Soft magnetic metal powder, dust core, and magnetic component
11152145 · 2021-10-19
Assignee
Inventors
- Takuma NAKANO (Tokyo, JP)
- Kazuhiro Yoshidome (Tokyo, JP)
- Hiroyuki Matsumoto (Tokyo, JP)
- Satoko MORI (Tokyo, JP)
- Seigo TOKORO (Tokyo, JP)
- Kenji Horino (Tokyo, JP)
Cpc classification
H01F1/15333
ELECTRICITY
H01F41/0246
ELECTRICITY
International classification
Abstract
Soft magnetic metal powder which includes a plurality of soft magnetic metal particles configured by a Fe-based nanocrystal alloy including Cu is provided, wherein the soft magnetic metal particles have core portions and first shell portions surrounding circumferences of the core portions; when an average crystallite size of Cu crystallites existing in the core portions is set as A, and the largest crystallite size of Cu crystallites existing in the first shell portions is set as B, B/A is 3.0 or more and 1000 or less.
Claims
1. Soft magnetic metal powder, comprising a plurality of soft magnetic metal particles configured by a Fe-based nanocrystal alloy comprising Cu, wherein the soft magnetic metal particles have core portions and first shell portions surrounding circumferences of the core portions; B/A is 3.0 or more and 1000 or less, in which an average crystallite size of Cu crystallites existing in the core portions is set as A, and the largest crystallite size of Cu crystallites existing in the first shell portions is set as B.
2. The soft magnetic metal powder according to claim 1, wherein C/A is 2.0 or more and 50 or less, in which the average crystallite size of the Cu crystallites existing in the core portions is set as A, and an average crystallite size of Cu crystallites existing in the first shell portions is set as C.
3. The soft magnetic metal powder according to claim 2, wherein D is 3.0 nm or more and 20 nm or less, in which an average minor axis diameter of the Cu crystallites existing in the first shell portions is set as D.
4. The soft magnetic metal powder according to claim 1, wherein D is 3.0 nm or more and 20 nm or less, in which an average minor axis diameter of the Cu crystallites existing in the first shell portions is set as D.
5. The soft magnetic metal powder according to claim 1, wherein an average crystallite size of Fe crystallites of the soft magnetic metal particles is 1.0 nm or more and 30 nm or less.
6. The soft magnetic metal powder according to claim 1, wherein the soft magnetic metal particles have second shell portions surrounding circumferences of the first shell portions, and the second shell portions are layers comprising Cu or Cu oxide.
7. The soft magnetic metal powder according to claim 1, wherein surfaces of the soft magnetic metal particles are coated by coating portions; and the coating portions comprise a compound of one or more elements selected from a group consisting of P, Si, Bi, and Zn.
8. A dust core, which is configured by the soft magnetic metal powder according to claim 1.
9. A magnetic component comprising the dust core according to claim 8.
Description
BRIEF DESCRIPTION OF THE DRAWINGS
(1)
(2)
(3)
(4)
(5)
DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS
(6) Hereinafter, the present invention is specifically described based on a detailed embodiment shown in the drawings in the following order.
(7) 1. Soft Magnetic Metal Powder
(8) 1.1. Soft Magnetic Metal Particle 1.1.1. Core Portion 1.1.2. First Shell Portion 1.1.3. Second Shell Portion
(9) 1.2. Coating Portion
(10) 2. Dust Core
(11) 3. Magnetic Component
(12) 4. Method for Producing Dust Core
(13) 4.1. Method for Producing Soft Magnetic Metal Powder
(14) 4.2. Method for Producing Dust Core
(15) (1. Soft Magnetic Metal Powder)
(16) As shown in
(17) In addition, an average particle size (D50) of the soft magnetic metal powder of the embodiment may be selected corresponding to the application and the material. In the embodiment, the average particle size (D50) is preferably within a range of 0.3-100 μm. Sufficient moldability or predetermined magnetic properties are easily maintained by setting the average particle size of the soft magnetic metal powder within the above range. A measurement method of the average particle size is not particularly limited, and a laser diffraction scattering method is preferably used.
(18) (1.1. Soft Magnetic Metal Particle)
(19) In the embodiment, the soft magnetic metal particles are configured by a Fe-based nanocrystal alloy including Cu. The Fe-based nanocrystal alloy is an alloy in which microcrystals of a nanometer order are deposited in an amorphous substance by heat-treating a Fe-based amorphous alloy or a Fe-based alloy having a nano-heterostructure in which initial microcrystals exist in the amorphous substance. In the embodiment, crystallites composed of Fe (Fe crystallites) and crystallites composed of Cu (Cu crystallites) disperse in the amorphous substance. Furthermore, Cu is preferably included in the Fe-based nanocrystal alloy by 0.1 atom % or more.
(20) The Fe-based nanocrystal alloy including Cu may be, for example, Fe—Si—Nb—B—Cu-based nanocrystal alloy, Fe—Nb—B—P—Cu-based nanocrystal alloy, Fe—Nb—B—P—Si—Cu-based nanocrystal alloy, Fe—Nb—B—P—Cu—C-based nanocrystal alloy, and Fe—Si—P—B—Cu-based nanocrystal alloy or the like.
(21) In the embodiment, the soft magnetic metal powder may only include soft magnetic metal particles having the same material, or the soft magnetic metal particles having different materials may be mixed in the soft magnetic metal powder. For example, the soft magnetic metal powder may be a mixture of a plurality of Fe—Si—Nb—B—Cu-based nanocrystal alloy particles and a plurality of Fe—Nb—B—P—Cu-based nanocrystal alloy particles.
(22) Furthermore, the difference in materials includes an occasion that the elements configuring the metal or the alloy are different, an occasion that even if the elements configuring the metal or the alloy are the same, the compositions are different, or the like.
(23) In addition, the average crystallite size of the Fe crystallites is preferably 1.0 nm or more and 50 nm or less, and more preferably 5.0 nm or more and 30 nm or less. By setting the average crystallite size of the Fe crystallites within the above range, when coating portions described later are formed on the soft magnetic metal particles, an increase in coercivity can be suppressed even when stress is applied to the particles. The average crystallite size of the Fe crystallites can be calculated, for example, based on a half-value width obtained by predetermined peaks of diffraction patterns obtained by an X-ray diffraction measurement of the soft magnetic metal powder.
(24) In addition, in the embodiment, as shown in
(25) (1.1.1. Core Portion) The core portions 2a are regions including centers of the soft magnetic metal particles 2, and as shown in
(26) As described later, A has a prescribed relationship with the largest crystallite size B of the Cu crystallites existing in the first shell portions.
(27) (1.1.2. First Shell Portion)
(28) The first shell portions 2b are regions surrounding the circumferences of the core portions 2a. As shown in
(29) B/A also depends on a value of the average crystallite size A of the Cu crystallites 3a existing in the core portions 2a, and is preferably 5.0 or more and 80.0 or less when A is about 5 nm. When B/A is too large, there is a tendency that greatly grown crystals of Cu are deposited on the surfaces of the particles and insulation between the particles is reduced accordingly, leading to a decrease in the withstand voltage property.
(30) Further, when the average crystallite size of the Cu crystallites 3b existing in the first shell portions 2b is set as C [nm], C is preferably 2.0 nm or more, and more preferably 5.0 nm or more. In addition, C is preferably 100 nm or less, and more preferably 50 nm or less. When C is too large, similar to the occasion of B/A, there is a tendency that greatly grown crystals of Cu are deposited on the surfaces of the particles and insulation between the particles is reduced accordingly, leading to a decrease in the withstand voltage property.
(31) In addition, C/A, which shows a ratio of the average crystallite size (C) of the Cu crystallites 3b existing in the first shell portions 2b with respect to the average crystallite size (A) of the Cu crystallites 3a existing in the core portions 2a, is preferably 2.0 or more and 50 or less.
(32) Note that, conventionally, it is considered that properties are improved by uniformly dispersing the crystallites deposited in the amorphous substance over the entire particles. However, in the embodiment, by differentiating the size and the existing state of the Cu crystallites between the center sides and the surface sides of the soft magnetic metal particles, the withstand voltage of the soft magnetic metal particles can be improved.
(33) In addition, in cross section shapes of the Cu crystallites existing in the first shell portions, when minimum diameters passing through centers are set as minor axis diameters ds, an average value of the minor axis diameters ds (an average minor axis diameter: D [nm]) is preferably 1.0 nm or more and 20 nm or less.
(34) In the embodiment, the average crystallite size is a diameter of a circle (an equivalent circle diameter) having an area the same as the area in which a cumulative distribution of the area of the crystallites is 50% (D50). As for the areas of the Cu crystallites, the Cu crystallites existing in the core portions and the first shell portions are respectively identified from observation images obtained by observing the Cu crystallites appearing on the cross sections of the soft magnetic metal particles by TEM or the like, and the areas of the Cu crystallites can be calculated by image processing software or the like. The number of the crystallites for which the areas are measured is about 100-500.
(35) In addition, the largest crystallite size is a diameter of a circle (an equivalent circle diameter) having an area the same as the largest area among the areas of the Cu crystallites calculated in the first shell portions.
(36) In addition, the average minor axis diameter is a minor axis diameter for which a cumulative distribution of the minor axis diameter of the Cu crystallites is 50% (D50). As for the minor axis diameters, similar to the above average crystallite size, the Cu crystallites are identified, and the minimum diameters passing through the centers of the crystallites in the Cu crystallites identified in the first shell portions are calculated as the minor axis diameters.
(37) Thicknesses of the first shell portions 2b are not particularly limited as long as the effect of the present invention is obtained. In the embodiment, the thicknesses of the first shell portions 2b are preferably about 1/100 of the particle diameters of the soft magnetic metal particles.
(38) The core portions and the first shell portions can be distinguished by observing a distribution of Cu by an element analysis of energy dispersive X-ray spectroscopy (EDS) which uses a transmission electron microscope (TEM) such as a scanning transmission electron microscope (STEM) or the element analysis of electron energy loss spectroscopy (EELS).
(39) For example, first, the crystallite sizes of Cu are calculated by STEM-EDS for the center portions of the soft magnetic metal particles 2 and the surface sides of the soft magnetic metal particles 2. On the center portions and the surface sides, when sizes of the calculated crystallite sizes of Cu are changed, it means that it is divided into the core portions and the shell portions. Furthermore, as a method for identifying the Cu crystallites, a three-dimensional atomic probe (sometimes referred to as 3DAP hereinafter) is used to measure the composition distribution and the sizes of the Cu crystallites can be identified. In addition, the Cu crystallites can be identified from information such as lattice constants or the like obtained from a fast Fourier transform (FFT) analysis or the like of the TEM images.
(40) (1.1.3. Second Shell Portion)
(41) In the embodiment, the soft magnetic metal particles 2 may also have second shell portions 2c. As shown in
(42) In the embodiment, the second shell portions are regions including Cu or Cu-containing oxide and are crystalline regions. Different from the core portions and the first shell portions described above, Cu or the Cu-containing oxide is not dispersed in the amorphous substance but continuously exists in the second shell portions 2c and forms layer-like regions. The insulation is improved by forming the second shell portions 2c in the soft magnetic metal particles 2, and thus the withstand voltage can be further improved.
(43) Furthermore, the second shell portions 2c are mainly configured by components not contributing to the improvement of the magnetic properties. Therefore, when the soft magnetic metal particles do not have the second shell portions, although the withstand voltage is slightly reduced, a proportion of the components contributing to the improvement of the magnetic properties can be improved, and thus the saturation magnetic flux density can be improved for example.
(44) Thicknesses of the second shell portions 2c are not particularly limited as long as the effect of the present invention is obtained. In the embodiment, the thicknesses of the second shell portions 2c are preferably 5 nm-100 nm.
(45) (1.2. Coating Portion)
(46) In the embodiment, the soft magnetic metal particles may be coated particles with the coating portions. As shown in
(47) In addition, in the embodiment, coating the surfaces by a substance means a form in which the substance is brought into contact with the surfaces and is fixed so as to cover the contacted parts. In addition, the coating portion coating the soft magnetic metal particle may cover at least part of the surface of the particle, and preferably covers the entire surface. Furthermore, the coating portion may continuously or intermittently cover the surface of the particle.
(48) The coating portions 10 are not particularly limited as long as they are configurations capable of insulating the soft magnetic metal particles configuring the soft magnetic metal powder from one another. In the embodiment, the coating portions 10 preferably include a compound of one or more elements selected from a group consisting of P, Si, Bi and Zn. In addition, the compound is more preferably an oxide, and particularly preferably oxide glass.
(49) Further, the compound of one or more elements selected from the group consisting of P, Si, Bi and Zn is preferably included as a main component in the coating portions 10. That “an oxide of one or more elements selected from the group consisting of P, Si, Bi and Zn is included as the main component” means, when a total amount of the elements except oxygen among the elements included in the coating portions 10 is set as 100 mass %, the total amount of the one or more elements selected from the group consisting of P, Si, Bi and Zn is the largest. In addition, in the embodiment, the total amount of these elements is preferably 50 mass % or more, and more preferably 60 mass % or more.
(50) The oxide glass is not particularly limited and may be, for example, phosphate (P.sub.2O.sub.5) glass, bismuthate (Bi.sub.2O.sub.3) glass, borosilicate (B.sub.2O.sub.3—SiO.sub.2) glass or the like.
(51) The P.sub.2O.sub.5-based glass is preferably the glass containing 50 wt % or more of P.sub.2O.sub.5, and P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 glass or the like is exemplified. Note that, “R” represents an alkali metal.
(52) The Bi.sub.2O.sub.3-based glass is preferably the glass containing 50 wt % or more of Bi.sub.2O.sub.3, and Bi.sub.2O.sub.3—ZnO—B.sub.2O.sub.3—SiO.sub.2 glass or the like is exemplified.
(53) The B.sub.2O.sub.3—SiO.sub.2-based glass is preferably the glass containing 10 wt % or more of B.sub.2O.sub.3 and 10 wt % or more of SiO.sub.2, and BaO—ZnO—B.sub.2O.sub.3—SiO.sub.2—Al.sub.2O.sub.3 glass or the like is exemplified.
(54) The insulation of the particles is further improved by having the coating portions with such insulation, so that the withstand voltage of the dust core configured by the soft magnetic metal powder including the coated particles is improved.
(55) In the embodiment, when a number proportion of the particles included in the soft magnetic metal powder is set as 100%, the number proportion of the coated particles is preferably 90% or more, and preferably 95% or more.
(56) The components included in the coating portions can be identified from the information such as the lattice constants or the like obtained from the element analysis of EDS using a TEM such as a STEM or the like, the element analysis of EELS, the FFT analysis of the TEM images, and the like.
(57) Thicknesses of the coating portions 10 are not particularly limited as long as the above effect is obtained. In the embodiment, the thicknesses are preferably 5 nm or more and 200 nm or less. In addition, the thicknesses are preferably 150 nm or less, and more preferably 50 nm or less.
(58) (2. Dust Core)
(59) The dust core of the embodiment is not particularly limited as long as the dust core is configured by the above soft magnetic metal powder and is formed to have a predetermined shape. In the embodiment, the soft magnetic metal powder and a resin serving as a binding agent are included, and the dust core is fixed into the predetermined shape by binding the soft magnetic metal particles configuring the soft magnetic metal powder with one another via the resin. In addition, the dust core may also be configured by mixture powder of the above soft magnetic metal powder and other magnetic powder and formed into the predetermined shape.
(60) (3. Magnetic Component)
(61) The magnetic component of the embodiment is not particularly limited as long as the above dust core is included. For example, the magnetic component of the embodiment may be a magnetic component in which an air core coil wound with wires is buried inside the dust core with the predetermined shape, or a magnetic component in which wires are wound for a predetermined number of turns on a surface of the dust core with the predetermined shape. The magnetic component of the embodiment has good withstand voltage, and thus the magnetic component is suitable for a power inductor used in a power circuit.
(62) (4. Method for Producing Dust Core)
(63) Next, a method for producing the dust core included in the above magnetic component is described. First, the method for producing the soft magnetic metal powder configuring the dust core is described.
(64) (4.1. Method for Producing Soft Magnetic Metal Powder)
(65) The soft magnetic metal powder of the embodiment can be obtained using the method the same as the publicly known method for producing soft magnetic metal powder. Specifically, the soft magnetic metal powder can be produced using a gas atomization method, a water atomization method, a rotary disk method or the like. In addition, the soft magnetic metal powder can also be produced by mechanically pulverizing ribbons obtained by a single-roll method. Among these methods, from a point of view of easily obtaining the soft magnetic metal powder having desirable magnetic properties, the gas atomization method is preferably used.
(66) In the gas atomization method, first, a molten metal in which raw materials of the nanocrystal alloy configuring the soft magnetic metal powder are melted is obtained. The raw materials (pure metals and the like) of each metal element included in the nanocrystal alloy are prepared and weighed so as to achieve the composition of the finally obtained nanocrystal alloy, and the raw materials are melted. Note that, a method for melting the raw materials of the metal elements is not particularly limited, and for example, the method of vacuuming within a chamber of an atomization device and subsequently melting the raw materials by high frequency heating is exemplified. A temperature at the time of melting may be determined by considering a melting point of each metal element, and the temperature may be set to 1200-1500° C. for example.
(67) The obtained molten metal is supplied into the chamber in the form of linear continuous fluid through a nozzle provided on the bottom of a crucible, high-pressure gas is blown to the supplied molten metal to make the molten metal into droplets and rapidly cool the molten metal to obtain fine powder. The obtained powder is configured by the amorphous alloy in which each metal element uniformly disperses in the amorphous substance, or the alloy having the nano-heterostructure. A gas blowing temperature, a pressure within the chamber and the like may be determined corresponding to conditions under which the nanocrystals (the Fe crystallites and the Cu crystallites) are easily deposited in the amorphous substance in the heat treatment described later. In addition, as for the particle diameters, a particle diameter adjustment can be made by a sieve classification, an air stream classification or the like.
(68) Then, the obtained powder is treated with heat. Although the heat treatment for making the nanocrystals deposited in the amorphous substance and the heat treatment for forming the core portions and the shell portions (the first shell portions and the second shell portions) in the soft magnetic metal particles may be carried out separately, in the embodiment, the heat treatment for making the nanocrystals deposited doubles as the heat treatment for forming the core portions and the shell portions.
(69) In the heat treatment, oxygen concentration in the atmosphere is preferably 100 ppm or more and 20000 ppm or less, preferably 10000 ppm or less, and more preferably 5000 ppm or less. The heat treatment for making the nanocrystals deposited usually reduces the oxygen concentration greatly, for example, to 10 ppm or less, but in the embodiment, a dispersion state of the Cu crystallites can have a deviation in the soft magnetic metal particles mainly by setting the oxygen concentration within the above range. As a result, the core portions and the shell portions are formed easily. When the oxygen concentration is too large, the Cu crystallites existing in the first shell portions grow too much. Particularly, when the coating portions described later are formed, because the Cu crystallites are aggregated, there is a tendency that the grown Cu crystallites fall from the soft magnetic metal particles, the falling Cu intrudes into an insulation portion and the withstand voltage decreases.
(70) In addition, the heat treatment temperature is preferably 500° C. or higher and 700° C. or lower, a holding time is preferably 10 minutes or longer and 120 minutes or shorter, a temperature raising rate is preferably 50° C./min or lower. These heat treatment conditions can also control the dispersion state of the Cu crystallites.
(71) After the heat treatment, the powder is obtained which includes the soft magnetic metal particles which are configured by the nanocrystal alloy and in which the core portions, the first shell portions and the second shell portions are formed. Note that, although the second shell portions improve the withstand voltage as described above, the second shell portions are regions disadvantageous for the improvement of the magnetic properties, and thus the second shell portions may be removed from the obtained powder corresponding to the desired properties. A method for removing the second shell portions is not particularly limited, for example, an etching processing in which the powder is brought into contact with a fluid for melting the components configuring the second shell portions to remove the second shell portions, or the like is exemplified.
(72) Then, the coating portions are formed on the obtained soft magnetic metal particles. The method for forming the coating portions is not particularly limited, and the publicly known method can be adopted. A wet processing may be carried out to the soft magnetic metal particles to form the coating portions, or a dry processing may also be carried out to form the coating portions.
(73) In the embodiment, the coating portions can be formed by a mechanochemical coating method, a phosphate processing method, a sol-gel method or the like. In the mechanochemical coating method, for example, a powder coating device 100 shown in
(74) In the mechanochemical coating method, by adjusting a rotation rate of the container, a distance between the grinder and the inner wall of the container or the like, the generated friction heat can be controlled to control the temperature of the mixture of the soft magnetic metal powder and the powder-like coating materials. In the embodiment, the temperature is preferably 50° C. or higher and 150° C. or lower. The coating portions are formed easily in the manner of covering the surfaces of the soft magnetic metal particles by setting such a temperature range.
(75) (4.2. Method for Producing Dust Core)
(76) The dust core is produced using the above soft magnetic metal powder. The specific producing method is not particularly limited, and the publicly known method can be adopted. First, the soft magnetic metal powder including the soft magnetic metal particles on which the coating portions are formed and the publicly known resins serving as the binding agent are mixed to obtain a mixture. In addition, the obtained mixture may be formed into granulation powder as necessary. Then, the mixture or the granulation powder is filled into a press mold to be compressed and molded, and a molded body with a shape of the dust core to be made is obtained. The heat treatment is carried out to the obtained molded body at 50-200° C. for example, and thereby the resins are hardened and the dust core with the predetermined shape in which the soft magnetic metal particles are fixed via the resins is obtained. The magnetic component such as the inductor or the like is obtained by winding the wires for predetermined turns in the obtained dust core.
(77) In addition, the above mixture or the granulation powder and an air core coil formed by winding the wires for predetermined turns may be filled into the press mold to be compressed and molded, and the molded body in which the coil is buried inside is obtained. The dust core with the predetermined shape in which the coil is buried is obtained by carrying out the heat treatment to the obtained molded body. Because the coil is buried inside, the dust core functions as the magnetic component such as the inductor or the like.
(78) The embodiment of the present invention is described above, but the present invention is not limited to the above embodiment and may be changed in various aspects within the scope of the present invention.
Example
(79) Next, examples are used to more specifically describe the invention, but the present invention is not limited to these examples.
(80) (Experimental Samples 1-10)
(81) First, the powder including the particles configured by the soft magnetic alloy having the composition shown in table 1 and of which the average particle size D50 is the value shown in table 1 is prepared. The heat treatment is carried out under conditions shown in table 1 to the prepared powder, and the nanocrystals are deposited. A spectrum analysis of STEM-EELS is carried out to experimental sample 2 in a vicinity of the surfaces of the soft magnetic metal particle, and Cu is mapped. The results are shown in
(82) Next, the powder including the particles in which the nanocrystals are deposited is fed into the container of the powder coating device together with powder glass (a coating material) having a composition shown in table 1, and the powder glass is coated on the surfaces of the particles to form the coating portions, thereby obtaining the soft magnetic metal powder. An addition amount of the powder glass is set to 0.5 wt % with respect to 100 wt % of the powder including the particles in which the nanocrystals are deposited.
(83) In the example, in P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 powder glass as phosphate-based glass, P.sub.2O.sub.5 is 50 wt %, ZnO is 12 wt %, R.sub.2O is 20 wt %, Al.sub.2O.sub.3 is 6 wt %, and the rest is accessory components.
(84) Note that, the present inventors confirm that results the same as the results described later are obtained even when the same experiment is carried out on the glass having a composition in which P.sub.2O.sub.5 is 60 wt %, ZnO is 20 wt %, R.sub.2O is 10 wt %, Al.sub.2O.sub.3 is 5 wt %, and the rest is accessory components, and the glass having a composition in which P.sub.2O.sub.5 is 60 wt %, ZnO is 20 wt %, R.sub.2O is 10 wt %, Al.sub.2O.sub.3 is 5 wt %, and the rest is accessory components, or the like.
(85) Then, the core portions, the first shell portions and the second shell portions are specified for the obtained soft magnetic metal powder, the average crystallite size of the Cu crystallites is measured in the core portions, the average crystallite size, the largest crystallite size and the average minor axis diameter of the Cu crystallites are calculated in the first shell portions, and a determination on whether Cu or Cu-containing oxide layers exist or not in the second shell portions is carried out.
(86) As for the average crystallite size, the largest crystallite size and the average minor axis diameter of the crystallites, cross sections of the soft magnetic metal particles are observed using STEM-EDS at a magnification of 100,000-1,000,000, and in the core portions, 500 Cu crystallites are observed and areas of the crystallites are measured by the image processing software to calculate the equivalent circle diameters and set the equivalent circle diameters as the crystallite sizes of the crystallites. From the obtained crystallite sizes, the crystallite size having a cumulative distribution of 50% is set as the average crystallite size (D50). In addition, in the first shell portions, 100 Cu crystallites are observed and areas of the crystallites are measured by the image processing software to calculate the equivalent circle diameters and set the equivalent circle diameters as the crystallite sizes of the Cu crystallites. The largest crystallite size among the calculated crystallite sizes is set as the largest crystallite size. Further, in the first shell portions, contours of the observed Cu crystallites are extracted, and the shortest diameters among the diameters passing through the centers of the crystallites are set as the minor axis diameters. From the obtained minor axis diameters, the minor axis diameter having a cumulative distribution of 50% is set as the average minor axis diameter (D50). In addition, as for the crystallite sizes of Cu, 3DAP is used to measure the crystallite sizes of Cu under conditions equivalent to the above approach and calculate the average crystallite size or the like. The calculated results are the same as the results obtained by STEM-EDS. Further, the average crystallite size of the crystallites of Fe is calculated by XRD. The results are shown in table 1.
(87) Next, an evaluation of the dust core is carried out. A total amount of an epoxy resin which is a thermosetting resin and an imide resin which is a hardening agent is weighed so as to be a value shown in table 1 with respect to 100 wt % of the obtained soft magnetic metal powder, the epoxy resin and the imide resin are added to acetone to be made into a solution, and the solution is mixed with the soft magnetic metal powder. After the mixing, granules obtained by volatilizing the acetone are sized with a mesh of 355 μm. The granules are filled into a press mold with a toroidal shape having an outer diameter of 11 mm and an inner diameter of 6.5 mm and are pressurized under a molding pressure of 3.0 t/cm.sup.2 to obtain the molded body of the dust core. The resins in the obtained molded body of the dust core are hardened under the condition of 180° C. and 1 hour, and the dust core is obtained. In—Ga electrodes are formed at both ends of the dust core, a source meter is used to apply voltage on the top and the bottom of the samples of the dust core, and the withstand voltage is calculated from a voltage value when an electric current of 1 mA flows and the thickness (a distance between the electrodes) of the dust core. In the example, among samples in which the composition of the soft magnetic metal powder, the average particle size (D50), and the resin amount used at the time of forming the dust core are the same, samples showing a withstand voltage higher than the withstand voltage of the samples being the comparative examples are considered as good. The reason is that the withstand voltage varies with the difference in the resin amount. The results are shown in table 1.
(88) TABLE-US-00001 TABLE 1 Soft magnetic metal powder Soft magnetic metal particle Entire Core portion particle Average Heat treatment conditions Average crystallite Average Oxygen crystallite size (A) Experi- Comparative particle Holding Holding Temperature concen- size of Fe of Cu mental example/ size D50 temperature time raising rate tration crystallites crystallites No. example Composition (at %) (μm) (° C.) (min) (° C./min) (ppm) (nm) (nm) 1 Comparative Fe73.5Cu1Nb3Si13.5B9 25 525 60 10 10 20.3 5.3 example 2 Comparative Fe73.5Cu1Nb3Si13.5B9 25 525 60 10 10 20.3 5.3 example 3 Example Fe73.5Cu1Nb3Si13.5B9 25 525 60 10 100 20.7 5.2 4 Example Fe73.5Cu1Nb3Si13.5B9 25 525 60 10 200 21.0 5.2 5 Example Fe73.5Cu1Nb3Si13.5B9 25 525 60 10 400 21.5 5.4 6 Example Fe73.5Cu1Nb3Si13.5B9 25 525 60 10 1000 21.4 5.4 7 Example Fe73.5Cu1Nb3Si13.5B9 25 525 60 10 2000 21.3 5.5 8 Example Fe73.5Cu1Nb3Si13.5B9 25 525 60 10 5000 21.6 5.4 9 Example Fe73.5Cu1Nb3Si13.5B9 25 525 60 10 10000 21.5 5.6 10 Example Fe73.5Cu1Nb3Si13.5B9 25 525 60 10 20000 21.4 5.6 Soft magnetic metal powder Soft magnetic metal particle First shell portion Largest Average Average crystallite crystallite minor axis Second shell Dust core size (B) size (C) diameter (D) portion Property Experi- of Cu of Cu of Cu layer Resin Withstand mental crystallites crystallites crystallites including Cu Coating portion amount voltage No. (nm) (nm) (nm) C/A B/A or Cu oxide Coating material (wt %) (V/mm) 1 7.2 5.8 4.3 1.1 1.4 Observed — 2 36 2 7.2 5.8 4.3 1.1 1.4 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 267 3 15.5 8.3 5.6 1.6 3.0 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 355 4 25.0 10.3 8.3 2.0 4.8 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 430 5 36.0 20.4 14.5 3.8 6.7 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 533 6 39.3 25.3 17.8 4.7 7.3 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 641 7 45.2 30.2 24.4 5.5 8.2 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 456 8 73.2 50.2 43.2 9.3 13.6 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 403 9 102.1 78.4 67.3 14.0 18.2 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 398 10 120.3 93.2 84.5 16.6 21.5 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 378
(89) According to table 1, it can be confirmed that, when B/A is within the above range, compared with an occasion that B/A falls out of the range, the withstand voltage is good. Note that, when B/A increases, the withstand voltage tends to decrease. It means that, when B/A is large, the Cu crystallites existing in the first shell portions are considerably grown than the Cu crystallites existing in the core portions.
(90) Further, it can be confirmed that, when C/A is within the above range, compared with an occasion that C/A falls out of the range, the withstand voltage is good. When C/A increases, the withstand voltage tends to decrease. It means that, when C/A is large, the Cu crystallites existing in the first shell portions are considerably grown than the Cu crystallites existing in the core portions.
(91) If the Cu crystallites grow too much, the Cu crystallites show a tendency to be deposited on the surface layers of the particles and are easily peeled from the particles at the time of forming the coating portions. If the grown Cu crystallites are peeled, the peeled Cu destroys the coating portions. As a result, it is considered that regions with a low insulation are formed and the withstand voltage of the dust core decreases.
(92) (Experimental Samples 11-41)
(93) Except that the heat treatment conditions in the samples of experimental sample 5 are set to the conditions shown in tables 2-4, the soft magnetic metal powder is made in the same way as experimental sample 5, and an evaluation the same as experimental sample 5 is carried out. In addition, the obtained powder is used to make a dust core in the same way as experimental sample 5, and an evaluation the same as the experimental sample 5 is carried out. The results are shown in table 2. Furthermore, for the samples of experimental sample 22, before the coating portions are formed, the spectrum analysis of STEM-EELS is carried out in the vicinity of the surfaces of the nanocrystal alloy particles, and Cu is mapped. The results are shown in
(94) TABLE-US-00002 TABLE 2 Soft magnetic metal powder Soft magnetic metal particle Entire Core portion particle Average Heat treatment conditions Average crystallite Average Oxygen crystallite size (A) Experi- Comparative particle Holding Holding Temperature concen- size of Fe of Cu mental example/ size D50 temperature time raising rate tration crystallites crystallites No. example Composition (at %) (μm) (° C.) (min) (° C./min) (ppm) (nm) (nm) 11 Comparative Fe73.5Cu1Nb3Si13.5B9 25 450 10 30 10 1.1 0.3 example 12 Comparative Fe73.5Cu1Nb3Si13.5B9 25 475 10 30 10 5.0 1.4 example 13 Comparative Fe73.5Cu1Nb3Si13.5B9 25 500 10 30 10 12.3 3.2 example 14 Comparative Fe73.5Cu1Nb3Si13.5B9 25 525 10 30 10 19.5 5.2 example 15 Comparative Fe73.5Cu1Nb3Si13.5B9 25 550 10 30 10 21.4 6.4 example 16 Comparative Fe73.5Cu1Nb3Si13.5B9 25 575 10 30 10 23.1 8.3 example 17 Comparative Fe73.5Cu1Nb3Si13.5B9 25 600 10 30 10 29.8 10.3 example 18 Comparative Fe73.5Cu1Nb3Si13.5B9 25 625 10 30 10 40.3 14.3 example 19 Example Fe73.5Cu1Nb3Si13.5B9 25 450 10 30 400 1.2 0.2 20 Example Fe73.5Cu1Nb3Si13.5B9 25 475 10 30 400 4.3 1.1 21 Example Fe73.5Cu1Nb3Si13.5B9 25 500 10 30 400 11.2 2.1 22 Example Fe73.5Cu1Nb3Si13.5B9 25 525 10 30 400 18.3 4.8 23 Example Fe73.5Cu1Nb3Si13.5B9 25 550 10 30 400 21.1 5.8 24 Example Fe73.5Cu1Nb3Si13.5B9 25 575 10 30 400 22.3 7.8 25 Example Fe73.5Cu1Nb3Si13.5B9 25 600 10 30 400 25.7 9.3 26 Example Fe73.5Cu1Nb3Si13.5B9 25 625 10 30 400 30.7 14.1 27 Example Fe73.5Cu1Nb3Si13.5B9 25 450 60 10 400 1.1 0.3 28 Example Fe73.5Cu1Nb3Si13.5B9 25 475 60 10 400 4.8 1.3 29 Example Fe73.5Cu1Nb3Si13.5B9 25 500 60 10 400 12.4 3.1 5 Example Fe73.5Cu1Nb3Si13.5B9 25 525 60 10 400 21.5 5.4 30 Example Fe73.5Cu1Nb3Si13.5B9 25 550 60 10 400 22.3 6.6 31 Example Fe73.5Cu1Nb3Si13.5B9 25 575 60 10 400 24.1 8.5 32 Example Fe73.5Cu1Nb3Si13.5B9 25 600 60 10 400 29.8 10.7 33 Example Fe73.5Cu1Nb3Si13.5B9 25 625 60 10 400 41.3 14.7 34 Example Fe73.5Cu1Nb3Si13.5B9 25 450 600 10 400 1.3 0.2 35 Example Fe73.5Cu1Nb3Si13.5B9 25 475 600 10 400 4.1 1.3 36 Example Fe73.5Cu1Nb3Si13.5B9 25 500 600 10 400 12.8 3.3 37 Example Fe73.5Cu1Nb3Si13.5B9 25 525 600 10 400 22.5 5.7 38 Example Fe73.5Cu1Nb3Si13.5B9 25 550 600 10 400 23.1 6.9 39 Example Fe73.5Cu1Nb3Si13.5B9 25 575 600 10 400 25.3 8.8 40 Example Fe73.5Cu1Nb3Si13.5B9 25 600 600 10 400 30.1 10.9 41 Example Fe73.5Cu1Nb3Si13.5B9 25 625 600 10 400 42.3 15.1 Soft magnetic metal powder Soft magnetic metal particle First shell portion Largest Average Average crystallite crystallite minor axis Second shell Dust core size (B) size (C) diameter (D) portion Property Experi- of Cu of Cu of Cu layer Resin Withstand mental crystallites crystallites crystallites including Cu Coating portion amount voltage No. (nm) (nm) (nm) C/A B/A or Cu oxide Coating material (wt %) (V/mm) 11 0.4 0.3 0.2 1.0 1.3 Not observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 231 12 1.8 1.6 1.3 1.1 1.3 Not observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 241 13 3.9 3.4 3.0 1.1 1.2 Not observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 244 14 6.7 5.3 4.9 1.0 1.3 Not observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 254 15 7.9 6.5 5.6 1.0 1.2 Not observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 234 16 11.2 9.1 7.5 1.1 1.3 Not observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 254 17 13.5 10.6 8.4 1.0 1.3 Not observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 234 18 19.3 14.5 12.3 1.0 1.3 Not observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 246 19 9.3 4.8 3.8 24.0 46.5 Not observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 321 20 11.3 5.3 4.2 4.8 10.3 Not observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 345 21 23.1 13.1 6.5 6.2 11.0 Not observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 367 22 31.2 19.2 13.2 4.0 6.5 Not observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 393 23 36.3 22.1 15.3 3.8 6.3 Not observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 483 24 44.6 26.7 17.8 3.4 5.7 Not observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 456 25 55.3 29.1 23.5 3.1 5.9 Not observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 432 26 73.1 31.2 28.4 2.2 5.2 Not observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 333 27 8.8 5.8 6.5 19.3 29.3 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 421 28 12.1 8.3 5.6 6.4 9.3 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 432 29 24.2 14.1 7.4 4.5 7.8 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 478 5 36.0 20.4 14.5 3.8 6.7 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 533 30 39.3 23.1 14.6 3.5 6.0 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 554 31 40.5 28.9 15.3 3.4 4.8 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 433 32 58.9 32.1 48.2 3.0 5.5 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 421 33 78.3 42.1 57.3 2.9 5.3 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 367 34 194 31 6.5 153.0 970 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 343 35 201 38 5.6 29.3 155 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 343 36 231 42 7.4 12.7 70.0 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 354 37 255 45 14.5 7.9 44.7 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 321 38 267 49 14.6 7.1 38.7 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 342 39 283 52 15.3 5.9 32.2 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 345 40 301 59 48.2 5.4 27.6 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 312 41 354 60 57.3 4.0 23.4 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 308
(95) According to table 2, it can be confirmed that when the oxygen concentration is 10 ppm, even if the other heat treatment conditions are changed, coarse Cu crystallites are not deposited on the surface sides of the particles, B/A falls out of the range of the present invention and the withstand voltage of the dust core decreases.
(96) It can be confirmed that when the oxygen concentration is 400 ppm, by changing the other heat treatment conditions, the deposition of the coarse Cu crystallites on the surface sides of the particles is controlled, and B/A changes within the range of the present invention. Specifically, it can be confirmed that when the holding temperature is low, the holding time is long, and the temperature raising rate is slow, B/A tends to increase.
(97) In addition, according to
(98) (Experimental Samples 42-43)
(99) Except that the coating material having the composition shown in table 3 is used to form the coating portions in the samples of experimental sample 5, the soft magnetic metal powder is made in the same way as experimental sample 5, and an evaluation the same as experimental sample 5 is carried out. In addition, the obtained powder is used to make the dust core in the same way as experimental sample 5, and the evaluation the same as experimental sample 5 is carried out. The results are shown in table 3.
(100) TABLE-US-00003 TABLE 3 Soft magnetic metal powder Soft magnetic metal particle Entire Core portion particle Average Heat treatment conditions Average crystallite Average Oxygen crystallite size (A) Experi- Comparative particle Holding Holding Temperature concen- size of Fe of Cu mental example/ size D50 temperature time raising rate tration crystallites crystallites No. example Composition (at %) (μm) (° C.) (min) (° C./min) (ppm) (nm) (nm) 5 Example Fe73.5Cu1Nb3Si13.5B9 25 525 60 10 400 21.5 5.4 42 Example Fe73.5Cu1Nb3Si13.5B9 25 525 60 10 400 21.5 5.4 43 Example Fe73.5Cu1Nb3Si13.5B9 25 525 60 10 400 21.5 5.5 Soft magnetic metal powder Soft magnetic metal particle First shell portion Largest Average Average crystallite crystallite minor axis Second shell Dust core size (B) size (C) diameter (D) portion Property Experi- of Cu of Cu of Cu layer Resin Withstand mental crystallites crystallites crystallites including Cu Coating portion amount voltage No. (nm) (nm) (nm) C/A B/A or Cu oxide Coating material (wt %) (V/mm) 5 36.0 20.4 14.5 3.8 6.7 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 533 42 36.0 20.4 14.5 3.8 6.7 Observed Bi.sub.2O.sub.3—ZnO—B.sub.2O.sub.3—SiO.sub.2 2 502 43 36.0 20.4 14.5 3.7 6.5 Observed BaO—ZnO—B.sub.2O.sub.3—SiO.sub.2—Al.sub.2O.sub.3 2 563
(101) According to table 3, it can be confirmed that when B/A is within the above range, regardless of the composition of the coating material, the withstand voltage of the dust core is good.
(102) In addition, in the example, in Bi.sub.2O.sub.3—ZnO—B.sub.2O.sub.3—SiO.sub.2 powder glass as the bismuth salt glass, Bi.sub.2O.sub.3 is 80 wt %, ZnO is 10 wt %, B.sub.2O.sub.3 is 5 wt %, and SiO.sub.2 is 5 wt %. It is confirmed that when the same experiment is also carried out on the glass serving as the bismuth salt glass and having other compositions, the same results as the results described later are obtained.
(103) Further, in the example, in BaO—ZnO—B.sub.2O.sub.3—SiO.sub.2—Al.sub.2O.sub.3 powder glass as the borosilicate glass, BaO is 8 wt %, ZnO is 23 wt %, B.sub.2O.sub.3 is 19 wt %, SiO.sub.2 is 16 wt %, Al.sub.2O.sub.3 is 6 wt %, and the rest is accessory components. It is confirmed that when the same experiment is also carried out on the glass serving as the borosilicate glass and having other compositions, and the same results as the results described later are obtained.
(104) (Experimental Samples 44-49)
(105) Except that the average particle size D50 of the powder in experimental samples 2 and 5 is set to the values shown in table 4, the soft magnetic metal powder is made in the same way as experimental samples 2 and 5, and an evaluation the same as experimental samples 2 and 5 is carried out. In addition, the obtained powder is used to make the dust core in the same way as experimental samples 2 and 5, and the evaluation the same as experimental samples 2 and 5 is carried out. The results are shown in table 4.
(106) TABLE-US-00004 TABLE 4 Soft magnetic metal powder Soft magnetic metal particle Entire Core portion particle Average Heat treatment conditions Average crystallite Average Oxygen crystallite size (A) Experi- Comparative particle Holding Holding Temperature concen- size of Fe of Cu mental example/ size D50 temperature time raising rate tration crystallites crystallites No. example Composition (at %) (μm) (° C.) (min) (° C./min) (ppm) (nm) (nm) 44 Comparative Fe73.5Cu1Nb3Si13.5B9 5 525 60 10 10 21.0 5.2 example 45 Comparative Fe73.5Cu1Nb3Si13.5B9 10 525 60 10 10 21.5 5.2 example 2 Comparative Fe73.5Cu1Nb3Si13.5B9 25 525 60 10 10 20.3 5.3 example 46 Comparative Fe73.5Cu1Nb3Si13.5B9 50 525 60 10 10 20.4 5.5 example 47 Example Fe73.5Cu1Nb3Si13.5B9 5 525 60 10 400 21.5 5.3 48 Example Fe73.5Cu1Nb3Si13.5B9 10 525 60 10 400 22.1 5.3 5 Example Fe73.5Cu1Nb3Si13.5B9 25 525 60 10 400 21.5 5.4 49 Example Fe73.5Cu1Nb3Si13.5B9 50 525 60 10 400 23.1 5.5 Soft magnetic metal powder Soft magnetic metal particle First shell portion Largest Average Average crystallite crystallite minor axis Second shell Dust core size (B) size (C) diameter (D) portion Property Experi- of Cu of Cu of Cu layer Resin Withstand mental crystallites crystallites crystallites including Cu Coating portion amount voltage No. (nm) (nm) (nm) C/A B/A or Cu oxide Coating material (wt %) (V/mm) 44 7.1 5.4 4.1 1.0 1.4 Observed P.sub.2O.sub.5—ZnO—R.sub.2O— Al.sub.2O.sub.3 3 204 45 7.3 5.6 4.2 1.1 1.4 Observed P.sub.2O.sub.5—ZnO—R.sub.2O— Al.sub.2O.sub.3 2 156 2 7.2 5.8 4.3 1.1 1.4 Observed P.sub.2O.sub.5—ZnO—R.sub.2O— Al.sub.2O.sub.3 2 267 46 7.5 5.9 4.8 1.1 1.4 Observed P.sub.2O.sub.5—ZnO—R.sub.2O— Al.sub.2O.sub.3 2 143 47 37.2 20.1 13.8 3.8 7.0 Observed P.sub.2O.sub.5—ZnO—R.sub.2O— Al.sub.2O.sub.3 3 306 48 36.4 20.4 14.6 3.8 6.9 Observed P.sub.2O.sub.5—ZnO—R.sub.2O— Al.sub.2O.sub.3 2 321 5 36.0 20.4 14.5 3.8 6.7 Observed P.sub.2O.sub.5—ZnO—R.sub.2O— Al.sub.2O.sub.3 2 533 49 37.9 20.5 14.2 3.7 6.9 Observed P.sub.2O.sub.5—ZnO—R.sub.2O— Al.sub.2O.sub.3 2 345
(107) According to table 4, it can be confirmed that when B/A is within the above range, the withstand voltage of the dust core is good regardless of the average particle size D50 of the powder.
(108) Note that, with respect to 100 wt % of the powder including the particles in which the nanocrystals are deposited, when the average particle size (D50) of the powder is 5 μm and 10 μm, the addition amount of the powder glass is set to 1 wt %, and when the average particle size (D50) of the powder is 25 μm and 50 μm, the addition amount of the powder glass is set to 0.5 wt %. A powder glass amount required for forming a predetermined thickness varies with the particle diameters of the soft magnetic metal powder on which the coating portions are formed.
(109) (Experimental Sample 50-181)
(110) Except that the heat treatment is carried out under the conditions shown in tables 5 to 8 to the powder which includes the particles configured by the soft magnetic alloy having the composition shown in tables 5 to 8 and of which the average particle size D50 is the value shown tables 5 to 8, and the nanocrystals are deposited, the soft magnetic metal powder is made in the same way as experimental samples 1-10, and an evaluation the same as experimental sample 5 is carried out. In addition, the obtained powder is used to make the dust core in the same way as experimental sample 5, and the evaluation the same as experimental sample 5 is carried out. The results are shown in tables 5 to 8.
(111) TABLE-US-00005 TABLE 5 Soft magnetic metal powder Soft magnetic metal particle Entire Core portion particle Average Heat treatment conditions Average crystallite Average Oxygen crystallite size (A) Experi- Comparative particle Holding Holding Temperature concen- size of Fe of Cu mental example/ size D50 temperature time raising rate tration crystallites crystallites No. Example Composition (at %) (μm) (° C.) (min) (° C./min) (ppm) (nm) (nm) 5 Example Fe73.5Cu1Nb3Si13.5B9 25 525 60 10 400 21.5 5.4 50 Example Fe77.5Cu1Nb3Si13.5B5 25 525 60 10 400 44.0 5.5 51 Example Fe75.5Cu1Nb3Si13.5B7 25 525 60 10 400 21.0 5.5 52 Example Fe71.5Cu1Nb3Si13.5B11 25 525 60 10 400 22.0 5.0 53 Example Fe69.5Cu1Nb3Si13.5B13 25 525 60 10 400 23.0 4.9 54 Example Fe74.4Cu0.1Nb3Si13.5B9 25 525 60 10 400 32.0 5.6 55 Example Fe71.5Cu3Nb3Si13.5B9 25 525 60 10 400 14.0 5.6 56 Example Fe79.5Cu1Nb3Si9.5B9 25 525 60 10 400 64.0 5.5 57 Example Fe75.5Cu1Nb3Si11.5B9 25 525 60 10 400 22.0 5.8 58 Example Fe73.5Cu1Nb3Si15.5B7 25 525 60 10 400 22.0 5.2 59 Example Fe71.5Cu1Nb3Si15.5B9 25 525 60 10 400 21.0 5.8 60 Example Fe69.5Cu1Nb3Si17.5B9 25 525 60 10 400 24.0 5.8 61 Example Fe75.5Cu1Nb1Si13.5B9 25 525 60 10 400 21.0 5.0 62 Example Fe71.5Cu1Nb5Si13.5B9 25 525 60 10 400 22.0 5.0 63 Example Fe66.5Cu1Nb10Si13.5B9 25 525 60 10 400 23.0 4.9 64 Example Fe73.5Cu1Ti3Si13.5B9 25 525 60 10 400 21.0 5.3 65 Example Fe73.5Cu1Zr3Si13.5B9 25 525 60 10 400 22.0 5.4 66 Example Fe73.5Cu1Hf3Si13.5B9 25 525 60 10 400 22.0 5.0 67 Example Fe73.5Cu1V3Si13.5B9 25 525 60 10 400 22.0 5.9 68 Example Fe73.5Cu1Ta3Si13.5B9 25 525 60 10 400 21.0 5.3 69 Example Fe73.5Cu1Mo3Si13.5B9 25 525 60 10 400 23.0 5.8 70 Example Fe73.5Cu1Hf1.5Nb1.5Si13.5B9 25 525 60 10 400 23.0 5.7 71 Example Fe79.5Cu1Nb2Si9.5B9C1 25 525 60 10 400 23.0 5.8 72 Example Fe79Cu1Nb2Si9B5C4 25 525 60 10 400 23.0 5.5 73 Example Fe73.5Cu1Nb3Si13.5B8C1 25 525 60 10 400 23.0 5.6 74 Example Fe73.5Cu1Nb3Si13.5B5C4 25 525 60 10 400 21.0 5.3 75 Example Fe69.5Cu1Nb3Si17.5B8C1 25 525 60 10 400 21.0 5.2 76 Example Fe69.5Cu1Nb3Si17.5B5C4 25 525 60 10 400 19.0 5.6 Soft magnetic metal powder Soft magnetic metal particle First shell portion Largest Average Average crystallite crystallite minor axis Second shell Dust core size (B) size (C) diameter (D) portion Property Experi- of Cu of Cu of Cu layer Resin Withstand mental crystallites crystallites crystallites including Cu Coating portion amount voltage No. (nm) (nm) (nm) C/A B/A or Cu oxide Coating material (wt %) (V/mm) 5 36.0 20.4 14.5 3.8 6.7 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 533 50 34.2 19.0 15.8 3.4 6.2 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 506 51 37.4 21.0 13.1 3.9 6.9 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 554 52 35.3 19.2 14.9 3.9 7.1 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 512 53 37.1 19.6 14.8 4.0 7.5 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 517 54 36.7 21.6 15.2 3.9 6.6 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 522 55 37.1 20.6 15.4 3.7 6.6 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 522 56 37.1 21.4 15.4 3.9 6.7 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 517 57 38.9 18.8 14.8 3.2 6.7 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 506 58 32.8 20.8 15.2 4.0 6.3 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 522 59 36.7 19.8 14.9 3.4 6.3 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 517 60 33.8 21.4 13.3 3.7 5.8 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 512 61 35.3 21.0 15.1 4.2 7.0 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 506 62 34.2 22.4 14.4 4.5 6.9 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 554 63 33.8 22.0 13.2 4.5 7.0 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 506 64 32.8 21.2 14.2 4.0 6.1 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 560 65 39.2 21.2 13.2 3.9 7.3 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 528 66 38.2 21.0 15.7 4.2 7.7 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 533 67 38.9 19.2 14.9 3.3 6.6 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 522 68 36.7 22.0 15.2 4.2 6.9 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 528 69 37.4 20.8 15.5 3.6 6.4 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 528 70 37.8 20.2 13.8 3.5 6.6 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 544 71 39.2 21.6 15.5 3.7 6.8 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 522 72 38.2 18.4 13.2 3.4 7.0 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 517 73 34.9 22.2 15.8 4.0 6.3 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 522 74 33.8 19.2 14.8 3.6 6.4 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 538 75 39.2 19.6 14.8 3.8 7.6 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 549 76 39.2 21.0 14.2 3.8 7.1 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 544
(112) TABLE-US-00006 TABLE 6 Soft magnetic metal powder Soft magnetic metal particle Entire Core portion particle Average Heat treatment conditions Average crystallite Average Oxygen crystallite size (A) Experi- Comparative particle Holding Holding Temperature concen- size of Fe of Cu mental example/ size D50 temperature time raising rate tration crystallites crystallites No. example Composition (at %) (μm) (° C.) (min) (° C./min) (ppm) (nm) (nm) 77 Example Fe89Zr7B3Cu1 25 600 60 10 400 7.0 5.2 78 Example Fe88Hf7B3Cu1 25 600 60 10 400 6.0 5.3 79 Example Fe84Nb3.5Zr3.5B8Cu1 25 600 60 10 400 7.0 5.6 80 Example Fe84Nb3.5Hf3.5B8Cu1 25 600 60 10 400 7.0 5.2 81 Example Fe90.9Nb6B3Cu0.1 25 600 60 10 400 7.0 5.6 82 Example Fe84Nb3.5Ti3.5B8Cu1 25 600 60 10 400 6.0 5.6 83 Example Fe84Nb3.5Ta3.5B8Cu1 25 600 60 10 400 7.0 5.6 84 Example Fe84Nb3.5Mo3.5B8Cu1 25 600 60 10 400 7.0 5.1 85 Example Fe84Nb3.5W3.5B8Cu1 25 600 60 10 400 7.0 5.8 86 Example Fe84Nb3.5Al3.5B8Cu1 25 600 60 10 400 7.0 5.9 87 Example Fe86.6Nb3.2B10Cu0.1C0.1 25 600 60 10 400 21.0 5.9 88 Example Fe75.8Nb14B10Cu0.1C0.1 25 600 60 10 400 15.0 5.1 89 Example Fe89.8Nb7B3Cu0.1C0.1 25 600 60 10 400 9.0 5.0 90 Example Fe72.8Nb7B20Cu0.1C0.1 25 600 60 10 400 15.0 5.5 91 Example Fe80.8Nb3.2B10Cu3C3 25 600 60 10 400 16.0 5.6 92 Example Fe70Nb14B10Cu3C3 25 600 60 10 400 13.0 5.0 93 Example Fe84Nb7B3Cu3C3 25 600 60 10 400 9.0 5.8 94 Example Fe67Nb7B20Cu3C3 25 600 60 10 400 11.0 5.6 95 Example Fe85Nb3B10Cu1C1 25 600 60 10 400 8.0 5.9 96 Example Fe84.8Nb3.2B10Cu1C1 25 600 60 10 400 12.0 5.9 97 Example Fe83Nb5B10Cu1C1 25 600 60 10 400 11.0 5.4 98 Example Fe81Nb7B10Cu1C1 25 600 60 10 400 8.0 5.6 99 Example Fe78Nb10B10Cu1C1 25 600 60 10 400 9.0 5.7 100 Example Fe76Nb12B10Cu1C1 25 600 60 10 400 10.0 5.3 101 Example Fe74Nb14B10Cu1C1 25 600 60 10 400 9.0 5.1 102 Example Fe75.8Nb14B10Cr0.1Cu0.1 25 600 60 10 400 8.0 5.2 103 Example Fe82.8Nb7B10Cr0.1Cu0.1 25 600 60 10 400 8.0 5.2 104 Example Fe86.8Nb3B10Cr0.1Cu0.1 25 600 60 10 400 12.0 5.1 105 Example Fe72.8Nb7B20Cr0.1Cu0.1 25 600 60 10 400 7.0 5.6 106 Example Fe89.8Nb7B3Cr0.1Cu0.1 25 600 60 10 400 6.0 4.9 107 Example Fe73Nb14B10Cr1.5Cu1.5 25 600 60 10 400 17.0 5.9 108 Example Fe80Nb7B10Cr1.5Cu1.5 25 600 60 10 400 9.0 5.2 109 Example Fe84Nb3B10Cr1.5Cu1.5 25 600 60 10 400 9.0 5.6 110 Example Fe70Nb7B20Cr1.5Cu1.5 25 600 60 10 400 10.0 5.2 111 Example Fe87Nb7B3Cr1.5Cu1.5 25 600 60 10 400 8.0 5.3 112 Example Fe72Nb11B14Cr1Cu2 25 600 60 10 400 12.0 5.5 113 Example Fe73Nb10B14Cr1Cu2 25 600 60 10 400 12.0 5.0 114 Example Fe90Nb5B3.5Cr0.5Cu1 25 600 60 10 400 8.0 5.0 115 Example Fe91Nb4.5B3Cr0.5Cu1 25 600 60 10 400 8.0 5.0 116 Example Fe74.5Nb14B10Cr0.5Cu1 25 600 60 10 400 11.0 5.8 117 Example Fe76.5Nb12B10Cr0.5Cu1 25 600 60 10 400 11.0 5.6 118 Example Fe78.5Nb10B10Cr0.5Cu1 25 600 60 10 400 12.0 5.9 119 Example Fe81.5Nb7B10Cr0.5Cu1 25 600 60 10 400 14.0 5.1 120 Example Fe83.5Nb5B10Cr0.5Cu1 25 600 60 10 400 12.0 5.7 121 Example Fe85.5Nb3B10Cr0.5Cu1 25 600 60 10 400 16.0 5.5 122 Example Fe80.9Nb7B10P0.1Cu1 25 600 60 10 400 6.0 5.9 123 Example Fe81.5Nb7B10P0.5Cu1 25 600 60 10 400 6.0 4.9 124 Example Fe81Nb7B10P1Cu1 25 600 60 10 400 6.0 5.3 125 Example Fe80Nb7B10P2Cu1 25 600 60 10 400 6.0 4.9 126 Example Fe79Nb7B10P3Cu1 25 600 60 10 400 6.0 5.9 127 Example Fe78Nb7B10P4Cu1 25 600 60 10 400 7.0 5.7 Soft magnetic metal powder Soft magnetic metal particle First shell portion Largest Average Average crystallite crystallite minor axis Second shell Dust core size (B) size (C) diameter (D) portion Property Experi- of Cu of Cu of Cu layer Resin Withstand mental crystallites crystallites crystallites including Cu Coating portion amount voltage No. (nm) (nm) (nm) C/A B/A or Cu oxide Coating material (wt %) (V/mm) 77 39.6 21.6 16.0 4.1 7.6 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 528 78 32.4 19.0 13.1 3.6 6.1 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 517 79 36.7 22.2 15.8 4.0 6.5 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 538 80 38.5 19.8 14.9 3.8 7.4 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 533 81 36.7 20.6 14.5 3.7 6.5 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 512 82 39.2 20.8 15.7 3.7 7.0 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 517 83 38.9 21.4 14.5 3.9 7.0 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 549 84 38.5 18.4 14.9 3.6 7.5 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 522 85 35.3 22.4 13.2 3.9 6.1 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 512 86 33.1 19.8 13.8 3.3 5.6 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 538 87 32.8 21.4 13.9 3.6 5.6 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 533 88 36.4 21.8 13.2 4.3 7.2 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 554 89 34.9 22.2 14.5 4.4 7.0 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 522 90 33.8 20.0 13.9 3.6 6.1 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 522 91 37.1 22.4 15.8 4.0 6.6 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 544 92 38.2 22.4 15.1 4.5 7.7 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 560 93 36.4 21.6 15.7 3.7 6.2 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 506 94 34.2 21.8 15.1 3.9 6.1 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 554 95 35.3 19.6 14.6 3.3 6.0 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 517 96 37.8 19.8 14.9 3.4 6.4 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 549 97 36.0 22.0 15.7 4.1 6.7 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 554 98 38.2 20.8 13.9 3.7 6.8 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 506 99 32.8 21.6 16.0 3.8 5.7 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 517 100 36.7 20.4 14.6 3.9 6.9 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 554 101 39.6 22.2 15.2 4.3 7.7 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 522 102 38.5 21.2 14.2 4.1 7.4 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 544 103 35.3 18.8 16.0 3.6 6.8 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 533 104 36.7 22.0 14.5 4.3 7.2 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 528 105 32.8 20.4 15.4 3.6 5.8 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 522 106 34.2 22.0 15.7 4.5 7.0 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 512 107 35.3 21.4 13.6 3.6 5.9 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 533 108 36.7 22.0 15.8 4.2 7.0 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 522 109 37.8 18.8 15.8 3.3 6.7 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 538 110 39.6 18.4 13.1 3.5 7.6 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 560 111 38.9 20.4 13.8 3.9 7.3 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 512 112 38.2 18.4 13.2 3.3 6.9 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 506 113 35.3 20.8 15.8 4.1 7.0 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 528 114 36.7 20.6 14.5 4.1 7.3 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 528 115 37.4 21.6 13.3 4.3 7.5 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 544 116 36.7 20.8 15.1 3.6 6.4 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 544 117 37.8 21.4 15.2 3.9 6.8 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 544 118 32.4 18.8 13.5 3.2 5.5 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 517 119 34.9 22.0 13.8 4.3 6.9 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 538 120 38.2 22.2 14.2 3.9 6.7 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 528 121 33.1 20.6 14.6 3.8 6.1 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 506 122 38.9 20.4 15.1 3.4 6.5 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 533 123 37.1 21.2 13.6 4.4 7.6 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 528 124 32.4 19.8 15.4 3.7 6.1 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 549 125 33.5 22.0 14.2 4.5 6.9 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 528 126 34.2 18.4 14.2 3.1 5.8 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 517 127 38.2 19.8 15.4 3.5 6.7 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 560
(113) TABLE-US-00007 TABLE 7 Soft magnetic metal powder Soft magnetic metal particle Heat treatment conditions Average Oxygen Experi- Comparative particle Holding Holding Temperature concen- mental example/ size D50 temperature time raising rate tration No. example Composition (at %) (μm) (° C.) (min) (° C./min) (ppm) 128 Example Fe93.8Nb3.2B2.8P0.1Cu0.1 25 600 60 10 400 129 Example Fe73.4Nb12B13P0.1Cu1.5 25 600 60 10 400 130 Example Fe90.9Nb3.2B13P3Cu0.1 25 600 60 10 400 131 Example Fe70.5Nb14B10P3Cu1.5 25 600 60 10 400 132 Example Fe80.9Nb7B10P0.1Cu1C1 25 600 60 10 400 133 Example Fe80.5Nb7B10P0.5Cu1C1 25 600 60 10 400 134 Example Fe80Nb7B10P1Cu1C1 25 600 60 10 400 135 Example Fe79Nb7B10P2Cu1C1 25 600 60 10 400 136 Example Fe78Nb7B10P3Cu1C1 25 600 60 10 400 137 Example Fe77.5Nb7B10P3.5Cu1C1 25 600 60 10 400 138 Example Fe93.7Nb3.2B2.8P0.1Cu0.1C0.1 25 600 60 10 400 139 Example Fe71.4Nb12B13P0.1Cu1.5C2 25 600 60 10 400 140 Example Fe90.8Nb3.2B2.8P3Cu0.1C0.1 25 600 60 10 400 141 Example Fe68.5Nb12B13P3Cu1.5C2 25 600 60 10 400 142 Example Fe81.4Nb7B10Cr0.5P0.1Cu1 25 600 60 10 400 143 Example Fe81Nb7B10Cr0.5P0.5Cu1 25 600 60 10 400 144 Example Fe80.5Nb7B10Cr0.5P1Cu1 25 600 60 10 400 145 Example Fe79.5Nb7B10Cr0.5P2Cu1 25 600 60 10 400 146 Example Fe78.5Nb7B10Cr0.5P3Cu1 25 600 60 10 400 147 Example Fe78Nb7B10P3.5Cr0.5Cu1 25 600 60 10 400 148 Example Fe93.7Nb3.2B2.8Cr0.1P0.1Cu0.1 25 600 60 10 400 149 Example Fe71.9Nb12B13Cr1.5P0.1Cu1.5 25 600 60 10 400 150 Example Fe90.8Nb3.2B2.8Cr0.1P3Cu0.1 25 600 60 10 400 151 Example Fe69Nb12B13Cr1.5P3Cu1.5 25 600 60 10 400 152 Example Fe80.4Nb7B10Cr0.5P0.1Cu1C1 25 600 60 10 400 153 Example Fe80Nb7B10Cr0.5P0.5Cu1C1 25 600 60 10 400 154 Example Fe79.5Nb7B10Cr0.5P1Cu1C1 25 600 60 10 400 155 Example Fe78.5Nb7B10Cr0.5P2Cu1C1 25 600 60 10 400 156 Example Fe77.5Nb7B10Cr0.5P3Cu1C1 25 600 60 10 400 157 Example Fe77Nb7B10P3.5Cr0.5Cu1C1 25 600 60 10 400 158 Example Fe93.6Nb3.2B2.8Cr0.1P0.1Cu0.1C0.1 25 600 60 10 400 159 Example Fe69.9Nb12B13Cr1.5P0.1Cu1.5C2 25 600 60 10 400 160 Example Fe90.7Nb3.2B2.8Cr0.1P3Cu0.1C0.1 25 600 60 10 400 161 Example Fe67Nb12B13Cr1.5P3Cu1.5C2 25 600 60 10 400 162 Example Fe79.9Nb7B9P3Si1Cu0.1 25 600 60 10 400 163 Example Fe77.9Nb7B9P3Si3Cu0.1 25 600 60 10 400 164 Example Fe75.9Nb7B9P3Si5Cu0.1 25 600 60 10 400 165 Example Fe70.9Nb7B9P3Si10Cu0.1 25 600 60 10 400 166 Example Fe65.9Nb7B9P3Si15Cu0.1 25 600 60 10 400 167 Example Fe78.9Nb7B9P3Si1Cu0.1C1 25 600 60 10 400 168 Example Fe76.9Nb7B9P3Si3Cu0.1C1 25 600 60 10 400 169 Example Fe74.9Nb7B9P3Si5Cu0.1C1 25 600 60 10 400 170 Example Fe69.9Nb7B9P10Si3Cu0.1C1 25 600 60 10 400 171 Example Fe64.9Nb7B9P15Si3Cu0.1C1 25 600 60 10 400 Soft magnetic metal powder Soft magnetic metal particle Entire Core portion First shell portion particle Average Largest Average Average Average crystallite crystallite crystallite minor axis crystallite size (A) size (B) size (C) diameter (D) Experi- size of Fe of Cu of Cu of Cu of Cu mental crystallites crystallites crystallites crystallites crystallites No. (nm) (nm) (nm) (nm) (nm) C/A B/A 128 7.0 4.9 38.2 19.6 16.0 4.0 7.8 129 6.0 5.7 32.8 20.2 14.6 3.5 5.7 130 7.0 5.9 36.0 21.6 15.1 3.6 6.1 131 7.0 5.7 36.4 22.4 14.1 3.9 6.4 132 7.0 5.5 34.2 20.4 15.4 3.7 6.2 133 6.0 5.6 33.5 19.8 13.5 3.6 6.0 134 7.0 5.9 34.9 18.8 15.1 3.2 5.9 135 7.0 5.6 32.4 18.8 14.5 3.4 5.8 136 7.0 5.8 36.4 19.2 14.1 3.3 6.2 137 7.0 5.7 38.2 18.4 15.4 3.2 6.7 138 7.0 5.2 37.8 21.0 14.1 4.1 7.3 139 6.0 5.2 39.6 19.4 15.1 3.7 7.6 140 7.0 5.1 38.2 21.4 14.6 4.2 7.5 141 7.0 5.8 34.6 22.0 13.6 3.8 5.9 142 8.0 5.0 33.8 21.2 13.1 4.3 6.8 143 9.0 5.0 35.3 22.2 14.6 4.4 7.0 144 8.0 5.6 38.9 19.4 14.1 3.5 7.0 145 7.0 5.0 37.8 19.6 14.2 3.9 7.5 146 8.0 5.9 38.9 21.0 14.2 3.5 6.5 147 7.0 5.3 35.3 20.6 15.7 3.9 6.7 148 8.0 4.9 32.4 21.4 14.1 4.4 6.7 149 7.0 5.9 34.9 20.0 16.0 3.4 5.9 150 7.0 5.0 39.2 20.0 14.1 4.0 7.8 151 12.0 5.4 38.2 21.0 14.5 3.9 7.1 152 9.0 5.8 36.0 21.4 14.8 3.7 6.2 153 9.0 5.7 34.6 19.4 15.5 3.4 6.0 154 9.0 5.3 32.4 20.8 14.2 3.9 6.1 155 9.0 5.8 32.4 20.4 13.2 3.5 5.6 156 8.0 5.9 36.0 21.6 13.5 3.7 6.1 157 9.0 5.6 32.8 20.8 15.5 3.7 5.8 158 8.0 5.1 38.5 20.6 13.3 4.0 7.5 159 9.0 5.2 32.8 19.4 13.6 3.7 6.3 160 14.0 5.5 35.6 22.0 14.6 4.0 6.5 161 13.0 5.3 35.6 22.2 15.4 4.2 6.7 162 7.0 5.5 38.2 21.6 13.3 4.0 7.0 163 8.0 5.6 32.4 21.4 15.1 3.8 5.8 164 7.0 5.2 33.1 20.8 13.2 4.0 6.3 165 7.0 5.3 38.9 19.8 14.5 3.7 7.3 166 7.0 5.7 34.2 21.0 13.6 3.7 6.0 167 7.0 5.2 38.2 21.6 13.9 4.1 7.3 168 8.0 5.8 36.7 19.0 14.4 3.3 6.3 169 7.0 5.3 34.6 19.4 14.5 3.7 6.5 170 10.0 5.1 38.2 20.6 13.2 4.1 7.5 171 8.0 4.9 35.6 19.6 15.2 4.0 7.3 Soft magnetic metal powder Soft magnetic metal particle Second shell Dust core portion Property Experi- layer Resin Withstand mental including Cu Coating portion amount voltage No. or Cu oxide Coating material (wt %) (V/mm) 128 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 544 129 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 549 130 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 549 131 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 506 132 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 506 133 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 533 134 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 549 135 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 560 136 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 538 137 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 522 138 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 549 139 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 533 140 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 512 141 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 512 142 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 538 143 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 560 144 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 528 145 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 549 146 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 533 147 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 517 148 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 538 149 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 522 150 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 506 151 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 533 152 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 528 153 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 549 154 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 517 155 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 517 156 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 528 157 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 544 158 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 528 159 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 560 160 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 544 161 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 560 162 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 533 163 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 538 164 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 528 165 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 517 166 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 517 167 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 544 168 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 549 169 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 522 170 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 538 171 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 554
(114) TABLE-US-00008 TABLE 8 Soft magnetic metal powder Soft magnetic metal particle Entire Core portion particle Average Heat treatment conditions Average crystallite Average Oxygen crystallite size (A) Experi- Comparative particle Holding Holding Temperature concen- size of Fe of Cu mental example/ size D50 temperature time raising rate tration crystallites crystallites No. example Composition (at %) (μm) (° C.) (min) (° C./min) (ppm) (nm) (nm) 172 Example Fe86.9Cu0.1P1Si2B9C1 25 450 60 10 400 18.0 5.7 173 Example Fe80.9Cu0.1P1Si8B9C1 25 450 60 10 400 18.0 6.1 174 Example Fe82.9Cu0.1P2Si2B9C4 25 450 60 10 400 19.0 5.2 175 Example Fe76.9Cu0.1P2Si8B9C4 25 450 60 10 400 21.0 5.4 176 Example Fe83.3Si6B10Cu0.7 25 450 60 10 400 25.0 5.5 177 Example Fe83.3Si4B10P2Cu0.7 25 450 60 10 400 23.0 5.5 178 Example Fe83.3Si2B10P4Cu0.7 25 450 60 10 400 18.0 5.0 179 Example Fe83.3B10P6Cu0.7 25 450 60 10 400 18.0 6.4 180 Example Fe83.3Si3B5P8Cu0.7 25 450 60 10 400 18.0 5.1 181 Example Fe83.3Si1B13P2Cu0.7 25 450 60 10 400 18.0 5.5 Soft magnetic metal powder Soft magnetic metal particle First shell portion Largest Average Average crystallite crystallite minor axis Second shell Dust core size (B) size (C) diameter (D) portion Property Experi- of Cu of Cu of Cu layer Resin Withstand mental crystallites crystallites crystallites including Cu Coating portion amount voltage No. (nm) (nm) (nm) C/A B/A or Cu oxide Coating material (wt %) (V/mm) 172 39.3 21.0 15.8 3.7 6.9 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 549 173 41.2 20.9 13.5 3.4 6.7 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 533 174 32.1 21.0 15.0 4.0 6.1 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 549 175 30.8 21.0 15.5 3.9 5.7 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 512 176 42.8 21.1 14.2 3.8 7.8 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 506 177 31.8 21.0 12.1 3.8 5.7 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 544 178 39.3 21.0 15.7 4.2 7.8 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 549 179 34.1 21.1 16.0 3.3 5.3 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 522 180 35.2 21.1 16.4 4.1 6.9 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 538 181 35.3 20.9 15.2 3.8 6.4 Observed P.sub.2O.sub.5—ZnO—R.sub.2O—Al.sub.2O.sub.3 2 517
(115) According to tables 5 to 8, it can be confirmed that even when the composition of the nanocrystal alloy is changed, when B/A is within the above range, the dust core having good withstand voltage is obtained. On the other hand, it can be confirmed that when B/A falls out of the above range, the withstand voltage of the dust core becomes worse. That is, it can be confirmed that the withstand voltage of the dust core can be improved by setting B/A within the above range regardless of the composition of the nanocrystal alloy. In addition, it can be confirmed that in order to make B/A within the above range, preferably, 0.1 atom % or more of Cu is included in the nanocrystal alloy.
REFERENCE SIGNS LIST
(116) TABLE-US-00009 1 coated particle 10 coating portion 2 soft magnetic metal particle 2a core portion 3a Cu crystallite 5 amorphous substance 2b first shell portion 3b Cu crystallite 5 amorphous substance 2c second shell portion