diffusion processes (e.g., inward, outward, and the like), low pressure plasma-spray, air plasma-spray, sputtering, cathodic arc, electron beam physical vapor deposition, high velocity plasma spray techniques (e.g., HVOF, HVAF, and the like), combustion processes, wire spray techniques, laser beam cladding, electron beam cladding, and the like.

[0048] The particle size for the bond coat 46 may be of any suitable size, and may be between about 15 microns (0.015 mm) and about 60 microns (0.060 mm) with a mean particle size of about 25 microns (0.025 mm). The bond coat 46 may be applied to any suitable thickness, and may be about 5 mils (0.127 mm) to about 10 mils (0.254 mm) thick. In some embodiments, the thickness may be about 6 mils (0.152 mm) to about 7 mils (0.178 mm) thick.

[0049] Next, a thermal barrier material 48 (FIG. 3) may be applied to the bond coat 46 (step 104). The thermal barrier material 48 may include a ceramic-based compound. Representative thermal barrier materials include, but are not limited to, a stabilized zirconate, a stabilized hafnate, combinations including at least one of the foregoing compounds, and the like, for example, yttria-stabilized zirconia, calcia-stabilized zirconia, magnesia-stabilized zirconia, yttria-stabilized hafnia, calcia-stabilized hafnia and magnesia-stabilized hafnia. Yttria-stabilized zirconia is commercially available as 7YSZ. One example preferred thermal barrier material 48 is a zirconia stabilized by between about 6 to about 8 wt % yttria that is about 0.05 to about 5 mil (about 0.00127 to about 0.127 mm) in thickness deposited, nominally at about 1 to about 3 mil (about 0.0254 to about 0.0761 mm).

[0050] The thermal barrier material 48 may be applied by various known methods. Suitable application methods include, but are not limited to, physical vapor deposition (e.g., electron beam), thermal spray (e.g., air plasma, high velocity oxygen fuel), sputtering, sol gel, slurry, combinations comprising at least one of the foregoing application processes, and the like.

[0051] The coating 40 comprising polynuclear aluminum oxide/hydroxide clusters (hereinafter the “coating”) is then prepared for application to the thermal barrier material 48. FIG. 4 is a cross-section through the component showing the coating formulation containing polynuclear aluminum oxide/hydroxide clusters, referred to as ‘Al.sub.13 Keggin complexes’ or ‘Al.sub.13 complexes’, and silica oxide/hydroxide precursors.

[0052] The coating is manufactured by reacting an aluminum salt with a base in a solution to produce an Al.sub.13 cluster or an Al.sub.13 complex. In an embodiment, the coating may comprise the Al.sub.13 cluster or the Al.sub.13 complex in its original solution. In another embodiment, the Al.sub.13 cluster or the Al.sub.13 complex may be precipitated from solution, purified and dried to form a powder. The powder may then be dissolved or suspended in another solution (a second solution) and disposed upon the thermal barrier coating to form the coating. In an embodiment, a polymeric binder may be added to the second solution and disposed upon the thermal barrier coating to form the coating. Upon being disposed on the thermal barrier coating, the coating may be heat treated to volatilize solvents or to degrade the polymeric binder.

[0053] In another embodiment, the Al.sub.13 cluster or a complex may be coagulated with a sodium silicate to form a hydroxy aluminosilicate. The hydroxy aluminosilicate along with the Al.sub.13 cluster or complexes in solution may be applied as a coating and dried. In an embodiment, a polymeric binder may be added to the solution containing the hydroxy aluminosilicate along with the Al.sub.13 cluster or complexes. During drying, the Al.sub.13 complexes aggregate to form hydrated pseudo-boehmite (AlOOH*H.sub.2O), aluminum trihydroxide, or a combination thereof. The coating can be transformed to a fully dense transition alumina coating comprising χ-Al.sub.2O.sub.3, η-Al.sub.2O.sub.3, or γ-Al.sub.2O.sub.3 upon being heat treated.

[0054] Preparation of the coating 40 is initiated via preparation of an aqueous aluminum salt solution (step 200; FIG. 4), containing a total Al concentration of about 0.02 to about 2.0 moles/liter. The aqueous solution of, for example, aluminum nitrate, Al(NO.sub.3).sub.3, with a total Al concentration of about 0.1 to 0.6 moles per liter, preferably about 0.2 to about 0.5 moles/liter, is formed under continuous stirring. Other aluminum salts can be used, either in conjunction with or in lieu of the aluminum nitrate, such as, for example: AlCl.sub.3, Al(CH.sub.3CO.sub.2).sub.3 (aluminium triacetate), and Al[OCH(CH.sub.3)C.sub.2H.sub.5].sub.3 (Al tri sec-butoxide). The solution is slowly titrated with a base, such as, for example, about 0.1 to about 0.6 moles per liter, preferably about 0.2 to about 0.5 moles/liter sodium hydroxide, NaOH, solution at about 70° C., until the [OH.sup.−]/[Al] molar ratio is between about 2.1 to about 2.6, preferably about 2.2 to about 2.4 and the pH is between about 4 to about 7. Examples of other bases that can be used in the aqueous solution include NaOH, KOH, Mg(OH).sub.2, Ca(OH).sub.2, NaHCO.sub.3 (sodium bicarbonate) and Na.sub.2CO.sub.3 (sodium carbonate).

[0055] The result of the neutralization of Al(NO.sub.3).sub.3 with the base is the formation of a high yield of polynuclear aluminum oxide/hydroxide clusters, [AlO.sub.4Al.sub.12(OH).sub.24(H.sub.2O).sub.12].sup.7+, referred to as ‘Al.sub.13 clusters’ or ‘Al.sub.13 Keggin clusters’, complexed with nitrate counter-ions, having the formula {[AlO.sub.4Al.sub.12(OH).sub.24(H.sub.2O).sub.12].sup.7+*7NO.sub.3.sup.−} (referred to as an ‘Al.sub.13 complex’ or an ‘Al.sub.13 Keggin complex’) in solution (Step 202).

[0056] Various salts (Al.sub.13 complexes) of the Al.sub.13 Keggin clusters may be formed and the salts are dependent upon the aluminum salt used to initiate the process of manufacturing the cluster. If other Al salts (other than aluminum nitrate) are used as precursors, the counter-ions in the Al.sub.13 Keggin complex will be formed from the salt anions of the precursor. For example, {[AlO.sub.4Al.sub.12(OH).sub.24(H.sub.2O).sub.12].sup.7+*7Cl.sup.−} will be formed from AlCl.sub.3 neutralization. The Al.sub.13 cluster is the most prevalent large polynuclear Al species. One other known large Al species has the formula Al.sub.2O.sub.8Al.sub.28(OH).sub.56(H.sub.2O).sub.26].sup.18+, referred to as the ‘Al.sub.30 cluster’, and is formed by the condensation of two Al.sub.13 clusters bridged with 4 monomeric Al ions. The Al.sub.13 clusters can also undergo condensation reactions to form higher molecular weight polymers, consisting of Al.sub.13 repeating units, especially under alkaline conditions.

[0057] These Al.sub.13 complexes can also be synthesized by electroless reduction of Al(NO.sub.3).sub.3 or other aluminum salt solutions. Alternatively, the Al.sub.13 complexes can be prepared by aqueous electrolysis using sacrificial Al anodes, following a similar method to Al electro-coagulation technologies employed for water purification.

[0058] The tailored surface passivation layer can be deposited directly from the aqueous solution or dispersion containing the metastable polynuclear Al oxide/hydroxide precursors, following the process flow diagram illustrated in FIG. 2. The Al.sub.13 clusters are all about 1.0 to about 1.8 nanometers (nm), preferably about 1.2 to about 1.7 nm in diameter and Al.sub.30 clusters are all approximately 3 nm in length. The Al.sub.13 repeating units can polymerize or flocculate to form higher molecular weight polymers, which will precipitate out of solution. After synthesis, the Al.sub.13 clusters and complexes can be precipitated by raising the solution pH, and further separating them by drying or concentrating them by other methods. The precipitates can be purified by washing in ethanol and redissolved in a coating formulation comprising Al.sub.13 cluster or complex concentrations of about 0.007 to about 0.07 moles/liter in an aqueous solution or in an organic solvent. This is detailed below.

[0059] In another instance, the coating can be deposited onto the thermal barrier coating from an aqueous solution or from a dispersion containing the reaction products of polynuclear Al and Si oxide/hydroxide precursors, having an Al/Si atomic ratio varying from about 5:1 to about 15:1. This is carried out by coagulating the Al.sub.13 clusters with sodium silicate, where the sodium silicate is present in varying amounts of about 0.01 to about 0.1 moles/liter of an aqueous solution. The sodium silicates are sodium meta-silicate (Na.sub.2SiO.sub.3), sodium orthosilicate (Na.sub.4SiO.sub.4), and disodium disilicate (Na.sub.2Si.sub.2O.sub.5).

[0060] The sodium silicates are first dissolved in water to form polynuclear silicic acid clusters (Si.sub.xO.sub.yH.sub.z). The silicic acid clusters react with the Al.sub.13 clusters to form less soluble hydroxy aluminosilicate oligomers that vary in character with the Si/Al ratio, pH, and preparation conditions. The hydroxy aluminosilicate formation reduces the Al.sub.13 concentration in proportion to the Si/Al ratio. The Al.sub.13/hydroxy aluminosilicate products are collected by filtration, purified by washing in ethanol and then dried. Next, the Al.sub.13/hydroxy aluminosilicate products are re-suspended in water to form a coating liquid formulation (step 204; FIG. 5).

[0061] In an embodiment, the Al.sub.13 or Al.sub.13/hydroxy aluminosilicate products can be reconstituted in an intermediate to high pH solution, concentrated aqueous solution or an organic solvent dispersion. The Al.sub.13 or Al.sub.13/hydroxy aluminosilicate products are present in concentrations of about 0.007 to about 0.07 moles/liter of the solution. Solvents and dispersion media include, but are not limited to, water, alcohols (methanol, ethanol, isopropanol, butanol, and the like), acetic acid, formic acid, N, N-dimethylformamide, ethyl acetate, tetrahydrofuran, acetone, or a combination thereof. The coating solution or dispersion formula can also contain water-soluble or polar organic solvent-soluble polymeric binders, like poly(vinyl pyrrolidone), polyacrylamides, polyacrylates, poly(acrylic acids), poly(vinyl alcohol), poly(ethylene oxides) or poly(ethylene glycols), polyethyleneimines, polyurethanes, and polyamines.

[0062] Polymers that are not water soluble may also be used. The polymers can include thermoplastic polymers or thermosetting polymeric binders. Suitable non-water soluble thermoplastic polymeric binders include polyolefins, polystyrene, polymethylmethacrylate, polyimides, polysulfones, polyethersulfones, polyetherimides, polysiloxanes, polycarbonates, polyphenylene ethers, or the like, or a combination thereof. Suitable non-water soluble thermosetting polymeric binders include polyepoxides, phenolics, polyurethanes, polysiloxanes, polyisoprene, polybutadiene, or the like, or a combination thereof.

[0063] In addition, ingredients like buffer species, co-coagulants, corrosion-inhibitors, chelating agents, or monomeric metal ions can be used to accelerate coagulation, deposition, and adhesion to the component substrate.

[0064] The Al.sub.13 or Al.sub.13/hydroxy aluminosilicate products are used in conjunction with a binder in an amount of 2 to 25 wt %, preferably 5 to 20 wt %, and more preferably 8 to 15 wt %, based on the total weight of the Al.sub.13 or Al.sub.13/hydroxy aluminosilicate products and the binder.

[0065] The liquid coating is then applied over the thermal barrier material 48 (Step 206; FIG. 5). The liquid coating is applied by dipping, painting, spraying, electrostatic spray, or spin-coating on the thermal barrier material 48. The viscosity of the precursor coating liquid is high enough to limit its infiltration into the thermal barrier material 48 intergranular gaps.

[0066] The coating is dried, to form a pre-condensed Al or Al—Si oxide/hydroxide layer, depending on the original liquid coating composition. During drying, the Al.sub.13 complexes may aggregate to form hydrated pseudo-boehmite (AlOOH*H.sub.2O) nanocrystallites and/or aluminum trihydroxide nanocrystallites that range from about 5 to about 500 nm in size, as well as amorphous phases. During drying, the mixed Al—Si oxides/hydroxides remain amorphous in character.

[0067] The coating layer is then condensed by heating the component (Step 208; FIG. 6). For example, the component may be heated to a temperature ranging between about 250 to about 500° C. for about two hours such as during a “green” run. During heating, ramp up over temperatures of about 100 to about 500° C. will cause any remaining water, ligands, and non-metallic counter-ions or additives present in the coating to desorb or to decompose. The pseudo-boehmite or aluminum trihydroxide transforms to a fully dense transition-alumina phase (χ-Al.sub.2O.sub.3, η-Al.sub.2O.sub.3 or γ-Al.sub.2O.sub.3), and the Al—Si oxides/hydroxides transform to an amorphous aluminosilicate matrix. Full alumina nanocrystallite transformation to α-Al.sub.2O.sub.3 is possible at temperatures above 1000° C. Sintering can occur at even higher temperatures, ca. above 1100° C.

[0068] The condensed coating caps the intergranular gaps in the thermal barrier material 48 at their opening to the surface, providing a first level passivation protection to delay CMAS ingress (Step 300). Once the Al-rich nanocrystallites are contacted by molten CMAS, they can initiate partial CMAS crystallization to a glass-ceramic type phase. In one example, the coating thickness is between about 1 to about 1000 nm.

[0069] Nanocrystallites in contact with CMAS liquid (FIG. 7) can operate as nuclei that accelerate kinetics for crystallizing intrinsic CMAS phases, such as anorthrite [CaAl.sub.2Si.sub.2O.sub.8], diopside [CaMgSi.sub.2O.sub.6], and pseudo-wollastonite [CaSiO.sub.3], and the like. Nanocrystallites can be dissolved in CMAS bulk, locally shifting reaction equilibria (Le Chatelier's principle) towards crystallization of Al-rich phases, such as: anorthrite, melilite [Ca.sub.2Al.sub.2SiO.sub.7], spinel [MgAl.sub.2O.sub.4 or MgAl.sub.2O.sub.7]. The glass-ceramic structure has significantly higher viscosity, prevents CMAS infiltration and dissolution into the thermal barrier material 48. The glass-ceramic forms a fully dense, impervious surface layer (glass-ceramics are used as sealants).

[0070] Co-coagulants, counter-ions, or ligands are formulated in the coating 40 to tailor composition and properties of CMAS intrinsic crystallization products. Co-coagulants, such as metal oxide clusters, including those formed with the oxides of the metals (Me): Si, Mo, W, V, Fe, Zn, and Cu, can be combined with Al.sub.13 Keggin complexes to facilitate self-assembly into 3D structures, i.e., to form larger sized precipitates. The co-coagulants contain metal oxides, Me.sub.xO.sub.y, that are added so that the Al/Me atomic ratio is within the range of about 1.5:1 to about 15:1. These other metal oxides may modify the precipitate crystalline ordering, enhance phase transformation kinetics of the coating consolidation, and/or act as nucleation agents for CMAS crystallization.

[0071] Polyaluminosilicate precipitates can be formed when a significant fraction of sodium silicate co-coagulants are combined with the Al.sub.13 Keggin clusters, such as in the naturally occurring zunyite aluminosilicate halide mineral, Al.sub.13Si.sub.5O.sub.20(OH,F).sub.18Cl, which contains a combination of Si.sub.5O.sub.16 and Al.sub.13 units. The polyaluminosilicates with the Al/Si atomic ratio varying from about 5:1 to about 15:1, contain a mixture of Al.sub.13 complexes and aluminosilicate oligomers. The coating 40 prepared from the Al.sub.13 complexes or the Al.sub.13/aluminosilicate mixtures can either nucleate the crystallization of intrinsic CMAS phases, or locally shift the equilibria towards the formation of more stable phases containing Al and Si, such as: andalusite, kyanite or sillimanite (Al.sub.2SiO.sub.5); and mullite (Al.sub.6S.sub.12O.sub.13).

[0072] The Al.sub.13 Keggin complexes and polyaluminosilicates can complex with metal ions (this is an important feature that is commonly used for water purification). Metallic counter-ions, Me.sup.+n, where n=2 to 4, with the Al/Me atomic ratio varying from about 10:1 to about 40:1. Some transition metal ions, e.g., Ti.sup.+3/+4, Fe.sup.+2/+3, and Mn.sup.+2/+4, are known nucleation agents used commercially for CMAS crystallization to form glass-ceramic products. Pre-condensed Al.sub.13 Keggin complexes seeded with these metal ions, may release these ions or their oxides during subsequent condensation reactions or during contact with molten CMAS phases (FIG. 7), in order that they can facilitate CMAS crystallization (FIG. 3).

[0073] The outer bound waters on the Al.sub.13 Keggin complexes can be exchanged with other ligands, such as F ions, carboxylic acids, and alcohols, where the maximum substitution is determined by charge neutralization requirements. Substitution of negatively charged ligands, e.g., F and carboxylate ions, will reduce the number of counter-ions in the outer coordination sphere. These ligands may be used to alter the Al.sub.13 Keggin complexes or co-coagulant stability or reactivity, and solubility or dispersibility in the pre-condensed liquid coating, as well as possibly during subsequent condensation reactions.

[0074] The use of the terms “a” and “an” and “the” and similar references in the context of description (especially in the context of the following claims) are to be construed to cover both the singular and the plural, unless otherwise indicated herein or specifically contradicted by context. It should be appreciated that relative positional terms such as “forward,” “aft,” “upper,” “lower,” “above,” “below,” and the like are with reference to the normal operational attitude of the vehicle and should not be considered otherwise limiting.

[0075] Although the different non-limiting embodiments have specific illustrated components, the embodiments of this invention are not limited to those particular combinations. It is possible to use some of the components or features from any of the non-limiting embodiments in combination with features or components from any of the other non-limiting embodiments.

[0076] It should be appreciated that like reference numerals identify corresponding or similar elements throughout the several drawings. It should also be appreciated that although a particular component arrangement is disclosed in the illustrated embodiment, other arrangements will benefit herefrom.

[0077] Although particular step sequences are shown, described, and claimed, it should be understood that steps may be performed in any order, separated or combined unless otherwise indicated and will still benefit from the present disclosure.

[0078] The foregoing description is exemplary rather than defined by the limitations within. Various non-limiting embodiments are disclosed herein, however, one of ordinary skill in the art would recognize that various modifications and variations in light of the above teachings will fall within the scope of the appended claims. It is therefore to be understood that within the scope of the appended claims, the disclosure may be practiced other than as specifically described. For that reason the appended claims should be studied to determine true scope and content.