METHOD OF MANUFACTURING A PHOTOLUMINESCENT ELEMENT

Abstract

A method of manufacturing a photoluminescent element (1), wherein a thick, 1000-1500 kg/m3 density transparent layer (11) is applied onto a plate (2) or into at least one mold (3) at an ambient temperature of 15-55° C. and allowed to dry for 10 minutes to 8 hours, followed by applying a thin, 100-200 mPa.Math.s viscosity transparent layer (12). Further, a photoluminescent powder (131) is immediately applied and allowed to fall by its gravity only through the thin transparent layer (12) to adhere at the interface of both the transparent layers (11, 12) and, therefore, to form a continuous photoluminescent layer (13). All the achieved layers (11, 12, 13) are finally hardened together.

Claims

1. A method of manufacturing a photoluminescent element comprising: (a) applying a thick transparent layer having a density of 1 to 1.5 t/m.sup.3 at an ambient temperature of 15-55° C. onto a plate or into at least one mold; (b) drying the thick transparent layer for 10 minutes to 8 hours; (c) applying a thin transparent layer having a viscosity from 100 to 200 cPs; and (d) applying a photoluminescent powder to the thin transparent layer, wherein the photoluminescent powder falls by gravity through the thin transparent layer and adheres at an interface of the thick transparent layer and the thin transparent layer thereby forming a continuous photoluminescent layer and hardening the thick transparent layer, the thin transparent layer, and the photoluminescent layer.

2. The method of manufacturing the photoluminescent element according to claim 1, characterized in that the thick transparent layer is applied in the way that it is shaped on its profile in order to increase the surface area of the thick transparent layer.

3. The method of manufacturing the photoluminescent element according to claim 1, characterized in that a shaped bottom of the plate or the mold is shaped into multi-sided pyramids, wherein the thick transparent layer copies the shaped bottom of the plate or the mold.

4. The method of manufacturing the photoluminescent element according to claim 3, characterized in that the shaped bottom of the plate or the mold is pyramid-shaped, wherein the pyramid height is from 0.2 to 15 mm and the wall angle is from 15° up to 75°.

5. The method of manufacturing the photoluminescent element according to claim 3, characterized in that the photoluminescent element is removed from the plate, turned around and placed on a flat-bottomed plate and a shaped surface is filled with a levelling transparent layer.

6. The method of manufacturing the photoluminescent element according to claim 5, characterized in that the plate and/or the flat-bottom plate are provided with a frame, wherein the frame is about 1% to 10% larger in shape than the photoluminescent element to allow the levelling transparent layer to flow around the side surfaces of the photoluminescent element.

7. The method of manufacturing the photoluminescent element according to claim 3, characterized in that the photoluminescent element is removed from the mold, turned around and inserted into a flat-bottomed mold and a surface is filled with a levelling transparent layer.

8. The method of manufacturing the photoluminescent element according to claim 7, characterized in that the mold is about 1% to 10% larger in shape than the photoluminescent element to allow the levelling transparent layer to flow around the side surfaces of the photoluminescent element.

9. The method of manufacturing the photoluminescent element according to claim 1, characterized in that the thick transparent layer is applied by a method of 3D printing.

10. The method of manufacturing the photoluminescent element according to claim 1, characterized in that into the thick transparent layer a pressure is made by pressuring means, wherein the pressuring means is shaped.

11. The method of manufacturing the photoluminescent element according to claim 10, characterized in that the pressing means comprises a pressing surface, wherein the pressing surface of the pressing means is arranged in the shape of multi-sided pyramids.

12. The method of manufacturing the photoluminescent element according to claim 1, characterized in that the thin transparent layer overlaps the thick transparent layer on top of the thick transparent layer by about 0.1 to 20 mm.

13. The method of manufacturing the photoluminescent element according to claim 1, characterized in that the bottom of the plate is arranged as smooth.

14. The method of manufacturing the photoluminescent element according to claim 12, characterized in that the plate is provided with an additional layer to ensure an easy removal of the plate from the of photoluminescent element.

15. The method of manufacturing the photoluminescent element according to claim 1, characterized in that the mold is provided with a secondary layer to ensure easy removal of the photoluminescent element.

16. The method of manufacturing the photoluminescent element according to claim 15, characterized in that the secondary layer is formed as a poly-film.

17. The method of manufacturing the photoluminescent element according to claim 1, characterized in that a white cover layer is applied onto the thick transparent layer, the thin transparent layer, and the photoluminescent layer after the hardening, wherein the thick transparent layer, the thin transparent layer, and the photoluminescent layer are hardened together.

18. The method of manufacturing the photoluminescent element according to claim 17, characterized in that the thickness of the white cover layer is from 0.1 to 10 mm.

19. The method of manufacturing the photoluminescent element according to claim 1, characterized in that the photoluminescent powder is applied on the thin transparent layer with a sieve.

20. The method of manufacturing the photoluminescent element according to claim 17, characterized in that the thin transparent layer and/or the white cover layer are provided with glass or carbon fibers to provide strengthening.

Description

DESCRIPTION OF THE DRAWINGS

[0027] FIG. 1 shows the applying of a photoluminescent powder (131) to a thin transparent layer (12) which the photoluminescent powder (131) falls through and adheres to the interface with the thick transparent layer (11) and creates a photoluminescent layer (13), as seen in FIG. 2, wherein the plate (2) is provided with a layer (21) to provide easy removal.

[0028] FIGS. 3 and 4 describes the applying of photoluminescent powder (131) and forming a photoluminescent layer (13) when applied in the mold (3), wherein the mold (3) is provided with a layer (31) to provide easy removal.

[0029] FIG. 5 shows in sectional view applying of the shaped thick transparent layer (11) on the plate (2) in such way that on the profile there is a thick transparent layer (11) spatially arranged, preferably in the shape of pyramids.

[0030] FIG. 6 is a view of the plate (2) with a shaped bottom and a applying of photoluminescent powder (131) to a thin transparent layer (12) which the photoluminescent powder (131) falls through and adheres to the interface with the thick transparent layer (11), and forms a shaped photoluminescent layer (13), as shown in FIG. 7. Here is also shown a white cover layer (14) containing glass fibers (15).

[0031] FIG. 8 in sectional view shows the plate (2′) with a put folded photoluminescent element (1), where the shaped surface of the thick transparent layer (11) is re-filled with a levelling transparent layer (16). Furthermore, there is shown a method of rolling a film (6) to provide a glossy surface into a photoluminescent element (1).

[0032] FIG. 9 shows the mold (3) with a shaped bottom and a applying of photoluminescent powder (131) to a thin transparent layer (12) which the photoluminescent powder (131) falls through and adheres to the interface with the thick transparent layer (11), and forms a spatially shaped photoluminescent layer (13). There is also displayed a white cover layer (14) containing glass fibers (15).

[0033] FIG. 10 in sectional view shows the mold (3′) with a put folded photoluminescent element (1) wherein the spatially shaped surface of the thick transparent layer (11) is re-filled with a levelling transparent layer (16). Furthermore, there is shown a method of rolling a film (6) to provide a glossy surface into a photoluminescent element (1).

[0034] FIG. 11 shows the embodiment of the pressure by the pressuring means (5) into the thick transparent layer (11), whereby a spatially shaped surface is formed.

EXAMPLE OF AN EMBODIMENT OF THE INVENTION

Example 1

[0035] Method of manufacturing a photoluminescent element 1 according to the present invention consists in the fact that at temperatures in the range from 15 to 55° C., preferably at about room temperature in the range from 20 to 23° C., on the plate 2, for example a plate of hard plastic or glass, there is applied a thin layer 21 to ensure easy removal of the plate, preferably the layer is formed by pouring or spraying hot liquid wax, which is spread over the surface and solidifies at ambient temperature. On thus prepared surface a thick transparent layer 11 is applied, the density of which is 1-1.5 t/m.sup.3, for example 1.1 t/m.sup.3, and this layer is spread over the prepared base plate 2.

[0036] The transparent layer 11 is in a preferred embodiment a binder resin or a mixture thereof or a polyurethane mixture which is transparent. It is possible to use a matt resin, for example a polyester resin, or a glossy one, for example natural mixtures. In the most preferred embodiment, the thick transparent layer 11 is colourless and water-repellent. The thick transparent layer 11 is poured onto the plate 2, in the most preferred embodiment the pouring is performed by means of an automatic robot. The layer 11 thus prepared is left at said temperature for 150 minutes, and the surface of this layer 11 becomes cloudy in said time. The thickness of the thick transparent layer 11 is in the range 0, 1 to 20 mm, preferably 0.8 mm. On the thick transparent layer 11 a thin transparent layer 12 is poured, a viscosity of which is 100 to 200 cP.Math.s, for example 130 cP.Math.s, and to a thin transparent layer 12 a photoluminescent powder 131 is immediately applied, which falls by gravity through this thin transparent layer 12 and adheres to the interface of the transparent layers 11 and 12, thereby forming a continuous photoluminescent layer 13. The thickness of layer 12 is in the range 0, 1 to 20 mm, in a most preferred embodiment the thickness is 2 mm.

[0037] Photoluminescent powder 131 is introduced as a metal oxide, in a preferred embodiment the oxide Al.sub.2O.sub.3 (corundum)+Strontium+Europium+Dysprosium+Cobalt where the individual elements sinter together at temperatures above 1 000° C. and the resulting ingot is then crushed and ground into a powder of different grain sizes, so as to maintain the maximum luminance of the photoluminescent powder 131. In the most preferred embodiment, a photoluminescent powder 131 with the largest possible grain size is used, since the degree of luminance is directly proportional to the grain-crystal size. The grain size—crystals size—is from 50 μm to 650 μm, in the case of using blue luminous crystals the grain size is preferably around 50 μm, in the case of yellow-green luminous crystals the grain size is preferably from 150-200 μm.

[0038] The photoluminescent powder 131, containing large crystals, is applied with a spatula—spread on the surface of the thin transparent layer 12, in a preferred embodiment it is applied automatically by screen printing, where the speed of movement of the knife is constant. The thickness of the photoluminescence layer 13 depends on the size of the crystals and their eventual overlap, this layer 13 is preferably formed by crystals fixed side by side without overlapping. The coverage of the surface of the thick transparent layer 11 with the photoluminescent layer 13 is 70 to 100%.

[0039] Thus prepared layers 11, 12 and 13 are hardened together in order to assemble a photoluminescent element 1. Hardening is preferably carried out at temperatures of 25-55° C. at time 10 hours to 3 hours, according to the particular used material of transparent layers.

[0040] In a preferred embodiment on the hardened layer 12 a white cover layer 14 is applied, in order to increase luminance. The layers 11, 12 and 13, 14 are hardened together again by the method of the used material. The white cover layer 14 is preferably introduced as a natural or synthetic resin containing, for example, titanium dioxide. The thickness of the white cover layer 14 is 0.05-0.5 mm, most preferably 0.1 to 0.2 mm. In a preferred embodiment, the white cover layer 14 is provided with glass or carbon fibers 15 to provide strengthening.

[0041] Photoluminescent element 1 in form of a plate, manufactured as mentioned above, is ready for further processing, in the preferred embodiment, due to chip machining or water jet cutting or other dividing manufactured desired shapes, e.g., round, square or triangular elements, letters, numerals, etc.

Example 2

[0042] Method of manufacturing a photoluminescent element 1 according to the present invention consists in the fact that at a temperature, preferably at room temperature ranged between 20-23° C., a thick transparent layer 11 is applied into the mold 3, for example into the mold of hardened plastic. The shape of the mold is molded according to the requirements of the particular shape, for example the mold 3 has a circular shape of defined dimension or oval, however the shape of the mold 3 can be of any shape. Most preferably, it is a system comprising several juxtaposed molds. In a preferred embodiment this mold 3 is provided with a thin polyurethane film 31 to ensure easy removal of the photoluminescent element 1 from the mold 3, wherein the mold 3 and the polyurethane film 31 form one unit together. For example, a wax may be used as the layer 31 to ensure easy removal of the photoluminescent element 1 from the mold 3.

[0043] On the thus prepared surface in the mold 3 a thick transparent layer 11 is applied, the density of which is 1-1.5 t/m.sup.3, for example 1, 1 t/m.sup.3, and this layer is spread over the prepared base surface of the mold 3. The thick transparent layer 11 is in a preferred embodiment a binder resin or a mixture thereof or a polyurethane mixture which is transparent. It is possible to use a matt resin, for example a polyester resin, or a glossy, for example natural mixtures. In the most preferred embodiment, the thick transparent layer 11 is colourless and water-repellent. The thick transparent layer 11 is poured onto the mold 3, in the most preferred embodiment the pouring is performed by means of an automatic robot. The thus prepared layer 11 is left at this temperature for 130 minutes, and the surface of the layer 11 becomes cloudy over said time.

[0044] The thickness of thick transparent layer 11 is in the range of 0.1 to 20 mm, preferably 0.8 mm. On the thick transparent layer 11 there is poured a thin transparent layer 12, a viscosity of which is 100 to 200 cP.Math.s, for example 110 cP.Math.s, and on this layer 12 is immediately applied a photoluminescent powder 131, which falls by gravity through this thin transparent layer 12 and adheres to the interface of the transparent layers 11 and 12, thereby forming a continuous photoluminescent layer 13. The thickness of the thin transparent layer 12 is in the range of 0, 1 to 20 mm, in a most preferred embodiment, the thickness is of 2 mm. The photoluminescent powder 131 is presented as a metal oxide, according to Example 1. The thickness of the photoluminescence layer 13 depends on the size of the crystals and their eventual overlap, most preferably this layer consists of crystals fixed side by side without overlapping. The coverage of the surface of the thick transparent layer 11 by the photoluminescent layer 13 is 70 to 100%. Thus prepared layers 11, 12 and 13 are harden together for the purpose of assembling the photoluminescent element 1. Hardening is preferably carried out at temperatures of 25-55° C. at time from 10 to 3 hours, depending on the specific used material of transparent layers.

[0045] Then onto the hardened layer 12 there is applied a white cover layer 14, which is altogether with the layers 11, 12 and 13 hardened again by the method according to the used material of transparent layers. The white cover layer 14 is preferably introduced as a natural or synthetic resin, for example, containing titanium dioxide. The thickness of the white cover layer is 0.05 to 0.5 mm, most preferably 0.1 to 0.2 mm. In a preferred embodiment, the white cover layer 14 is provided with glass or carbon fibers 15 to provide strengthening.

[0046] The thus manufactured photoluminescent elements after hardening are simply husked or moved out of the elastic mold. The photoluminescent element 1, shaped according to the negative of the mold, is intended for direct use. In this way, highly shining products are obtained, which can be in both 2D and 3D versions.

[0047] For example, said shining article is provided with a self-adhesive film and attached to another substrate, such as polymethyle-methacrylate, polycarbonate, metal, etc.

[0048] The photoluminescent element 1 can be glued or otherwise attached to the desired location. These products are for example incorporated into the barrier around roads etc. Luminance of the surface of the product is from 160 to 220 mcd/m.sup.2 over 1 hour from the illuminating by a halogen lamp with a luminance of 1 000 lux for 10 minutes, respectively by a xenon lamp with a luminance of 1 000 lux for 5 minutes. Xenon has a purpler colour of light, which provides more energy for the photoluminescent effect.

Example 3

[0049] Method of manufacturing a photoluminescent element 1 according to the present invention consists in the fact that at temperatures in the range between 15-55° C., preferably about room temperature in the range from 20 to 23° C., onto the plate 2, for example a plate of hard plastic or glass, a thin layer 21 is applied to ensure easy removal of the plate, preferably this layer is formed by pouring or spraying hot liquid wax, which spreads over the surface and solidifies at ambient temperature or a thick transparent layer is applied to the mold 3, for example to hardened plastic mold. The shape of the mold 3 is molded according to the requirements of the particular shape, for example the mold has a circular shape of defined dimension or oval shape, however the shape of the mold 3 can be of any shape, for example the mold shapes can be repeated in rows next to each other and/or one by the other.

[0050] In a preferred embodiment this mold 3 is provided with a thin polyurethane film 31 to ensure easy removal of the photoluminescent element 1 from the mold 3, for example a surface of a mold 3 is qualitatively adapted to ensure easy removal of the photoluminescent element.

[0051] On the thus prepared surface there is applied a thick transparent layer 11, the density of which is 1-1.5 t/m.sup.3, for example, 1.4 t/m.sup.3, where the density of layer 11 enables application that the thick transparent layer 11 is shaped on its profile, most preferably is in the form of pyramids, which in the most preferred embodiment are applied repeatedly next to each other and one by other, thus forming rows and then the area of the transparent layer 11 is larger. The surface prepared in this way is left to become cloudy.

[0052] The thick transparent layer 11 is in a preferred embodiment a binder resin or a mixture thereof or a polyurethane mixture which is transparent. It is possible to use a matt resin, for example a polyester resin, or a glossy, for example natural mixtures. In the most preferred embodiment, the thick transparent layer 11 is colourless and water-repellent. The thick transparent layer 11 is applied to the plate 2 or to the mold 3, in the most preferred embodiment the application is performed by means of an automatic robot.

[0053] The layer 11 thus prepared is allowed to stay at said temperature for 90 minutes, and the surface of this layer 11 becomes cloudy in said time. Height of the pyramids is from 0.2 to 12 mm. On pyramidal shaped layer 11 a thin transparent layer 12 is poured, a viscosity of which is 1 00-200 cP.Math.s. A photoluminescent powder 131 is immediately applied to this layer 12, which gravitationally falls through this thin transparent layer 12 and adheres to the interface of the transparent layers 11 and 12, thus forming a continuous pyramid-shaped photoluminescent layer 13. The thickness of layer 12 is in the range from 0.4 to 20 mm, in a most preferred embodiment the thickness is 4 mm. Shaping of thick transparent layer 11 generates a larger area of photoluminescent layer 13 and thus, provides a greater luminance of photoluminescent element. In a preferred embodiment, the plate 2 is provided with a frame 22 to prevent from the spillage of transparent layer 12.

[0054] The photoluminescent powder 131 is presented as a metal oxide, according to Example 1. Photoluminescent powder 131 having large crystals is applied using a spatula—sprinkled on the surface of the thin transparent layer 12, preferably is applied automatically by screen printing, where the speed of movement of the knife is constant. The thickness of the photoluminescence layer 13 depends on the size of the crystals and their eventual overlap, preferably this layer consists of crystals which are established side by side without overlapping. The coverage of the surface of the thick transparent layer 11 by the photoluminescent layer 13 is 70 to 100%. The thus prepared layer 11, 12 and 13 are hardened together for the purpose of assembling the photoluminescent element 1. Hardening is preferably carried out at temperatures of 25-55° C. at time from 10 to 3 hours, depending on the specific used material of the transparent layers. Then, in the preferred embodiment, a white cover layer 14 is applied onto the hardened layer 12 in order to increase luminance. The layers 11, 12 and 13, 14 are again hardened together by method according to the used material of the layers. The white cover layer 14 is preferably introduced as a natural or synthetic resin, for example, containing titanium dioxide. The thickness of the white cover layer 14 is 0.05 to 0.5 mm, most preferably 0, 1 to 0.2 mm. In a preferred embodiment, the white cover layer 14 is provided with glass or carbon fibers 15 to provide strengthening.

[0055] Photoluminescent element 1 in form of a plate, manufactured as mentioned above, is ready for further processing, in the preferred embodiment, due to chip machining or water jet cutting or other dividing manufactured desired shapes, e.g., round, square or triangular elements. The photoluminescent element 1 produced in the mold 3 after hardening is simply husked or moved out of the elastic mold. The photoluminescent element 1, shaped according to the negative of the mold, is intended for direct use.

Example 4

[0056] Method of manufacturing a photoluminescent element 1 according to the present invention consists in the fact that at a temperature, preferably at room temperature ranged between 20-23° C., a thick transparent layer 11 is applied onto the plate 2. The bottom of the plate 2 is arranged in the form of multi-sided pyramid, for example one next to each other repeating multi-sided pyramids, in a most preferred embodiment the multi-sided pyramid is introduced as a pyramid, while the height of the pyramid is from 0.2 to 15 mm, and an angle of the wall is from 15° to 75°, most preferably a height of 6-12 mm, under the angle of the wall of 45°. The plate 2 is for example made of hard plastic or glass, on which a thin layer 21 to ensure easy removal of the plate is applied, preferably a layer is formed by pouring or spraying hot liquid wax, which is spread over the surface and solidifies at ambient temperature. It is further preferred, that the plate 2 is provided with a frame 22 to prevent spillage of the layer 12 at the edges.

[0057] On thus prepared shaped surface on the board 2 there is applied a thick transparent layer 11, the density of which is 11.5 t/m.sup.3, for example, 1.4 t/m.sup.3 and this layer is spread over the prepared molded surface of the plate 2, whereby due to the physical properties of the transparent layer 11, this layer will copy the shape of the bottom and becomes cloudy in the copied shape. The transparent layer 11 is in a preferred embodiment a binder resin or a mixture thereof or a polyurethane mixture which is transparent. It is possible to use a matt resin, for example a polyester resin, or a glossy, for example natural mixtures. In the most preferred embodiment, the thick transparent layer 11 is colourless and water-repellent. The thick transparent layer 11 is poured onto the plate 2, in the most preferred embodiment the pouring is performed by means of an automatic robot. The thickness of layer 11 is in the range of 0.1 to 20 mm, preferably 0.8 mm. On layer 11 there is poured a thin transparent layer 12, a viscosity of which is 100 to 200 cP.Math.s. The height of the layer 12 is preferably about 0.1 to 3 mm taller than the height of the pyramid. A photoluminescent powder 131 is immediately applied to the layer 12, which gravitationally falls through this thin transparent layer 12 and adheres to the interface of the transparent layers 11 and 12, thus forming a continuous shaped photoluminescent layer 13. The thickness of layer 12 is in the range of 0, 1 to 20 mm, in a most preferred embodiment, the thickness is 2 mm.

[0058] By creating a larger real surface of photoluminescent layer 13 there is a significant increase of luminance of photoluminescent element 1.

[0059] The photoluminescent powder 131 is presented as a metal oxide, as mentioned above. The thickness of the photoluminescence layer 13 depends on the size of the crystals and their eventual m overlap, preferably this layer consists of crystals which are established side by side without overlapping. The coverage of the surface of the thick transparent layer 11 of the photoluminescent layer 13 is from 70 to 100%.

[0060] Thus prepared layer s 11, 12 and 13 are hardened together for the purpose of assembling the photoluminescent element 1. Hardening is preferably carried out at temperatures of 25-55° C. at time 10 hours to 3 hours, depending on the specific used material of the transparent layers. Then onto the hardened layer 12 the white cover layer 14 is applied, which altogether with the layers 11, 12, 13 is hardened again by the method according to the used material of the layers. The white cover layer 14 is preferably introduced as a natural or synthetic resin, for example, containing titanium dioxide. The thickness of the white cover layer 14 is 0.05 to 0.5 mm, most preferably 0.1 to 0.2 mm. In a preferred embodiment, the white cover layer 14 is provided with glass or carbon fibers 15 to provide strengthening. The photoluminescent element 1 in the form of a plate, produced in the manner described above, is ready for further processing, in a preferred embodiment the desired shapes, e.g. round, square or triangular elements, are made by means of chip machining or other material separation methods.

[0061] To ensure long-term luminance of molded photoluminescent layer 13 a photoluminescent element 1 is removed from the plate 2, turned around and inserted onto the plate 2′ provided with a frame 22′, wherein the frame 22′ is preferably about 6% larger than the photoluminescent element 1, and shaped surface is filled with a levelling transparent layer 16. The levelling layer 16 flows around the whole photoluminescent element 1, thereby avoiding distortion and degradation of the luminous layer of photoluminescent element 1. For example, the plate 2′ is equipped with layer 21′ to ensure easy removal. Furthermore, in a preferred embodiment, the levelling transparent layer 16 is provided with a film 6 for providing a smooth and glossy surface, which is incorporated into the surface of the photoluminescent element 1 by a rolling device 7.

[0062] The photoluminescent element 1, in the form of a plate, produced in the manner mentioned above, is ready for further processing, in a preferred embodiment the desired shapes are made by means of chip machining or water jet cutting or other means of division, e.g. round, square or triangular elements, letters, numbers etc. For example, said luminous article is provided with a self-adhesive film and attached to another surface, such as polymethyle methacrylate, polycarbonate, metal, etc. The attachment of the photoluminescent element 1 is also possible with glue, sealant or other known attachment methods.

[0063] These products are for example incorporated into the barrier around roads etc. The luminance of the surface of the article is from 160 to 220 mcd/m.sup.2 over 1 hour from illuminating by the halogen lamp of a luminance of 1 000 lux for 10 minutes, respectively by a xenon lamp with a luminance of 1 000 lux for 5 minutes. Xenon has a purpler colour of light, which provides more energy for the photoluminescent effect.

Example 5

[0064] Method of manufacturing a photoluminescent element 1 according to the present invention consists in the fact that at a temperature, preferably at room temperature ranged between 20-23° C., into the mold 3 a thick transparent layer 11 is applied. The bottom of the plate 2 is arranged in the form of multi-sided pyramid, for example one next to each other repeating multi-sided pyramids, in a most preferred embodiment the multi-sided pyramid is introduced as a pyramid, while the height of the pyramid is from 0.2 to 15 mm, and an angle of the wall is from 15° to 75°, most preferably a height of 6-12 mm, under the angle of the wall of 45°. The mold 3 is preferably made of hardened plastic and the shape of the mold is molded according to the requirements of the particular shape, for example the mold has a circular shape of defined size or oval, however the shape of the mold 3 can be of any shape. In the most preferred embodiment the system is arranged in rows next to each other and/or several molds in series. In a preferred embodiment, this mold 3 is provided with a thin polyurethane film 31 to ensure easy removal of the photoluminescent element 1 from the mold 3.

[0065] On the thus prepared substrate surface shaped in the mold 3 a thick transparent layer 11 is applied, the density of which is 1-1.5 t/m3, and this layer is spread over the prepared shaped surface of the bottom of the mold 3, wherein with respect to the physical properties of the transparent layer 11 this layer will copy the shape of the bottom and become cloudy in the copied shape. The transparent layer 11 is in a preferred embodiment a binder resin or a mixture thereof or a polyurethane mixture which is transparent. It is possible to use a matt resin, for example a polyester resin, or a glossy, for example natural mixtures. In the most preferred embodiment the thick transparent layer 11 is colourless and water-repellent. The thick transparent layer 11 is poured into the mold 3, in the most preferred embodiment the pouring is performed by means of an automatic robot. The thickness of layer 11 is in the range of 0.1 to 20 mm, preferably 0.8 mm. Onto the layer 11 a thin transparent layer 12 is poured with a viscosity of 100 to 200 cP.Math.s. The height of layer 12 is preferably about 0.1 to 3 mm taller than the height of the pyramid. A photoluminescent powder 131 is immediately applied onto the layer 12, which gravitationally falls through this thin transparent layer 12 and adheres to the interface of the transparent layers 11 and 12, thereby forming a continuous shaped photoluminescent layer 13. The thickness of layer 12 is in the range of 0.1 to 20 mm, in a most preferred embodiment, the thickness is 2 mm.

[0066] By creating a larger real surface of photoluminescent layer 13 there is a significant increase of luminance of photoluminescent element 1.

[0067] The photoluminescent powder 131 is presented as a metal oxide, as mentioned above, including coating density.

[0068] Thus prepared layer s 11, 12 and 13 are hardened together for the purpose of assembling the photoluminescent element 1. Hardening is preferably carried out at temperatures of 25-55° C. at time 10 hours to 3 hours, depending on the specific used material of the transparent layers. Then onto the hardened layer 12 the white cover layer 14 is applied, which altogether with the layers 11, 12, 13 is hardened again by the method according to the used material of the layers. The white cover layer 14 is preferably introduced as a natural or synthetic resin, for example, containing titanium dioxide. The thickness of the white cover layer 14 is 0.05 to 0.5 mm, most preferably 0.1 to 0.2 mm. In a preferred embodiment, the white cover layer 14 is provided with glass or carbon fibers 15 to provide strengthening. The photo-luminescent elements 1 formed in the molds 3 after hardening are simply husked or moved out of the elastic mold and are ready for direct use.

[0069] To ensure the long-term luminance of the shaped photoluminescent layer 13, the photoluminescent element 1 is removed from the mold 3, turned around and inserted into the mold 3′ while being preferred that the mold 3′ is about 7 percent larger than the photoluminescent element 1, and shaped surface is filled with a levelling transparent layer 16. The levelling layer 16 flows around the whole photoluminescent element 1, thereby avoiding distortion and degradation of the luminous layer of photoluminescent element 1. For example, the mold 3′ is equipped with layer 31′ to ensure easy removal. Furthermore, in a preferred embodiment, the levelling transparent layer 16 is provided with a film 6 for providing a smooth and glossy surface, which is incorporated into the surface of the photoluminescent element 1 by a rolling device 7.

[0070] For example, said luminous article is provided with a self-adhesive film and attached to another surface, such as polymethyle methacrylate, polycarbonate, metal, etc. The attachment of the photoluminescent element 1 is also possible with glue, sealant or other known attachment methods.

[0071] These products are for example incorporated into the barrier around roads etc. The luminance of the surface of the article is from 160 to 220 mcd/m.sup.2 over 1 hour from illuminating by the halogen lamp of a luminance of 1 000 lux for 10 minutes, respectively by a xenon lamp with a luminance of 1 000 lux for 5 minutes. Xenon has a purpler colour of light, which provides more energy for the photoluminescent effect.

Example 6

[0072] Method of manufacturing a photoluminescent element 1 according to the present invention consists in the fact that at temperatures in the range from 15 to 55° C., preferably at about room temperature in the range from 20 to 23° C., on the plate 2, for example a plate of hard plastic or glass, there is applied a thin layer 21 to ensure easy removal of the plate, preferably the layer is formed by pouring or spraying hot liquid wax, which is spread over the surface and solidifies at ambient temperature. On thus prepared surface a thick transparent layer 11 is applied, the density of which is 1-1.5 t/m.sup.3, for example 1.1 t/m.sup.3, and this layer is spread over the prepared base plate 2. The thick transparent layer 11 is in a preferred embodiment a binder resin or a mixture thereof or a polyurethane mixture which is transparent, same as mentioned above. In the most preferred embodiment, the thick transparent layer 11 is colourless and water-repellent. The thick transparent layer 11 is poured onto the plate 2, in the most preferred embodiment the pouring is performed by means of an automatic robot. The layer 11 thus prepared is left at said temperature for 80-350 minutes, and the surface of this layer 11 becomes cloudy in said time. The thickness of the thick transparent layer 11 is in the range 0, 1 to 20 mm, preferably 0.8 mm.

[0073] Into the thick transparent layer 11 a pressure is made by pressuring means, wherein the pressuring means 5 has a shaped surface. As a result, the thick transparent layer 11 is formed and its area is larger. Most preferably, the shaped surface is pyramidal. On the thick transparent layer 11 a thin transparent layer 12 is poured with a viscosity of 100 to 200 cP.Math.s, and a photoluminescent powder 131 is immediately applied onto the thin transparent layer 12, which falls by gravity through this thin transparent layer 12 and adheres to the interface of the transparent layers 11 and 12, thereby forming a continuous photoluminescent layer 13.

[0074] Reached photoluminescent layer 13 has a significantly greater area and thereby a higher luminance is achieved. The thickness of the thin transparent layer 12 is in the range of 0.1 to 20 mm, in a most preferred embodiment, the thickness is 2 mm.

[0075] Photoluminescent powder 131 is presented as a metal oxide as mentioned above, including its percentage coverage.

[0076] Thus prepared layers 11, 12 and 13 are hardened together for the purpose of assembling the photoluminescent element 1. Hardening is preferably carried out at temperatures of 25-55° C. at time from 10 hours to 3 hours, depending on the specific used material of the transparent layers.

[0077] In a preferred embodiment, a white cover layer 14 is applied to the hardened layer 12 to increase luminance. Layers 11, 12 and 13, 14 are hardened together again depending on the material used. The white cover layer 14 is preferably a natural or artificial resin containing, for example, titanium white. The thickness of the white cover layer 14 is 0.05 to 0.5 mm, most preferably 0.1 to 0.2 mm. In a preferred embodiment, the white cover layer 14 is provided with glass or carbon fibers 15 to provide strengthening.

[0078] The photoluminescent element 1, in the form of a plate, produced in the manner described above, is ready for further processing, in a preferred embodiment the desired shapes are made by means of chip machining or water jet cutting or other means of division, e.g. round, square or triangular elements, letters, numbers, etc.

Example 7

[0079] Method of manufacturing a photoluminescent element 1 according to the present invention consists in the fact that at a temperature, preferably at room temperature ranged between 20-23° C., a thick transparent layer 11 is applied into the mold 3, for example into the mold of hardened plastic. The shape of the mold is molded according to the requirements of the particular shape, for example the mold 3 has a circular shape of defined dimension or oval, however the shape of the mold 3 can be of any shape. Most preferably, it is a plate comprising several juxtaposed molds. In a preferred embodiment this mold 3 is provided with a thin polyurethane film 31 to ensure easy removal of the photoluminescent element 1 from the mold 3, wherein the mold 3 and the polyurethane film 31 form one unit together. For example, a wax may be used as the layer 31 to ensure easy removal of the photoluminescent element 1 from the mold 3.

[0080] On the thus prepared surface in the mold 3 a thick transparent layer 11 is applied, the density of which is 1-1.5 t/m.sup.3, and this layer is spread over the prepared base surface of the mold 3. The transparent layer 11 is in a preferred embodiment a binder resin or a mixture thereof or a polyurethane mixture which is transparent. It is possible to use a matt resin, for example a polyester resin, or a glossy, for example natural mixtures. In the most preferred embodiment, the thick transparent layer 11 is colourless and water-repellent. The thick transparent layer 11 is poured onto the mold 3, in the most preferred embodiment the pouring is performed by means of an automatic robot. The thus prepared layer 11 is left at said temperature for a period of 80-150 min, the surface of this layer 11 becomes cloudy in said time. The thickness of the thick transparent layer 11 is in the range 0, 1 to 20 mm, preferably 0.8 mm. Into the thick transparent layer 11 a pressure is made by pressuring means, wherein the pressuring means 5 has a shaped surface. As a result, the thick transparent layer 11 is formed and its area is larger. Most preferably, the shaped surface is pyramidal.

[0081] On the thick transparent layer 11 a thin transparent layer 12 is poured with a viscosity of 100 to 200 cP.Math.s, and a photoluminescent powder 131 is immediately applied onto the thin transparent layer 12, which falls by gravity through this thin transparent layer 12 and adheres to the interface of the transparent layers 11 and 2 thereby forming a continuous photoluminescent layer 13. The thickness of layer 12 is in the range of 0.1 to 20 mm, in a most preferred embodiment, the thickness is 2 mm. Photoluminescent powder 131 is introduced as a metal oxide, identically as described above. The layers 11, 12 and 13 thus prepared are hardened together in order to assemble the photoluminescent element 1. Hardening is preferably carried out at temperatures of 25-55° C. at time from 10 to 3 hours, depending on the specific used material of the transparent layers.

[0082] Then onto the hardened layer 12 the white cover layer 14 is applied, which altogether with the layers 11, 12, 13 is hardened again by the method according to the used material of the transparent layers. The white cover layer 14 is preferably introduced as a natural or synthetic resin, for example, containing titanium dioxide. The thickness of the white cover layer 14 is 0.05 to 0.5 mm, most preferably 0.1 to 0.2 mm. In a preferred embodiment, the white cover layer 14 is provided with glass or carbon fibers 15 to provide strengthening.

[0083] The thus manufactured photoluminescent elements after hardening are simply husked or moved out of the elastic mold. The photoluminescent element 1, shaped according to the negative of the mold, is intended for direct use. In this way, highly shining products are obtained, which can be in both 2D and 3D versions.

[0084] For example, said shining article is provided with a self-adhesive film and attached to another substrate, such as polymethyle-methacrylate, polycarbonate, metal, etc.

[0085] The photoluminescent element 1 can be glued or otherwise attached to the desired location. These products are for example incorporated into the barrier around roads etc. Luminance of the surface of the product is from 160 to 220 mcd/m.sup.2 over 1 hour from the illuminating by a halogen lamp with a luminance of 1 000 lux for 10 minutes, respectively by a xenon lamp with a luminance of 1 000 lux for 5 minutes.

LIST OF REFERENCE NUMBERS

[0086] 1 photoluminescent element [0087] 11 thick transparent layer [0088] 12 thin transparent layer [0089] 13 photoluminescent layer [0090] 131 photoluminescent powder [0091] 14 white cover layer [0092] 15 glass or carbon fibers [0093] 16 levelling transparent layer [0094] 2, 2′ plate [0095] 21, 21′ layer to provide easy removal [0096] 22 frame of the plate [0097] 22′ larger frame of the plate [0098] 3 mold [0099] 3′ larger mold [0100] 31, 31″ layer to provide easy removal [0101] 4 screen printing knife or cartridge of photoluminescent powder [0102] 5 pressing means [0103] 6 film to provide a smooth and glossy surface [0104] 7 rolling device