Polymerizable polar compound, liquid crystal composition and liquid crystal display device
11299675 · 2022-04-12
Assignee
Inventors
Cpc classification
C07C69/94
CHEMISTRY; METALLURGY
C09K2019/3413
CHEMISTRY; METALLURGY
C09K2019/3425
CHEMISTRY; METALLURGY
C09K19/2028
CHEMISTRY; METALLURGY
C09K19/2007
CHEMISTRY; METALLURGY
C09K19/32
CHEMISTRY; METALLURGY
C09K19/3477
CHEMISTRY; METALLURGY
G02F1/139
PHYSICS
C07C69/618
CHEMISTRY; METALLURGY
C07C69/90
CHEMISTRY; METALLURGY
C09K19/12
CHEMISTRY; METALLURGY
International classification
C09K19/12
CHEMISTRY; METALLURGY
G02F1/139
PHYSICS
Abstract
A polar compound having high chemical stability, high capability of aligning liquid crystal molecules, high solubility in a liquid crystal composition, and a large voltage holding ratio when the compound is used in a liquid crystal display device; and a composition containing the compound. The compound is represented by formula (1). In formula (1), for example, P.sup.1 is a group represented by any one of formulas (1b) to (1i), P.sup.2 is a group represented by formula (1d), Sp.sup.1 and Sp.sup.2 are a single bond, Z.sup.1, Z.sup.2, Z.sup.3, Z.sup.4 and Z.sup.5 are —COO—, and ring A.sup.1, ring A.sup.2, ring A.sup.3 and ring A.sup.4 are 1,4-phenylene: ##STR00001##
Claims
1. A compound, represented by formula (1): ##STR00696## wherein, in formula (1), a and b are independently 0, 1 or 2, wherein 0≤a+b≤3, ring A.sup.1, ring A.sup.2, ring A.sup.3 and ring A.sup.4 are independently 1,4-cyclohexylene, 1,4-cyclohexenylene, 1,4-phenylene, naphthalene-2,6-diyl, decahydronaphthalene-2,6-diyl, 1,2,3,4-tetrahydronaphthalene-2,6-diyl, tetrahydropyran-2,5-diyl, 1,3-dioxane-2,5-diyl, pyrimidine-2,5-diyl, pyridine-2,5-diyl, fluorene-2,7-diyl, phenanthrene-2,7-diyl, anthracene-2,6-diyl, perhydrocyclopenta[a]phenanthrene-3,17-diyl or 2,3,4,7,8,9,10,11,12,13,14,15,16,17-tetradecahydrocyclopenta[a]phenanthrene-3,17-diyl, and in the rings, at least one hydrogen may be replaced by fluorine, chlorine, alkyl having 1 to 12 carbons, alkenyl having 2 to 12 carbons, alkoxy having 1 to 11 carbons or alkenyloxy having 2 to 11 carbons, and in the groups, at least one hydrogen may be replaced by fluorine or chlorine, and when a is 2, two of ring A.sup.1 may be different, and when b is 2, two of ring A.sup.4 may be different; Z.sup.1, Z.sup.2, Z.sup.3, Z.sup.4 and Z.sup.5 are independently a single bond or alkylene having 1 to 10 carbons, and in the alkylene, at least one —CH.sub.2— may be replaced by —O—, —CO—, —COO—, —OCO— or —OCOO—, and at least one —(CH.sub.2).sub.2— may be replaced by —CH═CH— or —C≡C—, and in the groups, at least one hydrogen may be replaced by halogen, in which at least one in Z.sup.2, Z.sup.3 or Z.sup.4 is —COO—, —OCO—, —CH═CHCOO—, —OCOCH═CH—, —CH═CH—, —CH═CHCO— or —COCH═CH—, and when a is 2, two Z*s may be different, and two Z.sup.5s may be different; Sp.sup.1 and Sp.sup.2 are independently a single bond or alkylene having 1 to 10 carbons, and in the alkylene, at least one —CH.sub.2— may be replaced by —O—, —CO—, —COO—, —OCO— or —OCOO—, and at least one —(CH.sub.2).sub.2— may be replaced by —CH═CH— or —C≡C—, and in the groups, at least one hydrogen may be replaced by halogen; P.sup.1 is a group represented by any one of formulas (1b) to (1i); and P.sup.2 is a group represented by formula (1d); ##STR00697## wherein, in formulas (1b) to (1i), M.sup.1 and M.sup.2 are independently hydrogen, halogen, alkyl having 1 to 5 carbons, or alkyl having 1 to 5 carbons in which at least one hydrogen is replaced by halogen; R.sup.2 is hydrogen, halogen or alkyl having 1 to 5 carbons, and in the alkyl, at least one hydrogen may be replaced by halogen, and at least one —CH.sub.2— may be replaced by —O—; and R.sup.3, R.sup.4 and R.sup.5 are independently hydrogen or alkyl having 1 to 15 carbons, and in the alkyl, at least one —CH.sub.2— may be replaced by —O— or —S—, and at least one —(CH.sub.2).sub.2— may be replaced by —CH═CH— or —C≡C—, and in the groups, at least one hydrogen may be replaced by halogen.
2. The compound according to claim 1, represented by formula (1): ##STR00698## wherein, in formula (1), a and b are independently 0, 1 or 2, wherein 0≤a+b≤2; ring A.sup.1, ring A.sup.2, ring A.sup.3 and ring A.sup.4 are independently 1,4-cyclohexylene, 1,4-cyclohex enylene, 1,4-phenylene, naphthalene-2,6-diyl, decahydronaphthalene-2,6-diyl, 1,2,3,4-tetrahydronaphthalene-2,6-diyl, tetrahydropyran-2,5-diyl, 1,3-dioxane-2,5-diyl, pyrimidine-2,5-diyl, pyridine-2,5-diyl, fluorene-2,7-diyl, phenanthrene-2,7-diyl, anthracene-2,6-diyl, perhydrocyclopenta[a]phenanthrene-3,17-diyl or 2,3,4,7,8,9,10,11,12,13,14,15,16,17-tetradecahydrocyclopenta[a]phenanthrene-3,17-diyl, and in the rings, at least one hydrogen may be replaced by fluorine, chlorine, alkyl having 1 to 12 carbons, alkenyl having 2 to 12 carbons, alkoxy having 1 to 11 carbons or alkenyloxy having 2 to 11 carbons, and in the groups, at least one hydrogen may be replaced by fluorine or chlorine, and when a is 2, two of ring A.sup.1 may be different, and when b is 2, two of ring A.sup.4 may be different; Z.sup.1, Z.sup.2, Z.sup.3, Z.sup.4 and Z.sup.5 are independently a single bond, —(CH.sub.2).sub.2—, —C≡C—, —COO—, —OCO—, —CF.sub.2O—, —OCF.sub.2—, —CH.sub.2O—, —OCH.sub.2—, —CF═CF—, —CH═CHCOO—, —OCOCH═CH—, —CH═CH—, —CH═CHCO— or —COCH═CH—, in which at least one in Z.sup.2, Z.sup.3 or Z.sup.4 is —COO—, —OCO—, —CH═CHCOO—, —OCOCH═CH—, —CH═CH—, —CH═CHCO— or —COCH═CH—, and when a is 2, two Z's may be different, and two Z.sup.5s may be different; Sp.sup.1 and Sp.sup.2 are independently a single bond or alkylene having 1 to 10 carbons, and in the alkylene, at least one —CH.sub.2— may be replaced by —O—, —COO— or —OCO—, and at least one —(CH.sub.2).sub.2— may be replaced by —CH═CH—, and in the groups, at least one hydrogen may be replaced by fluorine or chlorine; and P.sup.1 is a group represented by any one of formulas (1b) to (1i), and P.sup.2 is a group represented by formula (1d); ##STR00699## wherein, in formulas (1b) to (1i), M.sup.1 and M.sup.2 are independently hydrogen, halogen, alkyl having 1 to 5 carbons, or alkyl having 1 to 5 carbons in which at least one hydrogen is replaced by halogen; R.sup.2 is hydrogen, halogen or alkyl having 1 to 5 carbons, and in the alkyl, at least one hydrogen may be replaced by halogen, and at least one —CH.sub.2— may be replaced by —O—; and R.sup.3, R.sup.4 and R.sup.5 are independently hydrogen or alkyl having 1 to 15 carbons, and in the alkyl, at least one —CH.sub.2— may be replaced by —O— or —S—, and at least one —(CH.sub.2).sub.2— may be replaced by —CH═CH— or —C≡C—, and in the groups, at least one hydrogen may be replaced by halogen.
3. The compound according to claim 1, represented by any one of formulas (1-1) to (1-3): ##STR00700## wherein, in formulas (1-1) to (1-3), R.sup.5 is hydrogen or alkyl having 1 to 15 carbons, and in the alkyl, at least one —CH.sub.2— may be replaced by —O— or —S—, and at least one —(CH.sub.2).sub.2— may be replaced by —CH═CH— or —C≡C—, and in the groups, at least one hydrogen may be replaced by halogen; ring A.sup.1, ring A.sup.2, ring A.sup.3 and ring A.sup.4 are independently 1,4-cyclohexylene, 1,4-phenylene, naphthalene-2,6-diyl, pyrimidine-2,5-diyl, pyridine-2,5-diyl, fluorene-2,7-diyl, phenanthrene-2,7-diyl or anthracene-2,6-diyl, and in the rings, at least one hydrogen may be replaced by fluorine, chlorine, alkyl having 1 to 12 carbons, alkenyl having 2 to 12 carbons, alkoxy having 1 to 11 carbons or alkenyloxy having 2 to 11 carbons, and in the groups, at least one hydrogen may be replaced by fluorine or chlorine; Z.sup.2, Z.sup.3 and Z.sup.4 are independently a single bond, —(CH.sub.2).sub.2—, —C≡C—, —COO—, —OCO—, —CF.sub.2O—, —OCF.sub.2—, —CH.sub.2O—, —OCH.sub.2—, —CF═CF—, —CH═CHCOO—, —OCOCH═CH—, —CH═CH—, —CH═CHCO— or —COCH═CH—, in which at least one in Z.sup.2, Z.sup.3 and Z.sup.4 is —COO—, —OCO—, —CH═CHCOO—, —OCOCH═CH—, —CH═CH—, —CH═CHCO— or —COCHCH—; Sp.sup.1 and Sp.sup.2 are independently a single bond or alkylene having 1 to 10 carbons, and in the alkylene, at least one —CH.sub.2— may be replaced by —O—, —COO—, —OCOO— or —OCO—, and at least one —(CH.sub.2).sub.2— may be replaced by —CH═CH—, and in the groups, at least one hydrogen may be replaced by fluorine or chlorine; and P.sup.1 is a group represented by any one of formulas (1b) to (1i); ##STR00701## wherein M1 and M2 are independently hydrogen, halogen, alkyl having 1 to 5 carbons, or alkyl having 1 to 5 carbons in which at least one hydrogen is replaced by halogen; R.sup.2 is hydrogen, halogen or alkyl having 1 to 5 carbons, and in the alkyl, at least one hydrogen may be replaced by halogen, and at least one —CH.sub.2— may be replaced by —O—; and R.sup.3, R.sup.4 and R.sup.5 are independently hydrogen or straight-chain, branched-chain or cyclic alkyl having 1 to 15 carbons, and in the alkyl, at least one —CH.sub.2— may be replaced by —O— or —S—, and at least one —(CH.sub.2).sub.2— may be replaced by —CH═CH— or —C≡C—, and in the groups, at least one hydrogen may be replaced by halogen.
4. The compound according to claim 1, represented by any one of formulas (1-1-1), (1-2-1) and (1-3-1): ##STR00702## wherein, in formulas (1-1-1), (1-2-1) and (1-3-1), R.sup.5 is hydrogen or alkyl having 1 to 15 carbons, and in the alkyl, at least one —CH.sub.2— may be replaced by —O— or —S—, and at least one —(CH.sub.2).sub.2— may be replaced by —CH═CH— or —C≡C—, and in the groups, at least one hydrogen may be replaced by halogen; ring A.sup.1, ring A.sup.2, ring A.sup.3 and ring A.sup.4 are independently 1,4-cyclohexylene, 1,4-phenylene or fluorene-2,7-diyl, and in the rings, at least one hydrogen may be replaced by fluorine, chlorine, alkyl having 1 to 12 carbons, alkenyl having 2 to 12 carbons, alkoxy having 1 to 11 carbons or alkenyloxy having 2 to 11 carbons; Z.sup.2, Z.sup.3 and Z.sup.4 are independently a single bond, —COO—, —OCO—, —CH═CHCOO—, —OCOCH═CH—, —CH═CH—, —CH═CHCO— or —COCH═CH—, in which at least one in Z.sup.2, Z.sup.3 and Z.sup.4 is —COO—, —OCO—, —CH═CHCOO—, —OCOCH═CH—, —CH═CH—, —CH═CHCO— or —COCH═CH—; Sp.sup.1 and Sp.sup.2 are independently a single bond or alkyl ene having 1 to 10 carbons, and in the alkylene, at least one —CH.sub.2— may be replaced by —O—, —COO—, —OCOO— or —OCO—, and at least one —(CH.sub.2).sub.2— may be replaced by —CH═CH—; and P.sup.1 is a group represented by any one of formula (1b), (1c) or (1d); ##STR00703## wherein, in formulas (1b) to (1d), R.sup.2 is hydrogen, halogen or alkyl having 1 to 5 carbons, and in the alkyl, at least one hydrogen may be replaced by halogen, and at least one —CH.sub.2— may be replaced by —O—; and R.sup.5 is hydrogen or alkyl having 1 to 15 carbons, and in the alkyl, at least one —CH.sub.2— may be replaced by —O— or —S—, and at least one —(CH.sub.2).sub.2— may be replaced by —CH═CH— or —C≡C—, and in the groups, at least one hydrogen may be replaced by halogen.
5. The compound according to claim 4, represented by any one of formula (1-1-1), (1-2-1) or (1-3-1), wherein any one of Z.sup.2, Z.sup.3 or Z.sup.4 is —COO— or —OCO—.
6. The compound according to claim 4, represented by any one of formula (1-1-1), (1-2-1) or (1-3-1), wherein any one of Z.sup.2, Z.sup.3 or Z.sup.4 is —CH═CHCOO—, —OCOCH═CH—, —CH═CH—, —CH═CHCO— or —COCH═CH—.
7. The compound according to claim 1, represented by formula (1-A): ##STR00704## wherein P.sup.1 is a group represented by formula (1b), (1c) or (1d); Sp.sup.1 and Sp.sup.2 are independently a single bond or alkylene having 1 to 10 carbons, and in the alkylene, at least one —CH.sub.2— may be replaced by —O—, —COO—, —OCOO— or —OCO—, and at least one —(CH.sub.2).sub.2— may be replaced by —CH═CH—; and R.sup.5 is hydrogen or alkyl having 1 to 15 carbons, and in the alkyl, at least one —CH.sub.2— may be replaced by —O— or —S—, and at least one —(CH.sub.2).sub.2— may be replaced by —CH═CH— or —C≡C—, and in the groups, at least one hydrogen may be replaced by halogen; ##STR00705## wherein, in formula (1b), R.sup.2 is hydrogen, halogen or alkyl having 1 to 5 carbons, and in the alkyl, at least one hydrogen may be replaced by halogen, and at least one —CH.sub.2— may be replaced by —O—; in formula (1d), R.sup.5 is hydrogen or alkyl having 1 to 15 carbons, and in the alkyl, at least one —CH.sub.2— may be replaced by —O— or —S—, and at least one —(CH.sub.2).sub.2— may be replaced by —CH═CH— or —C≡C—, and in the groups, at least one hydrogen may be replaced by halogen; and Y is a group represented by any one of formulas (MES-1-01) to (MES-1-10); ##STR00706## ##STR00707## wherein R.sup.a is independently fluorine, chlorine, methyl or ethyl; R.sup.b is independently hydrogen, fluorine, methyl or ethyl; and a representation of connecting 1,4-phenylene with (R.sup.a) by a straight line as shown below in the formulas indicates 1,4-phenylene in which one or two hydrogens may be replaced by R.sup.a: ##STR00708##
8. The compound according to claim 1, represented by formula (1-A): ##STR00709## wherein P.sup.1 is a group represented by formula (1b), (1c) or (1d); ##STR00710## wherein Sp.sup.1 and Sp.sup.2 are independently a single bond or alkylene having 1 to 10 carbons, and in the alkylene, at least one —CH.sub.2— may be replaced by —O—, —COO—, —OCOO— or —OCO—, and at least one —(CH.sub.2).sub.2— may be replaced by —CH═CH—; R.sup.2 is hydrogen, halogen or alkyl having 1 to 5 carbons, and in the alkyl, at least one hydrogen may be replaced by halogen, and at least one —CH.sub.2— may be replaced by —O—; R.sup.5 is independently hydrogen or alkyl having 1 to 15 carbons, and in the alkyl, at least one —CH.sub.2— may be replaced by —O— or —S—, and at least one —(CH.sub.2).sub.2— may be replaced by —CH═CH— or —C≡C—, and in the groups, at least one hydrogen may be replaced by halogen; and Y is a group represented by any one of (MES-2-01) to (MES-2-16); ##STR00711## ##STR00712## ##STR00713## wherein R.sup.a is independently fluorine, chlorine, methyl or ethyl; and a representation of connecting 1,4-phenylene with (R.sup.a) by a straight line as shown below in the formulas indicates 1,4-phenylene in which one or two hydrogens may be replaced by R.sup.a: ##STR00714##
9. A liquid crystal composition, containing at least one compound according to claim 1.
10. The liquid crystal composition according to claim 9, further containing at least one compound selected from the group of compounds represented by formulas (2) to (4): ##STR00715## wherein, in formulas (2) to (4), R.sup.1 and R.sup.2 are independently alkyl having 1 to 10 carbons or alkenyl having 2 to 10 carbons, and in the alkyl and the alkenyl, at least one —CH.sub.2— may be replaced by —O—, and at least one hydrogen may be replaced by fluorine; ring B.sup.1, ring B.sup.2, ring B.sup.3 and ring B.sup.4 are independently 1,4-cyclohexylene, 1,4-phenylene, 2-fluoro-1,4-phenylene, 2,5-difluoro-1,4-phenylene or pyrimidine-2,5-diyl; and Z.sup.11, Z.sup.12 and Z.sup.13 are independently a single bond, —CH.sub.2CH.sub.2—, —CH═CH—, —C≡C— or —COO—.
11. The liquid crystal composition according to claim 9, further containing at least one compound selected from the group of compounds represented by formulas (5) to (7): ##STR00716## wherein, in formulas (5) to (7), R.sup.13 is alkyl having 1 to 10 carbons or alkenyl having 2 to 10 carbons, and in the alkyl and the alkenyl, at least one —CH.sub.2— may be replaced by —O—, and at least one hydrogen may be replaced by fluorine; X.sup.11 is fluorine, chlorine, —OCF.sub.3, —OCHF.sub.2, —CF.sub.3, —CHF.sub.2, —CH.sub.2F, —OCF.sub.2CHF.sub.2 or —OCF.sub.2CHFCF.sub.3; ring C.sup.1, ring C.sup.2 and ring C.sup.3 are independently 1,4-cyclohexylene, 1,4-phenylene in which at least one hydrogen may be replaced by fluorine, tetrahydropyran-2,5-diyl, 1,3-dioxane-2,5-diyl or pyrimidine-2,5-diyl; Z.sup.14, Z.sup.15 and Z.sup.16 are independently a single bond, —CH.sub.2CH.sub.2—, —CH═CH—, —C≡C—, —COO—, —CF.sub.2O—, —OCF.sub.2—, —CH.sub.2O—, —CF═CF—, —CH═CF— or —(CH.sub.2).sub.4—; and L.sup.11 and L.sup.12 are independently hydrogen or fluorine.
12. The liquid crystal composition according to claim 9, further containing at least one compound represented by formula (8): ##STR00717## wherein, in formula (8), R.sup.14 is alkyl having 1 to 10 carbons or alkenyl having 2 to 10 carbons, and in the alkyl and the alkenyl, at least one —CH.sub.2— may be replaced by —O—, and at least one hydrogen may be replaced by fluorine; X.sup.12 is —C≡N or —C≡C—C≡N; ring D.sup.1 is 1,4-cyclohexylene, 1,4-phenylene in which at least one hydrogen may be replaced by fluorine, tetrahydropyran-2,5-diyl, 1,3-dioxane-2,5-diyl or pyrimidine-2,5-diyl; Z.sup.17 is a single bond, —CH.sub.2CH.sub.2—, —C≡C—, —COO—, —CF.sub.2O—, —OCF.sub.2— or —CH.sub.2O—; L.sup.13 and L.sup.14 are independently hydrogen or fluorine; and i is 1, 2, 3 or 4.
13. The liquid crystal composition according to claim 9, further containing at least one compound selected from the group of compounds represented by formulas (9) to (15): ##STR00718## wherein, in formulas (9) to (15), R.sup.15 and R.sup.16 are independently alkyl having 1 to 10 carbons or alkenyl having 2 to 10 carbons, and in the alkyl and the alkenyl, at least one —CH.sub.2— may be replaced by —O—, and at least one hydrogen may be replaced by fluorine; R.sup.17 is hydrogen, fluorine, alkyl having 1 to 10 carbons or alkenyl having 2 to 10 carbons, and in the alkyl and the alkenyl, at least one —CH.sub.2— may be replaced by —O—, and at least one hydrogen may be replaced by fluorine; ring E.sup.1, ring E.sup.2, ring E.sup.3 and ring E.sup.4 are independently 1,4-cyclohexylene, 1,4-cyclohexenylene, 1,4-phenylene in which at least one hydrogen may be replaced by fluorine, tetrahydropyran-2,5-diyl or decahydronaphthalene-2,6-diyl; ring E.sup.5 and ring E.sup.6 are independently 1,4-cyclohexylene, 1,4-cyclohexenylene, 1,4-phenylene, tetrahydropyran-2,5-diyl or decahydronaphthalene-2,6-diyl; Z.sup.18, Z.sup.19, Z.sup.20 and Z.sup.21 are independently a single bond, —CH.sub.2CH.sub.2—, —COO—, —CH.sub.2O—, —OCF.sub.2— or —OCF.sub.2CH.sub.2CH.sub.2—; L.sup.15 and L.sup.16 are independently fluorine or chlorine; S.sup.11 is hydrogen or methyl; X is —CHF— or —CF.sub.2—; and j, k, m, n, p, q, r and s are independently 0 or 1, a sum of k, m, n and p is 1 or 2, a sum of q, r and s is 0, 1, 2 or 3, and t is 1, 2 or 3.
14. The liquid crystal composition according to claim 9, further containing at least one polymerizable compound represented by formula (16): ##STR00719## wherein, in formula (16), ring F and ring I are independently cyclohexyl, cyclohexenyl, phenyl, 1-naphthyl, 2-naphthyl, tetrahydropyran-2-yl, 1,3-dioxane-2-yl, pyrimidine-2-yl or pyridine-2-yl, and in the rings, at least one hydrogen may be replaced by halogen, alkyl having 1 to 12 carbons, or alkyl having 1 to 12 carbons in which at least one hydrogen is replaced by halogen; ring G is 1,4-cyclohexylene, 1,4-cyclohexenylene, 1,4-phenylene, naphthalene-1,2-diyl, naphthalene-1,3-diyl, naphthalene-1,4-diyl, naphthalene-1,5-diyl, naphthalene-1,6-diyl, naphthalene-1,7-diyl, naphthalene-1,8-diyl, naphthalene-2,3-diyl, naphthalene-2,6-diyl, naphthalene-2,7-diyl, tetrahydropyran-2,5-diyl, 1,3-dioxane-2,5-diyl, pyrimidine-2,5-diyl or pyridine-2,5-diyl, and in the rings, at least one hydrogen may be replaced by halogen, alkyl having 1 to 12 carbons, alkoxy having 1 to 12 carbons, or alkyl having 1 to 12 carbons in which at least one hydrogen is replaced by halogen; Z.sup.22 and Z.sup.23 are independently a single bond or alkylene having 1 to 10 carbons, and in the alkylene, at least one —CH.sub.2— may be replaced by —O—, —CO—, —COO— or —OCO—, and at least one —CH.sub.2CH.sub.2— may be replaced by —CH═CH—, —C(CH.sub.3)═CH—, —CH═C(CH.sub.3)— or —C(CH.sub.3)═C(CH.sub.3)—, and in the groups, at least one hydrogen may be replaced by fluorine or chlorine; and P.sup.11, P.sup.12 and P.sup.13 are independently a polymerizable group selected from the group of groups represented by formulas (P-1) to (P-5); ##STR00720## wherein M.sup.11, M.sup.12 and M.sup.13 are independently hydrogen, fluorine, alkyl having 1 to 5 carbons, or alkyl having 1 to 5 carbons in which at least one hydrogen is replaced by fluorine or chlorine; Sp.sup.11, Sp.sup.12 and Sp.sup.13 are independently a single bond or alkylene having 1 to 10 carbons, and in the alkylene, at least one —CH.sub.2— may be replaced by —O—, —COO—, —OCO— or —OCOO—, and at least one —CH.sub.2CH.sub.2— may be replaced by —CH═CH— or —C≡C—, and in the groups, at least one hydrogen may be replaced by fluorine or chlorine; u is 0, 1 or 2; and f, g and h are independently 0, 1, 2, 3 or 4, and a sum of f, g and h is 2 or more.
15. The liquid crystal composition according to claim 9, further containing at least one polymerizable compound selected from the group of compounds represented by formulas (16-1) to (16-27): ##STR00721## ##STR00722## ##STR00723## wherein, in formulas (16-1) to (16-27), P.sup.11, P.sup.12 and P.sup.13 are independently a polymerizable group selected from the group of groups represented by formulas (P-1) to (P-3), in which M.sup.11, M.sup.12 and M.sup.13 are independently hydrogen, fluorine, alkyl having 1 to 5 carbons, or alkyl having 1 to 5 carbons in which at least one hydrogen is replaced by halogen; ##STR00724## wherein Sp.sup.11, Sp.sup.12 and Sp.sup.13 are independently a single bond or alkylene having 1 to 10 carbons, and in the alkylene, at least one —CH.sub.2— may be replaced by —O—, —COO—, —OCO— or —OCOO—, and at least one —CH.sub.2CH.sub.2— may be replaced by —CH═CH— or —C≡C—, and in the groups, at least one hydrogen may be replaced by fluorine or chlorine.
16. The liquid crystal composition according to claim 9, further containing at least one of a polymerizable compound other than formulas (1) and (16), a polymerization initiator, a polymerization inhibitor, an optically active compound, an antioxidant, an ultraviolet light absorber, a light stabilizer, a heat stabilizer and an antifoaming agent.
17. A liquid crystal display device, including at least one liquid crystal composition according to claim 9.
Description
DESCRIPTION OF EMBODIMENTS
(1) Usage of terms herein is as described below. Terms “liquid crystal composition” and “liquid crystal display device” may be occasionally abbreviated as “composition” and “device,” respectively. “Liquid crystal display device” is a generic term for a liquid crystal display panel and a liquid crystal display module. “Liquid crystal compound” is a generic term for a compound having a liquid crystal phase such as a nematic phase and a smectic phase, and a compound having no liquid crystal phase but to be mixed with the composition for the purpose of adjusting characteristics such as a temperature range of a nematic phase, viscosity and dielectric anisotropy. The compound has a six-membered ring such as 1,4-cyclohexylene and 1,4-phenylene, and rod like molecular structure. “Polymerizable compound” is a compound to be added for the purpose of forming a polymer in the composition. “Polar compound” assists alignment of liquid crystal molecules by interaction of a polar group with a substrate surface.
(2) The liquid crystal composition is prepared by mixing a plurality of liquid crystal compounds. A proportion (content) of the liquid crystal compounds is expressed in terms of weight percent (% by weight) based on the weight of the liquid crystal composition. An additive such as an optically active compound, an antioxidant, an ultraviolet light absorber, a dye, an antifoaming agent, the polymerizable compound, a polymerization initiator, a polymerization inhibitor and a polar compound is added to the liquid crystal composition when necessary. A proportion (amount of addition) of the additive is expressed in terms of weight percent (% by weight) based on the weight of the liquid crystal composition in a manner similar to the proportion of the liquid crystal compound. Weight parts per million (ppm) may be occasionally used. A proportion of the polymerization initiator and the polymerization inhibitor is exceptionally expressed based on the weight of the polymerizable compound.
(3) A compound represented by formula (1) may be occasionally abbreviated as “compound (1).” Compound (1) means one compound, a mixture of two compounds or a mixture of three or more compounds represented by formula (1). A same rule applies also to at least one compound selected from the group of compounds represented by formula (2), or the like. Symbol B.sup.1, C.sup.1, F or the like surrounded by a hexagonal shape corresponds to ring B.sup.1, ring C.sup.1 and ring F, respectively. The hexagonal shape represents a six-membered ring such as a cyclohexane ring and a benzene ring, or a condensed ring such as a naphthalene ring. An oblique line crossing the hexagonal shape represents that arbitrary hydrogen on the ring may be replaced by a group such as -Sp.sup.1-P.sup.1. A subscript such as e represents the number of groups subjected to replacement. When the subscript is 0, no such replacement exists.
(4) A symbol of terminal group R.sup.11 is used in a plurality of component compounds. In the compounds, two groups represented by two arbitrary R.sup.11s may be identical or different. For example, in one case, R.sup.11 of compound (2) is ethyl and R.sup.11 of compound (3) is ethyl. In another case, R.sup.11 of compound (2) is ethyl and R.sup.11 of compound (3) is propyl. A same rule applies also to a symbol of any other terminal group, ring, bonding group or the like. In formula (8), when i is 2, two of ring D.sup.1 exist. In the compound, two groups represented by two of ring D.sup.1 may be identical or different. A same rule applies also to two of arbitrary ring D.sup.1 when i is larger than 2. A same rule applies also to a symbol of any other ring, bonding group or the like.
(5) An expression “at least one ‘A’” means that the number of ‘A’ is arbitrary. An expression “at least one ‘A’ may be replaced by ‘B’” means that, when the number of ‘A’ is 1, a position of ‘A’ is arbitrary, and also when the number of ‘A’ is 2 or more, positions thereof can be selected without restriction. A same rule applies also to an expression “at least one ‘A’ is replaced by ‘B’.” An expression “at least one ‘A’ may be replaced by ‘B’, ‘C’ or ‘D’” includes a case where at least one ‘A’ is replaced by ‘B’, a case where at least one ‘A’ is replaced by ‘C’, and a case where at least one ‘A’ is replaced by ‘D’, and also a case where a plurality of ‘As’ are replaced by at least two ‘Bs’, ‘Cs’ and ‘Ds’. For example, “alkyl in which at least one —CH.sub.2-(or —CH.sub.2CH.sub.2—) may be replaced by —O— (or —CH═CH—)” includes alkyl, alkenyl, alkoxy, alkoxyalkyl, alkoxyalkenyl and alkenyloxyalkyl. In addition, a case where two consecutive —CH.sub.2-s are replaced by —O-s to form —O—O— is not preferred. In alkyl or the like, a case where —CH.sub.2— of a methyl part (—CH.sub.2—H) is replaced by —O— to form —O—H is not preferred, either.
(6) Halogen means fluorine, chlorine, bromine or iodine. Preferred halogen is fluorine or chlorine. Further preferred halogen is fluorine. Alkyl is straight-chain alkyl or branched-chain alkyl, but includes no cyclic alkyl. In general, straight-chain alkyl is preferred to branched-chain alkyl. A same rule applies also to a terminal group such as alkoxy and alkenyl. With regard to a configuration of 1,4-cyclohexylene, trans is preferred to cis for increasing the maximum temperature of the nematic phase. Then, 2-fluoro-1,4-phenylene means two divalent groups described below. In a chemical formula, fluorine may be leftward (L) or rightward (R). A same rule applies also to an asymmetrical divalent group formed by eliminating two hydrogens from a ring, such as tetrahydropyran-2,5-diyl.
(7) ##STR00005##
(8) The invention includes items described below.
(9) Item 1. A compound, represented by formula (1):
(10) ##STR00006##
wherein, in formula (1),
(11) a and b are independently 0, 1 or 2, and expressions: 0≤a+b≤3 hold,
(12) ring A.sup.1, ring A.sup.2, ring A.sup.3 and ring A.sup.4 are independently 1,4-cyclohexylene, 1,4-cyclohexenylene, 1,4-phenylene, naphthalene-2,6-diyl, decahydronaphthalene-2,6-diyl, 1,2,3,4-tetrahydronaphthalene-2,6-diyl, tetrahydropyran-2,5-diyl, 1,3-dioxane-2,5-diyl, pyrimidine-2,5-diyl, pyridine-2,5-diyl, fluorene-2,7-diyl, phenanthrene-2,7-diyl, anthracene-2,6-diyl, perhydrocyclopenta[a]phenanthrene-3,17-diyl or 2,3,4,7,8,9,10,11,12,13,14,15,16,17-tetradecahydrocyclopenta[a]phe nanthrene-3,17-diyl, and in the rings, at least one hydrogen may be replaced by fluorine, chlorine, alkyl having 1 to 12 carbons, alkenyl having 2 to 12 carbons, alkoxy having 1 to 11 carbons or alkenyloxy having 2 to 11 carbons, and in the groups, at least one hydrogen may be replaced by fluorine or chlorine, and when a is 2, two of ring A.sup.1 may be different, and when b is 2, two of ring A.sup.4 may be different;
(13) Z.sup.1, Z.sup.2, Z.sup.3, Z.sup.4 and Z.sup.5 are independently a single bond or alkylene having 1 to 10 carbons, and in the alkylene, at least one —CH.sub.2— may be replaced by —O—, —CO—, —COO—, —OCO— or —OCOO—, and at least one —(CH.sub.2).sub.2— may be replaced by —CH═CH— or —C≡C—, and in the groups, at least one hydrogen may be replaced by halogen, in which at least one in Z.sup.2, Z.sup.3 or Z.sup.4 is —COO—, —OCO—, —CH═CHCOO—, —OCOCH═CH—, —CH═CH—, —CH═CHCO— or —COCH═CH—, and when a is 2, two Z.sup.1s may be different, and two Z.sup.5s may be different;
(14) Sp.sup.1 and Sp.sup.2 are independently a single bond or alkylene having 1 to 10 carbons, and in the alkylene, at least one —CH.sub.2— may be replaced by —O—, —CO—, —COO—, —OCO— or —OCOO—, and at least one —(CH.sub.2).sub.2— may be replaced by —CH═CH— or —C≡C—, and in the groups, at least one hydrogen may be replaced by halogen;
(15) P.sup.1 is a group represented by any one of formulas (1b) to (1i); and
(16) P.sup.2 is a group represented by formula (1d);
(17) ##STR00007##
wherein, in formulas (1b) to (1i),
(18) M.sup.1 and M.sup.2 are independently hydrogen, halogen, alkyl having 1 to 5 carbons, or alkyl having 1 to 5 carbons in which at least one hydrogen is replaced by halogen;
(19) R.sup.2 is hydrogen, halogen or alkyl having 1 to 5 carbons, and in the alkyl, at least one hydrogen may be replaced by halogen, and at least one —CH.sub.2— may be replaced by —O—; and
(20) R.sup.3, R.sup.4 and R.sup.5 are independently hydrogen or alkyl having 1 to 15 carbons, and in the alkyl, at least one —CH.sub.2— may be replaced by —O— or —S—, and at least one —(CH.sub.2).sub.2— may be replaced by —CH═CH— or —C≡C—, and in the groups, at least one hydrogen may be replaced by halogen.
(21) Item 2. The compound according to item 1, represented by formula (1):
(22) ##STR00008##
wherein, in formula (1),
(23) a and b are independently 0, 1 or 2, and expressions: 0≤a+b≤2 hold;
(24) ring A.sup.1, ring A.sup.2, ring A.sup.3 and ring A.sup.4 are independently 1,4-cyclohexylene, 1,4-cyclohexenylene, 1,4-phenylene, naphthalene-2,6-diyl, decahydronaphthalene-2,6-diyl, 1,2,3,4-tetrahydronaphthalene-2,6-diyl, tetrahydropyran-2,5-diyl, 1,3-dioxane-2,5-diyl, pyrimidine-2,5-diyl, pyridine-2,5-diyl, fluorene-2,7-diyl, phenanthrene-2,7-diyl, anthracene-2,6-diyl, perhydrocyclopenta[a]phenanthrene-3,17-diyl or 2,3,4,7,8,9,10,11,12,13,14,15,16,17-tetradecahydrocyclopenta[a]phenanthrene-3,17-diyl, and in the rings, at least one hydrogen may be replaced by fluorine, chlorine, alkyl having 1 to 12 carbons, alkenyl having 2 to 12 carbons, alkoxy having 1 to 11 carbons or alkenyloxy having 2 to 11 carbons, and in the groups, at least one hydrogen may be replaced by fluorine or chlorine, and when a is 2, two of ring A.sup.1 may be different, and when b is 2, two of ring A.sup.4 may be different;
(25) Z.sup.1, Z.sup.2, Z.sup.3, Z.sup.4 and Z.sup.5 are independently a single bond, —(CH.sub.2).sub.2—, —C≡C—, —COO—, —OCO—, —CF.sub.2O—, —OCF.sub.2—, —CH.sub.2O—, —OCH.sub.2—, —CF═CF—, —CH═CHCOO—, —OCOCH═CH—, —CH═CH—, —CH═CHCO— or —COCH═CH—, in which at least one in Z.sup.2, Z.sup.3 or Z.sup.4 is —COO—, —OCO—, —CH═CHCOO—, —OCOCH═CH—, —CH═CH—, —CH═CHCO— or —COCH═CH—, and when a is 2, two pieces of Z.sup.1 may be different, and two pieces of Z.sup.5 may be different;
(26) Sp.sup.1 and Sp.sup.2 are independently a single bond or alkylene having 1 to 10 carbons, and in the alkylene, at least one piece of —CH.sub.2— may be replaced by —O—, —COO— or —OCO—, and at least one piece of —(CH.sub.2).sub.2— may be replaced by —CH═CH—, and in the groups, at least one hydrogen may be replaced by fluorine or chlorine; and
(27) P.sup.1 is a group represented by any one of formulas (1b) to (1i), and P.sup.2 is a group represented by formula (1d);
(28) ##STR00009##
wherein, in formulas (1b) to (1i),
(29) M.sup.1 and M.sup.2 are independently hydrogen, halogen, alkyl having 1 to 5 carbons, or alkyl having 1 to 5 carbons in which at least one hydrogen is replaced by halogen;
(30) R.sup.2 is hydrogen, halogen or alkyl having 1 to 5 carbons, and in the alkyl, at least one hydrogen may be replaced by halogen, and at least one piece of —CH.sub.2— may be replaced by —O—; and
(31) R.sup.3, R.sup.4 and R.sup.5 are independently hydrogen or alkyl having 1 to 15 carbons, and in the alkyl, at least one piece of —CH.sub.2— may be replaced by —O— or —S—, and at least one piece of —(CH.sub.2).sub.2— may be replaced by —CH═CH— or —C≡C—, and in the groups, at least one hydrogen may be replaced by halogen.
(32) Item 3. The compound according to item 1 or 2, represented by any one of formulas (1-1) to (1-3):
(33) ##STR00010##
wherein, in formulas (1-1) to (1-3),
(34) R.sup.5 is hydrogen or alkyl having 1 to 15 carbons, and in the alkyl, at least one piece of —CH.sub.2— may be replaced by —O— or —S—, and at least one piece of —(CH.sub.2).sub.2— may be replaced by —CH═CH— or —C≡C—, and in the groups, at least one hydrogen may be replaced by halogen;
(35) ring A.sup.1, ring A.sup.2, ring A.sup.3 and ring A.sup.4 are independently 1,4-cyclohexylene, 1,4-phenylene, naphthalene-2,6-diyl, pyrimidine-2,5-diyl, pyridine-2,5-diyl, fluorene-2,7-diyl, phenanthrene-2,7-diyl or anthracene-2,6-diyl, and in the rings, at least one hydrogen may be replaced by fluorine, chlorine, alkyl having 1 to 12 carbons, alkenyl having 2 to 12 carbons, alkoxy having 1 to 11 carbons or alkenyloxy having 2 to 11 carbons, and in the groups, at least one hydrogen may be replaced by fluorine or chlorine;
(36) Z.sup.2, Z.sup.3 and Z.sup.4 are independently a single bond, —(CH.sub.2).sub.2—, —C≡C—, —COO—, —OCO—, —CF.sub.2O—, —OCF.sub.2—, —CH.sub.2O—, —OCH.sub.2—, —CF═CF—, —CH═CHCOO—, —OCOCH═CH—, —CH═CH—, —CH═CHCO— or —COCH═CH—, in which at least one in Z.sup.2, Z.sup.3 and Z.sup.4 is —COO—, —OCO—, —CH═CHCOO—, —OCOCH═CH—, —CH═CH—, —CH═CHCO— or —COCH═CH—;
(37) Sp.sup.1 and Sp.sup.2 are independently a single bond or alkylene having 1 to 10 carbons, and in the alkylene, at least one piece of —CH.sub.2— may be replaced by —O—, —COO—, —OCOO— or —OCO—, and at least one piece of —(CH.sub.2).sub.2— may be replaced by —CH═CH—, and in the groups, at least one hydrogen may be replaced by fluorine or chlorine; and
(38) P.sup.1 is a group represented by any one of formulas (1b) to (1i);
(39) ##STR00011##
wherein
(40) M.sup.1 and M.sup.2 are independently hydrogen, halogen, alkyl having 1 to 5 carbons, or alkyl having 1 to 5 carbons in which at least one hydrogen is replaced by halogen;
(41) R.sup.2 is hydrogen, halogen or alkyl having 1 to 5 carbons, and in the alkyl, at least one hydrogen may be replaced by halogen, and at least one piece of —CH.sub.2— may be replaced by —O—; and
(42) R.sup.3, R.sup.4 and R.sup.5 are independently hydrogen or straight-chain, branched-chain or cyclic alkyl having 1 to 15 carbons, and in the alkyl, at least one piece of —CH.sub.2— may be replaced by —O— or —S—, and at least one piece of —(CH.sub.2).sub.2— may be replaced by —CH═CH— or —C≡C—, and in the groups, at least one hydrogen may be replaced by halogen.
(43) Item 4. The compound according to any one of items 1 to 3, represented by any one of formulas (1-1-1), (1-2-1) and (1-3-1):
(44) ##STR00012##
wherein, in formulas (1-1-1), (1-2-1) and (1-3-1),
(45) R.sup.5 is hydrogen or alkyl having 1 to 15 carbons, and in the alkyl, at least one —CH.sub.2— may be replaced by —O— or —S—, and at least one —(CH.sub.2).sub.2— may be replaced by —CH═CH— or —C≡C—, and in the groups, at least one hydrogen may be replaced by halogen;
(46) ring A.sup.1, ring A.sup.2, ring A.sup.3 and ring A.sup.4 are independently 1,4-cyclohexylene, 1,4-phenylene or fluorene-2,7-diyl, and in the rings, at least one hydrogen may be replaced by fluorine, chlorine, alkyl having 1 to 12 carbons, alkenyl having 2 to 12 carbons, alkoxy having 1 to 11 carbons or alkenyloxy having 2 to 11 carbons;
(47) Z.sup.2, Z.sup.3 and Z.sup.4 are independently a single bond, —COO—, —OCO—, —CH═CHCOO—, —OCOCH═CH—, —CH═CH—, —CH═CHCO— or —COCH═CH—, in which at least one in Z.sup.2, Z.sup.3 and Z.sup.4 is —COO—, —OCO—, —CH═CHCOO—, —OCOCH═CH—, —CH═CH—, —CH═CHCO— or —COCH═CH—;
(48) Sp.sup.1 and Sp.sup.2 are independently a single bond or alkylene having 1 to 10 carbons, and in the alkylene, at least one —CH.sub.2— may be replaced by —O—, —COO—, —OCOO— or —OCO—, and at least one —(CH.sub.2).sub.2— may be replaced by —CH═CH—; and
(49) P.sup.1 is a group represented by any one of formula (1b), (1c) or (1d);
(50) ##STR00013##
wherein, in formulas (1b) to (1d),
(51) R.sup.2 is hydrogen, halogen or alkyl having 1 to 5 carbons, and in the alkyl, at least one hydrogen may be replaced by halogen, and at least one —CH.sub.2— may be replaced by —O—; and
(52) R.sup.5 is hydrogen or alkyl having 1 to 15 carbons, and in the alkyl, at least one —CH.sub.2— may be replaced by —O— or —S—, and at least one —(CH.sub.2).sub.2— may be replaced by —CH═CH— or —C≡C—, and in the groups, at least one hydrogen may be replaced by halogen.
(53) Item 5. The compound according to item 4, represented by any one of formula (1-1-1), (1-2-1) or (1-3-1), wherein any one of Z.sup.2, Z.sup.3 or Z.sup.4 is —COO— or —OCO—.
(54) Item 6. The compound according to item 4, represented by any one of formula (1-1-1), (1-2-1) or (1-3-1), wherein any one of Z.sup.2, Z.sup.3 or Z.sup.4 is —CH═CHCOO—, —OCOCH═CH—, —CH═CH—, —CH═CHCO— or —COCH═CH—.
(55) Item 7. The compound according to any one of items 1 to 4, represented by formula (1-A):
(56) ##STR00014##
wherein
(57) P.sup.1 is a group represented by formula (1b), (1c) or (1d);
(58) Sp.sup.1 and Sp.sup.2 are independently a single bond or alkylene having 1 to 10 carbons, and in the alkylene, at least one —CH.sub.2— may be replaced by —O—, —COO—, —OCOO— or —OCO—, and at least one —(CH.sub.2).sub.2— may be replaced by —CH═CH—; and
(59) R.sup.5 is hydrogen or alkyl having 1 to 15 carbons, and in the alkyl, at least one —CH.sub.2— may be replaced by —O— or —S—, and at least one —(CH.sub.2).sub.2— may be replaced by —CH═CH— or —C≡C—, and in the groups, at least one hydrogen may be replaced by halogen;
(60) ##STR00015##
wherein, in formula (1b), R.sup.2 is hydrogen, halogen or alkyl having 1 to 5 carbons, and in the alkyl, at least one hydrogen may be replaced by halogen, and at least one —CH.sub.2— may be replaced by —O—;
(61) in formula (1d), R.sup.5 is hydrogen or alkyl having 1 to 15 carbons, and in the alkyl, at least one —CH.sub.2— may be replaced by —O— or —S—, and at least one —(CH.sub.2).sub.2— may be replaced by —CH═CH— or —C≡C—, and in the groups, at least one hydrogen may be replaced by halogen; and
(62) Y is a group represented by any one of formulas (MES-1-01) to (MES-1-10);
(63) ##STR00016## ##STR00017##
wherein
(64) R.sup.a is independently fluorine, chlorine, methyl or ethyl;
(65) R.sup.b is independently hydrogen, fluorine, methyl or ethyl; and
(66) a representation of connecting 1,4-phenylene with (R.sup.a) by a straight line as shown below in the formulas indicates 1,4-phenylene in which one or two hydrogens may be replaced by R.sup.a.
(67) ##STR00018##
(68) Item 8. The compound according to any one of items 1 to 4, represented by formula (1-A):
(69) ##STR00019##
wherein
(70) P.sup.1 is a group represented by formula (1b), (1c) or (1d);
(71) ##STR00020##
wherein
(72) Sp.sup.1 and Sp.sup.2 are independently a single bond or alkylene having 1 to 10 carbons, and in the alkylene, at least one —CH.sub.2— may be replaced by —O—, —COO—, —OCOO— or —OCO—, and at least one —(CH.sub.2).sub.2— may be replaced by —CH═CH—;
(73) R.sup.2 is hydrogen, halogen or alkyl having 1 to 5 carbons, and in the alkyl, at least one hydrogen may be replaced by halogen, and at least one —CH.sub.2— may be replaced by —O—;
(74) R.sup.5 is independently hydrogen or alkyl having 1 to 15 carbons, and in the alkyl, at least one —CH.sub.2— may be replaced by —O— or —S—, and at least one —(CH.sub.2).sub.2— may be replaced by —CH═CH— or —C≡C—, and in the groups, at least one hydrogen may be replaced by halogen; and
(75) Y is a group represented by any one of (MES-2-01) to (MES-2-16);
(76) ##STR00021## ##STR00022## ##STR00023##
wherein
(77) R.sup.a is independently fluorine, chlorine, methyl or ethyl; and
(78) a representation of connecting 1,4-phenylene with (R.sup.a) by a straight line as shown below in the formulas indicates 1,4-phenylene in which one or two hydrogens may be replaced by R.sup.a.
(79) ##STR00024##
(80) Item 9. A liquid crystal composition, containing at least one compound according to any one of items 1 to 8.
(81) Item 10. The liquid crystal composition according to item 9, further containing at least one compound selected from the group of compounds represented by formulas (2) to (4):
(82) ##STR00025##
wherein, in formulas (2) to (4),
(83) R.sup.11 and R.sup.12 are independently alkyl having 1 to 10 carbons or alkenyl having 2 to 10 carbons, and in the alkyl and the alkenyl, at least one —CH.sub.2— may be replaced by —O—, and at least one hydrogen may be replaced by fluorine;
(84) ring B.sup.1, ring B.sup.2, ring B.sup.3 and ring B.sup.4 are independently 1,4-cyclohexylene, 1,4-phenylene, 2-fluoro-1,4-phenylene, 2,5-difluoro-1,4-phenylene or pyrimidine-2,5-diyl; and
(85) Z.sup.11, Z.sup.12 and Z.sup.13 are independently a single bond, —CH.sub.2CH.sub.2—, —CH═CH—, —C≡C— or —COO—.
(86) Item 11. The liquid crystal composition according to item 9 or 10, further containing at least one compound selected from the group of compounds represented by formulas (5) to (7):
(87) ##STR00026##
wherein, in formulas (5) to (7),
(88) R.sup.13 is alkyl having 1 to 10 carbons or alkenyl having 2 to 10 carbons, and in the alkyl and the alkenyl, at least one —CH.sub.2— may be replaced by —O—, and at least one hydrogen may be replaced by fluorine;
(89) X.sup.11 is fluorine, chlorine, —OCF.sub.3, —OCHF.sub.2, —CF.sub.3, —CHF.sub.2, —CH.sub.2F, —OCF.sub.2CHF.sub.2 or —OCF.sub.2CHFCF.sub.3;
(90) ring C.sup.1, ring C.sup.2 and ring C.sup.3 are independently 1,4-cyclohexylene, 1,4-phenylene in which at least one hydrogen may be replaced by fluorine, tetrahydropyran-2,5-diyl, 1,3-dioxane-2,5-diyl or pyrimidine-2,5-diyl;
(91) Z.sup.14, Z.sup.15 and Z.sup.16 are independently a single bond, —CH.sub.2CH.sub.2—, —CH═CH—, —C≡C—, —COO—, —CF.sub.2O—, —OCF.sub.2—, —CH.sub.2O—, —CF═CF—, —CH═CF— or —(CH.sub.2) 4-; and
(92) L.sup.11 and L.sup.12 are independently hydrogen or fluorine.
(93) Item 12. The liquid crystal composition according to any one of items 9 to 11, further containing at least one compound selected from the group of compounds represented by formula (8):
(94) ##STR00027##
wherein, in formula (8),
(95) R.sup.14 is alkyl having 1 to 10 carbons or alkenyl having 2 to 10 carbons, and in the alkyl and the alkenyl, at least one —CH.sub.2— may be replaced by —O—, and at least one hydrogen may be replaced by fluorine;
(96) X.sup.12 is —C≡N or —C≡C—C≡N;
(97) ring D.sup.1 is 1,4-cyclohexylene, 1,4-phenylene in which at least one hydrogen may be replaced by fluorine, tetrahydropyran-2,5-diyl, 1,3-dioxane-2,5-diyl or pyrimidine-2,5-diyl;
(98) Z.sup.17 is a single bond, —CH.sub.2CH.sub.2—, —C≡C—, —COO—, —CF.sub.2O—, —OCF.sub.2— or —CH.sub.2O—;
(99) L.sup.13 and L.sup.14 are independently hydrogen or fluorine; and
(100) i is 1, 2, 3 or 4.
(101) Item 13. The liquid crystal composition according to any one of items 9 to 12, further containing at least one compound selected from the group of compounds represented by formulas (9) to (15):
(102) ##STR00028##
wherein, in formulas (9) to (15),
(103) R.sup.15 and R.sup.16 are independently alkyl having 1 to 10 carbons or alkenyl having 2 to 10 carbons, and in the alkyl and the alkenyl, at least one —CH.sub.2— may be replaced by —O—, and at least one hydrogen may be replaced by fluorine;
(104) R.sup.17 is hydrogen, fluorine, alkyl having 1 to 10 carbons or alkenyl having 2 to 10 carbons, and in the alkyl and the alkenyl, at least one —CH.sub.2— may be replaced by —O—, and at least one hydrogen may be replaced by fluorine;
(105) ring E.sup.1, ring E.sup.2, ring E.sup.3 and ring E.sup.4 are independently 1,4-cyclohexylene, 1,4-cyclohexenylene, 1,4-phenylene in which at least one hydrogen may be replaced by fluorine, tetrahydropyran-2,5-diyl or decahydronaphthalene-2,6-diyl;
(106) ring E.sup.5 and ring E.sup.6 are independently 1,4-cyclohexylene, 1,4-cyclohexenylene, 1,4-phenylene, tetrahydropyran-2,5-diyl or decahydronaphthalene-2,6-diyl;
(107) Z.sup.18, Z.sup.19, Z.sup.20 and Z.sup.21 are independently a single bond, —CH.sub.2CH.sub.2—, —COO—, —CH.sub.2O—, —OCF.sub.2— or —OCF.sub.2CH.sub.2CH.sub.2—;
(108) L.sup.15 and L.sup.16 are independently fluorine or chlorine;
(109) S.sup.11 is hydrogen or methyl;
(110) X is —CHF— or —CF.sub.2—; and
(111) j, k, m, n, p, q, r and s are independently 0 or 1, a sum of k, m, n and p is 1 or 2, a sum of q, r and s is 0, 1, 2 or 3, and t is 1, 2 or 3.
(112) Item 14. The liquid crystal composition according to any one of items 9 to 13, further containing at least one polymerizable compound selected from the group of compounds represented by formula (16):
(113) ##STR00029##
wherein, in formula (16),
(114) ring F and ring I are independently cyclohexyl, cyclohexenyl, phenyl, 1-naphthyl, 2-naphthyl, tetrahydropyran-2-yl, 1,3-dioxane-2-yl, pyrimidine-2-yl or pyridine-2-yl, and in the rings, at least one hydrogen may be replaced by halogen, alkyl having 1 to 12 carbons, or alkyl having 1 to 12 carbons in which at least one hydrogen is replaced by halogen;
(115) ring G is 1,4-cyclohexylene, 1,4-cyclohexenylene, 1,4-phenylene, naphthalene-1,2-diyl, naphthalene-1,3-diyl, naphthalene-1,4-diyl, naphthalene-1,5-diyl, naphthalene-1,6-diyl, naphthalene-1,7-diyl, naphthalene-1,8-diyl, naphthalene-2,3-diyl, naphthalene-2,6-diyl, naphthalene-2,7-diyl, tetrahydropyran-2,5-diyl, 1,3-dioxane-2,5-diyl, pyrimidine-2,5-diyl or pyridine-2,5-diyl, and in the rings, at least one hydrogen may be replaced by halogen, alkyl having 1 to 12 carbons, alkoxy having 1 to 12 carbons, or alkyl having 1 to 12 carbons in which at least one hydrogen is replaced by halogen;
(116) Z.sup.22 and Z.sup.23 are independently a single bond or alkylene having 1 to 10 carbons, and in the alkylene, at least one —CH.sub.2— may be replaced by —O—, —CO—, —COO— or —OCO—, and at least one —CH.sub.2CH.sub.2— may be replaced by —CH═CH—, —C(CH.sub.3)═CH—, —CH═C(CH.sub.3)— or —C(CH.sub.3)═C(CH.sub.3)—, and in the groups, at least one hydrogen may be replaced by fluorine or chlorine; and
(117) P.sup.11, P.sup.12 and P.sup.13 are independently a polymerizable group selected from the group of groups represented by formulas (P-1) to (P-5);
(118) ##STR00030##
wherein
(119) M.sup.1M.sup.12 and M.sup.13 are independently hydrogen, fluorine, alkyl having 1 to 5 carbons, or alkyl having 1 to 5 carbons in which at least one hydrogen is replaced by fluorine or chlorine;
(120) Sp.sup.11, Sp.sup.12 and Sp.sup.13 are independently a single bond or alkylene having 1 to 10 carbons, and in the alkylene, at least one —CH.sub.2— may be replaced by —O—, —COO—, —OCO— or —OCOO—, and at least one —CH.sub.2CH.sub.2— may be replaced by —CH═CH— or —C≡C—, and in the groups, at least one hydrogen may be replaced by fluorine or chlorine;
(121) u is 0, 1 or 2; and
(122) f, g and h are independently 0, 1,2,3 or 4, and a sum of f, g and h is 2 or more.
(123) Item 15. The liquid crystal composition according to any one of items 9 to 14, further containing at least one polymerizable compound selected from the group of compounds represented by formulas (16-1) to (16-27):
(124) ##STR00031## ##STR00032## ##STR00033##
wherein, in formulas (16-1) to (16-27),
(125) P.sup.11, P.sup.12 and P.sup.13 are independently a polymerizable group selected from the group of groups represented by formulas (P-1) to (P-3), in which M.sup.11, M.sup.12 and M.sup.13 are independently hydrogen, fluorine, alkyl having 1 to 5 carbons, or alkyl having 1 to 5 carbons in which at least one hydrogen is replaced by halogen;
(126) ##STR00034##
wherein
(127) Sp.sup.11, Sp.sup.12 and Sp.sup.13 are independently a single bond or alkylene having 1 to 10 carbons, and in the alkylene, at least one —CH.sub.2— may be replaced by —O—, —COO—, —OCO— or —OCOO—, and at least one —CH.sub.2CH.sub.2— may be replaced by —CH═CH— or —C≡C—, and in the groups, at least one hydrogen may be replaced by fluorine or chlorine.
(128) Item 16. The liquid crystal composition according to any one of items 9 to 15, further containing at least one of a polymerizable compound other than formulas (1) and (16), a polymerization initiator, a polymerization inhibitor, an optically active compound, an antioxidant, an ultraviolet light absorber, a light stabilizer, a heat stabilizer and an antifoaming agent.
(129) Item 17. A liquid crystal display device, including at least one liquid crystal composition according to any one of items 9 to 16.
(130) The invention further includes the following items: (a) the liquid crystal composition, further containing at least two of additives such as a polymerizable compound, a polymerization initiator, a polymerization inhibitor, an optically active compound, an antioxidant, an ultraviolet light absorber, a light stabilizer, a heat stabilizer and an antifoaming agent; (b) a polymerizable composition, prepared by adding a polymerizable compound different from compound (1) or compound (16) to the liquid crystal composition; (c) the polymerizable composition prepared by adding compound (1) and compound (16) to the liquid crystal composition; (d) a liquid crystal composite prepared by polymerizing the polymerizable composition; (e) a polymer sustained alignment mode device containing the liquid crystal composite; and (f) a polymer sustained alignment mode device, prepared by using a polymerizable composition prepared by adding compound (1), compound (16), and a polymerizable compound different from compound (1) or compound (16) to the liquid crystal composition.
(131) An aspect of compound (1), synthesis of compound (1), the liquid crystal composition and the liquid crystal display device will be described in the following order.
1. Aspect of Compound (1)
(132) Compound (1) of the invention has a mesogen moiety formed of at least one ring and an itaconate group. The itaconate group noncovalently interacts with a substrate surface of glass (or metal oxide), and therefore compound (1) tends to be unevenly distributed in a vicinity of the substrate surface in comparison with a compound having no itaconate group, and is useful. Thereby, an addition amount thereof becomes small. One of applications is as an additive for the liquid crystal composition used in the liquid crystal display device. Compound (1) is added for the purpose of horizontally controlling alignment of liquid crystal molecules. Such an additive preferably has chemical stability under conditions in which the additive is sealed in the device, high solubility in the liquid crystal composition, and a large voltage holding ratio when the compound is used in the liquid crystal display device. Compound (1) satisfies such characteristics to a significant extent.
(133) Preferred examples of compound (1) will be described. Preferred examples of R.sup.1, Z.sup.1 to Z.sup.5, A.sup.1 to A.sup.5, Sp.sup.1, Sp.sup.2, P.sup.2 and a in compound (1) apply also to a subordinate formula of formula (1) for compound (1). In compound (1), characteristics can be arbitrarily adjusted by suitably combining kinds of the groups. Compound (1) may contain a larger amount of isotope such as .sup.2H (deuterium) and .sup.13C than an amount of natural abundance because no significant difference exists in the characteristics of the compound.
(134) ##STR00035##
(135) Rings A.sup.1, A.sup.2, A.sup.3 and A.sup.4 are independently 1,4-cyclohexylene, 1,4-cyclohexenylene, 1,4-phenylene, naphthalene-2,6-diyl, decahydronaphthalene-2,6-diyl, 1,2,3,4-tetrahydronaphthalene-2,6-diyl, tetrahydropyran-2,5-diyl, 1,3-dioxane-2,5-diyl, pyrimidine-2,5-diyl, pyridine-2,5-diyl, fluorene-2,7-diyl, phenanthrene-2,7-diyl, anthracene-2,6-diyl, perhydrocyclopenta[a]phenanthrene-3,17-diyl or 2,3,4,7,8,9,10,11,12,13,14,15,16,17-tetradecahydrocyclopenta[a]phe nanthrene-3,17-diyl, and in the rings, at least one hydrogen may be replaced by fluorine, chlorine, alkyl having 1 to 12 carbons, alkenyl having 2 to 12 carbons, alkoxy having 1 to 11 carbons or alkenyloxy having 2 to 11 carbons, and in the groups, at least one hydrogen may be replaced by fluorine or chlorine, and when a is 2, two of ring A.sup.1 may be different, and when b is 2, two of ring A.sup.4 may be different.
(136) Preferred rings A.sup.1, A.sup.2, A.sup.3 and A.sup.4 are 1,4-cyclohexylene, 1,4-cyclohexenylene, 1,4-phenylene, naphthalene-2,6-diyl, decahydronaphthalene-2,6-diyl, 1,2,3,4-tetrahydronaphthalene-2,6-diyl, tetrahydropyran-2,5-diyl, 1,3-dioxane-2,5-diyl, pyrimidine-2,5-diyl, pyridine-2,5-diyl, perhydrocyclopenta[a]phenanthrene-3,17-diyl or 2,3,4,7,8,9,10,11,12,13,14,15,16,17-tetradecahydrocyclopenta[a]phe nanthrene-3,17-diyl, and in the rings, at least one hydrogen may be replaced by fluorine, chlorine, alkyl having 1 to 12 carbons, alkenyl having 2 to 12 carbons, alkoxy having 1 to 11 carbons or alkenyloxy having 2 to 11 carbons, and in the groups, at least one hydrogen may be replaced by fluorine or chlorine. Further preferred rings A.sup.1, A.sup.2, A.sup.3 and A.sup.4 are 1,4-cyclohexylene, 1,4-phenylene, perhydrocyclopenta[a]phenanthrene-3,17-diyl or 2,3,4,7,8,9,10,11,12,13,14,15,16,17-tetradecahydrocyclopenta[a]phe nanthrene-3,17-diyl, and in the rings, at least one hydrogen may be replaced by fluorine or alkyl having 1 to 5 carbons. Particularly preferred rings A.sup.1, A.sup.2, A.sup.3 and A.sup.4 are 1,4-cyclohexylene, 1,4-phenylene or perhydrocyclopenta[a]phenanthrene-3,17-diyl, and in the rings, at least one hydrogen may be replaced by fluorine, methyl or ethyl.
(137) Z.sup.1, Z.sup.2, Z.sup.3, Z.sup.4 and Z.sup.5 are independently a single bond or alkylene having 1 to 10 carbons, and in the alkylene, at least one —CH.sub.2— may be replaced by —O—, —CO—, —COO—, —OCO— or —OCOO—, and at least one —(CH.sub.2).sub.2— may be replaced by —CH═CH— or —C≡C—, and in the groups, at least one hydrogen may be replaced by halogen, in which at least one in Z.sup.2, Z.sup.3 or Z.sup.4 is any one of —COO—, —OCO—, —CH═CHCOO—, —OCOCH═CH—, —CH═CH—, —CH═CHCO— and —COCH═CH—, and when a is 2, two Z.sup.1s may be different, and two Z.sup.5s may be different.
(138) Preferred Z.sup.1, Z.sup.2, Z.sup.3, Z.sup.4 and Z.sup.5 are a single bond, —(CH.sub.2).sub.2—, —CH═CH—, —C≡C—, —COO—, —OCO—, —CF.sub.2O—, —OCF.sub.2—, —CH.sub.2O—, —OCH.sub.2— or —CF═CF—. Further preferred Z.sup.1, Z.sup.2, Z.sup.3, Z.sup.4 and Z.sup.5 are a single bond, —(CH.sub.2).sub.2— or —CH═CH—. Particularly preferred Z.sup.1, Z.sup.2, Z.sup.3, Z.sup.4 and Z.sup.5 are a single bond.
(139) Sp.sup.1 and Sp.sup.2 are a single bond or alkylene having 1 to 10 carbons, and in the alkylene, at least one —CH.sub.2— may be replaced by —O—, —CO—, —COO—, —OCO— or —OCOO—, and at least one —(CH.sub.2).sub.2— may be replaced by —CH═CH— or —C≡C—, and in the groups, at least one hydrogen may be replaced by halogen.
(140) Preferred Sp.sup.1 and Sp.sup.2 are a single bond, alkylene having 1 to 6 carbons, alkylene having 1 to 6 carbons in which one —CH.sub.2— is replaced by —O—, or —OCOO—. Further preferred Sp.sup.1 and Sp.sup.2 are alkylene having 1 to 6 carbons or —OCOO—.
(141) P.sup.1 is a group represented by any one of formulas (1b) to (1i).
(142) Preferred P.sup.1 is represented by formulas (1b), (1c) and (1d)
(143) ##STR00036##
(144) In formulas (1b) to (1i), M.sup.1 and M.sup.2 are independently hydrogen, halogen, alkyl having 1 to 5 carbons, or alkyl having 1 to 5 carbons in which at least one hydrogen is replaced by halogen.
(145) Preferred M.sup.1 or M.sup.2 is hydrogen, fluorine, methyl, ethyl or trifluoromethyl. Further preferred M.sup.1 or M.sup.2 is hydrogen.
(146) R.sup.2 is hydrogen, halogen or alkyl having 1 to 5 carbons, and in the alkyl, at least one hydrogen may be replaced by halogen, and at least one —CH.sub.2— may be replaced by —O—.
(147) Preferred R.sup.2 is hydrogen, fluorine, methyl, ethyl, methoxymethyl or trifluoromethyl. Further preferred R.sup.2 is hydrogen.
(148) R.sup.3, R.sup.4 and R.sup.5 are independently hydrogen or straight-chain, branched-chain or cyclic alkyl having 1 to 15 carbons, and in the alkyl, at least one —CH.sub.2— may be replaced by —O— or —S—, and at least one —(CH.sub.2).sub.2— may be replaced by —CH═CH— or —C≡C—, and in the groups, at least one hydrogen may be replaced by halogen.
(149) Preferred R.sup.3, R.sup.4 and R.sup.5 are hydrogen, straight-chain alkyl having 1 to 10 carbons, straight-chain alkenyl having 2 to 10 carbons, straight-chain alkoxy having 1 to 10 carbons or cyclic alkyl having 3 to 6 carbons. Further preferred R.sup.3, R.sup.4 and R.sup.5 are hydrogen, straight-chain alkyl having 2 to 6 carbons, straight-chain alkenyl having 2 to 6 carbons, straight-chain alkoxy having 1 to 5 carbons or cyclic alkyl having 4 to 6 carbons.
(150) Then, expressions: 0≤a+b≤2 preferably hold.
(151) Preferred examples of compound (1) include formulas (1-1) to (1-3).
(152) ##STR00037##
(153) R.sup.5 is hydrogen or alkyl having 1 to 15 carbons, and in the alkyl, at least one —CH.sub.2— may be replaced by —O— or —S—, and at least one —(CH.sub.2).sub.2— may be replaced by —CH═CH— or —C≡C—, and in the groups, at least one hydrogen may be replaced by halogen.
(154) Definition of other symbols in formulas (1-1) to (1-3) and preferred examples are identical to compound (1). Moreover, specific examples of compound (1) will be described in Examples described later.
(155) In formulas (2) to (15), component compounds of the liquid crystal composition are shown. Compounds (2) to (4) have small dielectric anisotropy. Compounds (5) to (7) have large positive dielectric anisotropy. Compound (8) has a cyano group, and therefore has larger positive dielectric anisotropy. Compounds (9) to (15) have large negative dielectric anisotropy. Specific examples of the compounds will be described later.
(156) In compound (16), P.sup.11, P.sup.12 and P.sup.13 are independently a polymerizable group.
(157) Preferred P.sup.11, P.sup.12 and P.sup.13 are a polymerizable group selected from the group of groups represented by formulas (P-1) to (P-5). Further preferred P.sup.11, P.sup.12 and P.sup.13 are group (P-1), group (P-2) or group (P-3). Particularly preferred group (P-1) is —OCO—CH═CH.sub.2 or —OCO—C(CH.sub.3)═CH.sub.2. A wavy line in group (P-1) to group (P-5) represents a site to form a bonding.
(158) ##STR00038##
(159) In the groups (P-1) to (P-5), M.sup.11, M.sup.12 and M.sup.13 are independently hydrogen, fluorine, alkyl having 1 to 5 carbons, or alkyl having 1 to 5 carbons in which at least one hydrogen is replaced by halogen.
(160) Preferred M.sup.11, M.sup.12 and M.sup.13 are hydrogen or methyl for increasing reactivity. Further preferred M.sup.11 is methyl, and further preferred M.sup.12 and M.sup.13 are hydrogen.
(161) Sp.sup.11, Sp.sup.12 and Sp.sup.13 are independently a single bond or alkylene having 1 to 10 carbons, and in the alkylene, at least one —CH.sub.2— may be replaced by —O—, —COO—, —OCO— or —OCOO—, and at least one —CH.sub.2CH.sub.2— may be replaced by —CH═CH— or —C≡C—, and in the groups, at least one hydrogen may be replaced by fluorine or chlorine.
(162) Preferred Sp.sup.11, Sp.sup.12 and Sp.sup.13 are a single bond.
(163) Ring F and ring I are independently cyclohexyl, cyclohexenyl, phenyl, 1-naphthyl, 2-naphthyl, tetrahydropyran-2-yl, 1,3-dioxane-2-yl, pyrimidine-2-yl or pyridine-2-yl, and in the rings, at least one hydrogen may be replaced by halogen, alkyl having 1 to 12 carbons, alkoxy having 1 to 12 carbons, or alkyl having 1 to 12 carbons in which at least one hydrogen is replaced by halogen.
(164) Preferred ring F and ring I are phenyl. Ring G is 1,4-cyclohe xylene, 1,4-cyclohexenylene, 1,4-phenylene, naphthalene-1,2-diyl, naphthalene-1,3-diyl, naphthalene-1,4-diyl, naphthalene-1,5-diyl, naphthalene-1,6-diyl, naphthalene-1,7-diyl, naphthalene-1,8-diyl, naphthalene-2,3-diyl, naphthalene-2,6-diyl, naphthalene-2,7-diyl, tetrahydropyran-2,5-diyl, 1,3-dioxane-2,5-diyl, pyrimidine-2,5-diyl or pyridine-2,5-diyl, and in the rings, at least one hydrogen may be replaced by halogen, alkyl having 1 to 12 carbons, alkoxy having 1 to 12 carbons, or alkyl having 1 to 12 carbons in which at least one hydrogen is replaced by halogen. Particularly preferred ring G is 1,4-phenylene or 2-fluoro-1,4-phenylene.
(165) Z.sup.22 and Z.sup.23 are independently a single bond or alkylene having 1 to 10 carbons, and in the alkylene, at least one —CH.sub.2— may be replaced by —O—, —CO—, —COO— or —OCO—, and at least one —CH.sub.2CH.sub.2— may be replaced by —CH═CH—, —C(CH.sub.3)═CH—, —CH═C(CH.sub.3)— or —C(CH.sub.3)═C(CH.sub.3)—, and in the groups, at least one hydrogen may be replaced by fluorine or chlorine.
(166) Preferred Z.sup.22 and Z.sup.23 are a single bond, —CH.sub.2CH.sub.2—, —CH.sub.2O—, —OCH.sub.2—, —COO— or —OCO—. Further preferred Z.sup.22 and Z.sup.23 are a single bond.
(167) Then, u is 0, 1 or 2.
(168) Preferred u is 0 or 1. Then, f, g and h are independently 0, 1, 2, 3 or 4, and a sum of f, g and h is 1 or more. Preferred f, g or h is 1 or 2.
2. Synthesis of Compound (1)
(169) A synthesis method of compound (1) will be described. Compound (1) can be prepared by suitably combining methods in synthetic organic chemistry. Any compounds whose synthetic methods are not described above are prepared according to methods described in books such as “Organic Syntheses” (John Wiley & Sons, Inc.), “Organic Reactions” (John Wiley & Sons, Inc.), “Comprehensive Organic Synthesis” (Pergamon Press) and “New Experimental Chemistry Course (Shin Jikken Kagaku Koza in Japanese)” (Maruzen Co., Ltd.).
2-1. Formation of Bonding Groups Z.SUP.1., Z.SUP.2., Z.SUP.3., Z.SUP.4 .and Z.SUP.5
(170) An example of a method for forming a bonding group in compound (1) is as described in a scheme below. In the scheme, MSG.sup.1 (or MSG.sup.2) is a monovalent organic group having at least one ring. Monovalent organic groups represented by a plurality of MSG.sup.1 (or MSG.sup.2) may be identical or different. Compounds (1A) to (1G) correspond to compound (1) or an intermediate of compound (1).
(171) ##STR00039## ##STR00040##
(I) Formation of a Single Bond
(172) Compound (1A) is prepared by allowing aryl boronic acid (21) to react with compound (22) in the presence of carbonate and a tetrakis(triphenylphosphine)palladium catalyst. Compound (1A) is also prepared by allowing compound (23) to react with n-butyllithium and subsequently with zinc chloride, and further with compound (22) in the presence of a dichlorobis(triphenylphosphine)palladium catalyst.
(173) (II) Formation of —COO— and —OCO—
(174) Carboxylic acid (24) is obtained by allowing compound (23) to react with n-butyllithium and subsequently with carbon dioxide. Compound (1B) having —COO— is prepared by dehydration of carboxylic acid (24) and phenol (25) derived from compound (21) in the presence of 1,3-dicyclohexylcarbodiimide (DCC) and 4-dimethylaminopyridine (DMAP). A compound having —OCO— is also prepared according to the method.
(175) (III) Formation of —CF.sub.2O— and —OCF.sub.2—
(176) Compound (26) is obtained by sulfurizing compound (1B) with Lawesson's reagent. Compound (1C) having —CF.sub.2O— is prepared by fluorinating compound (26) with a hydrogen fluoride-pyridine complex and N-bromosuccinimide (NBS). Refer to M. Kuroboshi et al., Chem. Lett., 1992, 827. Compound (1C) is also prepared by fluorinating compound (26) with (diethylamino) sulfur trifluoride (DAST). Refer to W. H. Bunnelle et al., J. Org. Chem. 1990, 55, 768. A compound having —OCF.sub.2— is also prepared according to the method.
(177) (IV) Formation of —CH═CH—
(178) Aldehyde (27) is obtained by allowing compound (22) to react with n-butyllithium and subsequently with N,N-dimethylformamide (DMF). Compound (1D) is prepared by allowing phosphorus ylide generated by allowing phosphonium salt (28) to react with potassium t-butoxide to react with aldehyde (27). A cis isomer may be formed depending on reaction conditions, and therefore the cis isomer is isomerized into a trans isomer according to a publicly-known method when necessary.
(179) (V) Formation of —CH.sub.2CH.sub.2—
(180) Compound (1E) is prepared by hydrogenating compound (1D) in the presence of a palladium on carbon catalyst.
(181) (VI) Formation of —C≡C—
(182) Compound (29) is obtained by allowing compound (23) to react with 2-methyl-3-butyn-2-ol in the presence of a catalyst of dichloropalladium and copper iodide, and then performing deprotection under basic conditions. Compound (1F) is prepared by allowing compound (29) to react with compound (22) in the presence of a catalyst of dichlorobis(triphenylphosphine)palladium and copper halide.
(183) (VII) Formation of —CH.sub.2O— and —OCH.sub.2—
(184) Compound (30) is obtained by reducing compound (27) with sodium borohydride. Compound (31) is obtained by brominating the obtained compound with hydrobromic acid. Compound (1G) is prepared by allowing compound (25) to react with compound (31) in the presence of potassium carbonate. A compound having —OCH.sub.2— is also prepared according to the method.
(185) (VIII) Formation of —CF═CF—
(186) Compound (32) is obtained by treating compound (23) with n-butyllithium, and then allowing the treated material to react with tetrafluoroethylene. Compound (1H) is prepared by treating compound (22) with n-butyllithium, and then allowing the treated material to react with compound (32).
(187) (VIV) Formation of —CH═CHCO— and —COCH═CH—
(188) Compound (1I) is prepared by allowing compound (40) to be subjected to aldol condensation reaction with compound (27) in the presence of NaOH.
(189) (X) Formation of —CH═CHCOO— and —OCOCH═CH—
(190) Compound (1J) is prepared by dehydration of cinnamic acid (41) and compound (25) in the presence of 1,3-dicyclohexylcarbodiimide (DCC) and 4-dimethylaminopyridine (DMAP).
2-2. Formation of Rings A.SUP.1., A.SUP.2., A.SUP.3 .and A.SUP.4
(191) A starting material is commercially available or a synthetic method is well known with regard to a ring such as 1,4-cyclohexylene, 1,4-cyclohexenylene, 1,4-phenylene, 2-fluoro-1,4-phenylene, 2-methyl-1,4-phenylene, 2-ethyl-1,4-phenylene, naphthalene-2,6-diyl, decahydronaphthalene-2,6-diyl, 1,2,3,4-tetrahydronaphthalene-2,6-diyl, tetrahydropyran-2,5-diyl, 1,3-dioxane-2,5-diyl, pyrimidine-2,5-diyl, pyridine-2,5-diyl, perhydrocyclopenta[a]phenanthrene-3,17-diyl and 2,3,4,7,8,9,10,11,12,13,14,15,16,17-tetradecahydrocyclopenta[a]phe nanthrene-3,17-diyl.
2-3. Formation of Linking Group Sp.SUP.1 .or Sp.SUP.2 .and Polymerizable Group P.SUP.1 .or P.SUP.2
(192) Preferred examples of polymerizable group P.sup.1 or P.sup.2 include acryloyloxy (1b), maleimide (1c), an itaconic acid ester (1d), oxiranyl (1h) or vinyloxy (1i).
(193) ##STR00041##
(194) An example of a method for preparing a compound in which the polymerizable group is bonded to a ring through linking group Sp.sup.1 or Sp.sup.2 is as described below. First, an example in which linking group Sp.sup.1 or Sp.sup.2 is a single bond will be described.
(195) (1) Synthesis of a Compound Having a Single Bond
(196) A method of preparing a compound having a single bond is as described in a scheme below. In the scheme, MSG.sup.1 is a monovalent organic group having at least one ring. Compounds (1S) to (1Z) correspond to compound (1). When the polymerizable group is an acrylate derivative, the acrylate derivative is prepared by performing esterification between the corresponding acrylic acid and HO-MSG.sup.1. Allyl ether is prepared by performing etherification between HO-MSG.sup.1 and vinyl bromide. An epoxy group is prepared by oxidation of a terminal double bond. A maleimide group is prepared by reaction between an amino group and maleic anhydride. An itaconic acid ester is prepared by performing esterification between the corresponding itaconic acid and HO-MSG.sup.1.
(197) ##STR00042## ##STR00043##
(198) A synthesis method of the compound in which linking group Sp.sup.1 or Sp.sup.2 is a single bond is described above. As for a method of producing other linking groups, other linking groups can be prepared according to the synthesis method of bonding groups Z.sup.1, Z.sup.2, Z.sup.3, Z.sup.4 and Z.sup.5.
2-4. Synthesis Example
(199) An example of a method for preparing compound (1) is as described below. In the compounds, MES is a mesogen group having at least one ring. Definitions of P.sup.1, M.sup.1, M.sup.2, Sp.sup.1 and Sp.sup.2 are identical to the definitions described above.
(200) Compound (51A) or compound (51B) is commercially available, or can be prepared according to a common organic synthesis method by using a mesogen (MES) having a suitable ring structure as a starting material. When a compound in which MES and Sp.sup.1 is linked through an ether bond is prepared, compound (53) can be obtained by allowing compound (51A) as a starting material to be subjected to etherification by using compound (52) and a base such as potassium hydroxide. Moreover, when a compound in which MES and Sp.sup.1 is linked with a single bond is prepared, compound (53) can be obtained by allowing compound (51B) as a starting material to be subjected to cross-coupling reaction by using compound (52), a metal catalyst such as palladium and a base. Compound (53) may be derived to compound (54) in which a protective group such as TMS and THP is allowing to act therewith, when necessary.
(201) Then, compound (56) can be obtained by allowing compound (53) or compound (54) to be subjected to etherification again in the presence of a base such as compound (55) and potassium hydroxide. On this occasion, when the protective group is allowed to act in a previous stage, the protective group is removed by a deprotection reaction.
(202) ##STR00044##
(203) Compound (1A) in which P.sup.2 is a group represented by formula (1d) can be prepared with compound (57) according to a method described below. Compound (1A) can be derived by allowing compound (57) to be subjected to an esterification reaction in the presence of compound (58), DCC and DMAP.
(204) ##STR00045##
3. Liquid Crystal Composition
(205) A liquid crystal composition of the invention contains compound (1) as component A. Compound (1) can control the alignment of liquid crystal molecules by non-covalent interaction with a substrate of the device. The composition contains compound (1) as component A, and preferably further contains a liquid crystal compound selected from components B, C, D and E described below. Component B includes compounds (2) to (4). Component C includes compounds (5) to (7) Component D includes compound (8). Component E includes compounds (9) to (15). The composition may contain any other liquid crystal compound different from compounds (2) to (15). When the composition is prepared, components B, C, D and E are preferably selected by taking into account largeness of positive or negative dielectric anisotropy, or the like. The composition in which the components are suitably selected has high maximum temperature, low minimum temperature, small viscosity, suitable optical anisotropy (more specifically, large optical anisotropy or small optical anisotropy), large positive or negative dielectric anisotropy, large specific resistance, high stability to heat and ultraviolet light and a suitable elastic constant (more specifically, a large elastic constant or a small elastic constant).
(206) A preferred proportion of compound (1) is about 0.01% by weight or more for maintaining high stability to ultraviolet light, and about 5% by weight or less for dissolution in the liquid crystal composition. A further preferred proportion is in the range of about 0.05% by weight to about 2% by weight. A most preferred proportion is in the range of about 0.05% by weight to about 1% by weight.
(207) Component B includes a compound in which two terminal groups are alkyl or the like. Preferred examples of component B include compounds (2-1) to (2-11), compounds (3-1) to (3-19) and compounds (4-1) to (4-7). In the compounds of component B, R.sup.11 and R.sup.12 are independently alkyl having 1 to 10 carbons or alkenyl having 2 to 10 carbons, and in the alkyl or the alkenyl, at least one —CH.sub.2— may be replaced by —O—, and at least one hydrogen may be replaced by fluorine.
(208) ##STR00046## ##STR00047## ##STR00048## ##STR00049##
(209) Component B has a small absolute value of dielectric anisotropy, and therefore is a compound close to neutrality. Compound (2) is mainly effective in decreasing the viscosity or adjusting the optical anisotropy. Compounds (3) and (4) are effective in extending a temperature range of a nematic phase by increasing the maximum temperature, or in adjusting the optical anisotropy.
(210) As a content of component B increases, the dielectric anisotropy of the composition decreases, but the viscosity decreases. Thus, as long as a desired value of threshold voltage of a device is met, the content is preferably as large as possible. When a composition for the IPS mode, the VA mode or the like is prepared, the content of component B is preferably 30% by weight or more, and further preferably 40% by weight or more, based on the weight of the liquid crystal composition.
(211) Component C is a compound having a halogen-containing group or a fluorine-containing group at a right terminal. Preferred examples of component C include compounds (5-1) to (5-16), compounds (6-1) to (6-120) and compounds (7-1) to (7-62). In the compounds of component C, R.sup.13 is alkyl having 1 to 10 carbons or alkenyl having 2 to 10 carbons, and in the alkyl and the alkenyl, at least one —CH.sub.2— may be replaced by —O—, and at least one hydrogen may be replaced by fluorine; and X.sup.11 is fluorine, chlorine, —OCF.sub.3, —OCHF.sub.2, —CF.sub.3, —CHF.sub.2, —CH.sub.2F, —OCF.sub.2CHF.sub.2 or —OCF.sub.2CHFCF.sub.3.
(212) ##STR00050## ##STR00051## ##STR00052## ##STR00053## ##STR00054## ##STR00055## ##STR00056## ##STR00057## ##STR00058## ##STR00059## ##STR00060## ##STR00061## ##STR00062## ##STR00063## ##STR00064##
(213) ##STR00065## ##STR00066## ##STR00067## ##STR00068##
(214) Component C has positive dielectric anisotropy, and superb stability to heat, light and so forth, and therefore is used when a composition for the IPS mode, the FFS mode, the OCB mode or the like is prepared. A content of component C is suitably in the range of 1% by weight to 99% by weight, preferably in the range of 10% by weight to 97% by weight, and further preferably in the range of 40% by weight to 95% by weight, based on the weight of the liquid crystal composition. When component C is added to a composition having negative dielectric anisotropy, the content of component C is preferably 30% by weight or less based on the weight of the liquid crystal composition. Addition of component C allows adjustment of the elastic constant of the composition and adjustment of a voltage-transmittance curve of the device.
(215) Component D is compound (8) in which a right-terminal group is —C≡N or —C≡C—C≡N. Preferred examples of component D include compounds (8-1) to (8-64). In the compounds of component D, R.sup.14 is alkyl having 1 to 10 carbons or alkenyl having 2 to 10 carbons, and in the alkyl and the alkenyl, at least one —CH.sub.2— may be replaced by —O—, and at least one hydrogen may be replaced by fluorine; and —X.sup.12 is —C≡N or —C≡C—C≡N.
(216) ##STR00069## ##STR00070## ##STR00071## ##STR00072## ##STR00073## ##STR00074## ##STR00075##
(217) Component D has positive dielectric anisotropy and a value thereof is large, and therefore is mainly used when a composition for the TN mode or the like is prepared. Addition of component D can increase the dielectric anisotropy of the composition. Component D is effective in extending a temperature range of a liquid crystal phase, adjusting the viscosity or adjusting the optical anisotropy. Component D is also useful for adjustment of the voltage-transmittance curve of the device.
(218) When the composition for the TN mode or the like is prepared, a content of component D is suitably in the range of 1% by weight to 99% by weight, preferably in the range of 10% by weight to 97% by weight, and further preferably in the range of 40% by weight to 95% by weight, based on the weight of the liquid crystal composition. When component D is added to a composition having negative dielectric anisotropy, the content of component D is preferably 30% by weight or less based on the weight of the liquid crystal composition. Addition of component D allows adjustment of the elastic constant of the composition and adjustment of the voltage-transmittance curve of the device.
(219) Component E includes compounds (9) to (16). The compounds have phenylene in which hydrogen in lateral positions are replaced by two halogens, such as 2,3-difluoro-1,4-phenylene.
(220) Preferred examples of component E include compounds (9-1) to (9-8), compounds (10-1) to (10-17), compound (11-1), compounds (12-1) to (12-3), compounds (13-1) to (13-11), compounds (14-1) to (14-3), compounds (15-1) to (15-3) and compounds (16-1) to (16-3). In the compounds of component E, R.sup.15 and R.sup.16 are independently alkyl having 1 to 10 carbons or alkenyl having 2 to 10 carbons, and in the alkyl and the alkenyl, at least one —CH.sub.2— may be replaced by —O—, and at least one hydrogen may be replaced by fluorine; and R.sup.17 is hydrogen, fluorine, alkyl having 1 to 10 carbons or alkenyl having 2 to 10 carbons, and in the alkyl and the alkenyl, at least one —CH.sub.2— may be replaced by —O—, and at least one hydrogen may be replaced by fluorine.
(221) ##STR00076## ##STR00077##
(222) Component E has large negative dielectric anisotropy. Component E is used when a composition for the IPS mode, the VA mode, the PSA mode or the like is prepared. As a content of component E increases, the dielectric anisotropy of the composition negatively increases, but the viscosity increases. Thus, as long as a desired value of threshold voltage of the device is met, the content is preferably as small as possible. When the dielectric anisotropy at a degree of −5 is taken into account, the content is preferably 40% by weight or more in order to allow a sufficient voltage driving.
(223) Among types of component E, compound (9) is a bicyclic compound, and therefore is mainly effective in decreasing the viscosity, adjusting the optical anisotropy or increasing the dielectric anisotropy. Compounds (10) and (11) are a tricyclic compound, and therefore are effective in increasing the maximum temperature, the optical anisotropy or the dielectric anisotropy. Compounds (12) to (15) are effective in increasing the dielectric anisotropy.
(224) When a composition for the IPS mode, the VA mode, the PSA mode or the like is prepared, the content of component E is preferably 40% by weight or more, and further preferably in the range of 50% by weight to 95% by weight, based on the weight of the liquid crystal composition. When component E is added to a composition having positive dielectric anisotropy, the content of component E is preferably 30% by weight or less based on the weight of the liquid crystal composition. Addition of component E allows adjustment of the elastic constant of the composition and adjustment of the voltage-transmittance curve of the device.
(225) The liquid crystal composition satisfying at least one of characteristics such as the high maximum temperature, the low minimum temperature, the small viscosity, the suitable optical anisotropy, the large positive or negative dielectric anisotropy, the large specific resistance, the high stability to ultraviolet light, the high stability to heat and the large elastic constant can be prepared by suitably combining components B, C, D and E described above. A liquid crystal compound different from components B, C, D and E may be added when necessary.
(226) A liquid crystal composition is prepared according to a publicly-known method. For example, the component compounds are mixed and dissolved in each other by heating. According to an application, an additive may be added to the composition. Specific examples of the additives include a polymerizable compound other than formula (1) and formula (16), a polymerization initiator, a polymerization inhibitor, an optically active compound, an antioxidant, an ultraviolet light absorber, a light stabilizer, a heat stabilizer and an antifoaming agent. Such additives are well known to those skilled in the art, and described in literature.
(227) The polymerizable compound is added for the purpose of forming a polymer in the liquid crystal composition. The polymerizable compound and compound (1) are copolymerized by irradiation with ultraviolet light while voltage is applied between electrodes, whereby the polymer is formed in the liquid crystal composition. On the occasion, compound (1) is immobilized in a state in which the polar group noncovalently interacts with the substrate surface of glass (or metal oxide). Thus, capability of controlling the alignment of liquid crystal molecules is further improved, and simultaneously the polar compound no longer leaks into the liquid crystal composition. Moreover, suitable pretilt angle can be obtained even in the substrate surface of glass (or metal oxide), and therefore a liquid crystal display device in which a response time is shortened and the voltage holding ratio is large can be obtained.
(228) Preferred examples of the polymerizable compound include acrylate, methacrylate, a vinyl compound, a vinyloxy compound, propenyl ether, an epoxy compound (oxirane, oxetane) and vinyl ketone. Further preferred examples include a compound having at least one acryloyloxy, and a compound having at least one methacryloyloxy. Still further preferred examples also include a compound having both acryloyloxy and methacryloyloxy.
(229) Still further preferred examples include compounds (M-1) to (M-17) In compounds (M-1) to (M-17), R.sup.25 to R.sup.31 are independently hydrogen or methyl; s, v and x are independently 0 or 1; t and u are independently an integer from 1 to 10; and L.sup.21 to L.sup.26 are independently hydrogen or fluorine, and L.sup.27 and L.sup.28 are independently hydrogen, fluorine or methyl.
(230) ##STR00078## ##STR00079## ##STR00080##
(231) The polymerizable compound can be rapidly polymerized by adding the polymerization initiator. An amount of a remaining polymerizable compound can be decreased by optimizing a reaction temperature. Examples of a photoradical polymerization initiator include TPO, 1173 and 4265 from Darocur series of BASF SE, and 184, 369, 500, 651, 784, 819, 907, 1300, 1700, 1800, 1850 and 2959 from Irgacure series thereof.
(232) Additional examples of the photoradical polymerization initiator include 4-methoxyphenyl-2,4-bis(trichloromethyl)triazine, 2-(4-butoxystyryl)-5-trichloromethyl-1,3,4-oxadiazole, 9-phenylacridine, 9,10-benzphenazine, a benzophenone-Michler's ketone mixture, a hexaarylbiimidazole-mercaptobenzimidazole mixture, 1-(4-isopropylphenyl)-2-hydroxy-2-methylpropane-1-one, benzyl dimethyl ketal, 2-methyl-1-[4-(methylthio)phenyl]-2-morpholinopropane-1-one, a mixture of 2,4-diethylxanthone and methyl p-dimethylaminobenzoate, and a mixture of benzophenone and methyltriethanolamine.
(233) After the photoradical polymerization initiator is added to the liquid crystal composition, polymerization can be performed by irradiation with ultraviolet light in a state in which an electric field is applied thereto. However, an unreacted polymerization initiator or a decomposition product of the polymerization initiator may cause poor display such as image persistence in the device. In order to prevent such an event, photopolymerization may be performed with no addition of the polymerization initiator. A preferred wavelength of light used for irradiation is in the range of 150 nanometers to 500 nanometers. A further preferred wavelength is in the range of 250 nanometers to 450 nanometers, and a most preferred wavelength is in the range of 300 nanometers to 400 nanometers.
(234) Upon mixing compound (1) having an ester-bonding group, a cinnamic acid ester-bond, a chalcone skeleton or a stilbene skeleton in the composition, a main effect of the component compound on the characteristics of the composition is as described below. When Fries rearrangement, photo-dimerization or cis-trans isomerization of a double bond is caused by polarized light, the compound (1) is aligned in a fixed direction at a molecular level. Accordingly, a thin film prepared from the polar compound aligns the liquid crystal molecules in the same manner as an alignment film of polyimide or the like.
(235) In a compound having an aromatic ester and a polymerizable group, photolysis in an aromatic ester moiety is caused by irradiation with ultraviolet light to form a radical, and photo-Fries rearrangement is caused. In the photo-Fries rearrangement, the photolysis of the aromatic ester moiety is caused when a polarization direction of polarized ultraviolet light and a major axis direction of the aromatic ester moiety are identical. Recombination of the compound is caused after photolysis to generate a hydroxyl group in the molecule by tautomerization. Interaction in a substrate interface is caused by the hydroxyl group, and the polar compound is considered to be easily adsorbed with anisotropy on a side of the substrate interface. Moreover, the compound has the polymerizable group, and therefore is immobilized by polymerization. The property is utilized, whereby the thin film capable of aligning the liquid crystal molecule can be prepared. Linearly polarized light is suitable as ultraviolet light used for irradiation in order to prepare the thin film. First, the polar compound is added to the liquid crystal composition in the range of 0.1% by weight to 10% by weight, and the resulting composition is warmed in order to dissolve the polar compound thereinto. The composition is injected into the device having no alignment film. Next, the devise is irradiated with the linearly polarized light while warming the device to cause the photo-Fries rearrangement of the polar compound to polymerize the compound.
(236) The polar compound in which the photo-Fries rearrangement is caused is aligned in a fixed direction, and the thin film formed after polymerization has a function as a liquid crystal alignment film.
(237) Upon storing the polymerizable compound, the polymerization inhibitor may be added thereto for preventing polymerization. The polymerizable compound is ordinarily added to the composition without removing the polymerization inhibitor. Specific examples of the polymerization inhibitor include hydroquinone, a hydroquinone derivative such as methylhydroquinone, 4-t-butylcatechol, 4-methoxyphenol and phenothiazine.
(238) The optically active compound is effective in inducing helical structure in the liquid crystal molecules to give a required twist angle, thereby preventing a reverse twist. A helical pitch can be adjusted by adding the optically active compound thereto. Two or more optically active compounds may be added for the purpose of adjusting temperature dependence of the helical pitch. Specific examples of a preferred optically active compound include compounds (Op-1) to (Op-18) described below. In compound (Op-18), ring J is 1,4-cyclohexylene or 1,4-phenylene, and R.sup.28 is alkyl having 1 to 10 carbons.
(239) ##STR00081## ##STR00082## ##STR00083##
(240) The antioxidant is effective for maintaining the large voltage holding ratio. Preferred examples of the antioxidant include compounds (AO-1) and (AO-2) described below; and IRGANOX 415, IRGANOX 565, IRGANOX 1010, IRGANOX 1035, IRGANOX 3114 and IRGANOX 1098 (trade names; BASF SE). The ultraviolet light absorber is effective for preventing a decrease of the maximum temperature. Preferred examples of the ultraviolet light absorber include a benzophenone derivative, a benzoate derivative and a triazole derivative. Specific examples thereof include compounds (AO-3) and (AO-4) described below; TINUVIN 329, TINUVIN P, TINUVIN 326, TINUVIN 234, TINUVIN 213, TINUVIN 400, TINUVIN 328 and TINUVIN 99-2 (trade names; BASF SE); and 1,4-diazabicyclo[2.2.2]octane (DABCO).
(241) The light stabilizer such as an amine having steric hindrance is preferred for maintaining the large voltage holding ratio. Specific examples of a preferred light stabilizer include compounds (AO-5) and (AO-6) described below; and TINUVIN 144, TINUVIN 765 and TINUVIN 770DF (trade names: BASF SE). The heat stabilizer is also effective for maintaining the large voltage holding ratio, and specific preferred examples include IRGAFOS 168 (trade name; BASF SE). The antifoaming agent is effective for preventing foam formation. Preferred examples of the antifoaming agent include dimethyl silicone oil and methylphenyl silicone oil.
(242) ##STR00084##
(243) In compound (AO-1), R.sup.40 is alkyl having 1 to 20 carbons, alkoxy having 1 to 20 carbons, —COOR.sup.41 or —CH.sub.2CH.sub.2COOR.sup.41, in which R.sup.41 is alkyl having 1 to 20 carbons. In compounds (AO-2) and (AO-5), R.sup.42 is alkyl having 1 to 20 carbons. In compound (AO-5), R.sup.43 is hydrogen, methyl or O. (oxygen radical), ring G is 1,4-cyclohexylene or 1,4-phenylene, and z is 1, 2 or 3.
4. Liquid Crystal Display Device
(244) The liquid crystal composition can be used in a liquid crystal display device having an operating mode such as the PC mode, the TN mode, the STN mode, the OCB mode and the PSA mode, and driven by an active matrix mode. The composition can also be used in a liquid crystal display device having the operating mode such as the PC mode, the TN mode, the STN mode, the OCB mode, the VA mode and the IPS mode, and driven by a passive matrix mode. The devices can be applied to any of a reflective type, a transmissive type and a transflective type.
(245) The composition can also be used in a nematic curvilinear aligned phase (NCAP) device prepared by microencapsulating a nematic liquid crystal, and a polymer dispersed liquid crystal display device (PDLCD) and a polymer network liquid crystal display device (PNLCD), in which a three-dimensional network-polymer is formed in the liquid crystal. When an amount of addition of the polymerizable compound is about 10% by weight or less based on the weight of the liquid crystal composition, a liquid crystal display device having the PSA mode is prepared. A preferred proportion thereof is in the range of about 0.1% by weight to about 2% by weight. A further preferred proportion is in the range of about 0.2% by weight to about 1.0% by weight. The device having the PSA mode can be driven by the driving mode such as the active matrix mode and the passive matrix mode. Such a device can be applied to any of the reflective type, the transmissive type and the transflective type. A polymer dispersed mode device can also be prepared by increasing the amount of addition of the polymerizable compound.
(246) In the polymer sustained alignment mode device, the polymer contained in the composition aligns the liquid crystal molecules. The polar compound assists alignment of the liquid crystal molecules. More specifically, the polar compound can be used in place of the alignment film. One example of a method for producing such a device is as described below.
(247) A device having two substrates referred to as an array substrate and a color filter substrate is arranged. The substrate has no alignment film. At least one of the substrates has an electrode layer. The liquid crystal composition is prepared by mixing the liquid crystal compounds. The polymerizable compound and the polar compound are added to the composition. The additive may be further added thereto when necessary. The composition is injected into the device. The device is irradiated with light. Ultraviolet light is preferred. The polymerizable compound is polymerized by irradiation with light. The composition containing the polymer is formed by the polymerization to prepare a device having the PSA mode.
(248) A method for producing the device will be described. First, the method includes a step of adding a polar compound to a liquid crystal composition, and then warming the resulting composition at a temperature higher than the maximum temperature thereof to dissolve the composition. Second, the method includes a step of injecting the composition into a liquid crystal display device. Third, the method includes a step of irradiating the composition with polarized ultraviolet light while warming the liquid crystal composition at a temperature higher than the maximum temperature thereof. The polar compound causes any one of the photo-Fries rearrangement, photo-dimerization or cis-trans isomerization of a double bond by linearly polarized light, and simultaneously polymerization thereof also progresses. A polymer formed of the polar compound is formed as the thin film on the substrate, and immobilized thereon. The compound is aligned in a fixed direction at a molecular level, and therefore the thin film has the function as the liquid crystal alignment film. A liquid crystal display device having no alignment film such as polyimide can be produced by the method described above.
(249) In the procedure, the polar group interacts with the substrate surface, and therefore the polar compound is unevenly distributed on the substrate. The polar compound is unevenly distributed, and thus an amount of addition of the compound can be suppressed in comparison with the compound having no polar group. The polar compound aligns the liquid crystal molecules by irradiation with polarized ultraviolet light, and simultaneously the polymerizable compound is polymerized by ultraviolet light, and therefore a polymer maintaining the alignment is formed. The alignment of the liquid crystal molecules is additionally stabilized by an effect of the polymer, and therefore the response time in the device is shortened. The image persistence is caused due to poor operation of the liquid crystal molecules, and therefore the persistence is also simultaneously improved by the effect of the polymer. In particular, compound (1) of the invention is a polymerizable polar compound, and therefore aligns liquid crystal molecules, and also is copolymerized with any other polymerizable compound. Thus, the polar compound is no longer leaked into the liquid crystal composition, and therefore the liquid crystal display device having a large voltage holding ratio can be obtained.
EXAMPLES
(250) Hereinafter, the invention will be described in greater detail by way of Examples (including Synthesis Examples and Use Examples of devices). However, the invention is not limited by the Examples. The invention includes a mixture of a composition in Use Example 1 and a composition in Use Example 2. The invention also includes a mixture prepared by mixing at least two compositions in each Use Example.
1. Example of Compound (1)
(251) Compound (1) was prepared according to procedures shown in Example. Unless otherwise specified, a reaction was performed under a nitrogen atmosphere. Compound (1) was prepared according to procedures shown in Example 1 or the like. The thus prepared compound was identified by methods such as an NMR analysis. Characteristics of compound (1), the liquid crystal compound, the composition and the device were measured by methods described below.
(252) NMR analysis: For measurement, DRX-500 made by Bruker BioSpin Corporation was used. In .sup.1H-NMR measurement, a sample was dissolved in a deuterated solvent such as CDCl.sub.3, and measurement was carried out under conditions of room temperature, 500 MHz and 16 times of accumulation. Tetramethylsilane was used as an internal standard. In .sup.19F-NMR measurement, CFCl.sub.3 was used as an internal standard, and measurement was carried out under conditions of 24 times of accumulation. In explaining nuclear magnetic resonance spectra obtained, s, d, t, q, quin, sex and m stand for a singlet, a doublet, a triplet, a quartet, a quintet, a sextet and a multiplet, and br being broad, respectively.
(253) Gas chromatographic analysis: For measurement, GC-2010 Gas Chromatograph made by Shimadzu Corporation was used. As a column, a capillary column DB-1 (length 60 m, bore 0.25 mm, film thickness 0.25 μm) made by Agilent Technologies, Inc. was used. As a carrier gas, helium (1 mL/minute) was used. A temperature of a sample vaporizing chamber and a temperature of a detector (FID) part were set to 300° C. and 300° C., respectively. A sample was dissolved in acetone and prepared to be 1% by weight of a solution, and then 1 microliter of the solution obtained was injected into the sample vaporizing chamber. As a recorder, GC Solution System made by Shimadzu Corporation or the like was used.
(254) HPLC analysis: For measurement, Prominence (LC-20AD; SPD-20A) made by Shimadzu Corporation was used. As a column, YMC-Pack ODS-A (length 150 mm, bore 4.6 mm, particle diameter 5 μm) made by YMC Co., Ltd. was used. As an eluate, acetonitrile and water were appropriately mixed and used. As a detector, a UV detector, an RI detector, a CORONA detector or the like was appropriately used. When the UV detector was used, a detection wavelength was set to 254 nanometers. A sample was dissolved in acetonitrile and prepared to be 0.1% by weight of a solution, and then 1 microliter of the solution was introduced into a sample chamber. As a recorder, C-R7Aplus made by Shimadzu Corporation was used.
(255) Ultraviolet-visible spectrophotometry: For measurement, PharmaSpec UV-1700 made by Shimadzu Corporation was used. A detection wavelength was adjusted in the range of 190 nanometers to 700 nanometers. A sample was dissolved in acetonitrile and prepared to be a 0.01 mmol/L solution, and measurement was carried out by putting the solution in a quartz cell (optical path length: 1 cm).
(256) Sample for measurement: Upon measuring phase structure and a transition temperature (a clearing point, a melting point, a polymerization starting temperature or the like), the compound itself was used as a sample.
(257) Measuring method: Measurement of characteristics was carried out by the methods described below. Most of the measuring methods are applied as described in the Standard of the Japan Electronics and Information Technology Industries Association (JEITA) (JEITA ED-2521B) discussed and established by JEITA, or modified thereon. No thin film transistor (TFT) was attached to a TN device used for measurement.
(258) (1) Phase Structure
(259) A sample was placed on a hot plate in a melting point apparatus (FP-52 Hot Stage made by Mettler-Toledo International Inc.) equipped with a polarizing microscope. A state of phase and a change thereof were observed with the polarizing microscope while the sample was heated at a rate of 3° C. per minute, and a kind of the phase was specified.
(260) (2) Transition Temperature (° C.)
(261) For measurement, a differential scanning calorimeter, Diamond DSC System, made by PerkinElmer, Inc., or a high sensitivity differential scanning calorimeter, X-DSC7000, made by SSI NanoTechnology Inc. was used. A sample was heated and then cooled at a rate of 3° C. per minute, and a starting point of an endothermic peak or an exothermic peak caused by a phase change of the sample was determined by extrapolation, whereby a transition temperature was determined. A melting point and a polymerization starting temperature of a compound were also measured using the apparatus. Temperature at which a compound undergoes transition from a solid to a liquid crystal phase such as the smectic phase and the nematic phase may be occasionally abbreviated as “minimum temperature of the liquid crystal phase.” Temperature at which the compound undergoes transition from the liquid crystal phase to liquid may be occasionally abbreviated as “clearing point.”
(262) A crystal was expressed as C. When kinds of the crystals were distinguishable, each of the crystals was expressed as C.sub.1 or C.sub.2. The smectic phase or the nematic phase was expressed as S or N. In the smectic phase, when smectic A phase, smectic B phase, smectic C phase or smectic F phase was distinguishable, the phases were expressed as S.sub.A, S.sub.B, S.sub.C or S.sub.F, respectively. The liquid (isotropic) was expressed as I. A transition temperature was expressed as “C 50.0 N 100.0 I,” for example. The expression indicates that a transition temperature from the crystals to the nematic phase is 50.0° C., and a transition temperature from the nematic phase to the liquid is 100.0° C.
(263) (3) Maximum Temperature of Nematic Phase (T.sub.NI or NI; ° C.)
(264) A sample was placed on a hot plate in a melting point apparatus equipped with a polarizing microscope, and heated at a rate of 1° C. per minute. Temperature when part of the sample began to change from a nematic phase to an isotropic liquid was measured. A maximum temperature of the nematic phase may be occasionally abbreviated as “maximum temperature.” When the sample was a mixture of compound (1) and the base liquid crystal, the maximum temperature was expressed in terms of a symbol T.sub.NI. When the sample was a mixture of compound (1) and a compound such as components B, C and D, the maximum temperature was expressed in terms of a symbol NI.
(265) (4) Minimum Temperature of Nematic Phase (T.sub.C; ° C.)
(266) Samples each having a nematic phase were kept in freezers at temperatures of 0° C., −10° C., −20° C., −30° C. and −40° C. for 10 days, and then liquid crystal phases were observed. For example, when the sample maintained the nematic phase at −20° C. and changed to crystals or a smectic phase at −30° C., T.sub.C was expressed as T.sub.C≤−20° C. A minimum temperature of the nematic phase may be occasionally abbreviated as “minimum temperature.”
(267) (5) Viscosity (Bulk Viscosity; r; Measured at 20° C.; mPa.Math.s)
(268) For measurement, a cone-plate (E type) rotational viscometer made by Tokyo Keiki Inc. was used.
(269) (6) Optical Anisotropy (Refractive Index Anisotropy; Measured at 25° C.; Δn)
(270) Measurement was carried out by an Abbe refractometer with a polarizing plate mounted on an ocular, using light at a wavelength of 589 nanometers. A surface of a main prism was rubbed in one direction, and then a sample was added dropwise onto the main prism. A refractive index (n∥) was measured when a direction of polarized light was parallel to a direction of rubbing. A refractive index (n⊥) was measured when the direction of polarized light was perpendicular to the direction of rubbing. A value of optical anisotropy (Δn) was calculated from an equation: Δn=n∥−n⊥.
(271) (7) Specific Resistance (ρ; Measured at 25° C.; Ω cm)
(272) Into a vessel equipped with electrodes, 1.0 milliliter of a sample was injected. A direct current voltage (10V) was applied to the vessel, and a direct current after 10 seconds was measured. Specific resistance was calculated from the following equation: (specific resistance)={(voltage)× (electric capacity of a vessel)}/{(direct current)× (dielectric constant of vacuum)}.
(273) The measuring method of the characteristics may be different between a sample having positive dielectric anisotropy and a sample having negative dielectric anisotropy. When the dielectric anisotropy was positive, the measuring methods were described in sections (8a) to (12a). When the dielectric anisotropy was negative, the measuring methods were described in sections (8b) to (12b).
(274) (8a) Viscosity (Rotational Viscosity; Yl; Measured at 25° C.; mPa.Math.s)
(275) Positive dielectric anisotropy: Measurement was carried out according to a method described in M. Imai et al., Molecular Crystals and Liquid Crystals, Vol. 259, p. 37 (1995). A sample was put in a TN device in which a twist angle was 0 degrees and a distance (cell gap) between two glass substrates was 5 micrometers. Voltage was applied stepwise to the device in the range of 16 V to 19.5 V at an increment of 0.5 V. After a period of 0.2 second with no voltage application, voltage was repeatedly applied under conditions of only one rectangular wave (rectangular pulse; 0.2 second) and no voltage application (2 seconds). A peak current and a peak time of transient current generated by the applied voltage were measured. A value of rotational viscosity was obtained from the measured values and calculation equation (8) described on page 40 of the paper presented by M. Imai et al. A value of dielectric anisotropy required for the calculation was determined using the device by which the rotational viscosity was measured and by a method described below.
(276) (8b) Viscosity (Rotational Viscosity; Yl; Measured at 25° C.; mPa.Math.s)
(277) Negative dielectric anisotropy: Measurement was carried out according to a method described in M. Imai et al., Molecular Crystals and Liquid Crystals, Vol. 259, p. 37 (1995). A sample was put in a VA device in which a distance (cell gap) between two glass substrates was 20 micrometers. Voltage was applied stepwise to the device in the range of 39 V to 50 V at an increment of 1 V. After a period of 0.2 second with no voltage application, voltage was repeatedly applied under conditions of only one rectangular wave (rectangular pulse; 0.2 second) and no voltage application (2 seconds). A peak current and a peak time of transient current generated by the applied voltage were measured. A value of rotational viscosity was obtained from the measured values and calculation equation (8) described on page 40 of the paper presented by M. Imai et al. In dielectric anisotropy required for the calculation, a value measured according to sections of dielectric anisotropy described below was used.
(278) (9a) Dielectric Anisotropy (as; Measured at 25° C.)
(279) Positive dielectric anisotropy: A sample was put in a TN device in which a distance (cell gap) between two glass substrates was 9 micrometers and a twist angle was 80 degrees. Sine waves (10 V, 1 kHz) were applied to the device, and after 2 seconds, a dielectric constant (ε∥) of liquid crystal molecules in a major axis direction was measured. Sine waves (0.5 V, 1 kHz) were applied to the device, and after 2 seconds, a dielectric constant (ε⊥) of liquid crystal molecules in a minor axis direction was measured. A value of dielectric anisotropy was calculated from an equation: Δε=ε∥−ε⊥.
(280) (9b) Dielectric Anisotropy (Δε; Measured at 25° C.)
(281) Negative dielectric anisotropy: A value of dielectric anisotropy was calculated from an equation: Δε=ε∥−ε⊥. A dielectric constant (ε∥ and ε⊥) was measured as described below.
(282) (1) Measurement of dielectric constant (ε∥): an ethanol (20 mL) solution of octadecyltriethoxysilane (0.16 mL) was applied to a well-cleaned glass substrate. After rotating the glass substrate with a spinner, the glass substrate was heated at 150° C. for 1 hour. A sample was put in a VA device in which a distance (cell gap) between two glass substrates was 4 micrometers, and the device was sealed with an ultraviolet-curable adhesive. Sine waves (0.5 V, 1 kHz) were applied to the device, and after 2 seconds, a dielectric constant (ε∥) of liquid crystal molecules in a major axis direction was measured.
(283) (2) Measurement of dielectric constant (ε⊥): a polyimide solution was applied to a well-cleaned glass substrate. After calcining the glass substrate, rubbing treatment was applied to the alignment film obtained. A sample was put in a TN device in which a distance (cell gap) between two glass substrates was 9 micrometers and a twist angle was 80 degrees. Sine waves (0.5 V, 1 kHz) were applied to the device, and after 2 seconds, a dielectric constant (ε∥) of liquid crystal molecules in a minor axis direction was measured.
(284) (10a) Elastic Constant (K; Measured at 25° C.; pN)
(285) Positive dielectric anisotropy: For measurement, HP4284A LCR Meter made by Yokogawa-Hewlett-Packard Co. was used. A sample was put in a horizontal alignment device in which a distance (cell gap) between two glass substrates was 20 micrometers. An electric charge of 0 V to 20 V was applied to the device, and electrostatic capacity and applied voltage were measured. The measured values of electrostatic capacity (C) and applied voltage (V) were fitted to equation (2.98) and equation (2.101) on page 75 of “Liquid Crystal Device Handbook” (Ekisho Debaisu Handobukku in Japanese; Nikkan Kogyo Shimbun, Ltd.), and values of K.sub.11 and K.sub.33 were obtained from equation (2.99). Next, K.sub.22 was calculated using the previously determined values of K.sub.11 and K.sub.33 in equation (3.18) on page 171. Elastic constant K was expressed in terms of a mean value of the thus determined K.sub.11, K.sub.22 and K.sub.33.
(286) (10b) Elastic Constant (Ku and K.sub.33; Measured at 25° C.; pN)
(287) Negative dielectric anisotropy: For measurement, Elastic Constant Measurement System Model EC-1 made by TOYO Corporation was used. A sample was put in a vertical alignment device in which a distance (cell gap) between two glass substrates was 20 micrometers. An electric charge of 20 V to 0 V was applied to the device, and electrostatic capacity and applied voltage were measured. Values of electrostatic capacity (C) and applied voltage (V) were fitted to equation (2.98) and equation (2.101) on page 75 of “Liquid Crystal Device Handbook” (Ekisho Debaisu Handobukku in Japanese; Nikkan Kogyo Shimbun, Ltd.), and a value of elastic constant was obtained from equation (2.100).
(288) (11a) Threshold Voltage (Vth; Measured at 25° C.; V)
(289) Positive dielectric anisotropy: For measurement, an LCD-5100 luminance meter made by Otsuka Electronics Co., Ltd. was used. A light source was a halogen lamp. A sample was put in a normally white mode TN device in which a distance (cell gap) between two glass substrates was 0.45/Δn (μm) and a twist angle was 80 degrees. A voltage (32 Hz, rectangular waves) to be applied to the device was stepwise increased from 0 V to 10 V at an increment of 0.02 V. On the occasion, the device was irradiated with light from a direction perpendicular to the device, and an amount of light transmitted through the device was measured. A voltage-transmittance curve was prepared, in which the maximum amount of light corresponds to 100% transmittance and the minimum amount of light corresponds to 0% transmittance. A threshold voltage is expressed in terms of voltage at 90% transmittance.
(290) (11b) Threshold Voltage (Vth; Measured at 25° C.; V)
(291) Negative dielectric anisotropy: For measurement, an LCD-5100 luminance meter made by Otsuka Electronics Co., Ltd. was used.
(292) A light source was a halogen lamp. A sample was put in a normally black mode VA device in which a distance (cell gap) between two glass substrates was 4 micrometers and a rubbing direction was anti-parallel, and the device was sealed with an ultraviolet-curable adhesive. A voltage (60 Hz, rectangular waves) to be applied to the device was stepwise increased from 0 V to 20 V at an increment of 0.02 V. On the occasion, the device was irradiated with light from a direction perpendicular to the device, and an amount of light transmitted through the device was measured. A voltage-transmittance curve was prepared, in which the maximum amount of light corresponds to 100% transmittance and the minimum amount of light corresponds to 0% transmittance. A threshold voltage is expressed in terms of voltage at 10% transmittance.
(293) (12a) Response Time (T; Measured at 25° C.; Ms)
(294) Positive dielectric anisotropy: For measurement, an LCD-5100 luminance meter made by Otsuka Electronics Co., Ltd. was used. A light source was a halogen lamp. A low-pass filter was set to 5 kHz. A sample was put in a normally white mode TN device in which a distance (cell gap) between two glass substrates was 5.0 micrometers and a twist angle was 80 degrees. A voltage (rectangular waves; 60 Hz, 5 V, 0.5 second) was applied to the device. On the occasion, the device was irradiated with light from a direction perpendicular to the device, and an amount of light transmitted through the device was measured. The maximum amount of light corresponds to 100% transmittance, and the minimum amount of light corresponds to 0% transmittance. A rise time (τr; millisecond) was expressed in terms of time required for a change from 90% transmittance to 10% transmittance. A fall time (τf; millisecond) was expressed in terms of time required for a change from 10% transmittance to 90% transmittance. A response time was expressed by a sum of the rise time and the fall time thus determined.
(295) (12b) Response Time (τ; Measured at 25° C.; Ms)
(296) Negative dielectric anisotropy: For measurement, an LCD-5100 luminance meter made by Otsuka Electronics Co., Ltd. was used. A light source was a halogen lamp. A low-pass filter was set to 5 kHz. A sample was put in a normally black mode PVA device in which a distance (cell gap) between two glass substrates was 3.2 micrometers, and a rubbing direction was anti-parallel. The device was sealed with an ultraviolet-curable adhesive. A voltage of a little exceeding a threshold voltage was applied to the device for 1 minute, and then the device was irradiated with ultraviolet light of 23.5 mW/cm.sup.2 for 8 minutes, while applying a voltage of 5.6 V. A voltage (rectangular waves; 60 Hz, 10 V, 0.5 second) was applied to the device. On the occasion, the device was irradiated with light from a direction perpendicular to the device, and an amount of light transmitted through the device was measured. The maximum amount of light corresponds to 100% transmittance, and the minimum amount of light corresponds to 0% transmittance. A response time was expressed in terms of time required for a change from 90% transmittance to 10% transmittance (fall time; millisecond).
(297) Raw Material
(298) Solmix (registered trademark) A-11 is a mixture of ethanol (85.5%), methanol (13.4%) and isopropanol (1.1%), and was purchased from Japan Alcohol Trading Co., Ltd.
Synthesis Example 1
Synthesis of Compound (No. 59)
(299) ##STR00085##
First Step
(300) Compound (T-1) (20 g), cyclohexanol (200 mL) and p-toluene sulfonic acid monohydrate (PTSA-H.sub.2O) (0.4 g) were put in a reaction vessel, and the resulting mixture was stirred at 60° C. for 48 hours. The resulting solution was concentrated under reduced pressure, and the residue was purified by silica gel chromatography (toluene: ethyl acetate=2:1 in a volume ratio) to obtain compound (T-2) (32 g; 98%).
(301) Second Step
(302) In a reaction vessel, 4,4′-biphenyldiol (10 g), 4-hydroxybenzoic acid (7.4 g), 4-dimethylaminopyridine (DMAP) (0.34 g), and dichloromethane (200 mL) were put, and the resulting mixture was cooled down to 0° C. Thereto, DCC (11 g) was added, and the resulting mixture was stirred for 12 hours while returning to room temperature. After an insoluble matter was filtered off, the reaction mixture was poured into water, and an aqueous layer was subjected to extraction with ethyl acetate. An organic layer was washed with water, and dried over anhydrous magnesium sulfate. The resulting solution was concentrated under reduced pressure, and the residue was purified by silica gel chromatography (ethyl acetate:toluene=1:1 in a volume ratio) to obtain compound (T-3) (3 g; 40%).
(303) Third Step
(304) Compound (T-3) (1.1 g), compound (T-2) (1.8 g), DMAP (0.26 g) and dichloromethane (100 mL) were put in a reaction vessel, and the resulting mixture was cooled down to 0° C. Thereto, DCC (1.8 g) was added, and the resulting mixture was stirred for 12 hours while returning to room temperature. After an insoluble matter was filtered off, the reaction mixture was poured into water, and an aqueous layer was subjected to extraction with dichloromethane. An organic layer was washed with water, and dried over anhydrous magnesium sulfate. The resulting solution was concentrated under reduced pressure, and the residue was purified by silica gel chromatography (ethyl acetate:toluene=1:5 in a volume ratio) to obtain compound (No. 59) (1.25 g; 50%).
(305) An NMR analysis value of the resulting compound (No. 59) was as described below.
(306) .sup.1H-NMR: chemical shift δ (ppm; CDCl.sub.3): 8.27 (d, 2H), 7.62 (d, 2H), 7.60 (d, 2H), 7.30 (d, 2H), 7.28 (d, 2H), 7.20 (d, 2H), 6.58 (d, 2H), 5.92 (d, 2H), 4.65-4.79 (m, 2H), 3.46 (s, 4H), 1.90-1.80 (m, 4H), 1.75-1.65 (m, 4H), 1.57-1.20 (m, 12H).
(307) Physical properties of compound (No. 59) were as described below.
(308) Transition temperature (° C.): C 137.0 I
Synthesis Example 2
Synthesis of Compound (No. 401)
(309) ##STR00086##
First Step
(310) In a reaction vessel, 4-hydroxybenzaldehyde (10 g), 4-hydroxyacetophenone (11 g), sodium hydroxide (6.5 g), and methanol (200 mL) were put, and the resulting mixture was stirred at 40° C. for 12 hours. The reaction mixture was poured into water, neutralized with hydrochloric acid, and then subjected to extraction with ethyl acetate. An organic layer was washed with water, and dried over anhydrous magnesium sulfate. The solution was concentrated under reduced pressure, and the resulting residue was recrystallized in ethyl acetate to obtain compound (T-4) (5 g; 25%).
(311) Second Step
(312) Compound (T-4) (5 g), compound (T-5) (6 g), DMAP (0.25 g) and dichloromethane (200 mL) were put in a reaction vessel, and the resulting mixture was cooled down to 0° C. Thereto, DCC (8.6 g) was added, and the resulting mixture was stirred for 12 hours while returning to room temperature. After an insoluble matter was filtered off, the reaction mixture was poured into water, and an aqueous layer was subjected to extraction with dichloromethane. An organic layer was washed with water, and dried over anhydrous magnesium sulfate. The resulting solution was concentrated under reduced pressure, and the residue was purified by silica gel chromatography (ethyl acetate:toluene=1:5 in a volume ratio) to obtain compound (No. 401) (7 g; 68%).
(313) An NMR analysis value of the resulting compound (No. 401) was as described below.
(314) .sup.1H-NMR: chemical shift δ (ppm; CDCl.sub.3): 8.07 (d, 2H), 7.80 (d, 1H), 7.68 (d, 2H), 7.48 (d, 1H), 7.28 (d, 2H), 7.21 (d, 2H), 6.60 (d, 2H), 5.94 (d, 2H), 5.74 (s, 6H), 3.49 (s, 2H), 3.48 (s, 2H).
(315) Physical properties of compound (No. 401) were as described below.
(316) Transition temperature (° C.): C 97.8 I
(317) Compounds (No. 1) to (No. 588) described below were prepared according to the synthesis methods described in Synthesis Examples.
(318) TABLE-US-00002 No.
2. Use Examples of Devices
(319) The compounds in Use Examples were represented using symbols according to definitions in Table 3 below. In Table 3, a configuration of 1,4-cyclohexylene is trans. A parenthesized number next to a symbolized compound corresponds to the number of the compound. A symbol (-) means any other liquid crystal compound. A proportion (percentage) of the liquid crystal compound is expressed in terms of weight percent (% by weight) based on the weight of the liquid crystal composition. Values of the characteristics of the composition are summarized in a last part.
(320) TABLE-US-00003 TABLE 3 Method for description of compounds using symbols R—(A.sub.1)—Z.sub.1—. . . —Z.sub.n—(A.sub.n)—R′ 1) Left-terminal group R— Symbol FC.sub.nH.sub.2n— Fn— C.sub.nH.sub.2n+1— n— C.sub.nH.sub.2n+1O— nO— C.sub.mH.sub.2m+1OC.sub.nH.sub.2n— mOn— CH.sub.2═CH— V— C.sub.nH.sub.2n+1—CH═CH— nV— CH.sub.2═CH—C.sub.nH.sub.2n— Vn— C.sub.mH.sub.2m+1—CH═CH—C.sub.nH.sub.2n— mVn— CF.sub.2═CH— VFF— CF.sub.2═CH—C.sub.nH.sub.2n— VFFn— C.sub.mH.sub.2m+1CF.sub.2C.sub.nH.sub.2n— m(CF2)n— CH.sub.2═CHCOO— AC— CH2═C(CH.sub.3)COO— MAC— 2) Right-terminal group —R′ Symbol —C.sub.nH.sub.2n+1 —n —OC.sub.nH.sub.2n+1 —On —COOCH.sub.3 —EMe —CH═CH.sub.2 —V —CH═CH—C.sub.nH.sub.2n+1 —Vn —C.sub.nH.sub.2n—CH═CH.sub.2 —nV —C.sub.mH.sub.2m—CH═CH—C.sub.nH.sub.2n+1 —mVn —CH═CF.sub.2 —VFF —F —F —Cl —CL —OCF.sub.3 —OCF3 —OCF.sub.2H —OCF2H —CF.sub.3 —CF3 —CF═CH—CF.sub.3 —FVCF3 —OCH═CH—CF.sub.3 —OVCF3 —C≡N —C —OCOCH═CH.sub.2 —AC —OCOC(CH.sub.3)═CH.sub.2 —MAC 3) Bonding group —Z.sub.n— Symbol —C.sub.nH.sub.2n— n —COO— E —CH═CH— V —CH.sub.2O— 1O —CH═CHO— VO —OCH═CH— OV —CF═CF— VFF —CH═CF— VF —OCH.sub.2— O1 —OCF.sub.2— x —CF.sub.2O— X —C≡C— T 4) Ring structure —A.sub.n— Symbol
1. Raw Material
(321) A composition to which an alignment control monomer was added was injected into a device having no alignment film. After the device was irradiated with linearly polarized light, alignment of liquid crystal molecules in the device was confirmed. First, a raw material will be described. The raw material was appropriately selected from compositions such as compositions (M1) to (M41), and alignment controls monomer such as compounds (No. 1) to (No. 588). The composition is as described below.
(322) TABLE-US-00004 3-HB (2F, 3F)-O2 (9-1) 10% 5-HB (2F, 3F)-O2 (9-1) 7% 2-BB (2F, 3F)-O2 (9-3) 7% 3-BB (2F, 3F)-O2 (9-3) 7% 3-B (2F, 3F) B (2F, 3F)-O2 (9-7) 3% 2-HHB (2F, 3F)-O2 (10-1) 5% 3-HHB (2F, 3F)-O2 (10-1) 10% 2-HBB (2F, 3F)-O2 (10-7) 8% 3-HBB (2F, 3F)-O2 (10-7) 10% 2-HH-3 (2-1) 14% 3-HB-O1 (2-5) 5% 3-HHB-1 (3-1) 3% 3-HHB-O1 (3-1) 3% 3-HHB-3 (3-1) 4% 2-BB (F) B-3 (3-6) 4%
(323) NI=73.2° C.; Tc<−20° C.; Δn=0.113; Δε=−4.0; Vth=2.18 V; η=22.6 mPa.Math.s.
(324) Composition (M2)
(325) TABLE-US-00005 3-HB (2F, 3F)-O4 (9-1) 6% 3-H2B (2F, 3F)-O2 (9-4) 8% 3-H1OB (2F, 3F)-O2 (9-5) 4% 3-BB (2F, 3F)-O2 (9-3) 7% 2-HHB (2F, 3F)-O2 (10-1) 7% 3-HHB (2F, 3F)-O2 (10-1) 7% 3-HH2B (2F, 3F)-O2 (10-4) 7% 5-HH2B (2F, 3F)-O2 (10-4) 4% 2-HBB (2F, 3F)-O2 (10-7) 5% 3-HBB (2F, 3F)-O2 (10-7) 5% 4-HBB (2F, 3F)-O2 (10-7) 6% 2-HH-3 (2-1) 12% 1-BB-5 (2-8) 12% 3-HHB-1 (3-1) 4% 3-HHB-O1 (3-1) 3% 3-HBB-2 (3-4) 3%
(326) NI=82.8° C.; Tc<−30° C.; Δn=0.118; Δε=−4.4; Vth=2.13 V; η=22.5 mPa.Math.s.
(327) Composition (M3)
(328) TABLE-US-00006 3-HB (2F, 3F)-O2 (9-1) 7% 5-HB (2F, 3F)-O2 (9-1) 7% 3-BB (2F, 3F)-O2 (9-3) 8% 3-HHB (2F, 3F)-O2 (10-1) 5% 5-HHB (2F, 3F)-O2 (10-1) 4% 3-HH1OB (2F, 3F)-O2 (10-5) 4% 2-BB (2F, 3F) B-3 (11-1) 5% 2-HBB (2F, 3F)-O2 (10-7) 3% 3-HBB (2F, 3F)-O2 (10-7) 8% 4-HBB (2F, 3F)-O2 (10-7) 5% 5-HBB (2F, 3F)-O2 (10-7) 8% 3-HH-V (2-1) 27% 3-HH-V1 (2-1) 6% V-HHB-1 (3-1) 3%
(329) NI=78.1° C.; Tc<−30° C.; Δn=0.107; Δε=−3.2; Vth=2.02 V; η=15.9 mPa.Math.s.
(330) Composition (M4)
(331) TABLE-US-00007 3-HB (2F, 3F)-O2 (9-1) 10% 5-HB (2F, 3F)-O2 (9-1) 10% 3-H2B (2F, 3F)-O2 (9-4) 8% 5-H2B (2F, 3F)-O2 (9-4) 8% 2-HBB (2F, 3F)-O2 (10-7) 6% 3-HBB (2F, 3F)-O2 (10-7) 8% 4-HBB (2F, 3F)-O2 (10-7) 7% 5-HBB (2F, 3F)-O2 (10-7) 7% 3-HDhB (2F, 3F)-O2 (10-3) 5% 3-HH-4 (2-1) 14% V-HHB-1 (3-1) 10% 3-HBB-2 (3-4) 7%
(332) NI=88.5° C.; Tc<−30° C.; Δn=0.108; Δε=−3.8; Vth=2.25 V; η=24.6 mPa.Math.s; VHR-1=99.1%; VHR-2=98.2%: VHR-3=97.8%.
(333) Composition (M5)
(334) TABLE-US-00008 3-HB (2F, 3F)-O2 (9-1) 7% 3-HB (2F, 3F)-O4 (9-1) 8% 3-H2B (2F, 3F)-O2 (9-4) 8% 3-BB (2F, 3F)-O2 (9-3) 10% 2-HHB (2F, 3F)-O2 (10-1) 4% 3-HHB (2F, 3F)-O2 (10-1) 7% 3-HHB (2F, 3F)-1 (10-1) 6% 2-HBB (2F, 3F)-O2 (10-7) 6% 3-HBB (2F, 3F)-O2 (10-7) 6% 4-HBB (2F, 3F)-O2 (10-7) 5% 5-HBB (2F, 3F)-O2 (10-7) 4% 3-HEB (2F, 3F) B (2F, 3F)-O2 (16-1) 3% 3-H1OCro (7F, 8F)-5 (13-2) 3% 3-HDhB (2F, 3F)-O2 (10-3) 5% 3-HH-O1 (2-1) 5% 1-BB-5 (2-8) 4% V-HHB-1 (3-1) 4% 5-HB (F) BH-3 (4-2) 5%
(335) NI=81.1° C.; Tc<−30° C.; Δn=0.119; Δε=−4.5; Vth=1.69 V; η=31.4 mPa.Math.s.
(336) Composition (M6)
(337) TABLE-US-00009 3-HB (2F, 3F)-O4 (9-1) 15% 3-HBB (2F, 3F)-O2 (10-7) 8% 4-HBB (2F, 3F)-O2 (10-7) 5% 5-HBB (2F, 3F)-O2 (10-7) 7% 3-dhBB (2F, 3F)-O2 (10-9) 5% 3-chB (2F, 3F)-O2 (16-2) 7% 2-HchB (2F, 3F)-O2 (16-3) 8% 5-HH-V (2-1) 18% 7-HB-1 (2-5) 5% V-HHB-1 (3-1) 7% V2-HHB-1 (3-1) 7% 3-HBB (F) B-3 (4-5) 8%
(338) NI=98.8° C.; Tc<−30° C.; Δn=0.111; Δε=−3.2; Vth=2.47 V; η=23.9 mPa.Math.s.
(339) Composition (M7)
(340) TABLE-US-00010 3-H2B (2F, 3F)-O2 (9-4) 18% 5-H2B (2F, 3F)-O2 (9-4) 17% 3-HHB (2F, 3Cl)-O2 (10-12) 5% 3-HBB (2F, 3Cl)-O2 (10-13) 8% 5-HBB (2F, 3Cl)-O2 (10-13) 7% 3-HDhB (2F, 3F)-O2 (10-3) 5% 3-HH-V (2-1) 11% 3-HH-VFF (2-1) 7% F3-HH-V (2-1) 10% 3-HHEH-3 (3-13) 4% 3-HB (F) HH-2 (4-7) 4% 3-HHEBH-3 (4-6) 4%
(341) NI=77.5° C.; Tc<−30° C.; Δn=0.084; Δε=−2.6; Vth=2.43 V; η=22.8 mPa.Math.s.
(342) Composition (M8)
(343) TABLE-US-00011 3-HB (2F, 3F)-O2 (9-1) 8% 3-H2B (2F, 3F)-O2 (9-4) 10% 3-BB (2F, 3F)-O2 (9-3) 10% 2O-BB (2F, 3F)-O2 (9-3) 3% 2-HHB (2F, 3F)-O2 (10-1) 4% 3-HHB (2F, 3F)-O2 (10-1) 7% 2-HHB (2F, 3F)-1 (10-1) 5% 2-BB (2F, 3F) B-3 (11-1) 6% 2-BB (2F, 3F) B-4 (11-1) 6% 2-HBB (2F, 3F)-O2 (10-7) 4% 3-HBB (2F, 3F)-O2 (10-7) 7% 3-HH1OCro (7F, 8F)-5 (13-6) 4% 3-HDhB (2F, 3F)-O2 (10-3) 6% 3-dhBB (2F, 3F)-O2 (10-9) 4% 3-HH-V (2-1) 11% 1-BB-5 (2-8) 5%
(344) NI=70.6° C.; Tc<−20° C.; Δn=0.129; Δε=−4.3; Vth=1.69 V; η=27.0 mPa.Math.s.
(345) Composition (M9)
(346) TABLE-US-00012 3-HB (2F, 3F)-O4 (9-1) 14% 3-H1OB (2F, 3F)-O2 (9-5) 3% 3-BB (2F, 3F)-O2 (9-3) 10% 2-HHB (2F, 3F)-O2 (10-1) 7% 3-HHB (2F, 3F)-O2 (10-1) 7% 3-HH1OB (2F, 3F)-O2 (10-5) 6% 2-HBB (2F, 3F)-O2 (10-7) 4% 3-HBB (2F, 3F)-O2 (10-7) 6% 4-HBB (2F, 3F)-O2 (10-7) 4% 3-HH-V (2-1) 14% 1-BB-3 (2-8) 3% 3-HHB-1 (3-1) 4% 3-HHB-O1 (3-1) 4% V-HBB-2 (3-4) 4% 1-BB (F) B-2V (3-6) 6% 5-HBBH-1O1 (4-1) 4%
(347) NI=93.0° C.; Tc<−30° C.; Δn=0.123; Δε=−4.0; Vth=2.27 V; η=29.6 mPa.Math.s.
(348) Composition (M10)
(349) TABLE-US-00013 3-HB (2F, 3F)-O4 (9-1) 6% 3-H2B (2F, 3F)-O2 (9-4) 8% 3-H1OB (2F, 3F)-O2 (9-5) 5% 3-BB (2F, 3F)-O2 (9-3) 10% 2-HHB (2F, 3F)-O2 (10-1) 7% 3-HHB (2F, 3F)-O2 (10-1) 7% 5-HHB (2F, 3F)-O2 (10-1) 7% 2-HBB (2F, 3F)-O2 (10-7) 4% 3-HBB (2F, 3F)-O2 (10-7) 7% 5-HBB (2F, 3F)-O2 (10-7) 6% 3-HH-V (2-1) 11% 1-BB-3 (2-8) 6% 3-HHB-1 (3-1) 4% 3-HHB-O1 (3-1) 4% 3-HBB-2 (3-4) 4% 3-B (F) BB-2 (3-8) 4%
(350) NI=87.6° C.; Tc<−30° C.; Δn=0.126; Δε=−4.5; Vth=2.21 V; η=25.3 mPa.Math.s.
(351) Composition (M11)
(352) TABLE-US-00014 3-HB (2F, 3F)-O4 (9-1) 6% 3-H2B (2F, 3F)-O2 (9-4) 8% 3-H1OB (2F, 3F)-O2 (9-5) 4% 3-BB (2F, 3F)-O2 (9-3) 7% 2-HHB (2F, 3F)-O2 (10-1) 6% 3-HHB (2F, 3F)-O2 (10-1) 10% 5-HHB (2F, 3F)-O2 (10-1) 8% 2-HBB (2F, 3F)-O2 (10-7) 5% 3-HBB (2F, 3F)-O2 (10-7) 7% 5-HBB (2F, 3F)-O2 (10-7) 5% 2-HH-3 (2-1) 12% 1-BB-3 (2-8) 6% 3-HHB-1 (3-1) 3% 3-HHB-O1 (3-1) 4% 3-HBB-2 (3-4) 6% 3-B (F) BB-2 (3-8) 3%
(353) NI=93.0° C.; Tc<−20° C.; Δn=0.124; Δε=−4.5; Vth=2.22 V; η=25.0 mPa.Math.s.
(354) Composition (M12)
(355) TABLE-US-00015 3-HB (2F, 3F)-O2 (9-1) 7% 5-HB (2F, 3F)-O2 (9-1) 7% 3-BB (2F, 3F)-O2 (9-3) 8% 3-HHB (2F, 3F)-O2 (10-1) 4% 5-HHB (2F, 3F)-O2 (10-1) 5% 3-HH1OB (2F, 3F)-O2 (10-5) 5% 2-BB (2F, 3F) B-3 (11-1) 4% 2-HBB (2F, 3F)-O2 (10-7) 3% 3-HBB (2F, 3F)-O2 (10-7) 8% 4-HBB (2F, 3F)-O2 (10-7) 5% 5-HBB (2F, 3F)-O2 (10-7) 8% 3-HH-V (2-1) 33% V-HHB-1 (3-1) 3%
(356) NI=76.4° C.; Tc<−30° C.; Δn=0.104; Δε=−3.2; Vth=2.06 V; η=15.6 mPa.Math.s.
(357) Composition (M13)
(358) TABLE-US-00016 2-H1OB (2F, 3F)-O2 (9-5) 6% 3-H1OB (2F, 3F)-O2 (9-5) 4% 3-BB (2F, 3F)-O2 (9-3) 3% 2-HH1OB (2F, 3F)-O2 (10-5) 14% 2-HBB (2F, 3F)-O2 (10-7) 7% 3-HBB (2F, 3F)-O2 (10-7) 11% 5-HBB (2F, 3F)-O2 (10-7) 9% 2-HH-3 (2-1) 5% 3-HH-VFF (2-1) 30% 1-BB-3 (2-8) 5% 3-HHB-1 (3-1) 3% 3-HBB-2 (3-4) 3%
(359) NI=78.3° C.; Tc<−20° C.; Δn=0.103; Δε=−3.2; Vth=2.17 V; η=17.7 mPa.Math.s.
(360) Composition (M14)
(361) TABLE-US-00017 3-HB(2F, 3F)—O2 (9-1) 5% 5-HB(2F, 3F)—O2 (9-1) 7% 3-BB(2F, 3F)—O2 (9-3) 8% 3-HHB(2F, 3F)—O2 (10-1) 5% 5-HHB(2F, 3F)—O2 (10-1) 4% 3-HH1OB(2F, 3F)—O2 (10-5) 5% 2-BB(2F, 3F)B-3 (11-1) 4% 2-HBB(2F, 3F)—O2 (10-7) 3% 3-HBB(2F, 3F)—O2 (10-7) 9% 4-HBB(2F, 3F)—O2 (10-7) 4% 5-HBB(2F, 3F)—O2 (10-7) 8% 3-HH—V (2-1) 27% 3-HH—V1 (2-1) 6% V—HHB-1 (3-1) 5%
(362) NI=81.2° C.; Tc<−20° C.; Δn=0.107; Δε=−3.2; Vth=2.11 V; η=15.5 mPa.Math.s.
(363) Composition (M15)
(364) TABLE-US-00018 3-H2B(2F, 3F)—O2 (9-4) 7% 3-HHB(2F, 3F)—O2 (10-1) 8% 3-HH1OB(2F, 3F)—O2 (10-5) 5% 2-BB(2F, 3F)B-3 (11-1) 7% 2-BB(2F, 3F)B-4 (11-1) 7% 3-HDhB(2F, 3F)—O2 (10-3) 3% 5-HDhB(2F, 3F)—O2 (10-3) 4% 2-HchB(2F, 3F)—O2 (16-3) 8% 4-HH—V (2-1) 15% 3-HH—V1 (2-1) 6% 1-HH—2V1 (2-1) 6% 3-HH—2V1 (2-1) 4% V2—BB-1 (2-8) 5% 1V2—BB-1 (2-8) 5% 3-HHB-1 (3-1) 6% 3-HB(F)BH-3 (4-2) 4%
(365) NI=88.7° C.; Tc<−30° C.; Δn=0.115; Δε=−1.9; Vth=2.82 V; η=17.3 mPa.Math.s.
(366) Composition (M16)
(367) TABLE-US-00019 V2—H2B(2F, 3F)—O2 (9-4) 8% V2—H1OB(2F, 3F)—O4 (9-5) 4% 3-BB(2F, 3F)—O2 (9-3) 7% 2-HHB(2F, 3F)—O2 (10-1) 7% 3-HHB(2F, 3F)—O2 (10-1) 7% 3-HH2B(2F, 3F)—O2 (10-4) 7% 5-HH2B(2F, 3F)—O2 (10-4) 4% V—HH2B(2F, 3F)—O2 (10-4) 6% V2—HBB(2F, 3F)—O2 (10-7) 5% V—HBB(2F, 3F)—O2 (10-7) 5% V—HBB(2F, 3F)—O4 (10-7) 6% 2-HH-3 (2-1) 12% 1-BB-5 (2-8) 12% 3-HHB-1 (3-1) 4% 3-HHB—O1 (3-1) 3% 3-HBB-2 (3-4) 3%
(368) NI=89.9° C.; Tc<−20° C.; Δn=0.122; Δε=−4.2; Vth=2.16 V; η=23.4 mPa.Math.s.
(369) Composition (M17)
(370) TABLE-US-00020 3-HB(2F, 3F)—O2 (9-1) 3% V—HB(2F, 3F)—O2 (9-1) 3% V2—HB(2F, 3F)—O2 (9-1) 5% 5-H2B(2F, 3F)—O2 (9-4) 5% V2—BB(2F, 3F)—O2 (9-3) 3% 1V2—BB(2F, 3F)—O2 (9-3) 3% 3-HHB(2F, 3F)—O2 (10-1) 6% V—HHB(2F, 3F)—O2 (10-1) 6% V—HB(2F, 3F)—O4 (10-1) 5% V2—HHB(2F, 3F)—O2 (10-1) 4% V2—BB(2F, 3F)B-1 (11-1) 4% V2—HBB(2F, 3F)—O2 (10-7) 5% V—HBB(2F, 3F)—O2 (10-7) 4% V—HBB(2F, 3F)—O4 (10-7) 5% V—HHB(2F, 3Cl)—O2 (10-12) 3% 3-HH—V (2-1) 27% 3-HH—V1 (2-1) 6% V—HHB-1 (3-1) 3%
NI=77.1° C.; Tc<−20° C.; Δn=0.101; Δε=−3.0; Vth=2.04 V; η=13.9 mPa.Math.s.
Composition (M18)
(371) TABLE-US-00021 V—HB(2F, 3F)—O2 (9-1) 10% V2—HB(2F, 3F)—O2 (9-1) 10% 2-H1OB(2F, 3F)—O2 (9-5) 3% 3-H1OB(2F, 3F)—O2 (9-5) 3% 2O—BB(2F, 3F)—O2 (9-3) 3% V2—BB(2F, 3F)—O2 (9-3) 8% V2—HHB(2F, 3F)—O2 (10-1) 5% 2-HBB(2F, 3F)—O2 (10-7) 3% 3-HBB(2F, 3F)—O2 (10-7) 3% V—HBB(2F, 3F)—O2 (10-7) 6% V—HBB(2F, 3F)—O4 (10-7) 8% V—HHB(2F, 3Cl)—O2 (10-12) 7% 3-HH-4 (2-1) 14% V—HHB-1 (3-1) 10% 3-HBB-2 (3-4) 7%
(372) NI=75.9° C.; Tc<−20° C.; Δn=0.114; Δε=−3.9; Vth=2.20 V; η=24.7 mPa.Math.s.
(373) Composition (M19)
(374) TABLE-US-00022 2-H1OB(2F, 3F)—O2 (9-5) 7% 3-H1OB(2F, 3F)—O2 (9-5) 11% 3-HH1OB(2F, 3F)—O2 (10-5) 8% 2-HBB(2F, 3F)—O2 (10-7) 3% 3-HBB(2F, 3F)—O2 (10-7) 9% 5-HBB(2F, 3F)—O2 (10-7) 7% V—HBB(2F, 3F)—O2 (10-7) 8% 3-HDhB(2F, 3F)—O2 (10-3) 3.5% 2-HH-3 (2-1) 21% 3-HH-4 (2-1) 5% 3-HB—O2 (2-5) 2.5% 1-BB-3 (2-8) 4% 3-HHB-1 (3-1) 1.5% 3-HBB-2 (3-4) 9.5%
(375) NI=80.8° C.; Tc<−20° C.; Δn=0.108; Δε=−3.8; Vth=2.02 V; η=19.8 mPa.Math.s.
(376) Composition (M20)
(377) TABLE-US-00023 2-H1OB(2F, 3F)—O2 (9-5) 5.5% 2-BB(2F, 3F)—O2 (9-3) 11% 2-HH1OB(2F, 3F)—O2 (10-5) 13% 3-HH1OB(2F, 3F)—O2 (10-5) 15.5% 3-HBB(2F, 3F)—O2 (10-7) 9% 2-HH-3 (2-1) 25% 3-HH-4 (2-1) 3% 3-HBB-2 (3-4) 14% 5-B(F)BB-2 (3-8) 4%
(378) NI=85.3° C.; Tc<−20° C.; Δn=0.109; Δε=−3.6; Vth=2.06 V; η=20.9 mPa.Math.s.
(379) Composition (M21)
(380) TABLE-US-00024 V—HB(2F, 3F)—O2 (9-1) 7% V—2BB(2F, 3F)—O2 (9-3) 10% V—HHB(2F, 3F)—O1 (10-1) 7% V—HHB(2F, 3F)—O2 (10-1) 9% V—2HHB(2F, 3F)—O2 (10-1) 8% 3-HH2B(2F, 3F)—O2 (10-4) 9% V—HBB(2F, 3F)—O2 (10-7) 7% V—HBB(2F, 3F)—O4 (10-7) 7% 2-HH-3 (2-1) 9% 3-HH-4 (2-1) 3% 3-HH—V (2-1) 15% 3-HH—V1 (2-1) 6% 1V2—HH-3 (2-1) 3%
(381) NI=87.5° C.; Tc<−20° C.; Δn=0.100; Δε=−3.4; Vth=2.25 V; η=16.6 mPa.Math.s.
(382) Composition (M22)
(383) TABLE-US-00025 3-HHXB(F, F)—F (6-100) 6% 3-BB(F, F)XB(F, F)—F (6-97) 13% 3-HHBB(F, F)—F (7-6) 4% 4-HHBB(F, F)—F (7-6) 5% 3-HBBXB(F, F)—F (7-32) 3% 3-BB(F)B(F, F)XB(F)—F (7-46) 2% 4-BB(F)B(F, F)XB(F, F)—F (7-47) 8% 5-BB(F)B(F, F)XB(F, F)—F (7-47) 7% 3-HH—V (2-1) 44% V—HHB-1 (3-1) 6% 2-BB(F)B-3 (3-6) 2%
(384) NI=79.8° C.; Tc<−30° C.; Δn=0.106; Δε=8.5; Vth=1.45 V; η=11.6 mPa.Math.s; γ1=60.0 mPa.Math.s.
(385) Composition (M23)
(386) TABLE-US-00026 5-HXB(F, F)—F (5-13) 3% 3-HHXB(F, F)—F (6-100) 3% 3-HHXB(F, F)—CF3 (6-100) 3% 3-HGB(F, F)—F (6-103) 3% 3-HB(F)B(F, F)—F (6-50) 5% 3-BB(F, F)XB(F, F)—F (6-97) 6% 3-HHBB(F, F)—F (7-6) 6% 5-BB(F)B(F, F)XB(F)B(F, F)—F (−) 2% 3-BB(2F, 3F)XB(F, F)—F (6-114) 4% 3-B(2F, 3F)BXB(F, F)—F (6-115) 5% 3-HHB(F, F)XB(F, F)—F (7-29) 4% 3-HB—CL (5-2) 3% 3-HHB—OCF3 (6-1) 3% 3-HH—V (2-1) 22% 3-HH—V1 (2-1) 10% 5-HB—O2 (2-5) 5% 3-HHEH-3 (3-13) 3% 3-HBB-2 (3-4) 7% 5-B(F)BB-3 (3-8) 3%
(387) NI=71.2° C.; Tc<−20° C.; Δn=0.099; Δε=6.1; Vth=1.74 V; η=13.2 mPa.Math.s; γ1=59.3 mPa.Math.s.
(388) Composition (M24)
(389) TABLE-US-00027 5-HXB(F, F)—F (5-13) 6% 3-HHXB(F, F)—F (6-100) 6% V—HB(F)B(F, F)—F (6-50) 5% 3-HHB(F)B(F, F)—F (7-9) 7% 2-BB(F)B(F, F)XB(F)—F (7-47) 3% 3-BB(F)B(F, F)XB(F)—F (7-47) 3% 4-BB(F)B(F, F)XB(F)—F (7-47) 4% 5-HB—CL (5-2) 5% 2-HH-5 (2-1) 8% 3-HH—V (2-1) 10% 3-HH—V1 (2-1) 7% 4-HH—V (2-1) 10% 4-HH—V1 (2-1) 8% 5-HB—O2 (2-5) 7% 4-HHEH-3 (3-13) 3% 1-BB(F)B—2V (3-6) 3% 1O1—HBBH-3 (4-1) 5%
(390) NI=78.5° C.; Tc<−20° C.; Δn=0.095; Δε=3.4; Vth=1.50 V; η=8.4 mPa.Math.s; γ1=54.2 mPa.Math.s.
(391) Composition (M25)
(392) TABLE-US-00028 3-HHEB(F, F)—F (6-12) 5% 3-HHXB(F, F)—F (6-100) 7% 5-HBEB(F, F)—F (6-39) 5% 3-BB(F, F)XB(F, F)—F (6-97) 10% 2-HHB(F)B(F, F)—F (7-9) 3% 3-HB(2F, 3F)BXB(F, F)—F (7-58) 3% 3-BB(2F, 3F)BXB(F, F)—F (7-59) 2% 5-HHB(F, F)XB(F, F)—F (7-28) 6% 2-HH-3 (2-1) 8% 3-HH—V (2-1) 20% 3-HH—V1 (2-1) 7% 4-HH—V (2-1) 6% 5-HB—O2 (2-5) 5% V2—B2BB-1 (3) 3% 3-HHEBH-3 (4-6) 5% 3-HHEBH-5 (4-6) 5%
(393) NI=90.3° C.; Tc<−20° C.; Δn=0.089; Δε=5.5; Vth=1.65 V; η=13.6 mPa.Math.s; γ1=60.1 mPa.Math.s.
(394) Composition (M26)
(395) TABLE-US-00029 3-BB(F, F)XB(F, F)—F (6-97) 12% 3-HHBB(F, F)—F (7-6) 5% 4-HHBB(F, F)—F (7-6) 4% 3-HBBXB(F, F)—F (7-32) 3% 3-BB(F)B(F, F)XB(F)—F (7-46) 3% 3-BB(F)B(F, F)XB(F, F)—F (7-47) 3% 4-BB(F)B(F, F)XB(F, F)—F (7-47) 5% 5-BB(F)B(F, F)XB(F, F)—F (7-47) 4% 2-HH-3 (2-1) 6% 3-HH-5 (2-1) 6% 3-HH—V (2-1) 25% 3-HH—VFF (2-1) 6% 5-HB—O2 (2-5) 7% V—HHB-1 (3-1) 6% V—HBB-2 (3-4) 5%
(396) NI=78.3° C.; Tc<−20° C.; Δn=0.107; Δε=7.0; Vth=1.55 V; η=11.6 mPa.Math.s; γ1=55.6 mPa.Math.s.
(397) Composition (M27)
(398) TABLE-US-00030 3-HHXB(F, F)—F (6-100) 3% 3-BBXB(F, F)—F (6-91) 3% 3-BB(F, F)XB(F, F)—F (6-97) 8% 3-HHBB(F, F)—F (7-6) 5% 4-HHBB(F, F)—F (7-6) 4% 3-BB(F)B(F, F)XB(F, F)—F (7-47) 3% 4-BB(F)B(F, F)XB(F, F)—F (7-47) 6% 5-BB(F)B(F, F)XB(F, F)—F (7-47) 5% 3-HH—V (2-1) 30% 3-HH—V1 (2-1) 5% 3-HHB—O1 (3-1) 2% V—HHB-1 (3-1) 5% 2-BB(F)B-3 (3-6) 6% F3-HH—V (2-1) 15%
(399) NI=80.4° C.; Tc<−20° C.; Δn=0.106; Δε=5.8; Vth=1.40 V; η=11.6 mPa.Math.s; γ1=61.0 mPa.Math.s.
(400) Composition (M28)
(401) TABLE-US-00031 3-HGB(F, F)—F (6-103) 3% 5-GHB(F, F)—F (6-109) 4% 3-GB(F, F)XB(F, F)—F (6-113) 5% 3-BB(F)B(F, F)—CF3 (6-69) 2% 3-HHBB(F, F)—F (7-6) 4% 3-GBB(F)B(F, F)—F (7-55) 2% 2-dhBB(F, F)XB(F, F)—F (7-50) 4% 3-GB(F)B(F, F)XB(F, F)—F (7-57) 3% 3-HGB(F, F)XB(F, F)—F (−) 5% 7-HB(F, F)—F (5-4) 3% 2-HH-3 (2-1) 14% 2-HH-5 (2-1) 4% 3-HH—V (2-1) 26% 1V2—HH-3 (2-1) 5% 1V2—BB-1 (2-8) 3% 2-BB(F)B-3 (3-6) 3% 3-HB(F)HH-2 (4-7) 4% 5-HBB(F)B-2 (4-5) 6%
(402) NI=78.4° C.; Tc<−20° C.; Δn=0.094; Δε=5.6; Vth=1.45 V; η=11.5 mPa.Math.s; γ1=61.7 mPa.Math.s.
(403) Composition (M29)
(404) TABLE-US-00032 3-HBB(F, F)-F (6-24) 5% 5-HBB(F, F)-F (6-24) 4% 3-BB(F)B(F, F)-F (6-69) 3% 3-BB(F)B(F, F)XB(F, F)-F (7-47) 3% 4-BB(F)B(F, F)XB(F, F)-F (7-47) 5% 3-BB(F, F)XB(F)B(F, F)-F (7-60) 3% 5-BB(F)B(F, F)XB(F)B(F, F)-F (—) 4% 3-HH2BB(F, F)-F (7-15) 3% 4-HH2BB(F, F)-F (7-15) 3% 2-HH-5 (2-1) 8% 3-HH-V (2-1) 25% 3-HH-V1 (2-1) 7% 4-HH-V1 (2-1) 6% 5-HB-O2 (2-5) 5% 7-HB-1 (2-5) 5% VFF-HHB-O1 (3-1) 8% VFF-HHB-1 (3-1) 3%
(405) NI=80.0° C.; Tc<−20° C.; Δn=0.101; Δε=4.6; Vth=1.71 V; η=11.0 mPa.Math.s; γ1=47.2 mPa.Math.s.
(406) Composition (M30)
(407) TABLE-US-00033 3-HHB(F, F)-F (6-3) 8% 3-GB(F)B(F)-F (6-116) 2% 3-GB(F)B(F, F)-F (6-117) 3% 3-BB(F, F)XB(F, F)-F (6-97) 8% 3-GB(F)B(F, F)XB(F, F)-F (7-57) 6% 5-GB(F)B(F, F)XB(F, F)-F (7-57) 5% 3-HH-V (2-1) 30% 3-HH-V1 (2-1) 10% 1V2-HH-3 (2-1) 8% 3-HH-VFF (2-1) 8% V2-BB-1 (2-8) 2% 5-HB(F)BH-3 (4-2) 5% 5-HBBH-3 (4-1) 5%
(408) NI=78.6° C.; Tc<−20° C.; Δn=0.088; Δε=5.6; Vth=1.85 V; η=13.9 mPa.Math.s; γ1=66.9 mPa.Math.s.
(409) Composition (M31)
(410) TABLE-US-00034 3-HHEB(F, F)-F (6-12) 4% 5-HHEB(F, F)-F (6-12) 3% 3-HBEB(F, F)-F (6-39) 3% 5-HBEB(F, F)-F (6-39) 3% 3-BB(F)B(F, F)-F (6-69) 3% 3-GB(F)B(F, F)XB(F, F)-F (7-57) 5% 4-GB(F)B(F, F)XB(F, F)-F (7-57) 5% 5-HB-CL (2-5) 5% 3-HHB-OCF3 (3-1) 4% 3-HHB(F, F)XB(F, F)-F (7-29) 5% 5-HHB(F, F)XB(F, F)-F (7-29) 3% 3-HGB(F, F)XB(F, F)-F (—) 5% 2-HH-5 (2-1) 3% 3-HH-5 (2-1) 5% 3-HH-V (2-1) 24% 4-HH-V (2-1) 5% 1V2-HH-3 (2-1) 5% 3-HHEH-3 (3-13) 5% 5-B(F)BB-2 (3-8) 3% 5-B(F)BB-3 (3-8) 2%
(411) NI=82.9° C.; Tc<−20° C.; Δn=0.093; Δε=6.9; Vth=1.50 V; η=16.3 mPa.Math.s; γ1=65.2 mPa.Math.s.
(412) Composition (M32)
(413) TABLE-US-00035 3-HHXB(F, F)-F (6-100) 9% 3-HBB(F, F)-F (6-24) 3% 3-BB(F)B(F, F)-F (6-69) 4% 3-BB(F)B(F, F)-CF3 (6-69) 4% 3-BB(F, F)XB(F, F)-F (6-97) 5% 3-GBB(F)B(F, F)-F (7-55) 3% 4-GBB(F)B(F, F)-F (7-55) 4% 3-HH-V (2-1) 25% 3-HH-V1 (2-1) 10% 5-HB-O2 (2-5) 10% 7-HB-1 (2-5) 5% V2-BB-1 (2-8) 3% 3-HHB-1 (3-1) 4% 1V-HBB-2 (3-4) 5% 5-HBB(F)B-2 (4-5) 6%
(414) NI=79.6° C.; Tc<−20° C.; Δn=0.111; Δε=4.7; Vth=1.86 V; η=9.7 mPa.Math.s; γ1=49.9 mPa.Math.s.
(415) Composition (M33)
(416) TABLE-US-00036 3-BB(F, F)XB(F, F)-F (6-97) 14% 5-BB(F)B(F, F)XB(F, F)-F (7-47) 7% 7-HB(F, F)-F (5-4) 6% 2-HH-5 (2-1) 5% 3-HH-V (2-1) 30% 3-HH-V1 (2-1) 3% 3-HH-VFF (2-1) 10% 3-HHB-1 (3-1) 4% 3-HHB-3 (3-1) 5% 3-HHB-O1 (3-1) 3% 1-BB(F)B-2V (3-6) 3% 3-HHEBH-3 (4-6) 3% 3-HHEBH-4 (4-6) 4% 3-HHEBH-5 (4-6) 3%
(417) NI=83.0° C.; Tc<−20° C.; Δn=0.086; Δε=3.8; Vth=1.94 V; η=7.5 mPa.Math.s; γ1=51.5 mPa.Math.s.
(418) Composition (M34)
(419) TABLE-US-00037 3-HBB(F, F)-F (6-24) 5% 5-HBB(F, F)-F (6-24) 4% 3-BB(F)B(F, F)-F (6-69) 3% 3-BB(F)B(F, F)XB(F, F)-F (7-47) 3% 4-BB(F)B(F, F)XB(F, F)-F (7-47) 5% 3-BB(F, F)XB(F)B(F, F)-F (7-60) 3% 5-BB(F)B(F, F)XB(F)B(F, F)-F (—) 4% 3-HH2BB(F, F)-F (7-15) 3% 4-HH2BB(F, F)-F (7-15) 3% 2-HH-5 (2-1) 8% 3-HH-V (2-1) 28% 4-HH-V1 (2-1) 7% 5-HB-O2 (2-5) 2% 7-HB-1 (2-5) 5% VFF-HHB-O1 (3-1) 8% VFF-HHB-1 (3-1) 3% 2-BB(2F, 3F)B-3 (11-1) 4% 3-HBB(2F, 3F)-O2 (10-7) 2%
(420) NI=81.9° C.; Tc<−20° C.; Δn=0.109; Δε=4.8; Vth=1.75 V; η=13.3 mPa.Math.s; γ1=57.4 mPa.Math.s.
(421) Composition (M35)
(422) TABLE-US-00038 3-HHEB(F, F)-F (6-12) 4% 3-HBEB(F, F)-F (6-39) 3% 5-HBEB(F, F)-F (6-39) 3% 3-BB(F)B(F, F)-F (6-69) 3% 3-HBBXB(F, F)-F (7-32) 6% 4-GBB(F, F)XB(F, F)-F (7-62) 2% 5-GBB(F, F)XB(F, F)-F (7-62) 2% 3-GB(F)B(F, F)XB(F, F)-F (7-57) 5% 4-GB(F)B(F, F)XB(F, F)-F (7-57) 5% 5-HHB(F, F)XB(F, F)-F (7-29) 3% 5-HEB(F, F)-F (5-10) 3% 5-HB-CL (5-2) 2% 3-HHB-OCF3 (6-1) 4% 3-HH-5 (2-1) 4% 3-HH-V (2-1) 21% 3-HH-V1 (2-1) 3% 4-HH-V (2-1) 4% 1V2-HH-3 (2-1) 6% 5-B(F)BB-2 (3-8) 3% 5-B(F)BB-3 (3-8) 2% 3-HB(2F, 3F)-O2 (10-7) 3% 3-BB(2F, 3F)-O2 (9-3) 2% 3-HHB(2F, 3F)-O2 (10-1) 4% F3-HH-V (2-1) 3%
(423) NI=78.2° C.; Tc<−20° C.; Δn=0.101; Δε=6.7; Vth=1.45 V; η=17.8 mPa.Math.s; γ1=67.8 mPa.Math.s.
(424) Composition (M36)
(425) TABLE-US-00039 3-HHB(F, F)-F (6-3) 10% 3-HHXB(F, F)-F (6-100) 2% 3-GHB(F, F)-F (6-109) 5% 3-BB(F)B(F, F)-F (6-69) 6% 3-BB(F, F)XB(F, F)-F (6-97) 14% 4-BB(F)B(F, F)XB(F, F)-F (7-47) 10% 5-BB(F)B(F, F)XB(F, F)-F (7-47) 6% 2-HH-3 (2-1) 5% 3-HH-4 (2-1) 11% 3-HH-O1 (2-1) 5% 5-HB-O2 (2-5) 8% 3-HHB-1 (3-1) 6% 3-HHB-3 (3-1) 6% 3-HHB-O1 (3-1) 6%
(426) NI=77.6° C.; Tc<−20° C.; Δn=0.109; Δε=10.6; Vth=1.34 V; η=22.6 mPa.Math.s; γ1=92.4 mPa.Math.s.
(427) Composition (M37)
(428) TABLE-US-00040 3-HBB-F (6-22) 3% 3-BB(F, F)XB(F)-OCF3 (6-96) 3% 3-HHB(F)-F (6-2) 3% 3-HGB(F, F)-F (6-103) 3% 5-GHB(F, F)-F (6-109) 3% 3-HBB(F, F)-F (6-24) 4% 3-BB(F, F)XB(F, F)-F (6-97) 5% 3-HHBB(F, F)-F (7-6) 5% 3-HBBXB(F, F)-F (7-32) 5% 3-BBVFFXB(F, F)-F (6-119) 8% 3-HH-V (2-1) 39% 1-HH-V1 (2-1) 3% 1-HH-2V1 (2-1) 4% 3-HHEH-5 (3-13) 3% 1-BB(F)B-2V (3-6) 3% 3-HHEBH-3 (4-6) 3% 5-HBB(F)B-2 (4-5) 3%
(429) NI=85.2° C.; Tc<−20° C.; Δn=0.102; Δε=4.1; γ1=43.0 mPa.Math.s.
(430) Composition (M38)
(431) TABLE-US-00041 3-HHBB(F)-F (7-5) 3% 2-HHEB(F, F)-F (6-12) 3% 5-BB(F)B(F, F)-F (6-69) 7% 3-HHB(F)B(F, F)-F (7-9) 3% 3-GB(F)B(F, F)XB(F, F)-F (7-57) 3% 3-BB(F, F)XB(F)B(F, F)-F (7-60) 3% 3-HHVFFXB(F, F)-F (6-120) 5% 3-BBVFFXB(F, F)-F (6-119) 5% 3-HBBVFFXB(F, F)-F (7-61) 3% 2-HH-5 (2-1) 5% 3-HH-V (2-1) 20% 5-HH-V (2-1) 12% 3-HH-V1 (2-1) 4% 4-HH-V1 (2-1) 5% 2-HH-2V1 (2-1) 3% 1-BB-3 (2-8) 3% V2-BB(F)B-1 (3-6) 5% V2-B(F)BB-1 (3-8) 5% 3-HB(F)HH-5 (4-7) 3%
(432) NI=85.8° C.; Tc<−20° C.; Δn=0.115; Δε=4.2; γ1=41.4 mPa.Math.s.
(433) Composition (M39)
(434) TABLE-US-00042 3-BB(F)XB(F)B(F, F)-F (7-60) 5% 3-HGB(F, F)-F (6-103) 3% 5-GHB(F, F)-F (6-109) 4% 3-GB(F, F)XB(F, F)-F (6-113) 5% 3-HHBB(F, F)-F (7-6) 4% 2-dhBB(F, F)XB(F, F)-F (7-50) 4% 3-GB(F)B(F, F)XB(F, F)-F (7-57) 3% 3-HGB(F, F)XB(F, F)-F (7) 5% 7-HB(F, F)-F (5-4) 3% 2-HH-3 (2-1) 14% 2-HH-5 (2-1) 4% 3-HH-V (2-1) 26% 1V2-HH-3 (2-1) 5% 1V2-BB-1 (2-8) 3% 2-BB(F)B-3 (3-6) 3% 3-HB(F)HH-2 (4-7) 4% 5-HBB(F)B-2 (4-5) 5%
(435) NI=78.4° C.; Tc<−20° C.; Δn=0.094; Δε=5.6; Vth=1.45 V; η=11.5 mPa.Math.s; γ1=61.7 mPa.Math.s.
(436) Composition (M40)
(437) TABLE-US-00043 3-HBB(F, F)-F (6-24) 5% 5-HBB(F, F)-F (6-24) 4% 3-BB(F)B(F, F)XB(F, F)-F (7-47) 3% 4-BB(F)B(F, F)XB(F, F)-F (7-47) 5% 3-BB(F, F)XB(F)B(F, F)-F (7-60) 10% 3-HH2BB(F, F)-F (7-15) 3% 4-HH2BB(F, F)-F (7-15) 3% 2-HH-5 (2-1) 4% 3-HH-V (2-1) 25% 3-HH-V1 (2-1) 10% 4-HH-V1 (2-1) 7% 5-HB-O2 (2-5) 5% 7-HB-1 (2-5) 5% VFF-HHB-O1 (3-1) 8% VFF-HHB-1 (3-1) 3%
(438) NI=79.3° C.; Tc<−20° C.; Δn=0.099; Δε=5.0; Vth=1.64 V; η=10.4 mPa.Math.s; γ1=44.7 mPa.Math.s.
(439) Composition (M41)
(440) TABLE-US-00044 3-GBXB(F)B(F, F)-F (7) 5% 3-HHB(F, F)-F (6-3) 7% 3-GB(F)B(F)-F (6-116) 2% 3-GB(F)B(F, F)-F (6-117) 3% 3-BB(F, F)XB(F, F)-F (6-97) 7% 3-GB(F)B(F, F)XB(F, F)-F (7-57) 4% 5-GB(F)B(F, F)XB(F, F)-F (7-57) 5% 3-HH-V (2-1) 30% 3-HH-V1 (2-1) 10% 1V2-HH-3 (2-1) 8% 3-HH-VFF (2-1) 8% V2-BB-1 (2-8) 2% 5-HB(F)BH-3 (4-2) 4% 5-HBBH-3 (4-1) 5%
(441) NI=79.7° C.; Tc<−20° C.; Δn=0.091; Δε=5.7; Vth=1.83 V; η=14.9 mPa.Math.s; γ1=69.3 mPa.Math.s.
2. Alignment of Liquid Crystal Molecules
Use Example 1
(442) To composition (M1), compound (No. 59) was added at a proportion of 0.1% by weight as a first additive, and compound (AO-1) in which R.sup.40 is n-heptyl was added at a proportion of 150 ppm as an antioxidant. The resulting mixture was injected into an IPS device having no alignment film at 90° C. (equal to or higher than a maximum temperature of a nematic phase). The IPS device was irradiated with linearly polarized ultraviolet light (313 nm, 2.0 J/cm.sup.2) from a direction normal to the device while heating the device at 90° C. to obtain a device subjected to alignment treatment. The resulting device was set on a polarizing microscope in which a polarizer and an analyzer were arranged perpendicularly to each other to be parallel to a polarization axis of linearly polarized light in the device. The device was irradiated with light from below, and presence or absence of light leakage was observed. A case where no light passed through the device was judged to be “Good” in alignment. A case where light passing through the device was observed was expressed by “Poor.” No light leakage was observed in the present Example 1, and therefore alignment was good.
Use Examples 2 to 589
(443) As shown in Tables 4 to 27 below, compositions (M1) to (M41) were used, compound (AO-1) in which R.sup.40 is n-heptyl was added at a proportion of 150 ppm as an antioxidant, and a first additive was mixed thereto at a proportion of 0.1% by weight as described in the following tables. Operation was performed in the same manner as in Use Example 1 except for the operation described above. When presence or absence of light leakage was observed in the same manner as in Use Example 1, no light leakage was observed, and therefore alignment was good.
(444) TABLE-US-00045 TABLE 4 Liquid crystal com Use Example position First additive Alignment 2 M2 No. 1 Good 3 M3 No. 2 Good 4 M4 No. 3 Good 5 M5 No. 4 Good 6 M6 No. 5 Good 7 M7 No. 6 Good 8 M8 No. 7 Good 9 M9 No. 8 Good 10 M10 No. 9 Good 11 M11 No. 10 Good 12 M12 No. 11 Good
(445) TABLE-US-00046 TABLE 5 13 M13 No. 12 Good 14 M14 No. 13 Good 15 M15 No. 14 Good 16 M16 No. 15 Good 17 M17 No. 16 Good 18 M18 No. 17 Good 19 M19 No. 18 Good 20 M20 No. 19 Good 21 M21 No. 20 Good 22 M22 No. 21 Good 23 M23 No. 22 Good 24 M24 No. 23 Good 25 M25 No. 24 Good 26 M26 No. 25 Good 27 M27 No. 26 Good 28 M28 No. 27 Good 29 M29 No. 28 Good 30 M30 No. 29 Good 31 M31 No. 30 Good 32 M32 No. 31 Good 33 M33 No. 32 Good 34 M34 No. 33 Good 35 M35 No. 34 Good 36 M36 No. 35 Good 37 M37 No. 36 Good
(446) TABLE-US-00047 TABLE 6 38 M38 No. 37 Good 39 M39 No. 38 Good 40 M40 No. 39 Good 41 M41 No. 40 Good 42 M1 No. 41 Good 43 M2 No. 42 Good 44 M3 No. 43 Good 45 M4 No. 44 Good 46 M5 No. 45 Good 47 M6 No. 46 Good 48 M7 No. 47 Good 49 M8 No. 48 Good 50 M9 No. 49 Good 51 M10 No. 50 Good 52 M11 No. 51 Good 53 M12 No. 52 Good 54 M13 No. 53 Good 55 M14 No. 54 Good 56 M15 No. 55 Good 57 M16 No. 56 Good 58 M17 No. 57 Good 59 M18 No. 58 Good 60 M19 No. 59 Good 61 M20 No. 60 Good
(447) TABLE-US-00048 TABLE 7 62 M21 No. 61 Good 63 M22 No. 62 Good 64 M23 No. 63 Good 65 M24 No. 64 Good 66 M25 No. 65 Good 67 M26 No. 66 Good 68 M27 No. 67 Good 69 M28 No. 68 Good 70 M29 No. 69 Good 71 M30 No. 70 Good 72 M31 No. 71 Good 73 M32 No. 72 Good 74 M33 No. 73 Good 75 M34 No. 74 Good 76 M35 No. 75 Good 77 M36 No. 76 Good 78 M37 No. 77 Good 79 M38 No. 78 Good 80 M39 No. 79 Good 81 M40 No. 80 Good 82 M41 No. 81 Good 83 M1 No. 82 Good
(448) TABLE-US-00049 TABLE 8 84 M2 No. 83 Good 85 M3 No. 84 Good 86 M4 No. 85 Good 87 M5 No. 86 Good 88 M6 No. 87 Good 89 M7 No. 88 Good 90 M8 No. 89 Good 91 M9 No. 90 Good 92 M10 No. 91 Good 93 M11 No. 92 Good 94 M12 No. 93 Good 95 M13 No. 94 Good 96 M14 No. 95 Good 97 M15 No. 96 Good 98 M16 No. 97 Good 99 M17 No. 98 Good 100 M18 No. 99 Good 101 M19 No. 100 Good 102 M20 No. 101 Good 103 M21 No. 102 Good 104 M22 No. 103 Good 105 M23 No. 104 Good 106 M24 No. 105 Good 107 M25 No. 106 Good 108 M26 No. 107 Good 109 M27 No. 108 Good 110 M28 No. 109 Good
(449) TABLE-US-00050 TABLE 9 111 M29 No. 110 Good 112 M30 No. 111 Good 113 M31 No. 112 Good 114 M32 No. 113 Good 115 M33 No. 114 Good 116 M34 No. 115 Good 117 M35 No. 116 Good 118 M36 No. 117 Good 119 M37 No. 118 Good 120 M38 No. 119 Good 121 M39 No. 120 Good 122 M40 No. 121 Good 123 M41 No. 122 Good 124 M1 No. 123 Good 125 M2 No. 124 Good 126 M3 No. 125 Good 127 M4 No. 126 Good 128 M5 No. 127 Good 129 M6 No. 128 Good 130 M7 No. 129 Good 131 M8 No. 130 Good 132 M9 No. 131 Good 133 M10 No. 132 Good 134 M11 No. 133 Good
(450) TABLE-US-00051 TABLE 10 135 M12 No. 134 Good 136 M13 No. 135 Good 137 M14 No. 136 Good 138 M15 No. 137 Good 139 M16 No. 138 Good 140 M17 No. 139 Good 141 M18 No. 140 Good 142 M19 No. 141 Good 143 M20 No. 142 Good 144 M21 No. 143 Good 145 M22 No. 144 Good 146 M23 No. 145 Good 147 M24 No. 146 Good 148 M25 No. 147 Good 149 M26 No. 148 Good 150 M27 No. 149 Good 151 M28 No. 150 Good 152 M29 No. 151 Good 153 M30 No. 152 Good 154 M31 No. 153 Good 155 M32 No. 154 Good 156 M33 No. 155 Good 157 M34 No. 156 Good 158 M35 No. 157 Good 159 M36 No. 158 Good
(451) TABLE-US-00052 TABLE 11 160 M37 No. 159 Good 161 M38 No. 160 Good 162 M39 No. 161 Good 163 M40 No. 162 Good 164 M41 No. 163 Good 165 M1 No. 164 Good 166 M2 No. 165 Good 167 M3 No. 166 Good 168 M4 No. 167 Good 169 M5 No. 168 Good 170 M6 No. 169 Good 171 M7 No. 170 Good 172 M8 No. 171 Good 173 M9 No. 172 Good 174 M10 No. 173 Good 175 M11 No. 174 Good 176 M12 No. 175 Good 177 M13 No. 176 Good 178 M14 No. 177 Good 179 M15 No. 178 Good 180 M16 No. 179 Good 181 M17 No. 180 Good 182 M18 No. 181 Good 183 M19 No. 182 Good 184 M20 No. 183 Good
(452) TABLE-US-00053 TABLE 12 185 M21 No. 184 Good 186 M22 No. 185 Good 187 M23 No. 186 Good 188 M24 No. 187 Good 189 M25 No. 188 Good 190 M26 No. 189 Good 191 M27 No. 190 Good 192 M28 No. 191 Good 193 M29 No. 192 Good 194 M30 No. 193 Good 195 M31 No. 194 Good 196 M32 No. 195 Good 197 M33 No. 196 Good 198 M34 No. 197 Good 199 M35 No. 198 Good 200 M36 No. 199 Good 201 M37 No. 200 Good 202 M38 No. 201 Good 203 M39 No. 202 Good 204 M40 No. 203 Good 205 M41 No. 204 Good 206 M1 No. 205 Good 207 M2 No. 206 Good 208 M3 No. 207 Good
(453) TABLE-US-00054 TABLE 13 209 M4 No. 208 Good 210 M5 No. 209 Good 211 M6 No. 210 Good 212 M7 No. 211 Good 213 M8 No. 212 Good 214 M9 No. 213 Good 215 M10 No. 214 Good 216 M11 No. 215 Good 217 M12 No. 216 Good 218 M13 No. 217 Good 219 M14 No. 218 Good 220 M15 No. 219 Good 221 M16 No. 220 Good 222 M17 No. 221 Good 223 M18 No. 222 Good 224 M19 No. 223 Good 225 M20 No. 224 Good 226 M21 No. 225 Good 227 M22 No. 226 Good 228 M23 No. 227 Good 229 M24 No. 228 Good 230 M25 No. 229 Good
(454) TABLE-US-00055 TABLE 14 231 M26 No. 230 Good 232 M27 No. 231 Good 233 M28 No. 232 Good 234 M29 No. 233 Good 235 M30 No. 234 Good 236 M31 No. 235 Good 237 M32 No. 236 Good 238 M33 No. 237 Good 239 M34 No. 238 Good 240 M35 No. 239 Good 241 M36 No. 240 Good 242 M37 No. 241 Good 243 M38 No. 242 Good 244 M39 No. 243 Good 245 M40 No. 244 Good 246 M41 No. 245 Good 247 M1 No. 246 Good 248 M2 No. 247 Good 249 M3 No. 248 Good 250 M4 No. 249 Good 251 M5 No. 250 Good 252 M6 No. 251 Good 253 M7 No. 252 Good 254 M8 No. 253 Good 255 M9 No. 254 Good 256 M10 No. 255 Good 257 M11 No. 256 Good
(455) TABLE-US-00056 TABLE 15 258 M12 No. 257 Good 259 M13 No. 258 Good 260 M14 No. 259 Good 261 M15 No. 260 Good 262 M16 No. 261 Good 263 M17 No. 262 Good 264 M18 No. 263 Good 265 M19 No. 264 Good 266 M20 No. 265 Good 267 M21 No. 266 Good 268 M22 No. 267 Good 269 M23 No. 268 Good 270 M24 No. 269 Good 271 M25 No. 270 Good 272 M26 No. 271 Good 273 M27 No. 272 Good 274 M28 No. 273 Good 275 M29 No. 274 Good 276 M30 No. 275 Good 277 M31 No. 276 Good 278 M32 No. 277 Good 279 M33 No. 278 Good 280 M34 No. 279 Good 281 M35 No. 280 Good 282 M36 No. 281 Good
(456) TABLE-US-00057 TABLE 16 283 M37 No. 282 Good 284 M38 No. 283 Good 285 M39 No. 284 Good 286 M40 No. 285 Good 287 M41 No. 286 Good 288 M1 No. 287 Good 289 M2 No. 288 Good 290 M3 No. 289 Good 291 M4 No. 290 Good 292 M5 No. 291 Good 293 M6 No. 292 Good 294 M7 No. 293 Good 295 M8 No. 294 Good 296 M9 No. 295 Good 297 M10 No. 296 Good 298 M11 No. 297 Good 299 M12 No. 298 Good 300 M13 No. 299 Good 301 M14 No. 300 Good 302 M15 No. 301 Good 303 M16 No. 302 Good 304 M17 No. 303 Good 305 M18 No. 304 Good 306 M19 No. 305 Good
(457) TABLE-US-00058 TABLE 17 307 M20 No. 306 Good 308 M21 No. 307 Good 309 M22 No. 308 Good 310 M23 No. 309 Good 311 M24 No. 310 Good 312 M25 No. 311 Good 313 M26 No. 312 Good 314 M27 No. 313 Good 315 M28 No. 314 Good 316 M29 No. 315 Good 317 M30 No. 316 Good 318 M31 No. 317 Good 319 M32 No. 318 Good 320 M33 No. 319 Good 321 M34 No. 320 Good 322 M35 No. 321 Good 323 M36 No. 322 Good 324 M37 No. 323 Good 325 M38 No. 324 Good 326 M39 No. 325 Good 327 M40 No. 326 Good 328 M41 No. 327 Good 329 M1 No. 328 Good
(458) TABLE-US-00059 TABLE 18 330 M2 No. 329 Good 331 M3 No. 330 Good 332 M4 No. 331 Good 333 M5 No. 332 Good 334 M6 No. 333 Good 335 M7 No. 334 Good 336 M8 No. 335 Good 337 M9 No. 336 Good 338 M10 No. 337 Good 339 M11 No. 338 Good 340 M12 No. 339 Good 341 M13 No. 340 Good 342 M14 No. 341 Good 343 M15 No. 342 Good 344 M16 No. 343 Good 345 M17 No. 344 Good 346 M18 No. 345 Good 347 M19 No. 346 Good 348 M20 No. 347 Good 349 M21 No. 348 Good 350 M22 No. 349 Good 351 M23 No. 350 Good 352 M24 No. 351 Good 353 M25 No. 352 Good 354 M26 No. 353 Good 355 M27 No. 354 Good
(459) TABLE-US-00060 TABLE 19 356 M28 No. 355 Good 357 M29 No. 356 Good 358 M30 No. 357 Good 359 M31 No. 358 Good 360 M32 No. 359 Good 361 M33 No. 360 Good 362 M34 No. 361 Good 363 M35 No. 362 Good 364 M36 No. 363 Good 365 M37 No. 364 Good 366 M38 No. 365 Good 367 M39 No. 366 Good 368 M40 No. 367 Good 369 M41 No. 368 Good 370 M1 No. 369 Good 371 M2 No. 370 Good 372 M3 No. 371 Good 373 M4 No. 372 Good 374 M5 No. 373 Good 375 M6 No. 374 Good 376 M7 No. 375 Good 377 M8 No. 376 Good 378 M9 No. 377 Good 379 M10 No. 378 Good 380 M11 No. 379 Good 381 M12 No. 380 Good 382 M13 No. 381 Good
(460) TABLE-US-00061 TABLE 20 383 M14 No. 382 Good 384 M15 No. 383 Good 385 M16 No. 384 Good 386 M17 No. 385 Good 387 M18 No. 386 Good 388 M19 No. 387 Good 389 M20 No. 388 Good 390 M21 No. 389 Good 391 M22 No. 390 Good 392 M23 No. 391 Good 393 M24 No. 392 Good 394 M25 No. 393 Good 395 M26 No. 394 Good 396 M27 No. 395 Good 397 M28 No. 396 Good 398 M29 No. 397 Good 399 M30 No. 398 Good 400 M31 No. 399 Good 401 M32 No. 400 Good 402 M33 No. 401 Good 403 M34 No. 402 Good 404 M35 No. 403 Good
(461) TABLE-US-00062 TABLE 21 405 M36 No. 404 Good 406 M37 No. 405 Good 407 M38 No. 406 Good 408 M39 No. 407 Good 409 M40 No. 408 Good 410 M41 No. 409 Good 411 M1 No. 410 Good 412 M2 No. 411 Good 413 M3 No. 412 Good 414 M4 No. 413 Good 415 M5 No. 414 Good 416 M6 No. 415 Good 417 M7 No. 416 Good 418 M8 No. 417 Good 419 M9 No. 418 Good 420 M10 No. 419 Good 421 M11 No. 420 Good 422 M12 No. 421 Good 423 M13 No. 422 Good 424 M14 No. 423 Good 425 M15 No. 424 Good
(462) TABLE-US-00063 TABLE 22 426 M16 No. 425 Good 427 M17 No. 426 Good 428 M18 No. 427 Good 429 M19 No. 428 Good 430 M20 No. 429 Good 431 M21 No. 430 Good 432 M22 No. 431 Good 433 M23 No. 432 Good 434 M24 No. 433 Good 435 M25 No. 434 Good 436 M26 No. 435 Good 437 M27 No. 436 Good 438 M28 No. 437 Good 439 M29 No. 438 Good 440 M30 No. 439 Good 441 M31 No. 440 Good 442 M32 No. 441 Good 443 M33 No. 442 Good 444 M34 No. 443 Good 445 M35 No. 444 Good 446 M36 No. 445 Good 447 M37 No. 446 Good 448 M38 No. 447 Good 449 M39 No. 448 Good 450 M40 No. 449 Good 451 M41 No. 450 Good 452 M1 No. 451 Good 453 M2 No. 452 Good
(463) TABLE-US-00064 TABLE 23 454 M3 No. 453 Good 455 M4 No. 454 Good 456 M5 No. 455 Good 457 M6 No. 456 Good 458 M7 No. 457 Good 459 M8 No. 458 Good 460 M9 No. 459 Good 461 M10 No. 460 Good 462 M11 No. 461 Good 463 M12 No. 462 Good 464 M13 No. 463 Good 465 M14 No. 464 Good 466 M15 No. 465 Good 467 M16 No. 466 Good 468 M17 No. 467 Good 469 M18 No. 468 Good 470 M19 No. 469 Good 471 M20 No. 470 Good 472 M21 No. 471 Good 473 M22 No. 472 Good 474 M23 No. 473 Good 475 M24 No. 474 Good 476 M25 No. 475 Good 477 M26 No. 476 Good
(464) TABLE-US-00065 TABLE 24 478 M27 No. 477 Good 479 M28 No. 478 Good 480 M29 No. 479 Good 481 M30 No. 480 Good 482 M31 No. 481 Good 483 M32 No. 482 Good 484 M33 No. 483 Good 485 M34 No. 484 Good 486 M35 No. 485 Good 487 M36 No. 486 Good 488 M37 No. 487 Good 489 M38 No. 488 Good 490 M39 No. 489 Good 491 M40 No. 490 Good 492 M41 No. 491 Good 493 M1 No. 492 Good 494 M2 No. 493 Good 495 M3 No. 494 Good 496 M4 No. 495 Good 497 M5 No. 496 Good 498 M6 No. 497 Good 499 M7 No. 498 Good 500 M8 No. 499 Good 501 M9 No. 500 Good 502 M10 No. 501 Good
(465) TABLE-US-00066 TABLE 25 503 M11 No. 502 Good 504 M12 No. 503 Good 505 M13 No. 504 Good 506 M14 No. 505 Good 507 M15 No. 506 Good 508 M16 No. 507 Good 509 M17 No. 508 Good 510 M18 No. 509 Good 511 M19 No. 510 Good 512 M20 No. 511 Good 513 M21 No. 512 Good 514 M22 No. 513 Good 515 M23 No. 514 Good 516 M24 No. 515 Good 517 M25 No. 516 Good 518 M26 No. 517 Good 519 M27 No. 518 Good 520 M28 No. 519 Good 521 M29 No. 520 Good 522 M30 No. 521 Good 523 M31 No. 522 Good 524 M32 No. 523 Good 525 M33 No. 524 Good 526 M34 No. 525 Good
(466) TABLE-US-00067 TABLE 26 527 M35 No. 526 Good 528 M36 No. 527 Good 529 M37 No. 528 Good 530 M38 No. 529 Good 531 M39 No. 530 Good 532 M40 No. 531 Good 533 M41 No. 532 Good 534 M1 No. 533 Good 535 M2 No. 534 Good 536 M3 No. 535 Good 537 M4 No. 536 Good 538 M5 No. 537 Good 539 M6 No. 538 Good 540 M7 No. 539 Good 541 M8 No. 540 Good 542 M9 No. 541 Good 543 M10 No. 542 Good 544 M11 No. 543 Good 545 M12 No. 544 Good 546 M13 No. 545 Good 547 M14 No. 546 Good 548 M15 No. 547 Good 549 M16 No. 548 Good 550 M17 No. 549 Good 551 M18 No. 550 Good
(467) TABLE-US-00068 TABLE 27 552 M19 No. 551 Good 553 M20 No. 552 Good 554 M21 No. 553 Good 555 M22 No. 554 Good 556 M23 No. 555 Good 557 M24 No. 556 Good 558 M25 No. 557 Good 559 M26 No. 558 Good 560 M27 No. 559 Good 561 M28 No. 560 Good 562 M29 No. 561 Good 563 M30 No. 562 Good 564 M31 No. 563 Good 565 M32 No. 564 Good 566 M33 No. 565 Good 567 M34 No. 566 Good 568 M35 No. 567 Good 569 M36 No. 568 Good 570 M37 No. 569 Good 571 M38 No. 570 Good 572 M39 No. 571 Good 573 M40 No. 572 Good 574 M41 No. 573 Good 575 M1 No. 574 Good 576 M2 No. 575 Good 577 M3 No. 576 Good 578 M4 No. 577 Good 579 M5 No. 578 Good 580 M6 No. 579 Good 581 M7 No. 580 Good 582 M8 No. 581 Good 583 M9 No. 582 Good 584 M10 No. 583 Good 585 M11 No. 584 Good 586 M12 No. 585 Good 587 M13 No. 586 Good 588 M14 No. 587 Good 589 M15 No. 588 Good
Comparative Examples 1 to 123
(468) As shown in Tables 28 to 33 below, (A-1-1-1) or (A-1-3-1) in which a polymerizable group is an acrylate group for both, and Formula 2 in which a polymerizable group is a methacrylate group for all as described in the Patent literature were added to each of compositions (M1) to (M41) at a proportion of 0.1% by weight. The resulting mixture was injected into an IPS device having no alignment film. When operation was performed in the same manner as in Use Example 1 except for injecting the mixture, and presence or absence of light leakage was observed in the same manner as in Use Example 1, light leakage was observed in all cases, and therefore alignment was poor.
(469) ##STR00695##
(470) TABLE-US-00069 TABLE 28 Comparative Liquid crystal Example composition First additive Alignment 1 M1 A-1-1-1 Poor 2 M2 A-1-1-1 Poor 3 M3 A-1-1-1 Poor 4 M4 A-1-1-1 Poor 5 M5 A-1-1-1 Poor 6 M6 A-1-1-1 Poor 7 M7 A-1-1-1 Poor 8 M8 A-1-1-1 Poor 9 M9 A-1-1-1 Poor 10 M10 A-1-1-1 Poor 11 M11 A-1-1-1 Poor 12 M12 A-1-1-1 Poor 13 M13 A-1-1-1 Poor
(471) TABLE-US-00070 TABLE 29 14 M14 A-1-1-1 Poor 15 M15 A-1-1-1 Poor 16 M16 A-1-1-1 Poor 17 M17 A-1-1-1 Poor 18 M18 A-1-1-1 Poor 19 M19 A-1-1-1 Poor 20 M20 A-1-1-1 Poor 21 M21 A-1-1-1 Poor 22 M22 A-1-1-1 Poor 23 M23 A-1-1-1 Poor 24 M24 A-1-1-1 Poor 25 M25 A-1-1-1 Poor 26 M26 A-1-1-1 Poor 27 M27 A-1-1-1 Poor
(472) TABLE-US-00071 TABLE 30 28 M28 A-1-1-1 Poor 29 M29 A-1-1-1 Poor 30 M30 A-1-1-1 Poor 31 M31 A-1-1-1 Poor 32 M32 A-1-1-1 Poor 33 M33 A-1-1-1 Poor 34 M34 A-1-1-1 Poor 35 M35 A-1-1-1 Poor 36 M36 A-1-1-1 Poor 37 M37 A-1-1-1 Poor 38 M38 A-1-1-1 Poor 39 M39 A-1-1-1 Poor 40 M40 A-1-1-1 Poor 41 M41 A-1-1-1 Poor 42 M1 A-1-3-1 Poor 43 M2 A-1-3-1 Poor 44 M3 A-1-3-1 Poor 45 M4 A-1-3-1 Poor 46 M5 A-1-3-1 Poor 47 M6 A-1-3-1 Poor 48 M7 A-1-3-1 Poor 49 M8 A-1-3-1 Poor 50 M9 A-1-3-1 Poor 51 M10 A-1-3-1 Poor
(473) TABLE-US-00072 TABLE 31 52 M11 A-1-3-1 Poor 53 M12 A-1-3-1 Poor 54 M13 A-1-3-1 Poor 55 M14 A-1-3-1 Poor 56 M15 A-1-3-1 Poor 57 M16 A-1-3-1 Poor 58 M17 A-1-3-1 Poor 59 M18 A-1-3-1 Poor 60 M19 A-1-3-1 Poor 61 M20 A-1-3-1 Poor 62 M21 A-1-3-1 Poor 63 M22 A-1-3-1 Poor 64 M23 A-1-3-1 Poor 65 M24 A-1-3-1 Poor 66 M25 A-1-3-1 Poor 67 M26 A-1-3-1 Poor 68 M27 A-1-3-1 Poor 69 M28 A-1-3-1 Poor 70 M29 A-1-3-1 Poor 71 M30 A-1-3-1 Poor 72 M31 A-1-3-1 Poor 73 M32 A-1-3-1 Poor 74 M33 A-1-3-1 Poor 75 M34 A-1-3-1 Poor 76 M35 A-1-3-1 Poor
(474) TABLE-US-00073 TABLE 32 77 M36 A-1-3-1 Poor 78 M37 A-1-3-1 Poor 79 M38 A-1-3-1 Poor 80 M39 A-1-3-1 Poor 81 M40 A-1-3-1 Poor 82 M41 A-1-3-1 Poor 83 M1 Formula 2 Poor 84 M2 Formula 2 Poor 85 M3 Formula 2 Poor 86 M4 Formula 2 Poor 87 M5 Formula 2 Poor 88 M6 Formula 2 Poor 89 M7 Formula 2 Poor 90 M8 Formula 2 Poor 91 M9 Formula 2 Poor 92 M10 Formula 2 Poor 93 M11 Formula 2 Poor 94 M12 Formula 2 Poor 95 M13 Formula 2 Poor 96 M14 Formula 2 Poor 97 M15 Formula 2 Poor 98 M16 Formula 2 Poor
(475) TABLE-US-00074 TABLE 33 99 M17 Formula 2 Poor 100 M18 Formula 2 Poor 101 M19 Formula 2 Poor 102 M20 Formula 2 Poor 103 M21 Formula 2 Poor 104 M22 Formula 2 Poor 105 M23 Formula 2 Poor 106 M24 Formula 2 Poor 107 M25 Formula 2 Poor 108 M26 Formula 2 Poor 109 M27 Formula 2 Poor 110 M28 Formula 2 Poor 111 M29 Formula 2 Poor 112 M30 Formula 2 Poor 113 M31 Formula 2 Poor 114 M32 Formula 2 Poor 115 M33 Formula 2 Poor 116 M34 Formula 2 Poor 117 M35 Formula 2 Poor 118 M36 Formula 2 Poor 119 M37 Formula 2 Poor 120 M38 Formula 2 Poor 121 M39 Formula 2 Poor 122 M40 Formula 2 Poor 123 M41 Formula 2 Poor
(476) In Use Examples 1 to 589, a kind and an amount of compositions or alignment control monomers, and a heating temperature during polarization exposure were changed, and no light leakage was observed. The results indicate that alignment is good even without any alignment film such as polyimide, and all liquid crystal molecules are arranged in a fixed direction. On the other hand, in Comparative Examples 1 to 123, light leakage was observed, indicating that the liquid crystal compounds were not aligned. From the results described above, the compounds of the present application are known to be able to form a thin film for aligning the liquid crystal composition by addition with a concentration lower than a level of the comparative compound. Accordingly, if the liquid crystal composition of the invention is used, a liquid crystal display device having characteristics such as a wide temperature range in which the device can be used, a short response time, a high voltage holding ratio, low threshold voltage, a large contrast ratio and a long service life can be obtained. Further, a liquid crystal display device having a liquid crystal composition satisfying at least one of characteristics such as high maximum temperature of a nematic phase, low minimum temperature of the nematic phase, small viscosity, suitable optical anisotropy, large negative dielectric anisotropy, large specific resistance, high stability to ultraviolet light and high stability to heat can be obtained.
INDUSTRIAL APPLICABILITY
(477) A liquid crystal composition of the invention can be used in a liquid crystal monitor, a liquid crystal television and so forth.