Method and Apparatus for Fabricating Fibers and Microstructures from Disparate Molar Mass Precursors
20220074051 · 2022-03-10
Inventors
- James L. Maxwell (Scottsboro, AL, US)
- Nicholas Webb (Madison, AL, US)
- James Allen (Huntsville, AL, US)
Cpc classification
C23C16/483
CHEMISTRY; METALLURGY
C04B2235/5296
CHEMISTRY; METALLURGY
C23C16/52
CHEMISTRY; METALLURGY
C04B35/58
CHEMISTRY; METALLURGY
C23C16/45517
CHEMISTRY; METALLURGY
C23C16/4488
CHEMISTRY; METALLURGY
D01F9/127
TEXTILES; PAPER
C23C16/4401
CHEMISTRY; METALLURGY
International classification
C23C16/48
CHEMISTRY; METALLURGY
C04B35/58
CHEMISTRY; METALLURGY
C04B35/622
CHEMISTRY; METALLURGY
C23C16/52
CHEMISTRY; METALLURGY
D01F9/127
TEXTILES; PAPER
Abstract
The disclosed methods and apparatus improve the fabrication of solid fibers and microstructures. In many embodiments, the fabrication is from gaseous, solid, semi-solid, liquid, critical, and supercritical mixtures using one or more low molar mass precursor(s), in combination with one or more high molar mass precursor(s). The methods and systems generally employ the thermal diffusion/Soret effect to concentrate the low molar mass precursor at a reaction zone, where the presence of the high molar mass precursor contributes to this concentration, and may also contribute to the reaction and insulate the reaction zone, thereby achieving higher fiber growth rates and/or reduced energy/heat expenditures together with reduced homogeneous nucleation. In some embodiments, the invention also relates to the permanent or semi-permanent recording and/or reading of information on or within fabricated fibers and microstructures. In some embodiments, the invention also relates to the fabrication of certain functionally-shaped fibers and microstructures. In some embodiments, the invention may also utilize laser beam profiling to enhance fiber and microstructure fabrication.
Claims
1. A method of fabricating fibers, comprising: introducing a first precursor species into a reaction vessel comprising silicon and carbon; introducing a second precursor species comprising hydrogen into said reaction vessel, said first precursor species having a molar mass at least 3 times more than the second precursor species; creating a reaction zone within the reaction vessel and a thermal diffusion region at or near the reaction zone, wherein at least one of the thermal diffusion region and reaction zone is at least partially created by a primary heating means, and the thermal diffusion region at least partially separates the first precursor species from the second precursor species and concentrates at least one of the precursor species at the reaction zone; and decomposing the first precursor species in the reaction zone to deposit a solid fiber.
2. The method of claim 1, further comprising decomposing the first precursor species to a derived precursor species having a lower molar mass than the first precursor species and decomposing the derived precursor species in the reaction zone to deposit a solid fiber.
3. The method of claim 2, wherein byproducts from the decomposition of the derived precursor species react with the second precursor species to form at least one intermediate byproduct species having a higher molar mass than at least one of the precursors, and wherein the intermediate byproduct species is concentrated away from the reaction zone.
4. The method of claim 1, wherein the decomposition results in a methane byproduct.
5. The method of claim 1, wherein the solid fiber comprises: a first internal structure phase positioned at a fiber core; and a second internal structure phase, different from the first internal structure phase, positioned outside of the fiber core.
6. The method of claim 5, wherein the first internal structure phase comprises a crystalline structure phase and the second internal structure phase comprises an amorphous structure phase.
7. The method of claim 6, wherein the first internal structure phase has grain sizes smaller than 100 nm.
8. The method of claim 1, wherein the solid fiber varies in structure phase across a cross section, wherein said cross section comprises an amorphous structure phase that transitions to a crystalline structure phase.
9. The method of claim 8, wherein the solid fiber is of uniform chemical composition.
10. The method of claim 8, wherein the solid fiber is of essentially circular cross section.
11. A method of fabricating fibers, comprising: introducing a first precursor species into a reaction vessel; introducing a second precursor species into said reaction vessel, said first precursor species having a molar mass at least 1.5 times greater than the second precursor species; creating a reaction zone within the reaction vessel and a thermal diffusion region at or near the reaction zone, wherein the thermal diffusion region at least partially separates the first precursor species from the second precursor species and concentrates the second precursor species at the reaction zone; decomposing the first precursor species to a first derived precursor species having a lower molar mass than the first precursor species and decomposing the first derived precursor species in the reaction zone, to deposit as a solid fiber in the reaction zone; and modulating the reaction zone or flow of the first precursor species to the reaction zone.
12. The method of claim 11, wherein the solid fiber comprises a first internal structure phase positioned at a fiber core comprising a crystalline structure phase with grain sizes smaller than 100 nm and a second internal structure phase comprising an amorphous fiber structure phase positioned outside of the fiber core.
13. The method of claim 11, wherein byproducts from the decomposition of the first derived precursor species react with the second precursor species to form at least one intermediate byproduct species having a higher molar mass than at least one of the precursors.
14. The method of claim 11, wherein the decomposition results in a methane byproduct.
15. The method of claim 11, wherein modulating the reaction zone or flow of the first precursor species to the reaction zone causes a diameter of the solid fiber to vary along a lengthwise direction of the solid fiber.
16. The method of claim 15, wherein the diameter of the solid fiber varies along the length of the solid fiber and comprises one or more elongate portions of constant diameter and one or more enlarged portions.
17. The method of claim 15, wherein the diameter of the solid fiber varies at regularly occurring intervals along the length of the solid fiber.
18. A method of concentrating a precursor species in a reaction zone, comprising. introducing a first precursor species into a reaction vessel; introducing a second precursor species into said reaction vessel, said first precursor species having a molar mass at least 1.5 times greater than the second precursor species; creating a reaction zone within the reaction vessel and a thermal diffusion region at or near the reaction zone, wherein the thermal diffusion region at least partially separates the first precursor species from the second precursor species and concentrates the second precursor species at the reaction zone; and decomposing the first precursor species in the reaction zone to deposit as a solid.
19. The method of claim 18, further comprising modulating the reaction zone or flow of the first precursor species to the reaction zone.
20. The method of claim 18, wherein the first precursor species comprises silicon and carbon, and the second precursor species comprises hydrogen.
Description
BRIEF DESCRIPTION OF THE DRAWINGS
[0030] It should be noted that identical features in different drawings are generally shown with the same reference numeral. Various other objects, features and attendant advantages of the present invention will become fully appreciated as the same becomes better understood when considered in conjunction with the accompanying drawings.
[0031]
[0032]
[0033]
[0034]
[0035]
[0036]
[0037]
[0038]
[0039]
[0040]
[0041]
[0042]
[0043]
[0044]
[0045]
[0046]
[0047]
[0048]
[0049]
[0050]
[0051]
[0052]
[0053]
[0054]
[0055]
[0056]
[0057]
[0058]
[0059]
[0060]
[0061]
[0062]
[0063]
[0064]
[0065]
[0066]
[0067]
[0068]
[0069]
[0070]
[0071]
[0072]
[0073]
DETAILED DESCRIPTION OF THE INVENTION
[0074]
[0160]
[0161] One aspect of some embodiments of this invention is that the reaction zone 35 is thermally insulated by the HMM precursor 20, thereby greatly reducing heat losses to the surrounding fluids. Much greater growth rates have been observed with vastly reduced input to the power of the primary heating means 40. Thus, one aspect of the invention's utility is that it makes the growth of many fibers 25 at once much more efficient and feasible. For example, in the growth of 10,000 fibers at once, where each heated spot receives 200 mW of incident power (as is common in traditional laser induced fiber growth), the total energy entering the vessel will be 2 kW. This substantial heat budget must be dealt with or the temperature in the surrounding gases will rise over time. This invention greatly decreases the power required at each reaction zone 35. Thus, for example, where only 40 mW may be required at each reaction zone 35 with the HMM precursor 20 and LMM precursor 15 mixture, the total energy entering the vessel is now only 400 W, which requires significantly less external cooling and provides energy savings making the process more economically viable.
[0162] Note that to prevent excessive homogeneous nucleation, the gases in the thermal diffusion regions 10 may generally be at a lower temperature than the threshold for rapid (complete) decomposition of the precursors, but this is not required. Since the thermal diffusion regions 10 and reaction zones 35 overlap close to the growing fiber 25, the thermal diffusion regions 10 may exceed this temperature. In some cases, it may even be useful to induce homogeneous nucleation to provide fresh nucleation sites at the fiber 25 tip, and this invention can provide an extended heated region where this can occur.
[0163] The reaction takes place inside a reaction vessel, which is any enclosure that will contain the precursors for the desired life of the system and withstand any heat from the primary or secondary heating means(s) 40 or 110. The reaction vessel may be rigid or flexible. For example, the reaction vessel could be lithographically-patterned microfluidic structures in silicon, a molded polymeric balloon, or a machined stainless steel vessel—there are many possible means to implement the vessel/enclosure. The reaction vessel may include any number of pressure controlling means to control the pressure of the reaction vessel. Non-limiting examples of pressure controlling means include a pump, a variable flow limiter, a piston, a diaphragm, a screw, or external forces on a flexible reaction vessel (that change the reaction vessel internal volume), or through the introduction of solids that also effectively change the available internal volume (e.g., the introduction of HMM precursor 20 in solid form).
[0164] As described further herein, the precursors can be introduced in a wide variety of different ways and configurations. As non-limiting examples, the LMM precursor 15 and HMM precursor 20 can be: (1) flowed jointly (pre-mixed) into the reaction vessel; (2) flowed co-axially and directed at a reaction zone(s); (3) flowed in alternating sheets and directed at a reaction zone(s); (4) flowed from alternating sources and directed at a reaction zone(s); (5) flowed from separate sources and directed tangential to the reaction zone; and (6) flowed from separate sources and directed at an angle relative to each other.
[0165] A wide variety of different LMM precursors 15 and HMM precursors 20 can be employed in combination in order to obtain the desired thermal diffusion region and controlling effects. For example, for silicon boride deposition, silane and diborane can be used as LMM precursor 15 gases, while HMM precursor 20 gases such as tetraiodosilane, SiI.sub.4, or decaborane, B.sub.10H.sub.14, can be used. This list is not intended to be exhaustive, and it is only for explanatory purposes. It is the substantive difference in mass and/or diffusivity that is important to achieve the best results. Other examples of LMM precursors 15 and HMM precursors 20 are outlined in the cross-referenced applications, including U.S. Application Ser. No. 62/074,703, incorporated by reference herein.
[0166] The HMM precursor 20 species can be introduced as gases, liquids, critical/supercritical fluids, solids, semi-solids, soft plastic solids, glassy solids, or very viscous liquids. Depending on the precursor chosen, the HMM precursor 20 may liquefy, evaporate, or sublime near the reaction zone(s) 35. The HMM precursor 20 species can vary widely depending on the type of fiber being produced. As non-limiting examples, HMM precursors 20 can be silanes, boranes, organo-aluminum, organo-silicon, organo-boron, metal halide, organometallics, hydrocarbons, fluorocarbons, chlorocarbons, iodocarbons, bromocarbons, or halogenated hydrocarbons species or mixtures thereof. The HMM precursor 20 may also be inert and not decompose, or have very limited decomposition, at the reaction zone 35. The HMM precursor 20 may also physically or chemically inhibit the formation of clusters and particulates near the reaction zone(s) 35.
[0167] Similar to the HMM precursors 20, the LMM precursor 15 species can vary widely depending on the type of fiber being produced, and can be introduced as gases, liquids, critical/supercritical fluids, solids, semi-solids, soft plastic solids, glassy solids, or very viscous liquids. As non-limiting examples, LMM precursors 15 can be silanes, methylsilanes, boranes, organo-aluminum, organo-silicon, organo-boron, metal halide, organometallics, hydrocarbons, fluorocarbons, chlorocarbons, iodocarbons, bromocarbons, or halogenated hydrocarbon species or mixtures thereof. Depending on the HMM precursor 20 and the LMM precursor 15, the LMM precursors 15 may (a) react with at least one HMM precursor 20, causing the LMM precursor to deposit, or partially decompose, such that a new “derived precursor species” will be formed and will be concentrated at the reaction zone(s) 35 (and this derived precursor decomposing, resulting in the growth of the fiber); or (b) act as a catalyst that decomposes the HMM precursor 20 to a derived precursor species (having a lower molar mass than the HMM precursor) that will be concentrated at the reaction zone(s) 35 (and this derived precursor species decomposing, resulting in the growth of the fiber).
[0168] Depending on the desired fiber characteristics, and HMM precursor 20 and LMM precursors 15 used, the precursors can be in a variety of states. For example: (1) the precursors can all be in a gaseous state; (2) the precursor(s) concentrated at the reaction zone 35 may be in a gaseous state while the precursor(s) outside of the reaction zone 35 are in a critical, liquid, or solid state; (3) the precursor(s) concentrated at the reaction zone 35 may be at the critical point while precursor(s) outside of the reaction zone 35 are in a liquid or solid state; (4) the precursor(s) concentrated at the reaction zone 35 may be in a supercritical state, while precursor(s) outside of the reaction zone 35 are in a supercritical, critical, liquid, or solid state; (5) all precursors are at the critical point or are in the supercritical fluid state, or (6) the precursor(s) concentrated at the reaction zone 35 may be in a liquid state while the precursor(s) outside of the reaction zone 35 are in a liquid or solid state. Of course, this is not intended as an exhaustive list. The “liquid” state above can include very viscous liquids or glasses, while the “solid” state can include soft plastic solids or semisolids. See generally,
[0169] In some embodiments, an intermediate molar mass (“IMM”) precursor may also be introduced into the reaction vessel. Depending on the fiber desired, and the LMM precursor 15 and HMM precursor 20 used, an IMM precursor may be introduced to further separate, react with, or break down the LMM precursor 15 and/or HMM precursor 20. For example, where the HMM precursor is hexadecane (C.sub.16H.sub.34) [molar mass=226.45 g/mol] and the LMM precursor is methane (CH.sub.4) [molar mass=16.04 g/mol], an IMM precursor such as carbon tetrafluoride (CF.sub.4) [molar mass=88.00 g/mol] could be added to react with both the methane and hexadecane, to produce a carbon fiber product and hydrogen+hydrogen fluoride by-products. In some embodiments, the IMM precursor is introduced to primarily react with, and break down, the HMM precursor 20 species. For example, where the HMM is icosane (C.sub.20H.sub.42) [molar mass=282.56 g/mol] and the LMM is silane (SiH.sub.4) [32.12 g/mol], an IMM precursor such as bromine (Br.sub.2) [molar mass=159.80 g/mol] can be introduced to react with the hydrogen in the icosane to produce carbon as a product (i.e., deposited as part of the fiber) and hydrogen bromide as a byproduct. While the silane, concentrated at the center of the thermal diffusion region will deposit spontaneously at low temperatures without bromine being present, the decomposition of icosane is enhanced through the reaction with bromine. Generally, the molar mass of the IMM precursor is between that of the LMM precursor and HMM precursor.
[0170] Just as examples, and not as limitations, the following types of fibers can be fabricated using the system and methods described herein: boron, boron nitride, boron carbide, carbon, aluminum oxide, aluminum nitride, silicon carbide, silicon nitride, silicon borocarbide, silicon oxynitride, nickel, iron, titanium, titanium carbide, tantalum carbide, hafnium carbide, tungsten, and tungsten carbide fibers, to name just a few. Other examples are outlined in the cross-referenced applications, including U.S. Application Ser. No. 62/074,703, incorporated by reference herein.
[0171]
[0172] Note that the primary heating means 40 can be any number of options known to those of skill in the art able to create localized reaction zone(s) 35 and thermal diffusion region(s) 10 (either alone or in combination with other primary heating means). As non-limiting examples, primary heating means 40 may be one or more focused spots or lines of laser light, resistive heating (e.g., passing electrical current through contacts on the fiber), inductive heating (e.g. inducing current in the fiber by passing current through coiled wires near or surrounding the fiber), high pressure discharges (e.g. passing current through the precursors from electrodes to the fibers), focused electron beams, focused ion beams, and focused particle bombardment (e.g. from a particle accelerator). For reference, radiative primary heating means 40 can also use soft X-ray, ultraviolet, visible, infrared, microwave, millimeter-wave, terahertz, or radio frequency radiation (e.g. within electromagnetic cavities) to create reaction zones. The primary heating means 40 in
[0173] Secondary heating means are not shown explicitly in
[0174]
[0175] Thus, in one embodiment of the invention that uses the methods of
[0176]
[0177] As shown in
[0178] Thus, from
[0179] It is important to note that the thermal diffusion region 10 need not only be in the gas phase, but may also occur within liquid precursors, critical or supercritical fluids, or combinations of the same. Thus, a mixture of LMM precursor 15 and HMM precursors 20 can enter the reaction vessel as a liquid and remain so within the thermal diffusion region 10 within the liquid. However, in another implementation, the liquid mixture of HMM precursors 20 and LMM precursors 15 can transform locally into a gas at each reaction zone 35, thereby producing a thermal diffusion region 10 within a gas bubble, and a secondary thermal diffusion region 10 in the liquid. Alternatively, one or more precursors, often the HMM precursors 20, can be driven into the reaction vessel as viscous liquids (e.g. silicone oils), viscoelastic polymers (e.g. pitch, rosin), and plastic solids (such as waxes or pitch), which, upon heating, will evaporate and surround each reaction zone 35, thereby creating a thermal diffusion region 10 at each reaction zone 35. In this case, the LMM precursors 15 can be provided as part of the solid or viscous liquid, or they can be flowed into the reaction vessel separately.
[0180] For example,
[0181]
[0182]
[0183]
[0184] In the embodiments shown in
[0185]
[0186]
[0187] Thus, in many embodiments (as shown in
[0188] As mentioned before, when a secondary heating means is used, in addition to influencing the thermal diffusion region, it can partially decompose the HMM precursor 20 or LMM precursor 15 near the reaction zone 35, thereby creating another set of precursor species of even lower molar mass (which we denote as a “derived precursor species”).
[0189] Thus, in one embodiment of the invention for fabricating fibers, at least one LMM precursor 15 is flowed into a reaction vessel and at least one HMM precursor 20 is introduced to the reaction vessel. As described above, the HMM precursor 20 preferably has a molar mass 1.5 to 3 times greater, and more preferably three or more times greater than the LMM precursor 15, and preferably a thermal conductivity substantively lower than that of the LMM precursor 15. One or more reaction zone(s) 35 are created within the reaction vessel by one or more primary heating means 40, resulting in the decomposition of at least one precursor species. The decomposition results in the growth of a solid fiber(s) 25 at each said reaction zone(s) 35. The solid fibers 25 can have a first end at or near the reaction zone(s) 35 and a second end that is drawn backward through a tensioner 45 and wound on a spooling device/mandrel 50 at a rate to maintain the first end within the reaction zone(s) 35. Other means can be used to remove the fiber from the reaction zone. One or more thermal diffusion region(s) 10 are established at/near said reaction zone(s) 35 to partially- or wholly-separate said LMM precursor 15 species from said HMM precursor 20 species using the thermal diffusion effect, thereby concentrating the LMM precursor 15 species at each reaction zone(s) 35. In this embodiment, a secondary heating means 110 using a heated wire is passed through or configured in proximity to the reaction zone 35 to further concentrate the LMM precursor 15 species at/near said heated wire(s) and reaction zone(s) 35, and the concentrated LLM precursor 15 substantively enhances the growth of the solid fiber(s) and the HMM precursor 20 species decreases the flow of heat from the reaction zone(s) 35, relative to that which would occur using the LMM precursor 15 species alone. Although one wire is shown in
[0190]
[0191] In a related implementation to
[0192]
[0193] Also remember that using the embodiment of
[0194] In a similar embodiment to the invention of
[0195] In most embodiments, the invention incorporates feedback means to measure characteristics of the fibers 25 being fabricated, and then use this feedback to control one or more aspects of the fabrication process and ultimately fiber characteristics/properties. Measurements of the geometry, microstructure, composition, and physical properties of the fibers can be made as they are grown. This feedback can be used to control the primary heating means(s) 40 and/or secondary heating means 110. For example, in
[0196] The feedback means (not shown in
[0197] Other devices and methodologies can also be used to obtain feedback of the process, and control the fabrication. In some embodiments, either together with one or more of the options discussed above, or by itself, the thermal diffusion regions 10 and/or the reaction zone 35 can be measured with real-time shadowgraphy or Schlieren imaging techniques to obtain feedback on the relative concentration/densities of the LMM precursors 15 species relative to the HMM precursor 20 species. Thus, in this embodiment, the feedback means is measuring the thermal diffusion region 10 and/or the reaction zone 35, rather than the fiber characteristics. This feedback can be used as input to control one or more aspects of the fabrication process, for example, modifying the primary heating means 40 or secondary heating means 110 to obtain solid fibers at a desired rate with desired fiber characteristics.
[0198]
[0199]
[0200] Thus, in one embodiment, the invention comprises a system for fabricating solid fiber(s) 25 having one or more reaction vessels, each reaction vessel containing or having an associated one or more primary heating means 40 and one or more secondary heating means 110. In use, the primary and secondary heating means create one or more reaction zones 35 and thermal diffusion regions 10 in each reaction vessel where fibers 25 are grown. The system can incorporate one or more spooling devices/mandrel 50 and tensioners 45 for grown fibers 25. The system can also include one or more precursor inlet channel(s), and one or more byproduct outlet channels. In practice, a precursor inlet channel allows the flow of LMM precursor 15 and HMM precursor 20 to flow into the reaction vessel. The primary heating means 40 can remain activated and can provide a relatively steady temperature in the reaction zone 35 and thermal diffusion region 10. The secondary heating means 110 can then be used to modulate/control the concentration of the LMM precursor 15 relative to the HMM precursor 20 at the thermal diffusion region(s) 10 and reaction zones 35. As before, any of the heating means discussed herein can be used for the primary heating means 40 and for the secondary heating means 110.
[0201] In one embodiment, the secondary heating means 110 is chosen from the group of: resistively heated wire(s), or focused infrared-, microwave-, millimeter-wave-, terahertz-, or radio-frequency electromagnetic radiation. If a resistively heated wire is used, in some embodiments, the heated wire(s) passes through, or encircles, the reaction zone(s) 35. In other embodiments, heated wires are interconnected to create at least one thermal diffusive valve. In some embodiments, the heated wire extends to the precursor inlet channel, creating a thermal diffusive conduit to the reaction zone 35 and thermal diffusion region 10, and/or the heated wire extends to the byproduct outlet channel thereby creating a thermal diffusive conduit (for example, see
[0202]
[0203]
[0204]
[0205]
[0206]
[0207]
[0208]
[0209]
[0210] While the disclosure above primarily discusses decomposition and disassociation of the precursors using various heating means, it should be recognized that other methods can also be used. For example, the precursors can be decomposed chemically, using x-rays, gamma rays, neutron beams, or other systems and methodologies. Additionally, while many embodiments discuss drawing the fiber backward during fabrication, and largely keeping the reaction zone stationary, it should be recognized that the fiber could remain stationary, and the reaction zone 35 and/or thermal diffusion region 10 moved. For example, the placement of the primary heating means(s) 40 can be moved. In one embodiment using a stationary fiber, if a laser beam is used as a primary heating means 40, the direction/orientation of the laser beam can be changed, the laser can be placed on a moveable, translatable mount, or various optics and lenses can be used to alter the focus of the laser. Similarly, if heated wires are used as the primary heating means 40, the wires can be moveable and translatable such that the thermal diffusion region 10 and/or reaction zone 35 can be moved.
[0211] Additionally, while the disclosure primarily relates to and utilizes LMM precursors and HMM precursors having highly disparate molar masses, the modulation of the thermal diffusion region 10 and/or reaction zone 35, can still be utilized, and highly beneficial, for many different types of precursors, even when their respective molar masses are not substantively different.
Recording Information on Modulated Fibers, Microstructures, and Textiles and Device for Reading the Same
[0212] As further described herein in some embodiments, methods and systems are disclosed for recording and reading information stored on or within modulated fibers, microstructures, and textiles. It should be noted that while the HMM precursor species and LMM precursor species discussed above can be used as precursors for recording information on modulated fibers as discussed below, depending on the desired characteristics of the fibers, the precursors need not share the same characteristics discussed above with respect to the difference between the HMM precursor and LMM precursor. Indeed, some embodiments of the systems and methods for recording information on fibers and microstructures do not require use or manipulation of a thermal diffusion region. Any number of systems and methods can be used to decompose and grow fibers, including high pressure laser chemical vapor deposition and chemical vapor deposition, hyperbaric laser chemical vapor deposition, electron beam deposition, ion beams, photolysis, and various focused energy sources. Recording and reading information in a fiber-based format is novel in itself.
[0213]
[0214] In another embodiment of the coating method of
[0215] Importantly, in all of these methods of
[0216] In another implementation, shown in in
[0217] One means of encoding alternating materials vs. length is where two precursors are used to grow fibers simultaneously (as disclosed in above, and in provisional U.S. Application No. 62/074,703, entitled “Doped Carbon Fibers and Carbon-Alloy Fibers and Method of Fabricating Thereof from Disparate-Molecular Mass Gaseous, Liquid, and Supercritical Fluid Mixtures”, filed on Nov. 4, 2014, and incorporated by reference herein), and these decompose at different temperatures (e.g. through a difference in rate constants or activation energies), a change in temperature can select for one material over another. For example, a silicon precursor, such as disilane (Si2H6), can be used to grow silicon fibers, but a carbon precursor, e.g. benzene, can be used to provide silicon carbide deposits. Disilane begins to decompose appreciably at 690-920 K, while benzene decomposes between 950-1200 K. Varying the reaction zone temperature during growth gives differing amounts of carbon in the deposit versus length. And since the length scale of the reaction zone is small, this temperature can be changed rapidly (on the order of femtoseconds to milliseconds). For example, in some embodiments using a laser as a primary heating means, the timing of the laser beam (or the power of the laser beam) can be controlled to change the temperature. In a similar implementation, a single precursor that bears two or more elements can be used to deposit one element at one temperature and another element at a higher temperature. For example, the precursor ferrocene, Fe(C5H5)2, is comprised of an iron atom with two attached cyclopentadienyl ligands (C5H5). At a low temperature, the iron is separated from the C5H5 ligands and is deposited without decomposition of C5H5 ligands themselves. At a higher temperature, however, the C5H5 ligands will also decompose, adding carbon to the iron deposits. In another implementation, two precursors with widely different masses or diffusive properties can be used to select one material over another by having a high concentration of the desired material at the reaction zone during writing (e.g., fiber creation) and excluding the other. For instance, since disilane has a molecular mass of 78 amu, and methane has a molecular mass of 16 amu, one could use their differing thermal diffusivities to select for methane at the reaction zone through the thermal diffusion effect. These same characteristics of different reactions at different temperatures, differing masses, and differing thermal diffusivities exist with the different precursors disclosed above, and provisional U.S. Application No. 62/074,703, entitled “Doped Carbon Fibers and Carbon-Alloy Fibers and Method of Fabricating Thereof from Disparate-Molecular Mass Gaseous, Liquid, and Supercritical Fluid Mixtures”, filed on Nov. 4, 2014, and can be used herein depending on the specific characteristics desired.
[0218] The composition-variation approach (
[0219] It is also possible during use of one or more precursors to induce a change in the microstructure of a fiber locally, e.g. to create more sp3-bonded carbon versus sp2-bonded carbon that can be read in various means, e.g. optically by their relative Raman peaks. Graphite (reflective) and glassy carbon (absorptive) also possess different optical properties that can be read optically. There are many different means through which changes in microstructure can be used to encode information.
[0220] As shown in
[0221] A given length can be provided for each bit or byte, similar to the clock timings of microelectronic data, and start and stop bits can be created that have unique diameters or lengths to periodically re-register the length measurement so that errors do not accumulate. An analog method of data representation can also be implemented that can encode the equivalent to analog voltages versus time as fiber diameters versus length. Again, a calibrating start/stop bit can be used to more accurately read out such data. In this implementation, only a single precursor to manufacture the fiber may be required, although it is possible to employ two or more precursors to provide fibers with binary or more complex compositions. Similar analog and/or digital representations can be implemented for fibers having specific compositions and/or coatings.
[0222] Encoding in circular or spiral patterns on fibers can also be used (as coatings, compositions, or geometries), which can increase data density, although these can be more challenging to read-out. Another means of achieving data encoding in fibers is to zig-zag the fibers discretely or in a gradual fashion to represent numbers. In this case, the axis of the fiber is shifted as it is grown, relative to a known reference axis, and the distance, orientation, or angle relative to the reference axis provides the indication of which number is represented. This approach, however, generally results in a lower encoding rate than diameter modulation.
[0223] It is important to note that a secondary heating means (in addition to the primary means) can be used to heat the gases locally and change the outcome of the fiber deposition in a rapid way. Thus, for instance, a focused laser beam can be combined with a heating coil; the laser beam induces the primary growth, while the coil can change the composition, microstructure, or geometry locally by heating the fiber inductively. In this example, the coil could perform grain refinement to change the microstructure, or zone refinement of a dopant within the fiber or as a coating on the fiber. Due to the small size of the fibers, these processes can occur rapidly. A secondary heating means can take many forms, including: wire(s), electrode(s), laser beams(s), etc. Several possible implementations of heating means are shown in
[0224] For example,
[0225]
[0226]
[0227]
[0228] One implementation that speeds up the data-encoding rate uses at least one LMM precursor (e.g. silane, SiH.sub.4), and at least one HMM precursor (e.g. n-icosane, C20H42, or n-tetracontane, C40H82). It can also employ massive reactive gases (e.g. iodine) that are not intended to add a deposit element/compound to the reaction, but can modify the microstructure or geometry of the fibers by their presence, e.g. the formation of sp3- vs. sp2-bonded carbon. This particular implementation employs the thermal diffusion effect to concentrate the LMM precursor at the thermal diffusion region 10 and reaction zone 35 discussed above. Any of the various embodiments disclosed above (e.g.,
[0229] In some embodiments, another aspect of the invention is that each fiber may (optionally) contain a calibration code, located at a designed place on the fiber, that allows it to be unique from the other fibers, but enables it to be read accurately. This also provides another means of encrypting data, and making it harder for unauthorized personnel to read-out the data. The calibration code can provide information on the type of characteristics that are to be read, sensed, or measured to decipher the code, e.g., the electrical conductivities, dielectric constants, thermal conductivity/capacity, optical transmittance, reflectance, and/or absorbance, or selective chemical reactivity/bonding, dangling bonds, or wetting characteristics at the surface of the fibers, or the length of each byte, start/stop bits, fiber diameters v. length, a calibrating start/stop bit, etc. It can also include a code key (discussed below). The calibration code and/or code key can be located in a pre-defined location in or along the fiber so that the calibration code and/or code key can be detected and read.
[0230] To Applicant's knowledge, sequential recording of information on or in fibers has not been done prior to this invention, including recording using active control a plurality of thermal diffusion regions.
[0231] Any of the various embodiments disclosed above that use or implement modulation in or around the reaction zone or thermal diffusion region or the flow of precursor using the selective conduits or switches/valves can be utilized for recording information on fibers. Examples of the modulation in or around the thermal diffusion region or the flow of precursor are shown and discussed in reference to
[0232] Importantly, data can be encoded on extremely stable materials, both physically and chemically, to preserve an archival record of information. For example, in the composition-encoding approach, fibers comprised of tantalum carbide, with a melting point of 3153-4100 K can be encoded with variations in the carbon concentration within the deposit of up to 2:1 (TaC versus TaC0.5). Or titanium oxide fibers can be grown, with varying concentrations of oxygen that change the opacity of the fibers to light—and the data can be read optically. Or the same system can be read by measuring the dielectric constant or resistivity of the deposit versus length.
[0233] A wide variety of different LMM precursors and HMM precursors can be employed in combination in order to obtain the desired thermal diffusion region and controlling effects. For example, for silicon deposition from an LMM precursor, hydrides could be used, including silane and disilane. While for HMM gases, precursors such as tetraiodo methane, or waxes can be used. This list is not intended to be exhaustive, and it is only for explanatory purposes. For instance, there are dozens of possible silicon precursors and wax combinations. Again, uses of LMM precursors and HMM precursors are optional.
[0234] A device to read-out the information recorded or encoded on the fiber is also disclosed. In some embodiments, an example of which is shown in
[0235] The various code keys (if utilized) can also be utilized in the manufacture of the fibers, and in connection with the feedback means and controlling means, when depositing the encoded information. The appropriate control systems for the fiber manufacture alter the operating parameters to encode the desired information using the code key. For example, if differing electrical conductivity is used, the code key might provide that an electrical conductivity between values A and B represents a “0” and an electrical conductivity between values C and D represents a “1”. If the user wants to deposit encoded information representing a data string of 010010011, the control systems of the manufacturing process (for example, the laser power, primary heating means, secondary heating means, amount of precursors, flow of precursor to the reaction zone, pressure, etc.) would be manipulated to ensure that the appropriate material is deposited at the appropriate locations that would trigger the appropriate a sensor reading. The code key can also be fabricated onto the fibers themselves for reading and use by the analog/digital system 470.
[0236] Thus, in one embodiment, a recording media is provided comprising fibers wherein the fibers have specific fiber states along the length of said solid fibers, the fiber states having known lengths (corresponding to a time duration of a signal), wherein values of said fiber states represent digital or analog values (corresponding to signal amplitudes), and wherein the combination of said known lengths and values of said fiber states encodes digital or analog information sequentially along said solid fibers. The “fiber states” can be a variety different characteristics, including (1) fiber geometries, (2) fiber diameters, (3) fiber composition, (4) fiber microstructures, (5) fiber microstructures and fiber composition, (6) physical properties, (7) chemical properties, and (8) presence, absence, or thickness of coatings on the surfaces of said solid fibers, or any combination of the foregoing.
[0237] In the embodiment wherein the “fiber state” is fiber geometry, various alternatives are available, including (a) the slopes of the surfaces of said solid fiber relative to the fiber axis; (b) the azimuthal position of the fiber growth direction relative to a known axis; and/or (c) the orientation of the fiber growth direction relative to a known axis.
[0238] In the embodiment wherein the “fiber state” is fiber composition, various alternatives are available, including (a) fiber compositions include two or more different elements/compounds, including wherein said different elements/compounds being deposited from two or more precursors with disparate decomposition rates versus temperature (b) fiber compositions include two or more different elements/compounds, including wherein said different elements/compounds being deposited from at least one multi-element-bearing precursor that yields disparate elements/compounds versus temperature.
[0239] In the embodiment wherein the “fiber state” is fiber microstructures, various alternatives are available, including where the fiber microstructures include (a) two or more allotropes; and (b) two or more solid phases.
[0240] In the embodiment wherein the “fiber state” is fiber physical properties, various alternatives are available, including optical, electrical, thermal, acoustic, physisorptive, adhesive, or mechanical properties.
[0241] In the embodiment wherein the “fiber state” is chemical properties, various alternatives are available, including chemisorptive, oxidative, reductive, reactive, bonding-, dandling bond-, or wetting-properties.
[0242] In another embodiment, a method of recording digital and/or analog information onto fibers and/or an array of fibers is provided, comprising (1) creating an array of reaction zone(s) within a vessel, wherein decomposition of at least one precursor species occurs; said array of reaction zone(s) being created by a primary heating means, the decomposition resulting in the growth of solid fiber(s) at each said reaction zone(s); (2) said solid fiber(s) having a 1st end at said reaction zone(s) and a 2nd end that is drawn backward through a tensioner 45 and spooling device/mandrel 50, at a rate to maintain the 1st end within (or near) said reaction zone(s); (3) said decomposition being modulated over time by a controlling means to create specific fiber states versus length along the growth direction of said solid fibers; (4) said fiber states having known lengths (corresponding to a time duration of a signal); (5) wherein values of said fiber states represent digital or analog values (corresponding to signal amplitudes); (6) wherein the combination of said known lengths and values of said fiber states encodes digital or analog information sequentially along said solid fibers. Thus, in some embodiments, the solid fibers can form an array that allows for massively parallel encoding of digital and/or analog information.
[0243] In another embodiment, a method of recording digital and/or analog information onto fibers and/or an array of fibers is provided, comprising (1) introducing at least one low-molecular mass (LMM) precursor species into a vessel; (2) introducing at least one high-molecular mass (HMM) precursor species into said vessel, of mass substantively greater than the LMM precursor species, and of thermal conductivity substantively lower than that of the LMM precursor species; (3) creating an array of reaction zone(s) within a vessel by a primary heating means, wherein decomposition of at least one precursor species occurs; (4) establishing thermal diffusive regions (TDRs) at/near said reaction zone(s) by a secondary heating means, to partially- or wholly-separate the LMM precursor species from the high molecular mass precursor species using the thermal diffusion effect, (5) said decomposition resulting in the growth of solid fiber(s) at each said reaction zone(s); said solid fibers being comprised of at least one element from said precursor species; (6) said solid fiber(s) having a 1st end at said reaction zone(s) and a 2nd end that is drawn backward through a tensioner 45 and spooling device/mandrel 50, at a rate to maintain the 1st end within (or near) said reaction zone(s); (7) said decomposition being modulated over time to create specific fiber states versus length along the growth direction of said solid fibers; said modulation occurring by controlling said TDRs by said secondary heating means (independent of said primary heating means); (8) said fiber states having known lengths (corresponding to a time duration of a signal); (9) wherein values of said fiber states represent digital or analog values (corresponding to signal amplitudes); and (10) wherein the combination of said known lengths and values of said fiber states encodes digital or analog information sequentially along said solid fibers.
[0244] The primary heating means can be a focused laser beam, an array of focused laser beams, inductive heating of the solid fibers, high-pressure electric discharges (e.g., plasma) and electric current through the precursor(s), focused line of laser light, and any combination of the foregoing. Other primary heating means are known to those of skill in the art and discussed herein.
[0245] The secondary heating means can be heated wire(s), wherein said heated wire(s) are heated resistively by flowing electrical currents through said wires. The secondary heating means can also be a focused laser beam, array of focused laser beams, high-pressure electric discharges and/or electric current through the precursors. Other secondary heating means are known to those of skill in the art and discussed herein. In some embodiments, the heated wires can be used to “flow” by-product species from decomposition in the reaction zone(s). The heated wires can take a variety of configurations, including but not limited to (a) where the heated wire(s) are comprised of at least two joined, but electrically separate sections, wherein the current through one said section is used to modulate the flow of low-molecular mass precursor species in real-time to the reaction zone(s), (i.e. the said section acts as a thermal diffusive valve); (b) where at least one section of said heated wire(s) is heated by a laser beam, and is used to modulate the flow of low-molecular mass precursor species in real-time to the reaction zone(s), (i.e. the said section acts as a thermal diffusive valve); (c) where at least one section of said heated wire(s) has attached cooling fins that may be heated resistively at their base, and is used to modulate the flow of low-molecular mass precursor species in real-time to the reaction zone(s), (i.e. the said fins act as a thermal diffusive valve); and (d) where at least one section of said heated wire(s) has attached dispersion wires that may be heated resistively to disperse the low-molecular mass precursor species along the thermal diffusive conduit, and is used to modulate the flow of low-molecular mass precursor species in real-time to the reaction zone(s), (i.e. the said dispersion wires act as an inverse thermal diffusive valve).
[0246] In some embodiments, the vessel in which precursors are introduced can also have a pressure controlling means as described above. As discussed above, the species introduced into the vessel can be in various forms. In some embodiments, all species are in the gaseous state. In other embodiments, the species concentrated at the reaction zone(s) are in the gaseous state, while all other species are in the liquid state. In other embodiments, the species concentrated at the reaction zone(s) are at the critical point or in the supercritical state, while all other species are in the liquid or solid state. In other embodiments, all species are at the critical point or are in the supercritical fluid state.
[0247] As discussed above, the sensing means (or sensors) can be used to obtain feedback of the decomposition of the precursors and the growth of the fibers, and to control secondary heating means to control the decomposition, growth, and composition of the solid fibers to encode digital and/or analog information. The sensing means (or sensors) can be of a wide variety of sensing devices/spectrometers known to those of skill in the art, including acoustical, mechanical, optical, ultraviolet, infrared, and X-ray.
[0248] In yet another embodiment, an apparatus for reading information from one or more of an array of solid fibers is provided, wherein (a) the fibers have specific fiber states along the length of said solid fibers; (b) the fiber states having known lengths (corresponding to a time duration of a signal); (c) wherein values of said fiber states represent digital or analog values (corresponding to signal amplitudes); (d) wherein the combination of said known lengths and values of said fiber states encodes digital or analog information sequentially along said solid fibers; (e) wherein said apparatus has a multiplicity of sensors located in a surface/grid; (f) said surface/grid having holes/passages through which fibers may pass; (g) said surface/grid being translatable (forward or backwards) along the length of said solid fibers (along the direction of fiber growth); and (h) said multiplicity of sensors being electrically connected to a computer or data acquisition system; wherein all said sensors can be read at a rate exceeding the Nyquist sampling criterion as said surface is translated. In some embodiments, the translation can be oscillated, to obtain multiple readings of said fibers.
Functionally-Shaped and Engineered Short Fiber and Microstructure Materials
[0249] In one aspect, this invention utilizes a new, highly flexible manufacturing process to grow short fibers from precursors. Precision, functionally-shaped, and engineered short fibers can be created through control of the process properties, e.g. heating means properties, precursor flow geometries and flow rates, local pressures, etc. as discussed herein. It should be noted that while the HMM precursor species and LMM precursor species discussed above (along with use of thermal diffusion regions) can be used as precursors for creating precision, functionally-shaped, and engineered fibers, depending on the desired characteristics of the fibers, the precursors need not share the same characteristics discussed above with respect to the difference between the HMM precursor and LMM precursor. Indeed, some embodiments of the systems and methods for creating precision, functionally-shaped fibers and microstructures do not require use or manipulation of a thermal diffusion region. Any number of systems and methods can be used to decompose and grow fibers, including high pressure laser chemical vapor deposition and chemical vapor deposition, hyperbaric laser chemical vapor deposition, electron beam deposition, ion beams, photolysis, and various focused energy sources.
[0250] Often, the primary heating means is a focused electromagnetic beam or other directed energy source, such as a laser, ion, or electron beam. However, other primary heating means can also be used, such as inductive or microwave coupling into the fiber material. The primary heating means can be modulated, shaped, or oriented to create specific geometries in the solid fibers as they are grown, rather than as an after-the-fact additional process that modifies existing fibers. In addition, more than one fiber can be grown at a time by using a multiplicity of primary heating means. For example, typical primary heating means could be an array of focused laser beams, an array of focused laser beams and a focused line of laser light, an array of high-pressure discharges, an array of electrodes that passes electric current through the precursors, an array of inductive primary heating means, and a set of resistively heated wires. And more than one primary heating means can be employed to provide additional processing flexibility.
[0251] This invention also provides for feedback control of the desired fiber characteristics, including shape, composition, and microstructure of the fiber materials, so that these characteristics can be controlled during the growth process (see
[0252] In addition to straight (cylindrical fibers), several specific fiber shapes versus length are also important for optimal composites, e.g. fibers that have sinusoidal diameter vs. length profiles (see
[0253] In addition, the cross-sections of fibers need not be circular, but could be grown in a wide-variety of shapes shown in
[0254] In addition, the growth direction of the fibers can be reoriented during deposition in a continuous fashion to create geometries not possible through any spinning or extrusion process. Just as examples, the position of the reaction zone can be altered (as described herein) or the substrate on which the fibers are being grown can be moved or reoriented. There are many possible shapes induced by reorientation and shown in
[0255] Even more complex shapes can be created by changing the intensity of the primary and/or secondary heating means, even as it is reoriented. For example, a complex curved fiber can be created with periodic undulations along its length (see
[0256] Another aspect of this invention is that it inherently provides sub-100 nanometer local smoothness in the surfaces that are grown, allowing for improved bonding at the fiber-matrix interface (e.g. through Van Der Waals or Covalent bonding). This can be improved to even greater precision through feedback control of the primary and/or secondary heating means and other process parameters during the growth process as described above. The carbon fiber shown in
[0257] Another aspect of the invention is that multiple materials can be grown simultaneously to create a functionally-graded fiber. For instance, where two materials are deposited at the same time under a Gaussian laser focus, with different threshold deposition temperature and kinetics, one material will naturally be more highly concentrated in the core of the fiber, while the other tends to grow preferentially toward the outside of the fiber. However, rather than having a distinct step transition from one material to another, as would be present in a coating for example, they can be blended together with a gradual transition from core to outer material. This can create a stronger transition from core to outer material that will not separate. This permits a very strong material that might otherwise react or degrade in contact with the matrix material to be permanently protected by an exterior material that contacts the matrix material. This can potentially improve bonding between fiber and matrix materials, allow for flexible transitions between fiber and matrix, and prevent undesirable alloying or chemical reactions. There are many possible implementations of this multiple material approach, and the fibers can be functionally graded radially and axially. The method for applying the precursors can also vary. For example, they can be flowed pre-mixed or separately to create anisotropic variations in composition (see
[0258]
[0259] Importantly, fibers can also be branched to create additional resistance to fiber pull-out. Fibers can form networks of connected strands, an example of which is shown in
[0260] In some embodiments, the invention also provides for a means of collecting and removing the fibers following their growth, with optional recirculation or re-use of an initial substrate (see
[0261] In another embodiment, shown in
[0262] In another embodiment shown in
[0263] In another embodiment, fibers can be grown on a wire, and the wire (ultrasonically) vibrated following growth to remove the fibers. In another embodiment, the fibers can be removed by flowing a fluid across the fibers. In another embodiment, electrostatic forces can be used to remove the fibers from the surface. Finally, in another embodiment, a temporary coating can be dissolved away from the substrate, removing the attachment point for the fibers.
[0264] In another embodiment, shown in
[0265] Following removal, the short fibers can be collected in a bin and then suctioned from the growth system with a vacuum or similar device. In another embodiment, fibers can pass through a vapor lock that prevents the precursor from leaving the reaction vessel, but moves the solid fibers through another fluid to the outside of the growth system. In another embodiment, fibers can be collected in a bin and removed through a traditional load-lock. There are many possible means of collecting and removing fibers in bulk; this is not intended as an exhaustive list.
[0266] It is also possible to utilize a reusable substrate in the form of a tape, mesh, or lattice onto which the fibers are grown. This substrate may be flexible, which can be coiled up and stored for later use, as shown in
[0267] Thus, in one embodiment of the invention, an engineered solid fiber material can be grown from fluid-based chemical precursors by a heating means that is less than 4 mm in cross-sectional extent/diameter, that is grown to a prescribed length, that has a prescribed cross-sectional fiber shape and size that can vary along its length, that has a prescribed composition versus radius, that has a prescribed geometric orientation versus its length, and that has a prescribed microstructure.
[0268] As described above, in some embodiments, the cross-section of the fiber can be circular, elliptical, triangular, X-shaped (cross), I-shaped, L-shaped, T-shaped, multi-pointed star, multi-pointed stars with T-like points, rectangular, hexagonal, polygonal, arbitrary, and/or modulated cross-sections. The cross-sectional fiber shape may vary along its length or it may be constant. In some embodiments, the cross-sectional fiber shape may vary along its length and repeat periodically. In some embodiments, the cross-sectional fiber shape varies along its length, and repeats periodically, and the cross-sectional fiber shape is a composite of two or more repeating profiles, and where at least one profile is modulating another. In some embodiments, the cross-sectional fiber size varies along its length while in others the fiber size is constant along its length. In some embodiments, the cross-sectional fiber size varies along its length, forming a profile that is selected from at least one of the following: (a) sinusoidal, (b) elliptical, (c) parabolic, (d) hyperbolic, (e) Gaussian, (f) saw-toothed/ramp-like, (g) dog-bone-like shapes, and (h) bed-post-like shapes. In some embodiments, the cross-sectional fiber size varies along its length and repeats periodically, forming a repeating profile that includes at least one of the following profiles: (a) sinusoidal, (b) elliptical, (c) parabolic, (d) hyperbolic, (e) Gaussian, (f) saw-toothed/ramp-like, (g) dog-bone-like shapes, and (h) bed-post-like shapes. In other embodiments, the cross-sectional fiber size varies along its length and repeats periodically, forming a repeating profile that includes linear sections with at least one of the following profiles: (a) sinusoidal, (b) elliptical, (c) parabolic, (d) hyperbolic, (e) Gaussian, (f) saw-toothed/ramp-like, (g) dog-bone-like shapes, and (h) bed-post-like shapes.
[0269] In some embodiments, the cross-sectional fiber size varies along its length and repeats periodically at more than one frequency, forming a complex multi-frequency repeating profile. In some embodiments, the cross-sectional fiber size varies along its length, forming a profile, and repeats periodically, and whose profile is a composite of two or more repeating profiles, and where at least one profile is modulating (or superimposed upon) another. In some embodiments, the cross-sectional fiber size varies randomly along its length, forming an arbitrary profile that does not repeat any particular pattern. In some embodiments, the cross-sectional fiber size varies along its length and repeats periodically, and whose profile has self-similar repeating profiles at different length scales (a fractal profile).
[0270] As described herein, the composition of the fibers can be varied depending on the desired characteristics. Thus, in some embodiments, the prescribed composition versus radius is a constant. In some embodiments, the prescribed composition versus radius varies from one or more core materials in the fiber center to one or more outer materials at the outer surface of the fiber. In some embodiments, the prescribed composition versus radius varies continuously from one or more core materials in the fiber center to one or more outer materials at the outer surface of the fiber, according to a prescribed concentration function. In some embodiments, the composition is a radial blend from core material(s) to outer material(s). In some embodiments, the composition is an axial blend from one material to another material. In some embodiments, the composition changes along a direction perpendicular to the axis of said solid fiber (e.g. a bi-morph).
[0271] As described herein, the microstructure of the fiber can be varied depending on the desired characteristics. Thus, in some embodiments, the prescribed microstructure of the fiber is amorphous or glassy. In some embodiments, the prescribed microstructure is a single crystal.
[0272] As also described herein, the orientation of the fiber can be varied depending on the desired characteristics. Thus, in some embodiments, the prescribed orientation changes along said fiber material's length. In some embodiments, the prescribed orientation changes along said fiber material's length according to at least one of the following patterns: a curvi-linear shape, a gentle curve, a sinusoid, a parabola, a hyperbola, a U-shape, hooked shapes, barbed shapes, zigzag-like shapes, ramp-like shapes, coiled shapes, and modulated shapes. In some embodiments, the fiber material branches (or divides) from one fiber into two or more fibers during growth. In some embodiments, the fiber material is locally smooth to better than 500 nm RMS roughness over at least 5 microns of length. In some embodiments, the fiber material is grown to a pre-scribed length, to better than 5 microns accuracy.
[0273] In another embodiment, the invention relates to a method for growing one or more engineered solid fibers from a chemical precursor within a reaction zone. The fibers may be grown on a reusable substrate. The solid fibers may have a first end, and at least one second end, said first end being attached temporarily at the reusable substrate(s), said second end(s) being within said reaction zone(s). The reaction zone can be created by a primary heating means and optionally a secondary heating means. In some embodiments, the reaction zone can be modulated and controlled in real-time, thereby generating specific fiber cross-sections, profiles, and geometric orientations versus length. The specific fiber cross-sections, profiles and geometric orientations versus length can be monitored in real-time by a monitoring system (or feedback means), and used to control the manufacturing process and properties of the reaction zone(s). The length of said solid fibers may also be monitored in real-time by a monitoring system (or feedback means), and used to control the manufacturing process and properties of the reaction zone(s), thereby growing said solid fibers to predetermined terminal lengths. The fibers may be detached and collected after growth from the substrate(s) by a collecting mechanism and the substrate(s) may be recycled/reused for the growth of additional solid fibers, for example, by a recycling mechanism (e.g., a rotating drum or belt).
[0274] As described above, the precursor can be in various forms, including gaseous fluids, liquid fluids, critical-fluids, or supercritical-fluids. The substrate is preferably reusable, and preferably has a texture, composition, or surface coating that provides sufficient adhesion during growth to secure a first end to the reusable substrate, while having sufficiently limited adhesion to allow said first end to be removed by a collecting mechanism (e.g., a wiper or knife-blade). The substrate can be of various forms, including but not limited to a wire, wire mesh, plate, wafer, flexible film, disc, drum, belt, helical coil, etc.
[0275] As described herein, in some embodiments, the reaction zone(s) can be split, thereby creating additional second end(s) for each fiber, which are branched off each fiber. The primary heating means can be any of the heating means discussed above, including but not limited to an array of focused laser beams, an array of focused laser beams and a line of focused laser light, two or more arrays of focused laser beams, high-pressure discharges, electric current through said precursors, inductive heating, coupled electromagnetic radiation, and/or a resistively heated wire.
[0276] As described herein, in some embodiments, the properties of the reaction zone can be altered using the systems and methods discussed above, including but not limited to the shapes, sizes, positions, and geometric orientations of the reaction zone(s), as well as the reaction rates across said reaction zones. In some embodiments, the reaction zones are created, modulated, and controlled in real-time, by (1) a primary heating means, (2) the flow rate of said chemical precursor(s), and (3) the local concentration of said chemical precursor(s), thereby modulating the cross-sectional shape, size, composition, and microstructure of said second end(s) in real-time to achieve specific fiber cross-sections, profiles, geometric orientations, compositions, and microstructures versus length.
[0277] In some embodiments of the method for growing the fibers, the cross-sections of the fiber(s) are controlled to desired size with a tolerance of better than 500 nm over a 5 micron length, terminal length is accurate to 5 microns or less, and fibers can have any of the cross-section shapes, profiles, geometric orientations, compositions, and variations described above (e.g., varying along the fiber's length, or constant, repeating or arbitrary, etc.).
[0278] In some embodiments, the reaction zones are also modulated and controlled in real-time by a secondary heating means, as described above, which may be, but is not limited to, at least one heated wire, which is heated resistively, inductively, or through coupled electromagnetic radiation.
[0279] In some embodiments, the reaction zones may also be modulated and controlled in real-time by introducing at least one high molar mass precursor and at least one low molar mass precursor, where this mixture will at least partially separate in the presence of a thermal gradient within the reaction zone; thereby modulating the reaction rate across said reaction zone when either the thermal gradient or the concentration of either precursor is changed. It should be recognized that the use of high molar mass precursors and low molar mass precursors as described herein is not required to create the functionally shaped and engineered fiber described herein.
[0280] In some embodiments, the monitoring system (or feedback means) is selected from at least one of the following: interferometric pattern measurements (e.g. a Fabry-Perot interferometer), adaptive optic focal-plane recognition, secondary laser beam attenuation, slit imaging/sensing of fiber lengths, knife-edge and chopper techniques (e.g. attenuation or shadowgraphy), ultrasonic measurements, and thermal measurements (e.g. thermal conduction to sensors in the substrate).
[0281] In some embodiments, a collecting mechanism is used to detach the solid fibers from a reusable substrate. The collecting mechanism (or “collecting means”) can take a variety of forms, including but not limited to: (1) translation and/or rotation of said reusable substrate, thereby driving said solid fibers against a wiper/blade, (2) moving a wiper/blade across said reusable substrate, (3) flexing a flexible substrate, (4) vibrating/shaking the substrate, (5) spinning the substrate to create centrifugal forces to remove said solid fibers, (6) flowing a fluid across said substrate which carries the solid fibers away, (7) using electrostatic/magnetic forces to remove the fibers, and (8) dissolution/etching of temporary coatings on said reusable substrate.
[0282] In some embodiments, a recycling mechanism can be used to cause the reusable substrate to be translated, rotated, or reoriented after a batch of said solid fibers are grown to bring said reusable substrate back into alignment with said reaction zone(s) to grow additional solid fibers. In some embodiments, the recycling mechanism causes the reusable substrate to be coated with a temporary coating after a batch of said solid fibers are grown, to grow additional solid fibers on said temporary coating. The recycling mechanism can take a variety of forms, including but not limited to: (1) collection in a bin and removal with a load-lock, (2) collection in a bin/tube and suction with a flowing fluid, (3) collection in a filter using a flowing fluid, (4) electrostatic collection on charged materials, (5) magnetic collection using magnetic materials/devices, and (5) using Van Der Waals forces and collection surfaces with high surface areas.
[0283] The substrate can be reusable in some embodiments. In some embodiments, the reusable substrate is a flexible tape or lattice that can be coiled in such a manner that said solid fibers remain on said flexible substrate and can be rolled up and stored for direct or indirect use in composite lay-ups.
Beam Intensity Profiling and Control of Fiber Internal Microstructure and Properties
[0284] A means of controlling both the beam intensity profile and shape of the thermal diffusion region can be important for obtaining desired microstructures for high-quality fiber. This portion of the invention focuses on creating useful primary heating means intensity profiles that will give useful fiber properties.
[0285] There are many beneficial intensity profiles that can be generated.
[0286] There are many ways, some known to those skilled in the art, some less so, that can be used to generate desired beam intensity profiles for fiber growth. Methods included in this invention are: refractive and reflective field mappers that employ controlled phase-front manipulation, gratings and diffractive optics, vortex beam shapers, superposition of diode-laser beamlets, microlens diffusers, adaptive optics, spatial light modulators, liquid crystal modulators, etc. This is not intended as an exhaustive list.
[0287] Now, the incident (laser) beam intensity profile can, through heat transfer, influence the temperature rise at the fiber surface within the reaction zone 35, as well as the shape of the thermal diffusion region 10. For example, a circular laser intensity profile can heat a fiber tip at its periphery, yielding a reaction zone that is hotter at the periphery than in the center, and a thermal diffusion region that is hottest in a ring within the surrounding fluid near the fiber periphery. In contrast, a Gaussian beam intensity profile would yield the thermal diffusion region that is hottest in the center. By using a circular laser intensity profile, the thermal diffusion effect drives the by-products of reaction, not to the center of the fiber, but to its edges, allowing the fiber to grow more rapidly in the center. This removes the TDGS described previously.
[0288] For example, as shown in
[0289] One subset of such a circular profile is a Bessel-shaped beam, which can be described by a Bessel function of the first kind. Only mode 1 is shown in
[0290] Most embodiments of the invention utilize such beam profiles/shapes for the first time to grow three-dimensional fibers by HP-LCVD, wherein the microstructure of the fibers are controlled to provide optimal material properties. It should be also noted that by varying the beam profile as a fiber grows, one can also induce phase and compositional changes that can be used for recording information (as discussed in another section of this application).
[0291] Consider the three fibers shown in
[0292] Similarly the strength of silicon carbide fibers grown by this technique can vary greatly depending on the beam intensity profile. This is because SiC can be grown in three phases: amorphous SiC, β-SiC, and α-SiC, in order of increasing deposition temperature. Hence, where the induced temperature rises at the surface can cross phase boundaries, one will generate two or more phases in a SiC fiber. As the strength of these phases are not the same (nor even isotopic for the crystalline phases), the value of the SiC fiber for fiber reinforcement depends on how well the primary heating means is profiled. This is true not only of carbon and SiC fibers, but most materials, especially binary, ternary, quaternary, and more complex compounds/alloys.
[0293] In this invention, we offer several new methods of generating useful primary heating means intensity profiles/geometries for fiber growth. Examples can be seen in
[0294] In the embodiment shown in
[0295] The embodiment shown in
[0296] In addition, very rapid scanning of one or more “micro beamlets” onto a fiber surface can simulate a complex beam profile over an extended area. In this case, the time for the surface to cool below the deposition threshold should be much longer than the repetition rate of the micro beamlet pattern. A pulsed laser can also be used, so long as the repetition rate is sufficient.
[0297]
[0298] Remember, a secondary heating means can also be used in conjunction with all of the profiled laser beam methods described herein. A secondary heating means can also, through heat transfer, potentially influence the temperature profile on the fiber surface. For example, a wire coil surrounding a fiber (as in
[0299] Thus any fiber deposition system is preferably designed to optimize the primary heating means profile/geometry (e.g. a focused beam) and secondary heating means geometry/profile (e.g. a conductive wire assembly). In addition, their placement on the fiber can be important. In many embodiments, these are used in concert to control both the reaction zone(s) and thermal diffusion region(s).
[0300] In some embodiments, a reaction zone is created within a reaction vessel to decompose at least one precursor, the decomposition resulting growth of a solid fiber in the reaction zone. The reaction zone is induced by a temperature rise at the surface being generated by a primary heating means and the temperature regions being controlled to have specific induced temperature rise at surface versus position and time at the surfaces of the solid fibers and within the solid fibers. As such, the fibers can be grown having specific microstructural properties by controlling the induced temperature rise at surface.
[0301] In some embodiments, the microstructural properties can be uniform across any cross section of the fibers. The cross section can also have two or more microstructural properties, and arranged to give desired physical and/or chemical properties, e.g., Young's moduli, Poisson's ratios, tensile strengths, compressive strengths, shear strengths, corrosive resistance, and/or oxidation resistance of the solid fiber.
[0302] In some embodiments, the fibers can be comprised of at least 60 atomic percent (at. %) carbon.
[0303] Various embodiments use specific beam intensity profiles versus radial position (to create induced temperature rises at the reaction zones), which can be approximately represented by functions with the following shapes: (a) flat top contours, (b) contours with central minima, (c) contours with a central depression and local central peak, (d) multiple-ring like shapes, and (e) toroidal shapes. The specific induced beam intensity profiles versus radial position can also be approximately represented by superpositions of the following functions: (a) Sinusoidal functions, (b) polynomials, (c) Bessel functions, (d) Laguerre-Gaussian functions, (e) associated Laguerre Polynomials, (f) and Hermite-Gaussian functions. Various modes of these above beams (functions) can be used solely or in concert to generate a desired intensity profile and temperature rise at the surface. For example, the beam intensity profiles can be generated from multiple Gaussian beam intensity profiles, superimposed to obtain a more globally-even temperature distribution.
[0304] The use of laser beam profiling to enhance fiber and microstructure fabrication can be implemented in any of the embodiments discussed herein, including use of LMM precursors, HMM precursors, and thermal diffusion regions. It can also be implemented for use in recording information on or in fibers and microstructures and the functionally shaped and engineered fibers. Thus, in one embodiment, a LMM precursor and a HMM precursor having substantially disparate molar masses are introduced into a reaction vessel, wherein the HMM precursor also has a thermal conductivity substantially lower than the LMM precursor. A thermal diffusion region is created at or near the reaction zone to partially or wholly separate the LMM precursor from the HMM precursor using the thermal diffusion effect, thereby concentrating the LMM precursor species at the reaction zone, and enhancing the growth of the solid fiber, and the HMM precursor species decreasing the flow of heat from the reaction zone relative to that which would occur using the LMM precursor alone. The thermal diffusion region can be at least partially created by an array of focused laser beam, with the focused laser beams are in the shape of a ring, with a maxima in a circle, and a local minimum in the center. Any of the laser beam profiles discussed herein can be used.