Copper Chelate Complex Compositions for Antifouling Protection

Abstract

The present invention relates to antifouling compositions comprising copper di(ethyl 4,4,4-trifluoroacetoacetate) (Cu(ETFAA)2) that are highly effective against marine biofouling of surfaces of ships and marine structures, their use for inhibiting marine biofouling, as well as antifouling paints comprising said compositions.

Claims

1. An antifouling composition comprising Cu(ETFAA).sub.2 and one or more biocidal agents selected from the group consisting of copper 2-pyridinethiol-1-oxide (copper pyrithione, CuPT), zinc 2-pyridinethiol-1-oxide (zinc pyrithione, ZnPT), 4,5-dichloro-2-n-octyl-4-isothiazolin-3-one (DCOIT), cuprous oxide (Cu.sub.2O), zinc oxide (ZnO), 4-bromo-2-(4-chlorophenyl)-5-(trifluoromethyl)-1H-pyrrole-3-carbonitrile (tralopyril), zinc ethane-1,2-diylbis(dithiocarbamate) (zineb), zinc N,N-dimethylcarbamodithioate (ziram), 3-(3,4-dichlorophenyl)-1,1-dimethylurea (diuron), copper(I) thiocyanate (CuSCN), 4-[1-(2,3-dimethylphenyl)ethyl]-1H-imidazole (medetomidine), triazines, fluanids and 2,4,5,6-tetrachloroisophthalonitrile (chlorothalonil).

2. The antifouling composition of claim 1, wherein the one or more biocidal agent is selected from the group consisting of CuPT, ZnPT, DCOIT, Cu.sub.2O, and tralopyril.

3. The antifouling composition of claim 1, wherein the one or more biocidal agent is selected from the group consisting of CuPT and Cu.sub.2O.

4. The antifouling composition of claim 1, wherein the biocidal agent is CuPT.

5. The antifouling composition of claim 1, wherein the biocidal agent is Cu.sub.2O.

6. The antifouling composition of claim 3, wherein the biocidal agents are CuPT and Cu.sub.2O.

7. The antifouling composition of claim 3, wherein the ratio of Cu(ETFAA).sub.2 (wt %) to CuPT (wt %) and/or the ratio of Cu(ETFAA).sub.2 (wt %) to Cu.sub.2O (wt %) is from 100:1 to 1:100.

8. Use of an antifouling composition for the inhibition of marine biofouling on a solid surface, wherein said antifouling composition comprises Cu(ETFAA).sub.2.

9. The use of claim 8, wherein the antifouling composition comprises Cu(ETFAA).sub.2 and one or more biocidal agents.

10. The use of claim 9, wherein the antifouling composition comprises Cu(ETFAA).sub.2 and one or more biocidal agents selected from the group consisting of copper 2-pyridinethiol-1-oxide (copper pyrithione, CuPT), zinc 2-pyridinethiol-1-oxide (zinc pyrithione, ZnPT), 4,5-dichloro-2-n-octyl-4-isothiazolin-3-one (DCOIT), cuprous oxide (Cu.sub.2O), zinc oxide (ZnO), 4-bromo-2-(4-chlorophenyl)-5-(trifluoromethyl)-1H-pyrrole-3-carbonitrile (tralopyril), zinc ethane-1,2-diylbis(dithiocarbamate) (zineb), zinc N,N-dimethylcarbamodithioate (ziram), 3-(3,4-dichlorophenyl)-1,1-dimethylurea (diuron), copper(I) thiocyanate (CuSCN), 4-[1-(2,3-dimethylphenyl)ethyl]-1H-imidazole (medetomidine), triazines, fluanids and 2,4,5,6-tetrachloroisophthalonitrile (chlorothalonil).

11. The use of claim 8, wherein the antifouling composition is used in combination with a polymer and/or copolymer allowing controlled release of Cu(ETFAA).sub.2.

12. An antifouling paint comprising the antifouling composition of claim 1 and a polymer and/or copolymer allowing controlled release of Cu(ETFAA).sub.2.

13. The antifouling paint of claim 12, wherein the content of Cu(ETFAA).sub.2 is from about 1 to about 25 wt %

14. The antifouling paint of claim 12, wherein the total content of said one or more biocidal agent is less than about 30 wt %.

15. The antifouling paint of claim 12, wherein the total content of CuPT is less than about 10 wt %, and/or the total content of Cu.sub.2O is less than about 20 wt %.

16. A method for inhibiting marine biofouling on a solid surface, comprising applying an antifouling paint of claim 12 onto the surface.

Description

BRIEF DESCRIPTION OF THE FIGURES

[0013] FIG. 1 depicts panels coated with the antifouling paints of example 2, Table 1, and shows the appearance of the panels after 24 months in sea-water in the un-rinsed state and after rinsing.

DETAILED DESCRIPTION OF THE INVENTION

[0014] Unless defined otherwise, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this invention is related. The following abbreviations and terms are used herein: [0015] AIBN: azobis(isobutyronitril) [0016] AMBN: azobis-(2-methylbutyronitrile) [0017] A630-20×: a fatty acid amide [0018] BA: butyl acrylate [0019] Chlorothalonil: 2,4,5,6-tetrachlorobenzene-1,3-dicarbonitrile [0020] Copper Omadine®, CuPT, copper pyrithione: copper 2-pyridinethiol-1-oxide [0021] Cu.sub.2O: cuprous oxide [0022] Cu(ETFAA).sub.2: copper di(ethyl 4,4,4-trifluoroacetoacetate) [0023] CuSCN: copper(I) thiocyanate [0024] DCOIT: 4,5-dichloro-2-n-octyl-4-isothiazolin-3-one [0025] Diuron: 3-(3,4-dichlorophenyl)-1,1-dimethylurea [0026] ETFAA: ethyl 4,4,4-trifluoroacetoacetate [0027] 2MEA: 2-methoxyethyl acrylate monomer [0028] Medetomidine: 4-[1-(2,3-dimethylphenyl)ethyl]-1H-imidazole [0029] MMA: methyl methacrylate monomer [0030] MIBK: methyl isobutylketone [0031] MPM: methoxy propylene monomer [0032] PGM: propylene glycol monomethylether [0033] TIPX: tri-isopropylsilyl acrylate monomer [0034] Tralopyril: 4-bromo-2-(4-chlorophenyl)-5-(trifluoromethyl)-1H-pyrrole-3-carbonitrile [0035] VAGH: vinyl chloride/vinyl acetate/vinyl alcohol copolymer (commercial product) [0036] Zineb: zinc ethane-1,2-diylbis(dithiocarbamate) [0037] Ziram: zinc N,N-dimethylcarbamodithioate [0038] ZnO: zinc oxide [0039] ZnPT, zinc pyrithione: zinc 2-pyridinethiol-1-oxide

[0040] The term “(meth)acrylate” is a collective term indicating both acrylate and methacrylate monomers. The term “methacrylate” or “meth-acrylate” indicates only methacrylate monomers.

[0041] Bentone SD2 is an organo clay added for anti-settling properties; Bentone #38 is quaternium 18-hectorite clay; Minex 4 is nepheline syenite clay. Disparlon 6900-20× (A630-20× polyamide wax) is a 20% dispersion of polyamide wax in xylene used as rheology modifier; Disperbyk 161 is a dispersing additive. Resin refers to all pre-polymers or polymers that may serve as raw materials for the binders to be used in the antifouling paints of the invention. Rosin or gum rosin refers to colophony (CAS: 8050-09-7, see also https://www.megaglori.com/what-is-gum-rosin/).

[0042] By “biocidal agent” is meant any chemical compound that prevents the settlement of marine organisms on a surface and/or prevents the growth of marine organisms on a surface and/or encourages the dislodgement of marine organisms from a surface.

[0043] The terms “antifouling paint”, “antifouling coating” and “antifouling formulation” are used interchangeably herein.

[0044] The present invention provides a new approach to inhibit the fouling of surfaces of underwater objects such as ship hulls or any other marine structures. Specifically, the present invention provides an antifouling composition comprising Cu(ETFAA).sub.2. It has been surprisingly found that Cu(ETFAA).sub.2 significantly enhances the antifouling efficacy of antifouling compositions against the settling of marine organisms such as barnacles, bryozoans, hydroids, mussels, algae and the like.

[0045] ETFAA is a compound that is known as an intermediate in the production of compounds used in agriculture and pharmaceuticals. The copper chelate complex of ETFAA may be formed by adding a 1:2 molar ratio of copper hydroxide (Cu(OH).sub.2) to ETFAA. The complex is formed rapidly at room temperature with high yield:

2ETFAA+Cu(OH).sub.2.fwdarw.Cu(ETFAA).sub.2+2H.sub.2O.

[0046] The antifouling composition of the invention may further comprise one or more biocidal agents capable of preventing the fouling on the surface of an object.

[0047] Such biocidal agents may be inorganic biocidal agents, organometallic biocidal agents or organic biocidal agents.

[0048] Examples of inorganic biocidal agents are copper and copper compounds such as copper oxides, e.g. cuprous oxide and cupric oxide; copper alloys, e.g. copper-nickel alloys; copper salts, e.g. copper thiocyanate (CuSCN), copper sulphide; or barium metaborate.

[0049] Examples of organometallic biocidal agents are zinc 2-pyridinethiol-1-oxide [ZnPT, zinc pyrithione]; organo-copper compounds such as copper 2-pyridinethiol-1-oxide [CuPT, copper pyrithione], copper acetate, copper naphthenate, copper 8-quinolinonate [oxine-copper], copper nonylphenolsulfonate, copper bis(ethylenediamine)bis (dodecylbenzensulfonate) and copper bis(pentachlorophenolate); dithiocarbamate compounds such as zinc N,N-dimethylcarbamodithioate [ziram], zinc ethane-1,2-diylbis(dithiocarbamate) [zineb], manganese ethylenebis(dithiocarbamate) [maneb] or manganese ethylenebis(dithiocarbamate) complexed with zinc salt [mancozeb].

[0050] Examples of organic biocidal agents are heterocyclic compounds such as 2-(tert-butylamino)-4-(cyclopropylamin)-6-(methylthio)-1,3,5-triazine [cybutryne], 4,5-dichloro-2-n-octyl-4-isothiazolin-3-one [DCOIT], 1,2-benzisothiazolin-3-one [BIT], 2-(thiocyanatomethylthio)-1,3-benzothiazole [benthiazole], 3-benzo[b]thien-2-yl-5,6-dihydro-1,4,2-oxathiazine-4-oxide [bethoxazin] and 2,3,5,6-tetrachloro-4-(methylsulphonyl)pyridine; urea derivatives such as 3-(3,4-dichlorophenyl)-1,1-dimethylurea [diuron]; amides and imides of carboxylic acids, sulphonic acids and sulphenic acids such as N-(dichlorofluoromethylthio)phthalimide, N-dichlorofluoromethylthio-N′,N′-dimethyi-N-phenylsulfamide [dichlofluanid], N-dichlorofluoromethylthio-N′,N′-dimethyl-N-p-tolylsulfamide [tolylfluanid] and N-(2,4,6-trichlorophenyl) maleimide; other organic compounds such as pyridine triphenylborane, amine triphenylborane, 3-iodo-2-propynyl-N-butylcarbamate [iodocarb], 2,4,5,6-tetrachloroisophthalonitrile [chlorothalonil], p-((diiodomethyl)sulphonyl) toluene or 4-bromo-2-(4-chlorophenyl)-5-(trifluoromethyl)-1H-pyrrole-3-carbonitrile [tralopyril].

[0051] Other examples of biocidal agents are tetra-alkylphosphonium halogenides, guanidine derivatives, imidazole containing compounds such as 4-[1-(2,3-dimethylphenyl)ethyl]-1H-imidazole [medetomidine] and derivatives, macrocyclic lactones including avermectins and derivatives thereof such as ivermectine, or spinosyns and derivatives thereof such as spinosad, or enzymes such as oxidase, or proteolytically, hemicellulolytically, cellulolytically, lipolytically or amylolytically active enzymes.

[0052] In one embodiment, the antifouling composition of the invention comprises Cu(ETFAA).sub.2 and further one or more biocidal agents selected from the group consisting of copper 2-pyridinethiol-1-oxide (CuPT, copper pyrithione), zinc 2-pyridinethiol-1-oxide (ZnPT, zinc pyrithione), 4,5-dichloro-2-n-octyl-4-isothiazolin-3-one (DCOIT), cuprous oxide (Cu.sub.2O), zinc oxide (ZnO), 4-bromo-2-(4-chlorophenyl)-5-(trifluoromethyl)-1H-pyrrole-3-carbonitrile (tralopyril), zinc ethane-1,2-diylbis(dithiocarbamate) (zineb), zinc N,N-dimethylcarbamodithioate (ziram), 3-(3,4-dichlorophenyl)-1,1-dimethylurea (diuron), copper(I) thiocyanate (CuSCN), 4-[1-(2,3-dimethylphenyl)ethyl]-1H-imidazole (medetomidine), triazines, fluanids and 2,4,5,6-tetrachloroisophthalonitrile (chlorothalonil).

[0053] In a preferred embodiment, the antifouling composition of the invention comprises Cu(ETFAA).sub.2 and one or more biocidal agents selected from the group consisting of CuPT, ZnPT, DCOIT, Cu.sub.2O and tralopyril.

[0054] In a more preferred embodiment, the antifouling composition of the invention comprises Cu(ETFAA).sub.2 and one or more biocidal agent selected from the group consisting of CuPT and Cu.sub.2O. The ratio of Cu(ETFAA).sub.2 (wt %) to CuPT (wt %) and/or the ratio of Cu(ETFAA).sub.2 (wt %) to Cu.sub.2O (wt %) is advantageously from 100:1 to 1:100, preferably from 10:1 to 1:10, and most preferably from 5:1 to 1:5.

[0055] In a specific embodiment, the antifouling composition of the invention comprises Cu(ETFAA).sub.2 and CuPT. The ratio of Cu(ETFAA).sub.2 (wt %) to CuPT (wt %) is advantageously from 100:1 to 1:100, preferably from 10:1 to 1:10, and most preferably from 5:1 to 1:5.

[0056] In another specific embodiment, the antifouling composition of the invention comprises Cu(ETFAA).sub.2 and Cu.sub.2O. The ratio of Cu(ETFAA).sub.2 (wt %) to Cu.sub.2O (wt %) is advantageously from 100:1 to 1:100, preferably from 10:1 to 1:10, and most preferably from 5:1 to 1:5.

[0057] In a more specific embodiment, the antifouling composition of the invention comprises Cu(ETFAA).sub.2, CuPT and Cu.sub.2O, wherein the ratio of Cu(ETFAA).sub.2 (wt %) to CuPT (wt %) is from 5:1 to 2:1, and wherein the ratio of Cu(ETFAA).sub.2 (wt %) to Cu.sub.2O (wt %) is 5:1 to 1:5.

[0058] In another specific embodiment, the antifouling composition of the invention comprises Cu(ETFAA).sub.2 and CuPT and is free of Cu.sub.2O, wherein the ratio of Cu(ETFAA).sub.2 (wt %) to CuPT (wt %) is from 5:1 to 2:1.

[0059] The antifouling compositions of the invention comprising Cu(ETFAA).sub.2 not only provide excellent antifouling properties, but are also essentially colorless and hence do not interfere with the bright colors oftentimes desired for ship hulls.

[0060] The present invention further provides the use of the antifouling compositions of the invention for the inhibition of marine biofouling on a solid surface. The solid surface may be any solid surface of underwater objects such as ships, an aquaculture fishnet, an underwater structure and equipment, a tank, an offshore construction, a pipe, a net, a pier, a pile or a pillar or the like.

[0061] The antifouling compositions of the invention may further be used in combination with a polymer and/or copolymer allowing the controlled release of Cu(ETFAA).sub.2, and if present also the controlled release of said one or more biocidal agents comprised therein, e.g., by releasing these agents from an antifouling coating overtime as is the case with self-polishing or ablative coatings.

[0062] The inventors have surprisingly found that Cu(ETFAA).sub.2 is a versatile agent that may be used in all types of antifouling coatings, i.e., in antifouling coatings based on various different polymers and/or copolymers typically used as binders for antifouling coating compositions. Thus, the polymers and/or copolymers allowing the controlled release of Cu(ETFAA).sub.2, and if present also the controlled release of said one or more biocidal agents comprised therein, may be any polymers and/or copolymers typically used as binder in antifouling coatings. Suitable polymers and/or copolymers for that purpose are known to the person skilled in the art. Depending on the amount and kind of binder used, Cu(ETFAA).sub.2 and the one or more biocidal agents will be released in a controlled manner at a predetermined desired rate, e.g., that is appropriate for the sailing pattern of a ship.

[0063] For example, the polymers and/or copolymers that are used as binders in “self-polishing antifouling coatings” allowing the controlled release of Cu(ETFAA).sub.2 and said one or more biocidal agents may be hydrolysable acrylate polymers such as (meth)acrylate based polymers and/or copolymers. The (meth)acrylate monomer moiety in a (meth)acrylate polymer and/or copolymer may be an alkyl (meth)acrylate, for example a methyl (meth)acrylate, ethyl (meth)acrylate, propyl (meth)acrylate, isopropyl (meth)acrylate, butyl (meth)acrylate, isobutyl (meth)acrylate, tert-butyl (meth)acrylate, pentyl (meth)acrylate, hexyl (meth)acrylate, heptyl (meth)acrylate, cyclohexyl (meth)acrylate, octyl (meth)acrylate, iso-octyl (meth)acrylate, 2-ethylhexyl (meth)acrylate, 3,5,5-trimethylhexyl (meth)acrylate, lauryl (meth)acrylate, cetyl (meth)acrylate and stearyl (meth)acrylate; but also phenyl (meth)acrylate; benzyl (meth)acrylate; or an alkoxyalkyl (meth)acrylate such as methoxymethyl (meth)acrylate, 2-methoxyethyl (meth)acrylate, ethoxymethyl (meth)acrylate, 2-ethoxyethyl (meth)acrylate, 4-methoxybutyl (meth)acrylate, methoxypropyl (meth)acrylate, ethoxypropyl (meth)acrylate, propoxyethyl (meth)acrylate, 2-butoxyethyl (meth)acrylate, isobutoxybutyl diglycol (meth)acrylate; but also a phenoxyethyl (meth)acrylate; or a hydroxyalkyl (meth)acrylate such as hydroxymethyl (meth)acrylate, 2-hydroxyethyl (meth)acrylate, 2-hydroxypropyl (meth)acrylate, 4-hydroxybutyl (meth)acrylate or 2-hydroxy-3-phenoxypropyl (meth)acrylate;

[0064] the (meth)acrylate monomer moiety in a (meth)acrylate polymer and/or copolymer may further be a silyl (meth)acrylate such as tribenzylsilyl (meth)acrylate, trimethylsilyl (meth)acrylate, triethylsilyl (meth)acrylate, tri-isopropylsilyl (meth)acrylate, tri-n-butylsilyl (meth)acrylate, tri-isobutylsilyl (meth)acrylate, tri-t-butylsilyl (meth)acrylate, tri-n-amylsilyl (meth)acrylate, tri-n-dodecylsilyl (meth)acrylate, tri-n-hexylsilyl (meth)acrylate, tri-n-octylsilyl (meth)acrylate, tri-n-propylsilyl (meth)acrylate or triphenylsilyl (meth)acrylate;

[0065] the (meth)acrylate polymers and/or copolymers may also comprise a metal salt moiety of acrylic or methacrylic acid, referred to herein as a “metal salt (meth)acrylate”. The metal may be any suitable metal known to the skilled artisan, e.g., zinc, calcium, magnesium, lithium, iron, zirconium, aluminum, cobalt, zirconium, barium and bismuth.

[0066] The polymer and/or copolymer allowing the controlled release of Cu(ETFAA).sub.2, and if present also the controlled release of said one or more biocidal agents, may also be a VAGH copolymer. The VAGH copolymer may be dissolved in 2:3 xylene:MIBK.

[0067] Thus, in one embodiment, the polymer and/or copolymer allowing the controlled release of Cu(ETFAA).sub.2, and if present also the controlled release of said one or more biocidal agents comprises a (meth)acrylate polymer and/or copolymer, or a VAGH copolymer. The (meth)acrylate polymer and/or copolymer may be a polymer or copolymer of monomer moieties selected from the group consisting of alkyl (meth)acrylate, phenyl (meth)acrylate, benzyl (meth)acrylate, alkoxyalkyl (meth)acrylate, hydroxyalkyl (meth)acrylate, zinc (meth)acrylates, and silyl-(meth)acrylate; or the (meth)acrylate polymer and/or copolymer may be a polymer or copolymer of monomer moieties selected from the group consisting of ethyl acrylate, methyl methacrylate, butyl acrylate, 2-methoxyethyl acrylate, zinc methacrylate, and tri-isopropylsilyl acrylate, preferably, the (meth)acrylate polymer and/or copolymer is a copolymer of monomer moieties selected from the group consisting of ethyl acrylate, methyl methacrylate, and zinc methacrylate, more preferably, the (meth)acrylate polymer polymer and/or copolymer is a copolymer of monomer moieties selected from the group consisting of ethyl acrylate, methyl methacrylate, 2-methoxyethyl acrylate and zinc methacrylate, and most preferably, the (meth)acrylate polymer polymer and/or copolymer is a copolymer of monomer moieties selected from the group consisting of methyl methacrylate, butyl acrylate, 2-methoxyethyl acrylate and tri-isopropylsilyl acrylate.

[0068] Consequently, the invention further provides an antifouling paint comprising the antifouling composition of the invention and a polymer and/or copolymer allowing the controlled release of Cu(ETFAA).sub.2, and if present also the controlled release of said one or more biocidal agents.

[0069] The content of Cu(ETFAA).sub.2 in the antifouling paint of the invention is from about 1 to about 25 wt %, preferably from about 3 to about 20 wt %, and more preferably from about 4 to about 18 wt %, and most preferably from about 5 to about 15 wt %.

[0070] Due to the excellent enhancing properties of Cu(ETFAA).sub.2, only low amounts of said one or more biocidal agents are required in the antifouling paint of the invention. The total content of the one or more biocidal agents in the antifouling paint of the invention is less than about 30 wt %, preferably less than about 25 wt %, more preferably less than about 20 wt %, and most preferably less than about 18 wt %.

[0071] The total content of CuPT in the antifouling paint of the invention is less than about 10 wt %, more preferably less than about 8 wt %, and most preferably less than about 7 wt %.

[0072] The total content of Cu.sub.2O in the antifouling paint of the invention is less than about 20 wt %, more preferably less than about 15 wt %, and most preferably less than about 12 wt %.

[0073] Thus, the content of toxic metal compounds, in particular of Cu.sub.2O, is kept at a very low level, and can even be avoided.

[0074] The present invention further provides a method for inhibiting marine biofouling on a solid surface, characterized in that an antifouling paint comprising the antifouling composition of the invention is applied on said surface. The solid surface may be any solid surface of underwater objects such as ships, an aquaculture fishnet, an underwater structure and equipment, a tank, an offshore construction, a pipe, a net, a pier, a pile or a pillar and the like.

[0075] In the following, the present invention will be further described with reference to Examples, but should be construed that the present invention is in no way limited to these Examples.

EXAMPLES

Example 1: Preparation of Exemplary Polymer-Based Binders for Antifouling Paints

[0076] Different exemplary polymer-based binders that can be used in self-polishing antifouling paints or hybrid coatings have been prepared as outlined in the following.

Example 1A: Synthesis of an Acrylate Polymer “Acid Acrylate Low Acid Value” Referred to Herein as “Ac (AV=100−)”

[0077]

TABLE-US-00001 Description Quantity (g) Weight (%) MPM 355.03 11.83 Xylene 671.01 22.37 ethyl acrylate 56.8 1.89 bring to 100° C. while mixing and drop into the following mixture over 6 hours methyl methacrylate 213.02 7.1 ethyl acrylate 1009.47 33.65 methacrylic acid 149.11 4.97 Xylene 147.93 4.93 Methyl Styrene Dimer 14.2 0.47 AIBN 35.5 1.18 AMBN 99.41 3.31 add chaser and xylene over 1/2 hour t-butylperoxy 2-ethylhexyl carbonate 7.1 0.24 Xylene 143.2 4.77 mix for 90 minutes after chaser is in. Cool down and add Xylene 98.22 3.27 Total 3000 100 Manual Yield % 100 Net 3000

Example 1B: Synthesis of an Acrylate Polymer “Acid Acrylate 100 Acid Value” Referred to Herein as “Ac (AV=100)”

[0078]

TABLE-US-00002 Description Quantity (g) Weight (%) MPM 355.5 11.85 Xylene 668.4 22.28 ethyl acrylate 56.7 1.89 bring to 100° C. while mixing and drop into the following mixture over 6 hours methyl methacrylate 142.2 4.74 ethyl acrylate 867.3 28.91 methacrylic acid 142.2 4.74 2-methoxyethyl acrylate 213.6 7.12 Xylene 142.2 4.74 Methyl Styrene Dimer 14.1 0.47 AIBN 35.4 1.18 AMBN 99.3 3.31 add chaser and xylene over 1/2 hour t-butylperoxy 2-ethylhexyl carbonate 7.2 0.24 Xylene 142.2 4.74 mix for 90 minutes after chaser is in. Cool down and add Xylene 113.7 3.79 Total 3000 100 Manual Yield % 100 Net 3000

Example 1C: Synthesis of a Binder Component Using the Acrylate Polymer “Ac(AV=100−)” to Give a Zinc Acrylate Polymer Referred to Herein as “Zn—Ac (AV=100−)”

[0079]

TABLE-US-00003 Description Quantity (g) Weight (%) Ac (AV = 100−) 3000 82.395 Zinc Oxide 81 2.225 zinc naphthenate 560 15.38 Mix for 6 hours at 100° C. and add 20 g water if ZnO is not dissolved after 6 hours Total 3641 100 Manual Yield % 100 Net 3641

Example 1D: Synthesis of a Binder Component Using the Acrylate Polymer “Ac (AV=100)” to Give a Zinc Acrylate Polymer Referred to Herein as “Zn—Ac (AV=100)”

[0080]

TABLE-US-00004 Description Quantity (g) Weight (%) Ac (AV = 100) 3000 75.82 Zinc Oxide 106.5 2.69 zinc naphthenate 850 21.48 Mix for 6 hours at 100° C. and add 20 g water if ZnO is not dissolved after 6 hours Total 3956.5 100 Manual Yield % 100 Net 3956.5

Example 1E: Synthesis of a Silyl Acrylate Polymer Standard TIPX Binder Component Referred to Herein as “Si—Ac”

[0081]

TABLE-US-00005 Description Quantity (g) Weight (%) Xylene 1826 45.65 add the following monomer mixture dropwise over 3 hours at 90° C. methyl methacrylate 665.4 16.64 butyl acrylate monomer 228 5.7 2-methoxyethyl acrylate 99.2 2.48 trisopropysilyl acrylate monomer (TIPX) 992.4 24.81 AIBN 20 0.5 after all monomer added, mix for additional 2 hours at 90° C., then add t-butylperoxy 2-ethylhexyl carbonate 10 0.25 Xylene 159 3.98 drop xylene mixture over 1/2 hour at 90° C., then mix another 1 hour before cooling down Total 4000 100 Manual Yield % 100 Net 4000

Example 1F: Synthesis of Silyl Acrylate Polymer Lower TIPX Binder Component Referred to Herein as “Si—Ac (TIPX-L)”

[0082]

TABLE-US-00006 Description Quantity (g) Weight (%) Xylene 1826 45.65 add the following monomer mixture dropwise over 3 hours at 90° C. methyl methacrylate 912 22.8 butyl acrylate monomer 310 7.75 2-methoxyethyl acrylate 60 1.5 trisopropysilyl acrylate monomer 703 17.58 AIBN 20 0.5 after all monomer added, mix for additional 2 hours at 90° C., then add t-butylperoxy 2-ethylhexyl carbonate 10 0.25 Xylene 159 3.98 Total 4000 100 Manual Yield % 100 Net 4000

Example 2: Comparison of Potency of Cu.SUB.2.O and Cu(ETFAA).SUB.2 .in Antifouling Paints

[0083] In order to confirm that the amount of Cu.sub.2O can be significantly reduced and even avoided if Cu(ETFAA).sub.2 is present in antifouling paints, the efficacy of a set of self-polishing antifouling paints was evaluated by immersing experimental painted panels in seawater on a test raft. Two self-polishing antifouling paints containing a silyl acrylate polymer as binder component and either Cu(ETFAA).sub.2 and CuPT (“experimental paint”) or Cu.sub.2O and CuPT (“control paint”) have been prepared for this purpose (cf., Table 1). The synthesis of the silyl acrylate polymer component used in these paints is provided in Example 1E above.

TABLE-US-00007 TABLE 1 Composition of the experimental paint and control paint: Paint Experimental Control Ingredient % wt Volume (ml) % wt Volume (ml) Si-Ac 50% in xylene 25.0 25.25 25.0 25.25 Gum Rosin 50% in xylene 5.0 5.15 5.0 5.15 Tricresyl phosphate 2.0 1.72 2.0 1.72 Fe.sub.2O.sub.3 3.0 0.52 3.0 0.52 Talc 2.5 0.91 0.0 0 ZnO 5.0 0.89 5.0 0.89 Bentonite clay 1.0 0.59 1.0 0.59 A630-20X polyamide wax 2.5 2.75 2.5 2.75 PGM 2.0 2.17 2.0 2.17 Ethyl Silicate 0.5 0.53 0.5 0.53 Xylene 10.0 11.61 10.0 11.61 Cu.sub.2O 0 0 40.0 6.78 CuPT 4.0 2.20 4.0 2.20 Cu(ETFAA).sub.2 8.2 4.50 0 0 Total 70.7 58.79 100.0 60.41

[0084] Because cuprous oxide is about 3 times more dense than Cu(ETFAA).sub.2, the addition of 2.5 g of talc was used to bring the volume of talc and Cu(ETFAA).sub.2 to about the volume of cuprous oxide in the paint. Adding more talc to fully make up for the volume of cuprous oxide would affect the amount of free binder since talc has a higher binder demand (surface area/gram) than cuprous oxide.

[0085] Results: The results after 24 months immersion in sea water from September 2015 until September 2017 are shown in FIG. 1, which shows pictures of the panels in the un-rinsed state and after rinsing. The rinsing of the panels with a low pressure stream of water simulates the slow movement of a boat. The movement of a boat will loosen and remove any of the loosely attached fouling. The “experimental paint” containing Cu(ETFAA).sub.2 and copper pyrithione effectively inhibited the growth of marine organisms, and was more potent in this regard than the control paint containing 40 wt % cuprous oxide and copper pyrithione. The experimental paint eroded slightly faster than the control paint. This was expected due to the known property of cuprous oxide of lowering the rate of erosion of the silyl acrylate polymer.

Example 3: Preparation of Antifouling Paints

[0086] Three sets of antifouling paints were prepared based on binder technologies used for different types of marine antifouling paints. Exemplary paints were prepared that included either self-polishing binder types, i.e., based on zinc acrylate polymers and silyl acrylate polymers in two different amounts of the functional monomer (zinc acrylate monomer or silyl acrylate monomer), or an ablative binder type based on rosin and a non-eroding VAGH polymer. Since the volumes of the materials for making the paints affect the properties of the paint, such as dry film thickness and amount of antifouling agent in the dry film, the volume solids of the materials in the formulations were kept essentially constant in each class of coating except where they were purposely varied to observe the effects of the material on the antifouling performance.

Self-Polishing Antifouling Paints Based on a “Zinc Acrylate Polymer-Based Binder”

[0087] Experimental Paint Nos 4, 11, 12 and control paint 69, all using the zinc acrylate polymer referred to herein as “Zn—Ac (AV=100)” according to example 1D as a binder component

TABLE-US-00008 Experimental Paint 4 11 12 69 % Weight Zn-Ac (AV = 100) 28.51 23.73 20.79 17.51 Gum Rosin/Xylene 1:1 — 6.4 9.71 8.00 Xylene 4.24 3.78 3.48 2.50 TiO2 R902+ 15.59 25.94 25.94 — Cu.sub.2O — 2.70 2.70 41.27 Zinc Oxide 15.59 — — 5.00 Bentone SD 2 0.39 0.40 0.40 0.38 red iron oxide 1.56 1.62 1.62 1.50 CuPT 3.95 4.05 4.05 3.33 Cu(ETFAA).sub.2 8.34 8.66 8.66 — Zn-Ac (AV = 100) 16.63 17.26 17.26 16.01 Xylene 5.20 5.39 5.39 4.50 Total 100.00 100.0 100.00 100.00

[0088] Experimental Paint Nos 22, 25, 20, 23 and 26 all using the zinc acrylate polymer referred to herein as “Zn—Ac (AV=100-)” according to example 1C as a binder component

TABLE-US-00009 Experimental Paint 22 25 20 23 26 % Weight Zn-Ac (AV = 100−) 29.35 29.17 23.02 23.53 23.32 Gum Rosin/Xylene 1:1 — — 6.37 6.51 6.46 Xylene 4.43 4.40 3.72 3.80 3.77 TiO2 R902+ 26.14 23.77 19.73 26.11 24.07 Zinc Oxide — — 10.62 — — Bentone SD 2 0.41 0.41 0.40 0.41 0.40 red iron oxide 1.63 1.62 1.59 1.63 1.61 CuPT 4.08 4.08 3.98 4.07 4.03 Cu(ETFAA).sub.2 8.70 8.73 8.52 8.71 8.63 Cu.sub.2O 2.72 5.4 — 2.71 5.38 Zn-Ac (AV = 100−) 17.12 17.02 16.73 17.10 16.94 Xylene 5.43 5.40 5.31 5.43 5.38 Total 100.00 100.00 100.00 100.00 100.00

Ablative Antifouling Paints

[0089] Experimental Paint Nos 32, 36, 37, 108A, 108B and 108C as well as control paint 70, all using a commercial VAGH polymer as a binder component

TABLE-US-00010 Paint 32 36 37 70 101 104 % Weight VAGH (22%) 11.32  31.58  19.07  15.69  16.80 16.80 in 2:3 xylene:MIBK Gum Rosin/ 32.3  19.12  25.68  17.17  17.78 17.78 Xylene 1:1 Tricresyl 3.66 3.19 4.28 2.70 3.17 3.17 Phosphate Disperbyk 161 1.83 1.59 2.14 1.35 1.30 1.30 Minex 4 — — — 8.58 8.24 8.24 Bentone SD 2 0.57 0.49 0.66 0.42 3.94 3.94 Zinc Oxide 9.32 — — 4.90 22.19 22.19 Cu.sub.2O — 8.55 5.06 36.78  — — CuPT 3.50 3.01 3.27 2.70 — — DCOIT — — — — — 16.03 TiO2 R902+ 15.98  13.90  19.46  — — — red iron oxide 2.20 1.91 2.57 1.62 — — Cu(ETFAA).sub.2 7.49 6.37 6.93 — 16.03 — Gum Rosin/ 9.16 7.97 7.78 3.68 — — Xylene 1:1 Disparlon 2.66 2.32 3.11 1.96 1.99 1.99 6900-20x Xylene — — — 2.45 8.56 8.56 Total 100.00  100.00  100.00  100.00  100.00 100.00

[0090] Experimental paint 108A: 1:1 mixture of experimental paints 101 and 104

[0091] Experimental paint 1081B: 5:3 mixture of experimental paints 101 and 104

[0092] Experimental paint 108C: 3:5 mixture of experimental paints 101 and 104

Self-Polishing Antifouling Paints Based on a “Silyl Acrylate” Polymer-Based Binder

[0093] Experimental Paint Nos 53, 60, 61, 63, 64, 66, 67 and 111 all using the silyl acrylate polymers referred to as “Si—Ac” or “Si—Ac (TIPX-L)” according to examples 1E and 1F as binder components

TABLE-US-00011 Experimental paint 53 60 61 63 64 66 67 111 % Weight Si—Ac 48.88  — — — — — — — Si—Ac — 35.35  28.60  35.35 28.60 35.35 28.60 42.16  (TIPX-L) Gum Rosin/ — 14.15  21.25  14.15 21.25 14.15 21.25 2.61 Xylene 1:1 Tricresyl 2.83 2.83 2.83 2.83 2.83 2.80 2.75 3.14 Phosphate CuPT 5.65 5.65 5.58 5.65 5.55 5.50 5.45 — Cu(ETFAA).sub.2 11.58  11.5  11.4  11.5 11.35 11.25 11.13 16.03  red iron oxide 4.00 4.25 4.25 4.25 4.25 4.25 4.25 — Cu.sub.2O 11.48  — — 7.5 7.5 11.25 11.0 — Minex 4 — 3.53 3.55 3.25 3.20 0.25 0.60 3.48 Zinc Oxide — 7.08 7.08 — — — — 7.84 Xylene — — — — — — — 9.71 Bentone SD 2 1.38 1.43 1.43 3.53 3.53 1.40 1.43 1.57 Disparlon 3.53 3.53 3.53 2.83 2.83 3.53 3.53 3.83 6900-20x MPM 2.75 2.83 2.83 0.70 0.70 2.83 2.83 — tetra ethyl 0.70 0.70 0.70 7.05 7.00 0.70 0.70 — ortho silicate Xylene 7.25 7.20 7.00 1.43 1.43 6.75 6.50 9.62 Total 100.00  100.00  100.00  100.00 100.00 100.00 100.00 100.00 

[0094] Each class of antifouling paint (i.e., based on the different binder types) may display some variations in the ratios of the specific materials used due to differences in how the materials interact and affect properties such as applicability and viscosity. The skilled artisan will understand that it is sometimes necessary to not have equivalent properties between the different classes of coatings such as volume solids because of the effects of the materials on application and viscosity of the coating. Variability in the compositions is also allowed (and warranted) to account for anticipated leach rates of the antifouling agents. For example, the antifouling agents will leach out from paints based on silyl acrylate based binders at a slower rate than from paints based on ablative binders or zinc acrylate based binders. Therefore, higher amounts of antifouling agents are used in paints based on silyl acrylate based binders because static raft testing requires a relatively high leach rate of antifouling agent to prevent fouling.

Example 5: Antifouling Experiment

[0095] The antifouling paints of Example 4 above were evaluated with regard to antifouling properties. Fiberglass (FRP) panels have been coated with these paints. Because the dry film thickness will have an effect on the antifouling performance, this has been carefully controlled by weighing the FRP panels after each coat of paint has dried and adjusting the weight of applied paint for the density of the dry paint to give a target dry film thickness of 150 μm. All the painted panels are within 10 μm of 150 μm dry film thickness.

[0096] The test panel dimensions were 457 mm×102 mm×3.33 mm. Therefore the volume of dry coating for the front of the panel required for 150 μm dry film thickness is 6.992 ml. The volume required for the back side and the edges is 6.992+0.533=7.525 ml. The volume of paint applied was not measured, but calculated by the density of the dry paint and the weight of the dry paint applied. [0097] a) Weight of dry paint applied to front of panel=6.992 ml×density of paint solids (g/ml) [0098] b) Weight of dry paint applied to back and edges of panel=7.525 ml×density of paint solids

[0099] The test panels were exposed to sea-water. The results after 2, 4, 6 and 8 months of immersion are shown in the following Table 2. All of the antifouling paints according to the invention exhibited excellent antifouling properties.

TABLE-US-00012 TABLE 2 Antifouling properties of antifouling paints Binder components Biocidal Antifouling property against marine organisms Rosin 1:1 agents Animal Algae IN XYLENE Cu(ETFAA).sub.2 Cu.sub.2O CuPT 2 m 4 m 6 m 8 m 2 m 4 m 6 m 8 m No Polymer % wt % wt % wt % wt Aut Winter Spr Aut Winter Spr SPC  4 Zn—Ac (AV = 100) — 8.34 — 3.95 4 4 4 4 4 4 3 3 SPC-Hybrid 11 Zn—Ac (AV = 100) 6.47 8.66 2.7 4.05 4 4 4 4 4 3 3 3 SPC-Hybrid 12 Zn—Ac (AV = 100) 9.71 8.66 2.7 4.05 4 4 4 4 4 3 3 3 control 69 Zn—Ac (AV = 100) 8.00 — 41.27 3.33 4 4 4 4 4 3 2 2 SPC 22 Zn—Ac (AV = 100-) — 8.70 2.72 4.08 4 4 4 4 4 4 4 4 SPC 25 Zn—Ac (AV = 100-) — 8.73 5.4 4.08 4 4 4 4 4 4 4 4 SPC-Hybrid 20 Zn—Ac (AV = 100-) 6.37 8.52 — 3.98 4 4 4 4 4 4 3 4 SPC-Hybrid 23 Zn—Ac (AV = 100-) 6.51 8.71 2.71 4.07 4 4 4 4 4 4 4 4 SPC-Hybrid 26 Zn—Ac (AV = 100-) 6.46 8.63 5.38 4.03 4 4 4 4 4 4 4 4 Ablative 32 VAGH 32.3 7.49 — 3.50 4 4 4 4 4 4 4 3 Ablative 36 VAGH 19.12 6.37 8.55 3.01 4 4 4 4 4 4 4 4 Ablative 37 VAGH 25.68 6.93 5.06 3.27 4 4 4 4 4 4 4 4 Control 70 VAGH 17.17 — 36.78 2.70 4 4 4 4 4 4 4 4 SPC 53 Si—Ac — 11.58 11.48 5.65 4 4 4 4 4 4 4 4 SPC-Hybrid 60 Si—Ac (TIPX-L) 14.15 11.5 — 5.65 4 4 4 4 4 4 4 4 SPC-Hybrid 61 Si—Ac (TIPX-L) 21.25 11.4 — 5.58 4 4 4 4 4 4 4 4 SPC-Hybrid 63 Si—Ac (TIPX-L) 14.15 11.5 7.5 5.65 4 4 4 4 4 3 2 2 SPC-Hybrid 64 Si—Ac (TIPX-L) 21.25 11.35 7.5 5.55 4 4 4 4 4 3 2 2 SPC-Hybrid 66 Si—Ac (TIPX-L) 14.15 11.25 11.25 5.50 4 4 4 4 4 3 2 2 SPC-Hybrid 67 Si—Ac (TIPX-L) 21.25 11.13 11.0 5.45 4 4 4 4 4 3 2 2 Biocidal Antifouling property against marine organisms Binder components agents Animal Algae Rosin Cu(ETFAA).sub.2 DCOIT 2 m 4 m 6 m 8 m 2 m 4 m 6 m 8 m No Polymer % wt % wt % wt Aut Winter Spr Aut Winter Spr Ablative 108A VAGH 17.78 8 8 4 4 4 4 4 4 4 4 Ablative 108B VAGH 17.78 10 6 4 4 4 4 4 4 4 4 Ablative 108C VAGH 17.78 6 10  4 4 4 4 4 4 4 4 SPC 111 .sup.  Si—Ac (TIPX-L) 2.61 16.03 — 4 4 4 4 4 4 3 .sup. 3.sup.5
Details of the categories applied for the results are explained in the following.
Antifoulinq properties with regard to Algae: Antifoulinq properties with regard to animals such as barnacles, bryozoans, hydroids, mussels and the like
Excellent (4): No algae.
Good (3): It is thin and covered with slime. Excellent (4): No animal.
Fair (2): It is thick and covered with slime. Good (3): It is covered with small and very few animals.
Poor (1): It is thick and covered with slime and/or few algae. Fair (2): It is covered with small and few animals.
Bad (0): It is thick and covered with slime and/or many algae. Poor (1): It is covered with small/large and few animals.
Bad (0): It is covered with small/large and many animals.