CATALYTIC UPCYCLING OF POLYOLEFINS VIA VERSATILE ALKYLALUMINUMS
20220213007 · 2022-07-07
Inventors
Cpc classification
C07C51/15
CHEMISTRY; METALLURGY
B01J37/0209
PERFORMING OPERATIONS; TRANSPORTING
C07C51/15
CHEMISTRY; METALLURGY
C07C53/126
CHEMISTRY; METALLURGY
C07C17/06
CHEMISTRY; METALLURGY
C07C231/02
CHEMISTRY; METALLURGY
C07C67/24
CHEMISTRY; METALLURGY
B01J31/1616
PERFORMING OPERATIONS; TRANSPORTING
B01J31/069
PERFORMING OPERATIONS; TRANSPORTING
B01J31/128
PERFORMING OPERATIONS; TRANSPORTING
C07C53/126
CHEMISTRY; METALLURGY
B01J31/123
PERFORMING OPERATIONS; TRANSPORTING
International classification
B01J31/16
PERFORMING OPERATIONS; TRANSPORTING
C07C17/06
CHEMISTRY; METALLURGY
C07C231/02
CHEMISTRY; METALLURGY
C07C51/15
CHEMISTRY; METALLURGY
Abstract
Disclosed herein is a process for the conversion of polymers, oligomers, or mixtures thereof into shorter alkanes, carboxylic acids, alcohols, alkyl halides or aldehydes. This process includes contacting the polymers, oligomers, or mixtures thereof with the compound of formula (I):
Al(R.sup.1).sub.3 (I)
where R.sup.1 is independently selected at each occurrence thereof from the group consisting of H, aryl, C.sub.1-C.sub.8 alkyl, and C.sub.1-C.sub.8 alkoxy, as a reaction mixture, in the presence of a catalyst selected from the group consisting of a transition metal catalyst, a lanthanide series metal catalyst, or combinations thereof.
Claims
1. A process comprising: providing one or more polymers, oligomers, or mixtures thereof; providing a compound of formula (I):
Al(R.sup.1).sub.3 (I) wherein R.sup.1 is independently selected at each occurrence thereof from the group consisting of H, aryl, C.sub.1-C.sub.8 alkyl, and C.sub.1-C.sub.8 alkoxy; contacting the polymers, oligomers, or mixtures thereof with the compound of formula (I), as a reaction mixture, in the presence of a catalyst selected from the group consisting of a transition metal catalyst, a lanthanide series metal catalyst, or combinations thereof, under conditions effective to form alkanes, carboxylic acids, alcohols, alkyl halides or aldehydes, which are shorter than the polymers, the oligomers, or the mixtures thereof; and recovering the formed shorter alkanes, carboxylic acids, alcohols, alkyl halides or aldehydes.
2. The process of claim 1, wherein the catalyst is formed from a metal selected from the group consisting of zirconium, titanium, hafnium, vanadium, niobium, tantalum, scandium, yttrium, lanthanum, cerium, praseodymium, neodymium, samarium, europium, gadolinium, terbium, dysprosium, holmium, erbium, thulium, ytterbium, and lutetium.
3. The process of claim 1, wherein the catalyst is in the form of formula (II):
Met(R.sup.2).sub.n@support (II) wherein Met is one or more transition metal or lanthanide series metal selected from the group consisting of zirconium, titanium, hafnium, vanadium, niobium, tantalum, scandium, yttrium, and lanthanum, cerium, praseodymium, neodymium, samarium, europium, gadolinium, terbium, dysprosium, holmium, erbium, thulium, ytterbium, and lutetium; R.sup.2 is independently selected at each occurrence thereof from the group consisting of H, C.sub.1-C.sub.10 alkyl, C.sub.1-C.sub.10 alkoxy or aryloxy, aryl, OH, halogen, C.sub.1-C.sub.10 arylalkyl, C.sub.1-C.sub.10 alkylsilylalkyl, siloxy, BH.sub.4, allyl, C.sub.1-C.sub.10 alkylamido, acetylacetonate, acrylate, acetate; n is an integer ranging from 1 to 3; and support is selected from the group consisting of silica, alumina, silica/alumina, zeolites, metal oxides, mesoporous oxides, natural clays, and mixtures thereof.
4. (canceled)
5. The process of claim 3, wherein the catalyst of formula (II) is selected from the group consisting of Zr(CH.sub.2CMe.sub.3).sub.n@SiAlO.sub.x, Zr(OCH.sub.2CMe.sub.3).sub.n@SiAlO.sub.x, Zr(CH.sub.2CMe.sub.3).sub.n@SiO.sub.2, Zr(OC.sub.3H.sub.7).sub.n@SiAlO.sub.x, Zr(OC.sub.4H.sub.9).sub.n@SiAlO.sub.x, Zr(OC.sub.4H.sub.9).sub.n@SiO.sub.2, Zr(H).sub.n@SiO.sub.2, and Zr(H).sub.n@SiAlO.sub.x, wherein n is an integer ranging from 1-3.
6. The process of claim 1, wherein the compound of formula (I) is selected from the group consisting of AliBu.sub.3, AlEt.sub.3, AlMe.sub.3, AlPh.sub.3, Al(C.sub.8H.sub.17).sub.3, and AlH.sub.3.
7. (canceled)
8. (canceled)
9. (canceled)
10. (canceled)
11. The process of claim 1, wherein the polymers, oligomers, or mixtures thereof are polyolefins and wherein said polyolefins are selected from the group consisting of high density polyethylene, low density polyethylene, polypropylene, linear low density polyethylene, polyethylene-polypropylene-copolymers, polystyrene, and mixtures thereof.
12. (canceled)
13. The process of claim 1, wherein said contacting is carried out at a temperature sufficient to melt the polymers, oligomers, or mixtures thereof.
14. (canceled)
15. (canceled)
16. The process of claim 1, wherein said contacting is carried out under atmospheric pressure or under a vacuum.
17. (canceled)
18. (canceled)
19. The process of claim 1, wherein said contacting is carried out under conditions effective to form the shorter alkanes and comprises: adding an alcohol or water to the reaction mixture to form the shorter alkanes.
20. (canceled)
21. The process of claim 1, wherein said contacting is carried out under conditions effective to form shorter carboxylic acids and comprises: adding carbon dioxide to the reaction mixture under conditions effective to form the shorter carboxylic acids.
22. (canceled)
23. (canceled)
24. The process of claim 1, wherein said contacting is carried out under conditions effective to form the shorter alcohols and comprises: adding oxygen to the reaction mixture to form the shorter alcohols.
25. The process of claim 1, wherein said contacting is carried out under conditions effective to form shorter alkyl halides and comprises: adding a halogen to the reaction mixture to form the shorter alkyl halides.
26. (canceled)
27. (canceled)
28. The process of claim 1, wherein said contacting is carried out under conditions effective to form the shorter aldehydes and comprises: adding an orthoester to the reaction mixture to form the shorter aldehydes.
29. The process of claim 1, wherein the molar ratio of the compound of formula (I) to the catalyst of formula (II) ranges from 3:1 to 20:1.
30. (canceled)
31. (canceled)
32. A process comprising: providing one or more polymers, oligomers, or mixtures thereof; providing a compound of formula (I):
Al(R.sup.1).sub.3 (I) wherein R.sup.1 is independently selected at each occurrence thereof from the group consisting of H, aryl, C.sub.1-C.sub.8 alkyl, and C.sub.1-C.sub.8 alkoxy; contacting the polymers, oligomers, or mixtures thereof with the compound of formula (I), as a reaction mixture, in the presence of a catalyst selected from the group consisting of a transition metal catalyst, a lanthanide series metal catalyst, or combinations thereof, under conditions effective to form an aluminum alkyl compound of formula (III)
Al(R.sup.1).sub.3-n(R.sup.3).sub.n (III) wherein R.sup.3 is independently selected at each occurrence thereof from C.sub.12-C.sub.60 alkyls, which are shorter than the polymers, the oligomers, or the mixtures thereof; and n is an integer ranging from one to three.
33. The process of claim 32, wherein the transition metal catalyst or the lanthanide series metal catalyst is selected from the group consisting of zirconium, titanium, hafnium, vanadium, niobium, tantalum, scandium, yttrium, lanthanum, cerium, praseodymium, neodymium, samarium, europium, gadolinium, terbium, dysprosium, holmium, erbium, thulium, ytterbium, and lutetium.
34. The process of claim 32, wherein the transition metal catalyst and/or lanthanide-catalyst has formula (II):
Met(R.sup.2).sub.n@support (II) wherein Met is a metal selected from the group consisting of zirconium, titanium, hafnium, vanadium, niobium, tantalum, scandium, yttrium, and lanthanum, cerium, praseodymium, neodymium, samarium, europium, gadolinium, terbium, dysprosium, holmium, erbium, thulium, ytterbium, and lutetium; R.sup.2 is independently selected at each occurrence thereof from the group consisting of H, C.sub.1-C.sub.10 alkyl, C.sub.1-C.sub.10 alkoxy, aryl, OH, halogen, C.sub.1-C.sub.10 arylalkyl, C.sub.1-C.sub.10 alkylsilylalkyl, BH.sub.4, allyl, C.sub.1-C.sub.10 alkylamido, acetylacetonate, acrylate, and acetate; n is an integer ranging from 1 to 3; and support is selected from the group consisting of silica, alumina, silica/alumina, zeolites, metal oxides, mesoporous oxides, natural clays, and mixtures thereof.
35. (canceled)
36. The process of claim 34, wherein the catalyst of formula (II) is selected from the group consisting of Zr(CH.sub.2CMe.sub.3).sub.n@SiAlO.sub.x, Zr(OCH.sub.2CMe.sub.3).sub.n@SiAlO.sub.x, Zr(CH.sub.2CMe.sub.3).sub.n@SiO.sub.2, Zr(OC.sub.3H.sub.7).sub.n@SiAlO.sub.x, Zr(OC.sub.4H.sub.9).sub.n@SiAlO.sub.x, Zr(OC.sub.4H.sub.9).sub.n@SiO.sub.2, Zr(H).sub.n@SiO.sub.2, and Zr(H).sub.n@SiAlO.sub.x, wherein n is an integer ranging from 1-3.
37. The process of claim 32, wherein the compound of formula (I) is selected from the group consisting of AliBu.sub.3, AlEt.sub.3, AlMe.sub.3, AlPh.sub.3, Al(C.sub.8H.sub.17).sub.3, and AlH.sub.3.
38. (canceled)
39. (canceled)
40. The process of claim 32, wherein the polymers, oligomers, or mixtures thereof are polyolefins and wherein said polyolefins are selected from the group consisting of high density polyethylene, low density polyethylene, polypropylene, linear low density polyethylene, polyethylene-polypropylene-copolymers, polystyrene, and mixtures thereof.
41. (canceled)
42. The process of claim 33, wherein said contacting is carried out at a temperature sufficient to melt the polymers, oligomers, or mixtures thereof.
43. (canceled)
44. (canceled)
45. The process of claim 33, wherein said contacting is carried out under atmospheric pressure or under a vacuum.
46. (canceled)
47. (canceled)
48. An alkyl aluminum of formula (III):
Al(R.sup.1).sub.3-n(R.sup.3).sub.n (III) wherein R.sup.1 is independently selected at each occurrence thereof from the group consisting of H, aryl, C.sub.1-C.sub.8 alkyl, and C.sub.1-C.sub.8 alkoxy; R.sup.3 is independently selected at each occurrence thereof from C.sub.12-C.sub.60 alkyls; and n is an integer ranging from one to three.
49. (canceled)
50. (canceled)
Description
BRIEF DESCRIPTION OF THE DRAWINGS
[0030]
[0031]
[0032]
[0033]
[0034]
[0035]
[0036]
[0037]
[0038]
[0039]
[0040]
[0041]
[0042]
[0043]
[0044]
[0045]
[0046]
[0047]
[0048]
[0049]
[0050]
[0051]
[0052]
[0053]
[0054]
[0055]
[0056]
[0057]
[0058]
[0059]
[0060]
[0061]
[0062]
[0063]
[0064]
[0065]
[0066]
[0067]
[0068]
[0069]
[0070]
[0071]
[0072]
[0073]
[0074]
[0075]
[0076]
[0077]
[0078]
[0079]
[0080]
[0081]
[0082]
[0083]
[0084]
[0085]
[0086]
[0087]
[0088]
[0089]
[0090]
[0091]
[0092]
[0093]
[0094]
[0095]
[0096]
[0097]
[0098]
[0099]
[0100]
[0101]
[0102]
[0103]
[0104]
[0105]
[0106]
[0107]
[0108]
[0109]
[0110]
[0111]
[0112]
[0113]
[0114]
[0115]
[0116]
[0117]
[0118]
[0119]
[0120]
[0121]
[0122]
[0123]
[0124]
[0125]
[0126]
DETAILED DESCRIPTION
[0127] One aspect of the present application relates to a process including:
[0128] providing one or more polymers, oligomers, or mixtures thereof;
[0129] providing a compound of formula (I):
Al(R.sup.1).sub.3 (I)
where [0130] R.sup.1 is independently selected at each occurrence thereof from the group consisting of H, aryl, C.sub.1-C.sub.8 alkyl, and C.sub.1-C.sub.8 alkoxy;
[0131] contacting the polymers, oligomers, or mixtures thereof with the compound of formula (I), as a reaction mixture, in the presence of a catalyst selected from the group consisting of a transition metal catalyst, a lanthanide series metal catalyst, or combinations thereof, under conditions effective to form alkanes, carboxylic acids, alcohols, alkyl halides or aldehydes, which are shorter than the polymers, the oligomers, or the mixtures thereof; and
[0132] recovering the formed shorter alkanes, carboxylic acids, alcohols, alkyl halides or aldehydes.
[0133] A second aspect of the present application relates to a process including:
[0134] providing one or more polymers, oligomers, or mixtures thereof;
[0135] providing a compound of formula (I):
Al(R.sup.1).sub.3 (I)
where [0136] R.sup.1 is independently selected at each occurrence from the group consisting of H, aryl, C.sub.1-C.sub.8 alkyl, and C.sub.1-C.sub.8 alkoxy;
[0137] contacting the polymers, oligomers, or mixtures thereof with the compound of formula (I), as a reaction mixture, in the presence of a catalyst selected from the group consisting of a transition metal catalyst, a lanthanide series metal catalyst, or combinations thereof, under conditions effective to form an aluminum alkyl compound of formula (III)
Al(R.sup.1).sub.3-n(R.sup.3).sub.n (III)
where [0138] R.sup.3 is independently selected at each occurrence thereof from C.sub.12-C.sub.60 alkyls, which are shorter than the polymers, the oligomers, or the mixtures thereof; and
[0139] n is an integer ranging from one to three.
[0140] As used above, and throughout the description herein, the following terms, unless otherwise indicated, shall be understood to have the following meanings. If not defined otherwise herein, all technical and scientific terms used herein have the same meaning as is commonly understood by one of ordinary skill in the art to which this technology belongs. In the event that there is a plurality of definitions for a term herein, those in this section prevail unless stated otherwise.
[0141] The term “alkyl” means an aliphatic hydrocarbon group which may be straight or branched. When not otherwise restricted, the term refers to an alkyl of 20 or fewer carbons. Branched means that one or more lower alkyl groups such as methyl, ethyl, or propyl are attached to a linear alkyl chain. Exemplary alkyl groups include methyl, ethyl, n-propyl, i-propyl, n-butyl, t-butyl, n-pentyl, 3-pentyl, and the like.
[0142] The term “aryl” means an aromatic monocyclic or multi-cyclic (polycyclic) ring system of 6 to about 19 carbon atoms, or of 6 to about 10 carbon atoms, and includes arylalkyl groups. The ring system of the aryl group may be optionally substituted. Representative aryl groups include, but are not limited to, groups such as phenyl, naphthyl, azulenyl, phenanthrenyl, anthracenyl, fluorenyl, pyrenyl, triphenylenyl, chrysenyl, and naphthacenyl.
[0143] The term “alkoxy” means groups of from 1 to 6 carbon atoms of a straight, branched, or cyclic configuration and combinations thereof attached to the parent structure through an oxygen. Examples include methoxy, ethoxy, n-propoxy, isopropoxy, n-butoxy, i-butoxy, t-butoxy, phenoxy, cyclopropyloxy, cyclohexyloxy, and the like. Alkoxy also includes methylenedioxy and ethylenedioxy in which each oxygen atom is bonded to the atom, chain, or ring from which the methylenedioxy or ethylenedioxy group is pendant so as to form a ring. Thus, for example, phenyl substituted by alkoxy may be, for example,
##STR00001##
[0144] As used herein, “halogen” refers to fluoro, chloro, bromo, or iodo.
[0145] Exemplary compounds of formula (I) which may be used in the present application include, but are not limited to AliBu.sub.3, AlEt.sub.3, AlMe.sub.3, AlPh.sub.3, Al(C.sub.8H.sub.17).sub.3, and AlH.sub.3.
[0146] In one embodiment of the process of the present application, the catalyst is formed from a metal selected from the group consisting of zirconium, titanium, hafnium, vanadium, niobium, tantalum, scandium, yttrium, lanthanum, cerium, praseodymium, neodymium, samarium, europium, gadolinium, terbium, dysprosium, holmium, erbium, thulium, ytterbium, and lutetium.
[0147] The transition metal catalyst and/or lanthanide-catalyst catalyst may be in the form of formula (II):
Met(R.sup.2)n@support (II)
where
[0148] Met is one or more transition metal or lanthanide series metal selected from the group consisting of zirconium, titanium, hafnium, vanadium, niobium, tantalum, scandium, yttrium, and lanthanum, cerium, praseodymium, neodymium, samarium, europium, gadolinium, terbium, dysprosium, holmium, erbium, thulium, ytterbium, and lutetium;
[0149] R.sup.2 is independently selected at each occurrence thereof from the group consisting of —H, C.sub.1-C.sub.10 alkyl, C.sub.1-C.sub.10 alkoxy or aryloxy, aryl, —OH, halogen, C.sub.1-C.sub.10 arylalkyl, C.sub.1-C.sub.10 alkylsilylalkyl, siloxy, —BH.sub.4, allyl, C.sub.1-C.sub.10 alkylamido, acetylacetonate, acrylate, acetate;
[0150] n is an integer ranging from 1 to 3; and
[0151] support is selected from the group consisting of silica, alumina, silica/alumina, zeolites, metal oxides, mesoporous oxides, natural clays, and mixtures thereof.
[0152] As used herein, the term “arylalkyl” refers to aryl groups as described herein in which one or more hydrogen atoms is substituted by alkyl groups, where the radical or point of attachment to the parent molecule is on the alkyl group.
[0153] As used herein, the term “alkylsilylalkyl” refers to a silane in which two or more hydrogen atoms are substituted by alkyl groups, where the point of attachment to the parent molecule is on one of the alkyl groups.
[0154] As used herein, as “alkylamido” refers to one or more alkyl groups on a nitrogen, attached to the parent molecule through the amido group.
[0155] “Unsubstituted” atoms bear all of the hydrogen atoms dictated by their valence.
[0156] The term “optionally substituted” is used to indicate that a group may have a substituent at each substitutable atom of the group (including more than one substituent on a single atom), provided that the designated atom's normal valency is not exceeded and the identity of each substituent is independent of the others. Up to three H atoms in each residue are replaced with alkyl, halogen, haloalkyl, hydroxy, lower alkoxy, carboxy, carboalkoxy (also referred to as alkoxycarbonyl), carboxamido (also referred to as alkylaminocarbonyl), cyano, carbonyl, nitro, amino, alkylamino, dialkylamino, mercapto, alkylthio, sulfoxide, sulfone, acylamino, amidino, phenyl, benzyl, heteroaryl, phenoxy, benzyloxy, or heteroaryloxy. When a substituent is keto (i.e., ═O), then two hydrogens on the atom are replaced. Combinations of substituents and/or variables are permissible only if such combinations result in stable compounds. A “stable compound” is meant to be a compound that is sufficiently robust to survive isolation to a useful degree of purity from a reaction mixture, and formulation into an efficacious therapeutic agent.
[0157] In some embodiments of catalyst in the form of formula (II),
[0158] Met is selected from the group consisting of zirconium, titanium, or hafnium; and
[0159] R.sup.2 is independently selected at each occurrence thereof from the group consisting of —H, -Me, -tBu, -Ph, —OH, —CH.sub.2Ph, —CH.sub.2SiMe.sub.3, —CH.sub.2CMe.sub.3, —BH.sub.4, —Cl, —Br, —I, —NMe.sub.2, —NEt.sub.2, —NnPr.sub.2, —NiBu.sub.2, μNC.sub.5H.sub.10, —NC.sub.6H.sub.12, —OMe, —OEt, —OnPr, —OiPr, —OtBu, —OnBu, —OPh, —OSiMe.sub.3, —OSiPh.sub.3, —OSi(OtBu).sub.3, acetylacetonate, acrylate, acetate, and allyl and substituted derivatives thereof.
[0160] Exemplary catalysts of formula (II) useful in the process of the present application include, but are not limited to, Zr(CH.sub.2CMe.sub.3).sub.n@SiAlO.sub.x, Zr(OCH.sub.2CMe.sub.3).sub.n@SiAlO.sub.x, Zr(CH.sub.2CMe.sub.3).sub.n@SiO.sub.2, Zr(OC.sub.3H.sub.7).sub.n@SiAlO.sub.x, Zr(OC.sub.4H.sub.9).sub.n@SiAlO.sub.x, Zr(OC.sub.4H.sub.9).sub.n@SiO.sub.2, Zr(H).sub.n@SiO.sub.2, and Zr(H).sub.n@SiAlO.sub.x, where n is an integer ranging from 1-3.
[0161] Exemplary support materials include, but are not limited to, silica, in amorphous form (e.g., gel, aerosil, or Stöber-type), mesoporous silica (e.g., MCM-41, SBA-15), or crystalline silica (e.g. β-cristobalite); silica-alumina of varying aluminum loadings in amorphous form or crystalline ordered materials; or alumina.
[0162] A third aspect of the present application relates to an alkyl aluminum of formula (III):
Al(R.sup.1).sub.3-n(R.sup.3).sub.n (III)
where
[0163] R.sup.1 is independently selected at each occurrence thereof from the group consisting of H, aryl, C.sub.1-C.sub.8 alkyl, and C.sub.1-C.sub.8 alkoxy;
[0164] R.sup.3 is independently selected at each occurrence thereof from C.sub.12-C.sub.60 alkyls; and
[0165] n is an integer ranging from one to three.
[0166] In some embodiments of the process of the present application, the aluminum alkyl compounds of formula (III) possess an R.sup.3 alkyl having anywhere from about 12, 15, 20, 25, 30, 35, 40, 45, 50, or 55 carbons to 20, 25, 30, 35, 40, 45, 50, 55, or 60 carbons. Some examples of the R.sup.3 groups include, but are not limited to, C.sub.12-C.sub.45 alkyls and C.sub.12-C.sub.38 alkyls.
[0167] In a further embodiment of the process of the present application, the shorter alkanes, carboxylic acids, alcohols, alkyl halides, or aldehydes formed have 12 to 60 carbons. For example, the shorter alkanes, carboxylic acids, alcohols, alkyl halides, or aldehydes have may have from about 12, 15, 20, 25, 30, 35, 40, 45, 50, or 55 carbons to 20, 25, 30, 35, 40, 45, 50, 55, or 60 carbons. In one embodiment, the number of carbons of the shorter alkanes, carboxylic acids, alcohols, alkyl halides, or aldehydes range from 12 to 45. In a further embodiment, the shorter alkanes, carboxylic acids, alcohols, alkyl halides, or aldehydes have 12 to 38 carbons.
[0168] In some embodiments of the process of the present application, when the contacting step is carried out under conditions effective to form shorter alcohols and alkyl halides, the shorter alcohols and alkyl halides formed are primary alcohols and alkyl halides, respectively. The process of making the shorter alcohols involves quenching the alkylaluminum species that forms in the reaction mixture with oxygen. The alkyl halides are formed upon quenching the alkylaluminum species with a halide. These process are discussed further infra.
[0169] In a further embodiment of the process of the present application, the polymers, oligomers, or mixtures thereof are polyolefins.
[0170] A wide variety of polyolefins (which may or may not have pendant unsaturation) are contemplated for use in the process of the present application. Examples of polyolefins include olefin homopolymers, copolymers, and terpolymers, such as, but not limited to, polyethylene (e.g., high density polyethylene, low density polyethylene, linear low density polyethylene), polyethylene with 1-octene, polypropylene (e.g.,), polyethylene-polypropylene-copolymers, polystyrene, polymers containing two or more monomers, polyisobutene, polymethacrylates, polyalkylstyrenes, partially hydrogenated polyolefins of butadiene and styrene and copolymers of isoprene, such as polymers of styrene and isoprene, and mixtures thereof. EPDM (ethylene/propylene/diene monomer) polymers, ethylene-propylene octene terpolymers and ethylene-propylene ENB terpolymers, are also contemplated for use.
[0171] The term “copolymer” refers to a polymer derived from more than one species of monomer.
[0172] The term “random copolymer” or “random polymer”, also known as “statistical copolymers”, refers to a copolymer in which there is no definite order for the sequence of the different building blocks (-M1M2M1M1M2M1M2M2-, wherein M1 and M2 represent different monomers).
[0173] The term “block copolymer” or “block polymer” refers to a macromolecule consisting of long sequences of different repeat units. Exemplary block polymers include, but are not limited to AnBm, AnBmAm, AnBmCk, or AnBmCkAn, wherein A, B, and C represent the different monomers, and n, m, and k are the number of monomers present in each block.
[0174] The term “pendant functional group,” as used herein refers to a functional group that is a pendant branch from the backbone of a co-polymer. The term “backbone,” “backbone chain,” or “main chain,” as used herein, refers to the linear chain to which all other chains, long or short or both, may be regarded as being pendant. The backbone chain or main chain of a polymer may be the series of covalently bonded atoms that together create the continuous chain of the molecule.
[0175] The copolymers useful in the present application may be selected from random copolymers, or block copolymers. The polymers and or oligomers may have pendent functional groups, which may include, for example, branching alkyl chains.
[0176] In one embodiment of the process of the present application, the contacting of the polymers, oligomers, or mixtures thereof with the compounds of formula (I) in the presence of a catalyst, forming a reaction mixture, is carried out at a temperature sufficient to melt the polymers, oligomers, or mixtures thereof.
[0177] The temperature required to melt the polymers, oligomers, or mixtures thereof is dependent on the polymer, oligomer, or mixture used. The methods for determination of the melting temperature of the polymer, oligomer, or mixture used is known in the art, and common polymeric materials have known melting temperature ranges. Exemplary temperatures that may be used in the method of the present application range from 100° C., 110° C., 120° C., 130° C., 140° C., 150° C., 160° C., 170° C., 180° C., 190° C., 200° C., 210° C., 220° C., 230° C. or 240° C., to 110° C., 120° C., 130° C., 140° C., 150° C., 160° C., 170° C., 180° C., 190° C., 200° C., 210° C., 220° C., 230° C., 240° C. or 250° C. For example, a temperature ranging from 150° C. to 250° C. may be used, however, higher or lower temperatures may also be of use.
[0178] In a further embodiment of the process of the present application, the molar ratio of the compound of formula (I) to the catalyst of formula (II) ranges from 3:1 to 20:1. The molar ratio of the polymers, oligomers, or mixtures thereof to the catalyst of formula (II) can range from 1:1 to 1:10.
[0179] In a further embodiment of the process of the present application, the contacting of the polymers, oligomers, or mixtures thereof with the compounds of formula (I) in the presence of a catalyst, forming a reaction mixture, is carried out while stirring under inert conditions. The contacting may be carried out under atmospheric pressure, or under a vacuum. Exemplary vacuum ranges include, but are not limited to pressures ranging from 760 mm Hg to 0.0001 mm Hg. Furthermore, the contacting may be carried out for a time period of 1 to 72 hours.
[0180] In one embodiment of the process of the present application, the contacting of the polymers, oligomers, or mixtures thereof with the compounds of formula (I) in the presence of a catalyst, forming a reaction mixture, is carried out under conditions effective to form shorter alkanes. These conditions include adding an alcohol or water to the reaction mixture to form the shorter alkanes. Exemplary alcohols that may be used in the formation of the shorter alkanes include, but are not limited to, methanol, ethanol, isopropanol, propanol, butanol, and isobutanol.
[0181] In another embodiment of the process of the present application, the contacting of the polymers, oligomers, or mixtures thereof with the compounds of formula (I) in the presence of a catalyst, forming a reaction mixture, is carried out under conditions effective to form shorter carboxylic acids. These conditions include adding carbon dioxide to the reaction mixture to form the shorter carboxylic acids.
[0182] The carboxylic acids formed from the process of the present application may be further converted via known reaction conditions to form esters, and amides. For example, in one embodiment of the process of the present application, the shorter carboxylic acids may be reacted with an alcohol and, optionally, an acid to form esters.
[0183] The term “ester group” generally refers to a substituent of the general formula —C(O)O—R.sup.1, where R.sup.1 may be either aliphatic or aromatic.
[0184] A proven and widely used method for preparing esters is the condensation of carboxylic acids with alcohols in the presence of catalysts. It is known that esters can be carried out autocatalytically or with catalysis, for example by Brønsted acids or by Lewis acids. Processes of this type are described in Lorz et al., “Phthalic Acid and Derivatives,” Ullmann's Encyclopedia of Industrial Chemistry, p 131-180 (2007), which is hereby incorporated by reference in its entirety.
[0185] In the process of esterification, the reaction mixture of the carboxylic acid and alcohol is usually heated for several hours and the water that is formed is removed. Methods are also known in which the esterification is carried out in a closed system under pressure and high temperatures. For example, WO 2007/126166 discloses a conventionally thermal esterification of fatty acids with alcohols at temperatures of from 200 to 350° C. and pressures of up to 10 bar. During the reaction over several hours, water formed in the reaction is continuously removed with excess alcohol. Some examples of the formation of esters from carboxylic acids are disclosed in U.S. Pat. No. 10,106,486 to Keller et al.; U.S. Pat. No. 7,186,856 to Meng et al.; and U.S. Pat. No. 8,293,935 to Orjueal et al, which are hereby incorporated by reference in their entirety. A further example of esters formed from the condensation reaction of carboxylic acids with alcohols is disclosed in Amore et al., Macromol. Rapid Commun, 28(4):473-477 (2007), which is hereby incorporated by reference in its entirety. Amore teaches a microwave-assisted method for producing propionic esters, in which the esterification is completed by water removal.
[0186] The carboxylic acid product of the present application may also undergo a condensation reaction with an amine to form an amide. As used herein, an “amine group” has the general formula NRR, where each R is independently a hydrogen, any alkyl or aryl group. The terms “carboxamide” or “amide” as used herein refer to C(O)NR.sub.aR.sub.b wherein R.sub.a and R.sub.b are each independently hydrogen, alkyl, or any other suitable substituent. One embodiment of the process of the present application includes reacting an amine with the shorter carboxylic acids to form amides. Optionally, coupling agents may be added to aid in the formation of the amides.
[0187] This reaction is well known in the art. The direct conversion of carboxylic acids and amines to form amides can be difficult due to the basic amine deprotonating the carboxylic acid thus forming a carboxylate. However, heating the ammonium carboxylate and the removing the water that is formed can push the reaction forward to form the amide (Lundberg et al., “Catalytic Amide Formation from Non-activated Carboxylic Acids and Amines,” Chem. Soc. Rev. 1-29 (2014), which is hereby incorporated by reference in its entirety). More commonly coupling agents are used to activate the carboxylic acid. Some common coupling agent that may be used in the present application include, for example, dicyclohexyl carbodiimide (DCC), N,N′-carbonyldiimidazole (CDI), N-ethyloxycarbonyl-2-ethyloxy-1,2-dihydroquinoline (EEDQ), N-isobutyloxy-carbonyl-2-isobutyloxy-1,2-dihydroquinoline (IIDQ), 1-Ethyl-3-(3-dimethylaminopropyl)carbodiimide (EDC) or benzotriazol-1-yl-oxy-tris-pyrrolidinophosphonium hexafluorophosphate (commercially available as PyBOP® (Novabiochem, a division of Merck KGaA, Darmstadt, Germany)). In some cases the reactions can be conducted in the presence of a base, for example a trialkylamine such as triethylamine or diisopropylethylamine, N-methylmorpholine, N-methylpyrrolidine, 4-DMAP or 1,8-diazabicycle[5.4.0]undec-7-ene (DBU). The coupling reactions preferably are conducted in an inert solvent, such as halogenated hydrocarbons, e.g. dichloromethane, chloroform, dipolar aprotic solvents such as acetonitrile, dimethylformamide, dimethylacetamide, DMSO, HMPT, and ethers such as tetrahydrofuran (THF). Exemplary amide formation reactions are disclosed in U.S. Pat. No. 7,705,025 to Finley et al.; U.S. Pat. No. 9,309,252 to Brian et al.; U.S. Pat. No. 7,820,821 to Mjalli et al.; U.S. Pat. No. 8,012,939 to Simmen et al.; and 9663519 to Charrier at el., which are hereby incorporated by reference in their entirety.
[0188] In another embodiment of the process of the present application, the contacting of the polymers, oligomers, or mixtures thereof with the compounds of formula (I) in the presence of a catalyst, forming a reaction mixture, is carried out under conditions effective to form shorter alcohols. These conditions include adding oxygen to the reaction mixture to form the shorter alcohols.
[0189] The shorter alcohols (e.g., fatty alcohols) of the present application may be further oxidized to form aldehydes, as is known in the art. In general, alcohol oxidation to an aldehyde is accomplished using a weak oxidizer. Examples of oxidizing agents that may be used for the conversion of the fatty alcohols to fatty aldehydes include, but are not limited to the Swern oxidation (oxalyl chloride, DMSO and trimethylamine), the Collins reagent (complex of chromium(VI) oxide with pyridine), pyridinium chlorochromate (PCC), and Dess-Martin Periodinane (DMP). These reactions are common place in the art and are disclosed in U.S. Pat. No. 7,951,958 to Brodney et al.; U.S. Pat. No. 9,145,410 to Hays et al.; U.S. Pat. No. 8,580,831 to Bur et al.; U.S. Pat. No. 7,915,271 to Ali et al., which are hereby incorporated by reference in their entirety.
[0190] In a further embodiment of the process of the present application, the contacting of the polymers, oligomers, or mixtures thereof with the compounds of formula (I) in the presence of a catalyst, forming a reaction mixture, is carried out under conditions effective to form shorter alkyl halides. These conditions include adding a halogen to the reaction mixture to form the shorter alkyl halides. The halogen may be dissolved in a solvent to aid addition. Exemplary solvents useful for halogen addition include, but are not limited to, dichloromethane, chloroform, toluene, and benzene.
[0191] The shorter alkyl halides of the present application may be reacted with an alkoxide to form an ether. As used herein, an “ether group” generally refers to a compound in which an oxygen atom is bonded to two alkyl or two aryl groups, or one alkyl and one aryl group.
[0192] The formation of an ether from an alkyl halide using an alkoxide is known in the art. The most commonly used method for the preparation of symmetrical and unsymmetrical ethers is the Williamson synthesis, involving a halide and an alkoxide. The reaction involves an S.sub.N2 reaction in which an alkoxide ion replaces a halogen, sulfonyl or a sulfate group, however, usually, alkyl halides are used. The alkoxide can be prepared by the reaction of the corresponding alcohol with an active metal such as metallic sodium or a metal hydride like NaH acting upon the alcohol. The resulting alkoxide salt is then reacted with the alkyl halide (sulfonate or sulfate) to produce the ether in an SN2 reaction. These reactions are common place in the art and are disclosed in U.S. Pat. No. 8,143,325 to Bezwada; U.S. Pat. No. 5,446,210 to Hees et al.; 10,111,422 and 6,811,703 to Elliott, which are hereby incorporated by reference in their entirety.
[0193] In another embodiment of the process of the present application, the contacting of the polymers, oligomers, or mixtures thereof with the compounds of formula (I) in the presence of a catalyst, forming a reaction mixture, is carried out under conditions effective to form shorter aldehydes. These conditions include adding an orthoester to the reaction mixture to form the shorter aldehydes. As used herein, an “orthoester” refers to compound in which three alkoxy groups are attached to one carbon atom, i.e. having the general formula RC(OR′).sub.3.
[0194] The environmental, economic, and health impacts of the plastic waste crisis motivate the design and study of new chemistries that enable efficient upcycling of polymers into versatile, value-added intermediates. A new catalytic strategy for transforming single-use polyolefin waste via reactive hydrocarbylaluminum intermediates into functionalized aliphatic chains, such as fatty alcohols and acids is reported herein. Earth-abundant zirconium surface sites catalyze the deconstruction of polyolefins under mild (<200° C.), solvent-free conditions via C—H bond activation, β-alkyl elimination for carbon-carbon bond cleavage, and aluminum-carbon bond formation for functionalization. Catalytic efficiency and selectivity are governed by the activation of surface-supported zirconium precatalysts, which become most effective in the presence of aluminum reagents capable of generating zirconium hydrides.
[0195] Intermediate length chain alkylaluminum species are high among desirable targets for polymer deconstruction processes because these organometallics, conventionally synthesized using the Ziegler process, can be converted into fatty alcohols and acids through established methods (Ziegler et al., “Metallorganische Verbindungen, XL Synthese von Alkoholen aus Organoaluminium-Verbindungen,” Liebigs Ann. Chem. 629:241-250 (1960); Ziegler et al., “Metallorganische Verbindungen, XLI Reaktionen der Aluminiumtrialkyle mit Kohlendioxyd und Schwefeldioxyd,” Liebigs Ann. Chem. 629:251-256 (1960), which are hereby incorporated by reference in their entirety). The heteroatom-functionalized species are biodegradable and, if produced from discarded polyolefins, would provide an environmentally friendly end-of-life for some plastics. In addition, the hydrido or organoaluminum reagents to be employed in such transformations are further advantaged because aluminum is widely available as the most abundant metal (8.2%, as an oxide) in the earth's crust, and it is readily converted (or recycled) from its oxide to metal to organoaluminum species in atom-economical, optimized processes performed on large scale (Sanders Jr, R. E., “Aluminum and Aluminum Alloys.” Kirk-Othmer Encyclopedia of Chemical Technology, 1-64 (2012), which is hereby incorporated by reference in its entirety).
[0196] The present application discloses that organotransition-metal species, generated as catalytic intermediates by cleavage of C—C bonds in saturated hydrocarbons, could undergo metathetical exchange with organo- or hydridoaluminum species, to create the new intermediate length-chain hydrocarbyl-aluminum species. Such alkyl group metathetical steps are established as part of processes such as carboalumination and hydroalumination of alkenes (Xu and Negishi, “Zirconium-Catalyzed Asymmetric Carboalumination of Unactivated Terminal Alkenes,” Acc. Chem. Res. 49:2158-2168 (2016); Camara et al, “Zirconium-Catalyzed Carboalumination of α-Olefins and Chain Growth of Aluminum Alkyls: Kinetics and Mechanism,” J. Am. Chem. Soc. 133:5263-5273 (2011), which are hereby incorporated by reference in their entirety) and as chain-transfer steps in chain-shuttling block co-polymerizations of ethylene and α-olefins (Arriola et al., “Catalytic Production of Olefin Block Copolymers via Chain Shuttling Polymerization,”Science 312:714-718 (2006), which is hereby incorporated by reference in its entirety). These processes commonly engage organozirconium catalysts. Moreover, coordinatively unsaturated zirconium sites are known to break C—C bonds by β-alkyl elimination (O'Reilly et al., “β-Alkyl Elimination: Fundamental Principles and Some Applications,” Chem. Rev. 116:8105-8145 (2016), which is hereby incorporated by reference in its entirety). The related β-allyl elimination and organozirconium/hydridoaluminum exchange are proposed in polybutadiene deconstruction and alumination, catalyzed by Cp.sub.2ZrHCl (Schwartz's reagent), which attaches to the chain by hydrozirconation rather than C—H bond metalation (Zheng et al., “Controlled Chain-Scission of Polybutadiene by the Schwartz Hydrozirconation,” Chem. Eur. J. 19:541-548 (2013), which is hereby incorporated by reference in its entirety).
[0197] Herein is reported the catalytic C—C bond alumination of sp.sup.3-hybridized carbon in aliphatic hydrocarbons, leveraging C—H bond activation and β-alkyl elimination steps of surface organometallic zirconium chemistry (Corker et al., “Catalytic Cleavage of the C—H and C—C Bonds of Alkanes by Surface Organometallic Chemistry: An EXAFS and IR Characterization of a Zr—H Catalyst,”Science 271:966-969 (1996); Zakharov et al., “Formation of Zirconium Hydrides in Supported Organozirconium Catalysts and Their Role in Ethylene Polymerization,” J Mol. Catal. 2:421-435 (1977); Yermakovt et al., “Hydride Complexes of Titanium and Zirconium Attached to SiO.sub.2 as Hydrogenation Catalysts,” J. Mol. Catal. 49:121-132 (1989); Schwartz and Ward, “Silica-supported Zirconium Hydrides as Isomerization or Hydrogenation Catalysts for Long-chain Olefins,” J. Mol. Catal. 8:465-469 (1980); Pasha et al., “C—H and C—C Activation of n-Butane with Zirconium Hydrides Supported on SBA15 Containing N-Donor Ligands: [(≡SiNH—)(≡SiX—)ZrH2], [(≡SiNH—)(≡SiX—)2ZrH], and [(≡SiN═)(≡SiX—)ZrH] (X=—NH—, —O—). A DFT Study,” Organometallics 33:3320-3327 (2014); Rataboul et al., “Molecular Understanding of the Formation of Surface Zirconium Hydrides upon Thermal Treatment under Hydrogen of [(SiO)Zr(CH2tBu).sub.3] by Using Advanced Solid-State NMR Techniques,” J. Am. Chem. Soc. 126:12541-12550 (2004); Wang et al., “Preparation and Characterization of Zirconium Containing Mesoporous Silicas. II. Grafting Reaction of Tetraneopentyl Zirconium on MCM-41 and Characterization of the Grafted Species and of the Resulting Materials,” Microporous Mesoporous Mater. 66:169-179 (2003); Quignard et al., “Surface Organometallic Chemistry of Zirconium: Application to the Stoichiometric Activation of the CH Bonds of Alkanes and to the Low-temperature Catalytic Hydrogenolysis of Alkanes,” J. Mol. Catal. 74:353-363 (1992); Casty et al., “Hydrogen/Deuterium Exchange Kinetics by a Silica-Supported Zirconium Hydride Catalyst: Evidence for a σ-Bond Metathesis Mechanism,” Organometallics 20:2246-2249 (2001), which are hereby incorporated by reference in their entirety). The studies of the present application have focused on identifying effective catalysts and aluminum reagents, as well as understanding their effects upon the elementary steps involved reactions through conversions of polyethylene into fatty aliphatic alkylaluminum species.
[0198] Typical chemical synthesis constructs large, intricate products from smaller building blocks. Yet, naturally occurring resources often contain pre-assembled molecular components, which nonetheless are not directly suitable for conventional routes to desired products. Thus, sustainable conversions would be advanced by efficient catalytic methods that restructure the carbon-based skeletons of molecules and install functional groups.
[0199] The present application reports a conversion in which long hydrocarbon chains of polymers are broken into shorter units with the introduction of aluminum end groups. These green organoaluminum species are easily derivatized into biodegradable fatty alcohols, carboxylic acids, or halides, providing high-value, end-of-first-life applications for the catenated chains of single-use polyolefins.
[0200] Preferences and options for a given aspect, feature, embodiment, or parameter of the technology described herein should, unless the context indicates otherwise, be regarded as having been disclosed in combination with any and all preferences and options for all other aspects, features, embodiments, and parameters of the technology.
[0201] The following Examples are presented to illustrate various aspects of the present application, but are not intended to limit the scope of the claimed application.
EXAMPLES
Materials and Methods
Materials
[0202] All manipulations were carried out under inert conditions, either using Schlenk techniques or in a glovebox under a purified nitrogen atmosphere, unless stated otherwise. Dry and degassed solvents were used throughout. Pentane was sparged with nitrogen, passed through activated alumina columns, and stored under nitrogen. Benzene-d6 was degassed via three consecutive freeze-pump-thaw cycles, dried over Na/K alloy, vacuum transferred, and stored over molecular sieves under nitrogen. Tetrakisneopentyl zirconium (Davidson et al., “Silylmethyl and Related Complexes II. Preparation, Spectra, and Thermolysis of the Tetraneopentyls of Titanium, Zirconium, and Hafnium,” J Organomet. Chem. 57:269-277 (1973), which is hereby incorporated by reference in its entirety), dimethylaluminum hydride (Downs et al., “Dimethylalane, [Me.sub.2AlH]n, in the Vapor Phase and in Hydrocarbon Solution: Gas-Phase Electron Diffraction, Spectroscopic, Colligative, and ab Initio Studies,” Organometallics 19:527-538 (2000), which is hereby incorporated by reference in its entirety), triphenylaluminum (Lehmkuhl and Ziegler, “Metallorganische Verbindungen: Al, Ga, In, Tl,” vol. XIII/4, Bahr Eds., Stuttgart: Georg Thieme Verlag, (1970), which is hereby incorporated by reference in its enitrety), and alane (Finholt et al., “Lithium Aluminum Hydride, Aluminum Hydride and Lithium Gallium Hydride, and Some of their Applications in Organic and Inorganic Chemistry,” J. Am. Chem. Soc. 69:1199-1203 (1947), which is hereby incorporated by reference in its entirety) were synthesized according to literature procedures. Trimethylaluminum, triethylaluminum, triisobutylaluminum, diisobutylaluminum hydride, high density polyethylene (HDPE, M.sub.n=6.2 kDa, M.sub.w=38.4 kDa, Ð=6.2), isotactic polypropylene (iPP, M.sub.n=36.8 kDa, M.sub.w=117.6 kDa, Ð=3.2), and Al(NO.sub.3).sub.3.9H.sub.2O (98%) were purchased from Sigma-Aldrich and used as received. Na.sub.2SiO.sub.3.9H.sub.2O (98%), NH.sub.4NO.sub.3, and concentrated HCl were purchased from Fisher Scientific, and used as received. Fumed silica (Aerosil) of surface area 300 m.sup.2/g was purchased from Evonik, calcined and partially dehydroxylated at 550° C. for 12 h. Titration of the surface silanols in this material with Mg(CH.sub.2Ph).sub.2(O.sub.2C.sub.4H.sub.8).sub.2 revealed a surface OH loading of 0.46±0.05 mmol/g.
Methods
[0203] 1D .sup.1H and .sup.13C{.sup.1H}, and 2D .sup.1H-.sup.1H COSY, TOCSY and .sup.1H-.sup.13C HSQC NMR spectra were acquired on a Brucker NEO 400 MHz spectrometer. Fourier transform infrared (FT-IR) spectra and diffuse reflectance infrared Fourier transform (DRIFT) spectra were recorded on a Bruker VERTEX 80 IR spectrometer. Samples for transmission IR were diluted with KBr and pressed into a pellet using a hydraulic press. DRIFT spectra were collected using a Harrick Praying Mantis accessory and a sealed, ambient-pressure sample chamber consisting of a dome with ZnSe windows. Elemental analysis was performed using a Perkin-Elmer 2400 Series II CHN/S at the Iowa State Chemical Instrumentation Facility. Inductively Coupled Plasma-Optical Emission Spectroscopy (ICP-OES) was performed to measure the amount of zirconium present in the catalytic materials. The samples (2.0-4.0 mg each) were digested for 24 h in aqueous HF and aqua-regia (0.18% and 5% respectively) and analyzed in a Perkin Elmer Optima 2100 DV Inductively Coupled Plasma-Optical Emission Spectroscope.
[0204] MALDI-TOF Mass Spectrometry
[0205] MALDI-TOF-MS experiments were carried out on a Shimadzu AXIMA Confidence MALDI-TOF mass spectrometer, equipped with an N.sub.2 laser (337 nm, 25 Hz repetition rate). The mass spectra were acquired in the linear and positive ion mode. 100 laser pulses were utilized for each measurement.
[0206] Stock solutions of products were prepared in tetrahydrofuran at a 0.5 mg/mL concentration, and a stock solution of silver nitrate was prepared in a 1:1 (v:v) mixture of tetrahydrofuran and acetonitrile at a concentration of 10 mg/mL. Final sample solutions for spotting were prepared by mixing equal volumes (0.2 mL) of stock solutions of alkanes and silver nitrate. The matrix (2,5-dihydroxybenzoic acid (DHB)) solution was prepared in a 3:2 (v:v) mixture of tetrahydrofuran and methanol at a 10 mg/mL concentration. The dried-droplet method of sample deposition was employed, where 0.5 μL of the sample solution was deposited on the stainless-steel sample plate, followed by 0.5 μL of the matrix solution. The solvents were allowed to evaporate by air-drying.
[0207] General Procedure for Catalytic Alumination of Polyolefins
[0208] In the glovebox, the polyolefin reactant, supported catalyst, and aluminum reagent were loaded into a glass tube equipped with a glass-encapsulated magnetic stirrer. The tube was which was sealed with a stainless steel UltraTorr fitting to a closed glass tube with a sidearm containing a re-sealable Teflon-glass valve. The vessel was heated in an aluminum block at the desired temperature (≥150° C. to ensure the polymer was above its melting point) for the required reaction time with mixing. The volatile components of the headspace were sampled and analyzed by GC-MS. After the appropriate time, the contents of the tube were quenched by passing dry air into the vessel through the sidearm for 1 h. The crude reaction mixture was extracted with CH.sub.2Cl.sub.2 (3×5 mL), and the volatile components were evaporated from the liquid to provide an oil which was further analyzed by spectroscopic and analytical techniques (NMR, IR, GC-MS, MALDI-TOF-MS). Yields of oils are given as a percentage of the starting polyolefin mass. The residual solid was dissolved in hot 1,2-dichlorobenzene and filtered to remove the catalyst. A solid crashed out from the filtrate upon cooling. The supernatant liquid was decanted, and the solid polymer was washed with CH.sub.2Cl.sub.2 (3×5 mL), dried in vacuo, and analyzed by IR spectroscopy.
Example 1—Preparation of Silica-Alumina (SiAlO.SUB.x.)
[0209] Silica-alumina was synthesized by a literature procedure (Yao et al., “A Novel Method to Synthesize Amorphous Silica-Alumina Materials with Mesoporous Distribution without Using Templates and Pore-Regulating Agents,” Chem. Mater. 14:122-129 (2002), which is hereby incorporated by reference in its entirety).
Example 2—Preparation of Zr(CH.SUB.2.CMe.SUB.3.).SUB.2.@SiAlO.SUB.x
[0210] Zr(CH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x was synthesized by a procedure adapted from reference (Wang et al., “Preparation and Characterization of Zirconium Containing Mesoporous Silicas. II. Grafting Reaction of Tetraneopentyl Zirconium on MCM-41 and Characterization of the Grafted Species and of the Resulting Materials,” Microporous Mesoporous Mater 66:169-179 (2003), which is hereby incorporated by reference in its entirety). In the glovebox, 0.30 g of Zr(CH.sub.2CMe.sub.3).sub.4 (0.8 mmol) was dissolved in anhydrous pentane (7 mL). This solution was added to a suspension of silica-alumina (1.00 g) in pentane (7 mL), and the resulting suspension was stirred at room temperature for 4 h. The suspension was allowed to settle, and the supernatant liquid was decanted. The residual solid was washed with pentane (3×5 mL) and dried overnight in vacuo to afford an off-white powder (0.92 g). This material contains 2.2±0.2 CH.sub.2CMe.sub.3 groups per Zr center, as determined by titration of Zr(CH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x with CH.sub.3OH and ICP-OES (2.7 wt % Zr, 0.30 mmol Zr/g). Solid-state .sup.13C NMR spectra and infrared spectra match reported literature values (Eedugurala et al., “Mesoporous Silica-Supported Amidozirconium-Catalyzed Carbonyl Hydroboration,” ACS Catal. 5:7399-7414 (2015), which is hereby incorporated by reference in its entirety). .sup.13C NMR (CP-MAS, 400 MHz): δ 94.78 (CH.sub.2CMe.sub.3), 32.88 (CH.sub.2CMe.sub.3). IR (DRIFTs, cm.sup.−1): 2959, 2907, 2872, 1478, 1398, 1366, 1205, 843 (
Example 3—Preparation of Zr(CH.SUB.2.CMe.SUB.3.).SUB.2.@SiO.SUB.2
[0211] Zr(CH.sub.2CMe.sub.3).sub.2@SiO.sub.2 was synthesized by a procedure adapted from reference (Wang et al., “Preparation and Characterization of Zirconium Containing Mesoporous Silicas. II. Grafting Reaction of Tetraneopentyl Zirconium on MCM-41 and Characterization of the Grafted Species and of the Resulting Materials,” Microporous Mesoporous Mater 66:169-179 (2003), which is hereby incorporated by reference in its entirety) and is compared to the reported material in reference Quignard et al., “Surface Organometallic Chemistry: Synthesis and Characterization of a Tris(neopentyl)zirconium(IV) Complex Grafted to the Surface of a Partially Dehydroxylated Silica,” Inorg. Chem. 31:928-930 (1992), and Rataboul et al., “Molecular Understanding of the Formation of Surface Zirconium Hydrides upon Thermal Treatment under Hydrogen of [(SiO)Zr(CH.sub.2tBu).sub.3] by Using Advanced Solid-State NMR Techniques,” J Am. Chem. Soc. 126:12541-12550 (2004), which are hereby incorporated by reference in their entirety. In the glovebox, 0.30 g of Zr(CH.sub.2CMe.sub.3).sub.4 (0.8 mmol) was dissolved in anhydrous pentane (7 mL). This solution was added to a suspension of Aerosil (1.00 g) in pentane (7 mL), and the resulting mixture was stirred at room temperature for 4 h. The suspension was allowed to settle, and the supernatant liquid was decanted. The residual solid was washed with pentane (3×5 mL) and dried overnight in vacuo to afford an off-white powder (0.98 g). This material contained 2.1±0.2 CH.sub.2CMe.sub.3 groups per Zr center, as revealed by titration of Zr(CH.sub.2CMe.sub.3).sub.2@SiO.sub.2 with CH.sub.3OH and ICP-OES (3.51 wt % Zr, 0.38 mmol Zr/g). IR (DRIFTs, cm.sup.−1): 2957, 2866, 1468, 1363, 1214, 1185, 1173, 1145, 823 (
Example 4—HDPE+Zr(CH.SUB.2.CMe.SUB.3.).SUB.2.@SiAlO.SUB.x.+AliBu.SUB.3 .(150° C.), (Table 1, Entry 1)
[0212] HDPE (0.63 g), Zr(CH.sub.2CMe.sub.3).sub.3@SiAlO.sub.x (0.10 g, 0.030 mmol Zr) and AliBu.sub.3 (60 μL, 0.24 mmol) were allowed to react at 150° C. for 12 h to provide an oil (0.19 g, 31%) which was characterized by NMR, IR, and MALDI, and residual HDPE (0.44 g). MALDI-TOF-MS revealed a bimodal distribution, with maxima at C.sub.39H.sub.79OH and C.sub.54H.sub.109OH.
Example 5—HDPE+Zr(CH.SUB.2.CMe.SUB.3.).SUB.2.@SiAlO.SUB.x.+AliBu.SUB.3 .(200° C.), (Table 1, Entry 2)
[0213] HDPE (1.00 g), Zr(CH.sub.2CMe.sub.3).sub.3@SiAlO.sub.x (0.13 g, 0.039 mmol Zr) and AliBu.sub.3 (100 μL, 0.40 mmol) were allowed to react at 200° C. for 12 h to provide an oil (0.40 g, 40%) and residual HDPE (0.50 g). Experiments with doubled initial catalyst and AliBu.sub.3 loading with respect to polyethylene (10.5 g HDPE/mmol Zr) also gave the oil in 40% yield after 12 h at 200° C. However, two portions of Zr(CH.sub.2CMe.sub.3).sub.3@SiAlO.sub.x and AliBu.sub.3, added initially and after 12 h gave 72% total yield of oil (C.sub.32˜C.sub.44 alcohol distribution).
Example 6—HDPE+Zr(CH.SUB.2.CMe.SUB.3.).SUB.2.@SiAlO.SUB.x.+AliBu.SUB.3 .(Zr Catalyst/AliBu.SUB.3 .Added in 3 Portions) (Table 1, Entry 3)
[0214] HDPE (1.00 g), Zr(CH.sub.2CMe.sub.3).sub.3@SiAlO.sub.x (0.11 g, 0.033 mmol Zr) and AliBu.sub.3 (120 μL, 0.48 mmol) were allowed to react at 200° C. for 12 h. The reaction tube was cooled to room temperature and additional (same as before) portions of Zr(CH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x and AliBu.sub.3 were added. The mixture was heated at 200° C. for 12 h. This procedure was repeated once more (after a total of 36 h) to provide an oil (0.84 g, 84%), and no visible polyethylene was remaining.
Example 7—HDPE+Zr(CH.SUB.2.CMe.SUB.3.).SUB.2.@SiAlO.SUB.x.+AliBu.SUB.3 .(Quenched with MeOH) (Table 1, Entry 4)
[0215] HDPE (1.00 g), Zr(CH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x (0.11 g, 0.033 mmol Zr) and AliBu.sub.3 (100 μL, 0.40 mmol) were allowed to react at 200° C. for 12 h. The reaction tube was cooled to room temperature, and degassed MeOH (3 mL) was added. After 30 min, the solvent was removed under reduced pressure and the residue was extracted with CH.sub.2C.sub.2 (3×5 mL) to provide an oil (0.38 g, 38%) and residual HDPE (0.64 g).
Example 8—HDPE+Zr(CH.SUB.2.CMe.SUB.3.).SUB.2.@SiAlO.SUB.x.+AliBu.SUB.3 .(Quenched with 12) (Table 1, Entry 5)
[0216] HDPE (0.54 g), Zr(CH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x (0.06 g, 0.019 mmol Zr) and AliBu.sub.3 (50 μL, 0.20 mmol) were allowed to react at 200° C. for 12 h. The reaction tube was cooled to room temperature and I.sub.2 (0.06 g, 0.23 mmol) in anhydrous and degassed CH.sub.2C.sub.2 (5 mL) was added. After 30 min, the solvent was removed under reduced pressure, and the residue was extracted with CH.sub.2C.sub.2 (3×5 mL) to provide an oil (0.23 g, 43%) and residual HDPE (0.32 g).
Example 9—HDPE+Zr(CH.SUB.2.CMe.SUB.3.).SUB.2.@SiAlO.SUB.x.+AliBu.SUB.3 .(Quenched with CO.SUB.2.) (Table 1, Entry 6)
[0217] HDPE (0.55 g), Zr(CH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x (0.06 g, 0.019 mmol Zr) and AliBu.sub.3 (50 μL, 0.20 mmol) were allowed to react at 200° C. for 12 h. The reaction tube was cooled to room temperature and evacuated. Dry CO.sub.2 was introduced into the vessel, which was then heated to 60° C. After 4 h, the reaction mixture was exposed to air, and the residue was extracted with CH.sub.2Cl.sub.2 (3×5 mL) to provide an oil (0.20 g, 36%) and residual HDPE (0.36 g).
Example 10—HDPE+Zr(CH.SUB.2.CMe.SUB.3.).SUB.2.@SiAlO.SUB.x.+AlEt.SUB.3 .(150° C.) (Table 1, Entry 7)
[0218] HDPE (0.51 g), Zr(CH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x (0.10 g, 0.03 mmol Zr) and AlEt.sub.3 (50 μL, 0.36 mmol) were allowed to react at 150° C. for 12 h to provide an oil (0.13 g, 25%) and residual HDPE (0.41 g).
Example 11—HDPE+Zr(CH.SUB.2.CMe.SUB.3.).SUB.2.@SiAlO.SUB.x.+AlEt.SUB.3 .(200° C.) (Table 1, Entry 8)
[0219] HDPE (0.60 g), Zr(CH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x (0.10 g, 0.03 mmol Zr) and AlEt.sub.3 (50 μL, 0.36 mmol) were allowed to react at 200° C. for 12 h to provide an oil (0.15 g, 24%) and residual HDPE (0.45 g).
Example 12—HDPE+Zr(CH.SUB.2.CMe.SUB.3.).SUB.2.@SiAlO.SUB.x.+AlPh.SUB.3 .(Table 1, Entry 9)
[0220] HDPE (0.64 g), Zr(CH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x (0.07 g, 0.021 mmol Zr) and AlPh.sub.3 (66 mg, 0.26 mmol) were allowed to react at 200° C. for 12 h to provide an oil (0.19 g, 29%) and residual HDPE (0.49 g).
Example 13—HDPE+Zr(CH.SUB.2.CMe.SUB.3.).SUB.2.@SiAlO.SUB.x.+AlH.SUB.3 .(Table 1, Entry 10)
[0221] HDPE (0.52 g), Zr(CH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x (0.10 g, 0.03 mmol Zr) and AlH.sub.3 (28 mg, 0.93 mmol) were allowed to react at 200° C. for 12 h to provide an oil (0.22 g, 42%) and residual HDPE (0.28 g).
Example 14—HDPE+Zr(OCH.SUB.2.CMe.SUB.3.).SUB.2.@SiAlO.SUB.x.+AliBu.SUB.3 .(Table 1, Entry 11)
[0222] Zr(CH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x (0.07 g, 0.021 mmol Zr) was exposed to dry air for 10 min at room temperature to provide Zr(OCH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x. HDPE (0.60 g), Zr(OCH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x, and AliBu.sub.3 (100 μL, 0.40 mmol) were allowed to react at 200° C. for 12 h to provide an oil (0.21 g, 34%) and a residual polymeric solid (0.42 g).
Example 15—HDPE+Zr(OCH.SUB.2.CMe.SUB.3.).SUB.2.@SiAlO.SUB.x.+AlH.SUB.3 .(Table 1, Entry 12)
[0223] Zr(CH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x (0.05 g, 0.015 mmol Zr) was exposed to dry air for 10 min at room temperature to provide Zr(OCH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x. HDPE (0.35 g), Zr(OCH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x and AlH.sub.3 (28 mg, 0.93 mmol) were allowed to react at 200° C. for 12 h to provide an oil (0.17 g, 49%) and a residual polymeric solid (0.18 g).
Example 16—HDPE+Zr(CH.SUB.2.CMe.SUB.3.).SUB.2.@SiO.SUB.2.+AliBu.SUB.3 .(Table 1, Entry 13)
[0224] HDPE (1.00 g), Zr(CH.sub.2CMe.sub.3).sub.2@SiO.sub.2 (0.11 g, 0.042 mmol Zr) and AliBu.sub.3 (100 μL, 0.40 mmol) were allowed to react at 200° C. for 12 h to provide an oil (0.35 g, 35%) and a residual polymeric solid (0.54 g). Catalytic materials employing SiO.sub.2 as the support generated small amounts of alkylsilanes at 200° C., such as iBu.sub.2SiH.sub.2, Et.sub.2SiH.sub.2 and Et.sub.3SiH, as side products during catalysis, whereas such species were not detected in catalytic reactions of Zr(CH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x.
Example 17—HDPE+Zr(CH.SUB.2.CMe.SUB.3.).SUB.2.@SiO.SUB.2.+AlEt.SUB.3 .(Table 1, Entry 14)
[0225] HDPE (0.41 g), Zr(CH.sub.2CMe.sub.3).sub.2@SiO.sub.2 (0.05 g, 0.019 mmol Zr) and AlEt.sub.3 (50 μL, 0.36 mmol) were allowed to react at 200° C. for 12 h to provide an oil (0.13 g, 33%) and a residual solid (0.29 g).
Example 18—HDPE Grocery Bag+Zr(CH.SUB.2.CMe.SUB.3.).SUB.2.@SiAlO.SUB.x.+AliBu.SUB.3 .(Table 1, Entry 15)
[0226] HDPE from a plastic grocery bag (0.60 g), Zr(CH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x (0.10 g, 0.03 mmol Zr) and AliBu.sub.3 (100 μL, 0.40 mmol) were allowed to react at 200° C. for 12 h to provide an oil (0.19 g, 31%) and a residual polymeric solid (0.41 g).
Example 19—Isotactic Polypropylene+Zr(CH.SUB.2.CMe.SUB.3.).SUB.2.@SiAlO.SUB.x.+AliBu.SUB.3 .(Table 1, Entry 16)
[0227] Isotactic polypropylene (iPP) (1.00 g), Zr(CH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x (0.14 g, 0.042 mmol Zr) and AliBu.sub.3 (120 μL, 0.48 mmol) were allowed to react at 200° C. for 12 h to provide an oil (0.27 g, 27%) and a residual polymeric solid (0.74 g).
Example 20—HDPE+Zr(OCH.SUB.2.CMe.SUB.3.).SUB.2.@SiAlO.SUB.x.+AlH.SUB.3 .(Under Dynamic Vacuum) (Table 1, Entry 17)
[0228] Zr(CH.sub.2CMe.sub.3).sub.3@SiAlO.sub.x (0.12 g, 0.036 mmol Zr) was exposed to dry air for 10 min at room temperature to provide Zr(OCH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x. HDPE (0.85 g), Zr(OCH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x, and AlH.sub.3 (29 mg, 0.97 mmol) were allowed to react at 200° C. under dynamic vacuum for 12 h to provide an oil (0.51 g, 60%) and residual HDPE (0.30 g).
[0229] A summary of the experimental results of the Zr-catalyzed deconstruction of polyolefins from Examples 4-20 is presented in Table 1.
TABLE-US-00001 TABLE 1 Zr-catalyzed deconstruction of polyolefins into fatty alcohols, acids, iodides, or alkanes. Percentage of Polymer Oil yield functionalized entry.sup.a mass.sup.b (g) AlR.sub.3 Catalyst T (° C.) g (%).sup.c molecules 1 0.63 AliBu.sub.3 Zr(CH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x 150 0.19 (31%) 71 2 1.00 AliBu.sub.3 Zr(CH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x 200 0.40 (40%) 68 3 1.00.sup.d AliBu.sub.3 Zr(CH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x 200 0.84 (84%) 66 4 1.00.sup.e AliBu.sub.3 Zr(CH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x 200 0.38 (38%) NA 5 0.54.sup.f AliBu.sub.3 Zr(CH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x 200 0.23 (43%) 68 6 0.55.sup.g AliBu.sub.3 Zr(CH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x 200 0.20 (36%) 75 7 0.51 AlEt.sub.3 Zr(CH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x 150 0.13 (25%) 39 8 0.60 AlEt.sub.3 Zr(CH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x 200 0.15 (24%) 54 9 0.64 AlPh.sub.3 Zr(CH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x 200 0.19 (29%) 66 10 0.52 AlH.sub.3 Zr(CH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x 200 0.22 (42%) 89 11 0.60 AliBu.sub.3 Zr(OCH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x 200 0.21 (34%) 51 12 0.35 AlH.sub.3 Zr(OCH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x 200 0.17 (49%) 62 13 1.00 AliBu.sub.3 Zr(CH.sub.2CMe.sub.3).sub.2@SiO.sub.2 200 0.35 (35%) 85 14 0.41 AlEt.sub.3 Zr(CH.sub.2CMe.sub.3).sub.2@SiO.sub.2 200 0.13 (33%) 82 15 0.60.sup.h AliBu.sub.3 Zr(CH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x 200 0.19 (31%) 60 16 1.00.sup.i AliBu.sub.3 Zr(CH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x 200 0.27 (27%) NA 17 0.85.sup.j AlH.sub.3 Zr(OCH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x 200 0.51 (60%) 67 .sup.aStandard conditions: 21 kg HDPE/mol Zr, Al:Zr = 10:1, 150-200° C., 12 h, followed by O.sub.2 quench to give fatty alcohols. .sup.bHDPE: M.sub.n = 6.2 kDa, M.sub.w = 38.6 kDa, Ð = 6.2. .sup.cyield = mass of oil/mass of PO. .sup.d3 portions of Zr(CH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x/AliBu.sub.3 were added over 36 h. .sup.eQuenched with MeOH to give saturated hydrocarbon products. .sup.fQuenched with I.sub.2 to provide long chain alkyl iodides. .sup.gQuenched with CO.sub.2 to form fatty acids. .sup.hpost-consumer HDPE: M.sub.n = 5.3 kDa, M.sub.w = 10.5 kDa, Ð = 19.8. .sup.iiPP: M.sub.n = 37.4 kDa, M.sub.w = 117.6 kDa, Ð = 3.2. Quantitative estimation of functional group analysis of the product is not possible due to quaternary carbon centers. .sup.jPerformed under dynamic vacuum
Example 21—DRIFT IR Experiments on Putative ZrH Surface Species
[0230] Generation of ZrH@SiAlO.sub.x and H/D Exchange Experiments
[0231] Zr(CH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x (0.4 g, 0.12 mmol Zr) and Excess AliBu.sub.3 (0.5 mL, 1.98 mmol) were added in a glass tube in the glovebox, which was sealed with an UltraTorr fitting to a closed glass tube adapted with a sidearm containing a re-sealable Teflon-glass valve. The sealed vessel was transferred from the glovebox and attached to a Schlenk line. The reactor inserted into an aluminum block and heated at 150° C. for 2 h. The reactor was then cooled to room temperature, evacuated, taken back into the glovebox, washed with anhydrous pentane (3×2 mL) and dried in vacuo to provide a brown powder, which was sampled and analyzed by DRIFT IR spectroscopy (
[0232] The spectrum in
[0233] In a second experiment, Zr(CH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x and 3 equiv. of AliBu.sub.3 were allowed to react at room temperature in benzene-d.sub.6, and the soluble portion of the reaction mixture was analyzed by .sup.1H NMR spectroscopy (
[0234] Experiments Ruling Out Ethylene Oligomerization as Route to Fatty Alcohols
[0235] As alternative pathway to fatty aluminum species, terminal polymerylzirconium species, formed by metalation of chain ends or by β-alkyl elimination, could also react by β-alkyl elimination to generate ethylene. This thermodynamically unfavorable step, the microscopic reverse of ethylene insertion during polymerization, could be coupled to an exothermic catalytic ethylene oligomerization that provides the medium length chains of the alkyl aluminum or alkane products (
Discussion of Examples
[0236] The first experiments employed Zr(CH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x (2.7 wt % Zr, 0.30 mmol Zr/g), which was prepared by grafting Zr(CH.sub.2CMe.sub.3).sub.4 onto partially dehydroxylated silica-alumina (0.38 mmol SiOH/g, 9.3 wt % Al) in pentane (Quignard et al., “Surface Organometallic Chemistry: Synthesis and Characterization of a Tris(neopentyl)zirconium(IV) Complex Grafted to the Surface of a Partially Dehydroxylated Silica,” Inorg. Chem. 31:928-930 (1992); Wang et al., “Preparation and Characterization of Zirconium Containing Mesoporous Silicas. II. Grafting Reaction of Tetraneopentyl Zirconium on MCM-41 and Characterization of the Grafted Species and of the Resulting Materials,” Microporous Mesoporous Mater 66:169-179 (2003); Tosin et al., “Reactivity of Tetraneopentylhafnium, Hf(CH.sub.2tBu).sub.4, with Silica Surfaces,” Organometallics 25:3324-3335 (2006), which are hereby incorporated by reference in their entirety). HDPE and AliBu.sub.3 react in the presence of this precatalyst over 12 h at 150° C. to give, after quenching with O.sub.2 and workup, an oil containing fatty alcohols and alkanes (31% yield by mass; Scheme 1; Table 1, entry 1).
##STR00002##
[0237] Under the reaction conditions, the HDPE is melted and mixed by magnetic stirring. The isolated reaction products were analyzed by infrared (IR) and NMR spectroscopy, matrix assisted laser desorption ionization-time of flight-mass spectrometry (MALDI-TOF-MS), and gas chromatography (GC)-MS. In the product analysis, detected fatty alcohols correspond to the alkylaluminum species and any active alkylzirconium sites present in the reaction mixture, prior to quenching with O.sub.2, whereas functional group-free hydrocarbons are formed prior to quenching.
[0238] First, an IR spectrum of the isolated oil revealed broad signals at 3430 and 1090 cm.sup.−1, characteristic of v.sub.O—H and v.sub.C—O (
#FG=2+#CH−#CH.sub.3 (1)
Using integration of the assigned .sup.1H NMR spectrum, the fact that all alcohols are terminal, and assuming that CMe.sub.2 groups are insignificant and cyclic species have not formed, this oil contains a mixture 7:3 ratio of monoalcohol:alkane.
[0239] The oil was further analyzed by MALDI-TOF-MS, which detected functionalized chains from C.sub.35H.sub.71OH up to C.sub.64H.sub.129OH directly and aliphatic hydrocarbons as Ag.sup.+ adducts (see
[0240] At 200° C., the Zr(CH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x-catalyzed reaction of HDPE and 10 equiv. of AliBu.sub.3 gives a higher yield of oils (40%, Table 1, entry 2) after 12 h. A MALDI-TOF-MS revealed shorter chains (a C.sub.34-centered distribution) compared to the products from the experiment at 150° C. Essentially identical yields are obtained after 24 h of continuous heating or upon addition of a second portion of AliBu.sub.3 after 12 h, suggesting that the zirconium catalyst deactivates during the first portion of the reaction. Experiments with more AliBu.sub.3 (50 equiv. relative to Zr) give only minimal amounts of oil (3%). Instead, improved conversion of HDPE is accomplished by adding portions of Zr(CH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x and AliBu.sub.3 every 12 h. Polymer was not observed after three reaction cycles with 84% total oil yield. In addition, the synthetic versatility of the alkylaluminum products was demonstrated in HDPE deconstruction reactions quenched with methanol, I.sub.2, or CO.sub.2 (Table 1, entries 4-6; MALDI-TOF-MS shown in
[0241] Mixtures of partially dehydroxylated zirconium-free SiAlO.sub.x, AliBu.sub.3, and HDPE heated at 200° C. for 12 h return the polymer with little change to its molecular weight (M.sub.n=5.8 kDa) and trace amounts of oil (<2%) containing trimerized isobutylene resulting from AliBu.sub.3 thermolysis (Ziegler et al., “Metallorganische Verbindungen, XXXII Zerfalls- und Austauschreaktionen der Aluminiumtrialkyle,” Liebigs Ann. Chem. 629:53-89 (1960), which is hereby incorporated by reference in its entirety). Thus, the catalytic species derived from (—SiO).sub.2Zr(CH.sub.2CMe.sub.3).sub.2 is the active site for carbon-carbon bond cleavage of polyethylene, and oligomeryl and polymeryl aluminum species are the primary products. Although acid sites on SiAlO.sub.x (or even weaker acid sites on SiO.sub.2) would mediate detectable degradation of HDPE at 200° C. (Yanik and Karayildirim, Feedstock Recycling and Pyrolysis of Waste Plastics, Scheirs Eds. Sussex, UK John Wiley & Sons, p 209-224 (2006), which is hereby incorporated by reference in its entirety), AliBu.sub.3 reacts to cap the few surface silanol sites (Werghi et al., “Well-defined Silica Supported Aluminum Hydride: Another Step Towards the Utopian Single Site Dream?” Chem. Sci. 6:5456-5465 (2015); Kermagoret et al., “Triisobutylaluminum: Bulkier and Yet More Reactive Towards Silica Surfaces Than Triethyl or Trimethylaluminum,” Dalton Trans. 42:12681-12687 (2013), which are hereby incorporated by reference in their entirety) and blocks acid-promoted thermolysis to favor zirconium-catalyzed pathways.
[0242] Main group alkyl and hydride reagents influence catalytic alkene polymerizations and could also affect these deconstruction reactions. The trend of reactivity of a series of main group compounds in this Zr(CH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x-catalyzed polyethylene upcycling process, in terms of yields of oils, is AlH.sub.3˜AliBu.sub.3>AlPh.sub.3˜AlEt.sub.3>>AlMe.sub.3˜HAliBu.sub.2 (DIBAL-H)˜HAlMe.sub.2˜ZnEt.sub.2. Several of these experiments are also mechanistically informative and provide evidence for metalation and carboalumination steps that are part of the processes.
[0243] The most effective co-reactant for Zr-catalyzed deconstruction of HDPE is AlH.sub.3, the reaction of which at 200° C. for 12 h provides an oil in comparable yield (42%) as with AliBu.sub.3 and significantly higher amounts of alcohol chains (89%) compared to alkanes (11%). Similar ranges of C.sub.nH.sub.2n+1OH species were observed in the MALDI-TOF-MS spectra of oils obtained in otherwise equivalent reactions using AlH.sub.3 and AliBu.sub.3 at 200° C., although the spectra were not identical. AlEt.sub.3 is less effective for carbon-carbon bond cleavage than AliBu.sub.3 or AlH.sub.3, affording oils in 23% yield after 12 h at both 150 and 200° C. The structure HO—CH.sub.2—CH(CH.sub.2CH.sub.3)—R (R=aliphatic polymer chain), identified from a .sup.1H-.sup.1H COSY experiment, was the dominant alcoholic species, based on the 1.53 ratio of integrated signals of (CH)—CH.sub.2—CH.sub.3 to CH.sub.2—OH. The fraction of molecules containing OH, calculated as described above, was 0.39. Thus, AlEt.sub.3 was less active and also less effective than AliBu.sub.3 for introducing aluminum into the products, giving the highest percentage of alkanes of all reactive aluminum reagents. A higher yield of oil product (29% by mass after workup with O.sub.2) from the catalyzed reaction of HDPE and AlPh.sub.3 at 200° C., compared to AlEt.sub.3, is partially affected by the formation of aromatic-containing species, identified by .sup.1H and .sup.13C NMR spectroscopy, GC-MS, and MALDI-TOF-MS (see Supplementary).
[0244] Zr(CH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x was initially tested because its surface hydrides are reported to be more active for propane metathesis and polyolefin hydrogenolysis than the silica-supported analogues (Dufaud and Basset, “Catalytic Hydrogenolysis at Low Temperature and Pressure of Polyethylene and Polypropylene to Diesels or Lower Alkanes by a Zirconium Hydride Supported on Silica-Alumina: A Step Toward Polyolefin Degradation by the Microscopic Reverse of Ziegler-Natta Polymerization,” Angew. Chem. Int. Ed. 37:806-810 (1998); Thieuleux et al., “Homologation of Propane Catalyzed by Oxide-Supported Zirconium Dihydride and Dialkyl Complexes,” Angew. Chem. Int. Ed 46:2288-2290 (2007), which are hereby incorporated by reference in their entirety). In addition, aluminum is known to incorporate into silica framework sites in reactions of excess AliBu.sub.3 and SiO.sub.2 (Kermagoret et al., “Triisobutylaluminum: Bulkier and Yet More Reactive Towards Silica Surfaces Than Triethyl or Trimethylaluminum,” Dalton Trans. 42:12681-12687 (2013), which is hereby incorporated by reference in its entirety), and this in situ support modification also could influence catalytic activity. In fact, an aerosil silica-supported zirconium catalyst, Zr(CH.sub.2CMe.sub.3).sub.2@SiO.sub.2, provides an alcohol-containing oil in nearly equivalent yield (35%) after heating HDPE and AliBu.sub.3 for 12 h at 200° C. Moreover, the oil is approximately 85% alcohols and only 15% alkanes. The Zr(CH.sub.2CMe.sub.3).sub.2@SiO.sub.2-catalyzed reaction with AlEt.sub.3 provided the oil product in similar single-pass yield (32%) and high alcohol content (82%), as a notable contrast with the silica-alumina supported catalyst. These reactions afforded alcohol species with a normal, ca. C.sub.35-centered distribution of monoalcohols, as detected by MALDI-TOF-MS (
[0245] The silica- or silica-alumina-supported neopentylzirconium, as well as the (≡SiO).sub.3ZrH catalyst for polyethylene hydrogenolysis, are exceedingly sensitive to irreversible reactions with air and moisture to give deactivated materials. Thus, small amounts of protic or oxidative impurities in the polyethylene reactant could have an outsized effect upon catalytic performance. Because the alkylaluminum reactant can serve as an alkylating agent for converting alkoxyzirconium into alkylzirconium sites, some poisoned sites could also be re-activated under catalytic conditions. In this context, the polyolefin reactants used in this study, although clean and dry, were essentially used as received and did not undergo exhaustive purification prior to use. More convenient precatalysts would be tolerant of ambient air, prior to treatment with alkylaluminum reagents for HDPE deconstruction. In fact, ≡SiO—Zr(CH.sub.2CMe.sub.3).sub.3 and O.sub.2 react to provide ≡SiO—Zr(OCH.sub.2CMe.sub.3).sub.3 (Quignard et al., “Surface Organometallic Chemistry of Zirconium: Application to the Stoichiometric Activation of the CH Bonds of Alkanes and to the Low-temperature Catalytic Hydrogenolysis of Alkanes,” J. Mol. Catal. 74:353-363 (1992), which is hereby incorporated by reference in its entirety), as does (≡SiO).sub.2Zr(CH.sub.2CMe.sub.3).sub.2. This air-exposed material, upon combination with AliBu.sub.3, generates a catalytically active species for HDPE deconstruction to an oil in 34% yield, approximately half of which are alcohols. The oil product contains less alcohol functionality (ca. 50% of molecules are mono-alcohols) than the oil from Zr(CH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x. The headspace of the reaction vessel is >98% isobutylene, with very little isobutane. Air-stable Zr(OCH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x can also be activated by AlH.sub.3, and the reaction with HDPE affords an oil (49% yield) containing a lower percentage of alcohols (62%). The MALDI-TOF-MS spectrum of this oil revealed a distribution of alcohols from C.sub.28H.sub.57OH to C.sub.51H.sub.103OH, which is similar to the product range of the analogous reaction with the air-sensitive catalyst.
[0246] The deconstruction of HDPE into long chain alkylaluminum species likely involves the sequence shown in
[0247] First, evidence for metalation in step i is provided by the reaction by-products. Neopentane (CMe.sub.4) is detected in the headspace within the first 15 min. of reactions catalyzed by Zr(CH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x, regardless of the organoaluminum reagent, suggesting that the polymer is metalated by a Zr—CH.sub.2CMe.sub.3 species. Likewise, benzene is observed in reactions involving AlPh.sub.3 prior to workup with O.sub.2, supporting the idea that phenylzirconium species react with hydrocarbons by metalation. In addition, a plausible pathway to long chain hydrocarbon side products involves the reaction of polyethylene chains and short polymerylzirconium intermediates. Finally, in the reaction of HDPE with Zr(OCH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x and AliBu.sub.3, CMe.sub.4 was not detected, further indicating that CMe.sub.4 formation is associated with metalation by neopentylzirconium rather than resulting from reaction of neopentylaluminum species and/or polymer hydrogenolysis.
[0248] Surface zirconium hydride species, formed by ligand exchange reactions of aluminum hydride and zirconium alkyls, also likely are involved in metalations. In support of this idea, hydridoaluminum species are formed from AliBu.sub.3 at high temperatures (Ziegler et al., “Metallorganische Verbindungen, XXXII Zerfalls- und Austauschreaktionen der Aluminiumtrialkyle,” Liebigs Ann. Chem. 629:53-89 (1960), which is hereby incorporated by reference in its entirety). During the catalytic HDPE deconstruction and alumination reactions involving AliBu.sub.3, isobutylene formation (major, along with a minor amount of isobutane) is consistent with the generation of hydridozirconium species. Furthermore, DRIFT analysis of the surface species revealed a band at 1623 cm.sup.−1 assigned to v.sub.ZrH in the material obtained by reaction of Zr(CH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x and AliBu.sub.3 at 150° C. for 4 h (34, 35). This signal disappeared upon treatment with D.sub.2 (the signal for presumed v.sub.ZrD is not resolved from Si/Al—O bands) and reappeared upon treatment with H.sub.2 (
[0249] Mid-chain polymerylzirconium species B are cleaved into a shorter terminal polymerylzirconium C and vinyl-terminated chain fragments via 3-alkyl elimination. This step is responsible for chain cleavage leading to polymer deconstruction. The newly shortened polymerylzirconium can react with AlR.sub.3 via alkyl group exchange or hydride transfer to form [Zr]—R or [Zr]—H and polymerylAlR.sub.2, step iii in
[0250] Other sequences of elementary steps could account for the observed structure of the products. For example, the polymerylzirconium intermediates C can react with small molecules, such as H.sub.2 or benzene. Accordingly, high alkane content was observed with the catalytic systems Zr(CH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x/AlPh.sub.3 (˜55%) and Zr(OCH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x/AliBu.sub.3 (˜50%). This influence of small molecules was further tested by reacting HDPE and AlH.sub.3 in the presence of Zr(OCH.sub.2CMe.sub.3).sub.2@SiAlO.sub.x under vacuum (Table 1, entry 17). Under these single-pass, dynamic low-pressure conditions, the mass of the reaction mixture decreased by 21% and a high yield (60%) was obtained. MALDI-TOF-MS analysis of this oil revealed significantly lower molecular weight alcohols, from C.sub.20H.sub.41OH to C.sub.38H.sub.77OH than that from the analogous reaction carried out in a sealed vessel. This oil contained comparable fraction of alcohol molecules (˜67%, by .sup.1H NMR analysis) as the experiment under N.sub.2. Clearly, the dynamic removal of small molecules from the reaction mixture allows chain cleavage by β-alkyl elimination to be kinetically more competitive compared to chain transfer processes; however, relative rates of chain transfer involving alumination and alkane production are not affected by dynamic vacuum.
[0251] In conclusion, these new polyolefin deconstruction/heterofunctionalization reactions will enable the development of incipient plastic upcycling efforts that contribute to efforts addressing the rapidly growing global plastic waste catastrophe. These methods could complement oxidative transformations, which typically provide diacids through radical pathways (Pifer and Sen, “Chemical Recycling of Plastics to Useful Organic Compounds by Oxidative Degradation,” Angew. Chem. Int. Ed. 37:3306-3308 (1998), which is hereby incorporated by reference in its entirety). Advantageously, the early-metal catalyst and alkylaluminum reagent influence the structure, size, and distribution of products by favoring unique combinations and influencing rates of elementary steps. That is, advances in catalyst design though organometallic chemistry promote desirable specific upcycling outcomes. Even though early metal alkyl and hydride reagents are notoriously sensitive to air and moisture compared to noble metal hydrogenolysis catalysts (Celik et al., “Upcycling Single-Use Polyethylene into High-Quality Liquid Products,” ACS Cent. Sci. 5:1795-1803 (2019); Watson and Roe, “β-Alkyl Transfer in a Lanthanide Model for Chain Termination,” J. Am. Chem. Soc. 104:6471-6473 (1982), which are hereby incorporated by reference in their entirety), the activation of air-stable and earth abundant zirconium catalyst precursors in situ by aluminum reagents allows techniques from polymerization to be applied to polymer upcycling. The aluminum reagents even protect the sensitive active site to allow the deconstruction/alumination of untreated post-consumer HDPE. Although hydrogen for upcycling by hydrogenolysis is less expensive than aluminum regents, the production of long chain alkylaluminum species from waste polyolefins should be compared to the traditional Ziegler synthesis (Ziegler, “A Forty Years' Stroll Through the Realms of Organometallic Chemistry” Advances in Organometallic Chemistry vol 6, Stone and West Eds. New York, N.Y.: Academic Press, p. 1-17 (1968), which is hereby incorporated by reference in its entirety). In fact, the abundance, accessibility (from aluminum, hydrogen, and alkenes), and large-scale industrial application of alkylaluminum reagents contribute to the potential of this new transformation in upcycling.
[0252] The combination of β-alkyl elimination and heterobimetallic alkyl group metathetical exchange at surface-immobilized organozirconium sites provides a valuable method to install reactive groups and reconstruct the carbon-skeleton of organic molecules, without the need for prior activation or directing groups. The alkylaluminum reagent can activate air-stable alkoxyzirconium species to generate highly air sensitive hydridozirconium active sites, which are also innoculated by the alkylaluminums against poisoning. Both AliBu.sub.3 and AlH.sub.3 react with alkyl and alkoxyzirconium species to generate surface zirconium hydrides. Moreover, both the catalysts and reactants are based upon earth-abundant, readily available, and non-toxic metal centers. In this regard, these catalytic reactions, as applied to polyolefins, are viable to compete with conventional syntheses of fatty alcohols. This new process could motivate recovery of discarded polyolefins from the environment, produce value-added chemical products, and offer an environmentally friendly end-of-life for materials currently destined for landfills.
[0253] Although preferred embodiments have been depicted and described in detail herein, it will be apparent to those skilled in the relevant art that various modifications, additions, substitutions, and the like can be made without departing from the spirit of the invention and these are therefore considered to be within the scope of the invention as defined in the claims which follow.