Reinforced battery package with sealed anode chamber

Abstract

A solid state battery cell has a frame formed by a non-electrically conductive material. The frame has a frame thickness (Tf). A cell core surrounded by and entirely within the frame has a cell-core thickness (Tc). The cell core includes at least one anode, at least one cathode and at least one electrolyte between the at least one anode and the at least one cathode. At least one cell-core swell-accommodating recess is surrounded by and entirely within the frame. The at least one cell-core swell-accommodating recess defines an internal cell volume into which the cell core is expandable and from which the cell core is contractible. The cell-core thickness (Tc) is less than or equal to the frame thickness (Tf) during cell-charge and/or cell-discharge cycling.

Claims

1. A solid state battery cell comprising: a dimensionally stable frame formed from a non-electrically conductive material, the frame having a frame thickness; a cell-core surrounded by and entirely within the frame and having a cell-core thickness, the cell core comprising at least one anode, at least one cathode and at least one electrolyte between the at least one anode and the at least one cathode, wherein the frame is mounted on the at least one cathode; at least one cell-core swell-accommodating recess surrounded by and entirely within the frame, the at least one cell-core swell-accommodating recess defining an internal cell volume into which the cell core is expandable and from which the cell core is contractible, wherein the cell-core thickness is less than or equal to the frame thickness during cell-charge and/or cell-discharge cycling; and a hermetically sealed housing within which the solid state battery cell-core is disposed; wherein the housing is an anode terminal of the solid state battery cell.

2. The solid state battery cell according to claim 1, further comprising: a conductive anode-current collector extending over a portion of the non-electrically conductive material forming the frame, the conductive anode-current collector in electrical contact with the at least one anode; and a conductive cathode-current collector extending over and in electrical contact with a portion of the at least one cathode, the conductive cathode-current collector exposed and accessible at a surface of the non-electrically conductive material forming the frame.

3. The solid state battery cell according to claim 2, further comprising: a tab extending outwardly directly from an exposed surface of the non-electrically conductive material forming the frame, the tab formed by the non-electrically conductive material of the frame; and an accessible cathode-current-collector terminal contact in the tab, the cathode-current-collector terminal contact in electrical communication with the cathode-current collector.

4. The solid state battery cell according to claim 2, wherein: the cell core is a symmetric bipolar pair of cells; the conductive cathode-current collector is a shared cathode-current collector; the at least one cathode is an active cathode material on opposite sides of the shared cathode-current collector; the at least one electrolyte is a layer of electrolyte on the active cathode material on opposite sides of the shared cathode-current collector; the at least one anode is a layer of lithium based anode material on each layer of the electrolyte material on opposite sides of the shared cathode-current collector; and the at least one cell-core swell-accommodating recess comprises a first internal cell volume and a second internal cell volume on opposite sides of the shared cathode-current collector, one cell of the bipolar pair of cells expandable into and contractible from the first internal cell volume and the other cell of the bipolar pair of cells expandable into and contractible from the second internal cell volume.

5. The solid state battery cell according to claim 4, further comprising: a tab extending outwardly directly from an exposed surface of the non-electrically conductive material forming the frame, the tab formed by the non-electrically conductive material of the frame; and an accessible cathode-current-collector terminal contact in the tab, the cathode-current-collector terminal contact in electrical communication with the cathode-current collector.

6. The solid state battery cell according to claim 4, further comprising a compliant polymer coating the conductive anode-current collector.

7. The solid state battery cell according to claim 4, further comprising a barrier to ion conduction and lithium plating applied between the at least one cathode and the frame.

8. The solid state battery cell according to claim 1, wherein the cell-core has a planar configuration and is positioned within the dimensionally stable frame which extends around its perimeter.

9. The solid state battery cell according to claim 1, wherein the dimensionally stable frame defines an area of the cell that is not active, is protected from electrochemical processes which occur in the cell-core during cycling, and wherein the area of the cell defined by the frame remains chemically and mechanically stable.

10. A multi-cell solid state battery comprising: a plurality of solid state battery cells according to claim 2 arranged in a stack and connected in series such that the conductive cathode-current collector and the conductive anode-current collector of adjacent cells are in contact with each other.

11. A multi-cell solid state battery comprising: a plurality of solid state battery cells according to claim 4 arranged in a stack such that the conductive cathode-current collectors accessible at a surface of the non-electrically conductive material forming the frame of each cell of the plurality of solid state battery cells are aligned and the conductive anode-current collector of adjacent cells of solid state battery cells are in electrical contact.

12. The multi-cell solid state battery according to claim 11 further comprising: an electrically conductive anode terminal strip attached to the conductive anode-current collector of each cell of the plurality of solid state battery cells; and an electrically conductive cathode-current-collector terminal strip attached to the conductive cathode-current collector of each cell of the plurality of solid state battery cells.

13. The multi-cell solid state battery according to claim 12 further comprising: a hermetically sealed housing within which the stack of the plurality of solid state battery cells is disposed; a bottom most anode-current collector in electrical contact with the housing such that the housing is an anode terminal of the multi-cell solid state battery; and a cathode terminal lead attached to the cathode-current-collector terminal strip, the cathode terminal lead extending beyond the housing such that the cathode terminal lead is a cathode terminal of the multi-cell solid state battery.

14. The multi-cell solid state battery according to claim 13 further comprising: a spring load distribution plate on a top of the stack; a spring between the housing and the top of the stack biasing the stack away from the top of the housing.

15. A method for fabricating the solid state battery cell of claim 2 comprising the steps of: fabricating a cathode sheet having a current collector substrate by applying an active cathode material to one side of the current collector substrate; applying a non-conducting material on the entire exposed surface of the active cathode material; creating an active area for the battery cell by removing an area of the non-conducting material to expose the active cathode material and to form a frame of the non-conducting material circumscribing the active area, the frame having a thickness such that as the battery cell is cycled an overall thickness of the battery cell does not exceed the thickness of the frame; applying an electrolyte on the active cathode material; applying an anode material on the electrolyte in the active area; and applying an anode collecting material on the anode and on the frame.

16. A method for fabricating the solid state battery cell of claim 4 comprising the steps of: fabricating a cathode sheet having a current collector substrate by applying an active cathode material to at least one side of the current collector substrate; cutting in the cathode sheet a pattern yielding an array of individual cells held in place by tabs, a cathode-current terminal contact in each tab; applying a non-conducting material on the entire exposed surface of each of the individual cells of the array; creating an active area in each individual cell by removing a corresponding area of the non-conducting material to expose the active cathode material of each cell and to form a frame of the non-conducting material circumscribing each active area, the frame having a thickness such that as each cell is cycled an overall thickness of the cell does not exceed the thickness of the frame; applying an electrolyte on the active cathode material in the active area of each cell; applying an anode material on the electrolyte in the active area of each cell; applying an anode collecting material on the anode and on the frame; and removing each individual cell from the array by cutting each tab from each cell, exposing the conductive cathode-current collector.

17. The method for fabricating the solid state battery cell according to claim 16, further comprising applying a barrier to the cathode sheet blocking ion conduction and electronic conduction.

18. The method for fabricating the solid state battery cell according to claim 16, further comprising applying a pliable polymer coating to the array of individual cells.

19. The method for fabricating the solid state battery cell according to claim 16 further comprising: stacking the individual cells in a stack such that the conductive cathode-current collectors are aligned; applying a cathode-coating conducting material interconnecting the conductive cathode-current collectors; and applying an anode-coating conducting-material interconnecting the conductive anode-collecting material of each cell.

20. The method for fabricating the solid state battery cell according to claim 19, further comprising: hermetically sealing the stack of in a housing such that the housing is an anode terminal of the battery by being in electrical contact with the anode-coating conducting-material and a cathode lead terminal which is insulated from and extends beyond the housing is a cathode terminal of the battery by being in electrical contact with the cathode-coating conducting material.

21. A solid state battery cell comprising: a dimensionally stable frame formed from a non-electrically conductive material, the frame having a frame thickness; a cell-core surrounded by and entirely within the frame and having a cell-core thickness, the cell core comprising at least one anode, at least one cathode and at least one electrolyte between the at least one anode and the at least one cathode, wherein the frame is mounted on the at least one cathode; at least one cell-core swell-accommodating recess surrounded by and entirely within the frame, the at least one cell-core swell-accommodating recess defining an internal cell volume into which the cell core is expandable and from which the cell core is contractible, wherein the cell-core thickness is less than or equal to the frame thickness during cell-charge and/or cell-discharge cycling; a conductive anode-current collector extending over a portion of the non-electrically conductive material forming the frame, the conductive anode-current collector in electrical contact with the at least one anode; a conductive cathode-current collector extending over and in electrical contact with a portion of the at least one cathode, the conductive cathode-current collector exposed and accessible at a surface of the non-electrically conductive material forming the frame; an electrically conductive anode terminal strip attached to the conductive anode-current collector; an electrically conductive cathode-current-collector terminal strip attached to the conductive cathode-current collector; a hermetically sealed housing within which the solid state battery cell-core is disposed; wherein the anode-current collector in electrical contact with the housing such that the housing is an anode terminal of the solid state battery cell; and a cathode terminal lead attached to the cathode-current-collector terminal strip, the cathode terminal lead extending beyond the housing such that the cathode terminal lead is a cathode terminal of the solid state battery cell.

Description

BRIEF DESCRIPTION OF THE SEVERAL VIEWS OF THE DRAWINGS

(1) The foregoing summary, as well as the following detailed description of preferred embodiments of the invention, will be better understood when read in conjunction with the appended drawings. For the purpose of illustrating the invention, the drawings show embodiments which are presently preferred. It should be understood, however, that the invention is not limited to the precise arrangements and instrumentalities shown.

(2) In the drawings:

(3) FIG. 1 is a top perspective view of an embodiment of a battery cell having packaging frame defining an inactive perimeter region and a maximum cell thickness in accordance with the teachings of the present invention;

(4) FIG. 2 is a sectional view of the cell of FIG. 1 taken along cross section plane A-A of FIG. 1;

(5) FIG. 3 is a sectional view of the cell of FIG. 1 but in a charged state where the volume of the lithium based anode has increased;

(6) FIG. 4 is a top perspective view of an embodiment of a battery cell stack wherein the frames of the cells in the stack determine the overall stack height in accordance with the teachings of the present invention;

(7) FIG. 5 is a sectional view of the cell stack of FIG. 4 taken along cross section plane B-B of FIG. 4 showing the packaging frames of the cells defining an inactive perimeter region separately from an active center region whereby expansion volume is available within the stack to accommodate changes in volume of the anodes of the cells with charge/discharge cycling without changing the overall stack height in accordance with the teachings of the present invention;

(8) FIG. 6 is a top perspective view of the cell stack of FIG. 4 having the cathodes of the individual cell interconnected to each other by a conductive strip and the anodes interconnected to each other by a conductive strip;

(9) FIGS. 7A, 7B, 7C, 7D, and 7E shows placement of the battery of FIG. 5 into a casing with connection to a common cathode terminal having a glass feed through of the casing and connection of the anodes to the casing with the casing functioning as the anode terminal in accordance with the teachings of the present invention;

(10) FIG. 8 is a top level functional flow diagram for a preferred embodiment of a method for manufacturing a solid state batter cell in accordance with the teachings of the present invention;

(11) FIG. 9 a top perspective view of a cathode structure consisting of an electronically conductive substrate having active cathode material bonded to both sides;

(12) FIG. 10 is a top perspective view of the cathode structure of FIG. 9 having an array of cathode masks applied to its surfaces to define active areas for an array of cells;

(13) FIG. 11 is a top perspective view of the cathode structure of FIG. 10 having a coating of insulation material applied to both sides and covering the array of cathode masks.

(14) FIG. 12 is a top perspective view of the cathode structure of FIG. 11 having been cut into an array of individual cells;

(15) FIG. 13 is a top perspective view of the cathode structure of FIG. 12 with the entire structure having been coated with insulation material;

(16) FIG. 14 is a top perspective exploded view an individual cell of FIG. 13 with its mask removed to expose the active surface area of the cathode;

(17) FIG. 15 is a top perspective view of the array of cells of FIG. 13 with the cathode masks removed to expose the surface of the individual cell cathodes;

(18) FIG. 16 is a top perspective view of the cell array of FIG. 14 with an electrolyte mask in place in preparation for an electrolyte coating;

(19) FIG. 17 is a top perspective view of the cell array of FIG. 16 wherein an electrolyte coating has been applied over the exposed active area of the individual cathodes;

(20) FIG. 18 is a top perspective view of the cell array of FIG. 16 with the electrolyte mask removed showing a coating of electrolyte on the active surface areas of the cells;

(21) FIG. 19 is a top perspective view of the cell array of FIG. 18 with a mask in place in preparation for a coating of active anode material onto the electrolyte in the active area of the cells;

(22) FIG. 20 is a top perspective view of the cell array of FIG. 19 with a coating of active anode material having been applied onto the active surface areas of the cells;

(23) FIG. 21 is a top perspective view of the cell array of FIG. 20 with the mask removed to provide a view of the coating of optional anode material in the active areas of the cells;

(24) FIG. 22 is a top perspective view of the cell array of FIG. 20 having a current collector mask in place in preparation for a coating of electrically conductive material that will extend over the edges of the cells to connect the anodes on both sides of a given cell to each other;

(25) FIG. 23 is a top perspective view showing the cell array of FIG. 22 wherein a coating of electrically conductive material has been applied covering the exposed surfaces of the cell array structure as defined by the current collector mask;

(26) FIG. 24 is a top perspective view of the cell array of FIG. 23 showing the current collector mask removed to provide a view of the surface areas covered by the current collector material;

(27) FIG. 25 is a top perspective view of the cell array of FIG. 24 having a mask in place in preparation for applying a coating of an pliable material such as a polymer coating onto the active areas of the cells;

(28) FIG. 26 is a top perspective view of the cell array of FIG. 25 having a coating of an pliable material coating on the active areas of the cells;

(29) FIG. 27 is a top perspective view of the cell array of FIG. 26 showing the pliable material mask removed to provide a view of the surface areas covered by the pliable material coating;

(30) FIG. 28 is a top level functional flow diagram for a preferred embodiment of a method for manufacturing a multi-cell solid state batter in accordance with the teachings of the present invention;

(31) FIG. 29 is a bottom perspective view of an embodiment of a battery cell having an alternate packaging frame defining an inactive perimeter region and a maximum cell thickness in accordance with the teachings of the present invention;

(32) FIG. 30 is a sectional view of the cell of FIG. 29 taken along cross section plane B-B of FIG. 29;

(33) FIG. 31 is a sectional view of a pair of cells representative of FIG. 29 taken along cross section plane B-B of FIG. 29 wherein the cells are configured having a common anode accommodating region; and

(34) FIG. 32 is a sectional view of a pair of cells representative of FIG. 29 taken along cross section plane B-B of FIG. 29 wherein the cells are configured stacked electrically connected in series with anode and cathode of adjacent cells in contact with each other.

DETAILED DESCRIPTION OF THE INVENTION

(35) Embodiments of the present invention are described herein. The disclosed embodiments are merely exemplary of the invention that may be embodied in various and alternative forms, and combinations thereof. As used herein, the word “exemplary” is used expansively to refer to embodiments that serve as illustrations, specimens, models, or patterns. The figures are not necessarily to scale and some features may be exaggerated or minimized to show details of particular components. In other instances, well-known components, systems, materials, or methods have not been described in detail in order to avoid obscuring the present invention. Therefore, at least some specific structural and functional details disclosed herein are not to be interpreted as limiting, but merely as a basis for the claims and as a representative basis for teaching one skilled in the art to variously employ the present invention.

(36) As an overview, the invention teaches an approach for a dimensionally stable battery package that accommodates the use of anodes that undergo significant volume changes as lithium is cycled in and out of the anode with charge/discharge cycling. Each cell is initially formed as a cathode comprised of active cathode material coated onto a current collector. The cathode is provided with a dimensionally stable picture frame like structure around its perimeter. The frame structure is comprised of electrical insulative material or at least has a non-conductive surface. It is mounted to the cell around the cell's perimeter which is intended to be inactive i.e. no lithium cycling. The insulation frame may be multilayered. The frame creates a recessed well in the region enclosed by its circumference. Electrolyte separator and anode coatings are located within the area enclosed by the frame and thus define the active area of the cell. The thickness of the frame determines the overall cell thickness. The recess well area surrounded by the frame provides a volume within which a lithium based or other anode can expand and contract with cycling of the cell without affecting the overall cell thickness established by the frame.

(37) The cell is fitted with a current collector coating which covers the active area of the cell and extends over the frame of insulation material such that when multiple cells are placed in a stack, electrical access to the current collectors is provided at the edge of the cells. The configuration is such that access is provided to the cathode at a cell edge or section of an edge not covered by anode current collector. The insulation frame is penetrated along an edge or location not covered by anode current collector to provide access to the cathode current collector. Electrical connections can be made at the edges of stacked cells to electrically connect cathode current collectors and anode current collectors to each other in series or in parallel.

(38) Optionally, the cells may be formed with in a bipolar cell configuration wherein the cathode current collector has a cell symmetrically mounted on both sides. Further, the cells may be formed via a series of die cuts, stampings and pressings, by a series of physical deposition coatings or a combination thereof. The present disclosure describes a combination wherein cathodes are first hot pressed onto current collectors and where the remaining components are applied by physical deposition to achieve a preferred cell structure.

(39) Although the term “battery” technically may more properly define a combination of two or more cells, it has come to be used popularly to refer to a single cell. Thus the term battery by itself is sometimes for convenience of explanation used herein to refer to what is actually a single cell. The teachings herein are directed to battery packages formed from cells wherein anode material is isolated in the battery package for a cell.

(40) Reference will now be made in detail to embodiments of the invention, examples of which are illustrated in the accompanying drawings. The terminology used in the description of the invention herein is for the purpose of describing particular embodiments only and is not intended to be limiting of the invention.

(41) As used in the description of the invention and the appended claims, the singular forms “a”, “an” and “the” are intended to include the plural forms as well, unless the context clearly indicates otherwise. The words “and/or” as used herein refers to and encompasses any and all possible combinations of one or more of the associated listed items. The words “comprises” and/or “comprising,” when used in this specification, specify the presence of stated features, integers, steps, operations, elements, and/or components, but do not preclude the presence or addition of one or more other features, integers, steps, operations, elements, components, and/or groups thereof.

(42) The words “right,” “left,” “lower” and “upper” designate directions in the drawings to which reference is made. The words “inwardly” and “outwardly” refer to directions toward and away from, respectively, the geometric center of the needle safety shield, and designated parts thereof. The terminology includes the words noted above, derivatives thereof and words of similar import.

(43) Although the words first, second, etc., are used herein to describe various elements, these elements should not be limited by these words. These words are only used to distinguish one element from another. For example, a first cell could be termed a second cell, and, similarly, a second cell could be termed a cell tube, without departing from the scope of the present invention.

(44) The following description is directed towards various embodiments of a reinforced battery package with sealed anode chamber in accordance with the present invention.

(45) Referring to the drawings in detail, where like numerals indicate like elements throughout, there is shown in FIGS. 1-3 a first preferred embodiment of the solid state battery cell, generally designated 10, and hereinafter referred to as the “battery cell” 10 in accordance with the present invention.

(46) The battery cell 10 has a frame 12 formed from a non-electrically conductive material which may be a polymer material or an inorganic material such as a metal oxide. The frame 12 has a frame thickness, Tf, which creates a recessed well 14 circumscribed by the frame 12. The recessed well 14 is an active region of the battery cell 10 within which a cell core 16 is disposed. The cell core 16 has a cell-core thickness, Tc and comprises at least one anode 18, at least one cathode 20 and at least one electrolyte 22 between the at least one anode 18 and the at least one cathode 20. Although the frame 12 is preferably mounted on the at least one cathode 20, in some embodiments the frame 12 may be mounted on the at least one anode 18.

(47) The cell core 16 may have a single anode and a single cathode. Alternatively, the cell core 16 may have a bipolar configuration wherein a common cathode structure is used in combination with two separate anodes, one on each side. A common anode structure could also be used. A bipolar cell based on a common cathode structure is disclosed below for instructive purposes wherein active cathode material is mounted on both sides of a common cathode current collector.

(48) In addition to the cell core 16, the recessed well 14 has at least one cell-core swell accommodating region 24 surrounded by and entirely within the frame 12. The at least one cell-core swell-accommodating recess 24 defines an internal volume into which the cell core 16 is expandable and from which the cell core 16 is contractible. Preferably, the internal volume of the accommodating region 24 is sized to accommodate an increase in the thickness of the at least one anode 18 when the battery cell 10 is in a charged state without changing the overall thickness of the battery cell 10. Accordingly, in preferred embodiments of the battery cell 10, the cell-core thickness (Tc) is less than or equal to the frame thickness (Tf) during cell-charge and/or cell-discharge cycling.

(49) The minimum depth of region 24 is determined by the resulting thickness of the lithium anode when the cell is fully charged. This depth is determined by the amount of lithium active material incorporated in the cathode. An example active material may be a form of Lithium Nickel Cobalt Manganese dioxide (NCM) which has a volumetric cycle-able lithium capacity of 100 μAh/cm.sup.2.μm. Assume a composite cathode structure that includes a binder material, an electron conductive material, a lithium ion conductive material and the NCM active material wherein the NCM active material represents 40% of the overall cathode volume. If the cathode thickness is 50 μm, then the equivalent active material thickness will be 20 um, (0.4*50 μm), and the net capacity will be 2 mAh/cm.sup.2, (100 μAh/cm.sup.2.μm*20 μm). Given the capacity of dense lithium metal of 200 μAh/cm.sup.2.μm, the depth required for region 24 would be 10 μm, (2mAh/cm.sup.2/200 μAh/cm.sup.2.μm).

(50) A conductive anode-current collector 26 extends over a portion of the non-electrically conductive material forming the frame 12 and also extends partially into the recessed well 14. A portion of the surface of the frame 12, preferably the front side, remains exposed. The conductive anode-current collector 26 is in electrical contact with the at least one anode 18.

(51) A tab 30, formed from the non-electrically conductive material of the frame 12, extends outwardly directly from the exposed surface of the non-electrically conductive material forming the frame 12.

(52) A conductive cathode-current collector 28 extends over and is in electrical contact with a portion of the at least one cathode 18. An accessible cathode-current-collector terminal contact 30, in electrical communication with the cathode-current collector 28 is in the tab 30.

(53) In some embodiments of the battery cell 10, the cell core 14 is a symmetric bipolar pair of cells 34, the conductive cathode-current collector 28 is a shared cathode-current collector, and the at least one cathode 20 is an active cathode material mounted on opposite sides of the shared cathode-current collector, the at least one electrolyte 22 is a solid electrolyte film deposited on the active cathode material and the at least one anode 18 is a lithium based anode film deposited on the solid electrolyte film.

(54) When the cell core 16 has a symmetric bipolar configuration, in a preferred embodiment, the at least one cell-core swell-accommodating region 22 comprises a first internal cell volume 36 and a second internal cell volume 38 on opposite sides of the shared cathode-current collector. One cell of the bipolar pair of cells is expandable into and contractible from the first internal cell volume 36 and the other cell of the bipolar pair of cells is expandable into and contractible from the second internal cell volume 38.

(55) In the symmetric bipolar configuration, the cell core 16 preferably has a conductive anode-current collector deposited on the lithium based anode film and over a portion of the non-electrically conductive material forming the frame 12. A tab 30, formed by the non-electrically conductive material of the frame 12, extends outwardly from an exposed surface of the non-electrically conductive material forming the frame 12. An accessible cathode-current-collector terminal contact 32, in electrical communication with the cathode-current collector 26, is in the tab 30.

(56) In some embodiments, the solid state battery cell preferably, but not necessarily, has a compliant polymer 40 coating the anode-current collector 26. Some embodiments may also have a barrier 42 to ion conduction and lithium plating applied between the at least one cathode 20 and the frame 12.

(57) Referring to FIGS. 4-7, there is shown a first preferred embodiment of a multi-cell solid state battery, generally designated 70, and hereafter referred to as the “multi-cell battery” 70 in accordance with the present invention.

(58) The multi-cell battery 70 has a plurality of solid state battery cells 10 with one or more of the elements described above. Accordingly, like reference numbers for like elements are used throughout. The solid state battery cells 10 are arranged in a stack 44 such that the tab 30 of each cell 10 of the plurality of solid state battery cells is aligned and the conductive anode-current collector 26 of adjacent cells 10 of the plurality of solid state battery cells are in electrical contact. An electrically conductive anode terminal strip 46 is attached to the anode-current collector 25 of each cell 10 of the plurality of solid state battery cells and an electrically conductive cathode-current-collector terminal strip 48 is attached to the cathode-current-collector terminal contact 32 of each cell 10 of the plurality of solid state battery cells.

(59) The stack 44 of the plurality of solid state battery cells is disposed in a housing 50 having a hermetically sealed lid 52. A spring load distribution plate 54 is on a top of the stack 44. A spring 56 between the housing 50 and the top of the stack 44 biases the stack 44 away from the top of the housing 50, such that the bottom most anode-current collector 58 is in electrical contact with the housing 50. A cathode terminal lead 60 is bonded to the cathode-current-collector terminal strip 48 by an electrically conductive binder 62. The binder 62 may be a conductive epoxy material or equivalent or it may be a metal applied by tack welding, molten spray, evaporation or other method. The cathode terminal lead 60 couples the cell cathodes 20 to a housing feed-through terminal 60 which forms a hermetic seal with the housing 50 using glass feed through 66. The lid 52 is sealed to the housing 50 by welding along a seam 68 such that the cell stack 44 is hermetically sealed within, thus protecting the cells 10 from the external environment. The housing 50 of the multi-cell battery 70 serves as an anode terminal 72 of the multi-cell battery 70 and the cathode terminal lead 60 serves as a cathode terminal 74 of the multi-cell battery 70.

(60) Referring to FIGS. 8-27, the following disclosure is directed to the preferred embodiment of a method for manufacturing the solid state batter cell 10 disclosed above, generally designated 200 and hereafter referred to as the method 200 in accordance with the present invention and to the preferred fabrication materials. FIG. 8 is a top level functional flow diagram of the method 200. Although the following disclosure is directed to cell ore 16 having a single anode and a single cathode, the method 200 is equally applicable for the manufacture of a bipolar cell if the method 200 is applied to both sides of a common cathode current collector.

(61) The first step 210 of the method 200 is fabricating a cathode sheet 76 having a current collector substrate 78 by applying an active cathode material 80 to at least one side of the current collector substrate 78.

(62) FIG. 9 shows a sheet of cathode material. It consists of conductive metal current collector substrate 78 which is coated of both sides with active cathode material 80 Current collector 78 is optional depending on the thickness of the cathode material and its structural integrity and electronic conductivity. If used it is preferably aluminum. Cathode material 80 preferably contains at least one lithium active material such as Lithium Manganese Oxide (LiMnO2), Lithium Cobalt Oxide (LiCoO2, LiCO), Lithium Nickel Manganese Cobalt Oxide (LiNi0.33Co0.33Mn0.33O2, NCM), or other suitable lithium reactive material or a combination of reactive materials. The cathode material 80 may also contain additional materials such as carbon or other electronic conductor to promote electron transport and an ion conductor such as LLZO to promote lithium ion transport. The active cathode material coating 80 may be applied by sputter or other physical deposition technique, by slurry casting and drying, sintering or other suitable process.

(63) The second step 220 of the method 200 is applying an active area mask 82 to the cathode sheet 76 of step 110. FIG. 10 is an illustration of the cathode structure of FIG. 9 having active masks 82 placed in an array on the surface of the active cathode material coating 80 so as to define the locations for the active areas 84 (see, FIG. 14) of individual cells 10 to be formed. For a bipolar cell, masks 82 are placed on both sides of the sheet of cathode material 76 and positioned in pairs that are symmetrically opposite each other.

(64) Referring to FIG. 11, in some embodiments, a barrier insulation coating 86 may be applied on both sides the sheet of cathode material 76 after the masks 82 are in place. The barrier insulation coating 86 is applied as a contiguous coating entirely covering the masks 82 of FIG. 10. The barrier insulation coating 86 is preferably an inorganic material such as aluminum oxide, zirconium oxide or other suitable material that blocks ion conduction as well as electronic conduction.

(65) The third step 230 of the method 200 is cutting in the cathode sheet 76 a pattern yielding an array of individual cells 90 held in place by tabs 88. A cathode-current collector terminal contact 90 is in each tab 88. FIG. 12 shows the cathode structure of FIG. 11 having been cut in the pattern yielding the array of individual cells 90 consistent with the locations of the masks 82 shown in FIG. 10. The illustrated cuts 92 extend all the way through the structure. The required cuts may be created by laser cutting techniques, die cutting/stamping or other suitable approach.

(66) The fourth step 240 of the method 200 is depositing a non-conducting material 94 on the entire exposed surface of each of the individual cells 90 of the array. FIG. 13 shows the non-conductive material coating 94 covering the entire surface of the cathode sheet 76 after the array of individual cells 90 have been cut. The non-conductive material coating 94 covering extends onto the side surface areas within the cuts such that each individual cell 90 is totally covered.

(67) The fifth step 250 of the method 200 is creating an active area 84 in each individual cell 90 by removing a corresponding area of the non-conducting material 94 to expose the active cathode material 80 of each cell 90 and to form a frame 96 of the non-conducting material 94 circumscribing each active area 84. The frame 96 has a thickness Tf, such that, as each cell 90 is cycled, an overall thickness of the cell does not exceed the thickness of the frame.

(68) FIG. 14 shows an individual cell 90 of the array with the masks 82 removed. The barrier insulation coating 86 and non-conductive material coating 94 deposited on the masks 82 are removed with the masks 82, exposing the surface of the active cathode material 80. The cut through tab 88 exposes the cathode current collector 32, 74 and cathode material 80 as an edge access point or location. FIG. 15 shows the array of cells 90 of FIG. 13 after masks 82 (see, FIG. 10) have been removed. Each cell 90 in the array has its edges and sides coated with non-conductive material 94. The surfaces of the active cathode material 80 of the individual cells are exposed.

(69) The sixth step 260 of the method 200 is depositing an electrolyte 22, 98 on the active cathode material 82 in the active area 84 of each cell 90. Prior to depositing the electrolyte 22, 98, an electrolyte mask 100 is placed over the surface of the non-conducting material 94 allowing the active cathode material 80 of the cells 90 to remain exposed as shown in FIG. 16.

(70) FIG. 17 shows the active cathode material 80 having been coated with electrolyte material 22, 98. The electrolyte 98 is a solid material such as Lithium Phosphorous Oxynitride (LiPON) or other suitable ion conductor, preferably a lithium ion conductor. Both sides of the cathode sheet 76 may be masked and coated in this way such that the symmetry is maintained in bipolar cells. FIG. 18 shows the cells 90 of the array with the electrolyte masks 100 removed. The illustration shows electrolyte coatings 22, 98 covering the previously exposed active cathode material 82 of each cell 90 in the array with the non-conductive coating material 94 covering the sides and edges of each cell 90.

(71) The seventh step 270 of the method 200 is depositing an anode material on the electrolyte in the active area of each cell. Prior to depositing the anode material 18, 102, an anode mask 104 is placed over the surface of the non-conducting material 94 allowing the electrolyte material 22, 98 of the cells 90 to remain exposed as shown in FIG. 19.

(72) The anode masks 104 are positioned on opposing sides of the cathode sheet 76. The configuration of the masks is such that the areas of the cathode sheet 76 coated by electrolyte coatings 98 are exposed. FIG. 20 shows the structure of FIG. 19 after a lithium active anode material 102 has been applied onto the electrolyte 98 of the individual cells 90. FIG. 21 shows the cathode sheet 76 after the anode masks 104 have been removed. Consistent with prior steps, both sides of the structure are masked and coated with the anode material.

(73) The eighth step 280 of the method 200 is depositing an anode-current collecting material 26, 106 on the electrolyte 22, 98 and on the frame 96 of non-conducting material 94. Prior to depositing the anode collecting material 26, 106, an anode-current collecting mask 108 is placed over the surface of the non-conducting material 94 allowing the anode material 18, 102 of the cells 90 to remain exposed as shown in FIG. 22. FIG. 23 shows the cathode sheet 76 of FIG. 22 after a coating of the anode current collector material 106 has been applied. The anode current collector material 106 is preferably applied by a physical vapor deposition process such as vacuum evaporation, laser deposition or other suitable approach. The anode current collector material coating covers the entire exposed active anode area as well as the exposed sides of each cell. FIG. 24 shows the configuration of the cells 90 of the array after the anode current collector masks 108 have been removed. The areas along the front edges, near tabs 30, 88, of the cells 90 are not coated with anode current collector material. By extending over the sides of the cells 90, the anode current collector coating connects the opposing anodes of each cell to each other in a bipolar cell.

(74) Referring to FIGS. 25-27, in some embodiments, a pliable polymer coating 110 may be applied on both sides the sheet of cathode material 76. FIG. 25 shows a pair of masks 112 placed over the cells 90 of the array in preparation for the application of a pliable polymer coating 110 which is an optional flexible coating that bonds with the anode current collector 106 to improve the ability of the anode current collector 106 to remain intact with repeated expansion and contraction of the anode with cell cycling. The coating is applied to the active areas 3 of the cells, the region where the anode volume changes occur. FIG. 26 shows the cells 90 of the array of FIG. 25 after pliable coating 110 has been applied. The coating 110 may be parylene or other suitable polymer material.

(75) FIG. 27 shows the final structure of the cells 90 of the array after the masks 112 for the pliable coating have been removed. The pliable material 112 covers the center active areas 84 of the cells 90 in the array. Anode current collector material 106 extends under the pliable polymer coating 110 and around the sides of the cells 90 to electrically couple the anodes to each other. The anode current collector 24, 106 does not cover non-conducting material 94 exposed along the edges of the cells 90 or tabs 30, 88.

(76) The ninth step 290 of the method 200 is cutting each tab 30, 88 exposing the cathode-current terminal contact 32 and removing each individual cell 90 from the array. After the tab 30, 88 has been cut, preferably by a laser cutting device, the individual cells 90 can now removed them from the array and have a cell configuration substantially the same as the cell 10 shown in FIGS. 1 and 2.

(77) The following disclosure refers to FIG. 28 and is directed to a preferred embodiment of a method for manufacturing a multi-cell solid state battery 70, generally designated 300 and hereafter referred to as the method 300 in accordance with the present invention.

(78) The first step 310 of the method 300 is fabrication of a plurality of cells in accordance with the method 200 disclosed above.

(79) The second step 320 of the method 300 is stacking the individual cells 10, 90 in a stack 44 such that the cathode-current terminal contacts 32 in the tabs 30 are aligned.

(80) The third step 330 of the method 300 is applying a cathode-coating conducting material 48 interconnecting the cathode-current terminal contacts 32.

(81) The fourth step 340 of the method 300 is applying an anode-coating conducting-material 46 interconnecting the anode-current collecting material 106 of each cell 10, 90.

(82) The fifth step 350 of the method 300 is hermetically sealing the stack 44 of in a housing 50 such that the anode-coating conducting-material 106 is in electrical contact with the housing 50 which functions as an anode terminal 72 of the battery and the cathode-coating conducting material 48 is in electrical contact with a cathode lead terminal 60 which is insulated from and extends beyond the housing 50 and functions as the cathode terminal 74 of the battery.

(83) Referring to FIGS. 29 and 30, a preferred embodiment of a single mono-polar battery cell in accordance with the present invention is shown therein and is hereafter referred to as the mono-cell 120. Since the mono-cell 120 comprises many of the same elements as the battery cell 10, like reference numbers for like elements are used throughout. Further, for brevity, the following discussion will be directed only to the features of the mono-cell 120 that are different than the feature of the battery cell 10 and the bipolar pair of cells 34.

(84) The mono-cell 120 has an alternative packaging frame 122 defining an inactive perimeter region 124 circumscribing a recessed well 14 including an accommodating region 24 for anode swelling. As can be seen in FIGS. 29 and 30, the entire outwardly facing surface 126 of the conductive cathode-current collector 28 is exposed. In some embodiments, it may be preferable to eliminate the conductive cathode-current collector 28 allowing the outwardly facing surface of the cathode 20 be serve as the cathode contact of the mono-cell 120.

(85) A pair of mono-cells may be stacked as shown in FIG. 31 to form a common anode accommodating region 128. Alternatively, a plurality of mono-cells 120 may be stacked and connected in series as shown in FIG. 32 with the anode and cathode of adjacent cells in contact with each other. In this configuration, the bottom most conductive cathode collector 28 serves as a cathode terminal for the stack and the anode terminal strip 46 serves as the anode terminal for the stack.

(86) The present disclosure describes construction of the invention using physical deposition techniques; however, it is understood that other techniques such as thermal lamination of selected layers may be desirable depending on the physical configuration of the cells. For thicker cells having greater changes in anode volume, lamination using a polymer film or 3D printing the desired frame pattern may be more suitable.

(87) The invention is particularly suitable as a package for a secondary battery, which is also known in the industry as a rechargeable battery. However, the packaging structure and methodology taught herein are applicable to other types of electrochemical cells including primary (or non-rechargeable) cells wherein it is desirable to protect an electrode by isolating it from other substances. Although the invention has been described in the context of isolating anode material, the teachings are equally applicable to the isolation of cathode material. In addition, the reinforced battery package taught provides protection for the electrolyte, anode and cathode cell components.

(88) Many variations and modifications may be made to the above-described embodiments without departing from the scope of the claims. All such modifications, combinations, and variations are included herein by the scope of this disclosure and the following claims. For example, the frame 12 and corresponding cell assembly are shown in rectangular or substantially square embodiments. The invention is not limited to these configurations but teaches any geometric configuration for a squat or low-profile substantially tubular frame structure. For example, suitable shapes include parallelogram, circle, ellipse and various polygons. The invention also encompasses variations in the number of plies of material that comprise the frame structure. The invention teaches that the frame may include plies in addition to the innermost ply and the outermost ply. Such additional plies will provide additional reinforcement and may comprise materials to enhance the performance of either the outermost, electrically conductive ply or the innermost, impermeable, non-electrically conductive ply. The conductive portions of the frames may be die cut and stamped into the desired shape and formed around the cell. The configuration of the of the frame is another example of variations taught by the invention. In an embodiment, the frame is displayed as “squat” or having a “low profile.” However, the shape is not limited to a squat, or low-profile, frame of the exemplary embodiment described and, furthermore, the invention contemplates extended as well as lesser elevations. For example, for cells having thicker anodes and/or cathodes, frames having a more extended elevation are employed without departing from the scope of the claims.

(89) It will be appreciated by those skilled in the art that changes could be made to the embodiments described above without departing from the broad inventive concept thereof. It is understood, therefore, that this invention is not limited to the particular embodiments disclosed, but it is intended to cover modifications within the spirit and scope of the present invention as defined by the appended claims.

(90) The foregoing detailed description of the invention has been disclosed with reference to specific embodiments. However, the disclosure is not intended to be exhaustive or to limit the invention to the precise forms disclosed. Those skilled in the art will appreciate that changes could be made to the embodiments described above without departing from the broad inventive concept thereof. Therefore, the disclosure is intended to cover modifications within the spirit and scope of the present invention as defined by the appended claims.

(91) All references, patent applications, and patents mentioned above are incorporated herein by reference in their entirety and are not to be construed as an admission that any of the cited documents constitutes prior art, or as an admission against interest in any manner.