Method for Preparing Connector-free Anode-supported Solid Oxide Fuel Cell Stack by Means of 3D Printing

Abstract

The present disclosure belongs to the technical field of solid oxide fuel cell stacks, and particularly relates to a method for preparing a connector-free anode-supported solid oxide fuel cell stack by means of 3D printing. The method includes taking a mixed paste of an anode ceramic powder and a photosensitive resin as a raw material, and preparing a three-dimensional channel honeycomb-type anode-supported matrix by means of 3D printing; and obtaining an anode-supported solid oxide fuel cell by means of an impregnation method, effectively bringing same into contact, and abutting and sealing same in the order of a cathode, an anode and a cathode, and forming the connector-free anode-supported solid oxide fuel cell stack after performing connection in series.

Claims

1. A method for preparing a connector-free anode-supported solid oxide fuel cell stack by means of 3D printing, wherein taking a mixed paste of an anode ceramic powder body and a photosensitive resin as a raw material, a honeycomb-type anode-supported matrix with three-dimensional channels is prepared by means of 3D printing; and anode-supported solid oxide fuel cells are obtained by means of an impregnation method, and the anode-supported solid oxide fuel cells are abutted and sealed effectively in a manner of cathode-anode-cathode, so that the connector-free anode-supported solid oxide fuel cell stack is formed after performing connection in series.

2. The method for preparing a connector-free anode-supported solid oxide fuel cell stack by means of 3D printing according to claim 1, comprising steps of: (1) with the mixed paste of the anode ceramic powder body and the photosensitive resin being taken as the raw material, designing a geometrical configuration of a cell stack using 3D drawing software, slicing and layering the geometrical configuration of the cell stack by means of 3D printing software, and performing layered printing using a 3D printer to prepare a green body of the honeycomb-type anode-supported matrix with three-dimensional channels in a manner of one-step forming; (2) debinding and sintering the green body to obtain the honeycomb-type anode-supported matrix with three-dimensional channels; (3) sequentially depositing an electrolyte layer and a cathode layer on the honeycomb-type anode-supported matrix with three-dimensional channels by means of the impregnation method, to obtain each of the anode-supported solid oxide fuel cells; and (4) effectively abutting and sealing a plurality of the anode-supported solid oxide fuel cells in the manner of cathode-anode-cathode, to realize a series connection of the plurality of the anode-supported solid oxide fuel cells, and form the connector-free anode-supported solid oxide fuel cell stack.

3. The method for preparing a connector-free anode-supported solid oxide fuel cell stack by means of 3D printing according to claim 2, wherein a mass percentage of the anode ceramic powder body to the photosensitive resin is 70:21-70:30.

4. The method for preparing a connector-free anode-supported solid oxide fuel cell stack by means of 3D printing according to claim 2, wherein (1) a material used for the anode ceramic powder body is one or more selected from the group consisting of conductive ceramic materials and mixed conductor oxide materials; the conductive ceramic materials are selected from the group consisting of Ni-based cermet materials, Ag-based composite anode materials and Cu-based cermet anode materials; the mixed conductor oxide materials are selected from the group consisting of LaCrO.sub.3-based series, SrTiO3-based series and Sr2MgMoO.sub.3-based series oxide materials; and the anode ceramic powder body and the electrolyte layer are of a same type of material; (2) a material used for the electrolyte layer is one or more selected from the group consisting of zirconium oxide-based oxides, cerium oxide-based oxides, bismuth oxide-based oxides, lanthanum gallate-based oxides, ABO.sub.3 perovskite-type structure electrolytes and apatite type electrolytes of a general formula Ln.sub.10(MO.sub.4).sub.6O.sub.2; and the zirconium oxide-based oxides, the cerium oxide-based oxides, and the bismuth oxide-based oxides have a structure of X.sub.aY.sub.1−aO.sub.2−δ, wherein X is one or more selected from the group consisting of calcium, yttrium, scandium, samarium, gadolinium and praseodymium metallic elements; Y is one or more selected from the group consisting of zirconium, cerium and bismuth metallic elements; and δ is a number of oxygen deficiency, 0≤a≤1; and (3) a material used for the cathode layer is one or more selected from the group consisting of a doped perovskite-type ceramic with a structure of ABO.sub.3−δ, a double perovskite-type ceramic with a structure of A.sub.2B.sub.2O.sub.5+δ, an R—P-type perovskite-like ceramic with a structure of A.sub.2BO.sub.4+δand a superconducting material, wherein A is one or more selected from the group consisting of lanthanum, cerium, praseodymium, neodymium, samarium, europium, gadolinium, terbium, dysprosium, holmium, erbium, thulium, ytterbium, lutetium, calcium, strontium and barium; B is one or more selected from the group consisting of scandium, titanium, vanadium, chromium, manganese, iron, cobalt, nickel, copper, zinc, gallium, aluminum, yttrium, zirconium, niobium, molybdenum, hafnium, tantalum, tungsten and rhenium; δ is the number of oxygen deficiency; the superconducting material comprises YSr.sub.2Cu.sub.2MO.sub.7+δ, YB.sub.aCo.sub.3ZnO.sub.7−δ and Ca.sub.3Co.sub.4O.sub.9−δ, wherein M is iron or cobalt; δ is the number of oxygen deficiency; all materials used for the anode ceramic powder body, the electrolyte layer and the cathode layer have a particle size of 0.02-10 μm.

5. The method for preparing a connector-free anode-supported solid oxide fuel cell stack by means of 3D printing according to claim 2, wherein the connector-free anode-supported solid oxide fuel cell stack is formed by effectively abutting and sealing, in the manner of cathode-anode-cathode, a plurality of the anode-supported solid oxide fuel cells in a manner of series connection; each cell comprises multiple groups of ceramic microtubes that are arranged in parallel to each other, intratubal fluid channels are formed inside the ceramic microtubes, each group of the ceramic microtubes is arranged on respective ceramic rib plates, each group of the ceramic microtubes comprises a plurality of the ceramic microtubes with tube openings of the ceramic microtubes being linearly arranged, the multiple groups of the ceramic microtubes arranged in parallel are separated from each other, to form inter-tube fluid channels; and upper ends and lower ends of the ceramic microtubes are connected with ceramic tube plates to fixedly connect the ceramic microtubes into a bundle, with an end face being in a honeycomb shape, two sides of two ceramic tube plates are connected by two ceramic support plates, and the ceramic support plates are perpendicular to the ceramic tube plates, and the ceramic tube plates, the ceramic support plates, the ceramic microtubes and the ceramic rib plates are all integrally molded by 3D printing; and the inter-tube fluid channels and the intratubal fluid channels are straight-through channels or S-shaped zigzag channels.

6. The method for preparing a connector-free anode-supported solid oxide fuel cell stack by means of 3D printing according to claim 2, wherein when the electrolyte layer and the cathode layer are sequentially deposited on the honeycomb-type anode-supported matrix with three-dimensional channels, impregnation is performed in one of two manners including an impregnation manner I or an impregnation manner II: the impregnation manner I: sequentially impregnating the electrolyte layer and the cathode layer on an outer surface ABCD of a ceramic tube plate where upper-end tube openings of the intratubal fluid channels and the ceramic microtubes are located; and the impregnation manner II: sequentially impregnating the electrolyte layer and the cathode layer on a left end face AA′D′D of end faces where the inter-tube fluid channels and the ceramic rib plates are located; wherein when the impregnation manner I is used, in an impregnation process, a blank area is reserved inside each of the intratubal fluid channels, and the blank area is only impregnated with the electrolyte layer, but no cathode layer; when the impregnation manner II is used, in an impregnation process, a blank area is reserved inside the inter-tube fluid channels, and the blank area is only impregnated with the electrolyte layer, but no cathode layer; and a fuel gas is introduced into a side of the honeycomb-type anode-supported matrix with three-dimensional channels, and an oxidizing gas or air is introduced into a side of the cathode layer.

7. The method for preparing a connector-free anode-supported solid oxide fuel cell stack by means of 3D printing according to claim 6, wherein when the impregnation manner I is used, the blank area is an annular area, located at a lower end of each of the intratubal fluid channels, and the annular area has a height of 0.1-1 mm; and when the impregnation manner II is used, the blank area is an area of all the inter-tube fluid channels formed between an end face resulted from translating, towards an interior of the cell by 0.1-1 mm, a right end face BB′C′C of end faces where the ceramic rib plates are located and the right end face BB′C′C.

8. The method for preparing a connector-free anode-supported solid oxide fuel cell stack by means of 3D printing according to claim 2, wherein the connector-free anode-supported solid oxide fuel cell stack is formed in a manner which is different depending on the different impregnation manner: when the impregnation manner I is used, an outer surface ABCD of a ceramic tube plate where upper-end tube openings of ceramic microtubes of one anode-supported solid oxide fuel cell are located and an outer surface A′B′C′D′ of a ceramic tube plate where lower-end tube openings of ceramic microtubes of another anode-supported solid oxide fuel cell are located are effectively abutted and sealed, in the manner of cathode-anode-cathode, to form the connector-free anode-supported solid oxide fuel cell stack; and when the impregnation manner II is used, a left end face AA′D′D of end faces where ceramic rib plates of one anode-supported solid oxide fuel cell are located and a right end face BB′C′C of end faces where ceramic rib plates of another anode-supported solid oxide fuel cell are located are effectively abutted and sealed, in the manner of cathode-anode-cathode, to form the connector-free anode-supported solid oxide fuel cell stack.

9. The method for preparing a connector-free anode-supported solid oxide fuel cell stack by means of 3D printing according to claim 2, wherein the debinding refers to heat treatment in a certain atmosphere at a temperature lower than 800° C. for 5-30 h; the sintering refers to heat treatment in a certain atmosphere at a temperature of 800-1600° C. for 2-10 h, wherein the atmosphere during the debinding is vacuum atmosphere, normal pressure atmosphere or inert gas atmosphere; and the atmosphere during the sintering is oxidizing atmosphere or ordinary atmosphere.

10. The method for preparing a connector-free anode-supported solid oxide fuel cell stack by means of 3D printing according to claim 2, wherein the electrolyte layer has a thickness of 1-20 μm; and the cathode layer is a porous layer, with a thickness of 5-20μm.

11. The method for preparing a connector-free anode-supported solid oxide fuel cell stack by means of 3D printing according to claim 5, wherein: when the electrolyte layer and the cathode layer are sequentially deposited on the honeycomb-type anode-supported matrix with three-dimensional channels, impregnation is performed in one of two manners including an impregnation manner I or an impregnation manner II: the impregnation manner I: sequentially impregnating the electrolyte layer and the cathode layer on an outer surface ABCD of a ceramic tube plate where upper-end tube openings of the intratubal fluid channels and the ceramic microtubes are located; and the impregnation manner II: sequentially impregnating the electrolyte layer and the cathode layer on a left end face AA′D′D of end faces where the inter-tube fluid channels and the ceramic rib plates are located; wherein when the impregnation manner I is used, in an impregnation process, a blank area is reserved inside each of the intratubal fluid channels, and the blank area is only impregnated with the electrolyte layer, but no cathode layer; when the impregnation manner II is used, in an impregnation process, a blank area is reserved inside the inter-tube fluid channels, and the blank area is only impregnated with the electrolyte layer, but no cathode layer; and a fuel gas is introduced into a side of the honeycomb-type anode-supported matrix with three-dimensional channels, and an oxidizing gas or air is introduced into a side of the cathode layer.

12. The method for preparing a connector-free anode-supported solid oxide fuel cell stack by means of 3D printing according to claim 6, wherein the connector-free anode-supported solid oxide fuel cell stack is formed in a manner which is different depending on the different impregnation manner: when the impregnation manner I is used, an outer surface ABCD of a ceramic tube plate where upper-end tube openings of ceramic microtubes of one anode-supported solid oxide fuel cell are located and an outer surface A′B′C′D′ of a ceramic tube plate where lower-end tube openings of ceramic microtubes of another anode-supported solid oxide fuel cell are located are effectively abutted and sealed, in the manner of cathode-anode-cathode, to form the connector-free anode-supported solid oxide fuel cell stack; and when the impregnation manner II is used, a left end face AA′D′D of end faces where ceramic rib plates of one anode-supported solid oxide fuel cell are located and a right end face BB′C′C of end faces where ceramic rib plates of another anode-supported solid oxide fuel cell are located are effectively abutted and sealed, in the manner of cathode-anode-cathode, to form the connector-free anode-supported solid oxide fuel cell stack.

Description

BRIEF DESCRIPTION OF DRAWINGS

[0049] FIG. 1 is a structural schematic diagram of a model of a honeycomb-type anode-supported matrix with three-dimensional channels of the present disclosure;

[0050] FIG. 2 is a structural schematic diagram of a connector-free anode-supported solid oxide fuel cell stack in Embodiment 1;

[0051] FIG. 3 is a structural schematic diagram of the inside of the connector-free anode-supported solid oxide fuel cell stack in Embodiment 1;

[0052] FIG. 4 is a schematic diagram of the connector-free anode-supported solid oxide fuel cell stack in Embodiment 2; and

[0053] FIG. 5 is a structural schematic diagram of the inside of the connector-free anode-supported solid oxide fuel cell stack in Embodiment 2;

[0054] In FIGS. 1-5, 1. blank area; 2. cathode layer; 3. electrolyte layer; 4. anode-supported matrix; 5. inter-tube fluid channel; 6. intratubal fluid channel; 7. ceramic support plate; 8. ceramic rib plate; 9. ceramic microtube; 10. ceramic tube plate.

DETAILED DESCRIPTION OF EMBODIMENTS

[0055] Below the present disclosure is further described in combination with the embodiments.

Embodiment 1

[0056] 100 g Ni−GDC (Gd.sub.0.1Ce.sub.0.9O.sub.2−δ) anode ceramic powder body (with a particle size of 800 nm) is mixed with a photosensitive resin and ethanol according to the proportion of 70 wt. % the powder body, 27.3 wt. % the photosensitive resin and 2.7 wt. % the ethanol, and the mixture is stirred and mixed for 12 h, and then ball-milled for 4 h to form a uniform paste. A model of a honeycomb-type anode-supported matrix with three-dimensional channels is established by utilizing Catia software, wherein the model is 2 cm in both length and width, and 1 cm in height, has 28 ceramic microtubes in a longitudinal direction to provide intratubal fluid channels, and 6 channels in a transverse direction to provide inter-tube fluid channels, referring to FIG. 1 for a structural schematic diagram thereof, and the model is led into CreationWorkshop software for slicing and printing. An AOTOCERA ceramic 3D printer of Beijing Ten Dimensions Technology Co. Ltd. is used as the 3D printer. The paste is added into a resin tank, and the three-dimensional printer is controlled by a computer to mold the paste by layered printing according to a designed three-dimensional entity model structure diagram, to obtain a green body of the honeycomb-type anode-supported matrix with three-dimensional channels. After the printing is completed, the green body of the honeycomb-type anode-supported matrix with three-dimensional channels is put into industrial alcohol to clean, to remove uncured paste, and is naturally dried in the air at room temperature, then is placed in a programmed temperature-control electric furnace, heated to 800° C. at a heating rate of 0.5° C./min under a vacuum condition, and the temperature is preserved for 2 hours so as to remove an organic binder in the green body. Then the debinded body is heated to 1100° C. at a heating rate of 2° C./min and 4 h plateau at 1100° C. to ensure the densification and high strength of the sintered body. Finally the sintered body is cooled to room temperature at a cooling rate of 2° C./min to obtain the honeycomb-type anode-supported matrix with three-dimensional channels.

[0057] On an outer surface ABCD of a ceramic tube plate 10 where upper-end tube openings of the intratubal fluid channels 6 and the ceramic microtubes 9 are located, a dense GDC electrolyte layer and a porous BSCF (Ba.sub.0.6Sr.sub.0.4Co.sub.0.5Fe0.5O.sub.3−δ) cathode layer are sequentially impregnated and deposited, to form an anode-supported solid oxide fuel cell. In the impregnation process, annular blank areas with height of 1 mm are reserved at lower ends of the intratubal fluid channels 6, and such annular blank area is only impregnated with the GDC electrolyte layer, but no BSCF porous cathode layer.

[0058] The outer surface ABCD of the ceramic tube plate 10 where upper-end tube openings of the ceramic microtubes 9 of one cell are located and an outer surface A′B′C′D′ of the ceramic tube plate 10 where lower-end tube openings of the ceramic microtubes 9 of another cell are located are effectively contacted, abutted and sealed by using a silver paste, realizing series connection of a plurality of cells without a connector, and forming a connector-free anode-supported solid oxide fuel cell stack, referring to FIG. 2. The dense electrolyte layer has a thickness of 8 μm, and the cathode layer has a thickness of 10 μm.

[0059] A silver wire is placed on the outer surface ABCD of an uppermost cell of the connector-free anode-supported solid oxide fuel cell stack, and a cathode current is led out through the silver wire; a silver wire is placed on the outer surface A′B′C′D′ of the lowermost cell of the connector-free anode-supported solid oxide fuel cell stack, and an anode current is led out through the silver wire.

[0060] In Embodiment 1, the connector-free anode-supported solid oxide fuel cell stack is formed by effectively contacting, abutting, and sealing a plurality of anode-supported solid oxide fuel cells, and connecting them in series in a manner of cathode-anode-cathode; each cell includes multiple groups of ceramic microtubes 9 which are arranged in parallel to each other, the intratubal fluid channels 6 are formed inside the ceramic microtubes 9, each group of ceramic microtubes 9 is arranged on respective ceramic rib plates 8, each group of ceramic microtubes 9 includes a plurality of ceramic microtubes 9 with the tube openings of the ceramic microtubes being linearly arranged, the multiple groups of ceramic microtubes 9 which are arranged in parallel are separated from each other, forming the inter-tube fluid channels 5; upper ends and lower ends of the ceramic microtubes 9 are connected with the ceramic tube plates 10 to fixedly connect the ceramic microtubes 9 into a bundle, with an end face being in a honeycomb shape, two sides of the two ceramic tube plates 10 are connected by two ceramic support plates 7, and the ceramic support plates 7 are perpendicular to the ceramic tube plates 10. The ceramic tube plates 10, the ceramic support plates 7, the ceramic microtubes 9 and the ceramic rib plates 8 are all integrally molded by 3D printing, referring to FIG. 3 for a structure thereof.

Embodiment 2

[0061] 70 g Ni—YSZ (Y.sub.0.08Zr.sub.0.92O.sub.2−δ) anode ceramic powder body (with a particle size of 500 nm) is uniformly mixed with 7 g starch by a mixer. 70 wt. % the powder body, 27.3 wt. % a photosensitive resin, 1.4 wt. % ethanol and 1.3 wt. % PEG are stirred and mixed for 12 h, and then ball-milled for 4 h to form a uniform paste. A model of a honeycomb-type anode-supported matrix with three-dimensional channels is established by utilizing UG software, wherein the model is 2 cm in both length and width, and 1 cm in height, has 28 ceramic microtubes in a longitudinal direction to provide intratubal fluid channels, and 6 channels in a transverse direction to provide inter-tube fluid channels, referring to FIG. 1 for a structural schematic diagram thereof, and the model is led into CreationWorkshop software for slicing and printing. An AOTOCERA ceramic 3D printer of Beijing Ten Dimensions Technology Co. Ltd. is used as the 3D printer. The paste is added into a resin tank, and the three-dimensional printer is controlled by a computer to mold the paste by layered printing according to a designed three-dimensional entity model structure diagram, to obtain a green body of the honeycomb-type anode-supported matrix with three-dimensional channels. After the printing is completed, the green body of the honeycomb-type anode-supported matrix with three-dimensional channels is put into industrial alcohol to clean, to remove uncured paste, and is naturally dried in the air at room temperature, then is placed in a programmed temperature-control electric furnace, heated to 600° C. at a heating rate of 0.5° C./min under a vacuum condition with holding time of 2 h at 600° C. so as to remove an organic binder in the green body of the honeycomb-type anode-supported matrix with three-dimensional channels. Then the debinded body of the honeycomb-type anode-supported matrix with three-dimensional channels is put into a sintering furnace, and heated to 1200° C. at a heating rate of 2° C./min in an air atmosphere, and 4 h plateau at 1200° C. so that the body is fully sintered, and finally the sintered body is cooled to room temperature at a cooling rate of 2° C./min to obtain the honeycomb-type anode-supported matrix with three-dimensional channels.

[0062] On a left end face AA′D′D of end faces where the inter-tube fluid channels 5 and the ceramic rib plates 8 are located, a dense YSZ electrolyte layer and a porous LSM (La.sub.0.8Sr.sub.0.2MnO.sub.3−δ) cathode layer are sequentially impregnated and deposited, to form an anode-supported solid oxide fuel cell. In the impregnation process, a blank area is left at a right ends of the inter-tube fluid channels 5, this blank area is only impregnated with the YSZ electrolyte layer, but no LSM cathode layer, and the blank area is an area of all the inter-tube fluid channels 5, which area is formed between an end face resulted from translating a right end face BB′C′C of end faces where the ceramic rib plates 8 are located towards the interior of the cell by 1 mm and the right end face BB′C′C. The left end face AA′D′D of the end faces where the ceramic rib plates 8 of one cell are located and the right end face BB′C′C of the end faces where the ceramic rib plates 8 of another cell are located are effectively contacted, abutted and sealed by using a silver paste, thereby realizing series connection of a plurality of cells without a connector, and forming a connector-free anode-supported solid oxide fuel cell stack, referring to FIG. 4. The dense electrolyte layer has a thickness of 10 μm, and the cathode layer has a thickness of 10 μm.

[0063] A silver wire is placed inside the ceramic microtube 9 of a leftmost cell of the connector-free anode-supported solid oxide fuel cell stack, and an anode current is led out through the silver wire; a silver wire is placed inside the inter-tube fluid channel 5 of a rightmost cell of the connector-free anode-supported solid oxide fuel cell stack, and a cathode current is led out through the silver wire.

[0064] In Embodiment 2, the connector-free anode-supported solid oxide fuel cell stack is formed by effectively contacting, abutting, and sealing a plurality of anode-supported solid oxide fuel cells, and connecting them in series in the manner of cathode-anode-cathode; each cell includes multiple groups of ceramic microtubes 9 which are arranged in parallel to each other, the intratubal fluid channels 6 are formed inside the ceramic microtubes 9, each group of ceramic microtubes 9 is arranged on respective ceramic rib plates 8, each group of ceramic microtubes 9 includes a plurality of ceramic microtubes 9 with the tube openings of the ceramic microtubes being linearly arranged, the multiple groups of ceramic microtubes 9 which are arranged in parallel are separated from each other, forming the inter-tube fluid channels 5; upper ends and lower ends of the ceramic microtubes 9 are connected with the ceramic tube plates 10 to fixedly connect the ceramic microtubes 9 into a bundle, with an end face being in a honeycomb shape, two sides of the two ceramic tube plates 10 are connected by two ceramic support plates 7, and the ceramic support plates 7 are perpendicular to the ceramic tube plates 10. The ceramic tube plates 10, the ceramic support plates 7, the ceramic microtubes 9 and the ceramic rib plates 8 are all integrally molded by 3D printing, referring to FIG. 5 for a structure thereof.

Embodiment 3

[0065] 70 g Ni-SDC (Sm.sub.0.2Ce.sub.0.8O.sub.2−δ) anode ceramic powder body (with a particle size of 500 nm) is uniformly mixed with 7 g starch by a mixer. 70 wt. % the powder body, and 30 wt. % a photosensitive resin are stirred and mixed for 20 h, and then ball-milled for 2 h to form a uniform paste. A model of a honeycomb-type anode-supported matrix with three-dimensional channels is established by utilizing 3DMax software, wherein the model is 2 cm in both length and width, and 1 cm in height, has 28 ceramic microtubes in a longitudinal direction to provide intratubal fluid channels, and 6 channels in a transverse direction to provide inter-tube fluid channels, referring to FIG. 1 for a structural schematic diagram thereof, and the model is led into CreationWorkshop software for slicing and printing. An AOTOCERA ceramic 3D printer of Beijing Ten Dimensions Technology Co. Ltd. is used as the 3D printer. The paste is added into a resin tank, and the three-dimensional printer is controlled by a computer to mold the paste by layered printing according to a designed three-dimensional entity model structure diagram, to obtain a green body of a honeycomb-type anode-supported matrix with three-dimensional channels. After the printing is completed, the green body of the honeycomb-type anode-supported matrix with three-dimensional channels is put into industrial alcohol to clean, to remove uncured paste, and is naturally dried in the air at room temperature, then is placed in a programmed temperature-control electric furnace, and heated to 600° C. at a heating rate of 0.5° C./min under a vacuum condition with holding time of 5 h at 600° C. so as to remove an organic binder in the green body of the honeycomb-type anode-supported matrix with three-dimensional channels. Then the debinded body of the honeycomb-type anode-supported matrix with three-dimensional channels is put into a sintering furnace, and heated to 1100° C. at a heating rate of 2° C./min in an air atmosphere with 4 h plateau at 1100° C. so that the body is fully sintered, and finally the sintered body is cooled to room temperature at a cooling rate of 2° C./min to obtain the honeycomb-type anode-supported matrix with three-dimensional channels.

[0066] On a left end face AA′D′D of end faces where the inter-tube fluid channels 5 and the ceramic rib plates 8 are located, a dense YSZ electrolyte layer and a porous LSCF (La.sub.0.6Sr.sub.0.4CO.sub.0.2Fe.sub.0.8O.sub.3−δ) cathode layer are sequentially impregnated and deposited, to form an anode-supported solid oxide fuel cell. In the impregnation process, a blank area is left at right ends of the inter-tube fluid channels 5, this blank area is only impregnated with the YSZ electrolyte layer, but no LSCF cathode layer, and the blank area is the area of all the inter-tube fluid channels 5 formed between an end face resulted from translating a right end face BB′C′C of end faces where the ceramic rib plates 8 are located towards the interior of the cell by 1 mm and the right end face BB′C′C. The left end face AA′D′D of the end faces where the ceramic rib plates 8 of one cell are located and the right end face BB′C′C of the end faces where the ceramic rib plates 8 of another cell are located are effectively contacted, abutted and sealed by using a silver paste, realizing series connection of a plurality of cells without a connector, and forming a connector-free anode-supported solid oxide fuel cell stack. The dense electrolyte layer has a thickness of 10 μm, and the cathode layer has a thickness of 12 μm.

[0067] A silver wire is placed inside the ceramic microtube 9 of a leftmost cell of the connector-free anode-supported solid oxide fuel cell stack, and an anode current is led out through the silver wire; a silver wire is placed inside the inter-tube fluid channel 5 of a rightmost cell of the connector-free anode-supported solid oxide fuel cell stack, and a cathode current is led out through the silver wire.

[0068] In Embodiment 3, the connector-free anode-supported solid oxide fuel cell stack is formed by effectively contacting, abutting, and sealing a plurality of anode-supported solid oxide fuel cells, and connecting them in series in the manner of cathode-anode-cathode; each cell includes multiple groups of ceramic microtubes 9 which are arranged in parallel to each other, the intratubal fluid channels 6 are formed inside the ceramic microtubes 9, each group of ceramic microtubes 9 is arranged on respective ceramic rib plates 8, each group of ceramic microtubes 9 includes a plurality of ceramic microtubes 9 with the tube openings of the ceramic microtubes being linearly arranged, the multiple groups of ceramic microtubes 9 which are arranged in parallel are separated from each other, forming the inter-tube fluid channels 5; upper ends and lower ends of the ceramic microtubes 9 are connected with the ceramic tube plates 10 to fixedly connect the ceramic microtubes 9 into a bundle, with an end face being in a honeycomb shape, two sides of the two ceramic tube plates 10 are connected by two ceramic support plates 7, and the ceramic support plates 7 are perpendicular to the ceramic tube plates 10. The ceramic tube plates 10, the ceramic support plates 7, the ceramic microtubes 9 and the ceramic rib plates 8 are all integrally molded by 3D printing.