Surface modification using abrasive blasting

Abstract

A method for the manufacture of a component comprises the following steps, in sequence using an additive layer manufacturing process to build a three-dimensional net shape of the component; performing a first abrasive blasting operation on a region of a surface of the component; and performing a second abrasive blasting operation on the region. The angle of incidence of the abrasive on the surface in the first abrasive blasting operation is less than the angle of incidence of the abrasive on the surface in the second abrasive blasting operation.

Claims

1. A method for the manufacture of a component, the method comprising, in sequence: a. using an additive layer manufacturing process to build a three-dimensional net shape of the component; b. performing a first abrasive blasting operation on a region of a surface of the component; and c. performing a second abrasive blasting operation on the region thereby removing a minimal amount of material from the component, the minimal amount of material being less than an amount of material removed by the first abrasive blasting operation; wherein an angle of incidence of the abrasive on the surface in the first abrasive blasting operation is between 30 and 60 degrees, and wherein an angle of incidence of the abrasive on the surface in the second abrasive blasting operation is between 60 and 90 degrees.

2. The method of claim 1, in which the first abrasive blasting operation acts to remove asperities from the region.

3. The method of claim 2, in which the asperities comprise semi-sintered particles adhered to the surface.

4. The method of claim 1, in which the first abrasive blasting operation acts to remove material carrying residual tensile stress from the region.

5. The method of claim 1, in which the second abrasive blasting operation acts to impart compressive stress into the region.

6. The method of claim 1, in which the region is an entire surface of the component.

7. The method of claim 1, in which the first and second abrasive blasting operations are performed using the same apparatus and nozzles, and the same abrasive material.

8. The method of claim 1, in which the angle of incidence of the abrasive on the surface region in the second abrasive blasting operation is between 75 and 90 degrees.

Description

DESCRIPTION OF THE DRAWINGS

(1) Embodiments will now be described by way of example only, with reference to the Figures, in which:

(2) FIG. 1 is a sectional side view of a gas turbine engine which may comprise components made in accordance with the method of the invention;

(3) FIG. 2 shows schematically an additive layer manufacturing method known to be used in prior art manufacturing;

(4) FIG. 3 is a flow chart illustrating the steps in a method in accordance with one embodiment of the invention; and

(5) FIG. 4 shows schematically (a) the as-manufactured surface of the component made in accordance with FIG. 3; (b) the effect of the first blasting operation of FIG. 3; and (c) the effect of the second blasting operation of FIG. 3.

DETAILED DESCRIPTION

(6) With reference to FIG. 1, a gas turbine engine is generally indicated at 10, having a principal and rotational axis 11. The engine 10 comprises, in axial flow series, an air intake 12, a propulsive fan 13, an intermediate pressure compressor 14, a high-pressure compressor 15, combustion equipment 16, a high-pressure turbine 17, and intermediate pressure turbine 18, a low-pressure turbine 19 and an exhaust nozzle 20. A nacelle 21 generally surrounds the engine 10 and defines both the intake 12 and the exhaust nozzle 20.

(7) The gas turbine engine 10 works in the conventional manner so that air entering the intake 12 is accelerated by the fan 13 to produce two air flows: a first air flow into the intermediate pressure compressor 14 and a second air flow which passes through a bypass duct 22 to provide propulsive thrust. The intermediate pressure compressor 14 compresses the air flow directed into it before delivering that air to the high pressure compressor 15 where further compression takes place.

(8) The compressed air exhausted from the high-pressure compressor 15 is directed into the combustion equipment 16 where it is mixed with fuel and the mixture combusted. The resultant hot combustion products then expand through, and thereby drive the high, intermediate and low-pressure turbines 17, 18, 19 before being exhausted through the nozzle 20 to provide additional propulsive thrust. The high 17, intermediate 18 and low 19 pressure turbines drive respectively the high pressure compressor 15, intermediate pressure compressor 14 and fan 13, each by suitable interconnecting shaft.

(9) Other gas turbine engines to which the present disclosure may be applied may have alternative configurations. By way of example such engines may have an alternative number of interconnecting shafts (e.g. two) and/or an alternative number of compressors and/or turbines. Further the engine may comprise a gearbox provided in the drive train from a turbine to a compressor and/or fan.

(10) Many components of the gas turbine engine could be manufactured by the method of the invention. For example (but without limitation), components in the turbine sections 17, 18 and 19, or the combustor 16 may be manufactured in accordance with the invention. The method is well suited to the manufacture of components with non-linear geometries.

(11) FIG. 2 has been discussed above.

(12) FIG. 3 is a flowchart illustrating a method for the manufacture of a component in accordance with one embodiment of the invention.

(13) In the first step shown in the flowchart, the net shape of the component to be produced is defined in known manner and loaded into the ALM system.

(14) In the second step shown in the flowchart, the component is manufactured by ALM in accordance with the definition. As described above, the as-manufactured component has a relatively rough surface finish, illustrated schematically in FIG. 4(a). The surface 40 of the component has numerous asperities 42, in particular caused by random semi-sintered particles adhering to the component surface. As a consequence of the manufacturing process, there may also be material close to the surface 40 carrying residual tensile stress which is undesirable.

(15) In the third step shown in the flowchart, a first blasting operation is performed. As illustrated in FIG. 4(b), a nozzle 44 of a blasting apparatus (not shown) has an angle of incidence of 45 degrees to the surface 40 of the component. The blasting apparatus is configured to traverse the nozzle 44 in the direction of the arrow V at a predetermined traverse speed. The nozzle delivers a jet of abrasive 46 towards the surface 40, also at an angle of 45 degrees to the surface 40.

(16) The angle of delivery of the abrasive 46 causes it to remove material from the surface 40, in particular to remove random semi-sintered particles and material carrying residual tensile stress. The portion 48 of the surface that has been treated by the first blasting operation therefore has a smoother and more homogenous surface finish than the untreated surface 40. It is anticipated that acceptable material removal will be obtained with nozzle angles of incidence between 10 and 75 degrees. Preferably, the nozzle angle of incidence will be between 30 and 75 degrees. More preferably, the nozzle angle of incidence will be between 45 and 60 degrees.

(17) In the fourth step shown in the flowchart, a second blasting operation is performed. As illustrated in FIG. 4(c), a nozzle 54 of a blasting apparatus (not shown) has an angle of incidence of 90 degrees to the surface 40 of the component (i.e. perpendicular to the surface 40). The blasting apparatus is configured to traverse the nozzle 54 in the direction of the arrow VV at a predetermined traverse speed, which may be the same as or different from the traverse speed in the previous step. The nozzle delivers a jet of abrasive 56 towards the surface 40, also at an angle of 90 degrees to the surface 40.

(18) The angle of delivery of the abrasive 56 causes it to impart a compressive stress into the surface region 58 of the component, without causing significant material removal. The magnitude of the compressive stress is proportional to v.sin θ, where v is the speed of the abrasive within the jet and θ is its angle of incidence. It is anticipated that an angle of incidence between 60 degrees and 90 degrees will be suitable for this blasting operation. Preferably, the angle of incidence will be between 75 and 90 degrees.

(19) Preferably, the nozzle is movable so that its angle of incidence can be changed. This allows the blasting apparatus of FIGS. 4(b) and 4(c) to be the same apparatus, and the nozzles 44 and 54 to be the same nozzle. It also allows the nozzle angle to be changed dynamically as the nozzle is traversed over the surface of the component, to ensure that the angle of incidence of the nozzle—relative to the component surface—can be kept constant throughout each of the first and second blasting operations, so that the whole surface of the component can be treated. In this way, the whole surface of the component can first be homogenised, and then be provided with a uniform compressive stress; thereby minimising the chance of any cracking during a subsequent HIP process.

(20) By using two abrasive blasting operations, and particularly by using the same apparatus and abrasive for both operations, the surface finish of the component can be improved and a compressive stress imparted into its surface in a simpler manner than by known methods. The need for a separate and costly machining step is removed. Furthermore, the method of this disclosure is more suitable for complex geometries of the type facilitated by ALM techniques.

(21) Any suitable blasting medium may be used; for example, but not limited to, ceramic, glass, metal.

(22) It will be understood that the invention is not limited to the embodiments above-described and various modifications and improvements can be made without departing from the concepts described herein. Except where mutually exclusive, any of the features may be employed separately or in combination with any other features and the disclosure extends to and includes all combinations and sub-combinations of one or more features described herein.