Method for applying a reinforcement of metal material to a component of metal material, particularly in the construction of a motor-vehicle body or a sub-assembly thereof

Abstract

A structural joint between two components of metal material is obtained by carrying out an electrical resistance welding spot between said components and subsequently performing a step of applying a cladding of metal material by an additive manufacturing technology. In one example, after a first step of applying a coarse base cladding, a second step of applying a fine cladding is carried out, again by additive manufacturing technology. The fine cladding can include a distribution of stiffening micro-ribs above the base cladding. The same method can also be applied to a single sheet metal component, rather than to a welded joint.

Claims

1. A method for applying a reinforcement of metal material to a component of metal material, said method comprising: applying a reinforcement cladding of metal material above said component using additive manufacturing technology, which includes a first step of applying a coarse base cladding and a second step of applying a fine cladding including a distribution of stiffening micro-ribs above the base cladding.

2. The method according to claim 1, wherein applying the reinforcement cladding of metal material above said component using additive manufacturing technology comprises a third, final step of local application of a zinc overlay.

3. The method according to claim 1, further comprising a local quenching step obtained by feeding a cold fluid above said cladding immediately after applying said cladding.

4. The method according to claim 1, wherein said reinforcement cladding is applied on said component before subjecting the component to a forming step in a mold.

5. The method according to claim 1, wherein the first step of applying the course base cladding includes applying a first coarse metal cladding above said component, defining reinforcing metal portions spaced apart from each other, the method further comprising applying a support layer between said reinforcing metal portions, the support layer being of a lighter material than the course base cladding, and wherein the second step of applying the fine cladding includes one or more subsequent steps of applying one or more additional levels of fine and/or superfine cladding, above said reinforcing portions and said support layer.

6. The method according to claim 1, wherein said coarse base cladding has a height on the order of millimeters, said fine cladding has a height on the order of microns and wherein above said fine cladding, at least one additional super-fine cladding is applied with a thickness on the order of tenths of a micron, each cladding being formed by one or more layers applied by an additive manufacturing technology.

7. A motor-vehicle component, obtained by the method according to claim 1.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0022] Further characteristics and advantages of the invention will become apparent from the description that follows with reference to the attached drawings, provided purely by way of non-limiting example, wherein:

[0023] FIG. 1 is a schematic cross-sectional view of a welded joint of two metal sheet elements, after a first step of an embodiment of the method according to the invention,

[0024] FIG. 2 is a schematic cross-sectional view of the same welded joint of FIG. 1, after a second step of the method according to the invention,

[0025] FIG. 3 is a partial perspective view of a superstructure made in the method according to the invention by additive manufacturing technology,

[0026] FIG. 4 illustrates a variant of FIG. 3,

[0027] FIG. 5 shows a cross-sectional view of a single cell forming part of the structure of FIG. 4,

[0028] FIG. 6 is a perspective view of a seashell,

[0029] FIGS. 7 and 8 are perspective views of tools usable in the method according to the invention,

[0030] FIG. 9 is a schematic plan view of the layout of a production line for motor-vehicles, which makes use of the method according to the invention,

[0031] FIG. 10 is a schematic cross-sectional view of a reinforcement applied above a metal sheet component by means of the method according to the invention,

[0032] FIGS. 11, 12 show two steps of the method of forming a metal sheet component provided with a reinforcement obtained using the method according to the invention, and

[0033] FIGS. 13-16 show another embodiment example of the method according to the invention.

DETAILED DESCRIPTION OF THE INVENTION

[0034] In FIG. 1, the reference number 1 indicates—in its entirety—a structural joint of two steel sheet components after a first step of the method according to a first embodiment of the invention. Two steel sheet components 2, 3 have respective flanges 2A, 3A rigidly connected to each other by an electrical resistance welding spot W obtained by using a conventional electrical resistance welding head (not illustrated), including two electrodes that are pressed from opposite sides against the two flanges 2A, 3A so as to exert a pressure and simultaneously create a flow of electric current through these flanges to produce local fusion of the metal in their contact zone.

[0035] According to a first aspect of the invention, above the welded joint of the two flanges 2A, 3A, a coarse base 4 cladding is applied by additive manufacturing technology.

[0036] FIG. 7 of the attached drawings shows, by way of example, a device 5 for additive manufacturing, comprising a head 6 arranged at the end of a flexible tube 7 of elastomeric material, inside which a duct 8 for the addition of metal powders, an optical guide 9 for transmitting a laser beam and a duct 10 for feeding zinc powder are arranged.

[0037] According to a technique known per se, the device 5 feeds metal powders through the duct 8, which are immediately melted above the sheet metal components 2, 3 by means of the laser beam transmitted by the optical guide 9, so as to form, layer by layer, the coarse cladding base 4 having the required configuration.

[0038] In another embodiment, the powder can be replaced by wire. In this case, one or more coils of metal wire (or of polymeric material in the multi-material version) are provided, of various diameters (from 1 millimeter to 10 microns) and different chemical composition, for the possible production of cladding at multiple finishing levels (from 1 to n levels).

[0039] According to this embodiment of the method of the invention, once the base cladding 4 is applied, the device 5 is used to apply a further overlay of fine cladding 11, including a distribution of stiffening micro-ribs above the base cladding 4.

[0040] FIG. 3 shows a first example of a fine cladding structure having a plurality of micro-ribs 12 defining a general irregular honeycomb pattern, including a plurality of cells 13. In the example of FIG. 3, the pattern has a two-dimensional configuration, in the sense that the micro-ribs 12 have a cross-section with a uniform shape and dimensions along their height.

[0041] FIG. 4 illustrates a variant of FIG. 3, in which the walls 12 have a cross-section with variable shape and dimensions along the height, according to the example illustrated, on an enlarged scale, in FIG. 5.

[0042] The Applicant has drawn inspiration for the design of the fine overlay 11 from the existence in nature of shell structures of the type illustrated in FIG. 6, which are characterized by an ideal combination of structural strength and lightness.

[0043] Thanks to the characteristics described above, the welded joint W completed at least with the coarse base cladding 4, and preferably with the fine cladding 11 as well, becomes a “structural” junction that is able to constitute a part that provides a significant contribution to the structural strength of the entire assembly.

[0044] A possible disadvantage of the method described above, which has been identified by the Applicant, is that the heat applied during the additive manufacturing step to the metal sheet structure can locally destroy an outer layer of zinc of which the sheet metal components 2, 3 can be provided with, and may furthermore jeopardize the advantages of structural strength of the sheets 2, 3 obtained by means of a quenching method to which said components have been previously subjected.

[0045] To overcome these drawbacks, the device 5 can include the duct 10 that has been mentioned above, for the addition of zinc powders, which are also applied with the additive manufacturing technique above the components, in order to restore the zinc coating above the joint coated with the layers 4 and/or 11. Furthermore, it is also possible to provide a device 5 of the type illustrated in FIG. 8 mounted, for example, on the wrist of a manipulator robot 14 (only partially visible in FIG. 8) and, in addition to the head 6 that has been described with reference to FIG. 7, it is also provided with a nozzle 15 for the addition of a cold fluid (for example nitrogen or argon) over the components 2, 3 in order to cause abrupt cooling of the components after the heating generated in the additive manufacturing step, so as to obtain local quenching of the metal components.

[0046] The method according to the invention allows the manufacturing of motor-vehicle structures, in particular the framing of motor-vehicle “bodies-in-white” with a lower number of electrical resistance welding spots, compared to conventional methods.

[0047] For example, with reference to FIG. 9, a motor-vehicle production plant can provide a line 16 on which the structures to be assembled proceed, for example conveyed on vehicles of the automated-guided type 18. Along the line 16, the vehicles 18 encounter a framing station F comprising locking devices of any known type (not illustrated) for locking the parts constituting the structures to be welded in a precise assembly position, and one or more welding robots 19 equipped with electrical resistance welding heads to perform a plurality of electrical welding spots on the structure carried by the vehicle 18. The framing station F may also comprise a plurality of robots 20 carrying devices 5 of the type described above with reference to FIG. 7, in order to apply, over the welded joints, a coarse layer of cladding, by means of additive manufacturing technology, according to the expedients that have been described above.

[0048] After leaving the framing station F, the welded structure transfers to a completion station S, in which additional robots 21 execute the application of the additional layer of fine cladding, again by means of additive manufacturing technology. These robots can also perform the restoration step of an outer zinc layer above the welded joint and carry out local quenching, according to the method described above, in order to restore the resistance characteristics of the sheet metal structures.

[0049] FIG. 10 shows a cross-section of a steel sheet component 22 on which a layer of coarse base cladding 23 and an overlap of fine cladding 24 have been applied, both with additive manufacturing technology, similar to that been described above with reference to the welded joint of FIGS. 1, 2.

[0050] If the metal sheet component 22 is a shaped component, it can be envisaged that the layers of cladding 23, 24 are applied after forming the sheet metal element, but a particularly interesting embodiment of the invention is where formation of the sheet metal component in a mold is carried out after applying the reinforcing element constituted by the base layer 23 and by the overlap 24, which preferably has a configuration of the type that has been described above with reference to FIG. 3 or to FIG. 4.

[0051] A variant of this embodiment is illustrated in FIGS. 11 and 12. These Figures show formation of a sheet metal component 22 in a mold having an upper mold 25 and a lower mold 26. In the case illustrated in FIGS. 11 and 12, before formation in the mold, a reinforcing element 23 is applied above the sheet metal 22 by means of additive manufacturing technology. Subsequently to the application of the reinforcement 23, the structure thus obtained is formed in the mold, by closing the two half-molds 25, 26 in such a way that the reinforcement 23 is incorporated into the thickness of the sheet 22.

[0052] FIGS. 13-16 show the subsequent steps of a further embodiment of the method according to the invention which produces multi-level and multi-material cladding.

[0053] FIG. 13 shows a first step of applying a first coarse metal cladding over the component 22, defining reinforcing metal portions 23 spaced apart from each other. FIG. 14 shows a second step of application between the reinforcing metal portions 23 of a support layer 27, of a lighter material, chosen for example from plastics, light metal alloys and ceramic materials. FIG. 15 shows a subsequent step of applying another level of fine cladding 28, and FIG. 16 shows the application of a superfine final cladding, to create layers 29 above the support layer 28.

[0054] As is evident from the above, the method according to the invention provides—in its preferred embodiment—a multi-level cladding, in which each level is created with successive layers, by means of additive manufacturing. The levels may all be of metal material or may be made of different materials and also comprise levels of synthetic material or ceramic material. Preferably, in addition, the various levels have a progressively smaller dimension in height, starting from the base level, which can be a coarse cladding, with a height in the order of millimeters (that is, between 0.1 mm and 10 mm), towards the progressively finer upper levels, which may have a thickness in the micron range (between 1 micron and 200 microns) and then in the order of 10ths of microns (between 0.1 micron and 1 micron) or even less.

[0055] As is clear from the above description, the method according to the invention opens the way to a series of improvements in the production process of motor-vehicles, above all, in terms of an ideal combination of strength and lightness of the obtained structure. Moreover, as is evident from what has been described, the method according to the invention is easily applicable and adaptable to the production plants currently in use, without high costs.

[0056] Of course, without prejudice to the principle of the invention, the embodiments and the details of construction may vary widely with respect to those described and illustrated purely by way of example, without departing from the scope of the present invention.