WELDING FILLER WIRE FOR FUSION WELDING PRECIPITATION-HARDENED AUSTENITIC Fe-Mn-Al-C ALLOYS

Abstract

A series of welding filler wires with innovative composition design for fusion welding precipitation-hardened lightweight austenitic Fe—Mn—Al—C alloys. The first class of the welding filler wires is composed of 23-34 wt. % Mn, 7.5-11.5 wt. % Al, 1.35-1.95 wt. % C, with the balance being essentially Fe. After fusion welding, there are high-density of nano-sized (˜3-5 nm) (Fe,Mn).sub.3AlC carbides (κ-carbides) uniformly distributed within the austenite dendrite cells in the fusion zone (FZ). The amount of nano-sized (˜6-10 nm) κ-carbides existing within the eutectic regions is significantly increased and the size of the austenite dendrite cells is substantially reduced. The second class of welding filler wires has the composition of 23-34 wt. % Mn, 7.5-11.5 wt. % Al, 1.40-1.95 wt. % C, 0.1-2.5 wt. % Ti, 0.1-3.0 wt. % Nb, 0.1-2.5 wt. % V, with the balance being essentially Fe. The microstructure of the FZ in the as-welded condition results in formation of substantial amount of nano-sized (˜6-10 nm) face-centered-cubic structured ductile Ti-rich Ti-carbides, Nb-rich Nb-carbides and V-rich V-carbides within the eutectic regions. These carbides are extremely hard (2000˜3500 Hv), enhancing hardness of the obtained FZ.

Claims

1. A welding filler wire, for fusion welding precipitation-hardened austenitic Fe—Mn—Al—C alloys, consisting essentially of, by weight, 23 to 34 percent manganese (Mn), 7.5 to 11.5 percent aluminum (Al), 1.35 to 1.95 percent carbon (C), and balance essentially iron (Fe).

2. A welding filler wire, for fusion welding precipitation-hardened austenitic Fe—Mn—Al—C alloys, consisting essentially of, by weight, 24 to 32 percent manganese (Mn), 8.0 to 11.0 percent aluminum (Al), 1.40 to 1.95 percent carbon (C), and balance essentially iron (Fe).

3. A welding filler wire, for fusion welding precipitation-hardened austenitic Fe—Mn—Al—C alloys, consisting essentially of, by weight, 23 to 34 percent manganese (Mn), 7.5 to 11.5 percent aluminum (Al), 1.40 to 1.95 percent carbon (C), 0.1 to 2.5 percent titanium (Ti), and balance essentially iron (Fe).

4. A welding filler wire, for fusion welding the precipitation-hardened austenitic Fe—Mn—Al—C alloys, consisting essentially of, by weight, 23 to 34 percent manganese (Mn), 7.5 to 11.5 percent aluminum (Al), 1.40 to 1.95 percent carbon (C), 0.1 to 3.0 percent niobium (Nb), and balance essentially iron (Fe).

5. A welding filler wire, for fusion welding precipitation-hardened austenitic Fe—Mn—Al—C alloys, consisting essentially of, by weight, 23 to 34 percent manganese (Mn), 7.5 to 11.5 percent aluminum (Al), 1.40 to 1.95 percent carbon (C), 0.1 to 2.5 percent vanadium (V), and balance essentially iron (Fe).

6. A welding filler wire, for fusion welding precipitation-hardened austenitic Fe—Mn—Al—C alloys, consisting essentially of, by weight, 23 to 34 percent manganese (Mn), 7.5 to 11.5 percent aluminum (Al), 1.40 to 1.95 percent carbon (C), and at least two of the elements from the group consisting of titanium (Ti), niobium (Nb), vanadium (V), the combined amount being equal to or smaller than 3.0 percent, and balance essentially iron (Fe).

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0042] FIG. 1(a)-(c) TEM micrographs of the as-hot-rolled Fe-28.5Mn-9.0Al-1.55C base material. (a) Bright field image; (b) A SADP, the zone axis is [001] (hkl: austenite; hkl: κ-carbide); (c) (100).sub.K dark field image taken from the same area in (a).

[0043] FIG. 1(d) The macroscale image of the welding bead obtained by GTAW with a Fe-27.8Mn-9.1Al-1.86C welding filler wire.

[0044] FIG. 1(e) SEM image taken from the as-welded weldment (FZ: fusion zone; HAZ: heat-affected zone; BM: base material). The inset shows the enlarged image of the area marked in the figure.

[0045] FIG. 1(f) SEM image and the microhardness indentation conducted across the FZ, HAZ and BM.

[0046] FIG. 1(g) Microhardness values corresponding to the respective measured points in (f).

[0047] FIG. 1(h) TEM bright field image taken from the FZ of the weldment. The solid and hollow arrows indicate the κ-carbides within the austenite dendrite cells and eutectic regions, respectively.

[0048] FIG. 1(i) A SADP taken from the FZ, the zone axis is [001] (hkl: austenite; hkl: κ-carbide).

[0049] FIG. 1(j) TEM-EDS profile obtained from the FZ of the weldment.

[0050] FIG. 1(k) Macroscale images of the tensile specimens before and after tensile test.

[0051] FIG. 2(a) The macroscale image of the welding bead obtained by GMAW with a Fe-28.2Mn-9.2Al-1.72C welding filler wire.

[0052] FIG. 2(b) SEM image taken from the as-welded weldment (FZ: fusion zone; HAZ: heat-affected zone; BM: base material). The inset shows the enlarged image of the area marked in the figure.

[0053] FIG. 2(c) SEM image and the microhardness indentation conducted across the FZ, HAZ and BM.

[0054] FIG. 2(d) Microhardness values corresponding to the respective measured points in (c).

[0055] FIG. 2(e) TEM bright field image taken from the FZ of the weldment. The solid and hollow arrows indicate the κ-carbides within the austenite dendrite cells and eutectic regions, respectively.

[0056] FIG. 2(f) A SADP taken from the FZ, the zone axis is [001] (hkl: austenite; hkl: κ-carbide).

[0057] FIG. 2(g) TEM-EDS profile obtained from the FZ of the weldment.

[0058] FIG. 2(h) Macroscale images of the tensile specimens before and after tensile test.

[0059] FIG. 3(a)-(c) TEM micrographs of the as-hot-rolled Fe-28.8Mn-8.9Al-1.62C base material. (a) Bright field image; (b) A SADP, the zone axis is [001] (hkl: austenite; hkl: κ-carbide); (c) (100).sub.K dark field image taken from the same area in (a).

[0060] FIG. 3(d) SEM image taken from the as-welded weldment obtained by GTAW with a Fe-28.2Mn-10.6Al-1.62C welding filler wire (FZ: fusion zone; HAZ: heat-affected zone; BM: base material).

[0061] FIG. 3(e) SEM image and the microhardness indentation conducted across the FZ, HAZ and BM.

[0062] FIG. 3(f) Microhardness values corresponding to the respective measured points in (e).

[0063] FIG. 3(g) TEM bright field image taken from the FZ of the weldment. The solid and hollow arrows indicate the κ-carbides within the austenite dendrite cells and eutectic regions, respectively.

[0064] FIG. 3(h) A SADP taken from the FZ, the zone axis is [001] (hkl: austenite; hkl: κ-carbide).

[0065] FIG. 3(i) TEM-EDS profile obtained from the FZ of the weldment.

[0066] FIG. 4(a) SEM image taken from the as-welded weldment obtained by GTAW with a Fe-29.5Mn-9.8Al-1.48C welding filler wire (FZ: fusion zone; HAZ: heat-affected zone; BM: base material).

[0067] FIG. 4(b) SEM image and the microhardness indentation conducted across the FZ, HAZ and BM.

[0068] FIG. 4(c) Microhardness values corresponding to the respective measured points in (b).

[0069] FIG. 4(d) TEM bright field image taken from the FZ of the weldment.

[0070] FIG. 4(e) A SADP taken from the FZ, the zone axis is [001] (hkl: austenite; hkl: κ-carbide).

[0071] FIG. 4(f) TEM-EDS profile obtained from the FZ of the weldment.

[0072] FIG. 5(a) SEM image taken from the as-welded wekdment obtained by GTAW with a Fe-33.8Mn-10.6Al-1.38C welding filler wire (FZ: fusion zone; HAZ: heat-affected zone; BM: base material).

[0073] FIG. 5(b) SEM image and the microhardness indentation conducted across the FZ, HAZ and BM.

[0074] FIG. 5(c) Microhardness values corresponding to the respective measured points in (b).

[0075] FIG. 5(d) TEM bright field image taken from the FZ of the weldment.

[0076] FIG. 5(e) A SADP taken from the FZ, the zone axis is [001] (hkl: austenite; hkl: κ-carbide).

[0077] FIG. 5(f) TEM-EDS profile obtained from the FZ of the weldment.

[0078] FIG. 6(a) SEM image taken from the as-welded weldment obtained by GTAW with a Fe-31.8Mn-9.2Al-1.25C welding filler wire (FZ: fusion zone; HAZ: heat-affected zone; BM: base material). The inset shows the enlarged image of the area marked in the figure.

[0079] FIG. 6(b) SEM image and the microhardness indentation conducted across the FZ, HAZ and BM.

[0080] FIG. 6(c) Microhardness values corresponding to the respective measured points in (b).

[0081] FIG. 6(d) Macroscale images of the tensile specimens before and after tensile test.

[0082] FIG. 7(a) The macroscale image of the welding bead obtained by GTAW with a Fe-30.5Mn-8.9Al-2.2C welding filler wire. Notice the solidification crack on the welding bead.

[0083] FIG. 7(b) SEM image taken from the as-welded weldment (FZ: fusion zone; HAZ: heat-affected zone; BM: base material). The inset shows the enlarged image of the area marked in the figure. The arrows indicate the coarse κ-carbides formed on the austenite grain boundaries.

[0084] FIG. 7(c) TEM bright field image taken from the FZ of the weldment.

[0085] FIG. 7(d) A SADP taken from a coarse κ-carbide marked as “K” in (c), the zone axis is (hkl: austenite; hkl: κ-carbide).

[0086] FIG. 7(e) TEM-EDS profile obtained from the coarse κ-carbide.

[0087] FIG. 8(a) The macroscale image of the welding bead obtained by GTAW with a Fe-30.5Mn-12.5Al-1.55C welding filler wire. Notice the solidification crack (indicated by the arrow) on the welding bead.

[0088] FIG. 8(b) SEM image taken from the as-welded weldment (FZ: fusion zone; HAZ: heat-affected zone; BM: base material). The arrows indicate the Al-rich particles (denoted as a) formed on the austenite grain boundaries.

[0089] FIG. 8(c) SEM-EDS profile taken from a discrete Al-rich particle.

[0090] FIG. 9(a) SEM image taken from the as-welded weldment obtained by GTAW with a Fe-20.1Mn-8.5 Al-1.52C welding filler wire (FZ: fusion zone; BM: base material). The arrows indicate the discrete ferrite phase (denoted as a) distributing in FZ.

[0091] FIG. 9(b) TEM bright field image taken from the FZ of the weldment. The discrete ferrite grain is denoted as a and the circle marks the coarse κ-carbide formed on the ferrite/austenite boundary.

[0092] FIG. 9(c) A SADP taken from the area circled in (b) (hkl: austenite; hkl: κ-carbide; (hkl): ferrite).

[0093] FIG. 9(d) TEM-EDS profile obtained from the austenite region.

[0094] FIG. 9(e) TEM-EDS profile obtained from the ferrite region.

[0095] FIG. 10(a)-(c) TEM micrographs of the as-hot-rolled Fe-29.3Mn-9.3Al-1.75C base material. (a) Bright field image; (b) A SADP, the zone axis is [001] (hkl: austenite; hkl: κ-carbide); (c) (100).sub.K dark field image taken from the same area in (a).

[0096] FIG. 10(d) The macroscale image of the welding bead obtained by GTAW with a Fe-28.5Mn-9.3Al-1.82C-1.6Ti welding filler wire.

[0097] FIG. 10(e) SEM image taken from the as-welded weldment (FZ: fusion zone; HAZ: heat-affected zone; BM: base material).

[0098] FIG. 10(f) SEM image and the microhardness indentation conducted across the FZ, HAZ and BM.

[0099] FIG. 10(g) Microhardness values corresponding to the respective measured points in (f).

[0100] FIG. 10(h) TEM bright field image taken from the FZ of the weldment. The arrows indicate the κ-carbides and Ti-rich Ti-carbides within the eutectic regions.

[0101] FIG. 10(i) A SADP taken from the area circled in (h) (hkl: austenite; hkl: κ-carbide; (hkl): Ti-carbide).

[0102] FIG. 10(j) TEM-EDS profile obtained from the same area circled in (h).

[0103] FIG. 10(k) Macroscale images of the tensile specimens before and after tensile test.

[0104] FIG. 11(a) The macroscale image of the welding bead obtained by GMAW with a Fe-29.5Mn-8.2Al-1.56C-1.0Nb welding filler wire.

[0105] FIG. 11(b) SEM image taken from the as-welded weldment (FZ: fusion zone; HAZ: heat-affected zone; BM: base material).

[0106] FIG. 11(c) SEM image and the microhardness indentation conducted across the FZ, HAZ and BM.

[0107] FIG. 11(d) Microhardness values corresponding to the respective measured points in (c).

[0108] FIG. 11(e) TEM bright field image taken from the FZ of the weldment. The arrows indicate the κ-carbides and Nb-rich Nb-carbides within the eutectic regions.

[0109] FIG. 11(f) A SADP taken from the area circled in (e) (hkl: austenite; hkl: κ-carbide; (hkl): Nb-carbide).

[0110] FIG. 11(g) TEM-EDS profile obtained from the same area circled in (e).

[0111] FIG. 11(h) Macroscale images of the tensile specimens before and after tensile test.

[0112] FIG. 12(a) The macroscale image of the welding bead obtained by GTAW with a Fe-31.2Mn-9.8Al-1.65C-1.2V welding filler wire.

[0113] FIG. 12(b) SEM image taken from the as-welded weldment (FZ: fusion zone; HAZ: heat-affected zone; BM: base material).

[0114] FIG. 12(c) SEM image and the microhardness indentation conducted across the FZ, HAZ and BM.

[0115] FIG. 12(d) Microhardness values corresponding to the respective measured points in (c).

[0116] FIG. 12(e) TEM bright field image taken from the FZ of the weldment. The arrows indicate the κ-carbides and V-rich V-carbides within the eutectic regions.

[0117] FIG. 12(f) A SADP taken from the area circled in (e) (hkl: austenite; hkl: κ-carbide; (hkl): V-carbide).

[0118] FIG. 12(g) TEM-EDS profile taken from the same area circled in (e).

[0119] FIG. 12(h) Macroscale images of the tensile specimens before and after tensile test.

[0120] FIG. 13(a) The macroscale image of the welding bead obtained by GTAW with a Fe-30.6Mn-9.2Al-1.88C-0.8Ti-1.0Nb welding filler wire.

[0121] FIG. 13(b) SEM image taken from the as-welded weldment (FZ: fusion zone; HAZ: heat-affected zone; BM: base material).

[0122] FIG. 13(c) SEM image and the microhardness indentation conducted across the FZ, HAZ and BM.

[0123] FIG. 13(d) Microhardness values corresponding to the respective measured points in (c).

[0124] FIG. 13(e) TEM bright field image taken from the FZ of the weldment. The arrows indicate the κ-carbides, Ti-rich Ti-carbides and Nb-rich Nb-carbides within the eutectic regions.

[0125] FIG. 13(f) TEM-EDS profile taken from the area circled in (e).

[0126] FIG. 13(g) Macroscale images of the tensile specimens before and after tensile test.

[0127] FIG. 14(a) SEM image taken from the as-welded weldment obtained by GTAW with a Fe-28.2Mn-10.6Al-1.62C welding filler wire (FZ: fusion zone; HAZ: heat-affected zone; BM: base material). Note that the base material was a Fe-31.5Mn-8.5Al-1.25C alloy after being hot-rolled, solution heat-treated, quenched and then aged at 550° C. for 12 hrs.

[0128] FIG. 14(b) SEM image and the microhardness indentation conducted across the FZ, HAZ and BM.

[0129] FIG. 14(c) Microhardness values corresponding to the respective measured points in (b).

[0130] FIG. 14(d) Macroscale images of the tensile specimens before and after tensile test.

[0131] FIG. 15(a) SEM image taken from the as-welded weldment obtained by GTAW with a Fe-28.2Mn-9.1Al-1.55C-1.8Mo welding filler wire (FZ: fusion zone; HAZ: heat-affected zone; BM: base material). The arrows indicate the coarse Mo-rich Mo-carbides formed on the austenite grain boundaries.

[0132] FIG. 15(b) SEM-EDS profile taken from a coarse Mo-rich Mo-carbide on the austenite grain boundary.

[0133] FIG. 16(a) SEM image taken from the as-welded weldment obtained by GTAW with a Fe-29.3Mn-8.8Al-1.58C-1.5Cr welding filler wire (FZ: fusion zone; HAZ: heat-affected zone; BM: base material). The arrows indicate the coarse Cr-rich Cr-carbides formed on the austenite grain boundaries.

[0134] FIG. 16(b) SEM-EDS profile taken from a coarse Cr-rich Cr-carbide on the austenite grain boundary.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0135] In the following, we give detailed description of the selected preferred embodiments to illustrate the innovative features of the present invention. In the following, unless otherwise specified, the Fe—Mn—Al—C base materials investigated in the present invention were prepared in an atmospheric induction furnace with various compositions. After being homogenized at 1150° C. for 2 hrs under protective argon atmosphere, the ingots were hot-rolled from 80 mm to 8-12 mm-thick plates and then water quenched to room temperature. The as-hot-rolled plates were then machined to form a single V butt for subsequent welding joints with a groove angle of 60°. The welding filler wires were prepared in an atmospheric induction furnace according to the designed compositions. The melt was cast into an 80 mm×80 mm×1500 mm steel mold. The ingots were then heated at 1150° C. for 2 hrs and hot-rolled into coils with diameter ϕ˜5 mm, followed by pickling and cold drawing into welding filler wires with diameter ϕ≈1.2, 2.4 and 3.2 mm, respectively. Fusion welding has been carried out by either GMAW or GTAW process using pure argon or the mixture of Ar+He gases as the shielding gas. The typical flow rates of the shielding gas were about ˜10 and ˜18 liters/min for GTAW and GMAW, respectively. The welding filler wire was fed at speed of ˜200 mm/min for GMAW process. The voltage and current used for the GMAW were 22˜26 V and 140˜170 A, respectively. For GTAW, depending on the diameter of the welding filler wire used, the voltage and current used were 15˜20 V and 125˜200 A, respectively. In all fusion welding conducted in the embodiment Examples, the root opening was kept at ˜1 mm. The microstructures of the weldment were analyzed by using optical microscope (OM), scanning electron microscope (SEM) and transmission electron microscope (TEM), respectively. The SEM specimens were prepared through mechanical polishing prior to etching with 5% nitric acid. For the TEM examinations, thin foil specimens were prepared using a twin jet electro-polisher with an electrolyte of 60% acetic acid, 30% ethanol and 10% perchloric acid. Energy dispersive spectrosmeter (EDS) attached to SEM or TEM was used for compositional analyses when needed. It is noted that quantitative EDS analyses are not reliable for elements with atomic number less than 10 (such as carbon) and thus are often ignored. The tensile test specimens were prepared according to ASTM E8 standard having a gauge length of 25 mm, a gauge width of 6.25 mm and a thickness of 4 mm. Tensile tests were carried out at room-temperature with an Instron 8501 tensile testing machine at a strain rate of 6.7×10.sup.−4 s.sup.−1. The YS was measured at 0.2% offset strain. Vickers microhardness measurements were performed to characterize the hardness in different regions, namely the fusion zone (FZ), heat-affected zone (HAZ) and base material (BM), of the weldment. The applied load of the Vickers tests was 100 gf with a loading duration equal to 15 s.

EXAMPLE 1

[0136] FIG. 1(a) is the TEM bright field (BF) image of an as-hot-rolled Fe-28.5Mn-9.0Al-1.55C base material, showing a high-density of nano-sized (˜3-5 nm) precipitates uniformly distributing within the matrix. Also noted that, as indicated by the arrows shown in FIG. 1(a), the precipitates existing on the dislocations are slightly larger in size (˜5-8 nm), suggesting that these precipitates were formed during the hot-rolling process. FIG. 1(b), the selected-area diffraction pattern (SADP) of the as-hot-rolled base material, demonstrates that the high-density of nano-sized precipitates are (Fe,Mn).sub.3AlC carbides (κ-carbides) having an L′1.sub.2-structure. FIG. 1(c) shows the (100).sub.K dark field (DF) image of the same area as displayed in FIG. 1(a) to illustrate the presence of the κ-carbides within the austenite matrix and on the dislocations. It is clear that the as-hot-rolled microstructure of the base material used in the present embodiment is single-phase austenite with uniformly distributed high-density of nano-sized κ-carbides. The tensile test revealed that the YS, UTS, and El of the as-hot-rolled base material are 952 MPa, 1100 MPa, and 56%, respectively.

[0137] Two plates of the as-hot-rolled base material with dimensions of 80 mm×80 mm×8 mm were machined to form a single V-groove butt weld. In the present Example the nominal composition of the welding filler wire was Fe-27.8Mn-9.1Al-1.86C with a wire diameter ϕ˜2.4 mm. The fusion welding was carried out using GTAW process with pure Ar as the shielding gas. FIG. 1(d) is the macroscale image of the welding bead, showing that there is no any visible macroscopic solidification crack and porosity in the fusion zone (FZ) of the as-welded sample.

[0138] FIG. 1(e) shows the typical SEM image of an area covering the FZ, HAZ and BM of the as-welded sample. As indicated in the SEM image, three distinctive regions representing the regions of FZ, HAZ, and BM are readily identified. Several features distinct from that reported in the prior art concerning fusion welding the precipitation-hardened Fe—Mn—Al—C alloys (with C≤1.29 wt. % as fusion welding filler) can be immediately noted. (i) It is evident that the FZ exhibits the typical columnar austenite grains composed of austenite dendrites and eutectic regions. More significantly, there exist a high-density of nano-sized κ-carbides within the austenite dendrite cells and eutectic regions. This is one of the striking features disclosed in the present invention for the first time. In the prior art reporting the fusion welded Fe—Mn—Al—C alloys with C≤1.29 wt. %, there was no precipitate within either the primary or secondary austenite dendrite cells being observed, except for a small amount of eutectic κ-carbides existing within the eutectic regions. Moreover, in the present Example, the amount of the nano-sized κ-carbides existing within the eutectic regions is much more than that observed in previous reports for C≤1.29 wt. %. (ii) From FIG. 1(e), it is evident that there is no apparent lengthy primary dendrites in the columnar austenite grains. The length and spacing of the austenite dendrite cells formed within the columnar austenite grains are only in the order of ˜20-30 μm and ˜5-10 μm, respectively. Obviously, the austenite dendrite cells in the present Example is substantially “refined”. This is quite different from that ubiquitously observed in the prior art or conventional fusion welding, wherein the microstructure of the as-welded bead was always composed of apparent primary dendrites with length extending over several hundred micrometers (i.e. >300 μm). The reasons for these differences might be explained as followings. As indicated in the enlarged image of the marked area shown on the upper right corner of FIG. 1(e), it is clearly seen that, in addition to the fine eutectic κ-carbides formed between austenite dendrites, there are precipitates existing at the tip of each austenite dendrite cell. Since during solidification after fusion welding, the stability of the solid-liquid interface is mostly determined by the thermal and constitutional supercooling conditions existing in the immediate vicinity of the interface, the dendrite size in a welding bead is strongly dependent on the cooling rate and alloying compositions. In the present case, it appears that the presence of precipitates at the tip of austenite dendrite cells due to constitutional supercooling may have decelerated the solidification front and effectively retard the growth of dendrite cells, which, in turn, results in the much shorter dendrite cells revealed in FIG. 1(e). As a result, the composition of the welding filler may be the more essential factor responsible for the short and narrow dendritic structure observed in the present Example. (iii) The FZ in the present Example is fully austenitic, whereas in the prior art the solidified microstructure after autogenous fusion welding always contained some amount of ferrite phase even if their base materials were fully austenitic before welding. In addition, FIG. 1(e) also indicates that no obvious microstructural changes are observable in HAZ and BM regions and there is no discernible difference in terms of the size and density of the κ-carbides in FZ, HAZ and BM of the present Example. As a result, there is no softening in the HAZ. Moreover, it is noted that, within the FZ and near the interface between the FZ and HAZ, there is no trace of microcrack and porosity can be observed, indicating that the use of the fusion filler disclosed in the present invention has evidently eliminated the solidification and liquation cracks commonly encountered in fusion welded precipitation-hardened alloys. FIG. 1(f) shows the microhardness measurements conducted across the FZ, HAZ and BM. The corresponding values of respective measured hardness points are displayed in FIG. 1(g). As can be seen in FIG. 1(g), the average microhardness of FZ (˜425 Hv) is in fact slightly larger than that of HAZ (˜417 Hv) and BM (˜412 Hv). This is in sharp contrast to the conventional wisdom that the FZ is always the weakest region after fusion welding. It is worth mentioning here that the microstructure of the BM used in the present Example, in the as-hot-rolled state, is fully austenitic with a high-density of nano-sized κ-carbides uniformly distributing within the austenite matrix and the microhardness of the BM is substantially larger than that of the optimally aged Fe—Mn—Al—C alloys with C≤1.20 wt. % (350˜400 Hv), as quoted in the Background section.

[0139] In order to fully comprehend the primary reasons giving rise to these unprecedented results, a more detailed analysis on the FZ microstructure is indispensable. TEM examinations indicated that in the present Example the matrix of FZ is fully austenitic and both the nano-sized precipitates within the austenite dendrite cells and the eutectic regions are κ-carbides. An example is shown in FIG. 1(h), which is the BF electron micrograph taken from the FZ. It clearly indicates that the sizes of the κ-carbides within the austenite dendrite cells (indicated by black arrow) and the associated eutectic regions (indicated by the white arrow) are on the order of 3˜5 nm and 6˜10 nm, respectively, and the length of the austenite dendrite cells is on the order of about 100-300 nm. This indicates that the alloy design of the present welding filler has effectively suppressed the progress speed of the dendrite growth front during the solidification process after fusion welding. The SADP shown in FIG. 1(i) confirms that only the austenite phase and κ-carbides are existent in the FZ of the weldment. Moreover, as revealed by the TEM-EDS profile taken from FZ shown in FIG. 1(j), the compositions of Fe, Mn, and Al in the FZ are about 64.3%, 26.7% and 9.0%, respectively.

[0140] Tensile test indicates that the weldment obtained by using the welding filler disclosed in the present Example exhibited remarkable ductile deformation behavior, with the YS, UTS and El being about 946 MPa, 1086 MPa and 44%, respectively. FIG. 1(k) shows the macroscale images of the specimens before and after tensile test. It is evident that, the entire weldment exhibits typical characteristics of ductile plastic deformation. In particular, the FZ region also exhibits typical features of ductile deformation with corrugated surface and substantial amount of elongation. Since the tensile specimen contains regions (i.e. FZ and BM) with potentially different mechanical properties, it is generally very difficult to infer the obtained YS to FZ or BM directly. Nevertheless, by judging from the width variations in the respective regions of the tensile-fractured specimen, one may be able to differentiate the relative magnitude of YS between FZ and BM. For instance, if the BM is having higher YS, when the tensile stress exceeds the YS of FZ but still lower than that of BM, then the FZ would be the first to exhibit plastic deformation (i.e. become elongated and thinned) and show a width reduction, while the BM being still in the elastic regime the width in the BM region would remain unchanged, and vice versa. As a consequence, when there is a noticeable difference between the YS of FZ and BM, the tensile-fractured specimen will show some width variations in the respective regions and the specimen edges will not be parallel. On the contrast, if the width of respective regions in the tensile-fractured specimen remains approximately the same and sample edges are essentially parallel, it is plausible to reason that both FZ and BM are having nearly the same magnitude of YS. The fact that the widths across the region containing the BM, HAZ and FZ (denoted as d.sub.BM, d.sub.INT and d.sub.FZ, in FIG. 1(k)) are essentially equal and the specimen edges across this region remains parallel indicates that the FZ and BM of the present tensile specimen are having approximately the same YS level. It is worthwhile to emphasize here that the extraordinary YS exhibited in the FZ of the present Example is, in fact, quite expectable. It is well known that the existence of a high-density of nano-sized κ-carbides would drastically enhance the YS of the material without significant loss in ductility, which is also the main reason responsible for the excellent combination of YS (or hardness) and El exhibited in most precipitation-hardened alloys. This is exactly what is witnessed in FIG. 1(h). On the other hand, it is also evident from FIG. 1(k) that the necking and eventual fracturing occurred in the opposite region of the BM (indicated by the white arrow), indicating that UTS of FZ is larger than that of BM, which may be also consistent with the slightly lower hardness in BM region depicted in FIG. 1(g).

[0141] Apparently, the existence of the high-density of nano-sized κ-carbides within the austenite dendrite cells should be the primary reason for the high-hardness and high-strength (especially YS) while maintaining high-ductility obtained in the FZ of the present Example. The obtained FZ microstructure described in the present Example undoubtedly is the most unique and unprecedented features resulted from the novel composition design of the welding filler wires disclosed in the present invention.

EXAMPLE 2

[0142] The purpose of the present Example attempts to clarify the effects of altering the carbon content in the welding filler wire on the characteristics of FZ in the as-welded sample. The base material used in this Example was the same as that used in Example 1. However, the GMAW welding process was employed in this Example. The dimensions of the BM plates were 80 mm×80 mm×12 mm, which were machined to form a single V-groove butt weld. The GMAW welding process was carried out with a voltage of 26 V and current of 140˜170 A. The flow rate of the shielding gas (25% Ar+75% He) was ˜18 liters/min and the welding filler wire feeding speed of was ˜200 mm/min, respectively. The nominal composition of the welding filler wire used in the present Example was Fe-28.2Mn-9.2Al-1.72C with a wire diameter ϕ˜1.2 mm.

[0143] FIG. 2(a) shows the macroscale image of the GMAW welding bead. It can be seen from FIG. 2(a) that the bead appears to have a very smooth morphology with no visible macrocrack and porosity appearing in the entire welding bead. FIG. 2(b) shows the SEM image of an area covering the FZ, HAZ, and BM of the welded sample. Similar to those revealed in Example 1, the FZ is composed of typical columnar austenite grains and there are a high-density of nano-sized κ-carbides existing within the austenite dendrite cells and eutectic regions. As indicated by the arrow shown in FIG. 2(b) and the enlarged image displayed on the upper right corner of FIG. 2(b), in addition to the fine eutectic κ-carbides formed within the eutectic regions, there also κ-carbides existing at the tip of each austenite dendrite cell. This indicates that the FZ microstructure does have very similar features to that observed in Example 1. Moreover, it is noted that, within the FZ and near the interface between the FZ and HAZ, there is no trace of microcrack and porosity can be observed. FIG. 2(b) also reveals that, similar to Example 1, the fusion welding process seemingly didn't cause the dissolution and significant coarsening of the κ-carbides in HAZ in the present Example.

[0144] FIG. 2(c) shows the Vickers microhardness measurements conducted across the FZ, HAZ and BM. The corresponding values of the respective measured hardness points are displayed in FIG. 2(d). The average microhardness of FZ, HAZ and BM are ˜410 Hv, ˜412 Hv and ˜413 Hv, respectively. Apparently, the microhardness of FZ and HAZ are comparable to that of BM, indicating that there is no significant softening in FZ and HAZ, which is consistent with the unique microstructure displayed in FIG. 2(b), wherein the most prominent strengthening ingredient of high-density nano-sized κ-carbides remains essentially intact in all three zones after fusion welding.

[0145] Transmission electron microscopy examinations of FZ indicated that significant amount of nano-sized κ-carbides were formed within the austenite dendrite cells and the eutectic regions. A typical example is shown in FIG. 2(e). In this TEM BF image, it is clearly seen that there is a high-density of nano-sized κ-carbides (˜3-5 nm) distributed within austenite dendrite cells (indicated by the black arrows) and eutectic regions (indicated by the white arrows). Comparing with the results described in Example 1 (FIG. 1(h)), the density of κ-carbides within the austenite dendrite cells and eutectic regions is slightly decreased. FIG. 2(f) is the SADP taken from FIG. 2(e), confirming that the FZ matrix is single austenite and the precipitates existing within both the austenite dendrite cells and the eutectic regions are κ-carbides having an ordered L′1.sub.2 structure. FIG. 2(g) is the TEM-EDS profile taken from the FZ, clearly indicating that the compositions of Fe, Mn and Al in FZ are about 63.4 wt. %, 27.5 wt. % and 9.1 wt. %, respectively.

[0146] Tensile test indicates that the weldment obtained by using the welding filler wire disclosed in the present Example also exhibited remarkable ductile deformation behavior, with the YS, UTS and El being about ˜942 MPa, ˜1075 MPa and ˜36%, respectively. FIG. 2(h) shows the macroscale images of the specimens before and after tensile test. It is evident that, the entire weldment exhibits typical characteristics of ductile plastic deformation. In particular, the zig-zag weaving fracture pattern and corrugated fracture surface appearing in the FZ is indicative of ductile deformation characteristics. It is also interesting to observe that, like in Example 1, the widths across the region containing the BM, FZ and the interface between them (denoted as d.sub.BM, d.sub.FZ and d.sub.INT, in FIG. 2(h)) are essentially equal and the specimen edges across this region remains parallel indicating that the FZ and BM of the present tensile specimen are having approximately the same YS level. The main reasons for the FZ to have such high YS is the same as those described in Example 1. However, in this case, unlike that observed in Example 1, slight necking and fracture occurred in FZ instead of in BM, indicating that the FZ has slightly lower UTS than BM. This is, in fact, quite consistent with the slightly lower microhardness values in FZ (˜410 Hv) comparing with that in BM (˜413 Hv). Based on the results presented in Example 1 and Example 2, it is evident that, with the composition design of the welding fillers disclosed in the present invention, the obtained as-welded samples, even after re-melting, alloying element redistribution and solidification during fusion welding, are evidently having excellent ductility with remarkable YS and microhardness.

EXAMPLE 3

[0147] In this Example, we investigated the effects of a slightly lower carbon content on the characteristics FZ in the as-welded sample. An as-hot-rolled base material with nominal composition of Fe-28.8Mn-8.9Al-1.62C was used in the present Example of embodiment. FIG. 3(a) is the TEM BF image of the hot-rolled base material. It is evident in FIG. 3(a) that the as-hot-rolled microstructure of BM used in the present Example is quite similar to that used in Example 1 and Example 2. Namely, there is a high-density of nano-sized (˜3-5 nm) precipitates uniformly distributing within the matrix and on the dislocations (as indicated by the arrows). FIG. 3(b) is the selected-area diffraction pattern (SADP) of the as-hot-rolled base material, which evidently confirms that the matrix of the base material is fully austenitic and the high-density nano-sized precipitates are the ordered L′1.sub.2-structured κ-carbides. FIG. 3(c) is the (100).sub.K DF image taken from the same area as displayed in FIG. 3(a), revealing the presence of the high-density nano-sized κ-carbides. TEM investigations showed that the as-hot-rolled microstructure of the base material used in the present Example is single-phase austenite with uniformly distributed high-density nano-sized κ-carbides. The tensile test revealed that the YS, UTS, and El of the as-hot-rolled base material are 975 MPa, 1152 MPa, and 50%, respectively.

[0148] Two plates of the as-hot-rolled base material with the dimensions 80 mm×80 mm×8 mm were machined to form a single V-groove butt weld. The nominal composition of welding filler wire was Fe-28.2Mn-10.6Al-1.62C with a wire diameter ϕ˜2.4 mm. The GTAW welding parameters were similar to those used in Example 1. FIG. 3(d) shows the typical SEM image covering the FZ, HAZ, and BM of the as-welded sample. Similar to that seen in Example 1 and Example 2, the FZ exhibits typical columnar austenite grains composed of austenite dendrite cells and eutectic regions. The genuine feature of a high-density of nano-sized κ-carbides distributed within the austenite dendrite cells and eutectic regions can also be observed. Nevertheless, comparing to Example 1 (FIG. 1(e)) and Example 2 (FIG. 2(b) the amount of nano-sized κ-carbides appears to be slightly reduced, presumably due to the lower carbon content in the welding filler wire used in the present Example. Moreover, it is noted that, within the FZ and near the interface between the FZ and HAZ, there is no trace of microcrack and porosity can be observed. Also, the density of the nano-sized κ-carbides originally existing in HAZ and BM apparently was not influenced during the welding process.

[0149] FIG. 3(e) shows the Vickers microhardness measurements conducted across the FZ, HAZ and BM. The corresponding values of the respective measured hardness points are displayed in FIG. 3(f), which reveals that the average microhardness of FZ, HAZ and BM is about 402 Hv, 417 Hv and 420 Hv, respectively. Apparently, there is negligible softening in FZ. It is worthwhile to note that in the present Example, the microhardness of FZ is still considerably larger than that of the optimally aged Fe—Mn—Al—C alloys with C≤1.2 wt. % (350˜400 Hv), as quoted in the Background section

[0150] FIG. 3(g) is the TEM BF image taken from FZ showing that the density of the nano-sized κ-carbides is decreased slightly as compared to that seen in Example 1 (FIG. 1(h)) and Example 2 (FIG. 2(e)). The SADP shown in FIG. 3(h) confirms that the microstructure of FZ is composed of austenite and κ-carbides. FIG. 3(i) is the TEM-EDS profile taken from the FZ, which shows that the compositions of Fe, Mn and Al in FZ are about 61.9%, 27.6% and 10.5%, respectively. The tensile test of the present as-welded sample showed that the tensile-fractured specimen exhibited substantial amount of plastic deformation in the FZ and the necking and fracture occurred mainly in FZ. On the other hand, the BM exhibited a relatively small amount of deformation. This might be due to the considerably lower microhardness value in the FZ (˜402 Hv) comparing with that in BM (˜420 Hv). As a result, despite the marked ductile deformation in FZ, the total elongation was slightly decreased as compared to the previous Examples. The YS, UTS and El of weldment of the present as-welded sample are ˜916 MPa, ˜1035 MPa and ˜33%, respectively.

[0151] From the above results, it is evident that the main features of microstructure and the resultant mechanical properties in the weldment of the present Example are very similar to that seen in Example 1 and Example 2.

EXAMPLE 4

[0152] In the present Example, the base material used was the same as that used in Example 3. The dimensions of the BM plates used in the present Example were 80 mm×80 mm×8 mm, which were machined to form a single V-groove butt weld. The nominal composition of the welding filler wire was Fe-29.5Mn-9.8Al-1.48C with a wire diameter ϕ˜2.4 mm. The fusion welding was carried out using the GTAW process with the pure Ar as the shielding gas and the welding parameters were similar to those used in Example 1.

[0153] FIG. 4(a) shows the typical SEM image covering the FZ, HAZ, and BM of the as-welded sample. Obviously, the FZ microstructure is very similar to that seen in the previous Examples 1-3. Namely, typical columnar austenite grains consist of austenite dendrite cells and eutectic regions. The unique feature of having nano-sized κ-carbides densely distributed within the austenite dendrite cells and eutectic regions is still observed. Nevertheless, due to the further reduction of carbon content in the welding filler used in the present Example, the amount of nano-sized κ-carbides distributed within the austenite dendrite cells and eutectic regions appears to be slightly reduced. Moreover, it is noted that, within the FZ and near the interface between the FZ and HAZ, there is no trace of microcrack and porosity can be observed. Also, the density of the nano-sized κ-carbides originally existing in HAZ and BM apparently was not influenced during the fusion welding process. FIG. 4(b) shows the Vickers microhardness measurements conducted across the FZ, HAZ and BM. The corresponding values of the respective measured hardness points are displayed in FIG. 4(c), which reveals that the average microhardness of FZ, HAZ and BM is about 385 Hv, 414 Hv, and 419 Hv, respectively. The lowering of the microhardness in FZ is presumably due to the lower carbon content of the welding filler used in the present Example. It is noted that, like that seen in previous Examples, there is no apparent softening originated from fusion welding.

[0154] FIG. 4(d) is the TEM BF image taken from the FZ, revealing the presence of nano-sized κ-carbides existing within the austenite dendrite cells and eutectic regions. However, it is evident that the density of κ-carbides within the austenite dendrite cells and eutectic regions is slightly lowered as compared to that seen in the previous Examples 1-3. FIG. 4(e) shows the SADP taken from FZ, which confirms that the microstructure of FZ is indeed composed of austenite and κ-carbides. FIG. 4(f) is the TEM-EDS profile taken from the FZ, which indicates that the compositions of Fe, Mn and Al in FZ are about 61.7%, 28.8% and 9.5%, respectively. The tensile test indicated that the YS, UTS and El of the weldment of the present Example were ˜875 MPa, ˜1012 MPa and ˜29.8%, respectively. A closer inspection showed that the tensile-fractured specimen also exhibited typical characteristics of ductile plastic deformation in FZ. However, due to the comparatively larger microhardness difference between the FZ (˜385 Hv) and BM (˜419 Hv) (FIG. 4(c)), the deformation has been mostly taking place in FZ, while the HAZ and BM regions exhibited a relatively small amount of deformation, resulting in an overall reduction of total elongation. Nevertheless, severe necking and corrugated free surface as well as the meandering fracture pattern observed in FZ after tensile test indicates the good ductility of the welding bead.

[0155] It is worthwhile to note here that the value of FZ microhardness (˜385 Hv) obtained in the present Example is comparable with that (350˜400 Hv) obtained in the optimally aged precipitation-hardened Fe—Mn—Al—C alloys with C1.2 wt. % as quoted in Background section. From the above SEM and TEM results, it is evident that, with the designed composition, the welding filler wire used in the present Example still preserves most of the main microstructural features in FZ, namely, high-density of nano-sized κ-carbides within the austenite dendrite cells and eutectic regions. Accordingly, it is reasonable to expect that the FZ should have outstanding combination of YS and ductility resulted from the innovative welding filler wire disclosed in the present invention. Indeed, the YS (˜875 MPa) and El (˜29.8%) obtained from the weldment of the present example are comparable with those obtained in the optimally aged precipitation-hardened Fe—Mn—Al—C alloys with C≤1.2 wt. % (YS: 680˜990 MPa and El: 55˜26%).

EXAMPLE 5

[0156] In the present Example, the base material used was the same as that used in Example 1. The dimensions of the base material plates used in the present Example were 80 mm×80 mm×8 mm. Two plates of base material were machined to form a single V-groove butt weld. The nominal composition of the welding filler wire used in the present Example was Fe-33.8Mn-10.6Al-1.38C with a wire diameter ϕ˜2.4 mm. The GTAW process was conducted with the parameters similar to those used in Example 1 and 75% Ar+25% He gas mixture was used as the shielding gas.

[0157] FIG. 5(a) is the SEM image, revealing the microstructure covering the FZ, HAZ and BM regions of the as-welded sample. Similar to previous Examples 1-4, the FZ is composed of typical columnar austenite grains and the unique feature of substantial amount of nano-sized κ-carbides uniformly distributed within the austenite dendrite cells and eutectic regions can still be observed. However, the density of nano-sized κ-carbides was considerably reduced. On the other hand, the density of the nano-sized κ-carbides originally existing in HAZ and BM apparently was not influenced during the fusion welding process. Moreover, it is noted that, within the FZ and near the interface between the FZ and HZ, there is no trace of microcrack and porosity can be observed. FIG. 5(b) shows the Vickers microhardness measurements conducted across the FZ, HAZ and BM. The corresponding values of the respective measured hardness points are displayed in FIG. 5(c), which reveals that the average microhardness values of FZ, HAZ and BM are about 369 Hv, 385 Hv, and 412 Hv, respectively. The lowering of the microhardness in FZ is presumably due to the lower carbon content of the welding filler wire used in the present Example, which evidently leads to further reduction in the density of nano-sized κ-carbides within the austenite dendrite cells and eutectic regions.

[0158] FIG. 5(d) is the TEM BF image taken from the FZ, revealing the presence of nano-sized κ-carbides existing within the austenite dendrite cells and the eutectic regions. It is evident that the density of κ-carbides within the austenite dendrite cells and eutectic regions is substantially reduced as compared to that seen in previous Examples 1-4. FIG. 5(e) shows the SADP taken from FZ, which again confirms that the microstructure of FZ is indeed composed of austenite and κ-carbides. FIG. 5(f) is the TEM-EDS profile taken from the FZ, which shows that the compositions of Fe, Mn and Al in FZ are about 56.6%, 33.1% and 10.3%, respectively.

[0159] The tensile test indicated that the YS, UTS and El of the weldment of the present Example were ˜725 MPa, ˜1005 MPa and ˜23.8%, respectively. A closer inspection of the tensile-fractured specimen revealed that the FZ region exhibited pronounced ductile plastic deformation behavior. However, due to the larger microhardness difference between the FZ (˜369 Hv) and BM (˜412 Hv) (FIG. 5(c)), the tensile-fractured specimen showed that the deformation was taking place mainly in FZ, and the HAZ and BM regions exhibited only slightly deformation, leading to a considerable reduction in total elongation.

[0160] From the above results, it is evident that with the designed composition the welding filler wire used in the present Example still preserves most of the unique microstructural features in FZ disclosed in the present invention. Moreover, the resultant microhardness in FZ (˜369 Hv) is still comparable to those obtained (˜350-400 Hv) in optimally aged precipitation-hardened Fe—Mn—Al—C alloys with C≤1.2 wt. %. As mentioned in Example 4, with the high similarity in the microstructure and resultant microhardness, the FZ of the present Example is expected to have a satisfactory combination of YS and ductility, as well. It is worthwhile to emphasize here the unique microstructural features of the base materials used in the embodiment Examples 1-5 of the present invention. Namely, in the as-hot-rolled state, the base material microstructure is already composed of full austenite with a high-density of nano-sized κ-carbides uniformly distributing within the austenitic matrix. The density of the nano-sized κ-carbides is even much higher than that obtained in optimally aged precipitation-hardened Fe—Mn—Al—C alloys with C≤1.2 wt. %. As a result, the microhardness of the BMs (˜412-420 Hv) used in Examples 1-5 was all significantly larger than those obtained (˜350-400 Hv) in the optimally aged precipitation-hardened Fe—Mn—Al—C alloys with C≤1.2 wt. %.

EXAMPLE 6

[0161] The purpose of the present Example attempts to clarify the effects of further lowering the carbon content in the welding filler wire on the characteristics of FZ in the as-welded sample. The base material used was the same as that used in Example 1. The dimensions of the BM plates were 80 mm×80 mm×8 mm, which were machined to form a single V-groove butt weld. The GTAW process was conducted with the parameters similar to those used in Example 1. The nominal composition of the welding filler wire used in the present Example was Fe-31.8Mn-9.2Al-1.25C with a wire diameter ϕ˜2.4 mm.

[0162] FIG. 6(a) shows the typical SEM image of an area covering the FZ, HAZ and BM of the as-welded sample. The FZ microstructure clearly reveals several features that are very distinct from those seen in Examples 1-5 described above. Firstly, the matrix is still fully austenitic containing austenite dendrite cells and eutectic regions. However, there is no κ-carbide distributing within the austenite dendrite cells and the amount of the κ-carbides in the eutectic regions is substantially reduced. To have a better view of this feature, an enlarged image of the marked area (indicated by the arrow) is inserted on the upper right corner of FIG. 6(a). This feature is quite different from the microstructures described in Examples 1-5. In fact, it is very similar to that observed previously by Chou and Lee in the autogenous fusion welding of Fe—Mn—Al—C alloys with C≤1.29 wt. %, namely, no κ-carbides distributing within the austenite dendrite cells, as quoted in the Background section.

[0163] FIG. 6(b) shows the Vickers microhardness measurements conducted across the regions of BM, HAZ, and FZ. The corresponding values of respective measured hardness points are shown in FIG. 6(c). It is evident from both figures that the microhardness in HAZ and BM is ˜412 Hv, however, the microhardness in FZ has dropped precipitously to only about 242 Hv. This value of microhardness is very close to the values of 210-230 Hv for the C≤1.2 wt. % precipitation-hardened austenitic Fe—Mn—Al—C alloys in their SHT and as-quenched state, as quoted in Background section. It is believed that the absence of κ-carbides within the austenite dendrite cells and the substantial reduction of κ-carbides within the eutectic regions are the primary reasons responsible for the drastic reduction in FZ microhardness.

[0164] FIG. 6(d) shows the macroscale images of specimens before and after the tensile test. The results indicate that the YS, UTS, and El of the weldment are about 462 MPa, 938 MPa and 14%, respectively. Obviously, both the YS and elongation of the weldment obtained from the present Example are far from satisfactory. The main reason for the significant reduction in elongation might have been due to the fact that the microhardness of FZ (˜242 Hv) is much smaller than that of HAZ and BM (˜412 Hv). As a result, during the tensile test the deformation of the entire weldment is essentially localized in the fusion zone, while the HAZ and BM remained almost undeformed, leading to a substantial reduction in elongation. It can also be observed in FIG. 6(d) that the fracturing crack appears to initiate at the interface between FZ and HAZ (as indicated by the arrow) and then penetrating the FZ transversely with a meandering zig-zag fracture line. The estimated elongation within the FZ is about 27%. The fact that the microhardness is only about 242 Hv and the localized deformation, initiation of necking and subsequent fracturing are all occurred in the FZ, suggests that the strength of FZ is considerably lower than that of the HAZ and BM. The primary reason is presumably due to the absence of high-density of κ-carbides distributing within the austenite dendrite cells and the substantial reduction in the amount of κ-carbides within eutectic regions. It seems that welding filler wires with 1.25 wt. % carbon content appear to be inadequate for promoting the formation of nano-sized κ-carbides within the austenite dendrite cells and eutectic regions during solidification, which is the most unique feature disclosed in the present invention.

EXAMPLE 7

[0165] The aim of this Example is to investigate the effects of higher carbon content in the welding filler wire on the characteristics of FZ in the as-welded sample. The base material used in the present Example was the same as that used in Example 3. The dimensions of the BM plates were 80 mm×80 mm×10 mm, which were machined to form a single V-groove butt weld. The GTAW process was conducted with parameters similar to those used in Example 1. The nominal composition of the welding filler wire used in the present Example was Fe-30.5Mn-8.9Al-2.2C with a wire diameter ϕ˜2.4 mm.

[0166] FIG. 7(a) shows the macroscale image of the welding bead, clearly revealing a macrocrack transpierced through the welding bead. Apparently, the higher carbon content in the welding filler wire had led to severe solidification hot cracking effect. FIG. 7(b) shows the SEM image of an area covering the FZ, HAZ, and BM of the as-welded sample. It is clear that the FZ is mainly composed of typical columnar austenite grains and there are high-density of nano-sized κ-carbides existing within the austenite dendrite cells and eutectic regions. This feature is similar to that observed in Examples 1-5. However, some μm-sized coarse carbides can be observed on the grain boundaries (as indicated by the arrows in FIG. 7(b)). An enlarged image of the marked area is displayed on the upper right corner of FIG. 7(b), which clearly reveals that there exist precipitation-free zones nearby the coarse carbides formed on the grain boundaries. Both the coarse grain boundary precipitates and the associated precipitation-free zones are well-known to have detrimental effects on the mechanical properties, especially the ductility. Moreover, FIG. 7(b) also reveals that the density of the nano-sized κ-carbides originally existing in HAZ and BM apparently was not affected noticeably during the fusion welding process.

[0167] FIG. 7(c) is the TEM BF image taken from the FZ, clearly showing that, in addition to the high-density of nano-sized κ-carbides, there are some μm-sized coarse precipitates (marked as K) existing on the austenite grain boundary. Moreover, there are apparent precipitation-free zones in the vicinity of the coarse precipitates. FIG. 7(d) is the SADP taken from a coarse grain boundary precipitate (marked as K), indicating that these grain boundary coarse precipitates are the L′1.sub.2-structured κ-carbides. The structure is the same as that of the nano-sized κ-carbides distributing within the austenite dendrites cells and eutectic regions. FIG. 7(e), the typical TEM-EDS profile of a grain boundary coarse κ-carbide indicates that the compositions of Fe, Mn and Al in the coarse κ-carbide are 56.7%, 34.2% and 9.1%, respectively.

[0168] Based on the above observations, it is clear that higher carbon content (i.e. 2.2 wt. %) in the welding filler wire, although can result in high-density of nano-sized κ-carbides existing within the austenite dendrite cells and eutectic regions, but also lead to some coarser κ-carbides appearing on the grain boundaries. The grain boundary coarse κ-carbides and their associated precipitation-free zones not only are expected to cause some detrimental effects, such as ductility, on the weldment, but also have resulted in severe solidification hot cracking effect in the welding bead, as shown in FIG. 7(a).

EXAMPLE 8

[0169] In this Example, we set to illustrate the effect of higher Al content in the welding filler wire on the characteristics of FZ in the as-welded sample. The base material used in the present Example was the same as that used in Example 1. Two plates of BM with the dimensions of 80 mm×80 mm×8 mm were machined to form single V-groove butt weld. The GTAW process was conducted with the parameters similar to those used in Example 1. The nominal composition of the welding filler wire was Fe-30.5Mn-12.5Al-1.55C with a wire diameter ϕ˜2.4 mm.

[0170] Preliminary inspections on the weldment revealed that there was solidification hot cracking appearing on part of the welding bead, as indicated by the arrow in FIG. 8(a). The SEM image shown in FIG. 8(b) indicates that the FZ microstructure contains mainly the typical columnar austenite grains composed of austenite dendrite cells and eutectic regions. Similar to those observed in Examples 1-5, there are high-density of nano-sized κ-carbides existing within the austenite dendrite cells and eutectic regions. However, in addition to the abovementioned features, some discrete particles can be observed on the austenite grain boundaries, as indicated by the arrows and marked with symbol a in FIG. 8(b). FIG. 8(c), the SEM-EDS profile taken from a discrete particle indicates that the compositions of Fe, Mn and Al are 52.3%, 34.2% and 13.5%, respectively. It is evident that the Al concentration in the discrete particle is quite high up to 13.5 wt. %. This indicates that Al-rich particles would form on the austenite grain boundaries during welding process. It has been well established that the existence of the Al-rich secondary phase on the austenite grain boundaries could cause drastic deterioration in ductility of the Fe—Mn—Al—C alloys. Thus, it appears that excessive Al content in the welding filler wire not only leads to the formation of solidification crack during welding process but also results in the formation of detrimental Al-rich phases on the austenite grain boundaries.

EXAMPLE 9

[0171] The main purpose of this Example is to examine the effects of Mn content in the welding filler wire on the characteristics of FZ in the as-welded sample. The base material used was the same as that used in Example 1. The dimensions of the BM plates were 80 mm×80 mm×8 mm, which were machined to form a single V-groove butt weld. The GTAW welding process was carried out using the parameters similar to those used in Example 1. The nominal composition of the welding filler wire used in the present Example was Fe-20.1Mn-8.5Al-1.52C with a wire diameter ϕ˜3.2 mm.

[0172] FIG. 9(a) shows the SEM image of an area covering the FZ and BM of the as-welded sample. It is obvious that the microstructure of FZ is distinctly different from that seen in Examples 1-5. Although the high-density of nano-sized κ-carbides can be still observed within the austenite dendrite cells and eutectic regions, there also exists a large amount of discrete ferrite phase (indicated by the arrows and marked as a in FIG. 9(a)) distributing in the entire FZ. The volume fraction of the ferrite phase was estimated to be about 18 vol. %, as determined by a point-counting technique.

[0173] FIG. 9(b) is the TEM BF image taken from the FZ, showing the nano-sized κ-carbides distributed within the austenite dendrites and eutectic regions. Moreover, it is apparent that some coarse μm-sized κ-carbides formed on the austenite/ferrite grain boundaries. FIG. 9(c) shows the SADP taken from the area circled in FIG. 9(b), clearly revealing that the existence of three phases, namely austenite, ferrite and κ-carbides. The orientation relationships between the austenite and ferrite phase are [011].sub.γ//[111].sub.α and (111).sub.γ//(110).sub.α, respectively. FIG. 9(d) and FIG. 9(e) show two typical TEM-EDS profiles taken from the austenite dendrite region and the ferrite phase region, respectively. The quantitative chemical compositions within the austenite dendrite region and ferrite phase are Fe-20.6% Mn-8.2% Al and Fe-15.8% Mn-8.8% Al, respectively.

[0174] On the basis of the above results, it is interesting to note here that usually for Fe—Mn—Al—C alloys with the compositions of Fe-(17.5˜35)Mn-(7.1˜12)Al-(0.8˜1.2)C, when hot-rolled, solution heat-treated and quenched, the microstructure is always single-phase austenite, as have been described in the Background section. Thus, the present Example further demonstrated that, even with the same chemical composition, the microstructure of the material after fusion welding can be quite different from that obtained by usual heat-treatment processes. Obviously, in order to obtain a ferrite-free full austenite FZ microstructure with high-density nano-sized κ-carbides distributing within the austenite dendrite cells and eutectic regions, the Mn content in the welding filler wire should be substantially higher than ˜20 wt. % used in the present Example.

EXAMPLE 10

[0175] In this Example of embodiment, we set to investigate the effects of titanium (Ti) addition to the welding filler wire on the characteristics of FZ in the as-welded sample. An as-hot-rolled base material with nominal composition of Fe-29.3Mn-9.3Al-1.75C was used in the present Example of embodiment. FIG. 10(a) is the TEM BF image of the as-hot-rolled base material, clearly revealing that there are high-density of nano-sized (˜3-5 nm) precipitates uniformly distributing within the matrix and formed on the dislocations (indicated by the arrows) during the hot-rolling process. FIG. 10(b), the selected-area diffraction pattern (SADP), evidently confirms that the matrix of the base material is fully austenitic and the high-density nano-sized precipitates are the ordered L′1.sub.2-structured κ-carbides. FIG. 10(c) is the (100).sub.K DF image taken from the same area as displayed in FIG. 10(a), revealing the presence of high-density of nano-sized κ-carbides within the austenite matrix and on the dislocations. TEM microstructural analyses confirmed that the as-hot-rolled microstructure of the base material used in the present Example is single-phase austenite with uniformly distributed high-density of nano-sized κ-carbides. The tensile test revealed that the YS, UTS and El of the as-hot-rolled base material are 1020 MPa, 1198 MPa and 45%, respectively.

[0176] Two plates of the as-hot-rolled base material with dimensions of 80 mm×80 mm×12 mm were machined to form a single V-groove butt weld. The GMAW welding process was carried out using the parameters similar to those used in Example 2. The nominal composition of the welding filler wire used in the present Example was Fe-28.5Mn-9.3Al-1.82C-1.6Ti with a wire diameter ϕ˜1.2 mm. FIG. 10(d) shows the macroscale image of the as-welded sample, revealing that the entire welding bead appears to have a very smooth morphology with no visible macrocrack and porosity. FIG. 10(e) is the SEM image of an area covering FZ, HAZ and BM of the welded sample. From FIG. 10(e), several distinct features resulting from the addition of Ti are readily noted. Firstly, the size of the austenite grains in the FZ is apparently much smaller than that seen in previous Examples 1-5 and is even smaller than that in HAZ and BM. Secondly, the morphology of the austenite grains becomes more globular and less oriented. Nevertheless, it is evident that there are still high-density of nano-sized κ-carbides uniformly distributed within the austenite dendrite cells and eutectic regions. Moreover, despite that slightly austenite grain growth in the HAZ is discernible, the high-density of nano-sized κ-carbides originally existing in the BM remained unchanged. Finally, it is noted that, within the FZ and near the interface between the FZ and HAZ, there is no trace of microcrack and porosity can be observed, indicating that the use of the fusion filler wire disclosed in the present invention has evidently eliminated the solidification and liquation cracks commonly encountered in fusion welded precipitation-hardened alloys. FIG. 10(f) shows the Vickers microhardness measurements conducted across the FZ, HAZ and BM. The corresponding values of the respective measured hardness points are displayed in FIG. 10(g), which reveals that the average microhardness of FZ, HAZ and BM of the present as-welded sample is about 451 Hv, 435 Hv, and 436 Hv, respectively. Apparently, the FZ does not exhibit any softening like that encountered in most of fusion welded precipitation-hardened alloys. This is mainly because that, in the as-welded conditions (FIG. 10(e)), there are high-density of nano-sized κ-carbides existing within the austenite dendrite cells and eutectic regions. Moreover, in addition to the nano-sized κ-carbides, there are also significant amount of high-hardness (2200˜3500 Hv) nano-sized Ti-rich Ti-carbides formed within the eutectic regions (FIG. 10(h)). As a result, the FZ not only does not show softening but also is having even higher microhardness than the BM.

[0177] Transmission electron microscopy examinations of FZ thin foils indicated that along with the Ti addition, a significant amount of nano-sized Ti-carbides having an ordered face-centered-cubic structure was formed within the eutectic regions. A typical example is shown in FIG. 10(h). In this TEM BF image, it is clearly seen that the length of austenite dendrite cells is only about 100-150 nm and there are high-density of nano-sized κ-carbides (˜3-5 nm) distributed within the austenite dendrite cells and eutectic regions. In addition, within the eutectic regions, there also exist some slightly larger nano-sized (˜6-10 nm) Ti-carbides, as indicated by the arrows in FIG. 10(h). FIG. 10(i) is the SADP taken from the area circled in FIG. 10(h), showing the co-existence of the austenite matrix, κ-carbides and Ti-carbides. Analysis of the SADP indicates that the orientation relationships among the three phases are cubic-to-cubic. FIG. 10(j) is the TEM-EDS profile taken from the same area, demonstrating the presence of Ti-rich Ti-carbides within the eutectic regions. Since the nominal compositions of welding filler wires used in Example 1 and Example 10 were having about the same Al and C contents, except that in Example 10 about 1.6 wt. % of Ti was added, thus, it is worthwhile to compare the FZ microstructures revealed in FIG. 1(h) and FIG. 10(h). In FIG. 1(h), although the size of austenite dendrite cells is slightly larger than that revealed in FIG. 10(h), it appears that the density of nano-sized κ-carbides within the austenite dendrite cells is slightly higher than that in FIG. 10(h) (the Ti-added sample). Moreover, both are having significant amount of nano-sized precipitates (κ-carbides in FIG. 1(h); κ-carbides and Ti-rich Ti-carbides in FIG. 10(h)) within the eutectic regions. However, the FZ microhardness of Example 10 (˜451 Hv) is considerably larger than that of Example 1 (˜425 Hv). The main reason for this could be due to the fact that the hardness of the Ti-rich Ti-carbides is ˜2200-3500 Hv, which is much higher than that of (Fe,Mn).sub.3AlC (˜630-670 Hv) carbides.

[0178] Tensile test indicated that the YS, UTS and El of the weldment were 1006 MPa, 1145 MPa and 40%, respectively. FIG. 10(k) shows the macroscale images of the specimens before and after the tensile test. The corrugated deformation surface seen in the FZ clearly evidences the ductile nature of the welded bead. Moreover, it is seen that the edges of the tensile-fractured specimen remained parallel across a range including FZ and BM with essentially the same width, as indicated by d.sub.FZ, d.sub.BM and d.sub.INT (here d.sub.INT denotes the width at the interface between BM and FZ) in FIG. 10(k). As has been discussed in details in Example 1 and Example 2, such unique deformation behavior strongly implies that the yield strength of FZ and BM is approximately of the same level. As mentioned above, the remarkable YS and microhardness obtained in the FZ can be attributed to the existence of the high-density nano-sized κ-carbides and nano-sized Ti-rich Ti-carbides in FZ. It is also noted that the slight necking and eventual fracturing occurred in the BM further indicates that the tensile strength of FZ is higher than that of the BM, which is consistent with the larger FZ microhardness, as displayed in FIG. 10(g).

[0179] Based on the above analyses, it is evident that the Ti-addition to welding filler wire clearly has given rise to following advantageous effects. Firstly, the morphology of austenite grains in the FZ changes from columnar into globular with a significant grain size refinement. Secondly, in the as-welded state, there are high-density of nano-sized κ-carbides existing in the much refined austenite dendrite cells and eutectic regions. In addition, there is also significant amount of high-hardness nano-sized Ti-rich Ti-carbides formed within the eutectic regions. Thirdly, the austenite dendrite cells, the nano-sized κ-carbides and nano-sized Ti-rich Ti-carbides composing of the FZ are all having the ductile face-centered-cubic structure. Moreover, the sizes of κ-carbides and Ti-rich Ti-carbides in the FZ are only in the range of 3˜10 nm, thus are very effective in enhancing the mechanical strength, in particular YS, without significant loss in ductility. Consequently, by using the welding filler wire disclosed in the present invention, the FZ in the as-welded sample has exhibited exceptional combination of hardness, YS, UTS and ductility simultaneously.

EXAMPLE 11

[0180] In this Example of embodiment, we investigated the effects of niobium (Nb) addition to the welding filler wire on the characteristics of FZ in the as-welded sample. The base material (BM) used in this Example was the same as that used in Example 10. Two BM plates with dimensions of 80 mm×80 mm×8 mm were machined to form a single V-groove butt weld. The GTAW welding process was carried out using the parameters similar to those used in Example 1. The welding filler wire has a nominal composition of Fe-29.5Mn-8.2Al-1.56C-1.0Nb with a wire diameter ϕ˜3.2 mm. FIG. 11(a) shows the macroscale image of the as-welded sample, revealing that the entire welding bead has a very smooth morphology with no visible macrocrack and porosity. FIG. 11(b) is the SEM image of an area covering FZ, HAZ and BM of the welded sample, showing that, unlike that seen in the previous Ti-added sample (Example 10), the austenite grains in the FZ have a mixture of “globular” and “columnar-like” morphologies. However, similar to that observed in Example 10, the high-density of nano-sized κ-carbides uniformly distributed within the austenite dendrite cells and eutectic regions can be observed. Similarly, there appears to have slightly austenite grain growth in the HAZ, while the high-density nano-sized κ-carbides originally existing in the hot-rolled BM remained essentially unchanged during fusion welding. Moreover, it is noted that, within the FZ and near the interface between the FZ and HAZ, there is no trace of microcrack and porosity can be observed, indicating that the use of the fusion filler disclosed in the present invention has evidently eliminated the solidification and liquation cracks. FIG. 11(c) shows the Vickers microhardness measurements conducted across the FZ, HAZ and BM. The corresponding values of the respective measured hardness points are displayed in FIG. 11(d), which reveals that the microhardness of FZ, HAZ and BM of the present as-welded sample are about 431 Hv, 435 Hv, and 437 Hv, respectively. Obviously, the FZ does not show any softening like that encountered in most of fusion welded precipitation-hardened alloys. The primary reasons for this, similar to those observed in Example 10, are due to the high-density of nano-sized κ-carbides existing within the austenite dendrite cells and eutectic regions, as well as a significant amount of high-hardness (2000˜3200 Hv) nano-sized Nb-rich Nb-carbides within the eutectic regions (FIG. 11(e)). As a result, the FZ can have about the same level of microhardness as compared with that of HAZ and BM.

[0181] Similar to that observed in the Ti-added samples (Example 10), the TEM analyses revealed that substantial amount of nano-sized Nb-rich Nb-carbides having an ordered face-centered-cubic structure was formed within the eutectic regions. FIG. 11(e) is the typical TEM BF image taken from the FZ of the as-welded sample, clearly revealing a very different morphology of the austenite dendrite cells and the eutectic regions as compared to that observed in Example 10. The dendrite cells and the surrounding eutectic regions appear to be more roundish. Nevertheless, the unique feature of the high-density of nano-sized κ-carbides (˜3-5 nm) distributed within the austenite dendrite cells and eutectic regions remained. In addition to the eutectic κ-carbides, there also exist substantial amount of slightly larger nano-sized precipitates (˜6-10 nm) in the eutectic regions, as indicated by the arrows in FIG. 11(e). FIG. 11(f) is the SADP taken from the area circled in FIG. 11(e), showing the co-existence of the austenite matrix, κ-carbides and Nb-rich Nb-carbides. Analysis of the SADP further indicates that the orientation relationships among the three phases are cubic-to-cubic. FIG. 11(g) is the TEM-EDS profile taken from the same area, confirming the presence of Nb-rich Nb-carbides. Since the hardness of Nb-rich Nb-carbides is ˜2000-3200 Hv, one may expect that the precipitation of nano-sized Nb-rich Nb-carbides would give rise to similar effects on the characteristics of FZ and account for the microhardness results displayed in FIG. 11(d).

[0182] Tensile test indicated that the YS, UTS and El of the weldment were 980 MPa, 1108 MPa and 46%, respectively. FIG. 11(h) shows the macroscale images of the specimens before and after the tensile test. In tensile-fractured specimen, it is clear that the corrugated deformation surface and the zig-zag weaving fracture pattern can be observed in the FZ, suggesting the ductile nature of the FZ. Moreover, it is also seen that the widths across the region containing the BM, FZ and the interface between them (denoted as d.sub.BM, d.sub.FZ and d.sub.INT) are essentially equal and the specimen edges across this region remains parallel, as indicated in FIG. 11(h). Such unique feature implies that the yield strength of FZ and BM is approximately the same level and the deformation under tensile stress proceeds in a uniform manner until the necking and eventual fracturing occurred in the FZ. The fact that slight necking and eventual fracturing occurred in the FZ indicates that UTS in the FZ is smaller than that of the BM.

[0183] Based on the above results, it is evident that Nb-addition to welding filler wire clearly has the similar effects as the addition of Ti (Example 10), namely, in addition to preserving the high-density of nano-sized κ-carbides existing within the austenite dendrite cells and eutectic regions, the formation of nano-sized Nb-rich Nb-carbides in the eutectic regions evidently is advantageous in enhancing the mechanical strength and microhardness of the FZ in the as-welded sample, while still maintaining excellent ductility. As described above in Example 10, because all the phases composing the FZ microstructure are all of ductile face-centered-cubic structure and the strengthening nano-sized κ-carbides and Nb-rich Nb-carbides are only about 3-10 nm and very effective in enhancing the YS. Thus, by using the welding filler wire disclosed in the present invention, the FZ in the as-welded sample can exhibit exceptional combination of hardness, YS, UTS and ductility simultaneously.

EXAMPLE 12

[0184] In this Example of embodiment, we investigated the effects of vanadium (V) addition to the welding filler wire on the characteristics of FZ in the as-welded sample. The base material (BM) used in this Example was the same as that used in Example 10. Two BM plates with dimensions of 80 mm×80 mm×10 mm were machined to form a single V-groove butt weld. The GTAW welding process was carried out using parameters similar to those used in Example 1. The welding filler wire has a nominal composition of Fe-31.2Mn-9.8Al-1.65C-1.2V with a wire diameter ϕ˜3.2 mm. FIG. 12(a) shows the macroscale image of the as-welded sample, revealing that the entire welding bead has a very smooth morphology with no visible macrocrack and porosity. FIG. 12(b) is the SEM image of an area covering FZ, HAZ and BM of the welded sample, showing that, similar to the previous Nb-added sample (Example 11), the austenite grains in the FZ have a mixture of “globular” and “columnar-like” morphologies. Moreover, as were observed in Example 10 and Example 11, there are high-density of nano-sized κ-carbides uniformly distributed within the austenite dendrite cells and the eutectic regions. Similarly, there appears to have slightly austenite grain growth in the HAZ, while the high-density of nano-sized κ-carbides originally existing in the hot-rolled BM remained essentially unchanged during fusion welding. Finally, it is noted that, within the FZ and near the interface between the FZ and HAZ, there is no trace of microcrack and porosity can be observed. FIG. 12(c) shows the Vickers microhardness measurements conducted across the FZ, HAZ and BM. The corresponding values of the respective measured hardness points are displayed in FIG. 12(d), which reveals that the average microhardness of FZ, HAZ and BM of the present as-welded sample are about 438 Hv, 434 Hv, and 436 Hv, respectively. Obviously, there is no softening in FZ and HAZ, which is consistent with the unique microstructure displayed in FIG. 12(b), wherein the prominent strengthening ingredient of high-density of nano-sized κ-carbides remains essentially unchanged in all three zones. Moreover, the addition of V has led to the formation of a significant amount of high-hardness (2200-3000 Hv) nano-sized V-rich V-carbides within the eutectic regions (FIG. 12(e)), giving rise to about the same level of microhardness in the FZ as compared with that of HAZ and BM, which is very similar to that observed in Example 11.

[0185] TEM analyses revealed that the V-addition has led to similar effects as those seen in Ti-addition (Example 10) and Nb-addition (Example 11). Namely, there were significant amount of nano-sized V-rich V-carbides having an ordered face-centered-cubic structure formed within the eutectic regions. FIG. 12(e) is the TEM BF image taken from the FZ, clearly revealing that the length of austenite dendrite cells is only about 20-60 nm and the morphology is different from that observed for Ti-added (FIG. 10(h)) and Nb-added (FIG. 11(e)) samples. However, the unique feature of high-density of nano-sized κ-carbides (˜3-5 nm) distributed within austenite dendrite cells and eutectic regions can still be observed. In addition, within the eutectic regions, there apparently exist substantial amount of slightly larger precipitates (˜6-10 nm), as indicated by the arrows in FIG. 12(e). FIG. 12(f) is the SADP taken from the area circled in FIG. 12(e), showing the co-existence of the austenite matrix, κ-carbides and V-rich V-carbides. Analysis of the SADP indicates that the orientation relationships among the three phases are cubic-to-cubic. FIG. 12(g) is the TEM-EDS profile taken from the same area, confirming the existence of V-rich V-carbides. Since the hardness of V-rich V-carbides is comparable to that of Nb-rich Nb-carbides and Ti-rich Ti-carbides, similar effects on the characteristics of FZ are expected and account for the microhardness results obtained in FIG. 12(d).

[0186] Tensile test indicated that the YS, UTS and El of the weldment were 998 MPa, 1167 MPa and 44%, respectively. FIG. 12(h) shows the macroscale images of the specimens before and after the tensile test. It is interesting to note that the edges of the tensile-fractured specimen remained parallel across a range including FZ and BM with essentially the same width, as indicated by d.sub.FZ, d.sub.BM and d.sub.INT (here d.sub.INT denotes the width at the interface between BM and FZ) in FIG. 12(h). As were discussed in Examples 1-2 and Examples 10-11, such unique feature implies that the yield strength of FZ and BM is approximately of the same level. Closer inspection on the tensile-fractured specimen indicates that the corrugated deformation surface (an indication of ductile nature) is especially obvious in the FZ of the welding bead. The estimated elongation within the FZ reached up to about 28%. Moreover, it appeared that, when the applied stress beyond the yield strength, the plastic deformation of the entire specimen, including FZ, HAZ and BM, exhibited excellent uniform deformation until the slightly necking and eventual fracturing occurred near the interface between FZ and HAZ, as indicated by the arrow in FIG. 12(h). As a consequence, even after fracture the edges of the entire remained almost in parallel. The fact that slight necking and eventual fracturing occurred in the vicinity of the FZ/HAZ interface indicates that the UTS in the FZ, HAZ and BM are very close to each other.

[0187] Based on the above results, it is evident that V-addition to welding filler clearly has the similar effects as the addition of Ti (Example 10) and Nb (Example 11). In all cases, in addition to preserving the high-density of nano-sized κ-carbides existing within the austenite dendrite cells and eutectic regions, the formation of nano-sized V-rich V-carbides evidently is advantageous in enhancing the mechanical strength and microhardness of the FZ in the as-welded sample. Moreover, since the nano-sized (3˜10 nm) κ-carbides, Ti-rich Ti-carbides, Nb-rich Nb-carbides and V-rich V-carbides are all having the same ductile face-centered-cubic structure as the austenite dendrite, the remarkable strengthening effect is attained without significant loss in ductility. The above detailed analyses clearly indicate that, by using the welding filler wires disclosed in the present invention for fusion welding, the resultant FZ could all have exceptional combination of microhardness, YS, UTS and ductility.

EXAMPLE 13

[0188] In this Example of embodiment, we further investigated the combined effects of Ti and Nb addition to the welding filler wire on the characteristics of FZ in the as-welded sample. The base material (BM) used in this Example was the same as that used in Example 10. Two BM plates with dimensions of 80 mm×80 mm×12 mm were machined to form a single V-groove butt weld. The GTAW welding process was carried out using the parameters similar to those used in Example 1. The welding filler wire has a nominal composition of Fe-30.6Mn-9.2Al-1.88C-0.8Ti-1.0Nb with a wire diameter ϕ˜3.2 mm. FIG. 13(a) shows the macroscale image of the as-welded sample, revealing that the entire welding bead has a very smooth morphology with no visible macrocrack and porosity. FIG. 13(b) is the SEM image of an area covering FZ, HAZ and BM of the welded sample. In this figure, it is obvious that the morphology of all austenite grains in FZ becomes globular and the size of the globular austenite grains has been substantially refined, which is even much smaller than that of HAZ and BM. Similar to that described in Examples 10-12, the high-density of nano-sized κ-carbides uniformly distributed within the austenite dendrite cells and eutectic regions can be observed. Also, the high-density of nano-sized κ-carbides originally existing in the hot-rolled BM remained essentially unchanged during fusion welding. Moreover, it is noted that, within the FZ and near the interface between the FZ and HAZ, there is no trace of microcrack and porosity can be observed. FIG. 13(c) shows the Vickers microhardness measurements conducted across the FZ, HAZ and BM. The corresponding values of the respective measured hardness points are displayed in FIG. 13(d), which reveals that the average microhardness of FZ, HAZ and BM of the present as-welded sample are about 467 Hv, 444 Hv, and 435 Hv, respectively. Remarkably, the FZ not only does not exhibit any softening but also has significant higher microhardness than that of HAZ and BM. Similar to Examples 10-12, this is mainly because that, in the as-welded conditions (FIG. 13(b)), there are high-density of nano-sized κ-carbides existing within the austenite dendrite cells and eutectic regions. Moreover, within the eutectic regions, in addition to nano-sized κ-carbides, there are also significant amount of high-hardness nano-sized Ti-rich Ti-carbides and Nb-rich Nb-carbides (FIG. 13(e)). Consequently, the FZ is having significantly higher microhardness than that of the HAZ and BM without showing any sign of softening. Moreover, the addition of both 0.8% Ti and 1.0% Nb appears to result in even higher microhardness in the FZ as compared with that of previous Examples 10-12, which might be due to the total amount of high-hardness nano-sized Ti-rich Ti-carbides and Nb-rich Nb-carbides is increased in the present Example.

[0189] FIG. 13(e) is the TEM BF image taken from the FZ, clearly revealing a very different morphology of the austenite dendrite cells and the eutectic regions as compared to that observed in Examples 10-12. The dendrite cells and the surrounding eutectic regions appear to be further refined and more intertwined to each other. Nevertheless, the unique feature of the high-density of nano-sized (˜3-5 nm) κ-carbides distributed within austenite dendrite cells and eutectic regions remained. Moreover, the amount of eutectic κ-carbides and slightly larger (˜6-10 nm) Ti-rich Ti-carbides and Nb-rich Nb-carbides within the eutectic regions appears to increase substantially, as indicated by the arrows in FIG. 13(e). FIG. 13(f) is the TEM-EDS profile taken from the area circled in FIG. 13(e), confirming the presence of Ti-rich Ti-carbides and Nb-rich Nb-carbides.

[0190] Tensile test indicated that the YS, UTS and elongation of the weldment were 1015 MPa, 1168 MPa and 38%, respectively. FIG. 13(g) shows the macroscale images of the specimens before and after the tensile test. The corrugated deformation surface observed in the FZ suggests the ductile nature of the FZ. Moreover, it is seen that the edges of the tensile-fractured specimen remained parallel in both sides of BM range up to interface between the FZ and BM with essentially the same d.sub.BM, d.sub.FZ, and d.sub.INT, as indicated in FIG. 13(g). Such unique feature implies that the yield strength of FZ and BM is approximately the same level and the deformation under tensile stress proceeds in a uniform manner until the necking and eventual fracturing occurred in the BM, as indicated by the arrow in FIG. 13(g). The fact that slight necking and eventual fracturing occurred in the BM indicates that UTS in the FZ is larger than that of the BM, which is also consistent with the obtained microhardness in FZ is substantially higher than in BM, as depicted in FIG. 13(d).

[0191] Based on the above results, it is evident that the addition of both Ti and Nb to welding filler wire has led to even more pronounced effect in morphology change and size refining of austenite grains in the FZ. Moreover, it also results in significant increase in the amount of high-hardness nano-sized Ti-rich Ti-carbides and Nb-rich Nb-carbides within the eutectic regions, as compared with that observed in Example 10 and Example 11. More importantly, the feature of high-density of nano-sized κ-carbides existing within the austenite dendrite cells and eutectic regions is still largely preserved. As mentioned above, since the nano-sized (˜3-10 nm) κ-carbides, Ti-rich Ti-carbides, Nb-rich Nb-carbides, V-rich V-carbides and the austenite dendrites are all having the same ductile face-centered-cubic structure, the remarkable strengthening effect is attained without significant loss in ductility. The detailed analyses presented in the above Examples clearly indicate that, by using the welding filler wires disclosed in the present invention for fusion welding, the resultant FZ can all have exceptional combination of microhardness, YS, UTS and ductility.

EXAMPLE 14

[0192] The remarkable progress in developing the high-strength, especially high YS, high-ductility precipitation-hardened austenitic Fe—Mn—Al—C alloys have been mainly relying on the heat-treatment, including solution heat-treatment (SHT), quenching and then optimal aging treatment for obtaining the high-density of nano-sized κ-carbides within the austenite matrix. However, as mentioned in the Background section, the issues of the weldability of these alloys remained largely unsolved despite of the tremendous research efforts devoted over the last several decades. Recently, in recognizing the pivotal importance of high-density nano-sized κ-carbides within the austenite matrix for retaining the strength, in particular YS, and ductility of the weldment, in 2019 Jeong et al. have tried to use Gleeble simulation to unveil the microstructure in the HAZ during welding and its influences on the mechanical properties of the HAZ of the lightweight precipitation-hardened austenitic Fe-31.4Mn-11.4Al-0.9C alloy. The alloy they used was hot-rolled at 1200° C. to a thickness of 13 mm, water quenched, SHT at 1050° C. for 2 hrs, water quenched, and then aged at 550° C. for 100 min for obtaining a high-density of nano-sized κ-carbides within the austenite matrix. The aging treatment evidently raised the hardness of the alloy from 298 Hv in SHT condition to 349 Hv after aged at 550° C. for 100 min. The simulations were conducted with peak temperature of 750, 950 and 1150° C. using a Gleeble simulator. The results showed that, when the simulated specimens were cooled to room temperature, softening behaviors indeed occurred in every age-hardened sample and for the sample with 1150° C. peak temperature complete dissolution of κ-carbides was observed. These observations inferred as the confirmation that the κ-carbide precipitation has a definite relationship with the transition in the mechanical properties of the HAZ. However, it is noted that in these Gleeble simulation studies, no direct fusion welding was conducted, thus, did not involve re-melting and re-solidification processes and could not directly obtain the actual structure and characteristics of FZ. Yet, in their Gleeble simulation studies, the aged specimens after being heated up to peak temperature of 750˜1150° C. and then cooled to room temperature, dissolution of the pre-existing strengthening κ-carbides and drastic softening in the HAZ was observed. This kind of phenomenon was in fact very similar to what happened in fusion welding precipitation-hardened 7xxx-series aluminum alloys, as mentioned in the Background section.

[0193] The following publication gave more detailed descriptions and discussions of the abovementioned characteristics and features.

[0194] [32] S. Jeong, G. Park, B. Kim, J. Moon, S. J. Park, C. Lee, “Precipitation behavior and its effect on mechanical properties in weld heat-affected zone in age hardened FeMnAlC lightweight steels”, Mater. Sci. Eng. A, 742 (2019) 61-68.

[0195] In this Example, we examine the effects of fusion welding on the characteristics of weldment using the age-hardened Fe—Mn—Al—C alloys as the base material. The nominal composition of the based material is Fe-31.5Mn-8.5Al-1.25C. Prior to fusion welding, the hot-rolled base material was solution heat-treated at 1050° C. for 1 hr, water quenched, and then aged at 550° C. for 12 hrs. Two aged BM plates with dimensions of 80 mm×80 mm×8 mm were machined to form a single V-groove butt weld. The GTAW welding process was carried out using the parameters similar to those used in Example 1. The welding filler wire used in the present Example was the same as that used in Example 3 with a filler wire diameter ϕ˜2.4 mm.

[0196] FIG. 14(a) is the SEM image showing the microstructure of an area covering FZ, HAZ and BM of the welded sample. It is evident from FIG. 14(a) that the FZ microstructure is very similar to that seen in FIG. 3(d), exhibiting typical microstructure of columnar austenite grains with a high-density of nano-sized κ-carbides distributed within the austenite dendrite cells and eutectic regions. However, in the present Example, drastic reduction in the amount of the nano-sized κ-carbides in HAZ is clearly observed, indicating that during fusion welding, the nano-sized κ-carbides originally existing in the aged BM were largely dissolved. Based on the investigations of the present invention, it is mainly owing to insufficient carbon content in the BM used in the present Example. This result is the same as that reported by Jeong et al. in 2019, where they used Gleeble simulation to investigate the effects of fusion welding on the HAZ in an age-hardened Fe-31.4Mn-11.4Al-0.9C alloy and found the dissolution of κ-carbides and significant softening in HAZ. In fact, this is also quite similar to that observed in fusion welding the precipitation-hardened AA7075 Al alloys, as quoted in the Background section.

[0197] FIG. 14(b) shows the Vickers microhardness measurements conducted across the FZ, HAZ and BM. The corresponding values of the respective measured hardness points are displayed in FIG. 14(c), which reveals that the average microhardness of FZ, HAZ and BM of the present as-welded sample is about 406 Hv, 282 Hv, and 380 Hv, respectively. Evidently, the dissolution of the strengthening nano-sized κ-carbides in the HAZ has led to drastic softening, similar to that reported in most of the prior art cited above. FIG. 14(d) shows the macroscale images of the specimens before and after the tensile test. From the tensile-fractured specimen, it is obvious that, due the substantial softening in the HAZ, the fracturing path propagated along the interface between the HAZ and BM, as indicated by the arrow.

[0198] Based on the above results, it is obvious that in order to preserve the strengthening nano-sized κ-carbides in the FZ and HAZ appropriate alloy design in both the welding filler and BM are essentially important.

EXAMPLE 15

[0199] The purpose of this Example is an attempt to clarify the effects of the molybdenum (Mo) addition in the welding filler wire on the characteristics of FZ in the as-welded sample. In the present Example, the base material used was the same as that used in Example 1. Two BM plates with dimensions of 80 mm×80 mm×10 mm were machined to form a single V-groove butt weld. The GTAW welding process was carried out using the parameters similar to those used in Example 1. The nominal composition of the welding filler wire was Fe-28.2Mn-9.1Al-1.55C-1.8Mo, with a wire diameter ϕ˜3.2 mm.

[0200] FIG. 15(a) is the SEM image showing the FZ, HAZ and BM regions of the as-welded sample. It is evident that the FZ microstructure contains mainly the typical columnar austenite grains and a high-density of nano-sized κ-carbides can be observed within the austenite dendrite cells and eutectic regions, which is similar to that observed in Examples 1-5. However, a significant amount of μm-sized coarse particles with wide precipitation-free zones can also be observed on the austenite grain boundaries (as indicated by the arrows). FIG. 15(b), the SEM-EDS profile taken from a coarse particle reveals that the coarse particles were Mo-rich Mo-carbides. It has been well established that the existence of coarse particles on the grain boundaries and the accompanied precipitation-free zones would be extremely detrimental to the alloy's ductility and strength. Thus, it is not recommended to add the strong carbide-forming Mo alloying element to the welding filler wires disclosed in the present invention.

EXAMPLE 16

[0201] The purpose of this Example is an attempt to clarify the effects of the chromium (Cr) addition in the fusion welding wire on the characteristics of FZ in the as-welded sample. In the present Example, the base material used was the same as that used in Example 1. Two BM plates with dimensions of 80 mm×80 mm×10 mm were machined to form a single V-groove butt weld. The GTAW welding process was carried out using the parameters similar to those used in Example 1. The nominal composition of the welding filler wire was Fe-29.3Mn-8.8Al-1.58C-1.5Cr, with a wire diameter ϕ˜3.2 mm.

[0202] FIG. 16(a) shows the typical SEM image of an area covering the FZ, HAZ and BM of the as-welded sample. The FZ microstructure contains mainly the typical columnar austenite grains and a high-density of nano-sized κ-carbides can be observed within the austenite dendrite cells and eutectic regions, which is similar to that observed in Examples 1-5. However, a significant amount of μm-sized coarse particles can also be observed on the austenite grain boundaries (as indicated by the arrows) with apparent precipitation-free zones surrounding the coarse particles. FIG. 16(b) is the SEM-EDS profile taken from a coarse particle, revealing that the coarse particles were Cr-rich Cr-carbides. As stated above in Example 15, the existence of coarse particles on the grain boundaries and the accompanied precipitation-free zones would be highly detrimental to the alloy's ductility and strength. Thus, it is not recommended to add the strong carbide-forming Cr alloying element to the welding filler wires disclosed in the present invention.

[0203] It is interesting to note that, although Ti, Nb, V, Mo, and Cr are all known to be strong carbide-forming alloying elements, the above Examples (10-13 and 15-16), nevertheless demonstrated that they could give rise to vastly different effects on the FZ microstructure of the welded samples. For Ti, Nb, and V, the present invention has evidently disclosed that they can form nano-sized (6˜10 nm) Ti-rich Ti-carbides, Nb-rich Nb-carbides and V-rich V-carbides within the eutectic regions during fusion welding, which not only leads to significantly enhancement in the microhardness and yield strength but also preserves excellent ductility in the FZ of the welded alloys. On the contrary, our examinations also revealed that the addition of Mo and Cr to the welding filler wires had caused the formation of μm-sized coarse Mo-rich Mo-carbides and Cr-rich Cr-carbides on the austenite grain boundary accompanied by the apparent precipitation-free zones surrounding the coarse carbides in the FZ, which are detrimental to the ductility of the as-welded alloys.

[0204] It is specifically emphasized here that the Examples described above are merely for the purposes of clarifying the unprecedented features resulted from the novel alloy design of the fusion welding filler wires disclosed in the present invention, and they should not be deemed as the scope of the present invention. All the alternatives based on the claims of the present invention should be regarded as being included in the scope of the patent.