Process for the Stabilisation of Hydrosulphite

Abstract

A process for the production of hydrosulphite is described, which provides the mixing of said hydrosulphite with one or more acids chosen among 4-aminobenzoic acid, 4-hydroxybenzoic acid or 4-methylbenzoic acid and with an alkaline salt of oxalic acid. Optionally, a compound is added, chosen among one or more alkaline carbonates and one or more alkaline tripolyphosphates. Advantageously, the components added to hydrosulphite make up a percentage ranging between 0.1 and 20% by weight of the total hydrosulphite. A formulation is also described, containing sodium hydrosulphite and between 0.1 and 20% by weight of a mixture containing: one or more acids chosen among 4-aminobenzoic acid, 4-hydroxybenzoic acid or 4-methylbenzoic acid; an alkaline salt of oxalic acid and possibly one or more alkaline carbonates; one or more alkaline tripolyphosphates.

Claims

1) A process for the stabilisation of hydrosulphite, characterised in that it provides the mixing of said hydrosulphite with one or more acids, chosen among 4-aminobenzoic acid, 4-hydroxybenzoic acid or a 4-alkyl benzoic acid and with an ammonium, alkaline or alkaline-earth salt of oxalic acid.

2) The process as claimed in claim 1, characterised in that a 4-alkyl benzoic acid is employed, chosen among 4-methylbenzoic acid and 4-ethylbenzoic acid.

3) The process as claimed in claim 1, characterised in that the acid used is 4-aminobenzoic acid.

4) The process as claimed in claim 1, characterised in that the ammonium, alkaline or alkaline-earth salts of oxalic acid are chosen from sodium oxalate, potassium oxalate, ammonium oxalate, lithium oxalate, caesium oxalate, calcium oxalate, magnesium oxalate.

5) The process as claimed in claim 1, characterised in that a compound is added, chosen among one or more ammonium or alkaline carbonates and one or more ammonium, alkaline or alkaline-earth tripolyphosphates.

6) The process as claimed in claim 5, characterised in that said ammonium or alkaline carbonates are chosen in the group consisting of lithium carbonate, ammonium carbonate, sodium carbonate, potassium carbonate, caesium carbonate.

7) The process as claimed in claim 5, characterised in that said tripolyphosphates are chosen from the group comprising lithium tripolyphosphate, ammonium tripolyphosphate, sodium tripolyphosphate, potassium tripolyphosphate, caesium tripoly phosphate, calcium tripolyphosphate, magnesium tripolyphosphate.

8) The process as claimed in claim 1, characterised in that the complex of the components added to hydrosulphite makes up a percentage ranging between 0.1 and 20% by weight of the total hydrosulphite.

9) The process as claimed in claim 8, characterised in that the complex of the components added to the hydrosulphite constitutes a percentage ranging between 0.1 and 15% by weight of the total hydrosulphite.

10) The process as claimed in claim 1, characterised in that the mixing of hydrosulphite with said added components occurs under dry conditions, in an industrial mixer.

11) The process as claimed in claim 1, characterised in that the additional components are previously mixed with one another and then they are cold mixed to the already dried hydrosulphite.

12) The process as claimed in claim 1, characterised in that a solution and/or suspension of the additional components in a solvent is prepared, washing the hydrosulphite with said solution and/or suspension and drying the solid product obtained, after suitable filtration.

13) The process as claimed in claim 12, characterised in that said solvent is methanol.

14) A formulation, comprising: sodium hydrosulphite and between 0.1 and 20% by weight of a mixture comprising: one or more acids chosen among 4-aminobenzoic acid, 4-hydroxybenzoic acid or 4-methylbenzoic acid; an ammonium, alkaline or alkaline-earth salt of oxalic acid.

15) The formulation as in claim 14, characterised in that said mixture furthermore comprises: one or more ammonium or alkaline carbonates; one or more ammonium, alkaline or alkaline-earth tripolyphosphates.

Description

[0020] Further features and advantages of the invention will anyhow be more apparent from the following detailed description of a preferred embodiment, given by mere way of non-limiting example and illustrated in the accompanying drawings, wherein:

[0021] FIG. 1 represents the temperature trend, during the execution of the test No. 4: Test method for self-heating substances, paragraph 33.3.1.6 UN manual of a formulation stabilised with only carbonate of an alkaline metal;

[0022] FIG. 2 represents the temperature trend, during the execution of the test No. 4: Test method for self-heating substances, paragraph 33.3.1.6 UN manual, of a formulation stabilised with carbonate of an alkaline metal and with an alkaline salt of benzoic acid; and

[0023] FIGS. 3 and 4 represent the results of tests similar to those of FIGS. 1 and 2, but with formulations according to the present invention.

[0024] As explained above, the problem addressed by the present invention is solved by adding a combination of an acid selected from 4-aminobenzoic acid, 4-hydroxybenzoic acid or 4-alkyl benzoic acid, such as 4-ethylbenzoic acid or 4-methylbenzoic acid with an ammonium or alkaline salt of oxalic acid. Preferably, the acid used is 4-aminobenzoic acid, for cost reasons, but the choice can be improved basing on considerations on costs, availability and conditions of use linked to the particular contingent situation.

[0025] The ammonium or alkaline salts of oxalic acid can be sodium oxalate, potassium oxalate, ammonium oxalate, lithium oxalate, caesium oxalate, while calcium and magnesium are used among the alkaline-earth salts.

[0026] It was found that the use of only one of each of the two components of the stabiliser, in the absence of the other, does not lead to the desired results.

[0027] Advantageously, a compound chosen from one or more ammonium or alkaline carbonates and one or more ammonium, alkaline or alkaline-earth tripolyphosphates can be added to the two components, further improving the stability of the final formulation. Usable alkaline carbonates are chosen from the group consisting of lithium carbonate, ammonium carbonate, sodium carbonate, potassium carbonate, caesium carbonate. Similarly, the tripolyphosphates which can be used according to the present invention are chosen from the group comprising lithium tripolyphosphate, ammonium tripolyphosphate, sodium tripolyphosphate, potassium tripolyphosphate, caesium tripolyphosphate, calcium tripolyphosphate, magnesium tripolyphosphate.

[0028] Preferably, the complex of the components listed above added to the hydrosulphite constitutes a percentage ranging between 0.1 and 20%, more preferably between 0.1 and 15% by weight of the total hydrosulphite: already at 15% the stabilisation is sufficient and a purer final product is maintained.

[0029] The preparation of the stabilised sodium hydrosulphite according to the present invention provides for the steps of mixing, in solid phase with an industrial mixer, the sodium hydrosulphite with an acid selected from 4-aminobenzoic acid, 4-hydroxybenzoic acid or 4-alkyl benzoic acid and an ammonium, alkaline or alkaline-earth salt of oxalic acid, such as sodium oxalate, potassium oxalate, ammonium oxalate, caesium oxalate, lithium oxalate, calcium oxalate, magnesium oxalate, possibly with an ammonium, alkaline or alkaline-earth salt of tripolyphosphate and possibly an ammonium or alkaline carbonate; the complex of the compounds added to the sodium hydrosulphite in the mixer must be not less than 0.1% and not more than 20%, preferably not more than 15% of the weight of the sodium hydrosulphite.

[0030] The mixing of the hydrosulphite with the added components occurs under dry conditions, in an industrial mixer, with a remarkable simplicity of preparation.

[0031] Preferably, the additional components (the stabilisers) are previously mixed with one another and then they are cold mixed to the hydrosulphite, which had preferably already been dried.

[0032] An alternative production process involves preparing a solution and/or suspension of the stabilisers in a suitable solvent—preferably methanol—washing the hydrosulphite with said solution and/or suspension and drying the solid product obtained, after suitable filtration. In this way, the distribution of the stabilisers within the hydrosulphite is more uniform.

[0033] The present invention also relates to a formulation, containing sodium hydrosulphite and between 0.1 and 20% by weight of a mixture containing: one or more acids chosen among 4-aminobenzoic acid, 4-hydroxybenzoic acid or a 4-alkyl benzoic acid, such as 4-ethylbenzoic acid or 4-methylbenzoic acid; an ammonium, alkaline or alkaline-earth salt of oxalic acid.

[0034] Preferably, said mixture furthermore contains: one or more ammonium or alkaline carbonates; one or more ammonium, alkaline or alkaline-earth tripolyphosphates.

[0035] In FIG. 1, curve 1 shows the temperature trend inside an oven within which a sample is arranged, stabilised with just alkaline carbonate, while curve 2 shows the temperature trend of the sample placed in the oven. The sample is placed in a cubic, metal mesh sample holder and the sample temperature is detected at the centre of the sample holder. It should be noted that, while the oven temperature reaches the value of 140 degrees in a time of about an hour, to which it remains stabilised for 22 hours, curve 2 has the same trend for 76 minutes, then a gradual rise begins, then after about 13 hours rises abruptly, reaching in a short time the value of 230° C., and then falling back to the value of 140° C. of the oven. This peak clearly shows the auto-ignition reaction. Basically, the effect of carbonate stabilisation is below expectations, managing to avoid auto-ignition for only 13 hours.

[0036] In FIG. 2, curve 1 shows, as in FIG. 1, the temperature trend inside an oven within which a sample of hydrosulphite is placed, stabilised with an alkali metal carbonate and with the benzoic salt of an alkaline metal, while the curve 3 represents the temperature trend in said hydrosulphite sample placed inside the oven. The sample is placed in a cubic, metal mesh sample holder and the sample temperature is detected at the centre of the sample holder. It should be noted that, while the oven temperature rises in several minutes to about 120° C., to then remain relatively stable for about 25 hours, curve 3 shows a linear temperature rise at the centre of the sample for about 3 hours, to then have a sharp rise up to about 420° C., from where there is a second peak and a fall down to 120° C. of the oven in a time of further about 4-5 hours; note that the two peaks of curve 3 correspond to two peaks of 130-140° C. of the oven temperature, highlighting how the amount of heat produced in the reaction of decomposition sulphur and sulphur combustion is such as to affect also the temperature of a stable and rather important heat source, like the oven. Note, however, that the sample volume in the experiment shown in FIG. 2 is about 64 times the one involved in the experiment of FIG. 1.

[0037] Basically, FIGS. 1 and 2 clearly show how the individual components used in the stabilisation system according to the present invention, do not provide sufficient stability to the sodium hydrosulphite if used singularly.

[0038] In FIGS. 3 and 4, the samples, prepared similarly to how they had been prepared in the previous two situations, but stabilised according to the present invention, are brought respectively to 140° C. and 120° C., with the same volume ratios as the two preceding tests, and substantially maintain the same oven temperature for at least 48 hours, with only a very slight rise at the beginning (about 4° C.), in the case of the test at 120° C. (curve 4), wherein the volume, and consequently the mass, of product is higher. This means that, substantially, the temperature at the centre of the sample is determined for the whole range of temperature of the oven and not by reactions that take place on the sample or in the sample. This is a clear indication of stability. Even the slight peak of curve 4 (less than 10° C.) seems due more to phenomena of thermal inertia (note that the temperature rise is slower than that of the oven), due to a delay in heat transfer, rather than to reactions, even in minimal quantities, of the hydrosulphite. The curves shown in FIGS. 3 and 4 can be obtained with different compositions according to the present invention. Some exemplary compositions are shown below (the percentages are intended by weight): 1) Sodium metabisulphite 4%-7%, Sodium carbonate 1%-2%, 4-amino benzoic acid 0.25%-1%, Sodium oxalate 0.25%-1%, Sodium hydrosulphite as required to 100%; 2) Sodium metabisulphite 4%-7%, Sodium tripoliphosphate 1%-2%, 4-amino benzoic acid 0.25%-1%, Sodium oxalate 0.25%-1%, Sodium hydrosulphite as required to 100%; 3) Sodium metabisulphite 4%-7%, Sodium tripoliphosphate 1%-2%, Sodium carbonate 1%-2%, 4-amino benzoic acid 0.25%-1%, Sodium oxalate 0.25%-1%, Sodium hydrosulphite as required to 100%; 4) Sodium metabisulphite 4%-7%, Sodium tripoliphosphate 1%-5%, 4-amino benzoic acid 0.25%-1%, Sodium oxalate 0.25%-1%, Sodium hydrosulphite as required to 100%; 5) Sodium metabisulphite 4%-7%, Sodium tripoliphosphate 5%, Sodium carbonate 0.5%-1%, 4-amino benzoic acid 0.25%-1%, Sodium oxalate 0.25%-1%, Sodium hydrosulphite as required at 100%. Of course, other compositions according to the present invention, different then the ones just described, also give similar results.

[0039] The experiments summarised in the attached figures clearly show the efficacy in the stabilisation of the hydrosulphite. The combination of the materials used according to the invention almost completely avoids the auto-ignition and heating of the hydrosulphite, as well as probably its decomposition to sulphur. In this way, the transport of hydrosulphite can take place in a quiet manner, without requiring special safety measures, normally linked to the transport of this substance. Since the additions of foreign substances are minimal compared to the total mass of hydrosulphite, there are no substantial interferences of reactivity in the vast majority of the uses of this substance.

[0040] The experiments just described refer to the decomposition of hydrosulphite in the barrels in which it is stored.

[0041] Other experiments have been carried out with regard to the decomposition and combustion of sulphur in the presence of water, a reaction for which codified tests did not exist so far.

[0042] A hydrosulphite sample is placed in a Dewar flask with an internal diameter of 90 mm and a height of 350 mm. A PT100 thermocouple is immersed within the sample, in stainless steel, suitable for detecting temperatures up to about 500° C., wrapped in a steel sheath. A Eurotherm Chessel 5000 Series recorder records the temperature trend over time. In a first step, the quantity of sample introduced into the Dewar is 250 g, deposited on the bottom of the Dewar. Subsequently, a quantity of water ranging between 3 and 10% is added, making it percolate on the steel sheath that protects the thermocouple. 250 g of product are added and the Dewar is closed.

[0043] The temperature trend includes three phases: one of hydration, during which the reactions are assumed:

Na.sub.2S.sub.2O.sub.4+2H.sub.2O<=>Na.sub.2S.sub.2O.sub.4.2H.sub.2O

Na.sub.2S.sub.2O.sub.4.2H.sub.2O---->NaHSO.sub.3+½Na.sub.2S.sub.2O.sub.3+3/2H.sub.2O

Na.sub.2S.sub.2O.sub.4+H.sub.2+½O.sub.2->2NaHSO.sub.3

Na.sub.2S.sub.2O.sub.5+H.sub.2O->2NaHSO.sub.3,

a second decomposition step and a third decomposition and combustion step. Besides the decomposition due to water, a radical type decomposition is assumed, according to the reactions:

2Na.sub.2S.sub.2O.sub.4+4NaHSO.sub.3->4Na.sub.2SO.sub.3+3SO.sub.2+S+2H.sub.2O

2NaHSO.sub.3->Na.sub.2SO.sub.3+H.sub.2O+SO.sub.2

SO.sub.2+2Na.sub.2S.sub.2O.sub.3->2Na.sub.2SO.sub.4+3S

such mechanism being due to the increase in temperature (up to 110-130° C.) due to decomposition. The third step, after a further increase in temperature due to radical reactions, starts at around 200° C.

[0044] In the absence of a stabiliser, the temperature of the hydrosulphite rises rapidly and the third step is immediately reached. In the case of stabilised product (for example with one of the above listed five mixtures), the temporal duration of the first two steps increases considerably, so that the sulphur ignition temperature is never reached or reached only after very long times. It should be considered that, while in all experiments without stabilisation the temperature reached at least 120-150° C. in a maximum of two hours (with peaks of 250° C.), once stabilisation had been carried out the temperature never exceeded 40° C. for at least 24 hours: under these conditions, it is also possible to intervene to remove the causes of decomposition, before problems occur.

[0045] It is clear that the present invention overcomes all the problems encountered with the hydrosulphite formulations used so far, allowing their transport and storage under normal conditions, without the need for particular precautions, burdensome for those who must implement them and, in any case, never able to completely eliminate all risks.

[0046] In particular, the present invention allows to pass the verification No. 4 of paragraph 33.3.1.6 of the UN manual, so as to exempt the transport from the ADR/IMDG standards for transport in packages up to 3 m.sup.3, without introducing new phases of risk and new pictograms (in addition to that of irritant-harmful, already present today), with an ecological impact not higher than that of hydrosulphite alone. The stabiliser additions, according to the present invention, allow to maintain a titre greater than 80% of active ingredient and the stability of the titre has duration and value comparable with those of the prior art.

[0047] It is understood, however, that the invention is not to be considered as limited by the particular arrangement illustrated above, which represents only an exemplary embodiment of the same, but different variants are possible, all within the reach of a person skilled in the art, without departing from the scope of the invention itself, as defined by the following claims.