METHOD FOR APPLYING A MATERIAL TO A FIBER COMPOSITE COMPONENT

Abstract

The invention relates to a method for applying a material (30) to a fiber composite component within an application region (13) of the fiber composite component, the fiber composite component being produced from a fiber composite material having a fiber material (11) and a matrix material (12), the method comprising the following steps: —providing at least one monofilament woven fabric (20), in which a plurality of or all threads each consist of a single filament, —arranging the at least one monofilament woven fabric (20) on a fiber preform (10) in the application region (13), which fiber preform is formed from the fiber material (11) of the fiber composite material, —curing, in a common process step, the matrix material (12) of the fiber composite material, which matrix material embeds the fibers material (11) of the fiber preform (10), and a matrix material (12) embedding the monofilament woven fabric (20), thereafter the matrix material (12) of the fiber preform (10) and the matrix material (12) of the monofilament woven fabric (20) being at least partially cured, —tearing off the monofilament woven fabric (20) integrally bonded to the fiber preform (10), and —applying the material (30) in the application region (13) after the monofilament woven fabric (20) has been torn off.

Claims

1. A method for applying a material to a fiber composite component within an application region of the fiber composite component, wherein the fiber composite component is produced from a fiber composite material comprising a fiber material and a matrix material, comprising: providing at least one woven monofilament fabric of threads in which a plurality or all of the threads are in each case composed of an individual filament, arranging the at least one woven monofilament fabric on a fiber preform which is formed of the fiber material of the fiber composite material, in the application region, curing the matrix material in which the fiber material of the fiber preform is embedded, and also a matrix material in which woven monofilament fabric is embedded, in a common process step, and, after the matrix material of the fiber preform and the matrix material of the woven monofilament fabric have been at least partially cured, pulling off the woven monofilament fabric which is connected to the fiber preform in a materially bonded manner, and applying material in the application region after the woven monofilament fabric has been pulled off.

2. The method as claimed in claim 1, wherein the at least one woven monofilament fabric is provided in the form of a plain-weave fabric, twill-weave fabric, atlas-weave fabric, plain-dutch-weave fabric, leno-weave fabric, and/or triaxial woven fabric.

3. The method as claimed in claim 1 wherein the at least one woven monofilament fabric is provided in such a way that weft thread(s) and/or or the warp threads are in each case composed of an individual filament.

4. The method as claimed in claim 1 wherein the at least one woven monofilament fabric is provided in such a way that a sum of all open areas of meshes of the woven monofilament fabric corresponds to at least 30% of a total base area of the woven monofilament fabric.

5. The method as claimed in claim 1 wherein the at least one woven monofilament fabric is provided in such a way that, after the woven monofilament fabric has been pulled off, a sum of all cohesively fractured regions within the application region corresponds to at least 30% of a total area of the application region.

6. The method as claimed in claim 1 the at least one woven monofilament fabric is provided with individual filaments made from polyester, polyethylene, polyethylene terephthalate, polyamide, and/or metal.

7. The method as claimed in claim 1 wherein the matrix material in which the at least one woven monofilament fabric is embedded, is also the matrix material of the fiber composite material in which the matrix material and the fiber material of the fiber preform is also embedded, or wherein the matrix material in which the at least one woven monofilament fabric is embedded, is a different material from the matrix material of the fiber composite material in which the matrix material and the fiber material of the fiber preform is embedded.

8. The method as claimed in claim 1 wherein the fiber material and/or the at least one woven monofilament fabric are/is pre-impregnated with the respective matrix material, or in that the matrix material of the fiber composite material is infused into the fiber material of the fiber preform in an infusion step.

9. The method as claimed in claim 1 wherein an adhesive is applied as material applied in the application region and a structural element is joined to the fiber composite component in an adhesively bonded manner by means of the applied adhesive, and/or in that a coating is applied as material in the application region.

10. The method as claimed in claim 1 wherein the one or more threads of the at least one woven monofilament fabric have a functional coating, wherein, after the pull-off operation, at least a part of a coating substance remains on the fiber composite component and assumes further functions.

11. A method of using a woven monofilament fabric of threads in which a plurality or all of the threads are in each case composed of an individual filament, as a woven pull-off fabric during application of a material to a fiber composite component in accordance with the method as claimed in claim 1.

Description

[0034] The invention is explained in more detail in exemplary fashion with reference to the appended figures, in which:

[0035] FIGS. 1a-1d—show schematic illustrations of the essential method steps of the method according to the invention;

[0036] FIG. 2—shows a schematic illustration of a woven monofilament fabric;

[0037] FIG. 3—shows a schematic macroscopic illustration of a fracture pattern.

[0038] In FIGS. 1a-1d, a possible progression of the method according to the invention for applying a material is illustrated. For example, a fiber preform 10 is initially provided in the first step 1a, said preform at least partially having the subsequent component form of the fiber composite component to be produced. The fiber preform 10 has in this case been formed from a fiber material 11 in that a plurality of layers of fiber materials were laid over one another. In the example of FIG. 1a, a very pronouncedly simplified component form is illustrated. It goes without saying that any desired complex component form can be produced here.

[0039] Furthermore, pre-impregnated fiber materials 11 were used, such that the matrix material 12 in which the fiber material 11 is embedded is contained in the fiber preform 10 already during the production of the fiber preform 10.

[0040] Furthermore, a woven monofilament fabric 20 is provided which likewise already contains a matrix material 21 and thus is likewise pre-impregnated. The woven monofilament fabric 20 has a plurality of woven fabric threads 22 which are configured in the form of individual filaments.

[0041] In the next method step 1b, the woven monofilament fabric 20 is then arranged within an application region 13 of the fiber preform, wherein another material is intended to be applied within the application region 13 at a later stage. However, in step 1b, the woven monofilament fabric 20 is then initially arranged in the application region 13, wherein, in this case, the matrix material 12 of the fiber preform 10 and the matrix material 21 of the woven monofilament fabric 20 come into contact with one another and possibly mix with one another in the boundary region (boundary layer).

[0042] The matrix material 12 of the fiber preform 10 and the matrix material 21 of the woven monofilament fabric 20 are subsequently at least partially cured, and this connects the woven monofilament fabric 20 to the fiber preform 10 or the fiber composite component in a materially bonded manner.

[0043] As shown in FIG. 1c, the woven monofilament fabric 20 is subsequently pulled off perpendicularly with respect to the fiber preform 10 or the fiber composite component, such that the materially bonded connection between the woven monofilament fabric 20 and the fiber composite component or the fiber preform 10 is cohesively fractured within the application region 13. The resulting rough surface 14 within the application region 13 in this case has a high surface energy, wherein the use of a woven monofilament fabric in particular prevents reinforcing fibers of the fiber material 11 of the fiber preform 10 from also being ripped out and damaged.

[0044] The proportion of the cohesively fractured surface within the application region 13 can in this case be set by the open areas or the mesh width of the woven monofilament fabric 20, with it being necessary here to take account of the fact that the woven monofilament fabric 20 as woven pull-off fabric also has to be removed from the fiber preform 10, after having been connected thereto in a materially bonded manner, without said fabric tearing in the process. In step 1d, the actual material 30 is subsequently applied within the application region 13, said application being able to be effected by means of an applicator 31, for example.

[0045] FIG. 2 shows a schematically pronouncedly simplified depiction of a detail of a woven monofilament fabric 20 in which the warp threads 23 and the weft thread(s) 24 are composed of an individual filament. This means that the warp threads 23 and the weft threads 24 are not multifilaments and thus do not have a plurality of filaments per se. It is rather the case that each warp thread 23 or weft thread 24 is composed of an individual filament. In this case, a mesh 25 is delimited by the respective warp thread and weft thread, wherein the open area 26 of a mesh 25 is in this case that region which is geometrically defined by the mesh width and mesh height.

[0046] In this case, the materially bonded connection between the woven monofilament fabric 20 and the fiber preform or the fiber composite component 10 is cohesively fractured within said open area 26, which leads to the desired surface energy.

[0047] FIG. 3 schematically shows the operation for pulling off the woven monofilament fabric 20 from the fiber preform 10. As can be seen, the materially bonded connection is in each case coherently fractured between the individual filaments 22, such that a cohesive surface 14 is produced here.

LIST OF REFERENCE DESIGNATIONS

[0048] 10—Fiber preform [0049] 11—Fiber material [0050] 12—Matrix material [0051] 13—Application region [0052] 14—Cohesively fractured surface [0053] 20—Woven monofilament fabric [0054] 21—Matrix material of the woven monofilament fabric [0055] 22—Woven fabric threads [0056] 23—Warp threads [0057] 24—Weft threads [0058] 25—Meshes [0059] 26—Open areas [0060] 30—Material to be applied [0061] 31—Applicator