Manufacturing method of aluminum alloy with high thermal conductivity

Abstract

A manufacturing method of an aluminum alloy with high thermal conductivity comprising steps of: preparing materials including pure aluminum ingots, silicon alloy, iron alloy and magnesium alloy; melting the pure aluminum ingots in a reverberatory furnace at two stages, melting, stirring, sampling for compositions determination; transferring the molten aluminum into a holding furnace, putting the ingots in, melting, removing slag, determining the compositions; calculating amount of the alloys to be added; melting the silicon alloy and iron alloy in the molten aluminum and analyzing the compositions; adding the ingots to cool the temperature of the molten aluminum down and then adding the magnesium alloy, confirming and making corrections if insufficient compositions; degassing and purifying the molten aluminum by adding drossing flux in the furnace and making a final compositions determination; transferring the molten aluminum into online degassing system to degas and purify; casting the molten aluminum into aluminum alloy ingots.

Claims

1. A manufacturing method of aluminum alloy comprising steps of: i. preparing materials: pure aluminum ingots, silicon (Si) alloy, iron (Fe) alloy, magnesium (Mg) alloy; ii. melting the pure aluminum ingots in a reverberatory furnace at two stages: at first stage, a weight percentage of the pure aluminum ingots being 40% of the usage amount, heating the reverberatory furnace up to temperature between 660° C.˜690° C. in order to melt and stir the pure aluminum ingots, taking 3˜5 hours to melt firstly, stirring once or twice after the first melting and each stirring taking 3˜10 minutes, sampling for a first compositions determination after completion of the first melting, at second stage, a weight percentage of the pure aluminum ingots being 47%˜48% of the usage amount so that the total usage amount at the two stages being 87%˜88%, taking 1˜3 hours to melt secondly, stirring once or twice and taking 3˜10 minutes to stir after the second melting, sampling for a second compositions determination after completion of the second melting; iii. transferring the molten aluminum from the reverberatory furnace into a holding furnace: after transferring the molten aluminum from the reverberatory furnace into the holding furnace, reconfirming the compositions, then inputting about 4˜5% of the usage amount of the pure aluminum ingots as third melting, by temperature between 660° C.˜690° C., after the completion of the third melting, removing the aluminum slag on judgment standard; iv. calculating and preparing amount of the silicon (Si) alloy, iron (Fe) alloy, magnesium (Mg) alloy and aluminum (Al) to be added: calculating and preparing amount of the alloys to be added including a weight percentage of silicon (Si) alloy being 2.0%˜5%, a weight percentage of iron (Fe) alloy being 0.4%˜0.5%, a weight percentage of magnesium (Mg) alloy being 0.4%˜0.6%, moreover, preparing the pure aluminum ingots with a weight percentage of 4˜5% as a cooling material; v. adding the silicon (Si) alloy and iron (Fe) alloy into molten aluminum in the holding furnace: firstly, inputting silicon (Si) alloy and iron (Fe) alloy prepared in step 4 in the holding furnace, taking 0.5˜1 hour to melt at temperature range between 730° C.˜750° C., stirring thoroughly, analyzing the compositions after stirring, analyzed values being used as initial values for subsequent alloy addition and correction; vi. putting the pure aluminum ingots to cool the temperature down, and adding the magnesium (Mg) alloy: putting the pure aluminum ingots prepared in step 4 into the molten aluminum in the holding furnace to cool the temperature down to 680° C.˜710° C., adding the magnesium (Mg) alloy into the holding furnace with a melting time of 15˜20 minutes after cooling, confirming the compositions after melting, for insufficient compositions in other master alloys, making corrections during this melting process; vii. degassing and purifying in the holding furnace: using granulated drossing flux with nitrogen to spray into the holding furnace as first degassing and purifying, after spreading, stirring thoroughly for 20˜30 minutes and controlling the molten aluminum temperature at 660° C.˜710° C., removing the impurities from the surface of the molten aluminum after stirring, then letting the molten aluminum stand for about 15˜30 minutes, making a final compositions determination; viii. degassing and purifying by online degassing system: confirming a temperature of the molten aluminum being between 660° C.˜710° C. after pouring into the online degassing system, the molten aluminum being second degassed and purified by the online degassing system; and ix. casting aluminum alloy ingots: after online degassing and purifying, casting aluminum ingots to make the aluminum alloy ingots with high thermal conductivity.

2. The manufacturing method of aluminum alloy as claimed in claim 1, wherein the aluminum alloy is mainly composed of aluminum (Al), silicon (Si), iron (Fe), magnesium (Mg), antimony (Sb), copper (Cu), zinc (Zn), manganese (Mn), nickel (Ni), chromium (Cr), titanium (Ti), lead (Pb), tin (Sn), bismuth (Bi), lithium (Li) and M components, weight percentages of the components are as follows: silicon (Si) 2.0%˜5.0%, iron (Fe) 0.4˜0.5%, magnesium (Mg) 0.4˜0.6%, antimony (Sb) less than 0.05%, contents of copper (Cu), zinc (Zn), manganese (Mn), nickel (Ni), chromium (Cr), titanium (Ti), lead (Pb), tin (Sn), bismuth (Bi), lithium (Li) elements are less than 0.01%, and M is another element with a content being limited to less than 0.005%, and the balance is aluminum (Al).

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) FIG. 1 is a flow chart of a manufacturing method of one embodiment of the invention.

(2) FIG. 2 is a compositions determination chart of one embodiment of the invention.

(3) FIG. 3 is a final compositions determination chart of one embodiment of the invention.

DETAILED DESCRIPTION OF THE INVENTION

(4) Regarding the technical means adopted by the invention to achieve the above-mentioned object and efficacies, a preferred and feasible embodiment is explained in details hereunder in conjunction with the figures.

(5) In a manufacturing method of an aluminum alloy with high thermal conductivity of the invention, in order to ensure that there are no impurities in a reverberatory furnace, the furnace is cleaned firstly by pure aluminum (Al) ingots. After the furnace is cleaned and drained, the manufacturing steps of the aluminum alloy with high thermal conductivity are able to initiate and the steps are comprising: (please refer to FIG. 1)

(6) 1. preparing materials: pure aluminum (Al) ingots, silicon (Si) alloy, iron (Fe) alloy, magnesium (Mg) alloy;

(7) 2. putting the pure aluminum (Al) ingots into a reverberatory furnace at two stages: at first stage, a weight percentage of the pure aluminum (Al) ingots being 40% of the usage amount, heating the reverberatory furnace up to temperature between 660° C.˜690° C. in order to melt and stir the pure aluminum (Al) ingots, taking 3˜5 hours to melt firstly, stirring once or twice after the first melting and each stirring taking 3˜10 minutes, sampling for a first compositions determination after completion of the first melting, at second stage, a weight percentage of the pure aluminum (Al) ingots being 47%˜48% of the usage amount so that the total usage amount at the two stages being 87% 88%, taking 1˜3 hours to melt secondly, stirring once or twice and taking 3˜10 minutes to stir after the second melting, sampling for a second compositions determination after completion of the second melting; the two compositions determinations must be in accordance with the chart in FIG. 2

(8) 3. transferring the molten aluminum (Al) from the reverberatory furnace into a holding furnace: after transferring the molten aluminum (Al) from the reverberatory furnace into the holding furnace, reconfirming the compositions, then inputting about 4˜5% of the usage amount of the pure aluminum (Al) ingots as third melting, by temperature between 660° C.˜690° C., after the completion of the third melting, removing the aluminum (Al) slag on a surface of the molten aluminum (Al) by raking, reconfirming the compositions with judgment standard as shown in the chart in FIG. 2;

(9) 4. calculating and preparing amount of silicon (Si) alloy, iron (Fe) alloy, magnesium (Mg) alloy and aluminum (Al) ingots to be added: calculating and preparing amount of the alloys to be added including a weight percentage of silicon (Si) alloy being 2.0%˜5%, a weight percentage of iron (Fe) alloy being 0.4%˜0.5%, a weight percentage of magnesium (Mg) alloy being 0.4%˜0.6%, moreover, preparing the pure aluminum (Al) ingots with a weight percentage of 4˜5% as a cooling material;

(10) 5. adding the silicon (Si) alloy and iron (Fe) alloy into molten aluminum (Al) in the holding furnace: firstly, inputting silicon (Si) alloy and iron (Fe) alloy prepared in step 4 in the holding furnace, taking 0.5˜1 hour to melt at temperature range between 730° C.˜750° C., stirring thoroughly, analyzing the compositions after stirring, analyzed values being used as initial values for subsequent alloy addition and correction;

(11) 6. putting the pure aluminum (Al) ingots to cool the temperature down, and adding the magnesium (Mg) alloy: putting the pure aluminum (Al) ingots prepared in step 4 into the molten aluminum (Al) in the holding furnace to cool the temperature down to 680 ° C.˜710 ° C., adding the magnesium (Mg) alloy into the holding furnace with a melting time of 15˜20 minutes after cooling, confirming the compositions after melting, for insufficient compositions in other master alloys, making corrections during this melting process; a minimum balance of aluminum (Al) being 93.6% min, the compositions confirmation standard being shown in the chart in FIG. 3;

(12) 7. degassing and purifying in the holding furnace: using granulated drossing flux in a powder spreading device with nitrogen in order to spray into the holding furnace as first degassing and purifying, the granulated drossing flux could be NIKKIN N200 with dosage: 20 kgs and ratio of 1 metric ton of the molten aluminum (Al) to 1 kg of the drossing flux, after completion of the drossing flux spreading, stirring thoroughly for 20˜30 minutes and controlling the molten aluminum (Al) temperature at 660° C.˜710° C., removing the impurities from the surface of the molten aluminum (Al) after stirring, then letting the molten aluminum (Al) stand (without stirring) for about 15˜30 minutes, making a final compositions determination, judgment standard as shown in the chart in FIG. 3;

(13) 8. degassing and purifying by online degassing system: confirming a temperature of the molten aluminum (Al) being between 660° C. and 710° C. after pouring from the holding furnace into a T-shape rotor manufactured by STAS, in the online degassing system, then, the molten aluminum (Al) being rotated and stirred by the rotor as second degassing and purifying; and

(14) 9. casting aluminum (Al) alloy ingots: after online degassing and purifying, casting aluminum (Al) ingots to make the aluminum (Al) alloy ingots with high thermal conductivity.

(15) The aluminum alloy with high thermal conductivity manufactured by the above steps of the invention is mainly composed of aluminum (Al), silicon (Si), iron (Fe), magnesium (Mg), antimony (Sb), copper (Cu), zinc (Zn), manganese (Mn), nickel (Ni), chromium (Cr), titanium (Ti), lead (Pb), tin (Sn), bismuth (Bi), lithium (Li) and M components, weight percentages of the components are as follows: silicon (Si) 2.0%˜5.0%, iron (Fe) 0.4˜0.5%, magnesium (Mg) 0.4˜0.6%, antimony (Sb) less than 0.05%, contents of copper (Cu), zinc (Zn), manganese (Mn), nickel (Ni), chromium (Cr), titanium (Ti), lead (Pb), tin (Sn), bismuth (Bi), lithium (Li) elements are less than 0.01%, and M is another element (such as silver Ag, boron B, beryllium Be, calcium Ca, cadmium Cd, cobalt Co, gallium Ga, mercury Hg, indium In, sodium Na, strontium Sr, etc.) with a content being limited to less than 0.005%, and the balance is aluminum (Al), a minimum balance of aluminum (Al) is 93.6% min.

(16) The manufacturing equipment of the invention is a reverberatory furnace and a holding furnace for melting. The molten aluminum is finally subjected to the second online degassing and purifying system using the T-shape rotor manufactured by STAS, and then an automatic casting machine is used to cast the aluminum alloy ingots to produce the aluminum alloy ingot products with high thermal conductivity. The aluminum alloy ingot with high thermal conductivity can be formed and processed efficiently to be used for conventional aluminum alloy die-casting, aluminum alloy semi-solid die-casting and casting. The products can be applied in parts of portable electronic devices, 5G communication equipment, automotive electronic parts, aerospace and satellite communications, and other parts and components with high heat dissipation and high heat conduction requirements.

(17) In summary, the invention has indeed achieved the intended object and efficacy of use, and is more ideal and practical than the prior art. However, the above-mentioned embodiment is merely the specific description of the preferred embodiment of the invention, the embodiment is not intended to limit the claims of the invention, and all other equivalent changes and modifications completed without departing from the technical means disclosed in the invention should be included in the claims covered by the invention.