Ni-based alloy, gas turbine material, and method for manufacturing Ni-based alloy

Abstract

The purpose of the present invention is to enhance the creep characteristics of an Ni-based alloy. The present invention relates to a Ni-based alloy characterized by having a composition containing, in terms of wt %, 15.00-25.00% Cr, 5.00-15.00% Co, 1.00% to less than 12.00% Mo, 1.50-2.50% Ti, 1.00-2.00% Al, 0.20-1.00% Nb, and 0.0010-0.10% C, and in terms of mass ppm, 10-200 ppm P, 30-250 ppm B, and 30-200 ppm N, the remainder comprising Ni and unavoidable impurities.

Claims

1. A Ni-based alloy having a composition consisting of: in terms of % by mass, Cr: 15.00 to 25.00%; Co: 8.00 to 15.00%; Mo: 1.00% or more and less than 12.00%; Ti: 1.50 to 2.50%; Al: 1.00 to 2.00%; Nb: 0.20 to 1.00%; and C: 0.0010 to 0.10%; and in terms of ppm by mass, P: 10 to 200 ppm; B: 30 to 250 ppm; and N: 30 to 200 ppm, with the balance being Ni and unavoidable impurities, wherein the grain boundary coverage defined by the ratio of the length of grain boundaries covered with carbides to the length of grain boundaries in the alloy is 85% or more.

2. The Ni-based alloy according to claim 1, wherein the content of P is P: 20 to 150 ppm by mass.

3. The Ni-based alloy according to claim 1, wherein grain boundaries are strengthened with precipitated carbides.

4. The Ni-based alloy according to claim 1, wherein the creep rupture time at 750° C. and 333 MPa is 600 hours or more.

5. The Ni-based alloy according to claim 1, wherein the minimum creep rate at 750° C. and 333 MPa is 1.5×10.sup.−5h.sup.−1 or less.

6. A gas turbine material comprising the Ni-based alloy according to claim 1.

7. The Ni-based alloy according to claim 1, wherein the content of Ti is Ti: 1.80 to 2.50%.

8. The Ni-based alloy according to claim 1, wherein the content of Al is Al: 1.00 to 1.70%.

9. A method for manufacturing a Ni-based alloy, comprising: subjecting a Ni-based alloy to a solution treatment, the Ni-based alloy having a composition consisting of, in terms of % by mass, Cr: 15.00 to 25.00%, Co: 8.00 to 15.00%, Mo: 1.00% or more and less than 12.00%, Ti: 1.50 to 2.50%, Al: 1.00 to 2.00%, Nb: 0.20 to 1.00%, and C: 0.0010 to 0.10% and, in terms of ppm by mass, P: 10 to 200 ppm, B: 30 to 250 ppm, and N: 30 to 200 ppm, with the remainder being Ni and unavoidable impurities; and subsequently subjecting the Ni-based alloy to a first aging treatment at a temperature of 1010 to 1050° C. and then a second aging treatment at a temperature of 760 to 790° C., wherein the grain boundary coverage defined by the ratio of the length of grain boundaries covered with carbides to the length of grain boundaries in the alloy is 85% or more.

Description

BRIEF DESCRIPTION OF DRAWINGS

(1) FIG. 1 is a graph showing a relationship between the creep rupture time and the P content of the Ni-based alloys of Examples and Comparative Examples.

(2) FIG. 2 is a graph showing a relationship between the minimum creep rate and the P content of the Ni-based alloys of Examples and Comparative Examples.

(3) FIG. 3 is an FE-SEM image in the vicinity of grain boundaries of the Ni-based alloys of Examples and Comparative Example.

(4) FIG. 4 is a graph showing a relationship between the grain boundary coverage and the P content of the Ni-based alloys of Examples and Comparative Example.

(5) FIG. 5 is a graph showing a relationship among the grain boundary coverage, the creep rupture time, and the minimum creep rate of the Ni-based alloys of Examples and Comparative Example.

DESCRIPTION OF EMBODIMENTS

(6) Hereinafter, an embodiment of the present invention will be described. The present invention is not limited to the embodiment described below.

(7) The Ni-based alloy of the present invention may have a composition comprising, in terms of % by mass or ppm by mass, Cr: 19 to 21%, Co: 9 to 11%, Mo: 1 to 10%, Ti: 1.8 to 2.2%, Al: 1.1 to 1.5%, Nb: 0.3 to 0.7%, C: 0.04 to 0.08%, P: 30 to 140 ppm, B: 30 to 70 ppm, and N: 40 to 80 ppm, the balance being Ni and unavoidable impurities.

(8) The following will explain the action and limitation reasons of the technical matters defined in the present invention. Among the alloy compositions, the contents of P, B, and N are shown in terms of ppm by mass, and the contents of the other elements are shown in terms of % by mass. Further, ppm by mass and % by mass have the same meanings as ppm by weight and % by weight, respectively, and “ . . . to . . . ” means that it is not less than the lower limit value and not more than the upper limit value.

(9) Cr: 15.00 to 25.00%

(10) Cr is an element necessary for enhancing oxidation resistance, corrosion resistance, and strength. Also, it combines with C to form a carbide, thereby enhancing high-temperature strength. However, too large content thereof invites destabilization of the matrix and promotes the formation of harmful TCP phases such as a σ phase and α-Cr, resulting in adverse influences on ductility and toughness. Therefore, the content of Cr is limited to 15.00 to 25.00%.

(11) For the same reason, it is preferable to control the lower limit of the Cr content to 18.00% or more and the upper limit to 22.00% or less.

(12) Co: 5.00 to 15.00%

(13) Co is an element that improves the segregation property of the alloy by bringing the distribution coefficients of alloying elements such as Al, Ti, Nb, and W close to 1. When the content of Co is less than 5.00%, the above effect cannot be obtained sufficiently. When it exceeds 15.00%, not only forgeability is deteriorated but also a Laves phase is easily generated, and hence the matrix structure at high temperature is rather destabilized and also high-temperature structural stability is deteriorated. Therefore, the content of Co is limited to the range of 5.00 to 15.00%.

(14) For the same reason, it is preferable to control the lower limit of the Co content to 8.00% or more and the upper limit to 12.00% or less.

(15) Mo: 1.00% or More and Less Than 12.00%

(16) Mo mainly solves in the matrix to strengthen it, and also solves in the γ′ phase to replace an Al site of the phase, thereby enhancing the stability of the phase. Thus, Mo is effective in enhancing both high-temperature strength and structural stability. When the Mo content is less than 1.0%, the above effects are insufficient, and when it is 12.00% or more, a Laves phase is easily generated, so that the matrix structure at high temperature is rather destabilized and also the high-temperature structural stability is deteriorated. Therefore, the content of Mo is limited to the range of 1.0% or more and less than 12.00%.

(17) For the same reason, it is preferable to control the lower limit of the Mo content to 5.00% or more and the upper limit to 10.00% or less.

(18) Ti: 1.50 to 2.50%

(19) Ti mainly forms a MC carbide to suppress crystal grain coarsening of the alloy and also combines with Ni to precipitate a γ′ phase, thereby contributing to precipitation strengthening of the alloy. However, when Ti is exceedingly contained, the stability of the γ′ phase at high temperature is lowered and an η phase is formed, thereby impairing strength, ductility, toughness, and high-temperature long-term structural stability. Therefore, the content of Ti is limited to the range of 1.50 to 2.50%.

(20) For the same reason, it is preferable to control the lower limit of the Ti content to 1.80% or more and the upper limit to 2.20% or less.

(21) Al: 1.00 to 2.00%

(22) Al combines with Ni to precipitate a γ′ phase, thereby contributing to precipitation strengthening of the alloy. However, when the content thereof is too large, the γ′ phase aggregates at grain boundaries and is coarsened, thereby remarkably impairing mechanical properties at high temperature and also lowering hot workability. Therefore, the Al content is limited to 1.00 to 2.00%.

(23) For the same reason, it is preferable to control the lower limit of the Al content to 1.30% or more and the upper limit to 1.70% or less.

(24) Nb: 0.20 to 1.00%

(25) Nb is an element that stabilizes the γ′ phase and contributes to strength enhancement, however, when Nb is exceedingly contained, the precipitation of the η phase, the σ phase, and the Laves phase that are harmful phases is promoted, thereby remarkably lowering the structural stability. Therefore, the content of Nb is limited to 0.20 to 1.00%. For the same reason, it is preferable to control the lower limit thereof to 0.30% or more and the upper limit to 0.70% or less.

(26) P: 10 to 200 ppm

(27) The present inventors have found that P has an effect of suppressing intra-grain precipitation of carbides and increasing grain boundary carbides during holding and cooling in the solution treatment and the first-stage aging. Specifically, in order to obtain effects of precipitating the grain boundary carbides and reducing the minimum creep rate, it has been found that grain boundary coverage defined by the ratio of the length of grain boundaries covered with carbides to the length of grain boundaries in the alloy (hereinafter, also simply referred to as “grain boundary coverage”) should be 85% or more, and for that purpose, a P content of 10 ppm or more is necessary. However, when P is excessively contained, there is a possibility that grain boundary segregation of P becomes excessive to lower the consistency of the grain boundaries, and ductility reduction and the like are brought about. Therefore, the upper limit of the P content is limited to 200 ppm.

(28) For the same reason, it is preferable to control the lower limit of the P content to 20 ppm or more and the upper limit to 150 ppm or less.

(29) C: 0.0010 to 0.10%

(30) C is an additive element that forms carbides to suppress crystal grain coarsening of an alloy and precipitates at the grain boundaries to improve high-temperature strength but, since a sufficient effect for improving the strength is not exhibited when the content is small, it is necessary to contain C in an amount of at least 0.0010% or more. However, when the content is too large, there is a concern of adverse effects such as reduction of the amount of the other effective precipitates such as the γ′ phase owing to excessive carbide formation, so that the upper limit is controlled to 0.10%. For the same reason, it is preferable to control the lower limit to 0.010% or more and the upper limit to 0.070% or less.

(31) B: 30 to 250 ppm

(32) B segregates at the grain boundaries and contributes to high-temperature properties, so that it is contained as desired. However, when B is excessively contained, a boride is prone to be formed, which contrarily invites grain boundary embrittlement. Therefore, the content of B to be contained as desired is controlled to 250 ppm or less. In order to obtain the above effect sufficiently, B is desirably contained in an amount of 30 ppm or more and, for the same reason as described above, it is preferable to control the lower limit to 40 ppm or more and the upper limit to 200 ppm or less.

(33) N: 30 to 200 ppm

(34) N is considered to form nitrides at grain boundaries to improve creep strength, but when the content is small, a sufficient effect cannot be obtained, and thus a content of 30 ppm or more is necessary. However, when the content is too large, excess nitrides are formed to invite ductility reduction, so that the upper limit is controlled to 200 ppm. For the same reason, it is preferable to control the lower limit to 40 ppm or more and the upper limit to 150 ppm or less.

(35) Ni and Unavoidable Impurities: Remainder

(36) The remainder of the Ni-based alloy of the present invention is Ni and unavoidable impurities.

(37) The contents thereof are not particularly limited, but Ni is usually contained in an amount of 55 to 65%. Moreover, the content is preferably 58% by mass or more, and 62% by mass or less.

(38) In addition, the unavoidable impurities are not particularly limited but, for example, S may be contained in an amount of 40 ppm or less.

(39) The contents of the ingredients contained in the Ni-based alloy of the present invention described above can be measured, for example, by fluorescent X-ray and the like.

(40) In the Ni-based alloy of the present invention, the creep rupture time at 750° C. and 333 MPa is preferably 600 hours or more. Further, the minimum creep rate at 750° C. and 333 MPa is preferably 1.5×10.sup.−5h.sup.−1 or less. In addition, the grain boundary coverage is preferably 85% or more.

(41) By satisfying the above numerical values, very excellent creep properties are exhibited.

(42) The method for manufacturing a Ni-based alloy of the present invention is not particularly limited, and for example, it can be smelted by a usual method.

(43) Further, by subjecting the smelted Ni-based alloy to a solution treatment and an aging treatment, a grain boundary strengthened Ni-based alloy can be obtained.

(44) Although the solution treatment varies depending on the composition of the alloy to be treated, the treatment can be performed, for example, under conditions of 1080 to 1100° C. for 5 to 8 hours. Under these conditions, the crystal grains are not coarsened, and become regulated fine grains having a crystal grain size according to JIS 60551: 2013 of about 5.

(45) The aging treatment is preferably performed in two stages. The first-stage aging treatment is preferably performed at a temperature of 1010 to 1050° C. for 20 to 24 hours. Under such conditions, the γ′ phase sufficiently grows and the strength is further improved. The second stage aging treatment is preferably performed at a temperature of 760 to 790° C. for 8 to 12 hours. Under such conditions, since the amount of precipitated M.sub.23C.sub.6-type carbides and the diameter of MC-type carbides fall within appropriate ranges, high-temperature ductility becomes good.

(46) Moreover, after the first-stage aging, it is preferable to air-cool the alloy to a cold material once, and then to raise the temperature to the second-stage aging temperature.

(47) In addition, processing such as forging can be further performed on the Ni-based alloy of the present invention as desired. The conditions in the processing are not particularly limited.

(48) The Ni-based alloy manufactured by performing the solution treatment and the aging treatment under the above-described preferable conditions is grain boundary strengthened with precipitated carbides, and the grain boundary coverage is 85% or more.

(49) Also, the alloy has properties that the creep rupture time at 750° C. and 333 MPa is 600 hours or more and the minimum creep rate at 750° C. and 333 MPa is 1.5×10.sup.−5h.sup.−1 or less, and is excellent in creep properties.

(50) By applying the Ni-based alloy of the present invention as a component (gas turbine material) of high-temperature equipment such as a gas turbine, it is expected that life extension and reliability improvement of the equipment can be achieved.

EXAMPLES

(51) Examples of the present invention will be described below based on Figures and Tables, but the present invention is not limited thereto.

(52) A 50 kg round ingot obtained by smelting the alloy having a composition shown in Table 1 by a vacuum induction melting method was forged in a forging ratio of 3.0 to obtain a forged plate.

(53) In the compositions shown in Table 1, P, B, and N are shown in terms of ppm by mass, and the other ingredients are shown in terms of % by mass. Further, “Bal.” In Table 1 means the remainder. Incidentally, in addition to the ingredients described in Table 1, unavoidable impurities may be contained.

(54) TABLE-US-00001 TABLE 1 C P Ni Cr Co Mo Ti Al Nb B N Comparative 0.056 8 Bal. 19.77 10.11 8.52 2.09 1.53 0.46 48 60 Example Example 1 0.054 32 Bal. 19.80 10.04 8.46 2.11 1.52 0.49 57 62 Example 2 0.060 100 Bal. 19.80 10.14 8.45 2.11 1.53 0.51 49 66 Example 3 0.057 140 Bal. 19.79 10.15 8.45 2.11 1.54 0.45 49 59

(55) The obtained forged plate was cut into an appropriate size and subjected to a solution treatment at 1100° C.×5 hours and two-step aging at 1050° C.×24 hours and 790° C.×8 hours to obtain a test material.

(56) Subsequently, the test material was machined to obtain a creep test specimen to be used in the evaluation of creep properties described below.

(57) The creep properties were evaluated by performing a creep plate test in accordance with JIS Z2271: 2013. The test temperature was controlled to 750° C., and the test stress was controlled to 333 MPa. The minimum creep rate and the rupture time were determined from the obtained creep rate-time curve.

(58) For each test material, using a field emission-type scanning electron microscope (FE-SEM), an FE-SEM image of about 10 fields of view was taken at a magnification of 3000, the ratio of the grain boundary length covered with precipitates to the whole grain boundary length within each field of view was determined, and the ratios were averaged to obtain grain boundary coverage.

(59) Table 2 shows the grain boundary coverage, creep rupture time, and minimum creep rate of each test material.

(60) FIG. 1 and FIG. 2 show P content dependency of the creep rupture time and the minimum creep rate, respectively. From the figures, it is found that the creep rupture time is longer and the minimum creep rate is smaller in Examples 1 to 3 than in Comparative Example.

(61) FIG. 3 shows an SEM image in the vicinity of grain boundaries of each example observed by FE-SEM. In all examples, carbides were observed at the grain boundaries.

(62) FIG. 4 shows a relationship between the P content and the grain boundary coverage. The grain boundary coverage increased as the P content increased, and became constant at about 88% regardless of the P content after the P content showed a maximum value of about 96% at 32 ppm.

(63) FIG. 5 shows a relationship among the grain boundary coverage, the minimum creep rate, and the creep rupture time. There was observed a good correlation among the grain boundary coverage, the minimum creep rate, and creep rupture time, and it was found that, at a grain boundary coverage of 85% or more, creep properties of a creep rupture time of 600 hours or more and a minimum creep rate of 1.5×10.sup.−5h.sup.−1 or less were obtained.

(64) TABLE-US-00002 TABLE 2 Grain boundary Creep rupture Minimum creep coverage (%) time (h) rate (h.sup.−1) Comparative 65.7 468.3 2.1 × 10.sup.−5 Example Example 1 96.2 732.7 7.1 × 10.sup.−6 Example 2 88.8 660.1 1.3 × 10.sup.−5 Example 3 88.4 615.2 1.1 × 10.sup.−5

(65) While the present invention has been described in detail and with reference to specific embodiments thereof, it will be apparent to one skilled in the art that various changes and modifications can be made therein without departing from the spirit and scope thereof. The present application is based on Japanese Patent Application No. 2017-027525 filed on Feb. 17, 2017, and the contents are incorporated herein by reference. Also, all the references cited herein are incorporated as a whole.