METHOD AND APPARATUS FOR MANUFACTURING SMC

Abstract

Disclosed is a method of and an apparatus for manufacturing a sheet molding compound (SMC), the method including: continuously supplying a bottom film; applying a bottom resin on the bottom film; continuously supplying a carbon fiber; spreading the carbon fiber for widening; cutting the carbon fiber into a predetermined length and distributing the cut carbon fiber on the bottom resin; continuously supplying a top film; applying a top resin on a lower surface of the top film; and laminating the bottom film and the top film such that the carbon fiber is impregnated with the resin. According to the present invention, a large tow carbon fiber is widened by spreading to improve resin impregnability, thereby being capable of manufacturing a high quality SMC having improved physical properties with low cost.

Claims

1. An apparatus for manufacturing an SMC, the apparatus comprising: a bottom film supplying portion (10) provided with a film roll and unwinding a bottom film wound on the film roll for supply thereof; a first slot die (20a) applying a bottom resin on the bottom film supplied from the bottom film supplying portion (10); a carbon fiber supplying portion (30) provided with a creel and unwinding a large tow carbon fiber wound on the creel for supply thereof; a spreading portion (40) spreading the large tow carbon fiber supplied from the carbon fiber supplying portion (30) for widening; a cutting portion (50) cutting the supplied spread carbon fiber into a predetermined length and distributing the cut carbon fiber on the bottom resin; a top film supplying portion (60) provided with a film roll and unwinding a top film wound on the film roll for supply thereof; a second slot die (20b) applying a top resin on the top film supplied from the top film supplying portion (60); and a film laminating portion (70) pressing the top film supplied upside down and the bottom film with a predetermined pressure to laminate.

2. The apparatus of claim 1, wherein the cutting portion (50) is provided with a first cutter (50a) and a second cutter (50b), which are disposed to be spaced apart from each other by a predetermined distance, and the apparatus further includes: a third slot die (20c) disposed between the first cutter (50a) and the second cutter (50b), and applying an intermediate resin on the carbon fiber, which is cut in a predetermined length by the first cutter (50a) and distributed on the bottom resin.

3. The apparatus of claim 1, further comprising: a dividing portion (80) dividing the large tow carbon fiber widely spread by the spreading portion (40) into multiple strands of small tow carbon fiber along the longitudinal direction of the fiber.

4. The apparatus of claim 1, further comprising: a reinforcing fabric supplying portion (90) provided with a fiber roll and unwinding the reinforcing fabric wound on the fiber roll and continuously supplying on the bottom resin applied on the bottom film to stack thereon.

5. The apparatus of claim 4, wherein the reinforcing fabric supplying portion (90) is provided in plural, the multiple reinforcing fabric supplying portions (90) disposed to be spaced apart from each other by predetermined intervals and supplying different types of reinforcing fabrics at the same time from each of the reinforcing fabric supplying portions (90), and the cutting portion (50) distributing the cut carbon fiber and a slot die for applying a resin are disposed between the multiple reinforcing fabric supplying portions (90).

6. The apparatus of claim 4, wherein the reinforcing fabric is any one among unidirectional (UD) carbon fabric, non-crimp fabric (NCF), carbon fabric, glass fabric, and aramid fabric.

7. The apparatus of claim 5, wherein the reinforcing fabric is any one among unidirectional (UD) carbon fabric, non-crimp fabric (NCF), carbon fabric, glass fabric, and aramid fabric.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0048] The above and other objects, features and other advantages of the present invention will be more clearly understood from the following detailed description when taken in conjunction with the accompanying drawings, in which:

[0049] FIG. 1 is an exemplary diagram showing a configuration of an apparatus for manufacturing sheet molding compound (SMC) of the related art;

[0050] FIG. 2 is a block diagram showing a manufacturing process according to an embodiment of a method of manufacturing an SMC of the present invention;

[0051] FIG. 3 is a diagram showing a configuration of an apparatus for manufacturing an SMC according to an embodiment of the present invention;

[0052] FIG. 4 is a side cross-sectional view showing a first slot die of the apparatus for manufacturing the SMC according to the embodiment of the present invention;

[0053] FIG. 5 is an exemplary plan view showing a spreading portion of the apparatus for manufacturing the SMC according to the embodiment of the present invention;

[0054] FIG. 6 is a side cross-sectional view showing a cutting portion of the apparatus for manufacturing the SMC according to the embodiment of the present invention;

[0055] FIG. 7 is a side cross-sectional view showing an SMC manufactured by the apparatus for manufacturing the SMC according to the embodiment of the present invention;

[0056] FIG. 8 is a diagram showing a configuration of an apparatus for manufacturing an SMC according to a second embodiment of the present invention;

[0057] FIG. 9 is a side cross-sectional view showing an SMC manufactured by the apparatus for manufacturing the SMC according to the second embodiment of the present invention;

[0058] FIG. 10 is a block diagram showing a manufacturing process according to a third embodiment of a method of manufacturing an SMC of the present invention;

[0059] FIG. 11 is a diagram showing a configuration of an apparatus for manufacturing an SMC according to the third embodiment of the present invention;

[0060] FIG. 12 is an exemplary plan view showing a dividing portion of the apparatus for manufacturing the SMC according to the third embodiment of the present invention;

[0061] FIG. 13 is a block diagram showing a manufacturing process according to a forth embodiment of a method of manufacturing an SMC of the present invention;

[0062] FIG. 14 is a diagram showing a configuration of an apparatus for manufacturing an SMC according to the forth embodiment of the present invention; and

[0063] FIGS. 15A and 15B are side cross-sectional views showing SMCs manufactured by the apparatus for manufacturing the SMC according to the fourth embodiment of the present invention.

DETAILED DESCRIPTION OF THE INVENTION

[0064] Hereinbelow, a method of and an apparatus for manufacturing a sheet molding compound (SMC) according to the present invention will be described in detail. The present invention may be embodied in many different forms and should not be construed as being limited to only the embodiments set forth herein, but should be construed as covering modifications, equivalents, or alternatives falling within ideas and technical scope of the present invention.

[0065] Throughout the drawings, the same reference numerals will refer to the same or like parts. Although the terms “first”, “second”, etc. may be used herein to describe various elements, these elements should not be limited by these terms. These terms are only used to distinguish one element from another element regardless of the importance, sequence, or order of the elements. For instance, a first element discussed below could be termed a second element without departing from the teachings of the present invention. Similarly, the second element could also be termed the first element.

[0066] The terminology used herein is for the purpose of describing particular embodiments only and is not intended to be limiting. As used herein, the singular forms “a”, “an”, and “the” are intended to include the plural forms as well, unless the context clearly indicates otherwise.

[0067] Unless otherwise defined, all terms including technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this invention belongs. It will be further understood that terms, such as those defined in commonly used dictionaries, should be interpreted as having a meaning that is consistent with their meaning in the context of the relevant art and the present disclosure, and will not be interpreted in an idealized or overly formal sense unless expressly so defined herein.

[0068] FIG. 2 is a block diagram showing a manufacturing process according to an embodiment of a method of manufacturing an SMC of the present invention; and FIG. 3 is a diagram showing a configuration of an apparatus for manufacturing an SMC according to an embodiment of the present invention.

[0069] A detailed description will be described with reference to FIGS. 2 and 3.

[0070] The method of manufacturing the SMC of the present invention includes supplying a bottom film (S10), applying a bottom resin (S20), supplying a carbon fiber (S30), spreading the carbon fiber (S40), cutting and distributing the carbon fiber (S50), supplying a top film (S60), applying a top resin (S70), and laminating the films (S80).

[0071] At the supplying of the bottom film (S10), the bottom film wound on a film roll is unwound therefrom and supplied continuously.

[0072] At the applying of the bottom resin (S20), the bottom resin is applied on a surface of the bottom film, which is continuously supplied at the supplying of the bottom film (S10). Here, using a slot die is preferable to apply the bottom resin.

[0073] Accordingly, the surface of the bottom film passing the slot die is provided with the bottom resin applied thereon in a predetermined thickness.

[0074] At the supplying of the carbon fiber (S30), a large tow carbon fiber wound on a fiber bobbin is unwound therefrom and supplied continuously.

[0075] At the spreading of the carbon fiber (S40), the large tow carbon fiber continuously supplied at the supplying of the carbon fiber (S30) is spread to increase the width thereof. Here, it is preferable to use a spreading machine provided with multiple spreading rollers 401 to widen the large tow carbon fiber.

[0076] Processes for the carbon fiber at the supplying of the carbon fiber (S30) and at the spreading of the carbon fiber (S40) are performed on a carbon fiber line which is separate from a film transport line on which processes for the film at the supplying of the bottom film (S10) and at the applying of the bottom resin (S20) are performed. Afterward, the carbon fiber is supplied to the film transport line.

[0077] At the cutting and distributing of the carbon fiber (S50), the widened carbon fiber and continuously supplied at the spreading of the carbon fiber (S40) is cut into a predetermined length while distributed on the bottom resin applied on the bottom film. Here, it is preferable to use a cutter provided with a cutting roller 502 to cut the carbon fiber.

[0078] Accordingly, the carbon fiber is evenly distributed by free fall on the bottom resin applied on the bottom film whereby the resin impregnability is improved.

[0079] At the cutting and distributing of the carbon fiber (S50), the large tow carbon fiber, widened at the spreading of the carbon fiber (S40), may be supplied to multiple cutting portions 50, which are provided to be spaced apart from each other, to be distributed at positions spaced apart from each other by a predetermined distance on the bottom resin.

[0080] Here, the multiple cutting portions 50 are provided at the predetermined distance along a transport direction of the bottom film.

[0081] Referring to FIG. 8 is desirable for helping with understanding the above embodiment.

[0082] Then, it is preferable that an intermediate resin F is applied to be placed between the carbon fibers by using a slot die, the carbon fibers distributed from the multiple cutting portions 50 provided to be spaced from each other at the predetermined distance. Accordingly, the slot die is preferably provided between the multiple cutting portions 50.

[0083] That is, during the transport process of the bottom film in a constant speed, in the case that the multiple cutting portions 50 provided to be spaced from each other distribute the carbon fiber at the positions spaced apart from each other by the predetermined distance on the bottom resin, a front multiple cutting portion 50 of the multiple cutting portions 50 distributes the carbon fiber and then the intermediate resin F discharged from the slot die is applied on the carbon fiber distributed on the bottom resin.

[0084] Then, the carbon fiber discharged from a rear cutting portion of the multiple cutting portions 50 is distributed on the intermediate resin F.

[0085] Thus, when the bottom film and the top film are laminated by a film laminating portion 70, the carbon fibers are disposed between the bottom resin applied on the bottom film and the top resin applied on a lower surface of the top film and the intermediate resin F.

[0086] Accordingly, the pressure applied by the film laminating portion 70 causes the bottom resin, the top resin, and the intermediate resin F to penetrate between filaments of the carbon fibers from the upper, middle, and lower portions of the carbon fibers. Thus, the resin impregnability is greatly improved whereby bubble generation is suppressed in the resin impregnation process, and bubbles that are possibly generated in the resin itself are removed by the pressure applied by the film laminating portion 70, thereby minimizing defects in molding SMC products and improving the physical properties thereof. Meanwhile, at the supplying of the top film (S60), the top film wound on a film roll is unwound therefrom and supplied continuously.

[0087] At the applying of the top resin (S70), the top resin is applied on the lower surface of the top film, which is continuously supplied at the supplying of the top film (S60). Here, using a slot die is preferable to apply the top resin.

[0088] Accordingly, the lower surface of the top film passing the slot die is provided with the top resin applied thereon in a predetermined thickness.

[0089] At the laminating of the films (S80), the top film is stacked on the bottom film, the top film supplied upside down to cover the top resin on the carbon fiber distributed on the bottom resin. Then, the bottom film and the top film pass between laminating rollers 701, which are arranged up and down respectively, at the same time such that the bottom film and the top film are pressurized laminating rollers 701 to laminate.

[0090] At this point, the pressure applied by the laminating rollers 701 causes the bottom resin and the top resin to penetrate between the filaments of the carbon fiber from the upper and lower portions of the carbon fiber such that the impregnation of the resin is performed.

[0091] The method of manufacturing the SMC of the present invention may further include dividing the carbon fiber (S90).

[0092] Referring to FIGS. 10 and 11 is desirable for helping with understanding the embodiment.

[0093] At the dividing of the carbon fiber (S90), the large tow carbon fiber widely spread at the spreading of the carbon fiber (S40) is multi-divided in the longitudinal direction of the fiber.

[0094] It is preferable to use multiple ring knives 801, which are provided at predetermined intervals in a direction perpendicular to the transport direction of the carbon fiber, to multi-divide the large tow carbon fiber in the longitudinal direction of the fiber, but is not limited thereto. As described above, multiple strands of small tow carbon fiber are formed when multi-dividing the large tow carbon fiber in the longitudinal direction of the fiber by using the multiple ring knives 801.

[0095] That is, in the case of supplying large tow carbon fiber having 12K to 24K filaments at the supplying of the carbon fiber (S30), after performing the dividing of the carbon fiber (S90), small tow carbon fibers are formed in which the large tow carbon fiber is divided into three to six strands.

[0096] Thus, as each of the small tow carbon fibers formed by dividing has 3,000 to 4,000 filaments, the resin impregnability is greatly improved.

[0097] In addition, as the small tow carbon fiber is obtained by dividing to have multiple strands and supplied to the cutter for the cutting and distributing of the carbon fiber (S50), the small tow carbon fiber obtained by dividing is cut and distributed, whereby the resin impregnability is improved. The method of manufacturing the SMC of the present invention may further include supplying a reinforcing fabric (S100).

[0098] Referring to FIGS. 13 and 14 is desirable for easy understanding of the embodiment.

[0099] At the supplying of the reinforcing fabric (S100), the reinforcing fabric wound on a fiber roll is unwound therefrom continuously, and is continuously stacked on the bottom resin applied on the bottom film along the longitudinal direction of the bottom film.

[0100] Here, the reinforcing fabric may be any one among unidirectional (UD) carbon fabric, non-crimp fabric (NCF), carbon fabric, glass fabric, and aramid fabric.

[0101] A process for the reinforcing fabric at supplying of the reinforcing fabric (S100) is performed on a reinforcing fabric line which is separate from the film transport line on which the processes for the film at the supplying of the bottom film (S10) and at the applying of the bottom resin (S20) are performed. Afterward, the reinforcing fabric is supplied to the film transport line.

[0102] As the bottom film and the top film are laminated by pressure of the laminating rollers 701 at the laminating of the films (S80), the reinforcing fabric is impregnated with the resin whereby the physical properties such as tensile strength, bend strength, etc. of the SMC are greatly improved.

[0103] That is, the carbon fiber is cut into a predetermined length by a cutter at the cutting and distributing of the carbon fiber (S50) and distributed on the bottom resin in the form of fiber strands such that the carbon fiber having a short length is impregnated with the resin, thereby improving the physical properties and moldability of the SMC.

[0104] Meanwhile, the reinforcing fabric supplied at the supplying of the reinforcing fabric (S100) has a form of a fabric with a predetermined width, and is supplied along the longitudinal direction of the bottom film, stacked on the bottom resin, and then impregnated with the resin at the laminating of the films (S80), whereby the physical properties such as tensile strength, bend strength, etc. of the SMC are greatly improved.

[0105] Thus, by further performing supplying of the reinforcing fabric (S100), the physical properties such as the tensile strength, the bend strength, etc. of the SMC can be improved.

[0106] FIG. 3 is a diagram showing a configuration of an apparatus for manufacturing the SMC according to an embodiment of the present invention.

[0107] A detailed description will be described with reference to FIG. 3.

[0108] The apparatus for manufacturing the SMC of the present invention includes a bottom film supplying portion 10, a first slot die 20a, a carbon fiber supplying portion 30, a spreading portion 40, a cutting portion 50, a top film supplying portion 60, a second slot die 20b, and a film laminating portion 70.

[0109] The bottom film supplying portion 10 is provided with a film roll and unwinds a bottom film wound on the film roll for supply thereof.

[0110] It is preferable that the bottom film is a plastic film such as polyethylene (PE), polypropylene (PP), polyvinylidene fluoride (PVDF), and polyethylene terephthalate (PET).

[0111] FIG. 4 is a side cross-sectional view showing the first slot die of the apparatus for manufacturing the SMC according to the embodiment of the present invention.

[0112] A detailed description will be described with reference to FIGS. 3 to 4.

[0113] The first slot die 20a is provided on a transport path of the bottom film supplied from the bottom film supplying portion 10 to apply a bottom resin on the bottom film.

[0114] The first slot die 20a includes die blocks 201 and a shim plate 202.

[0115] The die blocks 201 are provided as one symmetrical pair, and a first die block 201 is configured with a manifold 201a. A resin supplied by a resin supplier (not shown) is filled in the manifold 201a, and a discharge hole 201b through which the resin is discharged is provided at lower ends of the die blocks 201.

[0116] The shim plate 202 is disposed between the pair of die blocks 201, whereby it is possible to precisely control a discharge amount of the resin discharged from the discharge hole 201b of the die blocks 201 by adjusting the thickness or height of the shim plate 202.

[0117] In addition, the first slot die 20a applies the resin on the bottom film or on a lower surface of the top film while being spaced apart therefrom at a predetermined distance, whereby it is possible to precisely control the coating thickness of the resin by precise control of the discharge amount of the resin and control of the transport speed of the film.

[0118] In particular, with respect to a structure of the first slot die 20a, the discharge hole 201b through which the resin is discharged is structurally configured in a straight line without deviation of the height thereof such that, when the resin is discharged from the discharge hole 201b and applied on the bottom film, it is possible to minimize the thickness deviation of the right and left sides of the resin coated surface.

[0119] In addition, by controlling the discharge pressure of the resin, it is possible to discharge very small amount of the resin whereby it is easy to obtain a precise thickness of the resin.

[0120] The carbon fiber supplying portion 30 is provided with a creel on which multiple carbon fiber bobbins are mounted to supply a large tow carbon fiber, which is wound on the carbon fiber bobbins, by unwinding the large tow carbon fiber therefrom.

[0121] FIG. 5 is an exemplary plan view showing a spreading portion of the apparatus for manufacturing the SMC according to the embodiment of the present invention.

[0122] A detailed description will be described with reference to FIGS. 3 to 5.

[0123] The spreading portion 40 is provided with the multiple spreading rollers 401, which have a heating means and a vibrating means individually and are spaced apart from each other at predetermined intervals. In addition, the spreading portion 40 spreads the large tow carbon fiber supplied from the carbon fiber supplying portion 30 for widening while transporting the large tow carbon fiber in the longitudinal direction of the fiber.

[0124] Here, it is preferable that the large tow carbon fiber supplied from the carbon fiber supplying portion 30 has 12K to 24K filaments, and the width thereof is increased to 15 mm to 25 mm by the spreading portion 40.

[0125] Thus, when the large tow carbon fiber supplied from the carbon fiber supplying portion 30 passes through the spreading portion 40, the height thereof is lowered and the width thereof is increased such that spacings between the filaments composing the large tow carbon fiber is increased whereby the resin impregnability is improved.

[0126] FIG. 6 is a side cross-sectional view showing a cutting portion of the apparatus for manufacturing the SMC according to the embodiment of the present invention.

[0127] A detailed description will be described with reference to FIGS. 3 to 6.

[0128] The cutting portion 50 cuts the carbon fiber supplied from the spreading portion 40 to be increase the width thereof into a predetermined length and distributes the obtained carbon fiber on the bottom resin applied on the bottom film.

[0129] The cutting portion 50 includes a support roller 501, a cutting roller 502, and a drive motor 503, for cutting the carbon fiber.

[0130] The support roller 501 is provided with a first rotating shaft 501a, and configured with multiple cutting grooves on an outer circumferential surface thereof in predetermined intervals.

[0131] The cutting roller 502 is provided with a second rotating shaft 502a disposed in the same direction with the first rotating shaft 501a, and configured in which multiple pressing members 502b supporting the carbon fiber and multiple cutters 502c cutting the carbon fiber are alternately provided at predetermined intervals on an outer circumferential surface of the cutting roller 502.

[0132] The drive motor 503 provides rotating power to the support roller 501 and the cutting roller 502.

[0133] Thus, when the carbon fiber widened and transported from the spreading portion 40 is supplied between the support roller 501 and the cutting roller 502, the carbon fiber is held between the pressing members 502b and the outer circumferential surface of the support roller 501. Then, as the support roller 501 and the cutting roller 502 rotate in a direction to engage with each other, the cutters 502c are inserted into the cutting grooves such that the carbon fiber is cut, and the cut carbon fiber falls downward and is distributed on the bottom resin applied on the bottom film.

[0134] The top film supplying portion 60 is provided with a film roll and unwinds a top film wound on the film roll for supply thereof. It is preferable that the top film is the plastic film which is the same material as the bottom film, but it is not limited thereto.

[0135] The second slot die 20b is provided on a transport path of the top film supplied from the top film supplying portion 60 to apply a top resin on a lower surface of the top film.

[0136] The second slot die 20b has the same structure as the first slot die 20a. As the first slot die 20a, it is possible for the second slot die 20b to precisely control the coating thickness of the resin by precise control of the discharge amount of the resin and control of the transport speed of the film, whereby it is possible to minimize the thickness deviation of the right and left sides of the resin coated surface and to obtain a precise thickness of the resin.

[0137] FIG. 7 is a side cross-sectional view showing an SMC manufactured by the apparatus for manufacturing the SMC according to the embodiment of the present invention.

[0138] A detailed description will be described with reference to FIGS. 3 to 7.

[0139] The film laminating portion 70 passes the top film, which is supplied upside down such that the carbon fiber on the bottom resin is covered with the top resin, and the bottom film between laminating rollers 701 arranged up and down such that the bottom film and the top film are pressurized with a predetermined pressure to laminate.

[0140] The carbon fiber (C) is positioned between the bottom resin (B) applied on the bottom film (A) and the top resin (E) applied on the lower surface of the top film (D), and when the bottom film (A) and the top film (D) are laminated by the film laminating portion 70, the pressure applied by the film laminating portion 70 causes the bottom resin (B) and the top resin (E) to penetrate between the filaments of the carbon fiber (C) from the upper and lower portions of the carbon fiber (C) whereby the impregnation of the resin is performed.

[0141] FIG. 8 is a diagram showing a configuration of an apparatus for manufacturing an SMC according to a second embodiment of the present invention, and FIG. 9 is a side cross-sectional view showing an SMC manufactured by the apparatus for manufacturing the SMC according to the second embodiment of the present invention.

[0142] A detailed description will be described with reference to FIGS. 8 and 9.

[0143] The cutting portion 50 may be provided with a first cutter 50a and a second cutter 50b, and may be further provided with a third slot die 20c.

[0144] The first cutter 50a and the second cutter 50b are disposed to be spaced apart from each other by a predetermined distance along the transport direction of the bottom film such that the large tow carbon fiber widened at the spreading portion 40 is separately supplied to the first cutter 50a and the second cutter 50b. Therefore, in the case that the carbon fiber cut into the predetermined length by the first cutter 50a and the second cutter 50b is distributed on the bottom resin applied on the bottom film, the carbon fiber is distributed at a predetermined distance such that it is possible to suppress a concentration and an orientation of the distributed carbon fiber, thereby enabling uniform distribution of the carbon fiber.

[0145] That is, in the manufacturing process of SMC, the carbon fiber is distributed uniformly rather than being stacked in one place, whereby the resin impregnability is improved, which is advantageous for improving the physical properties of the SMC.

[0146] In the case of distributing the cut carbon fiber at a single point, when a predetermined amount, for example, 100 g of cut carbon fiber, is to be distributed on the bottom resin of a 1 m section applied on the bottom film being transported at a constant speed, the concentration and the orientation of the carbon fiber to be distributed are increased due to the large amount of the distributed carbon fiber at the single point such that the distribution of the carbon fiber is limited, which may limit the improvement of the resin impregnability.

[0147] On the other hand, in the case of distributing the cut carbon fiber at multiple points for dividing the distribution amount of the carbon fiber, when a predetermined amount, for example, 100 g of cut carbon fiber, is to be distributed on the bottom resin of a m section applied on the bottom film being transported at a constant speed, 50 g of the cut carbon fiber is individually distributed at the multiple points such that the concentration and the orientation of the carbon fiber are decreased because the amount of the carbon fiber distributed at the single point is reduced.

[0148] That is, when the carbon fiber is distributed at the first cutter 50a and the second cutter 50b, which are disposed to be spaced apart from each other, in the process of transporting the bottom film at a constant speed, the total carbon fiber distribution amount is the same but the total distribution amount is divided into two. As a result, as the concentration and the orientation of the distributed carbon fiber are decreased, it is possible to distribute the carbon fiber uniformly, thereby further improving the resin impregnability.

[0149] The third slot die 20c is disposed between the first cutter 50a and the second cutter 50b, which are disposed to be spaced apart from each other by the predetermined distance, and when the each of the first cutter 50a and the second cutter 50b distributes the carbon fiber, the third slot die 20c applies an intermediate resin F while disposed between the first cutter 50a and the second cutter 50b.

[0150] That is, in the process of transporting the bottom film at a constant speed, after the carbon fiber discharged from the first cutter 50a is distributed on the bottom resin applied on the bottom film, the intermediate resin F discharged from the third slot die 20c is applied on the carbon fiber distributed on the bottom resin, and then, the carbon fiber discharged from the second cutter 50b is distributed on the intermediate resin F.

[0151] Thus, when the bottom film and the top film are laminated by the film laminating portion 70, the carbon fiber is positioned between the bottom resin applied on the bottom film and the top resin applied on the lower surface of the top film and the intermediate resin F.

[0152] Accordingly, the pressure applied by the film laminating portion 70 causes the bottom resin, the top resin, and the intermediate resin F to penetrate between the filaments of the carbon fiber from the upper, middle, and lower portions of the carbon fiber. Thus, the resin impregnability is greatly improved whereby bubble generation is suppressed in the resin impregnation process, and bubbles that are possibly generated in the resin itself are removed by the pressure applied by the film laminating portion 70, thereby minimizing defects in molding SMC products and improving the physical properties thereof.

[0153] FIG. 10 is a block diagram showing a manufacturing process according to a third embodiment of a method of manufacturing an SMC of the present invention; FIG. 11 is a diagram showing a configuration of an apparatus for manufacturing an SMC according to the third embodiment of the present invention; and FIG. 12 is an exemplary plan view showing a dividing portion of the apparatus for manufacturing the SMC according to the third embodiment of the present invention; A detailed description will be described with reference to FIGS. 10 to 12.

[0154] The apparatus for manufacturing the SMC may be further provided with a dividing portion 80.

[0155] The dividing portion 80 includes multiple ring knives 801, which are provided at predetermined intervals in a direction perpendicular to the longitudinal direction of the fiber.

[0156] The dividing portion 80 divides the large tow carbon fiber widely spread by the spreading portion 40 into multiple strands by using the multiple ring knives 801 along the longitudinal direction of the fiber to obtain multiple strands of small tow carbon fiber.

[0157] Here, it is preferable that the large tow carbon fiber having 12K to 24K filaments and supplied from the carbon fiber supplying portion 30 is divided into three to six strands.

[0158] Thus, in the process of supplying the widely spread carbon fiber to the cutting portion 50, it is possible to prevent the widely spread carbon fiber from combining again due to entanglement of the filaments.

[0159] In addition, by dividing the large tow carbon fiber into the multiple strands of small tow carbon fiber to supply to the cutting portion 50, despite the possibility that the carbon fiber is combined due to entanglement of the filaments in the process of supplying the carbon fiber, the resin impregnability is improved compared to the case of using the large tow carbon fiber because the small tow carbon fiber has a small number of filaments.

[0160] Meanwhile, with respect to dividing the large tow carbon fiber by using the dividing portion 80, dividing into two strands has an effect such that efficiency is low compared to additional processes. On the other hand, when dividing the large tow carbon fiber into seven or more strands, the amount of dust generated in the dividing process of the large tow carbon fiber is increased such that additional dust processing equipment is required to handle the dust whereby the manufacturing cost is increased due to the operation of the dust processing equipment.

[0161] Furthermore, in the process of dividing the large tow carbon fiber by using the dividing portion 80, the filaments composing the carbon fiber may be cut off. When dividing the filaments into seven or more strands, the amount of cut filaments may increase.

[0162] FIG. 13 is a block diagram showing a manufacturing process according to a forth embodiment of a method of manufacturing an SMC of the present invention; FIG. 14 is a diagram showing a configuration of an apparatus for manufacturing an SMC according to the forth embodiment of the present invention; and FIGS. 15A and 15B are side cross-sectional views showing SMCs manufactured by the apparatus for manufacturing the SMC according to the fourth embodiment of the present invention.

[0163] A detailed description will be described with reference to FIGS. 13, 14, 15A, and 15B.

[0164] The apparatus for manufacturing the SMC may be further provided with a reinforcing fabric supplying portion 90.

[0165] The reinforcing fabric supplying portion 90 is provided with a fiber roll, and supplies the reinforcing fabric wound on the fiber roll by unwinding, and continuously stacks the unwound reinforcing fabric on the bottom resin applied on the bottom film along the longitudinal direction of the bottom film.

[0166] In addition, multiple reinforcing fabric supplying portions 90 may be disposed to be spaced apart from each other, the multiple reinforcing fabric supplying portions 90 supplying different types of reinforcing fabrics at the same time.

[0167] Here, it is preferable that the reinforcing fabric supplying portions 90 are disposed to be spaced apart from each other by predetermined intervals along the transport direction of the bottom film, and the cutting portion 50 distributing the cut carbon fiber and the slot die applying the resin are disposed between the multiple reinforcing fabric supplying portions 90.

[0168] The reinforcing fabric may be any one among unidirectional (UD) carbon fabric, non-crimp fabric (NCF), carbon fabric, glass fabric, and aramid fabric. Thus, as the bottom film and the top film are laminated by the pressure of the laminating rollers 701 of the film laminating portion 70, the reinforcing fabric is impregnated with the resin whereby the physical properties such as tensile strength, bend strength, etc. of the SMC are greatly improved.

[0169] That is, as the reinforcing fabric having a form of a fabric with a predetermined width is supplied along the longitudinal direction of the bottom film and stacked on the bottom resin, the physical properties such as tensile strength, bend strength, etc. of the SMC product with the reinforcing fabric are greatly improved compared to SMC manufactured by impregnating only the carbon fiber cut into the predetermined length with the resin.

[0170] Although the preferred embodiments of the present invention have been described for illustrative purposes, and should not be construed as being restrictive. Those skilled in the art will appreciate that various modifications, additions and substitutions are possible, without departing from the scope and spirit of the invention. In addition, it should be understood that other advantageous effects not described in the above description of the invention and apparent therefrom also fall within the scope of the invention.