COPPER ELECTROREFINING

Abstract

A metal composition includes from 90.10% wt up to 97% wt of copper, at least 0.1% wt of nickel, at least 0.0001% wt and less than 1.00% wt of iron, and 250-3000 ppm wt of oxygen. The composition is suitable for being processed by a process including the electrorefining of copper in an electrolytic cell, wherein the voltage difference over the cell is maintained at less than 1.6 volt, the anode comprises at most 98.0% wt of copper and less than 1.00% wt of iron, the current density through the cell is at least 180 A/m.sup.2 of cathode surface, electrolyte is removed from the cell during the operation at an average refreshing rate of 30-1900% per hour, by overflow of a stream of electrolyte over a cell wall, and a gas is bubbled through the electrolyte in between anode and cathode. The composition is even more suitable after a reduction of its oxygen content.

Claims

1. A molten liquid metal composition comprising at least 90.10% wt and at most 97% wt of copper, the balance being other elements as impurities as part of which the molten liquid metal composition comprises, at least 0.1% wt of nickel, at least 0.0001% wt and less than 1.00% wt of iron, and at least 250 ppm wt and at most 3000 ppm wt of oxygen.

2. The molten liquid metal composition according to claim 1 further comprising, as part of the impurities, at least 0.10% wt and at most 3.00% wt of antimony,

3. The molten liquid metal composition according to claim 1 further comprising, as part of the impurities, at least 0.010% wt and at most 0.50% wt of bismuth.

4. The molten liquid metal composition according to claim 1 further comprising, as part of the impurities, at most 6.00% wt of tin.

5. The molten liquid metal composition according to claim 1 further comprising, as part of the impurities, at most 6.00% wt of lead.

6. The molten liquid metal composition according to claim 1 further comprising, as part of the impurities, at least 0.0001% wt and at most 0.50% wt of silver.

7. The molten liquid metal composition according to claim 1 further comprising, as part of the impurities, at least 0.005% wt and at most 0.40% wt of arsenic.

8. The molten liquid metal composition according to claim 1 further comprising, as part of the impurities, at least 0.001% wt and at most 0.100% wt of sulphur.

9. The molten liquid metal composition according to claim 1 further comprising, as part of the impurities, at most 0.50% wt of zinc.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0092] FIG. 1 shows a flow diagram of the core part of an embodiment of the process according to the present invention.

DETAILED DESCRIPTION

[0093] The present invention will hereinafter be described in particular embodiments, and with possible reference to particular drawings, but the invention is not limited thereto, but only by the claims. Any drawings described are only schematic and are non-limiting. In the drawings, the size of some of the elements may be exaggerated and not drawn to scale for illustrative purposes. The dimensions and the relative dimensions in the drawings do not necessarily correspond to actual reductions to practice of the invention.

[0094] Furthermore, the terms first, second, third and the like in the description and in the claims, are used for distinguishing between similar elements and not necessarily for describing a sequential or chronological order. The terms are interchangeable under appropriate circumstances and the embodiments of the invention can operate in other sequences than those described and/or illustrated herein.

[0095] Moreover, the terms top, bottom, over, under and the like in the description and the claims are used for descriptive purposes and not necessarily for describing relative positions. The terms so used are interchangeable under appropriate circumstances and the embodiments of the invention described herein may operate in other orientations than described or illustrated herein.

[0096] The term “comprising”, as used in the claims, should not be considered as being limited to the elements that are listed in context with it. It does not exclude that there are other elements or steps. It should be considered as the presence provided of these features, integers, steps or components as required, but does not preclude the presence or addition of one or more other features, integers, steps or components, or groups thereof. Thus, the volume of “an article comprising means A and B” may not be limited to an object which is composed solely of agents A and B. It means that A and B are the only elements of interest to the subject matter in connection with the present invention. In accordance with this, the terms “comprise” or “embed” enclose also the more restrictive terms “consisting essentially of” and “consist of”. By replacing “comprise” or “include” with “consist of” these terms therefore represent the basis of preferred but narrowed embodiments, which are also provided as part of the content of this document with regard to the present invention.

[0097] Unless specified otherwise, all values provided herein include up to and including the endpoints given, and the values of the constituents or components of the compositions are expressed in weight percent or % by weight of each ingredient in the composition.

[0098] Additionally, each compound used herein may be discussed interchangeably with respect to its chemical formula, chemical name, abbreviation, etc..

[0099] The present invention is directed to the electrorefining of copper, i.e. the purification of a copper stream containing impurities, in particular other metals, from which anodes are made, into copper cathodes having a higher copper purity. This is significantly different from the electrowinning of copper. In the hydrometallurgical recovery of copper from ores or other feedstocks, metals are leached from the starting solid into a liquid leaching solution, dissolving the metals by means of strong acid solutions (such as sulphuric acid, hydrochloric acid). In the downstream copper electrowinning step, copper may be recovered from the liquid leaching solution, or from a concentrate derived therefrom, by selectively pushing the copper cations out of solution and depositing the copper on a cathode, under the driving force of an electric voltage difference between the cathode and a chemically inert anode, usually made of lead, at which surface water is electrochemically split into oxygen gas (O.sub.2, escaping from the cell) and protons (H.sup.+) which stay in solution. For each proton formed, one electron is released. These electrons pass through the electric circuit from the anode to the cathode, and are picked up at the cathode for the deposition of copper metal (primarily by the reaction Cu.sup.2++2 e.sup.−.fwdarw.Cu), similar to what happens at the cathode during electrorefining.

[0100] Because electrowinning has to also split water into oxygen and protons, it has been explained before in this document that the theoretically minimum required voltage difference over a copper electrowinning cell is significantly higher than for a copper electrorefining cell. The practical voltage difference over a copper electrowinning cell is therefore at least 1.6 V, and in practice differences in the range of 1.6-2.5 Volt are practised in order to overcome also the extra resistances in the electrowinning electrolyte.

[0101] In the context of the present invention, by electrolyte refreshing rate of an electrolytic cell is meant the electrolyte removal rate in percent relative to the liquid volume of the empty electrolytic cell per unit of time, usually per hour. With an empty electrolytic cell is meant the amount of liquid the cell may contain when it is still empty, i.e. the cell before any of the electrodes or other elements or submerged ancillaries are introduced, such as guides for electrodes and/or suction mouths, and/or manifolds and/or distributors for incoming and/or outgoing fluids, gas and/or liquid. The refreshing rate as defined in the context of the present invention is the refreshing rate of the electrolytic cell, albeit of one or more cells belonging to the same electrorefining unit, and therefore is totally independent of the volume of any bleed stream that is typically continuously withdrawn from the circulating electrolyte, which some may consider to represent also a “refreshing rate”, but then relative to the electrolyte cycle as a whole, and which has no connection whatsoever with the refreshing rate defined in the context of the present invention.

[0102] The prescriptions for the refreshing rate in the context of the present invention relate to the average refreshing rate throughout an entire electrolytic cycle, i.e. the operating period between two subsequent anode replacements. We shall discuss further in this document that more than one single stream of electrolyte may be removed from the cell, and that such a removal stream does not necessarily need to be continuous, but may also be discontinuous. It may therefore be that, during particular periods of operation, the removal rate of electrolyte from the cell may be significantly increased periodically. The prescription for the average refreshing rate in the context of this invention is therefore the average over the entire electrolytic cycle, including any periods during which the electrolyte removal rate is higher. The time period for the average refreshing rate relates to operating time only, i.e. time that the cell is at least partially in operating mode with the electrical current passing through the cell.

[0103] In an embodiment of the present invention, the voltage difference between the cathode and the anode in the electrolytic cell is at most 1.5 V, preferably at most 1.4 V, more preferably at most 1.3 V, even more preferably at most 1.2 V, preferably at most 1.1 V, more preferably at most 1.0 V, even more preferably at most 0.9 V, preferably at most 0.88 V, more preferably at most 0.85 V, even more preferably at most 0.83 V, preferably at most 0.80 V, more preferably at most 0.7 V, even more preferably at most 0.6 volt. Preferably the prescribed upper voltage limit is respected throughout a full electrolytic cycle, including the end of the cycle when the anodes have become substantially exhausted and are up for replacement, and the voltage over the cell is usually the highest. The applicants prefer to maintain the cell voltage below the prescribed upper limit because that reduces the cathode contamination and improves cathode quality, while it reduces the risk for excessive resistance build-up in the cell, which may lead to temperature rises which may cause thermal stresses, additive breakdown, and other undesired effects.

[0104] In an embodiment of the present invention, the anode comprises at most 97.5% wt of copper, preferably at most 97.0% wt, more preferably at most 96.5% wt, even more preferably at most 96.0% wt, preferably at most 95.5% wt, more preferably at most 95.0% wt, even more preferably at most 94.5% wt, preferably at most 94.0% wt, more preferably at most 93.5% wt, even more preferably at most 93.0% wt, preferably at most 92.5% wt, more preferably at most 92.0% wt, even more preferably at most 91.5% wt of copper. The applicants have found that several of the benefits of the present invention become even more significant when the anodes are less pure, i.e. leave more room for metals other than copper. For instance, this widens the acceptance quality requirements for the feedstocks of the upstream pyrometallurgical process steps as well as the operating window for the upstream pyrometallurgical steps by which the anode metal is produced.

[0105] In an embodiment of the present invention, the anode and/or the molten liquid metal composition according to the present invention comprises at most 0.90% wt of iron, preferably at most 0.80% wt, more preferably at most 0.70% wt, even more preferably at most 0.60% wt, preferably at most 0.50% wt, more preferably at most 0.40% wt, even more preferably at most 0.30% wt, preferably at most 0.25% wt, more preferably at most 0.20% wt, even more preferably at most 0.15% wt, preferably at most 0.10% wt, even more preferably at most 0.050% wt of iron. This brings the advantage that the electrolyte will also contain less iron, and that the problems which are associated with the presence of iron cations in the electrolyte are easier to keep of reduced importance, up to a point of being acceptable, or even become close to absent.

[0106] In an embodiment of the present invention, the current density through the cell is at least 190 A/m.sup.2, preferably at least 200 A/m.sup.2, more preferably at least 210 A/m.sup.2, even more preferably at least 220 A/m.sup.2, preferably at least 230 A/m.sup.2, more preferably at least 240 A/m.sup.2, even more preferably at least 250 A/m.sup.2, preferably at least 260 A/m.sup.2, more preferably at least 270 A/m.sup.2, even more preferably at least 280 A/m.sup.2. A higher current density through the cell typically brings the advantage that the productivity of the cell is increased, in particular if the contribution of the current to the transfer of copper cations is maintained high, and the part of the current that is used by mechanisms that do not contribute to the transfer of copper cations from anode to cathode is kept low, e.g. by keeping the amount of iron cations in the electrolyte low, such as by using anodes comprising iron at a level below the prescribed limit.

[0107] In an embodiment of the present invention, the current density through the cell is at most 400 A/m.sup.2, preferably at most 390 A/m.sup.2, more preferably at most 380 A/m.sup.2, even more preferably at most 370 A/m.sup.2, preferably at most 360 A/m.sup.2, more preferably at most 350 A/m.sup.2, even more preferably at most 340 A/m.sup.2, preferably at most 330 A/m.sup.2, more preferably at most 320 A/m.sup.2, even more preferably at most 310 A/m.sup.2, preferably at most 300 A/m.sup.2, more preferably at most 290 A/m.sup.2, even more preferably at most 280 A/m.sup.2. The applicants have found that respecting the prescribed upper limit for the current density through the cell brings the advantage that the problems that are increased by a higher current density are kept manageable and that the advantageous effects of the present invention are more readily obtained. These problems have been described elsewhere in this document, and anode passivation is a prime example of such a problem.

[0108] In an embodiment of the present invention, the electrolyte is removed from the cell at an average refreshing rate of more than 30%, preferably at least 35%, more preferably at least 40%, even more preferably at least 45%, preferably at least 50%, more preferably at least 55%, even more preferably at least 60% per hour, preferably at least 70%, more preferably at least 75%, even more preferably at least 80%, preferably at least 85%, more preferably at least 90%, even more preferably at least 95%, preferably at least 100%, more preferably at least 105%, even more preferably at least 110% per hour. The refreshing rate, and its average, is as defined above. The refreshing rate as specified is only accounting for the volume of the first stream of electrolyte which is leaving the cell by overflow. Any other stream of electrolyte leaving the cell, such as the second stream of electrolyte containing anode slimes which is introduced later in this document, is in addition to the first stream refreshing rate. The applicants have found that a higher refreshing rate of electrolyte is a strong contributor in controlling the amount of anode slime in the cell. This is a significant contributing element in keeping the cathode quality high, in spite of high levels of impurities in the anodes. It further brings other advantages, such as a faster access to the valuable anode slime for further upgrading. A higher refreshing rate also contributes to an increased agitation in the liquid bath inside the electrolytic cell. The higher liquid flows may bring some degree of liquid turbulence by themselves, at least locally, over and above the contribution of the gas introduction and bubbling, and therefore do help in reducing the thickness of the stagnant liquid films that inevitably form on the surfaces of anode and/or cathode, and facilitate the movement of copper cations from anode to cathode. Thanks to the upper limit of iron specified for the anode composition, the higher refreshing rate does not significantly increase any burden caused by iron cations in the electrolyte.

[0109] In an embodiment of the present invention, the electrolyte is removed from the cell at an average refreshing rate of at most 1700% per hour, preferably at most 1500%, more preferably at most 1200%, even more preferably at most 1000%, preferably at most 800%, more preferably at most 600%, even more preferably at most 400%, preferably at most 300%, more preferably at most 290%, even more preferably at most 250%, preferably at most 200%, more preferably at most 175%, even more preferably at most 150%, preferably at most 125% per hour. The applicants have found that compliance with the prescribed upper limit for the refreshing rate of electrolyte brings the advantage that the liquid pressure on the electrodes may remain limited. This brings the advantage that it may not be necessary to provide guides for all electrodes in the bath to limit electrode movement in the cell and to maintain the distance between adjacent electrodes within close limits from the desired (and usually design) values. Limiting the electrolyte refreshing rate below the specified upper limit brings the advantage that heavy anode slimes are given more chance to settle on the bottom of the cell, from which they may be removed during operation as explained further in this document.

[0110] In an embodiment of the present invention, the amount of gas introduced into the cell and bubbled through the electrolyte between the anode and the cathode is at least an effective amount, i.e. an amount that is effective in resulting in enhanced electrolyte agitation. An effective amount of gas achieves a noticeable reduction of the cell voltage at the desired current density as compared to the voltage established without any gas introduction. The gas needs to be supplied at a pressure which is at least sufficient to overcome the hydrostatic pressure represented by the column of liquid in the cell above the introduction level of the gas, and preferably higher. The applicants prefer to apply a pressure that is at least 0.1 bar above this minimum required pressure, preferably at least 0.3 bar, more preferably at least 0.5 bar above the hydrostatic pressure, together with a plurality of flow restrictions, such as small holes or nozzles, through which the gas is sparged into the cell, such that a pressure drop is established over flow restrictions and the gas flow is better distributed over the plurality of flow restrictions, and therefore the resulting gas bubbles are also more evenly distributed over the cell.

[0111] In an embodiment of the present invention, the metal composition comprises at least 90.5% wt of copper, preferably at least 91.0% wt, more preferably at least 91.5% wt, preferably at least 92.0% wt, more preferably at least 92.5% wt, even more preferably at least 93.0% wt of copper.

[0112] Preferably the molten liquid metal composition according to the present invention is also complying, where possible, with the concentration limits prescribed for the anode composition as part of the process according to the present invention, preferably also with the preferred concentration limits for the anode composition but with the exception of the oxygen content. The benefits associated with these concentration features prescribed for the molten liquid metal composition in accordance with the present invention are the same as described in the context of the anode composition as part of the process according to the present invention.

[0113] In an embodiment, the molten liquid metal composition according to the present invention comprises at least 0.25% wt of nickel, preferably at least 0.50% wt, more preferably at least 0.75% wt, even more preferably at least 1.00% wt, preferably at least 1.25% wt, more preferably at least 1.50% wt, even more preferably at least 2.00% wt, preferably at least 2.10% wt, more preferably at least 2.25% wt, even more preferably at least 2.50% wt of nickel. A higher nickel level in the metal composition allows the upstream process to accept more feedstocks that contain significant amounts of nickel. Such feedstocks are difficult to handle for most electrorefining operations, and are therefore more readily available at economically more favourable conditions. Optionally the metal composition comprises at most 10.0% wt of nickel, preferably at most 9.0% wt, more preferably at most 8.0% wt, even more preferably at most 7.00% wt, preferably at most 6.00% wt, more preferably at most 5.50% wt, preferably at most 5.00% wt, more preferably at most 4.50% wt, preferably at most 4.00% wt, more preferably at most 3.50% wt of nickel. At lower levels of nickel in the anode composition, the bleed stream may be kept smaller, which simplifies its further processing and the associated operating costs. Lower levels of nickel also reduce the need for adding extra copper cations into the electrolyte. Less nickel also reduces the anode passivation, which allows the measures taken to cope with anode passivation to be operated at a lower severity and/or intensity.

[0114] The applicants have found that it is important to have the oxygen content of the molten liquid metal composition in accordance with the present invention in compliance with the upper limit as specified, preferably less than 3000 ppm wt, more preferably at most 2800 ppm wt, even more preferably at most 2600 ppm wt, preferably at most 2500 ppm wt, more preferably at most 2400 ppm wt, even more preferably at most 2300 ppm wt, more preferably at most 2200 ppm wt, even more preferably at most 2100 ppm wt, preferably at most 2000 ppm wt, more preferably at most 1800 ppm wt, even more preferably at most 1600 ppm wt, yet more preferably at most 1400 ppm wt. On the other hand, the applicants submit that it is also important to maintain the oxygen content in compliance with the lower limit as specified, preferably at least 300 ppm wt, more preferably at least 400 ppm wt, even more preferably at least 500 ppm wt, yet more preferably at least 600 ppm wt, preferably at least 700 ppm wt, more preferably at least 800 ppm wt, even more preferably at least 1000 ppm wt, preferably at least 1250 ppm wt, more preferably at least 1500 ppm wt, even more preferably at least 1750 ppm wt, yet more preferably at least 2000 ppm wt.

[0115] In an embodiment of the present invention, the anode comprises at least 75.0% wt of copper, preferably at least 77.5% wt, more preferably at least 80.0% wt, even more preferably at least 82.5% wt, preferably at least 85.0% wt, more preferably at least 87.5% wt, even more preferably at least 90.0% wt, preferably more than 90% wt, more preferably at least 91.0% wt, even more preferably at least 91.5% wt, preferably at least 92.0% wt, more preferably at least 92.5% wt, even more preferably at least 93.0% wt of copper. This brings the advantage that the copper production of the cell is higher, and that the measures that are implemented for alleviating the problems brought by anode impurities are easier to provide and to control. It thus brings the advantage of less anode slimes to be removed and processed, lower anode passivation, as well as a higher cathode quality, both in terms of composition as with respect to the physical aspects and ease of stripping.

[0116] In an embodiment of the present invention, at least part of the anode slimes in the cell are removed from the cell with the first stream of electrolyte. The applicants have found that the first stream of electrolyte via the overflow of electrolyte over a cell wall is highly suitable for entraining a part of the anode slimes, which are continuously being generated during the electrolytic cycle due to a number of reasons, primarily the impurities in the anode, as explained above. The applicants have found that it are primarily the lower density and thus lighter slime particles that are more readily entrained with the first stream of electrolyte.

[0117] In an embodiment of the present invention, the flow of the first stream of electrolyte is kept positive throughout the electrolytic cycle. The applicants prefer to maintain a positive liquid overflow ongoing all throughout the full electrolytic cycle, such that at all times during the electrorefining operation, the cell is maintained full of liquid. This reduces and possibly avoids the risks associated with a loss of liquid level in an electrolytic cell, when it becomes possible that electric arcs are pulled, such as in between naked electrodes or between an electrode and the overhead crane above the cell, which may cause equipment damage or represent safety hazards.

[0118] In an embodiment of the present invention, the cell wall having the overflow of the first stream of electrolyte is a side wall which crosses the planes of the largest surfaces of the electrodes, preferably the cell having a rectangular footprint (or horizontal layout) and the side wall having the overflow running about perpendicular to the orientation of the electrodes. Such side wall is usually the longest as compared to the cell head walls, which brings the advantage that the liquid flows per unit of cell wall length in the overflow may be made lower. This feature also brings the advantage that the current direction of the electrolyte leaving the cell via the overflow has a reduced impact on the electrode surfaces, which reduces the risk that the electrodes move as a result of the outgoing electrolyte flow. Preferably the current direction of the outgoing electrolyte is parallel to the electrode surfaces, and the sideways pressure of the outgoing electrolyte current on the electrodes may be substantially inexistent. For this reason, the applicants prefer to have the electrolyte overflowing substantially over the entire length of at least one cell side wall, possibly interrupted intermittently over limited distances for passing construction elements for supporting any cell overhead structure. The applicants have further found that this feature brings the advantage of a more homogeneous distribution of the additives in the electrolyte throughout the entire cell, as compared to feeding the electrolyte at one head end of the cell and having the overflow at the opposite head end of the cell, i.e. a setup in which all the electrolyte is passing the full length of the cell and the additive concentration gradually drops because of consumption from feed to outlet. The concentration of these additives is usually controlled at the inlet point for the electrolyte to the cell. Because these additives are gradually consumed and/or broken down at the cathode surfaces, as the electrolyte moves through the cell from inlet to outlet, this setup of the electrolyte overflow improves the distribution of these additives over the bath.

[0119] In an embodiment of the present invention, the first stream of electrolyte is passed through at least one settler providing a sufficiently high residence time at a sufficiently low liquid velocity for anode slimes to settle on the bottom of the settler. The applicants have found that a settler is highly suitable for collecting and removing a major portion of the anode slimes entrained in the cell overflow stream before this electrolyte may be recycled to the electrolytic cell. This removal step of anode slime from the electrolyte overflow, especially when the cleaned electrolyte is recycled, is a first step in controlling the anode slime concentration in the electrolytic cell, in particular of the fine and/or light anode slime particles that are being formed during the electrolytic cycle. It is a strong contributor in allowing the anodes to contain higher levels of impurities. The applicants prefer to provide a plurality of settlers.

[0120] In an embodiment, a flocculant is added to the electrolyte on its way to the settler. This facilitates the coagulation of particles and the settling of the anode slimes on the bottom of the settler. This brings the further advantage that less fine anode slimes are recycled to the electrolytic cell, thereby improving the control of the presence of anode slimes in the cell, and hence also the quality of the cathodes produced.

[0121] In an embodiment of the present invention wherein the process comprises the settler on the first stream of electrolyte, a third stream of electrolyte containing anode slimes is removed from the bottom of the settler. The generation of this third stream of electrolyte is a second step in controlling the anode slime concentration in the electrolytic cell, in particular of the fine and/or light anode slime particles that are being formed during the electrolytic cycle. This second step allows for a continuous operation of the settler, which facilitates its operation and at the same time allows a more frequent access to the anode slimes collecting on the bottom of the settler, with the associated benefits discussed elsewhere in this document with respect to more ready access to anode slimes. The applicants prefer to generate this third stream of electrolyte containing anode slimes intermittently from the same settler. By allowing time for building up a layer of anode slimes on the bottom of the settler, the third stream of electrolyte may be richer in anode slimes, and its further processing may be more effective, simple, efficient and rewarding.

[0122] In an embodiment of the present invention, a second stream of electrolyte containing anode slimes is removed from the bottom of at least one electrolytic cell. The applicants have found that a part of the anode slimes succeed in sinking towards the bottom of the cell and in reaching the space in the cell below the level at which the gas is introduced. In this lower region, the liquid is moving much less, and the anode slime particles reaching this region readily form a layer of electrolyte on the bottom of the cell that is highly rich in anode slimes. The applicants prefer to also remove this anode slime, by withdrawing the second stream of electrolyte containing anode slimes from the bottom of the electrolytic cell.

[0123] In an embodiment of the present invention, the second stream of electrolyte is removed during the electrorefining operation from a bottom section of the cell provided below the electrodes for collecting anode slime. The applicants have found that it is advantageous to remove the second stream from the cell during the electrolytic cycle, and more preferably while the electrorefining is in operating mode, i.e. with the electrical current passing through the cell. The applicants have found that it is possible to remove the second stream from the cell while the cell is in full operation. This brings the advantage compared to many of the processes described in the art that the cell does not need to be taken out of service for removing the anode slime layer collecting on the bottom of the cell, and that it is easier to control the presence of anode slimes in the cell throughout the electrolytic cycle. The applicants prefer to provide in the cell a space below the electrodes, more preferably also below any equipment provided for introducing gas into the cell. In this bottom space the liquid flows slower and with less turbulence, because of the absence of gas bubbles. The applicants prefer to provide the electrolyte supply to the cell at a level that is above this bottom section, such that also the shortest liquid path between this liquid inlet point and the electrolyte overflow over the at least one cell wall does not pass, and thus hardly disturbs, the bottom space provided for collecting the heavy part of the anode slime that is formed.

[0124] In an embodiment of the present invention, the second and/or the third stream of electrolyte containing anode slimes is sucked from the bottom of the cell and/or from the bottom of the settler, preferably by a suction head moving over the bottom of the cell and/or settler. The applicants, preferably at regular intervals during the electrolytic cycle and while the electrolytic cell is in operating mode, pass a suction mouth through the cell in a space that is provided below the electrodes, also below any equipment provided for introducing gas into the cell, but above a space that is provided in the bottom section of the cell for collecting the anode slimes particles.

[0125] A suitable method for removing the second and/or third stream of electrolyte containing anode slimes is by sucking the stream by means of a suction mouth that is moved over the bottom of the cell and/or settler, preferably above the space provided for collecting the anode slime layer. A suitable method for this feature is described in WO 00/79025 A1.

[0126] The applicants prefer to remove the bottom layer of anode slimes in the cell before the top of the layer reaches the level in the cell at which the gas is introduced, preferably before the top of the layer reaches the level at which the suction mouth is moved through the cell for sucking up the second stream of electrolyte from the bottom of the cell, preferably rich in anode slimes.

[0127] The applicants prefer to also provide similar facilities and precautions in the settlers through which the first stream of electrolyte is passing, its anode slimes are supposed to largely settle at the bottom of the settler, by which an electrolyte is produced that is leaner in anode slimes as compared to the first electrolyte stream leaving the electrolytic cell.

[0128] In an embodiment of the present invention, the second stream of electrolyte is combined with the first and/or with the third stream of electrolyte into a combined stream of electrolyte containing anode slimes. This brings the advantage that these streams may be processed together, which simplifies the downstream operation.

[0129] In an embodiment of the present invention, the process comprises the recycle to the electrolytic cell of electrolyte that has been removed from the cell. This recycle brings significant advantages. The recycle of electrolyte brings the advantage that process chemicals in the electrolyte, such as sulphuric acid, are reused. A further advantage is that compounds that remain soluble in the electrolyte but tend to build up during electrorefining operation, are able to concentrate up to higher concentrations, which makes the downstream recovery of these compounds more effective.

[0130] In an embodiment of the present invention, the process comprises the removal of an electrolyte bleed stream from the electrolyte recycle. Such a bleed stream brings the advantage that its removal rate is able to control the concentration of compounds in the electrolyte that tend to build up in the electrolyte and remain in solution. One such compound is nickel sulphate, for which the solubility limit is significant.

[0131] In an embodiment of the present invention, the bleed stream is subject to at least one electrowinning step. The applicants have found that it is advantageous to recover particular metals from this bleed stream. The bleed stream contains significant levels of copper, and a major portion thereof may readily be selectively recovered by copper electrowinning. The bleed stream may also contain significant levels of nickel. Also these may selectively be recovered by nickel electrowinning, a process that is similar but somewhat different from copper electrowinning, and which operates better once the copper content of the electrolyte has been reduced to a level that is at most 20 grams/litre, preferably at most 15 grams/litre, more preferably at most 10 grams/litre, even more preferably at most 5 grams/litre, yet more preferably at most 1 grams per litre, preferably at most 750 milligrams/litre, more preferably at most 500 milligrams/litre, even more preferably at most 250 milligrams/litre, preferably at most 100 milligrams/litre, more preferably at most 50 milligrams/litre, even more preferably at most 10 milligrams/litre.

[0132] In an embodiment of the present invention, most of the metals are removed from the bleed stream, thereby forming a “black acid” stream, i.e. a concentrated acid stream. This black acid stream is typically and advantageously more concentrated in acid than the electrolyte. The applicants prefer to remove the metals, in particular the nickel, by evaporation of water from the bleed stream, preferably after reducing the copper content as described above. By this evaporation, nickel sulphate concentrates up to above its solubility limit, and crystallizes. The nickel sulphate crystals may then be recovered by sedimentation, filtration, centrifuging, or combinations thereof.

[0133] In an embodiment of the present invention, the black acid stream is recycled to the electrolytic cell, preferably the black acid stream being recycled after extra copper cations having been added to the black acid. This brings the advantage that most of the acid in the bleed stream may be reused, and less acid make-up is required in order to maintain the acid concentration in the electrolyte at the desired level. The applicants have further found that the black acid, because of its high acid concentration, particularly when higher than this of the electrolyte in the cell, is highly suitable for dissolving copper into, as discussed further down in this document. Together with contributing in the maintenance of the acid concentration in the electrolyte, the black acid recycle including extra copper cations contributes in maintaining the copper cation concentration in the electrolyte at the desired operating concentration.

[0134] In an embodiment of the present invention, anode slimes are separated from at least one of the first, the second and/or the third electrolyte streams, preferably from the combined stream of electrolyte containing anode slimes, preferably upstream of the removal of an electrolyte bleed stream from the electrolyte recycle, preferably the anode slimes being removed as a solid, more preferably using a filter press or a tube press. This brings the advantage of controlling the anode slimes concentration in the electrolytic cell. The applicants prefer to make this separation of anode slimes from the electrolyte as clean as possible, in order to reduce into the anode slimes by-product the presence of copper and/or nickel, at least the copper and/or nickel that are present as dissolved in the electrolyte.

[0135] In an embodiment of the present invention wherein the anode slimes are removed as a solid and wherein the anode slimes solid is water washed before recovery of the anode slime by-product from the overall process, the wash water being recycled to the electrorefining process. This same wash water may further be used, subsequent to the described washing step, and/or may have been used, prior to the described washing step, for other useful functions such as washing the spent anodes and/or cathodes after these have been removed from the electrolytic cell, and/or for dissolving ingredients that need to be added to the electrolytic cycle, such as additives or extra copper cations, before being recycled to the electrorefining process.

[0136] The washing of the anode slimes solids brings the advantage that a lesser amount of the soluble metals, in particular copper and/or nickel, are leaving the process with the anode slimes by-product in which they do not bring much value but usually represent a burden. By recycling this used wash water, more of these soluble metals may be kept in the process, and may then more conveniently be removed as part of the bleed stream, from which they are more readily recovered.

[0137] In an embodiment of the present invention wherein the anode slimes solid is water washed, the water wash of the anode slimes is operated at a temperature of at least 40° C., preferably at least 50° C., more preferably at least 60° C., even more preferably at least 65° C., and at most 90° C., preferably at most 85° C., more preferably at most 80° C., even more preferably at most 75° C. The applicants have found that a higher temperature of the water wash helps in washing the sulphate salts out of the anode slimes solid, in particular the copper sulphate and/or nickel sulphate. Because the used wash water is returned into the electrolyte cycle, it is advantageous to have this wash water having a temperature that is close to the desired electrolyte temperature, because it reduces any heating and/or cooling duty to assure a proper heat household in the electrolyte cycle. The applicants have also found that compliance with the upper temperature limit as specified reduces the risk for damage to the equipment construction material. The filter plates of the filter or filter press used to retain the anode slimes during the water wash may e.g. be made from polypropylene, and the applicants have found that this material is less subject to wear and tear at a temperature in compliance with the upper limit as specified.

[0138] In an embodiment of the process according to the present invention, the anode slimes that have been recovered, preferably after water washing, are treated with sufficient base, preferably NaOH, to convert most of the metal sulphates into a soluble sulphate salt, such as Na.sub.2SO.sub.4, and insoluble metal hydroxides. In this way the sulphur content of the anode slimes may be reduced, which makes them more acceptable for the downstream recovery of the metals, a.o. because it is more concentrated in the metals. Metal recovery processes are typically better equipped to handle metal oxides and/or hydroxides. Often other types of feedstocks are preferably roasted to obtain the oxides before the metals may be recovered.

[0139] The hydroxides are preferably heated to form oxides, and in a pyrometallurgical process step performed in a furnace, using a reducing agent such as iron, a multi-metal solder may be recovered from the anode slimes, and an iron oxide containing slag as by-product. In order to extract more Sn from the slag into the metal phase, and to improve the physical phase separation between the solder phase and the slag phase, extra lead may be added, preferably until the tin/lead weight ratio in the metal phase is close to ⅓.

[0140] In an embodiment of the present invention, extra copper cations are introduced into the electrolyte in the cell. The applicants have found that several contaminant metals in the anode consume electrical current when they go into solution into the electrolyte, over and above the current consumed by the anode copper going into solution. At the cathode this extra current causes more copper to deposit than there was copper dissolved at the anode. There is thus more copper depositing on the cathode than there is copper coming into solution at the anode. This imbalance represents a net consumer of copper from the electrolyte. In order to compensate for this net consumption, extra copper cations are added into the electrolyte in the electrolytic cell. The applicants have found that the copper imbalance becomes more important as the level of impurities in the anode increases. While conventional electrorefining operations, which start from anodes comprising 98-99% wt of copper, usually operate without addition of extra copper cations to the electrolyte, the applicants have found that this addition is highly beneficial in the process according to the present invention, in which the anodes comprise less copper and more other metals. The applicants have found that the addition allows the process to operate over a long period of time, with intensive electrolyte recycle, and with a high concentration of copper cations in the electrolyte, which is particularly beneficial at the cathode where the high concentration contributes to a high process productivity at a reduced power consumption and a better cathode quality. Indeed, the applicants have found that adding extra copper cations to the electrolyte helps to maintain the concentration of copper cations within the desired levels, which is important to maintain over the long term the production of high quality copper cathodes without causing or introducing extra operating problems. The applicants have found that this concern is of a higher importance with anode compositions that contain a higher level of impurities. The applicants have also found that this feature allows to avoid the need for stopping the operation because of depletion of the copper concentration in the electrolyte below the minimum desired level, such as in several of the processes disclosed in the art.

[0141] In an embodiment of the present invention wherein extra copper cations are added into the electrolyte, the extra copper cations are introduced into the electrolyte feed to the cell, preferably into the electrolyte that is recycled to the electrolytic cell. The applicants have found that this is a highly convenient method for controlling the copper concentration in the electrolyte at the desired level.

[0142] In an embodiment of the present invention wherein extra copper cations are added into the electrolyte, a liquid stream comprising at least part of the recycled electrolyte, and/or a stream which is even more concentrated in acid, such as at least a part of the recycled black acid, or at least a part of the bleed stream post copper removal by electrowinning, if present, or at least part of the acid make-up to the process, is contacted with a copper containing solid for dissolving more copper into the liquid stream, preferably in a leaching vessel, before the liquid stream with the extra copper cations is transferred to the electrolytic cell. The applicants find these streams highly suitable for dissolving copper from a copper containing solid and hence to pick up extra copper cations that are useful in controlling the copper concentration in the electrolyte in the electrolytic cell. The applicants prefer to use a stream which is available and which is more concentrated in acid than the electrolyte. Streams that qualify are e.g. the black acid recycle because that stream is more acidic and therefore more readily dissolves copper from a solid source. The volumes of this black acid recycle are however relatively small relative to the electrolyte inventory of the process, and may also be available only intermittently. The process usually also needs a make-up of acid, e.g. for compensating for the loss of acid in the formation of nickel sulphate and/or lead sulphate. Such acid make-up stream may also be a highly concentrated acid stream, such as at least 50% wt sulphuric acid, possibly even 96% wt sulphuric acid, which is in that case also capable of more readily dissolving copper from a solid source, as compared with the electrolyte which is recycling to the cell. The make-up volumes are also relatively small, and may not be added continuously. The applicants therefore prefer to use an acid stream that is more concentrated than the electrolyte recycling to the cell, such as the black acid recycle stream and/or the sulphuric acid make-up stream when these are available, but else they prefer to use the electrolyte recycle stream for picking up an amount of extra copper cations on its way to the cell.

[0143] In an embodiment of the present invention, the copper containing solid is in the form of granules, preferably the granules being hollow and open, optionally the granules having been produced in a pyrometallurgical process step upstream of the process. The applicants have found that the copper containing solid is preferably in a finely divided form, as compared to large blocks, because the finely divided form offers more contact surface to the extracting liquid for the same amount of solid. The applicants have found that granules are easier to handle than powder. Granules may readily be stacked in a leaching vessel, and can be retained in the vessel by a simple strainer provided on the liquid outlet nozzle. Preferably the granules are hollow, offering more contact surface for the same weight of solid material. The applicants have found that it is highly convenient that the granules of copper containing material are produced in a pyrometallurgical process step which his located upstream of the process according to the present invention. Most conveniently, this upstream process step is part of the process producing the copper intermediate product used for casting the anodes that are used in the electrolytic step of the process according to the present invention. The material of the granules may be identical to the material used for the anodes, or may have a different quality. Preferably the granules are of a higher purity copper material than the anodes.

[0144] The applicants prefer to produce high surface small copper granules by splashing liquid molten copper onto a refractory brick above the level of a large tank containing a cold liquid such as water. The liquid molten copper stream is broken up on the refractory brick and spreads into the cold liquid. This brings the advantage of local high steam generation, similar to explosion, and does form high surface small copper granules or “shots” that are highly suitable for dissolving into an acid liquid.

[0145] The applicants prefer to provide at least one leaching vessel or tower for the addition of extra copper cations into the process. Such a vessel may be a vertical cylindrical vessel. The vessel may be open to the atmosphere on top, such that the copper containing solids may readily be introduced into the vessel. The solids may be forming a bed on a support in the bottom of the vessel, above the inlet for the liquid feed. The liquid inlet is conveniently provided below the bed support. The liquid flows upwards through the bed of solids and leaves the vessel via an overflow duct. The vessel is preferably designed such that the liquid upward velocity is low, and the specific gravity of the copper containing solids is sufficient to avoid solids being entrained from the leaching vessel with the liquid outlet. Preferably the copper containing solids are of high purity, such as blister copper, of at least 98% wt Cu. As the copper dissolves, the height of the bed reduces and the inventory of copper solids may be replenished via the open top of the vessel.

[0146] In an embodiment of the present invention, oxygen containing gas is added to the step of contacting the liquid stream with the copper containing solid. The applicants have found that the copper from the granules more readily comes into solution in the acidic leaching liquid under an oxidising atmosphere. Preferably the applicants inject air or enriched air, even more preferably commercially obtainable oxygen gas, into the bottom section of the leaching vessel, preferably below the bed support upon which the solids are retained. The applicants have found that the presence of oxygen in the leaching step strongly facilitates the pick-up of copper cations by the leaching liquid.

[0147] In an embodiment of the present invention, extra sulphuric acid is introduced into the process, preferably into the recycled electrolyte, if present, preferably together with or upstream of the introduction of the extra copper cations, if present. This feature provides a sulphuric acid make-up stream, useful for controlling the sulphuric acid content of the electrolyte, which otherwise would risk to become depleted because of the consumption of sulphate anion in lead and/or nickel sulphate. As discussed above, the applicants prefer to use a concentrated sulphuric acid source for this make-up, such as 96% wt sulphuric acid, and prefer to introduce this make-up acid where it comes into contact with the copper containing solids for picking up extra copper cations. High concentration acid make-up brings the advantage that it represents little risk for the introduction into the process of elements that are undesired. A further advantage is that it takes much less volume and handling hassle as compared to a less concentrated stream, and that also the copper more readily dissolves in it.

[0148] In an embodiment of the present invention, the gas that is introduced into the cell is air. The applicants prefer to use air for bubbling through the electrolytic cell, rather than its possible alternatives nitrogen, carbon dioxide, or even sulphur dioxide (SO.sub.2) as proposed in U.S. Pat. No. 1,260,830 and by E. N. Petkova in “Mechanisms of floating slime formation and its removal with the help of sulphur dioxide during the electrorefining of anode copper”, Hydrometallurgy, Vol. 46, Issue 3, October 1997, pp 277-286. The applicants prefer air because of its convenience and the improved safety and industrial hygiene aspects. The use of nitrogen and/or carbon dioxide would bring the risk that personnel might inadvertently become exposed to clouds of an atmosphere that is oxygen deficient. Sulphur dioxide brings the extra features that it is a toxic gas having a pungent, irritating smell, and hence requires even more stringent safety and industrial hygiene measures. Air brings the additional advantage that it is an oxidising agent, which is highly convenient because it is able to oxidise As.sup.3+ to As.sup.5+ and/or Sb.sup.3+ to Sb.sup.5+, whereby these metals are able to form compounds, usually salts, such as arsenates, or oxides, that more readily sink to the bottom of the cells and/or the settlers and collect in the anode slimes layer. These phenomena are described in more detail by C. A.Möller et al in “Effect of As, Sb, Bi and Oxygen in Copper Anodes During Electrorefining”, Proceedings of Copper 2010, pp. 1495-1510. Air is to the applicants a much more convenient oxidising agent than sulphur dioxide, for the reasons explained above.

[0149] In an embodiment of the present invention, the gas introduced into the cell is at a temperature in the range of the electrolyte temperature +/−30 degrees Celsius. This reduces any temperature effects that the gas introduction may bring locally in the cell. Preferably the gas temperature differs at most 25 degrees Celsius from the temperature of the electrolyte in the cell, more preferably at most 20 degrees Celsius, even more preferably at most 15 degrees Celsius. Local drops in temperature are undesired because that may cause some salts to be crystallising out locally, such as around the holes in the gas distributor, and which could impair the gas flow through those holes. A local increase of temperature is also undesired because it may cause a more rapid degradation of some of the process additives. The applicant prefer to introduce the gas into the cell at a temperature of about 45° C. The applicants prefer to maintain the electrolyte in the cell at a temperature in the range of 65-70° C., preferably about 68° C.

[0150] In an embodiment of the present invention, the gas introduced into the cell is at least saturated in water at the temperature of introduction of the gas. This reduces the risk for crystallisation in and around the opening through which the gas enters the electrolyte.

[0151] In an embodiment of the present invention, water is injected, preferably as an aerosol, into the gas before it is introduced into the cell. The applicants prefer to inject water that is low in sodium content, preferably below the detection limit, preferably the injection water being obtained by reverse osmosis. The applicants have found that this feature reduces the formation of salts on the injection points of the gas into the electrolyte, and also on any microporous polymer sleeve that may be provided around the gas diffuser tubes.

[0152] In an embodiment of the present invention, the gas bubbles passing through the electrolyte have an average diameter in the range of 1 to 3 mm. The applicants have found that gas bubbles of at most 3 mm diameter are more effective in removing depleted electrolyte adjacent to the surfaces of the cathodes in order to permit fresh electrolyte to come into contact with the cathodes. The small bubbles also tend to minimise the production of acid mist above the electrolysis cell. Smaller bubbles are also preferred because they introduce a regime in the cell that becomes similar to a so-called “Dissolved Air Flotation” (DAF) regime, such that small particles of anode slimes are readily brought up to the surface of the liquid column and readily leave the cell via the overflow. The size of the gas bubbles may e.g. be determined as explained by Reza Al Shakarji et al, in “The sizing of oxygen bubbles in copper electrowinning”, Hydrometallurgy, 109 (2011), pp. 168-174.

[0153] In an embodiment of the present invention, the gas is introduced into the cell through a gas diffuser provided below the electrodes but above the space which is provided in the cell bottom for collecting the anode slimes layer, preferably the gas diffuser comprising selectively perforated diffuser pipes connected to the gas supply pipe. The location of the gas diffuser divides the vertical height of the electrolyte volume into two parts, the upper part through which gas bubbles rise which bring more turbulence, and the lower part without gas bubbles which is more stagnant, in particular if also the electrolyte feed is provided at about the height of the gas diffuser. The extra turbulence in the upper part brings the advantages discussed above in high detail. The lower fluid movement in the lower part facilitate the settling of anode slimes particles on the bottom of the cell. The applicants prefer to use a diffuse as described in WO 2005/019502 A1, using a plurality of hoses made from and/or including microporous material which permits, in use, the sparging gas to pass through this microporous material so as to form a multiplicity of fine bubbles in the electrolyte in the cell.

[0154] The applicants have found that the diffuser preferably provides a uniformly distributed presence of gas bubbles throughout the upper part of the electrolyte volume. Non-uniformity in the gas bubble presence may cause differences in hydrostatic pressure on an electrode, which brings the risk that the electrode may become tilted sideways and cause contact, and hence an electrical short-circuit, with an adjacent counter-electrode.

[0155] The applicants prefer to provide a gradient in the density of gas introduction, with less gas being introduced closer to the cell wall having the overflow and more gas closer to the opposite cell wall. This brings the advantage that the gas gradient creates an extra driving force for liquid flow in the direction of the overflow.

[0156] In an embodiment of the present invention, the gas is introduced into the cell using a pressure, in the supply line at the height of the liquid level in the cell, in the range of at least 0.5 bar gauge (barg), preferably at least 0.6 barg, more preferably at least 0.7 barg. This overpressure is necessary to overcome the hydrostatic pressure at the point of introduction of the gas into the cell, preferably below the electrodes. The applicants prefer to provide a higher overpressure than only the hydrostatic pressure, in order to enhance the sparging of the gas into the liquid and the formation of smaller bubbles. The pressure at the indicated point in the supply line is preferably at most 3.5 barg, preferably at most 3.0 barg, more preferably at most 2.5 barg, even more preferably at most 2.0 barg, preferably at most 1,75 barg, more preferably at most 1.50 barg, even more preferably at most 1.25 barg. Compliance with this upper limit reduces the risk for blowing out electrolyte from the cell, as well as the formation of nickel aerosols. Blown-out electrolyte may cause equipment damage, and the formation of nickel aerosols generates an industrial hygiene concern.

[0157] Primarily for the reasons of industrial hygiene, the applicants prefer to provide a cap above the cell equipped with an exhaust suction and a drop catcher to avoid acid droplets, possibly containing metal particles, from entering the working place.

[0158] In an embodiment of the present invention, the electrolyte in the cell is maintained at a temperature in the range of 20° C. to 75° C. Preferably the electrolyte temperature in the cell is at least 25° C., more preferably at least 30° C., even more preferably at least 35° C., preferably at least 40° C., more preferably at least 45° C., even more preferably at least 50° C., preferably at least 55° C., more preferably at least 60° C., even more preferably at least 65° C., preferably above 65° C. At higher temperatures, the copper diffusion rate is improved, and this is particularly beneficial for the diffusion of the copper cations through the stagnant or laminar flowing films that are typically present on the surfaces of anode and/or cathode. Higher temperatures also increase the solubility of sulphates in the electrolyte, and hence reduce the risk for crystallisation, especially at sensitive locations. The applicants prefer to maintain the electrolyte at a temperature below 75° C., preferably at most 72° C., more preferably at most 70° C. This brings the advantage that the additives which are temperature sensitive, such as gelatine and/or many flocculants, are more stable and less subject to degradation. A lower temperature also reduces the risk that the cathode would pre-strip, i.e. that the deposited copper layer would release from the stainless steel blank while the cathode is still in the electrolytic cell. A lower temperature also reduces the energy needed for maintaining the temperature of the electrolyte, which is usually above ambient and hence requires heat input.

[0159] In an embodiment of the present invention, the anode composition and/or the molten liquid metal composition according to the present invention comprises at least 0.25% wt of nickel, preferably at least 0.50% wt, more preferably at least 0.75% wt, even more preferably at least 1.00% wt, preferably at least 1.25% wt, more preferably at least 1.50% wt, even more preferably at least 2.00% wt, preferably at least 2.10% wt, more preferably at least 2.25% wt, even more preferably at least 2.50% wt, preferably at least 2.75% wt, more preferably at least 3.00% wt of nickel. A higher nickel level in the anode allows the upstream process to accept more feedstocks that contain significant amounts of nickel. Such feedstocks are difficult to handle for most electrorefining operations, and are therefore more readily available at economically more favourable conditions. Optionally the anode composition comprises at most 10.0% wt of nickel, preferably at most 9.0% wt, more preferably at most 8.0% wt, even more preferably at most 7.00% wt, preferably at most 6.00% wt, more preferably at most 5.50% wt, preferably at most 5.00% wt, more preferably at most 4.50% wt, preferably at most 4.00% wt, more preferably at most 3.50% wt of nickel. At lower levels of nickel in the anode composition, the bleed stream may be kept smaller, which simplifies its further processing and the associated operating costs. Lower levels of nickel also reduce the need for adding extra copper cations into the electrolyte. Less nickel also reduces the anode passivation, which allows the measures taken to cope with anode passivation to be operated at a lower severity and/or intensity. Less nickel also reduces the industrial hygiene concerns associated with nickel aerosols.

[0160] In an embodiment of the present invention, the anode composition and/or the molten liquid metal composition according to the present invention comprises at least 0.25% wt of lead, preferably at least 0.50% wt, more preferably at least 0.75% wt, even more preferably at least 1.00% wt, preferably at least 1.25% wt, more preferably at least 1.50% wt of lead. Allowing a higher lead level in the anode allows the upstream process to operate at a lower severity with respect to the separation between lead and copper, and also to accept more feedstocks that contain significant amounts of lead. Such feedstocks are difficult to handle for many copper production operations, and are therefore more readily available at economically more favourable conditions. Optionally the anode composition comprises at most 3 0 6.00% wt of lead, preferably at most 5.00% wt, more preferably at most 4.00% wt, even more preferably at most 3.00% wt, yet more preferably at most 2.50% wt, preferably at most 2.00% wt, more preferably at most 1.80% wt, even more preferably at most 1.60% wt, yet more preferably at most 1.50% wt of lead. At lower levels of lead in the anode composition, there is less lead sulphate forming in the cell. The consumption of acid towards lead sulphate is therefore reduced. Lead sulphate has a very low solubility in the electrolyte and therefore readily crystallizes out in the cell. The crystals represent a risk for being included into the cathode. A lower lead level in the anode therefore reduces the risk for lead being retrieved as an impurity in the cathode. The lead precipitates are preferably removed from the cell as part of the anode slimes in the first stream of electrolyte and/or in the second stream of electrolyte. Because the presence of lead does not contribute significantly to the value of the anode slimes produced by the process, but does contribute to the operating burden for processing the anode slimes, a lower lead presence in the anode is beneficial because it reduces the anode slimes volume and hence its operating burden, without reducing the value of the anode slimes by-product from the process. A lower level of lead in the anode composition also reduces the concern of lead releasing into the workplace during human intervention, e.g. when the anode slimes are released from the filter press, with which is associated a concern of industrial hygiene.

[0161] In an embodiment of the present invention, the anode composition and/or the molten liquid metal composition according to the present invention comprises at least 0.25% wt of tin, preferably at least 0.50% wt, more preferably at least 0.75% wt, even more preferably at least 1.00% wt, preferably at least 1.25% wt, more preferably at least 1.50% wt of tin. Allowing a higher tin level in the anode allows the upstream process to operate at a lower severity with respect to the separation between tin and copper, and also to accept more feedstocks that contain significant amounts of tin. Such feedstocks are difficult to handle for many copper production operations, and are therefore more readily available at economically more favourable conditions. In addition, the tin in the anode slimes is quite readily recoverable therefrom, and represents a significant part of the commercial value obtainable from the anode slimes by-product from the process according to the present invention. Optionally the anode composition comprises at most 6.00% wt of tin, preferably at most 5.00% wt, more preferably at most 4.00% wt, even more preferably at most 3.00% wt, yet more preferably at most 2.50% wt, preferably at most 2.00% wt, more preferably at most 1.80% wt, even more preferably at most 1.60% wt of tin. At lower levels of tin in the anode composition, the volume of anode slimes is reduced, because tin primarily leaves the process as an oxide of tin or tin plus antimony, both expected to end up in the anode slimes. Less tin in the anode therefore reduces the burden of processing the anode slimes. A lower tin level in the anode reduces the risk for tin being retrieved as an impurity in the cathode. Less tin also reduces the risk for growth of solid SnSb compounds on the wetted surfaces of the electrolytic cycle, in particular in and around the electrolytic cells.

[0162] In an embodiment of the present invention, the anode composition and/or the molten liquid metal composition according to the present invention comprises at least 0.10% wt of antimony, preferably at least 0.15% wt, more preferably at least 0.20% wt, even more preferably at least 0.25% wt, preferably at least 0.30% wt, more preferably at least 0.35% wt, preferably at least 0.40% wt, more preferably at least 0.50% wt of antimony. Allowing a higher antimony level in the anode allows the upstream process to operate at a lower severity with respect to the separation between antimony and copper, and also to accept more feedstocks that contain significant amounts of antimony. Such feedstocks are difficult to handle for many copper production operations, and are therefore more readily available at economically more favourable conditions. Optionally the anode composition comprises at most 3.00% wt of antimony, preferably at most 2.50% wt, more preferably at most 2.00% wt, even more preferably at most 1.50% wt, yet more preferably at most 1.25% wt, preferably at most 1.00% wt, more preferably at most 0.90% wt, even more preferably at most 0.80% wt of antimony. At lower levels of antimony in the anode composition, there is less risk for the formation of SnSb oxide compounds which may come out of solution and form solid deposits and grow on the wetted surfaces of the electrolytic cycle, in particular in and around the electrolytic cells. A lower antimony level in the anode reduces the risk for antimony being retrieved as an impurity in the cathode. The antimony is preferably removed from the cell as part of the anode slimes in the first stream of electrolyte and/or in the second stream of electrolyte, usually in the form of an intermetallic oxide, e.g. of tin with antimony. Because the presence of antimony brings hardly any contribution to the value of the anode slimes produced by the process, but does contribute to the operating burden for processing the anode slimes, a lower antimony presence in the anode is beneficial because it reduces the anode slimes volume and hence its operating burden, without reducing the value of the anode slimes by-product obtained from the process.

[0163] In an embodiment of the present invention, the anode composition and/or the molten liquid metal composition according to the present invention comprises at least 0.010% wt of bismuth, preferably at least 0.015% wt, more preferably at least 0.020% wt, even more preferably at least 0.025% wt, preferably at least 0.030% wt, more preferably at least 0.035% wt of bismuth. Allowing a higher bismuth level in the anode allows the upstream process to operate at a lower severity with respect to the separation between bismuth and copper, and also to accept more feedstocks that contain significant amounts of bismuth. Such feedstocks are difficult to handle for many copper production operations, and are therefore more readily available at economically more favourable conditions. Optionally the anode composition comprises at most 0.50% wt of bismuth, preferably at most 0.25% wt, more preferably at most 0.200% wt, even more preferably at most 2 0 0.150% wt, yet more preferably at most 0.100% wt, preferably at most 0.090% wt, more preferably at most 0.080% wt, even more preferably at most 0.070% wt of bismuth. A lower bismuth level in the anode reduces the risk for bismuth being retrieved as an impurity in the cathode. The bismuth is preferably removed from the cell as part of the anode slimes in the first stream of electrolyte and/or in the second stream of electrolyte, presumably as metallic bismuth and/or as an arsenate, such as BiAsO.sub.4, if sufficient arsenic is present. Because the presence of bismuth brings hardly any contribution to the value of the anode slimes produced by the process, but does contribute to the operating burden for processing the anode slimes, a lower bismuth presence in the anode is beneficial because it reduces the anode slimes volume and hence its operating burden, without reducing the value of the anode slimes by-product obtained from the process.

[0164] In an embodiment of the present invention, the anode composition and/or the molten liquid metal composition according to the present invention comprises at least 0.0010% wt of zinc, preferably at least 0.0050% wt, more preferably at least 0.0075% wt, even more preferably at least 0.010% wt, preferably at least 0.015% wt, more preferably at least 0.020% wt of zinc. Allowing a higher zinc level allows the upstream process to operate at a lower severity with respect to the removal of zinc of the copper containing streams leading to the anode composition, and also to accept more feedstocks that contain significant amounts of zinc. Such feedstocks are difficult to handle for many copper production operations, and are therefore more readily available at economically more favourable conditions. Optionally the anode composition comprises at most 0.50% wt of zinc, preferably at most 0.25% wt, more preferably at most 0.200% wt, even more preferably at most 0.150% wt, yet more preferably at most 0.100% wt, preferably at most 0.090% wt, more preferably at most 0.080% wt, even more preferably at most 0.070% wt, preferably at most 0.050% wt, more preferably at most 0.025% wt of zinc. A lower zinc level in the anode reduces the risk for zinc being retrieved as an impurity in the cathode. The zinc is preferably removed from the process as part of the bleed from the electrolyte cycle and/or as part of the anode slimes in the first stream of electrolyte and/or in the second stream of electrolyte. Because the presence of zinc brings hardly any contribution to the value of the anode slimes and/or of the bleed stream produced by the process, but does contribute to the operating burden for processing the anode slimes and/or the bleed stream, a lower zinc presence in the anode is beneficial because it reduces the anode slimes volume and hence its operating burden, without reducing the value of the anode slimes by-product obtained from the process. The same applies to the value of the bleed stream and its processing burden.

[0165] In an embodiment of the present invention, the anode composition comprises at least 0.005% wt of arsenic, preferably at least 0.010% wt, more preferably at least 0.020% wt, even more preferably at least 0.025% wt, preferably at least 0.050% wt, more preferably at least 0.060% wt, even more preferably at least 0.070% wt, yet more preferably at least 0.075% wt of arsenic. Allowing a higher arsenic level in the anode allows the upstream process to operate at a lower severity with respect to the removal of arsenic of the copper containing streams leading to the anode composition, and also to accept more feedstocks that contain significant amounts of arsenic. Such feedstocks are difficult to handle for many copper production operations, and are therefore more readily available at economically more favourable conditions. Arsenic is also claimed to reduce anode passivation, and is able to form intermetallic compounds such as arsenates, such as SbAsO.sub.4 and BiAsO.sub.4, which readily come out of solution and bring other metal impurities into the anode slimes. A higher arsenic compound may therefore also bring the advantage of a reduced anode passivation and a more ready removal of other impurity metals by making them become part of anode slimes. Optionally the anode composition comprises at most 0.40% wt of arsenic, preferably at most 0.30% wt, more preferably at most 0.250% wt, even more preferably at most 0.200% wt, yet more preferably at most 0.175% wt, preferably at most 0.150% wt, more preferably at most 0.125% wt, even more preferably at most 0.100% wt of arsenic. A lower arsenic level in the anode reduces the risk for arsenic being retrieved as an impurity in the cathode. The arsenic is preferably removed from the cell as part of the anode slimes in the first stream of electrolyte and/or in the second stream of electrolyte, e.g. as an arsenate of another metal impurity such as antimony or bismuth, or as a mixed oxide such as 2As.sub.2O.sub.5.3Sb.sub.2O.sub.3, or being bound and/or caught in the oxides of tin and/or tin plus antimony. Because the presence of arsenic brings hardly any contribution to the value of the anode slimes produced by the process, but does contribute to the operating burden for processing the anode slimes, a lower arsenic presence in the anode is beneficial because it reduces the anode slimes volume and hence its operating burden, without reducing the value of the anode slimes by-product obtained from the process.

[0166] In an embodiment of the present invention, the anode composition and/or the molten liquid metal composition according to the present invention comprises at least 0.0001% wt of silver, preferably at least 0.0010% wt, more preferably at least 0.0050% wt, even more preferably at least 0.0100% wt, preferably at least 0.0150% wt, more preferably at least 0.0200% wt, even more preferably at least 0.0250% wt, preferably at least 0.0300% wt, more preferably at least 0.0350% wt, even more preferably at least 0.0400% wt of silver. Silver readily leaves the process of the present invention most typically as part of the anode slimes, and silver is a strong contributor to the value of the anode slimes by-product of the process according to the present invention. A higher silver content is thus favoured because it makes the processing of the anode slimes, and the recovery of the metals contained therein, economically more rewarding. Optionally the anode composition and/or the molten liquid metal composition according to the present invention comprises at most 0.50% wt of silver, preferably at most 0.25% wt, more preferably at most 0.200% wt, even more preferably at most 0.150% wt, yet more preferably at most 0.100% wt, preferably at most 0.075% wt, more preferably at most 0.060% wt, even more preferably at most 0.050% wt of silver. A high presence of silver increases the risk for silver being incorporated into the cathodes. The silver in the copper anode does not bring any extra economic value and is thus a downgrade compared to silver in the anode slimes. Silver is an unwanted contaminant in cathode copper, because it brings technical problems in the main end-use of copper, i.e. the pulling of copper wire.

[0167] In an embodiment of the present invention, the anode composition comprises at most 0.0500% wt or 500 ppm wt of oxygen, preferably at most 0.0400% wt, more preferably at most 0.0300% wt, even more preferably at most 0.0200% wt, yet more preferably at most 0.0180% wt, preferably at most 0.0150% wt, more preferably at most 0.0125% wt, even more preferably at most 0.0100% wt or 100 ppm wt of oxygen. The applicants prefer the oxygen content to be below the specified limit because excessive oxygen presence increases the risk for anode malformation during casting and cooling, as explained elsewhere in this document. For that reason the applicants prefer that the anode composition contains oxygen below the upper limit as specified.

[0168] Optionally the anode composition comprises at least 0.0005% wt or 5 ppm wt of oxygen, preferably at least 0.0010% wt, more preferably at least 0.0015% wt, even more preferably at least 0.0020% wt, preferably at least 0.0025% wt, more preferably at least 0.0030% wt, even more preferably at least 0.0040% wt, preferably at least 0.0050% wt, more preferably at least 0.0075% wt, even more preferably at least 0.0100% wt or 100 ppm wt of oxygen. The applicants have found that it is preferable to not reduce the oxygen content in the anode composition to very low levels. The burden and effort of achieving very low levels of oxygen in the anode composition is not compensated by an equivalent economic benefit. On the contrary, the extra efforts typically performed for further reducing the oxygen content down to below the lower limit as specified are usually tedious, complex, and tend to also remove some valuable metals from the anode composition, hence reduce its volume and create lower value side streams. For that reason, the applicants prefer to have a level of oxygen in the anode composition in compliance with the lower limit as specified.

[0169] In an embodiment of the present invention, the anode composition is the molten liquid metal composition according to the present invention from which the oxygen content has been brought further down, preferably to have it arrive within the concentration range that is specified for the anode composition of the process according to the present invention, for instance of from 5 ppm wt to 500 ppm wt.

[0170] In an embodiment of the present invention, the electrolyte composition complies with at least one and preferably all of the following conditions: [0171] copper in the range of 20 to 55 grams/litre, [0172] nickel in the range of 25 to 90 grams/litre, [0173] sulphuric acid in the range of 130 to 200 grams/litre, preferably at most 190 grams/litre, more preferably at most 180 grams/litre, even more preferably at most 170 grams/litre, yet more preferably at most 160 grams/litre, and optionally at least 140 grams/litre, [0174] tin in the range of 0.4 to 1.4 grams/litre, preferably at most 1.2 grams/litre, more preferably at most 1.0 grams/litre, even more preferably at most 0.90 grams/litre, yet more preferably at most 0.80 grams/litre, and [0175] arsenic in the range of 10 to 200 milligrams/litre, preferably at least 15 milligrams/litre, more preferably at least 20 milligrams/litre and optionally at most 175 milligrams/litre, preferably at most 150 milligrams/litre, more preferably at most 100 milligrams/litre, even more preferably at most 75 milligrams/litre, and yet more preferably at most 50 milligrams/litre.

[0176] The applicants have found that it is advantageous to maintain the dissolved copper content of the electrolyte within the prescribed limits, because that range provides an excellent balance between its positive function at the cathode, where a high concentration helps the diffusion through the stagnant film on the cathode surface, and its possible negative functionality at the anode where a high concentration reduces the driving force for the diffusion through the stagnant film on the anode surface.

[0177] The applicants prefer to maintain the nickel content in the electrolyte within the prescribed limits, preferably at least 30 grams/litre, more preferably at least 35 grams/litre, even more preferably at least 40 grams/litre, preferably at least 45 grams/litre, more preferably at least 50 grams/litre, even more preferably at least 55 grams/litre, preferably at least 60 grams/litre, more preferably at least 65 grams/litre. A higher nickel content increases the value of the bleed stream from which the nickel may be recovered by its further processing, because of the higher amount of nickel present, but also because its recovery becomes more efficient. On the other hand a higher nickel content in the electrolyte also increases the risk that locally, e.g. in cold spots or in drops of electrolyte that have splashed onto equipment parts that are not submerged into the electrolyte but may be hot, nickel sulphate comes out of solution and forms a solid which may impair or even hinder a proper equipment operation. For those reasons, the applicants prefer to maintain the nickel content in the electrolyte at a level of at most 85 grams/litre, preferably at most 80 grams/litre, more preferably at most 75 grams/litre, even more preferably at most 70 grams/litre.

[0178] The applicants have found that it is advantageous to maintain the sulphuric acid content of the electrolyte within the prescribed limits, because that range provides an excellent balance between on the one hand its positive functions, to dissolve metals from the anode and to bring electrical conductivity to the electrolyte, and on the other hand its possible negative functionality by increasing the density and the viscosity of the electrolyte, which impairs mass and heat transfer and anode slimes settling rates, and the risk for damaging the operating equipment that may come into contact with the electrolyte. Higher sulphuric acid concentrations may impose the selection of more exotic and hence expensive construction materials, i.e. extra investment costs that may be avoided by complying with the upper limit as specified.

[0179] The applicants have found that tin dissolved in the electrolyte has a tendency to form so-called “floating slimes”, anode slime particles that do not sink to the bottom in the electrolytic cell, nor sink to the bottom in a settler where the residence time may be significantly higher and the liquid velocities may be significantly lower than in the cell. Such floating slimes are thus not removed from the electrolyte by the various provisions of the process as described for anode slimes removal.

[0180] The applicants desire to have the level of arsenic in the electrolyte to stay below the upper limit as specified. The presence of arsenic above the specified lower limit may be beneficial because it reduces the anode passivation mechanism, and is able to bring more other metal contaminants into intermetallic compounds that are solid and become part of the anode slimes. More arsenic than the specified upper limit in the electrolyte may however be disadvantageous because it leads to more arsenic in the bleed stream that needs further processing for recovery of most of its metal content, and also brings more arsenic in the anode slimes by-product. More arsenic may bring extra burdens for the further processing of the anode slimes and/or of the bleed stream removed from the electrolytic cycle, to the point that it even may necessitate an extra step in their respective further processing. More arsenic brings no extra value to the by-product streams, and is therefore preferably kept below the upper limit as specified. On the other hand, the applicants have found that low levels of arsenic, in compliance with the lower limit as specified, are acceptable because the extra burden or restrictions imposed by a requirement for an even lower arsenic content are not fully compensated by the extra benefits of the lower presence of arsenic.

[0181] In an embodiment of the present invention, at least one and preferably all of the following process chemicals are added into the electrolyte as prescribed: [0182] surface active components (e.g. gelatine) in the range of 25 to 900 grams/ton of cathode copper produced, preferably at least 50 grams/ton, more preferably at least 100 grams/ton, even more preferably at least 150 grams/ton, preferably at least 200 grams/ton, more preferably at least 250 grams/ton, preferably at least 300 grams/ton, more preferably at least 350 grams/ton, even more preferably at least 400 grams/ton, yet more preferably at least 450 grams/ton, preferably at least 500 grams/ton, more preferably at least 600 grams/ton and optionally at most 800 grams/ton, preferably at most 700 grams/ton, more preferably at most 600 grams/ton, even more preferably at most 500 grams/ton, even more preferably at most 400 grams/ton, preferably at most 350 grams/ton of cathode copper produced, [0183] hydrochloric acid (HCl) in the range of 25 to 250 grams of HCl per ton of cathode copper produced, [0184] hydrobromic acid (HBr) in the range of 25 to 400 grams of HBr per ton of cathode copper produced, [0185] at least one flocculant in the range of 800 to 3000 milligrams per ton of cathode copper produced, preferably at least 1000, optionally at most 2500, preferably at most 2000, more preferably at most 1500 milligrams/ton of cathode copper produced, and [0186] thiourea in the range of 15-150 grams per ton of cathode copper produced.

[0187] The applicants prefer to add at least one surface active component to the electrolyte. The applicants have found that the surface active components reduce/avoid the growth of dendrites on the cathodes, and hence reduce the risk for short-circuit formation. The applicants have found that gelatine is a very suitable surface active component. The applicants have found that the prescribed addition range, and typically about 650 grams gelatine per ton of cathode copper produced, is sufficiently effective without causing extra problems or unwarranted operating costs.

[0188] The applicants prefer to add hydrochloric acid (HCl) into the electrolyte. The hydrochloric acid brings the advantage that the polymerisation of any gelatine that may be added is impaired and its polymer chains are cut into smaller pieces, such that the gelatine retains its activity. Even more important is that the chlorine from the hydrochloric acid is able to bind silver (Ag) in an insoluble form (AgCl) which readily ends up as part of the anode slimes, and may conveniently be removed from the process, such that a high portion of the silver may be recovered economically. The applicants prefer to add at least 30 grams of hydrochloric acid per ton of cathode copper produced, preferably at least 50 grams, more preferably at least 75 grams, even more preferably at least 100 grams per ton of cathode copper produced, and optionally at most 225 grams, preferably at most 200 grams, more preferably at most 175 grams, preferably at most 150 grams per ton of cathode copper produced. The applicants find it most convenient to introduce the hydrochloric acid as a 30% wt solution, and prefer to add about 430 millilitre thereof per ton of cathode copper produced, but other concentrations may be used if convenient.

[0189] The applicants prefer to add also hydrobromic acid (HBr) to the electrolyte, in the dosing range as specified. The applicants prefer to add at least 30 grams of hydrobromic acid per ton of cathode copper produced, preferably at least 50 grams, more preferably at least 75 grams, even more preferably at least 100 grams per ton of cathode copper produced, and optionally at most 350 grams, preferably at most 300 grams, more preferably at most 250 grams, preferably at most 200 grams per ton of cathode copper produced. The applicants prefer to add typically about 125 grams HBr per ton of cathode copper produced. The hydrobromic acid brings the same advantages as the hydrochloric acid. Hydrobromic acid addition brings the extra benefit that its silver salt (AgBr) is even less soluble than the chloride. The hydrobromic acid thus brings the advantage that it is able to remove more silver from the electrolyte into the anode slimes. The applicants prefer to use HBr as a 48% wt solution but other concentrations may be used if convenient. The applicants prefer to use both the HCl and the HBr as specified.

[0190] The applicants prefer to add at least one flocculant to the electrolyte, preferably where the electrolyte enters the settlers, in the dosing range as specified and typically about 1035 milligrams per ton of cathode copper produced. We prefer to use a cationic polyacrylamide, based on adipic acid, which is e.g. available under the tradename ZETAG®, type 7565.

[0191] The applicants prefer to also add thiourea to the electrolyte, preferably where the electrolyte enters the settlers, at a dosing rate of 15-150 grams per ton of cathode copper produced, preferably at least 18, more preferably at least 20, even more preferably at least 25, yet more preferably at least 30 and optionally at most 125 grams, preferably at most 100 grams, more preferably at most 75 grams, even more preferably at most 50 grams, yet more preferably at most 49 grams, and typically about 32 grams of thiourea per ton of cathode copper produced. The thiourea is added to influence (together with the aforementioned process chemicals) the deposit morphology (roughness and/or nodule formation), the crystal shape (round and/or sharp) and the grain type (elongated and/or field oriented), which largely results in the avoidance of nodules, porosities and dendrites in the cathode. More information about the functions of thiourea and other additives in electrorefining have been described by Baumback J, Bombach H and Stelter M, “Investigations of the Behaviour of Thiourea and alternative Additives in Copper Electrorefining”, Proceedings EMC, 1 (2015), p 151-160. The applicants prefer not to exceed the upper limit as specified, in order to keep the amount of sulphur in the cathodes low.

[0192] In an embodiment of the present invention, the cathode blanks are made of stainless steel, preferably SS316L or “duplex” steel. The applicants have found that the deposited copper layer may readily be stripped from a stainless steel blank, and that the remaining blanks may readily be reused with a minimum of reprocessing for a new cathode run in the electrolytic cell.

[0193] In an embodiment of the present invention, the cathode spacing is at least 95 mm, preferably at least 100 mm, more preferably at least 105 mm, even more preferably at least 110 mm, preferably at least 115 mm, more preferably at least 120 mm. Although a smaller cathode spacing is beneficial for the electrical resistance through the cell, and hence also for the energy required by the electrorefining operation, the applicants have found that the high level of impurities in the anode composition brings extra risks for dendrite formation and growth, which are causes of short circuiting between a cathode and an adjacent anode. In order to reduce the operator intervention required in order to resolve such short circuiting, the applicants prefer to maintain the cathode distance as specified. The applicants have further found that a higher cathode distance brings the benefit of a higher cathode purity, in spite of a lower anode purity.

[0194] With cathode distance in the context of the present invention is meant the distance from the middle point of one cathode blank to the corresponding middle point of the adjacent cathode blank, and this includes the thickness of one cathode and of one anode in addition to two times the distance between a cathode surface and the surface of the adjacent anode facing the cathode surface.

[0195] In an embodiment of the present invention, the at least one cathode is renewed at a frequency that is higher than the renewal frequency of the anode. The applicants prefer to replace the cathodes in the cell by new blanks at a higher rate than replacing the spent anodes in the same cell by newly casted anodes. This brings the advantage that the cathodes are easier to strip because the layer of deposited copper is less thick. A further advantage is that the thinner copper layer on the cathode reduces the risk for damage of the blank during the stripping. Yet a further advantage is that a higher renewal frequency of the cathode reduces the risk for short circuit occurrence in the cell during the electrorefining operation. Such short circuiting causes the need for operator intervention, which is labour intensive.

[0196] The applicants have found that it is possible and advantageous to replace the cathodes partially from a particular electrolytic cell, e.g. only one third of the cathodes at one time. This brings the advantage that during the cathode replacement, the electrolytic cell may be kept in operation, and this even at its full production rate. The applicants find it advantageous to replace cathodes numbers 1, 4, 7, 10, etc. . . . by blanks, once this is done to replace cathodes numbers 2, 5, 8, 11, etc. . . . by blanks, and once these have been reduced replace the remaining cathode numbers 3, 6, 9, 12, etc. . . . by blanks. The applicants have found that it is possible to keep the electrolytic cell in operation during a cathode replacement performed in this way. The applicants have found that the cell may be kept in full operation, and that the ⅔ of cathodes present in the cell are able to cope with the full current density for the short periods of time required for each time replacing ⅓ of the cathodes by new blanks.

[0197] The applicants have found that it is readily possible to reduce the oxygen content of the metal composition according to the present invention down to a level that is preferred for the anode composition as part of the process according to the present invention. The benefits of bringing the oxygen content of the metal composition in accordance of the present invention within the limits prescribed for the anode composition as part of the process according to the present invention are described elsewhere in this document.

[0198] The applicants prefer to reduce the oxygen content of the metal composition according to the present invention by means of a process step known as “poling”. In a poling step, the molten liquid metal composition is contacted with a source of carbon. The carbon reacts with the oxygen in the metal composition and forms carbon oxides, CO+CO.sub.2, gasses that escape from the molten liquid metal composition and form a reducing atmosphere above the liquid metal bath. The carbon source may be any convenient carbon containing material, such as any hydrocarbon such as natural gas or a hydrocarbon liquid, carbon black, charcoal, coal, any organic material, including wood. The applicants prefer to use natural gas because of its convenience. Thanks to the operating conditions in which the composition is molten and liquid, it is easy to create an intensive contact and the carbon in the carbon source readily reacts with the oxygen in the composition to form carbon oxides (CO or carbon dioxide) which escape as a gas from the molten liquid metal composition, leaving the metal that was bound to the oxygen in its elemental form. The poling is preferably performed at a temperature of at least 1150° C., such that the molten liquid bath becomes highly fluid, and any slag is preferably first removed from the metal liquid bath. The off-gas from the poling step is preferably submitted to an afterburning step to convert the carbon monoxide into carbon dioxide before disposal. The applicants found that it is quite convenient to correctly dose the carbon source in order to bring the oxygen content down to within the range desirable for the anode composition as part of the process according to the present invention.

[0199] The molten liquid metal composition according to the present invention preferably further comprises, as part of the impurities, at least one and more preferably all of the following elements at a level which complies with the respective limit as specified for each element: [0200] at least 0.10% wt and/or at most 3.00% wt of antimony, [0201] at least 0.010% wt and/or at most 0.5% wt of bismuth, [0202] at most 6.00% wt of tin, [0203] at most 6.00% wt of lead, [0204] at least 0.0001% wt and at most 0.50% wt of silver, [0205] at least 0.005% wt and at most 0.40% wt of arsenic, [0206] at least 0.001% wt and at most 0.100% wt of sulphur, and [0207] at most 0.50% wt of zinc.

[0208] In an embodiment, the molten liquid metal composition according to the present invention comprises sulphur within the range as specified, preferably at least 0.005% wt, more preferably at least 0.010% wt and optionally at most 0.080% wt, preferably at most 0.070% wt, more preferably at most 0.060% wt.

[0209] The applicants have found that a limited amount of sulphur may be allowed in the molten liquid metal composition, and that it brings the advantage of widening the acceptance criteria for the feedstocks of the upstream process, which therefore is allowed to accept more sulphur in its raw materials. The applicants have also found that it is advantageous to maintain the sulphur in the molten liquid metal composition in compliance with the upper limit, because more sulphur increases the risk for more sulphur ending up as a cathode impurity, and also brings more sulphur in the anode slimes. The latter may be undesired if the anode slimes are to be further processed by means of a process that includes a pyrometallurgical step, because the sulphur in the anode slimes may then cause the generation of sulphur oxide gasses (SO.sub.2 and/or SO.sub.3).

EXAMPLE

[0210] The following example shows a preferred embodiment of the present invention. The example is further illustrated by the

[0211] Figure, which is showing a flow diagram of the core part of an embodiment of the process according to the present invention. In this process part are recovered, starting from the anode composition 1, a cathode product 6, an anode slime product 4, a bleed-off product 5 and a spent anode product 7.

[0212] In the Figure, the numbers represent the following claim features: [0213] 1. Anodes [0214] 2. Copper shots [0215] 3. Black acid [0216] 4. Anode slimes [0217] 5. Bleed-off [0218] 6. Cathodes [0219] 7. Spent anodes

[0220] An impure molten liquid copper-based metal composition further containing nickel, tin, lead and other minor metals was prepared in accordance with the process described in our co-pending patent application PCT/EP2018/084384, filed on 11 Dec. 2018. The composition is further detailed in Table I.

TABLE-US-00001 TABLE I Impure molten liquid metal composition % wt Cu 92.80 Ni 3.08 Sn 1.39 Pb 1.71 Sb 0.65 Ag 0.04 As 0.10 Bi 0.05 Fe 0.02 S 0.02 Zn 0.03 Oxygen 0.10 Total 99.99
The composition further contained about 5 ppm wt of gold (Au).

[0221] The impure molten liquid copper-based metal composition was introduced into a furnace, and brought at a temperature of about 1200° C. by burning natural gas into the furnace. Any remaining slag floating on the molten metal was poured off. Natural gas was injected into the liquid metal, until the oxygen content of the liquid metal had been reduced down to in the range of 20-170 ppm wt.

[0222] The liquid molten metal having the reduced oxygen content was then cast in thin, flat plates constituting the anodes 1 for the subsequent electrorefining operation, and allowed to cool to ambient temperature.

[0223] A total of 52 anodes having an average weight of 444 kg and 51 stainless steel plate starter sheets (blanks) were immersed in each of 100 electrolytic cells (200) containing an acidified copper sulphate solution at 68° C. which served as the electrolyte. The average electrolyte composition throughout the full electrolysis cycle is shown in Table II, in grams/litre for the major components and in ppm wt for the minor components.

TABLE-US-00002 TABLE II Average electrolyte composition grams/litre Cu 39.8 Ni 67.7 Sn 0.93 ppm wt Sb 344.7 As 63.1 Bi 9.0 Fe 403.1 Al 152.5 Cd 29.7

[0224] The sulphuric acid concentration was kept at an average concentration of 160 grams/litre by introducing concentrated sulphuric acid (96%), when and as needed, in the leaching vessel described further below. The following addition rates of process additives were maintained on average throughout the electrolysis cycle, by introducing them into the electrolyte inlet to the settlers (300): [0225] Gelatine at about 650 grams/ton of cathode copper produced, [0226] HCl in a 30% wt solution, at about 430 millilitre/ton of cathode copper produced, [0227] HBr in a 48% wt solution, at about 176 millilitre/ton of cathode copper produced, [0228] Flocculant ZETAG® type 7565, a cationic polyacrylamide, at about 1035 milligrams per ton of cathode copper produced, [0229] Thiourea at about 32 grams per ton of cathode copper produced

[0230] The average composition of the anodes (stream 1) is shown in Table III.

TABLE-US-00003 TABLE III Average anode composition % wt Anodes—1 Cu 92.90 Ni 3.08 Sn 1.39 Pb 1.71 Sb 0.65 Ag 0.04 As 0.10 Bi 0.05 Fe 0.02 S 0.02 Zn 0.03 Oxygen 0.02 Total 100.01
The anodes further contained about 5 ppm wt of gold (Au).

[0231] The anodes (stream 1) and stainless steel blanks were interleaved (spacing 120 mm) in an electrically parallel arrangement while the electrolytic cells themselves were connected in series. An average current density of 290 A/m.sup.2 was applied causing an average electrical potential between the anodes (positive electrodes) and the cathodes (negative electrodes) of 0.46V.

[0232] The passage of the electrical current causes copper to oxidize and go into solution via the electrochemical pathway. However, some copper will also go into solution by the purely chemical pathway. All elements (metals) present in the anodes and being under the given process conditions less noble than copper will also go into solution to a certain extent at the anodes. The electrochemically and chemically dissolved metals other than copper were continuously removed by means of bleed stream 5 of electrolyte. This bleed stream was subject to a further purification step (not shown) in which the metals were selectively removed and a purified electrolyte was left over. This prevents the impurities from building up in the electrolyte during electrorefining and prevents co-deposition of the impurities on the cathodes. The purified bleed-off, also called black acid, was recycled into the electrolyte circuit as stream 3. The average bleed-off composition as well as the average black acid composition are set forth in Table IV.

TABLE-US-00004 TABLE IV Average bleed-off and black acid composition Bleed-off Black acid % wt 5 3 Cu 3.32 0.0000 Ni 5.15 0.0930 Sn 0.02 0.0000 Pb 0.0013 0.0000 Sb 0.0001 0.0000 Ag 0.0001 0.0000 As 0.0014 0.0390 Bi 0.0000 0.0000 Au 0.0000 0.0000 Fe 0.03 0.0155 Pt 0.0000 0.0000 S 6.57 22.0501 Zn 0.03 0.0000

[0233] The copper which dissolved from the anodes flowed through the electrolyte solution towards the cathodes where the copper was plated onto the stainless steel starter sheets to produce copper cathodes. The electrolyte was fed at one head end of the cell. The cell wall having the overflow was a side wall perpendicular to the orientation of the electrodes. The flow of electrolyte was kept positive throughout the electrolytic cycle. An average refresh rate of approximately 55% cell volume per hour for each cell was used in combination with heated air sparging underneath the electrodes to prevent anode passivation. The incoming air was saturated with water vapour at a temperature close to that of the electrolyte before sparging through a gas diffuser and was introduced into each cell at an average pressure of 0.75 barg. All cells were regularly inspected during electrorefining to locate short-circuited anode/cathode pairs by using a Gauss meter mounted on the overhead crane. Short-circuits were repaired by respacing the offending anodes and cathodes or by removing nodules of electrodeposited copper which may had grown between the short-circuited anode/cathode pairs. The proper control of all these parameters resulted in high quality cathodes. The average cathode composition (stream 6) is given in Table V. The cathode deposits obtained during electrorefining were brightened and smoothed by continuously adding the organic addition agents gelatine and thiourea (stream 8) to the electrolyte just upstream of the pumping system to ensure good mixing.

TABLE-US-00005 TABLE V Average cathode composition Cathodes % wt 6 Cu 99.9761 Ni 0.0025 Sn 0.0069 Pb 0.0020 Sb 0.0029 Ag 0.0063 As 0.0007 Bi 0.0001 Au 0.0000 Fe 0.0002 Pt 0.0000 S 0.0016 Zn 0.0001 Total 99.9994

[0234] Gold and the platinum group metals did not dissolve in the sulphate electrolyte and hence they did not enter the electrolyte or plate at the cathode as can be seen in Table II and Table V. Silver dissolved from the anodes to some extent but was made to precipitate from the electrolyte as AgCl and AgBr by adding small amounts of HCl and HBr to the electrolyte (stream 8). The appearance of silver in the cathode is believed to be primarily due to the occlusion of a small quantity of anode residues.

[0235] Lead and tin were forming compounds which are insoluble in the electrolyte and hence these metals hardly entered the electrolyte. The majority of the insoluble impurities from the anodes collected as undissolved slimes at the bottom of the electrolytic cells. These slimes were periodically removed from the cells (400) during the electrorefining operation by a suction head moving over the bottom section of the cell which was provided below the electrodes. Some insoluble impurities were lighter and were leaving the cells via the cell overflows to the settlers (300). Also these lighter slimes were periodically removed from the bottom of the settlers (400), once the slimes had sufficient time to settle down after adding flocculant to the electrolyte on its way to the settler. This way, all anode slimes were collected in a combined stream of electrolyte containing anode slimes and were further processed by a filter press (500) which separated the anode slimes (stream 4) from the clear electrolyte. Part of this clear electrolyte was recycled to the circulation tanks (100). Another part of this clear electrolyte was removed as a bleed stream (stream 5) to remove impurities such as copper and nickel by electrowinning that otherwise would build up in the electrolyte. The anode slimes were washed with heated water at 70° C. to reduce the amounts of copper and nickel that were present as dissolved in the electrolyte. The washing water was recycled to the electrorefining process. The average anode slime composition (stream 4) is given in Table VI. The balance of the composition is probably oxygen and some carbon, most likely from the organic process additives.

TABLE-US-00006 TABLE VI Average anode slimes composition % wt Anode Slimes—4 Cu 5.40 Ni 1.87 Sn 17.17 Pb 21.21 Sb 8.05 Ag 0.43 As 1.29 Bi 0.62 Fe 0.07 S 6.98 Zn 0.12
The anode slimes were further found to contain about 60 ppm wt of gold and about 5 ppm wt of platinum.

[0236] To compensate for the electrochemically dissolving impurities at the anodes, which would otherwise cause a depletion of copper in the electrolyte, copper containing hollow and open nuggets (stream 2) obtained from an upstream process step were leached (600) in a leaching vessel by contacting the copper containing nuggets with the concentrated sulphuric acid used for make-up, the black acid stream returned from the bleed stream processing, as well as with a part of the electrolyte. The liquid product from the leaching vessel was recycled into the electrolyte circuit during the electrorefining process. The average composition of the nuggets used (stream 2) is set forth in Table VII. The dissolution of the copper nuggets was assisted by introducing oxygen gas at the bottom of the leaching vessel.

TABLE-US-00007 TABLE VII Average copper nuggets composition Copper nuggets % wt 2 Cu 95.75 Ni 1.63 Sn 0.98 Pb 1.13 Sb 0.31 Ag 0.03 As 0.03 Bi 0.03 Fe 0.01 S 0.02 Zn 0.09

[0237] The content of gold and platinum in the copper nuggets was less than 1 ppm wt.

[0238] At the end of an anode cycle, each anode had been dissolved for about 75%. The undissolved remains of the anodes (anode scrap) were removed as spent anodes (stream 7) from the electrolytic cells and after washing, weighing and stacking they were melted and recast as fresh anodes. The average composition of the spent anodes was obviously the same as the average anode composition as shown in Table Ill.

[0239] The above process allowed to operate in standard electrolysis cycles of 24 days per cell, i.e. a period of 24 days of continuous operation between the introduction of a new set of anodes. The cathodes were pulled after about every 8 days, and they were replaced ⅓ at the time, while the electrolysis was continued, and at full current density. The anode slimes were removed from the bottom of the cells, at a frequency as needed that could vary from once every 3 days to once every 10 days, and this also while the electrolysis was continued at full current density.

[0240] Having now fully described this invention, it will be appreciated by those skilled in the art that the invention can be performed within a wide range of parameters within what is claimed, without departing from the scope of the invention, as defined by the claims.