Method for manufacturing an annular casing equipping a turbomachine

Abstract

The invention relates to a method for manufacturing a carrying casing (12) provided with a collar (18) for supporting at least one cartridge of abradable material for a turbomachine, said carrying casing (12) comprising at least one bare annular casing (16) and one block of honeycomb material (20) that comprises an outer face (22) configured to be secured to an inner face (24) of said bare annular casing (16), said block being covered with a skin (26), characterized in that it comprises successively: —a step in which the outer face (22) of the block (20) is secured to the inner face (24) of the bare annular casing (16), —a step in which the circularity of San inner face (32) of the block (20) is monitored and in which, if necessary, the inner face (32) of the block (20) is machined to round, —a step in which, simultaneously, said skin (26) is produced and is secured to said block (20).

Claims

1. Method for manufacturing a carrying casing provided with a collar intended to carry at least one cartridge of abradable material for a turbomachine, said carrying casing comprising at least one bare annular casing and one block of material that comprises an outer face configured to be secured to an inner face of said bare annular casing, said block being covered with a skin able to carry said cartridge of abradable material, said block and said skin forming said collar, wherein the method comprises successively: a step (ET1′) during which the outer face of the block is secured to the inner face of the bare annular casing, a step (ET2′) during which the circularity of an inner face of the block is monitored and during which, if necessary, the inner face of the block is round-machined, a step (ET4′) during which, simultaneously, said skin is produced and is secured to said block.

2. The method according to claim 1, wherein during the step (ET4′) whereby the skin is produced and is secured to the block, said block is covered with an impregnated composite material and said composite material is polymerised on said block to obtain said skin while securing it to the block.

3. The method according to claim 2, wherein during the step (ET4′) whereby the skin is produced and is secured to the block, the bare annular casing, the block and the composite material are arranged together in a cooking device simultaneously enabling the polymerisation of the composite material and the attachment thereof to the block.

4. The method according to claim 3, wherein during the step (ET4′) whereby the skin is produced and is secured to the block, the cooking device implemented is an autoclave enclosure.

5. The method according to claim 3, wherein during the step (ET4′) whereby the skin is produced and is secured to the block, a woven and impregnated composite material is used to drape the block.

6. The method according to claim 3, wherein during the step (ET4′) whereby the skin is produced and is secured to the block, at least one other element is secured to the carrying casing.

7. The method according to claim 1, wherein during the first step (ET1′), a block of honeycomb material with a constant thickness is used.

Description

(1) The invention will be better understood and other details, characteristics and advantages of the present invention will more clearly appear upon reading the following description, provided as an example and not limited thereto, and with reference to the appended drawings, in which:

(2) FIG. 1 is a schematic cross-sectional view of an equipped casing of a turbomachine according to the prior art;

(3) FIGS. 2A and 2B are schematic views representing the steps of a method to manufacture a support collar for the equipped casing in FIG. 1, and being part of the first phase of a method for the manufacturing of the equipped casing of FIG. 1;

(4) FIG. 3 is a schematic view of a manufacturing step of a carrying casing, being part of the first phase of a method for the manufacturing of the equipped casing of FIG. 1;

(5) FIG. 4 is a flowchart representing all the phases of the method for manufacturing the equipped casing of FIG. 1;

(6) FIGS. 5A, 5B, and 5C are schematic views representing the three manufacturing phases of a carrying casing according to the invention;

(7) FIG. 6 is a flowchart representing all the phases of a method for manufacturing an equipped casing according to the invention.

(8) In the following description, identical reference numbers describe identical parts, or parts with similar functions.

(9) In the following description, the “inner” and “outer” orientations are defined in reference to an axis of rotation of the rotors of a turbomachine, the “outer” orientations being turned in the direction opposite said axis, and the “inner” orientations being turned towards said axis.

(10) FIG. 1 represents an equipped annular casing 10 for a turbomachine. In a known manner, the equipped annular casing 10 is constituted of a plurality of annular elements that are concentric and coaxial with respect to an axis A of the turbomachine, the axis A corresponding, for example, to an axis of rotation of the rotors (not represented) of the turbomachine. Thus, the equipped casing 10 is constituted, from the outside towards the inside, of a carrying casing 12 equipped with a collar receiving an annular cartridge 14 of abradable material that determines a gas duct of said turbomachine. More particularly, the carrying casing 12 is formed by a bare casing 16 receiving internally a support collar 18. The support collar 18 is therefore configured to receive internally the annular cartridge 14 of abradable material.

(11) In a known manner, the support collar 18 is constituted of a block 20 of honeycomb material comprising an outer face 22 configured to be secured to the inner face 24 of said bare annular casing 16 and covered by a skin 26.

(12) The skin 26 is generally, but in a non-limiting manner of the invention, a skin 26 made of a composite material achieved by cooking a skin preform (not represented) of resin-impregnated composite material, for example woven carbon fibres impregnated with epoxy resin.

(13) Also in a known manner, the outer face 22 of the block 20 of honeycomb material, which also corresponds to the outer face 22 of the support collar 18, is secured to the inner face 24 of the bare annular casing 16, via a film of glue 28.

(14) In a first phase P1 of a method for manufacturing an equipped casing 10 according to a known method of the state of the art, the collar 18 is manufactured, then the carrying casing 12 is manufactured by assembling the collar 18 to the bare casing 16 and, in a second phase P2, the abradable material 14 is assembled to the carrying casing 12 to achieve an equipped casing 10.

(15) Thus, as represented in FIGS. 2A to 3, the method begins, during a first phase, the steps of which are represented in FIGS. 2A and 2B, by manufacturing the support collar 18.

(16) As shown in FIG. 4, the manufacturing of the support collar 18 starts with a first step ET1, during which a block 20 of honeycomb material, also called “Nida”, is inserted in a skin preform made of an impregnated composite material, this assembly being preferably maintained in a suitable mould (not represented) in order to avoid it deforming. Then, in a second step ET2, this assembly is cooked. The result is a raw collar 18, such as that represented in FIG. 2A.

(17) Following this step ET2, the skin preform of composite material has become a rigid skin 26, such as that represented in FIG. 2A. The block 20 of honeycomb material and the skin 26 are adhered to one another following the cooking of the composite material.

(18) Moreover, the inner surface 24 of the bare casing 16 previously represented in FIG. 1 does not necessarily correspond to the theoretical profile thereof. In particular, in the case of a rotating bare casing 16 made of a composite material, it has been observed that the inner face 24 of the bare casing 16 after manufacturing tended to have a shape that is not perfectly circular, instead of the circular shape theoretically required, which is adapted to receive without significant leaks, a compressor wheel, or a turbine wheel of the turbomachine (not represented). Furthermore, the inner face 24 of the bare casing 16 can have possible surface defects.

(19) Upon completion of step ET2, insofar as the general shape of the rigid skin 26 must not be modified, as it must have a nominal minimum thickness, it is necessary to machine the outer peripheral face 22 of the support collar 18, such that it fits with the inner peripheral face 24 of the bare casing 16, in order to minimise, on the one hand, the deformations that the support collar 18 may undergo with respect to its theoretical profile, and on the other hand, the positioning deviations of the support collar 18 with respect to the axis A of the turbomachine once it is mounted in the bare annular casing 16. Indeed, such deformations and positioning deviations could consequently change the position required for the support collar 18, and consequently for the cartridge of abradable material 14 that the support collar 18 must receive.

(20) To this end, as shown in FIG. 4, during a third step ET3 (not represented), the dimensions of the inner peripheral face 24 of the bare casing 16 are measured to deduce from it, a three-dimensional profile that the outer peripheral face 22 of the support collar 18 must fit with, this peripheral face 22 also corresponding to the outer peripheral face 22 of the block 20 of honeycomb material.

(21) Then, during a fourth step ET4, the support collar 18 is placed in equipment (not visible) adapted to maintain it in position and, as represented in FIG. 2B, the outer peripheral face 22 of the support collar 18 is then machined to a three-dimensional profile corresponding to that of the inner peripheral face 24 of the bare casing 16, for example by using a two-size end mill 30.

(22) Then, during a fifth step ET5, the support collar 18 is glued in the bare annular casing 16 via the film of glue 28 to obtain the carrying casing 12.

(23) The first to fifth steps ET1 to ET5 of the methods for manufacturing the support collar 18 and the carrying casing 12 with the collar 18 thereof, comprising in particular the steps ET1 and ET4, represented in FIGS. 2A and 2B, constitute a first phase P1 of the method for manufacturing the equipped casing 10 with the abradable material. Then, in a second phase P2 for the manufacturing of the equipped casing represented in FIG. 4, the cartridge of abradable material 14 is glued in the carrying casing 12 of FIG. 3 so as to obtain the equipped casing 10, such as represented in FIG. 1.

(24) This design has the disadvantage of requiring a measuring operation of the inner peripheral face 24 of the bare annular casing 16 with very high tolerance values, since any defect of the shape of this inner peripheral face 24 could have consequences on the positioning of the support collar 18 after the attachment thereof and on the quality of the bond between the inner face 24 of the bare casing 16 and of the collar 18. It is therefore consequently necessary to minimise such defects maximally.

(25) Moreover, the machining operation is highly constraining, because of the equipment implemented for the achievement thereof. Indeed, once cooked, the support collar 18 must be positioned in specific equipment enabling to clamp it during machining operations, as it can naturally not be machined in the absence of a support. This equipment is therefore voluminous and expensive.

(26) To overcome this disadvantage, it is desirable to allow the manufacturing of the support collar 18 by enabling the machining of the block of honeycomb material with a reduced specific equipment, and even in the absence of specific equipment, and implementing lower tolerance values.

(27) For this purpose, the invention proposes a method for manufacturing the support collar 18 in the absence of specific equipment.

(28) To this end, the invention advantageously proposes a method for manufacturing the support collar 18 that is integrated to the method for manufacturing the carrying casing 12, the support collar 18 being realised at the same time as the carrying casing 12.

(29) For this purpose, as shown in FIG. 5A to 5C, the method for manufacturing the carrying casing 12 comprises successively a step during which the outer face 22 of the block 20 is glued to the inner face 24 of the bare annular casing 16, then a step during which the circularity of the inner face of the block 20 is monitored and during which, if necessary, this inner face 32 of the block 20 is round-machined, and finally a step whereby, the skin 26 is manufactured and simultaneously secured to the block 20.

(30) As shown in FIG. 6, the manufacturing of the carrying casing 12 starts with a first step ET1′, during which the block 20 of honeycomb material or “Nida” is inserted directly in the bare annular casing 16, as represented in FIG. 5A. In particular, the peripheral outer face 22 of the block 20 of honeycomb material is raw and is therefore not machined, and is glued in the raw form thereof via the film of glue 28. During this first step ET1′ a block 20 of honeycomb material with a constant thickness is used.

(31) The honeycomb material of the block 20 is relatively flexible and fits with the profile of the inner face 24 of the bare annular casing 26.

(32) Then, during a second step ET2′, the block 20 of honeycomb material is glued, for example by cooking.

(33) Then, during a third step ET3′, the circularity of the inner face 32 of the block 20 is monitored.

(34) If the bare annular casing 16 is perfectly circular, the block 20 of honeycomb material is also, in theory, perfectly circular and should therefore not require any additional machining operations. However, it is possible to consider machining operations as a precautionary measure.

(35) On the contrary, if necessary, the inner face 32 of the block 20 is machined to round, as represented in FIG. 5B. This machining is, for example, performed using two-sized end mills 30, and consists in conferring the inner face 32 of the block 20 a perfectly circular cross-section over the entire axial length thereof.

(36) As can be seen, the method according to the invention is particularly advantageous in that it enables to avoid the machining of the outer peripheral face 22 of the block 20 of honeycomb material.

(37) A first consequence of this configuration is that, the block 20 of honeycomb material being maintained by the bare casing 16, it is not necessary to place the block 20 in specific equipment, as the bare casing 16 secures and maintains the block during machining operations using the end mill 30. This configuration enables to do without such equipment, and consequently reduces to total duration of the manufacturing method by the time necessary to place the block in this equipment and to remove it therefrom.

(38) A second consequence of this configuration is that, the machining of the inner face 32 of the block 20 being a round machining, it is not necessary, as was the case with the methods according to the prior art, to perform a measurement of the inner face 24 of the bare casing 16. The only condition to abide by when machining to round the inner face 32 of the block 20 is a coaxial condition with respect to the axis A of the turbomachine.

(39) At the end of this step ET3′, the bare casing 16 is provided with the block 20 of honeycomb material, but does not yet constitute a carrying casing 12, as the collar 18 is not constituted, since the block 20 of honeycomb material is not covered with the skin 26.

(40) Thus, unlike the carrying case 12 according to the prior art, the carrying casing 12 according to the invention, when the bare annular casing 16 thereof does not have an inner face 24 having a perfectly circular cross-section over at least one part of the axial length thereof, comprises a block 20 of which the inner face 32 is round-machined to comply with the circularity constraint.

(41) Then, during a fourth step ET4′, the skin 26 is simultaneously manufactured and secured in the block 20.

(42) For this purpose, in a preferred embodiment of the invention, the block 20 is preferably covered with an impregnated composite material and said composite material is polymerised on the block 20 to obtain the skin 26, while securing it to the block 20.

(43) The result is a carrying casing 12, such as represented in FIG. 5C.

(44) It will be noted, that according to the method, the collar 18, constituted of a block 20 of an elastomer material and the skin 26, is manufactured at the same time as being secured to the carrying casing 12.

(45) Preferably, during this fourth step, the cooking of the impregnated composite material constituting the skin 26 is not realised independently. The bare annular casing 16, the block 20 of honeycomb material and the composite material of the skin 26 are placed together in a cooking device that enables simultaneously, through the increase of temperature it induces, the polymerisation of the composite material, thereby securing it to the block 20.

(46) Preferably, for the manufacturing of the skin 26, a woven and impregnated composite material is used to drape the block 20 of honeycomb material.

(47) For information purposes, during the fourth cooking step, the cooking is carried out at a temperature of 150° C.

(48) From this fourth step, the impregnated composite material has become a rigid skin 26, capable of receiving a cartridge of abradable material. The block 20 of honeycomb material and the skin 26 are adhered following the cooking of the composite material and form a support collar 18 integrated in the carrying casing 12.

(49) The first to fourth steps ET1′ to ET4′ of the method for manufacturing a carrying casing 12 constitute the first phase P1′ of the method for manufacturing the equipped casing 10. Then, during a second phase P2′, represented in FIG. 6, the cartridge 14 of abradable material is glued to obtain the equipped casing represented in FIG. 1, this gluing operation being also achievable by cooking.

(50) The bare annular casing 16 implemented in the method can be a casing of any known type according to the prior art. However, preferably, the bare annular casing 16 is a casing made of composite material also obtained beforehand by cooking a preform made of composite material.

(51) The composite material of the skin 26 being only capable of withstanding a limited number of cooking cycles, it will be understood that, advantageously, the cooking cycle thereof is provided to coincide with a step whereby another element is secured to the carrying casing 12.

(52) Thus, during the step ET4′, the cooking cycle can be used to secure another element to the carrying casing 12. For example, the cooking cycle can be used to secure to the bare annular casing 16 a thermal protection element made of fibreglass, also known as “glass wool”, that provides local thermal protection to the bare casing 16. It is also possible to secure to the outer surface of the bare annular casing 16 panels of sound insulation, or attachment elements enabling to secure members and ducts on the outer surface of the bare casing 16.

(53) Thus, as seen above, the manufacturing of an equipped casing 10 according to the invention comprises a first phase P1′ of four steps ET1′, ET2′, ET3′, ET4′ followed by a second phase P2′, i.e. a total of five operations, while according to the prior art, the equipped annular casing 10 was obtained upon completion of a first phase P1′ of five steps ET1′, ET2′, ET3′, ET4′, ET5′ followed by a second phase P2′, i.e. a total of six operations. It consequently results from this a significant time gain in the context of a large-scale production, not only because of the reduction of the number of operations, but also because of the reduced complexity thereof.

(54) The invention therefore applies to any equipped annular casing 10 of a turbomachine, and in particular to any equipped annular casing 10 comprising a bare annular casing 16 made of a composite material.