Method for producing a multi-layer substrate

Abstract

The present invention relates to a method for producing a multi-layer substrate, said substrate comprising a multifunctional coating, and to the use of the substrate produced by this method.

Claims

1. A method of producing a multi-layer substrate comprising the following steps: a) providing a first material having a first surface with at least one edge region and at least one inner region enclosed by the edge region; b) applying a coating material to partial portions of the inner region of the first surface, the coating material comprising expandable microparticles; c) drying the coating material; and d) contacting the first surface of the first material with a surface of a second material to form the multi-layer substrate such that the coating material is between the first material and the second material, wherein the inner region does not contain an adhesive wherein the coating material consists of: (i) 30 to 70 wt-% of VAE copolymer dispersion; (ii) 5 to 15 wt. % of paraffin dispersion; (iii) 15 to 30 wt. % of microparticles; (iv) 5 to 10 wt. % of glycerol; and (v) optionally, hydroxyethylcellulose, wherein the total weight of the coating material and add up to 100 wt. %.

2. The method according to claim 1, characterized in that the contacting in step d) is carried out using an adhesive, wherein the adhesive is applied continuously to the edge region of the first material.

3. The method according to claim 1, characterized in that the coating material is dried at a temperature of 80° C. or less.

4. The method according to claim 1, characterized in that the coating material is a polymer-based coating material which has 10 to 40 wt. %, of expandable microparticles based on the total weight of the coating material.

5. The method according to claim 4, characterized in that the expandable microparticles are thermally expandable microparticles.

6. The method according to claim 1, characterized in that the multi-layer substrate is converted into a packaging in a further step.

7. The method according to claim 6, characterized in that the packaging is an envelope, a mailing bag, a bag, a carrier bag, a pouch or a carton.

8. The method according to claim 1, characterized in that the method comprises a further step e) in which the multi-layer substrate is subjected to a treatment for expanding the expandable microparticles.

9. The method according to claim 8, characterized in that the treatment is a heat treatment carried out at a temperature of 85° C. to 150° C.

10. The method according to claim 8, characterized in that the treatment is carried out separately from the other method steps from time and/or location.

11. The method according to claim 8, characterized in that the treatment is a heat treatment which is carried out using infrared radiation and/or warm air.

12. A method of producing a package using a multi-layer substrate produced by a method according to claim 1, wherein the multi-layer substrate is formed into the package by cutting and folding.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) FIG. 1 shows schematically the first material in the form of a continuous web, wherein (1) denotes the edge region and (2) the inner region.

(2) FIG. 2 shows schematically the first material in the form of a single unit, wherein (1) denotes the edge region and (2) the inner region.

DETAILED DESCRIPTION OF THE INVENTION

(3) The method according to the invention is distinguished by its rapid process control, which allows large quantities of the multi-layer substrate to be produced in a short time. This is achieved, among other things, by carefully coordinating the properties of the materials used. Therefore, an embodiment of the present invention is preferred in which the drying of the coating material is carried out at a temperature of 80° C. or less, preferably at a temperature of 40° C. to 75° C. It has surprisingly been found that rapid drying is achieved at these temperatures without the performance of the coating material being impaired, as a result of which the process throughput is improved.

(4) The best results in terms of process throughput were achieved when a polymer-based coating material was used. An embodiment is therefore preferred in which the coating material is a polymer-based coating material which has 10 to 40 wt. %, preferably 15 to 35 wt. % of expandable microparticles, in each case based on the total weight of the coating material. It has surprisingly been found that such a coating material can be applied at a high speed, but at the same time has sufficient stability so that it does not run after application.

(5) The coating material used in the method according to the invention has expandable microparticles. The microparticles preferably have a particle size, expressed as a D50 value, of 5 to 18 μm, preferably 10 to 17 μm, in the unexpanded state.

(6) The expandable microparticles are preferably thermally expandable microparticles, which preferably have the shape of spheres.

(7) In a preferred embodiment of the method according to the invention, the multi-layer substrate is converted into packaging in a further step. This implementation can take place, for example, by cutting and folding the multi-layer substrate. The packaging is preferably an envelope, a mailing bag, a bag, a carrier bag, a pouch or a carton, the format and size being variable. In a particularly preferred embodiment, the packaging is a mailing bag.

(8) In a preferred embodiment, the method according to the invention comprises a further step in which the multi-layer substrate is subjected to a treatment for expanding the expandable microparticles.

(9) In a preferred embodiment, the heat treatment step follows step d) of the method according to the invention.

(10) The method according to the invention allows the production of a substrate, the volume of which can be increased by a heat treatment, wherein this heat treatment can be carried out independently of the production method. In a preferred embodiment, the heat treatment is carried out separately from the other method steps in terms of time and/or location. In this way it is possible to transport and store the substrate in the state of a small volume. The substrate reaches its final volume as a result of the heat treatment, which causes the microparticles of the coating material to expand. The method according to the invention makes it possible to carry out the heat treatment only shortly before the substrate is used, which was not possible with conventional methods described in the prior art. For example, the substrate can be further processed into a mailing bag, which takes up little space due to the small volume and the small thickness. Before the mailing bag is used, it can be subjected to a heat treatment, whereby the microparticles are expanded and the mailing bag develops its desired cushioning effect. In this way, valuable storage and transport capacity can be saved by the method according to the invention.

(11) The heat treatment is preferably carried out at temperatures from 85° C. to 150° C., preferably 90 to 140° C. This ensures that the microparticles fully expand without being damaged and without losing their shock-absorbing effect.

(12) In order to achieve optimal absorption of mechanical influences, it has proven to be advantageous if the microparticles in the expanded state have a particle size in the range from 20 μm to 200 μm. An embodiment is therefore preferred in which the microparticles in the expanded state have a particle size, expressed as a D50 value, of 20 μm to 200 μm, preferably 20 to 150 μm.

(13) The heat treatment is preferably carried out using conventional heat sources. The heat treatment is particularly preferably carried out using infrared radiation and/or warm air.

(14) The multi-layer substrate produced by the method according to the invention is distinguished by its flexible volume. Another object of the present invention is therefore a multi-layer substrate which can be obtained by the method according to the invention. The substrate according to the invention is preferably in the form of a continuous web. In an alternative preferred embodiment, the substrate according to the invention is in the form of a packaging, preferably in the form of an envelope, a mailing bag, a bag, a carrier bag, a pouch or a carton, the format and the size being variable.

(15) The substrate according to the invention can be easily processed into packaging. Another object is therefore a method for producing a package using a multi-layer substrate which has been produced by the method according to the invention, the multi-layer substrate being formed into a package by means of cutting and folding.

(16) Another object of the present application is a package obtainable according to the inventive method. The packaging is preferably an envelope, a mailing bag, a bag, a carrier bag, a pouch or a carton, the format and the size being variable.

(17) The present invention is to be explained in more detail with reference to the following example, which is in no way to be understood as a restriction of the inventive concept.

(18) A suitable coating material can contain 30 to 70 wt-% of VAE copolymer dispersion (Vinamul® 3928), 5 to 15 wt. % of paraffin dispersion (Michemlube® 743 PE), 15 to 30 wt. % of microparticles (Expancel® 031 WUF 40), 5 to 10 wt. % of glycerol and optionally up to a wt. % of hydroxyethylcellulose (MEHC, Natrosol® 250LR), wherein the weight percentages refer to the total weight of the coating material and add up to 100 wt. %.

(19) FIG. 1 shows schematically the first material in the form of a continuous web, wherein (1) denotes the edge region and (2) the inner region.

(20) FIG. 2 shows schematically the first material in the form of a single unit, wherein (1) denotes the edge region and (2) the inner region.