PRECOATED ALUMINUM MATERIAL AND ALUMINUM COMPOSITE MATERIAL

Abstract

A precoated aluminum material to which various resin members can be bonded and an aluminum composite material that is prepared using this precoated aluminum material are provided. A precoated aluminum material (1) comprises: a substrate (2) composed of an aluminum material; and a primer coating (3) formed on the substrate (2). The primer coating (3) contains urethane resin. In the infrared-absorption spectrum of the primer coating (3), the value of the optical absorption A.sub.C═O at the peak top of the maximum peak among peaks present in the wavenumber range of 1,180-1,330 cm.sup.−1 is 0.8-1.5 times that of the optical absorption A.sub.urethane at the peak top of the maximum peak among peaks present in the wavenumber range of 1,670-1,770 cm.sup.−1.

Claims

1. A precoated aluminum material, to which a resin member is bondable, comprising: a substrate composed of an aluminum material; and a primer coating formed on the substrate; wherein: the primer coating: contains urethane resin; and has an infrared-absorption spectrum in which the value of the optical absorption A.sub.C═O at the peak top of the maximum peak among peaks present in the wavenumber range of 1,180-1,330 cm.sup.−1 is 0.8-1.5 times that of the optical absorption A.sub.urethane at the peak top of the maximum peak among peaks present in the wavenumber range of 1,670-1,770 cm.sup.−1.

2. The precoated aluminum material according to claim 1, wherein, in the infrared-absorption spectrum of the primer coating, the value of the optical absorption A.sub.COC at the peak top of the maximum peak among peaks present in the wavenumber range of 990-1,150 cm.sup.−1 is 0.7-1.3 times that of the optical absorption A.sub.urethane.

3. The precoated aluminum material according to claim 1, wherein, in the infrared-absorption spectrum of the primer coating, the value of the optical absorption A.sub.aromatic at the peak top of the maximum peak among peaks present in the wavenumber range of 660-760 cm.sup.−1 is 1.0-1.7 times that of the optical absorption A.sub.urethane.

4. The precoated aluminum material according to claim 1, wherein the urethane resin contains a structural unit derived from a polyester polyol.

5. The precoated aluminum material according to claim 1, wherein the urethane resin contains a structural unit derived from an aromatic polyisocyanate.

6. The precoated aluminum material according to claim 1, wherein the primer coating contains 3-50 parts by mass of an acrylic resin to 100 parts by mass of the urethane resin.

7. The precoated aluminum material according to claim 1, wherein the primer coating contains 0.3-13 parts by mass of a melamine resin in relation to 100 parts by mass of the urethane resin.

8. An aluminum composite material comprising: the precoated aluminum material according to claim 1; and a resin member, which contains one or two or more from among polybutylene terephthalate, polyamide, polyphenylene sulfide, and acrylonitrile-butadiene-styrene copolymer and is bonded to the primer coating of the precoated aluminum material.

9. The precoated aluminum material according to claim 2, wherein, in the infrared-absorption spectrum of the primer coating, the value of the optical absorption A.sub.aromatic at the peak top of the maximum peak among peaks present in the wavenumber range of 660-760 cm.sup.−1 is 1.0-1.7 times that of the optical absorption A.sub.urethane.

10. The precoated aluminum material according to claim 9, wherein the urethane resin contains a structural unit derived from a polyester polyol.

11. The precoated aluminum material according to claim 10, wherein the urethane resin contains a structural unit derived from an aromatic polyisocyanate.

12. The precoated aluminum material according to claim 11, wherein the primer coating contains 3-50 parts by mass of an acrylic resin per 100 parts by mass of the urethane resin.

13. The precoated aluminum material according to claim 12, wherein the primer coating contains 0.3-13 parts by mass of a melamine resin per 100 parts by mass of the urethane resin.

14. An aluminum composite material comprising: the precoated aluminum material according to claim 13; and a resin member bonded to the primer coating of the precoated aluminum material, the resin member comprising at least one polymer selected from the group consisting of polybutylene terephthalate, polyamide, polyphenylene sulfide, and acrylonitrile-butadiene-styrene copolymer.

15. A composition of matter, comprising: a substrate composed of aluminum or an aluminum alloy; and an adhesive primer coating bonded to the substrate and comprising a polyurethane; wherein an infrared-absorption spectrum of the adhesive primer coating exhibits: a maximal value of optical absorption A.sub.C═O in the wavenumber range of 1,180-1,330 cm.sup.−1, a maximal value of optical absorption A.sub.urethane in the wavenumber range of 1,670-1,770 cm.sup.−1, and the maximal value of optical absorption A.sub.C═O is 0.8-1.5 times the maximal value of optical absorption A.sub.urethane.

16. The composition of matter according to claim 15, wherein the infrared-absorption spectrum of the adhesive primer coating further exhibits: a maximal value of optical absorption A.sub.COC in the wavenumber range of 990-1,150 cm.sup.−1, a maximal value of optical absorption A.sub.aromatic in the wavenumber range of 660-760 cm.sup.−1, the maximal value of optical absorption A.sub.COC is 0.7-1.3 times the optical absorption A.sub.urethane, and the maximal value of optical absorption A.sub.aromatic is 1.0-1.7 times the optical absorption A.sub.urethane.

17. The composition of matter according to claim 16, wherein the polyurethane is composed of alternating structural units derived from a polyester polyol and from an aromatic diisocyanate.

18. The composition of matter according to claim 17, wherein the adhesive primer coating further contains 3-50 parts by mass of an acrylic resin per 100 parts by mass of the polyurethane.

19. The composition of matter according to claim 18, wherein the adhesive primer coating further contains 0.3-13 parts by mass of a melamine resin per 100 parts by mass of the polyurethane.

20. An aluminum composite material comprising: the composition of matter according to claim 17; and a resin member bonded to the adhesive primer coating, the resin member comprising at least one polymer selected from the group consisting of polybutylene terephthalate, polyamide, polyphenylene sulfide, and acrylonitrile-butadiene-styrene copolymer.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0020] FIG. 1 is a partial, cross-sectional, enlarged view that shows the principal parts of a precoated aluminum material according to a working example.

[0021] FIG. 2 is an explanatory diagram that shows the infrared-absorption spectrum of the primer coating of Test Material A1 according to the working example.

[0022] FIG. 3 is an explanatory diagram that shows the infrared-absorption spectrum of the primer coating of Test Material A2 according to the working example.

[0023] FIG. 4 is an oblique view of a test piece used in the evaluation of the shear strength of adhesive bonds according to the working example.

MODES FOR CARRYING OUT THE INVENTION

[0024] In the above-mentioned precoated aluminum material, the material properties and the grade of the aluminum material that constitutes the substrate are not particularly limited. Aluminum or an aluminum alloy having the desired characteristics in accordance with the application of the aluminum-alloy composite material after a resin member has been bonded to the aluminum or the aluminum alloy can be used as the substrate.

[0025] For example, in a situation in which the aluminum-alloy composite material is to be used in an application such as a mechanical part, A1000-series aluminum (pure aluminum), A2000-series alloy, A3000-series alloy, A5000-series alloy, A6000-series alloy, A7000-series alloy, or the like can be used as the aluminum material that constitutes the substrate.

[0026] In addition, in a situation in which a metal part, which is obtained by forming a sheet as in a body panel of an automobile, is to be substituted with an aluminum composite material, A5000-series alloy, which has good formability, A6000-series alloy, which has good bake hardenability, that is, it has a property such that its strength increases when hardened by heating, such as by paint-baking, or the like can be used as the aluminum material that constitutes the substrate. In a situation in which a rod-shaped metal part, such as a door beam, a bumper beam, instrument-panel reinforcement, or the like of an automobile is to be substituted with an aluminum-alloy composite material, A6000-series alloy, which excels in extrudability, A7000-series alloy, which is advantageous for its high strength and for lightening, or the like can be used as the aluminum material that constitutes the substrate.

[0027] In a situation in which the aluminum composite material is to be used in a component for a heat exchanger or the like, A1000-series aluminum, which excels in corrosion resistance and thermal conductivity, A3000-series alloy, which exhibits a good balance among corrosion resistance, thermal conductivity, and strength, or the like can be used as the aluminum material that constitutes the substrate.

[0028] In a situation in which the aluminum composite material is to be used in a component of a vehicle such as a train, A6000-series alloy, which excels in extrudability, A7000-series alloy, which is advantageous for its high strength and for weight reduction, or the like can be used. In a situation in which the aluminum composite material is to be used in a component of a ship or the like, A5000-series alloy, which excels in ductility and corrosion resistance, or the like can be used. In a situation in which the aluminum composite material is to be used in the component of an aircraft or the like, A2000-series alloy, A7000-series alloy, and the like, which have high strength, can be used.

[0029] The substrate may have an undercoating on its surface. By forming the primer coating on the undercoating, adhesion between the substrate and the primer coating can be further increased. As a result, the adhesive strength between the substrate and the resin member of the aluminum-alloy composite material can be further increased.

[0030] For example, a reactive-type coating, such as a phosphoric-chromate coating, a titanium-based coating, and a zirconium-based coating; a deposition-type coating composed of a coating film that contains a metal compound, such as a chromium compound, a titanium compound, or a zirconium compound, and a binder, which holds the compound on the substrate; a porous anodized coating that is formed by electrolysis in a phosphoric-acid bath, a sulfuric-acid bath, or an alkaline bath; a boehmite coating; or the like can be used as the undercoating.

[0031] The undercoating is preferably a phosphoric-chromate coating or a porous anodized coating. Phosphoric-chromate coatings are low cost, which is required in processing, and excel in mass producibility and corrosion resistance. In addition, after the primer has been applied to the porous anodized coating, the primer tends to penetrate into the pores of the anodized coating. Consequently, owing to an anchoring effect, adhesion between the primer coating and the substrate can be further improved.

[0032] The primer coating is provided on the substrate. The primer coating may cover the entire surface of the substrate or may cover a portion of the substrate. From the viewpoint of reducing the amount of the primer used, it is preferable that the primer coating covers a portion of the substrate.

[0033] The amount of the primer coating that is adhered is not particularly limited; however, in case the adhered amount is too small, then the resin of the primer will be introduced into the resin member, and thereby the amount of the resin in the primer coating existing between the substrate and the resin member will tend to become insufficient. As a result, there is a risk that it will lead to a decrease in adhesion with the substrate. In addition, in case the adhered amount is too large, the primer coating will tend to undergo cohesive failure when an external force has been applied, and there are situations in which that will lead to a decrease in the adhesive strength between the substrate and the resin member.

[0034] From the viewpoint of avoiding such problems, the amount of adhered primer coating is preferably 0.1-10 g/m.sup.2, more preferably in the range of 1-7 g/m.sup.2, and yet more preferably in the range of 2-5 g/m.sup.2.

[0035] The primer coating contains a urethane resin. For example, a polymer compound obtained by a polyaddition reaction of a polyisocyanate with a polyol can be used as the urethane resin. For example, an aliphatic isocyanate, such as hexamethylene diisocyanate, isophorone diisocyanate, etc.; an aromatic isocyanate, such as toluene diisocyanate, diphenylmethane diisocyanate, etc.; or the like can be used as the polyisocyanate. These isocyanates may be used independently, or two or more may be used in combination.

[0036] The urethane resin preferably contains a structural unit derived from an aromatic isocyanate. In this case, adhesion between the primer coating and the substrate can be further increased, and adhesion between the primer coating and a resin, which is highly polar, can be further increased. For this reason, the adhesive strength between the substrate and the resin member of the aluminum-alloy composite material can be further increased.

[0037] For example, a polyol such as ethylene glycol, propylene glycol, glycerin, trimethylolpropane, pentaerythritol, etc.; a polyether polyol such as polyethylene glycol, polypropylene glycol, etc.; a polyester polyol composed of an ester of polycarboxylic acid and a polyol; a polycarbonate polyol made by bonding together, via a carbonate bond, structural units derived from polyols; or the like can be used as the polyol.

[0038] The urethane resin preferably contains a structural unit derived from a polyester polyol. That is, the urethane resin preferably is a polyester-based polyurethane. In this case, adhesion between the primer coating and the substrate can be further increased, and adhesion between the primer coating and a resin, which is highly polar, can be further increased. For this reason, the adhesive strength between the substrate and the resin member of the aluminum-alloy composite material can be further increased.

[0039] The primer coating has an infrared-absorption spectrum in which the value of the optical absorption A.sub.C═O at the peak top of the maximum peak among the peaks present in the wavenumber range of 1,180-1,330 cm.sup.−1 is 0.8-1.5 times that of the optical absorption A.sub.urethane at the peak top of the maximum peak among the peaks present in the wavenumber range of 1,670-1,770 cm.sup.−1. In the infrared-absorption spectrum of the primer coating that contains urethane resin, a peak originating from C═O stretching vibration of the urethane bond appears within the wavenumber range of 1,670-1,770 cm.sup.−1. In addition, a peak originating from C═O stretching vibration of a carbonyl group appears within the wavenumber range of 1,180-1,330 cm.sup.−1. Accordingly, it is presumed that the ratio A.sub.C═O/A.sub.urethane, which is the ratio of the value of the optical absorption A.sub.C═O to the value of the optical absorption A.sub.urethane described above, indicates the amount of carbonyl groups in the urethane resin.

[0040] Primer coatings, in which the value of the optical absorption A.sub.C═O is in the specific range, excel in both adhesion with the aluminum material that constitutes the substrate and adhesion with a resin, which is highly polar. For example, it is conceivable that the following reason is why the primer coating is highly adhesive. The carbonyl group (—C(═O)—) is polarized such that positive charge is shifted toward the carbon atom and negative charge is shifted toward the oxygen atom. Consequently, owing to electrostatic forces, hydrogen bonds, and the like, it is conceivable that carbonyl groups can improve adhesion with the resin member, which is highly polar. For this reason, by forming such a primer coating on the substrate, a precoated aluminum material that excels in adhesion with the resin member can be obtained.

[0041] From the viewpoint of further improving both adhesion between the primer coating and the substrate and adhesion between the primer coating and the resin member, the value of the optical absorption A.sub.C═O is preferably 1.0-1.5 times and is more preferably 1.1-1.3 times that of the optical absorption A.sub.urethane.

[0042] In the infrared-absorption spectrum of the primer coating, the value of the optical absorption A.sub.COC at the peak top of the maximum peak among the peaks present in the wavenumber range of 990-1,150 cm.sup.−1 is preferably 0.7-1.3 times that of the optical absorption A.sub.urethane described above. In this case, adhesion between the precoated aluminum material and the resin member can be further improved.

[0043] For example, it is conceivable that the following reason is why the primer coating is highly adhesive. In the infrared-absorption spectrum of a primer coating that contains urethane resin, a peak originating from C—O—C stretching vibration of the ether bond appears within the wavenumber range of 990-1,150 cm.sup.−1. Accordingly, it is presumed that the ratio A.sub.COC/A.sub.urethane, which is the ratio of the value of the optical absorption A.sub.COC to the value of the optical absorption A.sub.urethane described above, indicates the amount of ether bonds in the urethane resin.

[0044] The same as with the carbonyl group, the ether bond (—C—O—C—) is polarized such that positive charge is shifted toward the carbon atoms and negative charge is shifted toward the oxygen atom. Consequently, owing to electrostatic forces, hydrogen bonds, and the like, it is conceivable that ether bonds can improve adhesion with the resin member, which is highly polar. For this reason, by forming such a primer coating on the substrate, adhesion between the precoated aluminum material and the resin member can be further improved.

[0045] From the viewpoint of further improving both adhesion between the primer coating and the substrate and adhesion between the primer coating and the resin member, the value of the optical absorption A.sub.COC is more preferably 0.9-1.0 times that of the optical absorption A.sub.urethane.

[0046] In the infrared-absorption spectrum of the primer coating, the value of the optical absorption A.sub.aromatic at the peak top of the maximum peak among the peaks present in the wavenumber range of 660-760 cm.sup.−1 is preferably 1.0-1.7 times and more preferably 1.2-1.5 times that of the optical absorption A.sub.urethane described above. In this case, adhesion between the precoated aluminum material and the resin member can be further improved.

[0047] The primer coating may contain urethane resin and a resin other than urethane resin. For example, acrylic resin, melamine resin, or the like can be used as the resin(s) other than urethane resin.

[0048] A resin obtained by polymerizing a monomer having a (meth)acryloyl group, such as methyl acrylate and methyl methacrylate, can be used as the acrylic resin. The acrylic resin preferably contains a structural unit that is derived from methyl methacrylate. In this case, adhesion between the primer coating and the substrate can be further increased, and adhesion between the primer coating and a resin, which is highly polar, can be further increased. For this reason, the adhesive strength between the substrate and the resin member of the aluminum-alloy composite material can be further increased.

[0049] The content of the acrylic resin in the primer coating is preferably set to 3-50 parts by mass to 100 parts by mass of the urethane resin. In this case, adhesion between the primer coating and the substrate can be further increased, and adhesion between the primer coating and a resin, which is highly polar, can be further increased. For this reason, the adhesive strength between the substrate and the resin member of the aluminum-alloy composite material can be further increased.

[0050] For example, methylated-melamine resin; etherified-melamine resin, in which some or all of the methylol groups in the methylated-melamine resin have been etherified by reacting with alcohol; or the like can be used as the melamine resin. A mixed etherified-melamine resin, in which some or all of the methylol groups in the methylated-melamine resin have been etherified by reacting with two or more types of alcohol, is preferably used as the melamine resin. In this case, adhesion between the primer coating and the substrate can be further increased, and adhesion between the primer coating and a resin, which is highly polar, can be further increased. For this reason, the adhesive strength between the substrate and the resin member of the aluminum-alloy composite material can be further increased.

[0051] The content of the melamine resin in the primer coating is preferably set to 0.3-13 parts by mass to 100 parts by mass of the urethane resin. In this case, adhesion between the primer coating and the substrate can be further increased, and adhesion between the primer coating and a resin, which is highly polar, can be further increased. For this reason, the adhesive strength between the substrate and the resin member of the aluminum-alloy composite material can be further increased.

[0052] The precoated aluminum material can be prepared by, for example, the method below. First, the substrate for forming the primer coating is prepared. For example, a rolled sheet, an extruded material, a forged material, or the like can be used as the substrate. In a situation in which a rolled sheet is used as the substrate, it is also possible to form a desired shape by performing pressing or the like on the rolled sheet in advance.

[0053] Next, the surface of the substrate is cleaned to eliminate machining oil, foreign matter, and the like that has adhered to the surface. In a situation in which an undercoating is provided on the surface of the substrate, a surface treatment in accordance with the type of undercoating should be performed after the cleaning of the substrate.

[0054] Subsequently, a primer is applied over a desired region of the substrate surface. For example, an aqueous-urethane emulsion, in which micelles of the urethane resin are dispersed in water, can be used as the primer. In a situation in which it is attempted to form, as the primer coating, a coating that contains urethane resin and another resin, such as acrylic resin and melamine resin, a liquid mixture, in which an emulsion containing the urethane resin and an emulsion containing the other resin are mixed, should be used as the primer. At this time, the mixing ratio between the urethane resin and the resin other than urethane resin in the primer coating can be controlled by adjusting the ratio of solid content in the liquid mixture.

[0055] After the primer has been applied to the substrate surface, the primer coating can be formed on the surface of the substrate by drying of the primer. When the primer is being dried, the primer may be heated as needed. The drying temperature and the drying time of the primer can be set as appropriate in accordance with the type of primer. For example, the drying temperature of the primer can be set as appropriate within the range of 150-300° C.

[0056] The drying temperature and the drying time of the primer are preferably set to a temperature and a time at which the mechanical characteristics of the substrate are not impaired. That is, in a situation in which, for example, an aluminum material that has undergone work hardening, a heat solution treatment, or thermal refining by quenching or the like in the manufacturing process is to be used as the substrate, there are situations in which the aluminum alloy will soften due to the heating during drying.

[0057] For example, in the case of A1100-H18, when heating is performed for 15 min at 260° C., the proof stress, which was approximately 150 MPa prior to heating, decreases to approximately 100 MPa. In addition, in the case of A5052-H18 alloy, when heating is performed for 10 min at 290° C., the proof stress, which was 300 MPa prior to heating, decreases to approximately 250 MPa. Such softening can be avoided by a method in which the temperature during drying is further lowered, the drying time is further shortened, or both the temperature is lowered and the time is shortened.

[0058] Precoated aluminum materials can be obtained as described above.

[0059] By bonding a resin member, which contains polybutylene terephthalate (PBT), polyamide (PA), polyphenylene sulfide (PPS), or an acrylonitrile-butadiene-styrene copolymer (ABS), to the primer coating of the precoated aluminum material, an aluminum composite material, in which the substrate and the resin member are bonded via the primer coating, can be obtained. The primer coating of the precoated aluminum material excels in adhesion with the resin described above. For this reason, according to the above-mentioned aluminum composite material, peeling of the resin member off of the substrate can be curtailed.

[0060] The method of bonding the substrate and the resin member is not particularly limited. For example, methods such as a hot-pressing method in which the resin member and the substrate that have been formed into a desired shape in advance are compression bonded together while being heated, an insert-molding method in which the resin member is insert molded onto the substrate, or the like can be used as the method of bonding the substrate and the resin member together.

Working Examples

[0061] Working examples of the precoated aluminum material will now be explained, with reference to FIG. 1 to FIG. 4. It is noted that specific aspects of the precoated aluminum material according to the present invention are not limited to the aspects of the working examples and can be modified as appropriate within a range that does not deviate from the gist of the present invention.

[0062] In the present example, sheet materials composed of JIS A5052-H34 and each having a thickness of 1.5 mm were used as the substrates. In addition, primers, in which a urethane-resin emulsion, an acrylic-resin emulsion, a melamine-resin emulsion, a polyolefin emulsion, and a polyamide emulsion were mixed together such that their solid-content ratios became the proportions listed in Table 1, were prepared as the primers.

[0063] The urethane resin of the present example contained a structural unit derived from a polyester polyol and a structural unit derived from an aromatic polyisocyanate. The acrylic resin of the present example contained a structural unit derived from methyl methacrylate. The melamine resin of the present example was a mixed etherified-melamine resin.

[0064] After the primers listed in Table 1 were applied to the substrates, the substrates were heated at a temperature of approximately 200° C. for 1 min, and thereby the primers were dried. Based on the above, as shown in FIG. 1, precoated aluminum materials 1 (Test Materials A1-A8), each comprising a substrate 2 and a primer coating 3 layered on the substrate 2 and having the compositions listed in Table 1, could be obtained.

[0065] Infrared-absorption spectrums of the primer coatings 3 were obtained for Test Materials A1-A5, from among the Test Materials A1-A8, in which the primer coating contained urethane resin. FIG. 2 and FIG. 3 show, as examples of the infrared-absorption spectrums, the infrared-absorption spectrums of the primer coatings 3 in Test Material A1 and Test Material A2. The ordinate in FIG. 2 and FIG. 3 represents the optical absorption, and the abscissa represents the wavenumber (cm.sup.−1). It was possible to measure the primer coatings 3 using, for example, a total-reflection measuring method in which the number of scans was 15.

[0066] The value of the optical absorption A.sub.urethane at the peak top of the maximum peak among the peaks present in the wavenumber range of 1,670-1,770 cm.sup.−1, the value of the optical absorption A.sub.C═O at the peak top of the maximum peak among the peaks present in the wavenumber range of 1,180-1,330 cm.sup.−1, the value of the optical absorption A.sub.COC at the peak top of the maximum peak among the peaks present in the wavenumber range of 990-1,150 cm.sup.1, and the value of the optical absorption A.sub.aromatic at the peak top of the maximum peak among the peaks present in the wavenumber range of 660-760 cm.sup.−1 were each calculated from the infrared-absorption spectrums obtained. Table 1 lists the values of the ratio A.sub.C═O/A.sub.urethane of A.sub.C═O to A.sub.urethane calculated based on the infrared-absorption spectrums of Test Materials A1-A5, the values of the ratio A.sub.COC/A.sub.urethane of A.sub.COC to A.sub.urethane, and the values of the ratio A.sub.aromatic/A.sub.urethane of A.sub.aromatic to A.sub.urethane. It is noted that the symbol “-” in Test Materials A6-A8 indicates that an infrared-absorption spectrum was not obtained.

[0067] It was possible to evaluate the adhesion between the precoated aluminum materials and the resin members using a method compliant with ISO 19095. The method of evaluating the adhesion between the precoated aluminum material and the resin members was, specifically, as follows.

[0068] First, a small piece 10, which exhibited an oblong shape having a length of 45 mm and a width of 17 mm, was cut from the precoated aluminum material 1. Next, as shown in FIG. 4, a test piece 100 for evaluating the shear strength of adhesive bonds was prepared by forming a resin sheet 40, which served as a resin member 4 and contained a resin as listed in Table 1, on the primer coating 3 at one end of the small piece 10 in a longitudinal direction using injection molding. The length of the resin sheet 40 was set to 45 mm, the width was set to 10 mm, and the thickness was set to 3 mm. In addition, the length of an overlapping portion 41, at which the small piece 10 of the precoated aluminum material 1 and the resin sheet 40 overlap, was set to 5 mm.

[0069] Using the resulting test piece 100, a tensile-shear test was performed in accordance with the method stipulated in ISO 19095. The fracture strength obtained as a result thereof is listed in Table 1 as the shear strength of adhesive bonds between the precoated aluminum material 1 and the resin member 4 (that is, the resin sheet 40).

TABLE-US-00001 TABLE 1 Test Test Test Test Test Test Test Test Material Material Material Material Material Material Material Material Test Material Symbol A1 A2 A3 A4 A5 A6 A7 A8 Primer Urethane parts by 100 100 100 100 100 — — — coating resin mass Acrylic parts by — 20 20 20 20 100 — — resin mass Melamine parts by — — 1.1 1.1 1.1 — — — resin mass Polyolefin parts by — — — — — — 100 — mass Polyamide parts by — — — — — — — 100 mass Adhered g/m2 6 6 6 6 6 6 6 6 amount Infrared A.sub.C=O/A.sub.urethane times 1.3 1.2 1.1 1.1 1.1 — — — absorption A.sub.COC/A.sub.urethane times 1.0 1.0 0.9 0.9 0.9 — — — spectrum A.sub.aromatic/A.sub.urethane times 1.5 1.4 1.2 1.2 1.2 — — — Resin member — ABS ABS ABS PBT PPS PBT PBT PBT Shear strength of adhesive bonds MPa 5 12 15 5 6 0 0 0

[0070] Test Materials A1-A5 contain urethane resin and, as shown in FIG. 2 and FIG. 3, comprise a primer coating that has an infrared-absorption spectrum in which the value of the ratio A.sub.C═O/A.sub.urethane of the value of the optical absorption A.sub.C═O to the value of the optical absorption A.sub.urethane is within the specific range. Primer coatings 3 of this kind excel in both adhesion with a substrate 2 and adhesion with a resin member 4, which contains a resin such as PBT, PPS, or ABS.

[0071] From a comparison of Test Materials A1-A3, for which adhesion with respect to a resin member that contains ABS was evaluated, it could be understood that Test Material A2, which comprised the primer coating 3 that contained urethane resin and acrylic resin, had a higher shear strength of adhesive bonds than Test Material A1. In addition, it could be understood that Test Material A3, which comprised the primer coating 3 that contained urethane resin, acrylic resin, and melamine resin, had a higher shear strength of adhesive bonds than Test Material A1.

[0072] In contrast, Test Material A6, which comprised a primer coating that was composed only of acrylic resin, Test Material A7, which comprised a primer coating that was composed only of polyolefin, and Test Material A8, which comprised a primer coating that was composed only of polyamide, exhibited virtually no adhesion with respect to resin members that contained PBT.