Lubricant comprising spherical graphite nanoparticles

Abstract

The present invention relates to an engine oil containing, as a bearing particle, 0.1 g to 2 g of spherical graphite particles having an average diameter of 1 nm to 300 nm per liter, and an additive composition therefor.

Claims

1. An engine oil containing, as a bearing particle, 0.1 g to 2 g of spherical graphite particles having an average diameter of 1 nm to 300 nm per liter.

2. The engine oil of claim 1, wherein the spherical graphite particle has a specific gravity of 1.9 to 2.3.

3. The engine oil of claim 1, wherein the engine oil improves engine output and reduces exhaust gas emissions compared to engine oils not containing spherical graphite particles having an average diameter of 1 nm to 300 nm.

4. The engine oil of claim 1, wherein the engine oil reduces emission of hydrocarbons, carbon dioxide, carbon monoxide, and nitrogen oxides by 90% or more in exhaust gas compared to engine oils not containing spherical graphite particles having an average diameter of 1 nm to 300 nm.

5. An additive composition for an engine oil containing, as a bearing particle, spherical graphite particles having an average diameter of 1 nm to 300 nm.

6. The additive composition for an engine oil of claim 5, wherein the spherical graphite particle has a specific gravity of 1.9 to 2.3.

Description

BRIEF DESCRIPTION OF DRAWINGS

(1) FIG. 1 is a diagram showing an SEM image of spherical graphite nanoparticles which are dispersed in a general water system and used as an additive for an engine oil according to an embodiment of the present invention.

(2) FIGS. 2 and 3 are diagrams showing SEM images measured at different magnifications of spherical graphite nanoparticles which are dispersed in an engine oil and used as an additive for an engine oil according to an embodiment of the present invention.

(3) FIG. 4 is a diagram showing a high-resolution TEM image of spherical graphite nanoparticles which are used as an additive for an engine oil according to an embodiment of the present invention.

(4) FIG. 5 is a diagram showing the amount of exhaust gas and fuel efficiency measured when using an engine oil containing or not containing spherical graphite nanoparticles according to an embodiment of the present invention.

(5) FIG. 6 is a diagram showing a combination of the total collected data of fuel consumption (one-time fuel injection amount expressed in mcc) according to the driving speed when using an engine oil containing or not containing spherical graphite nanoparticles according to an embodiment of the present invention.

(6) FIG. 7 is a diagram showing the average of 200 representative data points of fuel consumption (one-time fuel injection amount expressed in mcc) according to the driving speed when using engine oil containing or not containing spherical graphite nanoparticles according to an embodiment of the present invention.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

(7) The first aspect of the present invention provides an engine oil containing, as a bearing particle, 0.1 g to 2 g of spherical graphite particles having an average diameter of 1 nm to 300 nm per liter.

(8) The second aspect of the present invention provides an additive composition for an engine oil, containing, as a bearing particle, spherical graphite particles having an average diameter of 1 nm to 300 nm.

(9) Additionally, the present invention provides a use of an additive composition for an engine oil containing, as a bearing particle, spherical graphite particles having an average diameter of 1 nm to 300 nm.

(10) Hereinafter, the present invention will be described in detail.

(11) As used herein, the term “bearing” refers to a machine element that reduces friction between moving parts, and is a machine (component) that enables free movement by supporting a rotating or reciprocating shaft at a fixed position. For example, the design of the bearing freely provides the movement of the linear moving part and rotation around a fixed axis. In addition, by limiting the vertical force of the vector, the burden of movement is prevented. Many bearings also minimize friction to facilitate the desired motion as much as possible, and reduce energy loss and heat generation due to friction, preventing damage to the components.

(12) Even when an oil film is formed on the piston and the cylinder wall of the engine by using the engine oil, direct friction therebetween cannot be excluded. Meanwhile, the engine oil of the present invention contains a suitable amount of spherical graphite particles having an average diameter of 1 nm to 300 nm evenly dispersed in a liquid oil, so that these particles are inserted between the piston and the cylinder wall to act as a bearing, thereby reducing the friction therebetween.

(13) Meanwhile, when the compression ratio in the internal combustion engine during combustion is high, the thermal efficiency is high and the fuel consumption low. Therefore, when the engine oil according to the present invention is used, the spherical graphite particles having an average diameter of 1 nm to 300 nm in the engine oil during combustion in the internal combustion engine serve as a bearing, reducing the friction between the components of the internal combustion engine, and thus, the compression pressure of the cylinder is not deteriorated, and an appropriate amount of fuel is injected, so that the fuel and air can be mixed smoothly to produce high output through complete combustion. Accordingly, the engine performance, power, and fuel efficiency can be improved, even when a low air:fuel ratio (A:F ratio) is applied. Such an improvement of the fuel efficiency can increase the distance that can be driven with the same amount of fuel, and thus the exhaust gas emission is fundamentally reduced in proportion. Further, since the amount of heat generated in the piston can be reduced due to a decrease in friction when using the engine oil according to the present invention, it is possible to inhibit the generation of NO.sub.x oxides generated at high temperatures.

(14) Viscosity is a measure of a fluid's resistance to flow, and is affected by temperature. In the case of gases, the viscosity increases as the temperature increases, but in liquids, the viscosity decreases as the temperature increases.

(15) In a specific embodiment of the present invention, a commercial engine oil (Kixx Da 10W-30) having a viscosity of 140 at room temperature was used. Accordingly, the engine oil added with the spherical graphite particles according to the present invention showed an increase in viscosity within about 10. This reduces the viscosity of the engine oil in the vehicle as the engine overheats when the car is driving at a high speed, which may result in inducing the effect of reducing the degree of the viscosity of the engine oil through the heat dissipation effect due to the graphite particles and the effect of preventing overheating due to the decrease in friction of the engine.

(16) The present invention provides an engine oil containing, as bearing particles, 0.1 g to 2 g of spherical graphite particles having an average diameter of 1 nm to 300 nm per liter. In particular, since the graphite particles have a specific gravity of 1.9 to 2.3, the graphite particles may be maintained evenly dispersed in the base oil of the engine oil.

(17) The engine oil of the present invention contains spherical graphite particles, and thus, the improvement in the engine efficiency may be expected due to the bearing effect. Meanwhile, when the graphite particles are smaller than 1 nm in diameter, they may not have sufficient strength, decreasing durability, and the bearing effect cannot be continuously exhibited. For example, fullerenes, which are another type of spherical carbon particle, are a very expensive material and thus economically infeasible. Further, it may not exhibit a bearing effect because the particle size is also smaller than 1 nm. In contrast, when the particle size exceeds 300 nm, the number of particles that can be contained in an engine oil is limited due to their size, considering that the particle must be included at a predetermined number density in order to achieve an appropriate bearing effect. When particles are added in a large amount so as to achieve a desired number density, they can no longer be dispersed evenly in the engine oil and may aggregate and precipitate.

(18) For example, the engine oil containing the spherical graphite particles of the present invention can improve the engine output and reduce the exhaust gas emissions compared to engine oils not containing the spherical graphite particles having an average diameter of 1 nm to 300 nm. According to a specific embodiment of the present invention, when the graphite particles are contained by driving an engine in which spherical graphite particles are added or not added to a commercial engine oil, it was confirmed that the exhaust gas emission was reduced by more than 90%; specifically, the emissions of hydrocarbons, carbon dioxide, carbon monoxide, and nitrogen oxides were reduced by more than 90%, and fuel efficiency was improved by more than 10%.

(19) Additionally, the present invention provides an additive composition for an engine oil containing, as a bearing particle, spherical graphite particles having an average diameter of 1 nm to 300 nm.

(20) Further, the present invention provides a use of an additive composition for an engine oil containing, as a bearing particle, spherical graphite particles having an average diameter of 1 nm to 300 nm.

(21) The engine oil is the same as described above.

(22) The composition may further include a surfactant and/or a dispersant for promoting the dispersion of the particles in the engine oil, and it may further include detergents, antioxidants, friction modifiers, anti-wear agents, extreme pressure (EP) additives, emulsifiers, anti-foaming agents, viscosity index improvers (viscosity regulators), pour point depressant, rust inhibitors, corrosion inhibitors, and the like, which are generally added to engine oils, but is not limited thereto.

MODE FOR CARRYING OUT THE INVENTION

(23) Hereinafter, the present invention will be described in more detail by way of Examples. However, these Examples are provided for illustrative purposes only, and the scope of the invention is not intended to be limited to or by these Examples.

Example 1: Preparation of Engine Oil Containing Spherical Graphite Nanoparticles as Additives

(24) First, after ball milling using ethanol as a solvent for 10 days, the particles were selected using centrifugation, and graphite nanoparticles prepared by selecting only particles of 300 nm or less were used. An engine oil prepared by dispersing spherical graphite nanoparticles (1-100 nm graphite, Hongwoo Co., Ltd.) having an average diameter of 10 nm to 70 nm in a colloidal state was prepared in an amount of 0.5 g per 1 L as described above. As the engine oil, a commercial engine oil (Kixx Da, SAE viscosity of 10W-30, GS Caltex) was used, and the same engine oil without the spherical graphite nanoparticles was used as a control. The microstructure of the spherical graphite used in the present invention was observed by SEM and TEM, and the results are shown in FIGS. 1 to 4.

Example 2: Effect of Reducing Exhaust Gas by Additives

(25) A dynamo test was performed based on the IM240 mode according to the international standard specifications to measure exhaust gas emissions and analyze fuel efficiency. Hyundai cars loaded with a 2014 gasoline engine of 1600 cc were used for the experiment. The measured result is shown in FIG. 5. Specifically, the amounts of hydrocarbons (HC), carbon dioxide (CO.sub.2), carbon monoxide (CO), and nitrogen oxides (NO.sub.x) contained in the exhaust gas were measured separately. As shown in FIG. 5, the amounts of the four components were all reduced by more than 90% compared to the case when the engine oil containing no additives was used, and the fuel efficiency, that is, the mileage per liter, was increased by more than 10%.

Example 3: Effect of Reducing RPM at High Speed by Additives

(26) A dynamo test was performed based on the IM240 mode according to the international standard specification, and thousands of sets of raw data were analyzed to measure the change in RPM according to the speed, and the results are shown in FIG. 6. As shown in FIG. 6, as a result of arranging the data before and after the addition of the additives based on the vehicle driving speed, the RPM after the injection was improved as compared with before the injection of the additives. The degree of the improvement was insignificant at low speed, but the degree of the improvement of RPM was significantly increased at high speed.

(27) In order to effectively analyze the data, 200 data points according to the vehicle driving speed were averaged and analyzed, and the results are shown in FIG. 7. As shown in FIG. 7, the data before and after the addition of the additives were not significantly different at low speeds, particularly up to about 30 km/h, but an increase in the difference of fuel consumption was observed from thereafter up to about 55 km/h. At speeds above about 70 km/h, the difference was significantly increased, and thus, the increase in RPM according to increasing driving speed upon addition of additives was significantly reduced.